Search Documents

By S H. Hyun, J W. Cho

Jun 19, 2024

By S Maritsa, E K. Chiwandika, S M. Masuka

The iron and steel industry is experiencing an increase in the use of iron and steel commodities within societies, decarbonisation pressures, depletion of high iron ore grades and high energy consumption. This necessitates scrap metal recycling, low-grade ore utilisation using the induction or electric arc furnace to achieve the global target of net zero CO2 emission. The available highquality scrap metal cannot sustain the steel industry but the world has unused hematite-goethite ores. It is the aim of this research that this resource be utilised using the induction furnace to sustain the steel industry in an environmentally friendly manner. Indurated pellets prepared from the hematite-goethite ore, 5 wt per cent limestone and 5 wt per cent coal addition were smelted in the induction furnace at 1350 ± 50°C with 25 mins holding time. The effects of basicity and carbon content were also investigated to optimise the smelting parameters. The results showed that the careful control of the basicity, and iron-to-carbon ratio maximised total metal recovery. The optimal basicity ratio was determined to be 1.3 and a carbon to iron ratio of 1.4 achieved a total metal recovery of 73 per cent. The metal recovery was closely related to the estimated slag melting temperature. The basicity ratio of 1.3 achieved the lowest slag melting temperature estimated to be around 1380°C based on the CaO-SiO2-Al2O3 phase diagram. The recovered metal had a comparable chemical composition and microstructure to that products from an ITmk3 furnace.

Jun 19, 2024

By A Takahashi, Y Uchisawa, M Hayashi, T Watanabe, M Susa

Owing to the deterioration of iron ore, the Al2O3 concentration in iron ore increases, and thus it is important to investigate the effect of increment in Al2O3 concentration on the microstructures of iron ore sinters. During the sintering process, a melt is present in the sinter for only a few minutes, and therefore the microstructure of the sinter doesn’t reach thermodynamic equilibrium. Nevertheless, the formation process of the microstructures can be interpreted and predicted to some extent from the equilibrium phase diagram. This study investigated the liquidus isotherm in the CaO-SiO2-Fe2O3- 5 mass% Al2O3 system at 1240°C in air and the phase equilibria of silico-ferrite of calcium and aluminium (denoted by SFCA) and SFCA-I by XRD (X-ray diffraction analysis) and electron probe micro analyzer (EPMA). The following results were obtained: 1. The ferrite melt region with a high Fe2O3 concentration shifts to the lower Fe2O3 side than the liquidus isotherm in the CaO-SiO2-Fe2O3 system. 2. The compositional region of SFCA extends in the CaOꞏ3Fe2O3-4CaOꞏ3SiO2 direction than the silico-ferrite of calcium (denoted by SFC) composition region with a 0 mass% Al2O3. 3. SFCA-I is observed in the present system, which suggests that the increment in the Al2O3 concentration contributes to the stability of SFCA-I. These results imply that an increment in Al2O3 concentration in iron ore leads to a decrement in the volume fraction of the bonding phase and that the fraction of the SFCA phase increases, and those of 2CaOꞏSiO2 and slag phases decrease in the bonging phase. The SFCA-I phase is also precipitated from the slag with an Al2O3 concentration around 5 mass%.

Jun 19, 2024

By F Tang, Ö K. Büyükuslu, M Baben, S Petersen

GTT-Technologies’ ChemApp for Python was developed to provide a powerful, easy to use interface to ChemApp for a programming language highly popular with scientists and engineers. It is used, for instance, by GTT to develop program modules such as the CALPHAD Optimiser for the FactSage™ software, by customers to move from interactive FactSage calculations to perform versatile scripting with Python, and by GTT and its partners in research projects in the area of materials informatics. Computational thermochemistry is fundamental for advancing sustainable metallurgy and creating new alloy compositions for engineering applications. Materials informatics involves handling vast amounts of data and complex workflows. GTT’s approach uses ChemApp for Python and the FactSage thermodynamic databases to design recyclable alloys from the start, incorporating a higher percentage of scraps while aiming to simplify the workflows to simulate material design steps. Challenges arise due to recycling scraps, introducing more elements for consideration. CALPHAD-based databases accurately cover materials from primary metallurgy, but additional data for minority and critical elements is crucial for precise computational modelling. GTT combines machine learning-based ab-initio databases with traditional CALPHAD databases to cover the complete chemical space with appropriate accuracy. The design of a hardfacing alloy through a high-throughput materials informatics approach is used as a demonstrator of the current possibilities.

