Search Documents

By T. Toda, R. Maddin

A study has been made of the microstructure and mechanical properties of splat-cooled aluminum-base gold alloys with gold concentration from 0.25 to 5.0 wt pct. These alloys have been quenched from the liquid state by a torsion-catapult technique, which has made it possible to pepare specimens suitable for mechanical property measwements. From the electron micrographs it has been shown that the solid solubility of gold in aluminum can be extended to 2.5 wt pct (0.35 at. pct) by splat-cooling, while the maximum equilibrium solubility is known to be less than 0.3 wt pct (0.04 at. pct). The very fine grain size (several tenths of a micron), the extended solid solubility, and the fine dispersion of a second phase (AuAl2) contribute concurrently to a substantial strengthening effect. In Al-5 wt pct Au splat-cooled specimens of less than 50 thickness, the yield strength is 17 kg per sq mm or 6 times as large as the strength of bulk specimens. For the Al-1.0 to 2.5 wt pct Au solid solution obtained by splat-cooling, the yield strength reaches 7.5 kg per sq mm after an aging treatment (for 10 hr at 200°C), while it is 3.7 kg per sq mm for the corresponding bulk specimens. A great deal of research has been done in recent years on the structure and the properties of metals and alloys rapidly quenched from the liquid state.' The term "splat-cool" has been used with the meaning of a rapid quenching from the liquid state., The splat-cooling techniques have produced large numbers of new structures, which are expressed in terms of metastable phases,3 concentrated solid solutions,4 amorphous phases,5'6 new phases,7 and so forth. Nearly all previous studies have concentrated on the physical properties; i.e., crystallography, structure, electrical resistivity, magnetism, and so forth, of the splat-cooled metals and alloys. The mechanical strength of splat-cooled metals and alloys has hardly been investigated except for some recent work by MOSS' on A1-V alloys. The principle common to all experimental techniques developed to obtain very rapid quenching rates is based on the heat transfer by conduction. Liquid must be in good thermal contact with a substrate of high heat conductivity. Both of the published devices known as the "gun" and the "piston and anvil" techniques suffer from certain shortcomings. For example, the specimen obtained by the gun technique is very small and flaky, and hence inadequate for mechanical properties measurements. On the other hand if the material is forced to yield a continuous speci- men by the piston and anvil technique, it is probable that some plastic deformation occurs during the quench. A novel method for rapid quenching of a liquid metal or alloy, the "torsion-catapult", has been devised by Roberge and Herman9 at the University of Pennsylvania. In the apparatus the melt is thrown out of a curved furnace by a catapult and impinges on a copper substrate. The apparatus has the advantage of producing a continuous foil which is relatively large in size and of a quality suitable for the measurements of mechanical properties. The quenching rate is estimated to be of the order of l05 to l06 ºC per sec, (comparable to rates achieved by the piston and anvil technique). In selecting an alloy to be studied we were made aware of the fact that gold was believed to be "insoluble" in in and consequently age hardening in the A1-Au system appeared to be interesting. Quite recently Heirnendahl13-15 revealed that the solid solubility, as determined by transmission electron microscopy, was 0.3 wt pct Au at 640°C and 0.25 wt pct Au at 600°C, decreasing with decreasing temperature. In an A1-0.2 pct Au alloy after quenching from a solution treating temperature of 600°C the yield stress was 2 kg per sq mm, and it increased up to 6 kg per sq mm after aging for 1 to 10 hr at 200°C. The precipitation occurred in the form of platelike particles mainly on (100) matrix planes. The intermediate phase n', the equilibrium phase n (AuAl2), and lattice relationships between both precipitates and the matrix were also investigated by electron microscopy. One of the purposes of the present research is to determine whether or not the solid solubility in this system, in which gold has a very small solubility in

Jan 1, 1970

By H. l. Burghoff, A. I. Blank

The state of knowledge bearing on the stability of copper under stress at elevated temperatures is generally known to be in need of revision and extension. The present investigation, dealing with the creep characteristics of a deoxidized copper of low residual phosphorus content, is intended to contribute in some small measure toward this end. The experimental data presented herein have been correlated by methods of evaluation and interpretation familiar to those who are concerned with crecp of metals. In practice it is common, if not requisite, to use structurally stable materials at elevated temperatures. It is frequently desirable, however, to test materials under conditions that produce structural change, in order to determine the extent of such change and its effect on physical properties, thus making it possible to establish accurately the limiting conditions to which such materials may be safely exposed. The creep characteristics of the drawn copper wire of this investigation arc directly associated with its structural instability at elevated temperatures. Complete realization of this fact is essential to the evaluation of its creep resistance under various conditions. Creep results should apply to steady deformation under equilibrium conditions, but these are seldom attained in only one or two thousand hours. It will be shown that steady creep rate for copper at useful stresses does not usually begin until considerably more time has elapsed. A wholly satisfactory substitute or shortcut for extensive creep testing does not appear to be evident in the application of mathematical analyses to limited experimental data. Material A single lot of phosphorized copper wire was drawn down to 0.125-i11. diameter with a final reduction of 84 per cent. After mechanical straightening, a portion of this wire was annealed to an average grain size of 0.013 mm. in a controlled-atmosphere furnace. The composition and initial properties of the copper in these two conditions are listed in Table I. Photomicrographs of the original structure are shown in Fig. I.

