By Ryokichi Shimpo

Much amount of sludge is produced from the wastewater treatments in surface finishing industry. There are many problems for the abandonment of the sludge because of the high water content and heavy metals included. It is often observed that hexavalent chromium, which is toxic, is generated in the course of heat treatments of the sludge for reducing its amount by dispersing water. In this study, conditions of the sludge calcinations for reducing water contents have been examined. Maximum hexavalent chromium generation was observed in the temperature range around 773 K, at which most of the crystallization water decomposed from the sludge. When the heating temperature became higher than 1173 K, the amount of the hexavalent chromium extracted from the calcined sludge became as low as 10 mg/kg sludge. When the sludge was heated with iron oxides, FeO or Fe203, iron ferrite has been synthesized which may be used as a magnetic material. The amounts of hexavalent chromium generated in the heat treatment with iron oxides were not much different from those without iron oxides.

Jan 1, 2003

By Hiromichi Ohta

Precise thermal properties of molten materials are essentially required for analyzing the metal production process. These properties are also important as a clue to consider the dynamic structure of liquid materials. However, it is difficult to obtain the precise thermal diffusivity values of molten oxides at high temperature because of the experimental uncertainties arising from the bubble formation or the severe separation of radiative and conductive heat components. Recently a novel laser flash method has also developed for measuring thermal diffusivity of molten oxides at high temperature. In this new technique, the sample is melted in a metal crucible and heated to the desired temperature. A single laser pulse is flashed on the bottom of the metal crucible and the infrared ray irradiated from the same bottom surface is measured for obtaining the temperature decay, from which the thermal diffusivity of the liquid sample can be estimated. The usefulness and validity of this new laser flash technique have been confirmed by obtaining the thermal diffusivity values of silicate melts in the wide temperature range between 773 and 1673 K.

Jan 1, 2003

By Liangying Wen, Feng Xia, Chenguang Bai

"The situation of the Ti-V-Magnetite samples reduced with microwave has been investigated in laboratory. Firstly, the paper focuses on the heating behaviors of vanadium-titanium magnetite and characteristics of carbothermic reduction of V-Ti-magnetite in the microwave field. The effect of concentrate's size, quality on heating behaviors and reduction processes were researched. Results show that microwave heating may be a new heating resource replace of carbonic combustion reaction in reducing reaction. When the allocation of carbon is (16.7-30)%, carbothermic reduction of V-Ti-magnetite in the microwave field can proceed; with the increasing of carbon mixed, the metallization rate increases; and Fe, V can be reduced from their oxides in the microwave field; Titanic low oxide can be reduced from TiO2.1. IntroductionThe resource of Ti-V-Magnetite is abundant in the western area of Panzhihua in China, so far a mineral deposit of 4.64 billion tons have been proved up, it contains 14.75 million tons of V2O S which accounted for 87% of the vanadium and 5.93 hundred million tons of TiO2 accounted for 94% of the titanium resource respectively in China. The previous study proved that the major composition of mineral of the Ti-V-magnetite are Ti-magnetite, limonite, iron spinel, magnesium spinel etc, and the main elements of the Ti-V-magnetite in this area are Fe, Ti, V, Cr, Co, Ni, Ga, Sc etc[1] Due to the restrict of the BF-BOF process technical, during the smelting of the iron, the level of extracting the vanadium, titanium as well as other metal elements is limited. This results serious wasting of resources. To develop a new reduction process of Ti-V-magnetite is on the agenda, the microwave assistant reduction could meets this need, based on its characteristic of easy controlling of heating rate. To make use of the microwave energy to substitute the released heat sources of carbon combustion with air, use the solid phase state reduction at a relative lower temperature, make the beneficial element in Ti-V-magnetite transferred into the metal phase, then separated from the impurity. It is well worth to point out that once the microwave based reduction method has its industrial scale, it will take an outstanding position by its less release of carbon dioxide. This new environment-friendly process will play a vital role in the development of social industry and economy."