Jun 19, 2024

By K Vallo, T Haimi, J Pihlasalo, J Hamuyuni, M Lindgren, F Tesfaye

Decarbonisation of the steel industry has recently attracted a lot of research and technological development. Most of the technological developments are centred around the replacement of blast furnace (BF), which has been the main primary smelting furnace in the ironmaking step of steel production. Replacement of the BF is not an easy task because of BF’s many established capabilities over the years, especially its ability to use low-grade iron feed. In this regard, Metso has developed its own technology, Metso’s Outotec direct reduced iron (DRI) smelting furnace, to tackle this problem. The recently developed six-in line electric furnace for DRI smelting can be used for primary smelting of DRI from blast furnace grade iron ore. Unlike the electric arc furnace (EAF), the DRI smelting furnace can handle larger slag volumes that emanate from the high gangue in BF grade DRI. Therefore, fluxing plays an important role in operating the DRI smelting furnace. This paper presents fluxing options and proposes slag quality and operating windows for the DRI smelting furnace. Also, the effect of slag on refractory durability will be discussed.

Jun 19, 2024

By S Bright, M J. Masamvu, E K. Chiwandika, S Dandi, S M. Masuka

The depletion of high-grade hard and lumpy chrome ores has forced Zimbabwean ferrochrome producers to resort to low-grade friable ores that have an average of 28 per cent fines against a set limit of 12 per cent. Submerged open arc furnaces currently in use are associated with eruptions within the furnace because of the high amounts of fines, high energy consumption, as well as high SO2 and CO2 emissions. Traditionally employed agglomeration methods such as pelletising and the use of coke in the furnace have been discarded because of the pressure to lower operational costs and to achieve higher profit margins. This research aims to develop a method to incorporate lowgrade friable ore fines and unprocessed coal into production while lowering CO2 and SO2 emissions through a closed direct current (DC) arc furnace. The closed DC arc furnace could incorporate the friable ores and coal while maintaining above 90 per cent reduction rates. Preliminary findings also show that energy consumption could be reduced by up to 35 per cent by incorporating a pre-heating and pre-reduction system using the flue gases from the furnace. In the proposed circuit, the cost of production per ton of ferrochrome might be potentially lowered by an average of 30 per cent.

Jun 19, 2024

By X Li, R Chu, X Deng

The hot-dip galvanising industry is the largest consumer of zinc, with over 40 per cent of the world’s total annual production of zinc used for galvanised steel. The dross generated in the hot-dip galvanising coating process is a valuable co-product, since it contains high quantities of recyclable metal. A new method to recover the metal from the industrial galvanising dross was proposed using supergravity separation. During the hot-dip galvanising process, the presence of zinc dross has a serious impact on the surface quality of the hot-dip galvanised sheet, forming zinc dross defects. To reduce the impact of zinc dross, the zinc dross on the surface of the zinc pool needs to be manually or mechanically removed at regular intervals. However, during the dross removal process, a large amount of metal zinc is inevitably carried out, resulting in low zinc utilisation rate and high zinc loss rate. This article proposes an efficient and low-cost technology for the recycling and utilisation of hotdip galvanised dross, which uses super-gravity technology to recover hot-dip galvanised dross online. The metal in the hot-dip galvanised dross returns to the zinc pot in situ, while a small part of the dross remains in the super-gravity equipment, which can reduce the amount of zinc dross by more than 60 per cent and achieve a reduction in zinc loss from 17 per cent to less than 7 per cent.