Jan 1, 1945

By Peter Soo

Pvestrained Ferrovac E iron has been neutron-irradiated at approximately 90°C to an integrated flux of 1020 nut (E > 0.82 mev]. The irradiation was found to produce an incveased temperature dependence of the flow stress in addition to a greatly increased athemal stress. Measurements of the flow stress and stress relaxation, from which the activation volume and activation energy for slip were deduced, show that neutron irradiation changes the rate -controlling slip process to one based on dislocation interactions with tetragonal distortions which are Produced around submicroscopic interstitial loops in the lattice. The study indicates that without prestraining prior to irradiation the chances of detecting a change in the rate -controlling slip process are greatly reduced because in the initial stages of slip a substantial fraction of the radiation defects are swept out of the slip plane by gliding dislocations. Thus, activation parameters which are subsequently measured are representative of a greatly reduced defect density and would not differ appreciably from those for unirradi-ated material. The large increase in the athermal component of the flow stress is probably connected with the presence of depleted zones in the lattice which are introduced by irradiation. ALTHOUGH fast neutron-irradiation has not been observed to markedly alter the activation parameters for slip in bcc metals,' small but significant changes do occur. Most experimenters agree that irradiation predominantly increases the athermal component of the yield stress.'-= In addition to this, Laidler and smidt7 have shown that in iron irradiated to 5 X 10" nvt and molybdenum irradiated to 10" nvt, changes occur in the activation volumes for slip. A similar conclusion has been reached by Milasin and Malkin8 for irradiated iron. Work by Ohr et a1.5 shows that for Ferrovac E iron, irradiated to 1.2 X 1016 nvt, small increases in the activation energy for slip also occur. So far these changes in the activation parameters have not been explained on a firm theoretical basis. One important factor which would minimize the chances of detecting a change in the slip mechanism upon irradiation is the presence of "channeling" which has been observed in molybdenum,9 niobium,10 and iron.11These channels are formed by gliding dislocations which sweep irradiation defects out of the active slip planes and thereby create zones in which continued dislocation motion is encouraged. The activation parameters for the dislocations gliding in the defect-free channels would, therefore, be similar to those for unirradiated iron and a change in the rate-controlling slip process would be difficult to detect. In the present work, an attempt has been made to reduce the effect of uneven deformation on the measured activation parameters for slip in neutron-irradiated Ferrovac E iron polycrystals, so that a more realistic assessment of the effects of neutron-irradiation could be made. Primarily, the experiments involve the irradiation of specimens which had been prestrained to 9 pct elongation at room temperature prior to insertion into the reactor. It was hoped that the introduction of a large number of evenly distributed dislocations would substantially decrease any channeling effect which might otherwise occur. MATERIAL AND EXPERIMENTAL PROCEDURE The starting material was vacuum-melted Ferrovac E iron, an analysis of which is given in Table I. The standard tensile specimen had a gage length of 1.125 in., a cross-sectional diameter of 0.120 in., and a re-crystallized grain size of 1.2 x 10-3 in. All tensile tests were conducted on a floor model "Instron" tensile machine at a strain rate of 3 x 10-4 per sec. The irradiation of the prestrained specimens was performed in the Brookhaven High Flux Beam Reactor to an integrated flux of 1020 nvt (E > 0.82 mev) at a temperature of about 90°C. All specimens were excap-sulated in high-purity aluminum sheaths which were lightly swaged around the samples to ensure good thermal contact. Subsequent measurements on the irradiated specimens showed that within experimental accuracy the swaging had not deformed them. EXPERIMENTAL RESULTS Fig. 1 shows the flow stresses for a series of unirradiated control samples. In order to produce a comparable dislocation substructure throughout the test sm range, all specimens were prestrained

Jan 1, 1970

By Charles H. Jacoby, Stanley J. LeFond

Salt, or halite, has a long and most varied history. While we know the Chinese were producing salt as early as 3000 B.C., the first written reference to salt appears in the book of Job recorded about 2250 B.C., which reads: "Can nothing which is unsavory be eaten without salt?" We do not know when man first used or realized that he needed salt. Perhaps one of our early Eolithic ancestors noted a piece of salt shining along the shore of a salt lake or a bay. He may have been attracted by its shining luster and tasted it. He found that it had a tart, zesty, distinctive flavor and perhaps chewing a large piece, became ill. However, by experimentation he soon learned that taken in the proper proportions salt was a very pleasant additive to his food. He may have noticed, too, that it increased his feeling of well-being. Thus, when the curtain of recorded history rises, we find man using salt for his health's sake, seasoning his food with it, feeding it to his animals, and using it in many superstitious and religious ceremonies. These uses, however, are a far cry from the uses for salt today. The first attempts of white man to make salt in continental United States were reported in the year 1614, while the first commercial production was in 1753 from the Kanawha licks. Practically all this salt was for human consumption, preserving food, and curing hides. Prior to the coming of the white man, Indians are known to have made salt from salt springs such as those that existed at Avery Island, LA, Charleston, WV, Saltville, VA, and Onondaga, NY. In 1862 the first rock salt was mined in the US from the Avery Island salt dome. Almost immediately thereafter, rock salt was mined at Saltville, VA and then at Retsof, NY in 1885. Of the more than 39 million tons produced annually in the United States, about 58% or 23 million tons are consumed by the chemical industry in the production of chlorine, caustic soda, hydrochloric acid, sodium metal, and some 30 other basic chemicals. These basic chemicals, in turn, are used in the preparation of approximately 14,000 chemicals which range from soap and detergents, to such chlorinated hydrocarbons as DDT, BHC, carbon tetrachloride, etc. Utilization of cavities created in salt beds and domes has grown rapidly since 1947 until now the waste salt is creating an ecological problem. The uses for both dry- and solution-mined cavities range from the storage of liquid hydrocarbons to containerized storage of toxic wastes, from compressed air for the peak shaving of power to storage of nuclear wastes. Geology Mineralogy Properties: Because of its simple structure, halite, the mineralogical name for salt, was the first structure to be analyzed by X-rays. It has the following properties: Formula: NaCl (Na-39.34%. Cl2-60.66% ) Crystallography: isometric, hexoctahedral, 4/m 32/m Space group: Fm3m A0: 5.627 kX Cell contents: Na4CI4 Habit: usually cubic, rarely octahedral, massive, granular to compact Physical properties: Refractive index: 1.554 Twinning: observed on {111} Cleavage: {001} perfect Fracture: conchoidal, brittle

Jan 1, 1983

By Craig S. Hartley

An approximate expression is obtained for the energy of a closed dislocation loop in equi1ibriu)n with a constant net stress. The result obtained is valid for loops in isotropic or anisotropzc materials provided that they are suJficiently large that the energy per unit length of a segment of the loop can be approximated by that of an infinite straight dislocation tangent to the loop. It is shown that this approximation leads to very close agreement with a more rigorous calculation of the elastic energy of a circular glide loop. The Gibbs-Wulff Form, GWF, of a dislocation is the closed planar loop which has the smallest elastic self-energy of all possible loops having the same Burgers vector and enclosing a fixed area, A.' The energy of such a loop is related to the net resolved shear stress* required to expand the loop and to the stress required to activate a Frank-Read source.223 In the following sectiorls the problem of determining the form of the GWF is discussed and an approximate method for calculating its elastic self-energy is presented. It is demonstrated that the approximations employed lead to no serious errors when applied to a calculation of the elastic energy of a circular glide loop. This method is then used to obtain a closed form expression for the energy of GWFs in isotropic and anisotropic materials. THEORY Burton, Frank, and cabrera4 have proved that the relationship of the equilibrium shape of a two-dimensional array of atoms under the influence of the Gibbs free energy associated with unit length of its boundary, G(O), is that the polar plot of G(0) vs 0 is proportional to the pedal of the GWF.* The angle 0 is measured "The pedal of the polar graph ofG(0) vs0 is the envelope of tangents to the eraph.relative to some crystallographic reference direction. The difficulty in applying this result to a closed dislocation loop arises from the self-interaction of the loop. For a dislocation the energy analogous to G(0) is a function of the total configurati~n.~ Consequently the relation which determines the GWF is an integro-differential equation rather than the simple differen- tial equation which results when G(8) is a function of 0 alone. Mitchell and smialek3 and Brown~ have used the self-stress concept introduced by ~rown' to calculate the shapes of dislocations in equilibrium with an applied stress. In this approach the glide force on an element of the dislocation loop due to the interaction of the element with the rest of the loop is equated to the glide force exerted by the local applied stress. The shape of the loop is then adjusted so that the two forces above are equal at all points on the loop. It is possible to calculate the energies of such loops by noting that, for equilibrium with an applied stress, the energy is equal to pijbiAj (summation convention) where bi is the Burgers vector, p.. is the local net stress tensor, and Ai is a vector directed perpendicular to the plane of thd loop with magnitude equal to the area of the loop. Also Brown' has calculated the energy of a hypothetical polygonal GWF using the above technique and anisotropic elasticity. However, his indicated solution for the energy in the general case of an arbitrary GWF is only slightly less involved than an iterative solution of the integrodifferential equation referred to earlier. In the present work the approximation employed by DeWit and Koehler' is used to calculate the energy of a closed loop in equilibrium with an applied stress. That is, the energy of a loop segment, ds, is approximated by the product of ds and the energy per unit length of an infinite, straight dislocation in a cylinder coaxial with the tangent to the loop at the angular position of the segment. This is known as the "line tension" approximation. The inner cutoff radius of the elastic solution defines the core radius, while the outer cutoff radius is determined by some characteristic dimension of the loop. Actually, both of these radii vary with the edge-screw character of the segment. The effective core radius changes because of the orientation dependence of the Peierls width of a dislocation,8 and the outer radius should be the radial distance from the circumference of the loop to the center of symmetry of the area enclosed by the loop.g However, since the energy varies logarithmically with the ratio of these radii while depending directly on the effective elastic constants, only the effect of the latter is considered. This approximation also neglects the self-interaction of the loop segments. For small loops this will doubtless be extremely important, but for large glide loops produced by plastic deformation the self-interaction is not nearly so important in determining the energy of the loop. This point is illustrated by the following calculation of the energy of a circular loop. Consider a circular loop of radius R which lies in the XI - x, plane of an infinite isotropic continuum and whose Burgers vector makes an angle $ with xs. The first-order solution for the elastic self-energy is:'