Jan 1, 2008

By S. P. Vanka, B. G. Thomas, S. Sivaramakrishnan

"During the continuous casting of steel, transient 'flow events can be very important to the generation of quality problems, such as shear entrainment, surface level fluctuations and bubble entrainment. These phenomena can be better predicted using Large Eddy Simulation (LES) models than the K-E models, which have been extensively studied. In this work the turbulent transient flow in a water model of a continuous caster has been both simulated using LES models and measured using Particle Image Velocimetry (PIV). The results of PIV and LES have been compared to validate the LES model and also to enhance the understanding of the prominent transient features of the flow field. The flow near the top surface in PIV was found to contain periods of 5-1 Os when the velocities were three to four times their mean values, which is of importance to the shear entrainment of the liquid flux. In both simulation and PIV the upper roll structure is found to change chaotically from a single large recirculation structure to a set of distinct vortices. The inlet swirl in PIV is seen to persist more than halfway across the mold, causing a characteristic staircase velocity vector pattern when viewed in a plane parallel to the wide faces. The lower rolls in PIV are significantly asymmetric for very long periods of time (- I-hour) and go through a repeating sequence of features. One of these features involving a short circuit between the upward and downward flow in the lower roll is also seen in the simulation and is of significance to bubble entrapment.IntroductionThe turbulent flow through the nozzle and in the mold of the continuous caster has been studied extensively using computational Reynolds Averaged Navier Stokes (RANS) models of turbulent flow [1,2]. Defects, such as internal inclusion of liquid fl4x through surface shear, pencil pipe defects due to bubble entrapment, surface defects due to level fluctuations are caused by transient flow phenomena oc'curring in the mold. These phenomena can be better predicted using transient Large Eddy Simulation [3] or ""LES"" models."

Jan 1, 2000

By Nan Zhang, Gai-feng Xue, Shangchao Liu, Benquan Fu

"The high-magnetization microspheres of Fe3O4 encapsulated with S1O2 and T1O2 layers (Fe3O4@SiO2@TiO2) were prepared. The microspheres were characterized by transmission electron microscopy and scanning electron microscopy. These high-magnetization microspheres could be readily dispersed by shaking whereas they could be rapidly separated from the aqueous solution simply by applying an external magnetic field. The two shells of S1O2 and T1O2 protected the iron oxide well and the microspheres were stable in acid and base solutions. Therefore, they have a good potential for the enrichment of phosphopeptides or photocatalytic activity. They could also be used to remove metal ions from waste water.IntroductionSolid-phase extraction (SPE) is the most commonly used separation technique for its simplicity, consumption of small volumes of organic solvent, and the ability to achieve a higher enrichment factor. The quest for new adsorbents is an important factor in improving analytical sensitivity and precision in SPE techniques. To date, many novel adsorbents, such as nanometer-sized materials, carbon nanotubes, mesoporous materials and magnetic nanoparticles have been employed in SPE.Magnetic polymeric microspheres, an interesting advanced composite material, have received increasing attention in the past few decades because of their unique physical and chemical properties and their potential for use in applications in various fields [1]. Magnetic microspheres consisting of an iron oxide core and a silica shell have attracted particular attention for their unique magnetic response, low cytotoxicity, and chemically modifiable surface. The core-shell magnetic silica microspheres have shown great potential in the fields of biotechnology and biomedicine for applications such as cell labeling and separation, enzyme and protein separations, targeted drug delivery, and magnetic ferrofluids hyperthermia."

Jan 1, 2012

By Cheng Pan, Qiugang Yuan, Xuewei Lv, Mei Liu, Enguang Guo

Land-based nickel resources include nickel sulfide and nickel laterite. With the consumption of high grade nickel sulfide, use of nickel laterite has received more and more attention. The mineralogy and sintering behavior of limonitic nickel laterite with high iron and low nickel and silica was studied to offer technical support for producing ferronickel through sintering–blast furnace route. The mineralogy results showed that the main phases in this kind of nickel laterite are goethite (FeO(OH)), gibbsite (Al(OH)3) and NiFe2O4. The TGA (Thermogravimetric Analysis) and DSC (Differential Scanning Calorimetry) revealed hydroxide minerals in addition to absorbed water. After the sintering experiments the chemical composition, phases present (XRD analysis) and physical properties of the sinter were studied. The content of FeO in the sinter increased with increasing basicity up to 1.3, and then decreased with further increase in basicity. The yield of sinter increased (from 73% to 80%) with increase in the basicity from 1.1 to 1.7, and then the yield decreased with the further increase in basicity. Mg(Ni)(Fe,Al)2O4 is the main phase in the sinter while MgCaSiO4 and Fe2SiO4 is the main binder phase when the basicity is 1.1~1.5, and MgCaSiO4, Fe2SiO4 and SFCA is the main binder phase when the basicity is 1.7~2.1.