Jun 19, 2024

By S Basu, S L. A Gowravaram

CaF2 has been a common constituent in a wide variety of welding fluxes, including those used for submerged arc welding (SAW). The widespread use of CaF2 stems from its role in lowering the liquidus temperature as well as the viscosity of the molten slag that covers the weld pool. However, the harmful effect of fluoride evaporation from molten flux, on the environment as well as the health of the users is becoming increasingly evident over the years. This has led to increasing attention towards reducing the CaF2 concentration in the fluxes. The fluoride-free formulations face the challenging requirement to maintain the thermo-physical properties (viscosity, liquidus temperature etc) like those observed in fluoride-containing fluxes. In the present work, three fluxes with compositions in the CaO-MnO-SiO2-Al2O3 system have been identified as promising alternatives to the CaF2-rich fluxes. However, the thermo-physical properties of any such flux need to be comparable to CaF2-based commercial SAW fluxes before it can be adopted for regular use. The single hot thermocouple technique (SHTT) has been used by several researchers in the past as a tool for observing the melting and solidification characteristics of fluxes. This device has been developed in the present work and is used to characterise the melting behaviour of the fluxes. The measured solidus and liquidus temperatures from SHTT were compared with the results from differential thermal analysis (DTA) and simulations using the FactSage™ software for a comprehensive understanding. In spite of having a slight deviation in the measured values from the multiple techniques, the results obtained from these multiple methods show that the selected compositions could be potential CaF2 free alternative welding fluxes.

Jun 19, 2024

By E Jak, P Hayes, J Chen

The paper provides an overview of the various analytical and microanalytical techniques currently in use to characterise the outcomes of pyrometallurgical processes, examining the advantages and limitations of these approaches. Specific focus with be given to quantitative microanalysis techniques including electron probe microanalysis and laser ablation, covering general principles, capabilities and limitations and recent development to address specific challenges associated with analysing molten slag, matte, and alloys, highlighting the necessity of embracing the application of these and other innovative analytical methodologies.

Jun 19, 2024

By J Safarian, M K. Kar

Bauxite residue is one of the most important by-products from the alumina industry with no commercial use till now. The utilisation of bauxite residue through pelletising with different lime additions, hydrogen reduction, and smelting has been studied in this work. Three different types of green pellets were made with varying calcite-to-bauxite residue ratio and subsequently sintered at elevated temperatures. The sintered pellets were isothermally reduced at 1000°C under hydrogen gas followed by smelting of the reduced pellets in argon at 1500°C. Smelting of the reduced pellets leads to the recovery of metallic iron and the formation of a leachable calcium aluminate slag. X-ray diffraction (XRD) and scanning electron microscope (SEM) were used to characterise the phases and microstructural analysis. The iron produced in the smelting process has a high purity, above 99.5 wt per cent. While the iron content of the slags is quite low, and the slags shows variations of krotite (CaAl2O4), gehlenite (Ca2Al2SiO7), and perovskite (CaTiO3) phases based on the variation of calcite addition. It was found that the more calcite addition in pelletising yields higher percentage of krotite phase as compared to lower calcite-containing pellets. Employing quantitative XRD analysis, the krotite phase fraction was found approximately 85 wt per cent for higher calcite-added pellet, and around 74 wt per cent for lower calcite-added pellet. FactSage™, ver 8.1 (Thermfact and GGTTechnologies) thermodynamic software was used to evaluate the obtained experimental data, they both revealed that the

Jun 19, 2024

By V Shrotri L Muhmood, P Gandhre

The current work deals with the measurement of some thermophysical properties of Ca(NO3)2 based ternary nitrate molten salts as HTF (heat transfer fluid) / TES (Thermal Energy Storage) material for CSP (Concentrating solar power) plants. The density and viscosity of different compositions of the ternary salt mixture containing Ca(NO3)2, NaNO3 and KNO3 close to the liquidus has been experimentally measured. An attempt has also been made to measure the melting point of the salt using the cooling curve technique as well as Differential Scanning Calorimetry (DSC). Thermogravimetric analysis has also been performed to estimate the peak operating temperature of the salt. Compatibility of suitable pipe material (SS304) with molten salt has also been discussed. The salt mixture proves to be a viable alternative to the already existing HTFs like Therminol VP-1 (organic oil) or Solar Salt® in regards to its lower melting point, wider operating range, low cost, nontoxicity, sufficiently high density and comparable viscosity.