Jan 1, 1970

By G. Sachs

X-RAY analysis and single-crystal study have been utilized in recent years as a new means of following constitutional changes in alloys. If such transformations can be suppressed by rapid cooling, they can be followed at room temperature in a particularly convenient manner. In the following we shall consider changes in solubility and polymorphic transformations with particular reference to phenomena of the age-hardening type. Finally a thermodynamic viewpoint is developed for examining such transformations.

Jan 1, 1931

By Robert Maes, Robert de Strycker

The Fe-Ni-As phase diagram has been established by the study of about a hundred alloys, by microscopic observation, and by thermal analysis, with arsenic contents up to 50 pct. The iron and nickel arsenides present extensive solid-solution fields, owing to the substitution of nickel by iron and vice versa; the extent of the solubility field of each compound has been determined with an accuracy of ±1 pct. In the investigated range of compositions, the solidification reactions were established, and the temperatures of the invariant reaclions detevmined with a preciston of iZ°C in the most favorable and ±5°C in the least favorable cases. The isothermal lines of the liquidus surface have also been drazum, with an accuracy estimated at i5°C. Reactions in the solid state, which take place for the formation or the decomposition of certain phases , were investigated in detail. ThE constitution diagram of the Fe-Ni-As system is fundamental for the understanding of the properties of nickel speiss; these by-products of the extraction of certain nonferrous metals indeed often contain the three elements iron, nickel, and arsenic as main constituents. The Fe-Ni-As system has already been the object of earlier investigations. In 1932, Guertler and Savels-berg' have presented some elements of the ternary phase diagram, for arsenic contents up to 55 pct (all percentages in this paper are given in weight percent), including the vertical section FezAs-Ni&s2. This investigation is, however, incomplete and certain anomalies suggested the necessity to verify the results published by these authors: the section Fe2As-Ni5AsZ, for example, is presented as quasi-binary, with a field of complete miscibility in the solid state, even though these compounds do not have the same structure. Recently, ~useck' established an isothermal section at 800°C in the Fe-Ni-As system by X-ray diffraction and microscopic examination of water-quenched alloys. These techniques are sometimes inaccurate for the determination of the fields where alloys are liquid at the investigated temperature, and they may lead to erroneous conclusions when a compound exists at the investigated temperature but is not stable at room temperature and cannot be maintained by quenching. LIMITING BINARY PHASE DIAGRAMS The Fe-As constitution diagram has been the object of several investigations which have been reviewed by Hansen and Anderko.3 For the Ni-As phase diagram, a recent study has been effected by Yund.4 In this system, Heyding and calvert5 have determined the existence of a compound of unidentified structure at arsenic contents slightly higher than those corresponding to Ni5As2 and at temperatures lower than about 200°C; by analogy with iron and cobalt arsenides, this compound could correspond to the formula Ni2As, as suggested by Kulle-rud; although this is not definitely established. In the region of arsenic contents from 35 to 55 pct, Fried-rich7 detected anomalies in the solidification reactions; an interpretation of these anomalies was given by Hansen ,8 which assumed that the solidification reactions in practice are not in equilibrium, but are meta-stable. The main features of the Fe-Ni constitution diagram are the existence of a complete miscibility field, at least at high temperatures, for the fcc phase (which will be designated by My in the remainder of this work) and of a limited solubility field for the bcc phase (designated by Ma). EXPERIMENTAL METHODS The fundamental technique used in this investigation was microscopic observation, which allowed the determination of the reactions occurring during solidification of the alloys, and possible reactions in the solid state.