Jan 1, 2014

By G. Upadhya

Of late, solidification modeling has progressed considerably to emerge as a viable simulation tool for the foundry engineer. A wide variety of tools exist in the commercial market to cater to the various needs of the design/ foundry engineer. In fact, recent developments in the area of solidification modeling have been so rapid that a comprehensive review of the state-of-the-art is very much needed. In this paper, an attempt is made to summarize the various issues of solidification modeling, at the same time addressing the historical evolution of the subject. The various phenomenological issues covered in this paper include: heat transfer, fluid flow during mold-filling, solidification kinetics and microstructural evolution, quick-analysis schemes for approximations, porosity prediction models, and the phenomena of fluid flow in the mushy zone. Modeling issues related to the development of solidification stresses which lead to defects such as hot tears and the development of artificial intelligence concepts in the area of rigging design are also discussed. Due emphasis is given to the various phenomena which add to the complexity of the whole subject, and the various alternatives available for solving a particular problem. For example, the heat transfer problem can be approached by the use of simple modulus schemes or by solving the conduction equation to obtain a more accurate temperature distribution. Similarly the microstructural evolution can be handled in a deterministic way by use of nucleation and growth models, or in a probabilistic way by use of empirical models. The main goal of this paper is to put the multi-faceted problem of solidification modeling in proper perspective so that it can serve as a guide for future developments in this area.

Jan 1, 1994

By K. Prashant Sarswat

Isotopes are critical to a variety of applications including physical science analyses, biology, medicine, pharmaceuticals, and national security. In most cases isotopes must be relatively pure or highly enriched before they become useful. Current isotope separation technologies are relatively inefficient, capital and labor intensive, and often produced by a limited number of suppliers. In the category of isotopes, lithium is among other important candidates. Lithium is found naturally in two isotopes, 6Li which accounts for 7.5% of all lithium, and 7Li which makes up the balance of 92.5%. Each of these isotopes is important to the nuclear industry. 7Li is often used in the form of lithium hydroxide which is used to control pH in pressurized water reactors. The current supply of 7Li is based mostly outside of the United States, and its long-term supply is uncertain. Apart from supply issues, the use of mercury for 7Li separation is also a concern in commercial processing using the most common and efficient approach [1–3]. Hence, a reliable, environmentally friendly, and efficient technique is needed to produce 7Li. In this line of investigations, the authors used a two-compartment system and significant separation was achieved. In this piece of research, some preliminary results are presented including cell design and actual isotope ratio after enrichment. Applying an electro-potential across two electrodes can be used to drive electromigration of Li isotopes. The electromigration is in addition to normal diffusion. Note that 6Li diffuses faster and hence there will be a lowering of the 6Li concentration near the positively charged electrode and an enhancement in 6Li near the negative electrode during the separation process. Similarly, 7Li will be more prevalent near the positive electrode and less prevalent near the negative electrode during the initial separation stage [1].

By A. C. Mollison

In November of 1983 a fire inside the autoclave caused the curtailment of operation of the Kidd Creek pressure leaching facility. Subsequent repairs and recommissioning of the autoclave in 1984 allowed Kidd Creek to increase its production of zinc as originally planned. This paper describes the operation of this process from 1984 to 1988 and details major mechanical work carried out on the vessel in 1.988:

Jan 1, 1990

By Jiangtao Li, Zhongwei Zhao, Xingyu Chen, Xuheng Liu

In tungsten ion-exchange process, excessive sodium impurity enters into ammonium tungstate solution. However, the Na content of the final ammonium paratungstate (APT) product must be strictly controlled. Consequently, it is necessary to remove Na from the ammonium tungstate solution during processing in order to obtain the required purity of APT. In this study, porous Na specific absorbent, Na1+xAlxTi2−x(PO4)3, is used to remove Na from the ammonium tungstate solution. Through experiments, the effect of reagent concentration of Na1+xAlxTi2−x(PO4)3, reaction time, reaction temperature and Na concentration on the Na removal were investigated. The results showed that under optimal reaction conditions of reagent amount of NATP 1.0 times of theoretical amount, reaction temperature 25 °C and reaction time 15 min, the Na removal from commercial (NH4)2WO4 solution can reach 98%. Na1+xAlxTi2−x(PO4)3 has a good applicability to different Na+ concentrations. The obtained APT product reaches the national standard purity of zero level.

Jan 1, 2014

By Yuanbo Zhang, Huanpeng Mi, Guanghui Li, Binjun Liang, Zhiwei Peng, Tao Jiang

Ludwigite ore has not yet been utilized on an industrial scale due to its complex mineralogy and fine mineral dissemination. In this study, sodium salts were employed to enhance the separation of iron and boron by reductive roasting-magnetic separation. It was found that the separation of iron and boron as well as the iron grade and recovery were significantly improved b y the addition of Na2SO4 or Na2CO3. Under the reduction temperature of 1050 °C, reduction time of 60 min and magnetic intensity of 0.1T. Compared with the inexistence of sodium salts, the iron grade and recovery of the magnetic concentrate increased from 83.3% and 88.6% to 93.2% and 95.1%, respectively, by adding 6% Na2CO3. The XRD and microstructure analyses indicated that the iron oxides were transformed into metallic iron and the average metallic iron grains were grown to over 40μm which was beneficial for separation of metallic iron from gangue.

Jan 1, 2016

By Jesus Gonzalez

Peirce-Smith converters (PSC) are long cylindrical chemical reactors where copper matte reacts with air. Traditionally, air is injected laterally through submerged tuyeres at different subsonic velocities. However, the accumulated experience in steelmaking, particularly in the basic oxygen furnace (BOF) process, shows that the gas bottom injection may improve the mixing efficiency of a liquid pool. The aim of bottom injection is to maximize the copper kinetic energy meanwhile avoiding excessive reactor splashing. When gas is injected from a single orifice at the bottom of a liquid pool, two main gas flow regimes can be identified, bubbling and jetting. In this work, a PSC with bottom air injection is studied by means of multiphase 3D CFD numerical simulations considering multiple air velocities. Special attention is paid to the bubbles and jet formation mechanism. The mixing efficiency is measured by calculating the turbulent kinetic energy of the copper matte.

Jan 1, 2008

By W. L. Dalmijn

The processing of scrap and scrap cars starts with size reduction by a hammermill, or shredder. After the liberation the magnetic fraction is removed. The remaining non¬magnetic fraction mixed with other materials is screened and each fraction is processed separately. The increased use of plastic has a negative effect on the recovery of metals and waste production. At Huron Valley, Belleville Michigen, USA, the non-ferrous fraction from 5 million obsolete cars per year, containing 200,000 tons of non-ferrous metal, is processed. Aluminium Is recovered with a heavy medium separation process and concentrated with eddy current separators. The remaining heavy non-ferrous fraction is concentrated by a new combination of eddy current separation and image processing. After this separation process the zinc fraction is melted and refined and the copper, brass, stainless steel and other high-quality concentrates are sold to the secondary industries. The recycling of car scrap has become an important source of metals and materials for the secondary. materials processing industry.

Jan 1, 1995

By R. H. Lien

The Bureau of Mines, U. S. Department of the Interior, is investigating chemical and biological decontamination of complex wastewaters such as tailings pond water containing 280 ppm CN and 5 ppm Se as well as significant concentrations of arsenic, copper, iron, silver, and zinc. The most effective chemical procedure involves cyanide oxidation using hydrogen peroxide or sodium hypochlorite followed by selenium reduction using ferrous hydroxide. The effluent contains <l ppm CN and 20 ppb Se; concentrations of other major contaminants meet EPA drinking water standards. Preliminary research indicates that biological cyanide oxidation is possible even in highly alkaline solutions (pH 10.5) containing high cyanide concentrations; indigenous bacteria destroyed 85 pet of the cyanide. Exploratory research shows that other bacteria removed up to 79 pet of the selenium from chemically oxidized, low-cyanide water. These promising results may lead to a final processing scheme that involves a combination of chemical and biological techniques.