Jun 19, 2024

By S Natsui, Y Goto, S Kawanishi, J Takahashi, H Nogami

The demand for copper increases yearly, and further improvements in copper smelting efficiency using flash furnaces are required. This study was conducted to understand and promote the interfacial reaction associated with the collision of silica flux and iron oxide particles, ie the formation reaction of fayalite slag, in the reaction shaft of the flash furnace. High-temperature microscopy was used to observe the reaction behaviour of a 2 mm granular SiO2 reagent in contact with micrometreorder- sized FeO reagents in situ. When the amount of FeO was lower than the stoichiometric amount with SiO2, the molten slag formed at the interface between FeO and SiO2 diffused into the SiO2 particle before dissolving the remaining FeO particles. It did not contribute to the subsequent reaction, and despite having the lowest amount of FeO among the samples in this study, many unreacted FeO particles remained on the surface of the samples after testing. On the other hand, under conditions with high FeO content and close to the eutectic composition of the FeO-SiO2 system, a liquid phase formed from low temperatures, gradually increasing in volume and eventually completely dissolving the 2 mm SiO2 grain. These results indicate that the early-stage slag is essential in increasing the interfacial area between FeO and SiO2 and facilitating the supply of FeO to SiO2. In other words, the FeO/SiO2 determines the amount of liquid phase and significantly influences the subsequent interfacial reaction rate between FeO and SiO2. Therefore, the local FeO/SiO2 of the particles falling down the reaction shaft should also be optimised to ensure early slag formation. Meanwhile, the time required for 2 mm SiO2 to complete the reaction for the temperature history employed in this study was significantly longer than the particle residence time in the reaction shaft. Further detailed investigation of the effects of silica flux particle size, composition, and reaction temperature on the reaction time will help find the conditions under which the reaction of silica flux can be completed in the reaction shaft. These kinetic approaches could contribute to future innovations in the copper smelting process using flash furnaces.

Jun 19, 2024

By M A. Rhamdhani, K Avarmaa, A Putera, J Chen, G Brooks

Silicon-based photovoltaic cells are currently the most dominant types applied to convert solar energy to electricity. In solar-grade silicon (SG-Si), the control of boron (B) and phosphorus (P) is very critical. Generally, these elements are difficult to remove into acceptable sub-ppm levels from lower grade Si. This study investigates slag treatment as a process for Si refining, focusing on the behaviour of P and B. The experiments were conducted by equilibrating Si-B-P alloys with 43 wt per cent SiO2 – 47 wt per cent CaO – 10 wt per cent Al2O3 slag under inert atmosphere at 1500°C. Different crucible materials were used (Al2O3, SiO2 and MgO), which determined the primary saturation phase for the system and modified the final slag composition accordingly. The samples were equilibrated and analysed with microanalysis techniques (EPMA (electron probe microanalysis) and LA-ICP-MS (laser ablation inductively coupled plasma mass spectrometry)). New standards were prepared and applied in the LA-ICP-MS analyses. Experimental results show that silver is essentially fully dissolved in silicon, as well as most phosphorus with LP ( = wt per cent P in slag/wt per cent P in Si) between 0.1–0.3. The distribution coefficient of boron was measured to be between 1 and 2. The crucible material used had an influence on the phase compositions and slight influence on the distribution coefficients of boron and phosphorus. The experimental results provided new accurate data when considering applicability of slag treatment as a technique for Si refining and Si PV cell recycling.

Jun 19, 2024

By B J. Monaghan, R J. Longbottom, D J. Pinson, S J. Chew

Recycling steel plant by-products is a critical issue for achieving both environmental and economic sustainability of integrated steel plants. A key steel plant by-product stream is dust from basic oxygen steelmaking (BOS), which can be recycled back to the BOS vessel as iron units and to aid slag formation. The major limitations for its recycling are zinc and the uncertainty in zinc speciation of the dust. This uncertainty affects the amount of dust recycled and how it interacts with the slag during processing. BOS dust in stockpiles can undergo self-sintering reactions that oxidise the iron-bearing components. As this occurs, zinc (or oxide) may combine with iron oxides to form a zinc-iron spinel solid solution phase. Knowing which zinc-bearing species are present in the BOS dust is a key aspect in understanding and developing an efficient recycling process for the dust. To overcome difficulties associated with phase identification in the BOS dust (both fresh and selfsintered), particularly the magnetite-zinc ferrite spinel solid solution using X-ray diffraction (XRD) / scanning electron microscopy (SEM) / energy dispersive spectroscopy (EDS), high end characterisation tools, transmission electron microscopy (TEM) and Mössbauer spectroscopy, were also used. Such an approach allowed improved phase identification of key zinc- and iron-bearing phases that were not previously resolvable. The zinc in fresh BOS dust was mostly present as extremely fine separate particles of zinc oxide, attached to the iron particles. These extremely fine particles were <10 nm in size. Additionally, a small amount of zinc ferrite was also identified within the sample (most likely contained within a magnetite-zinc ferrite spinel solid solution). However, the zinc in the self-sintered BOS dust, was found to be present entirely in a magnetite-zinc ferrite spinel solid solution. While this spinel phase had been previously identified by XRD, it was not clear that it contained zinc. The Mössbauer results provided definitive evidence of zinc within the spinel phase.