Jan 1, 1968

By R. A. Davidson, L. Silverman

RESIDENTS of many urban centers are becoming increasingly aware of the obscuring effect of fume and smoke discharge from power, metallurgical, chemical, and other industries; and they, as well as the legislatures of these affected cities, are agitating for cleaner air. Management's most pressing problem is to find an economical way to reduce process effluents in response to the growing pressure from population and legislative demands. The removal must be done, if possible, without handicap to the current operation, since the costs of relocating are often excessive or prohibitive. In fume recovery or disposal, an important item to consider is whether or not the material being discharged has any value. If it has commercial value, the cost of its recovery may offset or aid amortization. For this reason, in making a study of the specific problem in hand, a major factor was the nature of the material emanating from the stack: in particular, its particle size, size range, and its chemical and physical composition, as well as its potential value and utility when recovered (in either a wet or dry state). Should the product have no commercial value, it must be disposed of at minimum cost in a way to prevent recontamination. Initial studies were therefore made to determine stack concentrations and volumes of material evolved from the operations. The next phase of the study concerned the physical and chemical nature of the collected fume. The third portion of this paper describes the wet and dry collector studies undertaken to recover the fume. Cleaning Requirements for Ferroalloy Furnace Operation The basic need for any effluent collection equipment is the highest possible efficiency and the lowest tolerable resistance when the power consumption involved is considered. Since the electric furnace effluent is largely composed of fume of small size (less than 0.5u), it has high light obscuring properties, and even low concentrations will cause some loss of visibility and be evident to nearby residents. The permissible limit for fly ash emission in many cities is based on a weight value (viz, approximately 0.4 grains per cu ft), but the smoke density values are dependent upon a shade of color. In the case of the Los Angeles County code, emission is restricted to pounds per pound of material processed per hour basis (but not exceeding 40 lb per hr for any one given plant operation). If an average particle size of the fume from ferro-silicon alloy electric furnaces is assumed to be 0.4u (as shown later, this is the approximate mean size) and an average loading of 1 grain per cu ft (stp), each cubic foot of stack gas will contain approximately 75x10 10 particles (based on assumed, and confirmed, spherical shape and a standard deviation of unity). When it is realized that the air in metropolitan areas, which are also general industrial areas, contains approximately 5x108 particles, the tremendous light scattering effect of this concentration becomes apparent. Consequently, nearly 100 pct collection would be necessary to equal the average concentration. Fortunately, however, discharge from a high point above ground (50 to 100 ft) will result in at least a thousandfold dilution, or the stack concentration reaching the ground in the foregoing case might result in a ground concentration of ' particles. If the concentration at the source could be reduced by a factor of 100 (99 pct efficiency of collection), then a concentration of 75x10" particles would be diluted to 7.5x10' which would be very satisfactory. An efficiency of 90 pct (factor of 10 decontamination) at the source would result in a discharge of 75x109 articles which upon dilution yields 75x10 which is still 15 times the general air value. Another approach to this consideration is to use the value of concentration of 0.005 grains per cu ft for the value of a visible effluent as cited by Kayse.1 To attain this value with an average loading of 1 grain per cu ft would require an efficiency of 99.5 pct. Since the foregoing value is not based on any reported size of fume particles, it is felt that the numbers' approach given previously is more reliable. These calculations serve to indicate the desirability of thorough cleaning, preferably at the source, and with efficiencies well above 90 pct, preferably above 95 pct (dilution 1:20). One of the most important items in any control program is to reduce the concentrations as close to their sources as possible. The use of better furnace design, deeper coverage over the electrodes, and the prevention of blows or breaks in the surface all help to reduce dissemination; consequently, all of these improvements should be made, if possible, to cut down the effluent load. In addition, in order to minimize the volume of contaminated air that has to be cleaned, the furnace should be enclosed as much as possible. Test Arrangements Before fundamental studies with collectors were made, a furnace stack selected for the test program was sampled to determine the gas temperatures and

Jan 1, 1956

By Norman Carmichael

This paper describes the evolution of transportation at an important mining property, beginning at a time when the railhead was 400 mi. distant, and tracing the steps leading to the development of what is probably the heaviest ore train ever operated in underground mine service over narrow-gage tracks, a 300-ton ore train on a 20-in. track, at working costs closely approximating those obtained on systems involving much greater capital expenditure. Useful where geological and financial considerations render inadvisable the excavation and maintenance of large tunnels and heavier rolling stock. THE problem of transportation in the Clifton-Morenci district of Arizona has been one of peculiar difficulty and consequently has been an important factor in the cost of mining and treating the ores produced. From the crude beginning made over 50 years ago, many changes have been necessary to keep pace with the increased output of copper. A heavy-duty haulage system has developed on the original 20-in. track gage to meet the existent metal-mine conditions.

Jan 3, 1924

By J. A. Berger, G. W. Wiener

Several transition metal nitrides have been prepared and their saturation magnetization determined. On the basis of an atomic model of ferromagnetism involving a consideration of nearest neighbor interactions and the assumption that all atomic moments of the metal point in the same direction, it appears that the nitrogen interacts with d-shell of the transition metal in such a way as to reduce the magnetic moment. THERE is a large class of materials having metallic properties which are formed by a combination of hydrogen, boron, carbon, oxygen, or nitrogen with the transition metals. Several attempts have been made to establish the type of metal-nonmetal bonding in these interstitial alloys because it is believed that many of the physical properties of these materials are determined by the characteristics of this bond. Several of these alloys are ferromagnetic, and thus a powerful method is available for investigating the structures in a direct manner by measuring the saturation magnetization. The latter is a fundamental property of ferromagnetic metals and alloys which depends primarily on the electron distribution surrounding the atom. For the first row of transition metals, this refers specifically to the 3 d-shell. Since bonding involves the electronic configuration between atoms, there is reason to suppose that a relationship exists between ferromagnetism and bond type. In the case of the interstitial structures studied in this work, bonding will refer to the distribution of electrons between the transition metal and the nonmetal. Since these alloys have metallic properties, it is further proposed that any bonding interactions will involve the outer p-shell of the interstitial element and the incomplete d-shell of the transition metal. If this is the case, then the relationship between ferromagnetism and metal-non-metal bonding is established qualitatively. In order to investigate the subject quantitatively, certain transition metal nitrides were chosen because they have simple crystal structures, are ordered alloys, and are ferromagnetic. They also have sufficiently high saturation magnetization to be of technical interest. Currently there are two major theories of ferromagnetism, each of which has been applied to the interpretation of the saturation magnetization in terms of atomic structure. They are usually referred to as the band theory and the atomic theory. The former has found widespread application to the study of pure metals and certain solid-solution allays. However, it has not been applied to the interstitial structures or ordered alloys because it does not interpret the properties directly in terms of the crystal structure. The atomic theory on the other hand is especially suited to the study of interstitial structures because it permits an interpretation of ferromagnetic phenomena in terms of the crystal geometry. As has been pointed out previously, the nitrides have simple ordered crystal structures and, therefore, the choice of the atomic theory for the interpretation of the data is a natural one. One of the prime difficulties with the atomistic theory is that its mathematical justification is much more difficult, and for this reason its general acceptance will depend to a large extent on the value it has in explaining and predicting the results of experiment. Before the presentation of the theoretical basis for understanding the metal-nonmetal bond, it is useful to review the ideas existing prior to this work. Four different interpretations have been given to the metal-nonmetal bond. These are summarized as follows: 1—acceptance of electrons by the nonmetal from the incomplete d-shell of the transition metal, 2—transfer of electrons from the nonmetal to the incomplete shell of the transition metal, 3—no exchange of electrons between the two atoms, and 4— a resonating type of bond involving the p electrons of the interstitial atom giving rise to half bonds. Zener'-4 in a recent series of papers has proposed a new theory of ferromagnetism and has developed an explanation of the observed saturation magnetization of iron nitride (Fe,N) using the concept that nitrogen accepts electrons from the 3d-shell of iron. Jack," on the basis of atom size considerations in iron carbonitrides, has proposed that nitrogen transfers or donates electrons to the inner 3d-shell. He found that the effective size of the carbon atom was less than that of nitrogen and thus suggested that the interstitial atoms give up electrons. Kiessling" has studied the borides of several transition metal atoms and proposed that boron loses one p electron to the transition metal. He postulated that the additional electron added to the metal lattice compensates for the loss in metallic properties which results from the increased metal-metal atom separation. GuillaudT3" has proposed similar arguments from some recent magnetic studies he had made on manganese nitride. However, he did not base his conclusions on a quantitative argument. Pauling," in a recent paper, discussed electron transfer in in-termetallic compounds. He classified nitrogen as a hyperelectronic atom which can increase its valence by giving up electrons. He classified the transition metals as buffer atoms which are capable of either accepting or giving UP an electron. He pointed out that two factors are operating which promote electron transfer because they lead to increased stability. The first is an increase in the number of bonds, and the second is a decrease in the electric charges on the atoms. These ideas when applied to the interstitial nitrides would indicate a viewpoint favoring electron transfer by nitrogen to the transition metal. Hagg7s arguments in favor of no exchange are adequately summarized by Wells." Implicitly, Hagg

