By S. Tanaka

The Tamano Smelter of Hibi Kyodo Smelting Co. Ltd. was commissioned in 1972. Since start up, the anode production capacity has increased from 101,000 tpy to 290,000 tpy, as a result of the application of continuous improvements at each phase of the expansion projects. The Tamano Smelter had developed several innovations, including the original coke combustion technology for Flash Smelting Furnace operations (T-FSF), and has also been able to extend the operating life of the Peirce-Smith converters. This paper will present several improvements implemented at the Tamano Smelter, and will discuss relevant P-S converter operation.

Jan 1, 2005

By Anat Deepatana

Bioleaching of nickel laterite ores is the extraction technology based on the use of heterotrophic micro-organisms and their organic acid products to dissolve metals from oxide minerals. This study examined the chemical leaching kinetics of limonite and nontronite ores with metabolites including citric, lactic and malic acids. The leaching process was found to follow the chemically controlled model. The leaching kinetics was found to be significantly influenced by the acid strength or dissociation of acids in solution. Although increasing the acid strength increased the rates of leaching, this trend was not indefinite. An optimal acid concentration that defined the fastest leaching rates was identified for each acid. The amenabilities of the minerals hosting the nickel and cobalt in limonite and nontronite to organic acid leaching were also established.

Jan 1, 2006

By M. E. Alam

In the present study, 1.1 volume percent of nano size copper was incorporated into pure tin using hybrid microwave sintering assisted powder metallurgy route. Microwave sintered samples were extruded both at room temperature and at 230 °C. Microstructural characterization studies were conducted on the extruded samples to investigate the distribution characteristics of secondary phase and grain morphology. Room temperature tensile test results revealed that hot extruded Sn-Cu samples exhibited higher strengths (~ 41%, in case of 0.2% yield strength and ~ 38%, in case of ultimate tensile strength) and ductility (~ 15%) when compared to room temperature extruded samples. On the contrary, the tensile properties of pure tin remained independent of extrusion temperature. An attempt is made in this study to correlate the effect of extrusion temperature on the microstructural evolution and tensile properties of Sn-Cu solder.

Jan 1, 2009

By Emma Arakelova

An increase in concentration of a Zn-containing volatile complex for synthesis of ZnO films was investigated when processing their target by ultraviolet radiation emitted by mercury lamp. The experiments were carried out using a flow-type quartz reactor. ZnO tableted target was preliminarily irradiated during 2 to 7 hours. H2O2 (98%) vapor at 25Pa passed through the reactor with ZnO target at 373K. As substrate material, five subsequent quartz cylinders were used at 423K. The experiment lasts 4 hours. H2O2 decomposition on ZnO surface was accompanied by formation of a Zn-containing volatile complex which passed in gas phase and decomposed on the substrates with isolation of final ZnO. The concentration of the Zn-containing volatile complex (N) in gas phase increases with UV pre-irradiation time (t) (without irradiation N = 1.05 1011 particles/cm3; after t=2 hours, N = 5.19 1011 particles/cm3, after t=4 hours, N = 9.95 1011 particles/cm3; after t=7 hours, N = 1.86 1012 particles/cm3.

Jan 1, 2006

By F. A. Guo

Ultrafine-grained surface layers were obtained by surface mechanical attrition treatment (SMAT) in copper and titanium samples. The thermal properties of the deformed layers were characterized using a scanning thermal microscopy (SThM) that allows thermal conductivity to be mapped down to the submicrometer scale. A theoretical approach, based on this investigation, was used to calculate the heat flow from the probe tip to the sample and then estimate the thermal conductivities at different scanning positions. Experimental results and theoretical calculation demonstrate that SThM can be used as a powerful tool for the thermal property and microstructural analysis of ultrafine-grained microstructures.

Jan 1, 2006

By David Arana

The use of gas-water dispersion of a molten material flow onto a vibrating surface is developed as a process to minimize water pumping requirements, minimize the risks of explosions, and minimize the post solidification dewatering and fines handling equipment requirements. The process uses existing vibration transport technologies and common plant utilities. Plant trials using the smaller footprint and the progressive molten particle cooling time have yielded encouraging results. The results are analyzed and reported.