Jan 1, 1990

By Ximeng Zhu

The electrochemical behavior of mineral and coal pyrites in stirred and quiescent alkaline boratelsulfate solutions @H 7.9-10.5) have been investigated using cyclic voltammetry. Significant differences in the electrochemical response of these pyrites were observed. At the mineral pyrite surface, three anodic peaks at about -0.8 V, -0.1 V and +0.5 V (SCE) have been detected along with their corresponding reduction peaks. The first two peaks correspond to FeIFeOI) and FeOI)lFe(III) oxidation. The third peak is present for quiescent conditions but disappears as a distinct peak when the electrolyte is stirred. In the upper voltage region +0.30V (SCE), the current increases markedly during stirring and the reactions correspond to the oxidation of pyrite with the formation FeOII) oxides plus elemental sulfur. Also there is evidence that Fe oxy-ions form. Coal pyrites, under rapid sweep conditions display only the first two anodic peaks, the associated reduction peaks and an additional reduction peak corresponding to one or more of the high voltage oxidation products. After prolonged exposure to high potentials, coal pyrite displays reactions similar to those of mineral pyrite but at much higher current densities demonstrating the much higher reactivity of the coal pyrite. The reactivity sequence was Upper Freeport coal pyrite > Pittsburgh coal pyrite > mineral pyrite.

Jan 1, 1991

By R. E. Brewer

Pilot scale flotation tests were conducted with a l?ft-diam column at the Barrick Resources (USA) Mercur mine, Tooele County, UT, to scavenge unleached (0.01 to 0.018 oz/st) gold values from the tailings of a carbon-in-leach (CIL) circuit. The optimal recovery was 35 pct of the unamenable-to-leaching gold, at a grade of 0.353 ounces of gold per short ton, using a mixture of dithiophosphate, xanthate, and diesel fuel as a collector. This was achieved by floating approximately 1.6 wt pet of the CIL tailings. The gold values are believed to be contained in arsenic-bearing minerals, attrited carbon, and carbonaceous material in the ore. Redox potentials were measured with a gold electrode during the conditioning stage prior to flotation. The correlation between flotation recovery and redox potential values could be used to control reagent additions. Treatment of a previously leached and weathered tailings material, averaging about 0.055 ounces of gold per short ton, was also investigated. The tailings were first water leached at approximately 60? C, and the water-leached tailings, containing approximately 0.03 ounces of gold per short ton, were then fed to the column flotation unit. The effects of pH&apos; and sodium sulfide addition on gold flotation recovery and redox potentials were examined. Maximum gold flotation recovery, 36 pct, was achieved at pH 8,5 with a sodium sulfide addition of 0.18 Ib/st. Overall gold recovery by leaching and flotation was in the range of 70 to 80 pet.

Jan 1, 1989

By Patricia A. Wells

In the remelting of scrap, the ultimate goal is to produce clean aluminum while minimizing metal losses. Recently, it has become more difficult to make significant recovery improvements in Reynolds&apos; Reclamation Plants since metal recoveries were nearing the theoretical maximum. In an effort to gain a better understanding of the factors impacting Reynolds remelting process, a series of experiments using a Taguchi-type design was performed. Specifically, the critical variables and interactions affecting metal recovery of shredded, delacquered Used Beverage Containers (UBC) melted in a side-well reverbatory furnace were examined. This furnace was equipped with plunger-style puddlers and metal circulation. Both delacquecing and melting processes operated continuously with downtime only for necessary mechanical repairs. The experimental design consisted of an orthogonal array with eight trials, each using nominal 500;000 lb shred charge volumes. Final recovery results included molten output and metal easily recovered from dross generated during the test.