Jan 1, 1956

By Carl Pierce

The writer of this article has not attempted to write a technical paper; on the contrary, he has tried to express in "steel-plant English," for steel men, a viewpoint drawn from his practice and experience. It is not his thought that it shall be taken as the "last word" in the making of this class of steel, or that good rimming steel cannot be made by any other practice. The paper was written to serve as the basis of a discussion from which it is hoped much benefit may be derived. The paper deals only with rimming steel made by the open-hearth process, and with the lower carbon steels, such as sheet and tin bar, rivet stock, skelp, etc., although good rimming steel as high as 40 to 50 carbon can be made by having good open slags and giving proper attention to working and tapping temperatures. Definition of Rimmed Steel Rimmed steel is sometimes called open or effervescing steel to differentiate it from killed or partly killed steel. It is steel made by a process which permits the free escape of gases from the metal in the molds. In passing up through the metal, the gases keep it in a rolling action from the walls of the mold inward. The top of the ingot rims in as the metal chills and the walls of the ingot get thicker, the center part remaining fluid until it reaches a pasty condition when it is covered with a cast-iron cap. The Charge In making up a charge for rimming steel, clean stock of a known composition must be selected, special attention being given to the analysis of the materials. The silicon in good rimming steel must be eliminated to a trace, therefore it is advisable to have a uniform amount going into the charge. Too much silicon gives a raw melting heat from which rimming steel is unlikely to result. For this reason a charge containing not to exceed 40 per cent. pig iron and 60 per cent. scrap, with no iron ore, is preferred to the Monell type of charge in which as high as 65 to 70 per cent. pig iron is used with a proportional amount of iron ore for the removal of the excess silicon and carbon. The silicon content of pig iron varies so much from day to day in the average blast-furnace practice that there is danger of getting too much of this element in the latter mixture when

Jan 1, 1926

By E. W. Engle

For several years the Fansteel Products Co. has been engaged in e production and development of various of the rarer metals. It is at present engaged in the commercial production of tantalum, tungsten, and molybdenum in a very high state of purity. The information contained in this paper is partly a general compilation from various sources and partly information obtained as a result of recent years of work in the laboratory of this company. Tantalum, tungsten, and molybdenum form a group peculiar to themselves among the commercially available metals. Their very high melting points (tantalum 2770' C., tungsten 3350' C., and molybdenum 2550" C.) set them apart so far as the metallurgical processes for their production are concerned. Further, when properly prepared and treated they will stand a somewhat unusual degree of cold work, that is work below the temperature at which marked crystal growth takes place. Such cold-worked metal may show a high tensile strength; tantalum to 130,000 lb. per sq. in., tungsten to 490,000 lb., and molybdenum to 260,000 lb., in the form of fine wire. In physical appearance, these metals are not unlike some steels; they may be better described by saying that polished tantalum somewhat resembles lead; polished tungsten, iron; and polished molybdenum, nickel. The polished surfaces of all three remain untarnished in ordinary air. Air containing corrosion-producing impurities will, in general, show molybdenum the least resistant to corrosion and tantalum the most resistant. Molybdenum has, however, a high degree of resistance to corrosion by hydrochloric acid, a property that should render it of commercial interest. On the other hand, it is markedly attacked by some of the weaker organic acids. The three metals oxidize rapidly when heated at or above a dull red in air. This feature limits their use in many applications where their high melting point and strength make them appear usable. Tungsten and molybdenum, at red heat, are quite inert to hydrogen and nitrogen; while tantalum has a rather remarkable affinity for all the ordinary gases, which results in its becoming embrittled in their presence. This

Jan 1, 1925

By P. F. Gnirk, J. B. Cheatham

The results of combined analytical and experimental studies involving simulated multiple bit-tooth penetration into mck are incorporated into a drilling rate equation for roller-cone bits assuming rather idealized downhole conditions. In particular, it is assumed that the rock behaves statically in a ductile fashion during bit-tooth penetration and that the rock chips are instantaneously removed from the bottom of the drill hole. The general analysis demonstrates an application of plasticity theory for the rock/bit-tooth interaction to the formulation of an upper limit on rotary drilling rate. INTRODUCTION Extensive experimentation involving single and indexed bit-tooth penetration into rock in a confining pressure environment has demonstrated that the chip formation process is of a ductile, or pseudoplastic, nature at sufficiently low differential pressures so as to be of interest in rotary drilling. Coincident with the experimentation, analytical consideration has been given to the theoretical problems of single and indexed bit-tooth penetration into rock. In general, the analyses have assumed that the rock behaves statically in a rigid-plastic fashion and obeys the Mohr-Coulomb yield criterion. The quantitative comparison between experimental and calculated values of bit-tooth load required for chip formation has been remarkably good for a variety of rocks commonly encountered in drilling and at simulated differential pressures as low as 500 to 1,000 psi. Results obtained recently for indexed bit-tooth penetration indicate that the work (or energy) required to produce a unit volume of rock chip can be minimized by a proper combination of bit-tooth spacing and bit-tooth load for a given rock type and differential pressure. By utilizing this information, it is possible to formulate a drilling rate equation, at least in a preliminary fashion, for a roller-cone bit performing under rather idealized downhole conditions. In particular, through the use of characteristic dimensionless quantities pertinent to a roller-cone bit and to indexed bit-tooth penetration, interrelationships among bit weight, rotary speed, rotary power, bit diameter, rock strength and bit-tooth shape and spacing can be explicitly expressed. In the formulation of the equations, however, it is assumed that the rock chips are instantaneously removed from the bottom of the drill hole and- that the rock behaves in a ductile manner during bit-tooth penetration. In addition, the effects of bit-tooth load application and penetration by a yawed tooth at an oblique angle are neglected. Although the analysis is presented in the light of some rather restrictive conditions, it does demonstrate a method of applying fundamental rock/bit-tooth interaction data, obtained by combining the results of analysis and experiment to the formulation of a drilling rate equation for rotary drilling. JNDEXED BIT-TOOTH/ROCK INTERACTION PREVIOUS RESULTS The mechanics of bit-tooth/rock interaction under simulated conditions of borehole environment have been extensively described in a number of papers.l-ll In particular, the effects of differential pressure, mechanical properties of rock, pore fluid, bit-tooth shape and spacing, rate of bit-tooth load application and dynamic filtration below the bit-tooth have been investigated experimentally. From a sequence of experiments.1-4 it was demonstrated that, for dry rock at atmospheric pore pressure, the mode of chip formation exhibits a transition, with increasing confining pressure, from predominantly brittle to predominantly ductile. This transition