Jan 1, 2006

By Tian Sugui

By direct aging treated, creep properties measurement and microstructure observation, the influences of the direct aging treatment on the creep behaviors of Hot Continuous Rolled GH4169 superalloy are investigated. Results show that the creep resistance of Hot Continuous Rolled GH4169 superalloy may be obviously improved by directly aged treatment. Under the applied stress of 700MPa at 660, the creep lifetime of the alloy is enhanced to 126h from 60h. During hot continuous rolling, the deformation features of the alloy are the twinning and the double orientations slipping of the dislocation activated within the twinning regions. After direct aging treated, the alloy displays a smaller grain size, and the finer g² phase is dispersedly precipitated in the matrix of the alloy, which is thought to be a main reason of enhancing creep lifetime of the alloy.

Jan 1, 2010

By Napisporn Memongkol

Syntheses of Al-TiC-Al2O3 and Al-SiC-Al2O3 composites were obtained in situ by carbothermal reduction of mixtures of Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders. The reductions were carried out in a horizontal tube furnace under flow of inert gas. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The synthesized products were mixtures of aluminum reinforce with titanium carbide and alumina and aluminum reinforce with silicon carbide and alumina. The effect of the reaction temperature (1000 o C ? 1200 o C) and condition of precursors on the Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders were investigated using XRD and SEM method. The synthesized products showed those composites with aluminum matrix and titanium carbide and alumina as reinforced phases and aluminum matrix and silicon carbide and alumina as a reinforced phase was formed.

Jan 1, 2006

By Ulises Crossa Archiopoli

We describe a technique that allows rapid imaging of the thermal diffusivity of the sample by a modified photo-thermal technique. The thermal diffusivity in hardened steels strongly correlates to the hardness. Hence in a noncontact manner and with optical microscope resolution, a 2D map exhibiting the crystallographic phases and hardness of the sample can be retrieved. Two almost collinear laser beams scan the surface, one as a modulated pump and a second as a CW probe. The deflection of the probe carries information on the thermal expansion of the sample and with it, on the thermal diffusivity. It is shown that a single determination of the time delay of the modulation of the probe beam can be used to retrieve the thermal diffusivity.

Jan 1, 2010

By P. N. Anyalebechi

Keywords: Aluminum alloy 3004, Solidification rate, Homogenization, Second phase particles The effects of the fineness of as-solidified cast microstructure and temperature on the response of aluminum alloy 3004 to homogenization heat treatment (a.k.a. preheat) have been investigated. The study was conducted at 538oC and 595oC on directionally solidified laboratory-size ingots with a range of solidification rate of 0.10oC/s to 29.4oC/s. Optical and electron microscopy, quantitative image analysis, electrical conductivity, and electron probe microanalysis were used to quantify the effects of the homogenization heat treatment on the microstructure of aluminum alloy 3004. In general, increase in fineness of as-cast microstructure and homogenization temperature enhances the a-transformation reaction, dissolution of Mg2Si, elimination of dendritic microsegregation, and dispersoid formation. The homogenization heat treatment reduces the average size of second phase particles in castings solidified at <1oC/s. However, in castings solidified at above 1oC /s, homogenization causes the coarsening of the second phase particles. Mn in solid solution is independent of homogenization heat treatment temperature.

Jan 1, 2005

By M. A. Barakat

"Adsorption of heavy metal ions specifically, Cu(II), Zn(II), Mn(II), and Cr(VI) from aqueous solution on synthetic 4A Zeolite was evaluated. The 4A zeolite was synthesized previously by dehydroxylation of low grade Kalabsha Kaolin at 800 °C, and reacted hydrothermally with 2-4 M NaOH solution at 100 °C for 2h. The adsorption capacity of the metal ions were found to be strongly dependent on pH and initial metal ion concentration. At the optimium conditions the adsorption capacity decreased in the order Cu(II) > Zn(II) > Mn(II) > Cr(VI) ions. Almost complete adsorption was achieved for both of Cu(II) and Zn(II) ions at pH > 6, while the adsorption capacity for both Mn(II) and Cr(VI) was 96, and 55.3 % at pH 11 and pH 3, respectively. The results also showed that the grain size of the 4A zeolite has a little effect on the adsorption capacity. The experimental data was compared with two adsorption isotherms, Langmuir and Freundlich isotheroms. The results showed a good agreement of the Langmuir plots with the experimental data.1. IntroductionSeveral industrial wastewater streams may contain heavy metals such as Cr, Cu, Pb, Zn, Co, Ni, Mn, etc. including the waste liquids generated by metal finishing or the mineral processing industries. Heavy metals are considered hazardous pollutants due to their toxicity, even at low concentration, and nonbiodegradability. Increasing level of heavy metals in natural water bodies poses a serious threat to all living species including humans. It is, therefore, essential to reduce the heavy metal concentration in effluents/wastewater before it is discharged into the water bodies [1]."