Jan 1, 1995

By llya Perederiy, Vladimiros G. Papangelakis, Indje Mihaylov

"Nickel slags obtained from various smelting furnaces and converters differ in terms of their chemical composition and microstructure. The microstructure of the slag is largely affected by how fast the slag is cooled after being discharged from the furnace. Slow cooling is known to promote crystallization and growth of phases such as crystalline fayalite (Fe2Si04), magnetite (Fe3Ü4) and vitreous silica (S1O2). Slag granulation causes rapid solidification of the melt in the form of either an amorphous solid or highly intergrown crystalline silicate and oxide phases. Smelter slags contain entrapped Ni, Co and Cu in the form of dissolved oxides and matte inclusions. Extraction of the entrapped metals by high pressure oxidative acid leaching (250°C, 70 g/L initial H2SO4, up to 90 psi O2, 45 min) relies on the dissolution of the metal bearing minerals. The impact of the slag microstructure on the accessibility of these minerals to leaching, as well as the morphology of the produced residues is discussed in this paper.IntroductionIt was shown previously that entrapped base metals can be efficiently extracted from naturally cooled (as opposed to granulated) crystalline nickel smelter and converter slags using high pressure oxidative acid leaching operating at 250°C, ~40 g/L terminal acid and 60 to 90 psig oxygen overpressure [1, 2,3,4, 5, 6].Mineral characterization work performed on a naturally cooled crystalline nickel furnace slag from Vale's operations in Sudbury (ON, Canada) was previously reported [4]. Fayalite (Fe2Si04) and magnetite (Fe3U4) were detected using powder X-ray diffraction. These two minerals as well as silica (S1O2) and matte ([Fe,Ni,Cu]Sx) were also identified with the help of energy dispersive X-ray spectroscopy (EDX) on cross-sectional images obtained with a scanning electron microscope (SEM) operating in the backscattered mode. Nickel converter slags obtained from Vale's operations in Sudbury were found to be mineralogically similar to the furnace slag, but with higher contents of matte entrainment and magnetite based on the SEM-EDX observations [6]."

Jan 1, 2012

By V. D. Tathavadkar

Natural chromite mineral is a solid solution of spinet end members namely: chromite (FeCr2O4), hercynite (FeA1204), magnetite (Fe3O4), magnesio-chromite (MgCr2O4), (MgA12O4), and magnesio-ferrite (MgFe2O4). A phase transformation in chromite minerals occurs in oxidising conditions during the soda-ash roasting reaction. This phase transformation plays an important role in improving the extraction efficiency of Cr3+ from mineral phase. The extraction efficiency of chromium (Cr3+) from chromite to a water¬soluble sodium chromate (Cr6+) salt depends upon the decomposition kinetics of the spinet phase. An investigation of the phase changes in chromite ores in the absence of sodium carbonate was carried out in air, argon, and in argon +5 % hydrogen gas mixture. The thermodynamics of phase transformation reaction in chromite solid solution phase is discussed using the solution model proposed by Sack and Ghiorso [1]. The microstructural changes and the changes in elemental compositions of different phases were examined by SEM and electron probe microanalysis (EPMA) respectively. The experimental results indicate that the solid solution spinet phase in chromite mineral undergoes spinodal decomposition under the influence of oxygen partial pressure and temperatures. The structure of phases formed and their morphologies suggest that the phase decomposition may be similar to those observed by Burkert et. a]. 121, although the scale of phase separation in chromite appears to be strongly dependent on oxygen partial pressure.

Jan 1, 2001

By J. Bostjancic

As wastewater discharge regulations become more stringent, power plants, manufacturing plants and other industrial sites are looking for ways to reduce makeup water requirements and to recycle and reuse as much wastewater as possible. In some cases, environmental regulations require zero liquid discharge, meaning all wastewater must either be retained on site or reduced to solids for disposal off site. Zero liquid discharge or "closed-loop" wastewater treatment systems using evaporators and other process equipment have been well-accepted in recent years. Often overlooked is the fact that zero discharge is not just the latest fashion--many commercial zero liquid discharge systems have been in operation since the mid-70&apos;s. This paper will give specific examples of zero liquid discharge operations from 1974 to the present, showing how evaporation equipment and processes have changed to meet the requirements of industry and environmental regulations.

Jan 1, 1996