Jan 1, 1970

By Attilio Ligasacchi

The production of magnetite in copper smelting has been the subject of wide investigation in the past.1-9 It is accepted that most of the magnetite is produced in the converters and returned to the re-verberatory furnace with the converter slag. Part of this magnetite is circulated back to the converters in the matte. As a result, if proper fluxing practice is not followed, and temperatures in the converting process are not strictly controlled, an undesirable circulating load of magnetite may occur. This might ultimately lead to saturation in the reverberatory bath with consequent settling of the magnetite at the furnace bottom. This paper contains the cumulative results of a series of investigations on the formation and control of magnetite presently being conducted by the metallurgical department of the Chino Mines Division of Kennecott Copper Corp. THE METHOD USED FOR THE DETERMINATION OF MAGNETITE AND OTHER MAGNETIC MATERIALS Conventional wet chemical magnetite analyses are neither reproducible nor theoretically sound. These analyses are sensitive to time, temperature, and heating rate-all factors which tend to decrease their accuracy and reproducibility. To overcome the unreliability of the above method, H. W. Mossman1 developed an inductance bridge magnetite "meter" which completely replaces the wet chemical analysis with the advantage of quicker and reproducible results. Fig. 1 is a schematic diagram of the meter in use in the Chino metallurgical laboratory. When a pulverized specimen with magnetic properties is placed in coil A of the inductance bridge circuit, the permeability of the core is increased, causing a voltage drop across the coil. The unbalance is amplified to operate the balancing motor which adjusts the movable iron core in coils C and D to bring the bridge back to balance. An indicator arm connected to the movable iron core indicates directly the percent, or weight, of the magnetic material in the specimen. Coil B acts as a reference coil and a zero adjustment. The meter is standardized with a set of various amounts of -100 mesh pure magnetite crystals (99.8 pet Fe3O4) thoroughly mixed in a test tube with -100 mesh quartz sand. These mixtures are combined with inert transoptic powder and heated to 140° to 160°C (melting point of the powder) and subsequently cooled to room temperature, solidifying the whole mixture, in this manner eliminating any possible preferential orientation of the magnetite grains. In order to determine the effect of the particle size" of the magnetite and other magnetic materials on the meter determinations, five size fractions were obtained by wet screening of the 99.8 pet pure magnetite and several reverberatory matte and slag samples. The following size fractions were investigated: -80 + 100; -100 + 150; -150 + 180; -200 + 250; -250 + 300 and -100 mesh. The deviation of the meter readings for the various sizes of each sample never exceeded ±0.3 pet. This deviation is considered well within the accuracy needed for common smelter operation procedures. Further investigation proved also that grinding slag and matte samples in our laboratory disc grinder normally produced a powder constituted of 95 pet -200 + 300 mesh. For practical purposes a - 100 mesh size was used as standard for our studies. It was also found that for rapid determinations tamping of the sample in the test tube was sufficient and gave comparable results with those samples solidified with transoptic powder. For the purpose of this study we define the magnetite content in copper smelter slags and matte as the equilibrium amount of crystalline Fe3O4 existent in the specimen at a given reference temperature, excluding any secondary magnetite precipitated in the specimen during nonequilibrium conditions. MAGNETITE DETERMINATION IN SLAGS Since it is impossible to ascertain the status of equilibrium of a conventional slag sample, due to

Jan 1, 1965

By L. L. Swift

AT the present time there are four base metals being used for automotive bearing alloys. Of course there are numerous variations in the amounts of alloying elements added to each base metal and nearly all of these alloys have the conventional, if not classical, duplex structure; that is, they are composed of a hard constituent embedded in a soft matrix. The well-known theory is that the former will wear well, while the latter will be plastic enough to allow the bearing to be broken in and conform to the contours of the shaft. The requirements of the modern bearing have been most aptly described by W. M. Corse: In order to meet the engineering demands of today a good bearing metal must be able to carry the weight of the shaft and stand up under steady or suddenly applied loads, or even blows in some types of service. A certain amount of plasticity is desired to compensate for minute irregularities in the shaft or bearing surface, and to permit yielding, thereby avoiding dangerous stresses in bearing and shaft and preventing overheating and rapid wear of parts. Less plasticity is required in a bearing metal if the surfaces of bearings and journals are machined accurately, aligned, and kept in alignment. It is desirable, of course, that a bearing metal have a low coefficient of friction. Under most operating conditions the friction depends on the unit pressure of the bearing, the speed, the temperature, and the properties of the lubricant. A good bearing metal must have a low rate of wear to reduce the necessity for frequent replacements, and adjustment of the bearings. It must wear more rapidly, however, than the journal or shaft running on it, because replacement of the journal or shaft is more difficult and costly than replacement of the hearing., The hardness of, the bearing alloy is a property closely related to several of the foregoing. With a duplex microstructure, the measurement of hardness with any of the usual commercial devices means little. The Bierbaum method of measuring the hardness of the individual constituents was developed to, fill this need. MICROCHARACTER The Bierbaum microcharacter2.3 measures the scratch-hardness of a solid by pulling a weighted diamond point over the surface. The diamond point is ground. so that it is the corner of a cube, and mounted

Jan 1, 1938

By D. H. Yardley

GEOCHEMICAL investigation of trace elements in surface materials was begun near Ely, Minn., in 1953 along the basal contact of Duluth gabbro with Giants Range granite (Fig. 1). This article presents data on the distribution of copper and nickel in till and in stream sediments in the area and proposes an explanation for the types of distribution found. The Duluth gabbro, one of the world's largest basic intrusives, intrudes rocks which range in age from Keewatin to middle Keweenawan. Within the test area the gabbro is in contact with granite except for short sections where it is in contact with remnants of iron formation. Sulfide mineralization occurs within the gabbro, near and parallel to the basal contact for a distance of several miles. Schwartz and Davidson' have described the geologic setting of the mineralization. The sulfides, believed to be syngenetic, include chalcopyrite, cubanite, pentlandite, pyrrhotite, and minor amounts of bornite. They occur disseminated in the silicates and as small interstitial masses. The ratio of copper to nickel is about 3.8:1, based on 66 chemical analyses of rock samples from various outcrops (Ref. 1, p. 702, and Ref. 2). Test Procedures: With specified exceptions, all nickel and copper tests were made by the chromo-graph method,:' which measures the intensity of a colored spot formed by a reaction between the metal being determined and special reagent paper. The intensity is then compared to the intensity of spots prepared from samples of known metal content. Details of the test procedure are outlined in another article (Ref. 4, pp. 77,78). All soil samples tested in this investigation to date have been weighed on an analytical balance. However, a volumetric scoop designed to provide about 0.1 g of soil adds to the speed and ease of testing and has been found to give satisfactory results (Ref. 5, p. 531, and Ref. 19). The size of the samples used for the tests was 0.1 g. Whenever such small samples are used there is some question as to whether they are representative of the several grams in the field sample. Many repeat tests of the samples used in this investigation demonstrated that results can be reproduced within the limits of accuracy of the method without formal mixing beyond that inherent in screening the soil fractions. Furthermore, the 0.1 g is probably as representative of the field sample as the field sample is of its area of influence. Hawkes and Lakin (Ref. 6, p. 291), who considered the general problem, compared ground and quartered bulk samples of 500 g with 5-g grab samples. They concluded that "there is no significant loss in accuracy of data by substituting grab samples for bulk samples." The term soil implies somewhat different things to the geologist, engineer, and soil scientist.' For convenience the term as used in this article refers to unconsolidated material (the mantle) overlying bed rock. Sampling Procedure: Samples were taken at 100-ft intervals along north-south traverse lines across the gabbro-granite contact. The soil (till) samples were taken at an average depth of 1 ft, which was below the high-humus surface layer and into clean till. Samples taken at 1-ft intervals down to ledge showed as high a metal content at 1 ft below the air-surface as at greater depths and in two instances were slightly higher. The till at 1-ft depth did not appear to differ from material at greater depths. Total depth to bedrock has been tested at only a few points and where measured varied from 1 to 10 ft. Aerial Distribution Contours and Profiles: Plotting of copper, nickel, and cobalt content in contour form (Fig. 2) shows that anomalous amounts of these metal ions occur in till over and closely adjacent to mineralized areas of the gabbro. Contouring nickel content alone, or the copper content, outlines the same target area. Contours of the copper content provide a more distinct anomaly than nickel because of the higher copper concentration. The traverses are rather widely spread for interpolation; however, drilling has confirmed the target area essentially as shown.