Jan 1, 2008

By Thomas P. Battle

Ilmenite (iron titanate) is the source of over 90% of all the titanium produced in the world today. At some point during production of titanium dioxide or titanium metal the iron impurity must be removed. Too often it becomes a waste instead of a product. DuPont and MINPRO have developed a solid-state process which separates the iron and titanium components of ilmenite into different high-purity powders, which can be separated using conventional mineral processing techniques. The main reactor in this process is a unique high-temperature ball mill, where the iron segregates from the ilmenite lattice with the assistance of catalytic quantities of He\. The results of lab, pilot plant, theoretical, and scale-up studies are presented and discussed.

Jan 1, 1996

By Othon do Rêgo Monteiro Neto

[The present study has investigated the extraction of copper from a chalcopyrite flotation concentrate using an adapted strain of Thiobacillus ferrooxidans and shake flasks, tank leaching and Warburg respirometer techniques. From the shake flask experiments, the activation energy and the frequency factor have been determined to be ?ka = 59.4 kJ and A = 3.3 x 105 S-1, respectively. The temperature coefficient was found to be Q10 = 2.2 in the range of 20 to 35°C. It was suggested that the reaction mechanism of chalcopyrite leaching by T. ferrooxidans involves the formation of an activated complex. whose thermodynamic values have been calculated to be ?G? = 92.1 kJ, ?S? -148.8 J K-1 and ?H$ = 47.8 kJ. The maximum volumetric oxygen mass transfer coefficient for the reactor leaching was found to be achieved by using an optimum air flow rate of 1970 cm min l at a rotational frequency of 1000 min-1. The highest copper extraction in tank (reactor) leaching experiment was 86.8% after 17 days of leaching, while in the sterile runs the corresponding copper extraction was only 40.1%. The copper extraction was suggested to be diffusion controlled. The power requirement of the aerated reactor was calculated to be Pg = 2.02 watts. During leaching, the oxygen saturation concentration was found to be C* = 6.70 mg dm-3. Using the gassing out method the critical oxygen concentration was assessed to be CCrit 0.05 mg dm 3. From the Warburg experiments, the kinetic parameters of the Monad equation were derived with a new evaluation technique to be Vmsp = 9.0 µm3 02 min-1 mg protein-1 and K = 7.4% pulp density for the effect of substrate concentration. The order of reaction and the overall reaction rate constant were determined from the modified van&apos;t Hoff plot to be n = 0.0 and k = 1.49 p dm3 02 min-1 mg Protein -1 for the chalcopyrite concentrate oxidation by T. ferrooxidans. On the basis of this experimental work, a preliminary flow sheet has been proposed for the bioextraction of copper from flotation concentrates.]

Jan 1, 1985

By Godwin Beene

During recent years, copper and acid production from Nkana Smelter has formed a significant proportion of ZCCM&apos;s total output, but a number of problems affecting the smelter over the last decade have only been recently overcome. This paper discusses recent developments in the smelting practice, highlighting some of the operational problems experienced and associated solutions. The smelter performance over the decade is discussed and the innovations in the smelting technology employed to sustain production in the wake of limited re-capitalization are dealt with in detail.

Jan 1, 1999

By Murat Alkan

In this study, a self-propagating high-temperature synthesis (SHS) and following acid leaching techniques were carried out to produce boron carbide (B4C) powder. First, B2O3 was obtained through calcinations of H3BO3 at 1073 K for 2 hours. Then, the glassy B2O3 obtained was crushed and sieved. In the SHS experiments, different amounts of B2O3, Mg and C black were used. The SHS product was obtained in the form of black, spongy solid. In the leaching step, the SHS product was leached in a HCl solution to eliminate the MgO and Mg3B2O6. The effect of acid concentration on the selective leaching was studied at different concentration range, solid/liquid (S/L) ratio, and temperature. The products obtained were characterized by using X-ray diffraction, chemical analysis and SEM techniques.