Jan 1, 1959

By L. A. Schrider, J. A. Wasson

A method of predicting waterflood performance has been developed that combines certain facets of several previously published prediction techniques. The manner of combination has required the development and use of some new and some little-known relationships and has eliminated several of the weaker assumptions inherent in the original individual prediction methods. This approach, which was designed for computer solution, has removed the necessity of referring to plotted curves and permits the analytical prediction of water flood performance for a five-spot well pattern in either homogeneous or stratified reservoirs. The Predicted values are expressed in common oilfield units rather than in abstract or dimensionless terms. The calculation procedure has been programmed in FORTRAN IV and the entire program listing is available to potential users.* Introduction Prior to initiation of secondary recovery of oil by waterflooding, the possibilities of economic success or failure must be evaluated with the greatest practical accuracy. Although many prediction techniques are available, most, if not all, have serious limitations. In recent years, the Bureau of Mines has attempted to stimulate interest in the secondary recovery of oil from Appalachian pressure-depleted reservoirs. Waterflooding, because of its widespread acceptance and success, is the principal secondary-recovery method considered. During the life of the project, several performance prediction methods have been studied and applied. Because these methods, individually, have inherent assumptions and limi-tations, portions of some of them have been selected and combined in an effort to eliminate such shortcomings wherever possible. We believe that the resulting technique is as accurate as the necessary available data will permit and that it has several distinct advantages over previously published methods. Development of the Method The fractional flow equation developed by Buckley and Leverett' from Darcy's law is the fundamental mathematical statement describing immiscible fluid-fluid displacement in porous media. A generalized form of this relationship, whose derivation is readily available in the literature, is The formation dip, a, is usually very small in those petroleum reservoirs being considered for pattern waterflooding in the Appalachian area. Therefore. in many cases. a has an almist negligible value. In addition, Ap, the difference between the density of water and the density of oil, is relatively small. For these reasons the gravitational term may often be neglected. Capillary pressure is a function of saturation, which is in turn a function of distance from the upstream boundary of the system or the injection well. In this study it is assumed that the frontal zone of the waterflooding (or zone of capillarity) has negligible length and that only those saturations in the water-swept zone at breakthrough and later are of interest. As the distance in a waterflood pattern is comparatively large and the change in water saturation with distance is usually small, the change in capillary pressure with distance is negligible. The simplified form of the fractional flow equation is appropriate, therefore, in this application. Three variables must be considered in determining that fraction of the total fluid flow that consists of water: the viscosity ratio, saturation, and relative permeability ratio.

Jan 1, 1969

By L. T. Larson, M. L. Picklesimer

The relationship between the apparent angle of rotation of monochromatic plane polarized light and the tilt of the basal pole from the surface normal has been experimentally determined for zirconium over the wavelength range of 500 to 655 mp. This relationship allows the determination of the spatial orientation of the basal pole of an individual grain in a polycvystal-ling zivrconium specimen to within ±3 deg by three simple tneasurements with a polarized-light metallurgical microscope. The method of measurement is discussed in detail. THE optical anisotropy of materials having noncubic crystal structures has long been used to reveal features by polarized-light microscopy. Petrographers have used measurements of certain optical properties to identify and classify transparent or translucent minerals. More recent work (i.e., Cameron1) has extended such measurements to opaque minerals in reflected light. Few attempts have been made to make similar measurements on noncubic metals. Couling and pearsall2 have reported that a sensitive tint plate can be used in a polarized-light metallurgical microscope to determine the position of the basal-plane trace in a grain of polycrystalline magnesium. Reed-Hill3 has reported that the same technique can be used for zirconium. We have found that the precision of measurement can be increased to about ±0.5 deg by using a Nakamura plate4,5 to determine the exact extinction position after the sensitive tint plate has been used to locate approximately the basal-plane trace. This report describes a method for measurement of another optical property, the apparent angle of rotation. This measurement permits determination of the angle between the basal pole of a grain of a hcp metal and the normal to the surface of the specimen. When the two measurements are combined, the orientation of the basal pole in space can be determined from three simple measurements on a single surface. One to two hundred such determinations will permit plotting of a basal-pole figure for the polycrystalline material with reasonable accuracy. When normally incident, monochromatic, plane-polarized light is reflected from the surface of an optically anisotropic material, the light may be converted to elliptically polarized light, the plane of vibration may be rotated, or both may occur. The el- lipticity, the angle of rotation, and the reflectivity can be related to the indices of refraction and the absorption coefficients of the material.6,7 Ellipticity values can be determined with an elliptical compensator, but not with the ease and precision desirable for the present purposes. Measurement of the angle of rotation requires only the determination of the angle from the crossed position (90 deg to the polarizer) that the analyzer must be rotated to obtain extinction when the trace of the optical axis in the surface is at 45 deg to the vibration direction of the polarizer. The angle of rotation of the analyzer is approximately 6/5 that of the true angle of rotation of the light as reflected from the specimen because there is a small amount of additional rotation produced during the passage of the reflected light through the mirror of the microscope. Since we are presently interested only in determining the tilt of the basal pole, the angle of rotation of the analyzer (the apparent angle of rotation of the light, i.e., uncorrected) can be used. Precision of the measurement can be increased substantially by the use of a Nakamura plate4,5 in determining the extinction position. In an optically uniaxial material (hcp or tetragonal crystal structure) the angle of rotation depends only on the optical properties of the material and the orientation of the optical axis of the grain relative to the plane of incidence of the plane-polarized light.7,8 Thus, in a metal such as zirconium, the apparent angle of rotation at the 45-deg position in any given wavelength of light is a direct measure of the tilt of the basal pole from the normal to the surface. If the optical properties vary with wavelength, the apparent angle of rotation for any given tilt of the basal pole will vary. None of the required information exists in the literature for zirconium nor for any other non-cubic metal. MEASUREMENTS ON SINGLE-CRYSTAL ZIRCONIUM A single-crystal sphere of zirconium 9/16 in. in diam was spark-cut from a single-crystal rod grown from iodide bar by an electron-beam zone-melting process.9 The damaged surface was removed by chemical polishing in a 45/45/10 mixture (by vol) of water, concentrated HNO3, and HF (48 pct) and then electropolishing at 50 v in a bath1' of methyl alcohol and perchloric acid (95/5 by vol) at -70-C. The single-crystal sphere was mounted in a five-axis goniometer stage having a removable eucentric X-ray diffraction goniometer head for the two inner orientation axes. The basal pole of the single-crysta sphere was aligned parallel to a third axis of the goniometer stage by using the sensitive tint method to determine the basal-plane trace at several rotational positions of the sphere. The alignment was then checked by removing the sphere and eucentric gonio-

Jan 1, 1967

By K. C. Hong, R. B. Jensen

The problem of determining the optimum set of steam volumes and cycle lengths for a single well undergoing multicycle steam stimulation in order to maximize the cumulative discounted net income has been formulated mathematically and programmed for a digital computer. The mathematical fonnulation of the problem and the method for its solution are discussed in this paper. The oil production performance during each stimulation cycle was simulated by either a constant percentage or a harmonic decline. Using simple analytical expressions for production performance, the cumulative discounted net income and cumulative time of operation were related to the pertinent process and cost parameters and two principal process control variables (cycle length and steam injection volume). The discrete maximum principles was used to transform the equations for cumulative time of operation and cumulative discounted net income into a set of simultaneous equations. The simultaneous equations then were solved by trial and error on a digital computer to determine the set of cycle lengths and stem injection volumes that gives maximum cumulative discounted net income over the project life. INTRODUCTION Steam stimulation is a process for improving the oil recovery rate from wells producing high-viscosity crudes. The process is applied on an individual well basis and is executed in a series of cycles, each consisting of three phases: steam injection, soaking (steam condensation), and production. Significant increases in production rate following the stimulation operation result from heating the reservoir around the wellbore. As heat is removed with produced fluids and dissipated into nonproductive formations, the production rate declines, usually to near the prestimulation value. Typical production responses are given in case histories reported by Owens and Suter,l and are depicted in Fig. 1. Duration of the production phase is equal to the time for the oil production rate to decline to some specified value and is called the cycle length. (Cycle length is defined as the producing portion of the cycle and does not include the downtime required for steam injection and soaking operations.) Termination of the production phase coincides with the start of steaming for the next cycle. The process is continued, cycle by cycle, until it becomes unprofitable. Models 2-4 have been developed to simulate behavior of a single well during one cycle of steam stimulation and have been used to investigate the effects of system and operating conditions on the production responses. However, these investigations have not shown how the models can be used to determine a most profitable set of operating conditions for a multicycle stimulation project. Perhaps these models are too complicated mathematically to be adapted readily to an optimization study. This paper presents a method for optimizing a multicycle steam stimulation project based on simple production performance models. First, the performance of a steam-stimulated well during each cycle was simulated by either a constant percentage or a harmonic decline model. Using these simple analytical expressions for production performance, the cumulative discounted net income (before tax) and cumulative time of operation for each cycle were related to the pertinent process and cost parameters and two process control variables—the cycle length and the steam injection volume. Finally, the profit function to be maximized was formed. The analogy between the above problem and problems of optimizing multistage decision processes that have been reported extensively in the chemical engineering literatures5-10 in recent years has led this investigation to the use of the discrete maximum principle.5-7 This principle was used to transform the equations for cumulative discounted net income and cumulative time of operation into a set of simultaneous equations characterizing the optimum operating conditions in terms of the two control variables. These equations

Jan 1, 1970

By Robert E. Green, P. W. Kingman

Application of a constant geometry compression test to single crystals of aluminum of selected diameters from 1/4 to 1/64 in. showed the presence of a diameter-dependmt size effect. The most pronounced effects were found in those crystals oriented for single slip, while for specimens possessing orientations in the comers of the standard stereographic triangle virtually no size effect was exhibited. The yield stress of the crystals oriented for single slip was found to increase with decrease in specimen diameter, while the strain-hardening rate was found to be lower for the smaller specimens. The experimental results are in general agreement with those of other investigators obtained from lensile tests on copper and aluminum crystals. THE earliest systematic investigation of a possible size effect on the plasticity of metals was that of no,' who in 1926 performed tensile tests on cylindrical aluminum single crystals with diameters of 3 to 8 mm. Ono concluded that the gross stress-strain curve did not show a diameter dependence, but that the resistance to slip for strains of 0.1 pet and less appeared higher for 3-mm-diam crystals than for larger sizes. Later studies of aluminum by Maddin et al2 tentatively concluded that a size effect exists, but the conclusions were again open to question because of inconsistencies in the experimental data. Wu and Smoluchowski3 had previously shown that the slip system activated in a single-crystal sheet specimen of aluminum is a function of the specimen cross section in the slip direction, but no stress-strain data were obtained. Subsequently Fleischer and Chalmers4 studied the effect of the length of the slip direction of the primary-slip system on the stress-strain curve by testing aluminum crystals with geometrically dissimilar cross sections. In the course of this investigation a size effect was indicated in rather large crystals; however, the number of these tests was small. Other investigators have indicated that a size effect in aluminum is appreciable only for diameters of 0.5 mm or less.5, 6 Size-effect studies have also been carried out on copper crystals, the most detailed being that of Suzuki et a1.7 who performed tensile tests on specimens of many diameters ranging from 2 to 0.12 mm. Suzuki found a strong size dependence in the easy-glide region, both the extent of the easy glide and the hardening rate in easy glide were size-dependent, and the size effect was found to be orientation-dependent. Suzuki's results are in agreement with the less extensive observations of Pater-sonB and those of Garstone et al.9 A size effect was found by Rebstock using tubular copper crystals.'0 Size effects have also been noted in a brass,6, 11 in cadmium,12'19 and in hexagonal crystals.14 All the previously cited works have been entirely concerned with the variation of specimen cross section. The effects of specimen length and the change of specimen geometry which results from using progressively thinner specimens while maintaining the same specimen length have been largely ignored. A theoretical discussion of the effects of specimen length and geometry has been given by Hauser and Jackson,15 who predict a grip effect on easy glide as a function of specimen geometry provided that the specimen dimensions are large compared with the spacing between the slip bands, and by Fleischer and Chalmers,18 whose analysis of grip effects resulting from lattice rotation predicts an increase in easy glide with an increase in specimen length. A study of size and geometry effects in aluminum crystals by Kitajima and shimba17 indicated increasing amounts of easy glide in specimens of increasing length and identical cross section, and nearly identical stress-strain curves for specimens of different sizes having constant length-to-diameter ratios. Since the present study is primarily concerned with diameter dependence, the following factors were taken into account: specimen material, specimen geometry, testing method, range of sizes to be tested, and possible influence of surface and volume effects. Aluminum was chosen because of the present lack of conclusive results and the seeming possibility of size effects at relatively large diameters, the

Jan 1, 1964