Jan 1, 2009

A sinter plant baghouse dust has been treated as a hazardous solid waste, and disposed at a very high price. A series of leaching tests were conducted to examine the possibility to produce high grade potassium chloride from the solid waste. It is found that around 40% of the solid wastes can dissolve into water, and a deposit with more than 90% KCl can be produced after simply drying the solution.

Jan 1, 2009

By Jilai Xue

Experiments with various industrial cathodes ranging from 35 wt.% to 100 wt.% graphitic and fully graphitized carbons were carried out in a laboratory aluminum electrolysis cell. Sodium and cryolite bath penetration into the cathode samples was measured by XRD and SEM-EDS analysis. For a higher cryolite ratio in the bath, the cathodes with lower graphitic carbons exhibited more sodium penetration than the fully graphitized. The increased graphitization in the cathode materials can reduce Na, NaF and Na3AlF6 penetration. SEM-EDS inspection reveals that the sodium and fluorides penetration within the cathode samples has different patterns for varying graphitization of the carbon materials. XRD quantitative analysis indicates that there is a large percentage of Na3AlF6 in the penetrated bath. The results can provide useful information for quality evaluation of the industrial cathode products.

Jan 1, 2010

By Yue-yuan Li

China has abundant magnesite resource, but the low-grade and powder ores have always been rejected, which influences the comprehensive utilization of resource and often causes circumstance problems. The present work investigated the preparation of magnesia whisker using magnesite tailings as starting materials by preparation magnesium carbonate whisker as precursor firstly in the route of calcination, hydration, carbonation and pyrolysis, follows by second calcination of the precursor. The influence of pyrolysis conditions and additives on morphology of magnesium carbonate crystal as well as the influence of calcination conditions on morphology of magnesia whisker was investigated. The results showed that thermal decomposition products was MgCO3?3H2O. Magnesium carbonate whisker with length of 10~60 µm and the length-to-diameter ratio of 10~20 was prepared when soluble magnesium salt was added. While temperature was elevated at 1°C?min-1, magnesia whisker with length of 10~60µm was obtained.

Jan 1, 2010

By Daudi R. Waryoba

Keywords: Wire Drawing, OFHC Copper, Recrystallization, Orientation imaging Microscopy (OIM), Texture inhomogeneity Textural inhomogeneities have been investigated in oxygen free high conducting (OFHC) copper wire drawn at room temperature to a true strain of 2.31, and isothermally annealed at 250°C and 750°C for annealing times ranging from 10 s to 1 hr. Local orientations were mapped by means of orientation imaging microscopy (OIM). The microtexture of the drawn wires showed a strong <111> + weak <100> duplex fiber texture at the inner core, whereas the mid and surface regions had a comparatively weak texture. Annealing at 250°C resulted into a recrystallization which originated from the mid section, proceed towards the surface regions and ends in the inner core. Recrystallization resulted into a strong<100>+weak<111> duplex fiber texture. A similar textural inhomogeneity was observed during short annealing at 750°C. However, prolonged annealing gave rise to abnormal grain-growth that proceed from the inner core to the outer surfaces with a dominant <111> fiber component at the inner region and mixed components of <111>, <100>, and <112> at the outer surfaces.

Jan 1, 2005

By WU Jian-hui

Keywords: metallic material, precursor synthesis, precipitation, nickel, fibrillar powder The composition and morphology of the precursor of fibrillar nanocrystalline nickel powder prepared by oxalate precipitation are characterized by XRD,IR and SEM analysis, and the effects of temperature, nickel concentration, pH, surfactant and drying process on the morphology and the dispersion of the precursor are investigated. By the experiment results, the fibrillar precursor is a complicated nickel salt. The precursor prepared in the of 60~70°C,0.6~0.8 mol/L nickel ion, pH=8.4~8.6 and with addition of PVP surfactant is well dispersive and in fiber form. The powder dried by azeotropic distillation is dispersive.

Jan 1, 2005