Jun 19, 2024

By M I. Pownceby, M A. Rhamdhani, D M. Fellicia, S Palanisamy, R Z. Mukhlis

The trend of global copper production has prospectively increased over time. Based on typical mined ore grades, 1 t of copper ore generates approximately 6–10 kg of copper, which requires much energy, usually in the form of metallurgical coke. Copper production using carbon as a fuel and reductant contributes up to 0.3 per cent to global greenhouse gas (GHG) emissions. As a result, research into decarbonisation processes applicable to reducing low-grade copper sulfide ores, copper oxides, electronic wastes and other alternative complex Cu-rich materials has increased. Alternative fuels for reducing carbon-rich emissions in pyrometallurgical copper processing include methane, ammonia, biomass, solar and wind power, but in recent times increased focus has been on hydrogen as a potential fuel and reducing agent for materials such as oxidised copper scrap, Cu2O/CuO and Cu-rich slags/e-wastes. From a thermodynamic perspective, hydrogen exhibits a significantly more negative standard Gibbs free energy (ΔG°) than copper oxide making it a suitable reductant and the exothermic thermal effect from reaction between hydrogen and Cu2O/CuO may be used to control process parameters. These characteristics renders hydrogen an ideal gas for reducing copper oxides and copper-containing slags/e-wastes. This review article assesses previous research on utilising hydrogen for producing and refining copper from primary and secondary feed materials.

Jun 19, 2024

By C Zschiesche, alam, A Abadias Llamas, A K

Lead has the ability to collect and carry valuable metals such as copper, bismuth, antimony, tin and precious metals for their downstream recovery. Therefore, lead metallurgy is key for the raw material supply that our society demands. Lead smelters, excluding lead-acid battery recyclers, tend to process more complex primary and secondary raw materials, which are mostly processed via the pyrometallurgy route. Accordingly, understanding the slag system of these metallurgical processes is key for the efficient industrial operation and recovery of minor elements. Glencore Nordenham is an integrated lead and zinc smelter in northern Germany with a production of 92 000 t of lead and 164 700 t of zinc in 2022. The lead production line processes complex leadbearing raw materials through the direct smelting process. Firstly, the feed mix is smelted in a Top Submerged Lance (TSL – Ausmelt®) furnace, where a lead bullion containing minor metals and a lead-rich slag are produced. Then, the lead-rich slag from the TSL is tapped (via launder) into a Side- Blown Furnace (SBF), where lead oxide is reduced to produce lead bullion (with minor elements) and discard slag. The lead bullion from both stages is refined to produce lead (>99.9 per cent) and recover the minor elements (Cu, Ag, Au, Sb, Te, Bi etc). This paper reflects the experience of operating the SBF after the first five years of operation and describes its ‘PbO-SiO2-FeOx-CaO-ZnO’ slag system. Firstly, the slag system, the furnace operating region and the potential solid phases present are discussed from a theoretical point of view. This theoretical study has been performed using FactSage™ 8.2 and the database developed by the Pyrosearch group at the University of Queensland, Australia (UQPY). Then, the FactSage™ simulations are compared with industrial slag measurements. Finally, some examples on how the slag knowledge gained at Glencore Nordenham can help the industrial operation of the SBF are discussed.

Jun 17, 2024

By M. Z. Emad, A. Khan, N. Abbas, K. G. Li

Probability-based empirical methods were employed as an alternative approach to predicting uncertainties associated with rock mass properties. The focus was on developing probabilistic spreadsheets to forecast rock mass classification indexes. Histograms were constructed to describe the best distribution in predicting rock mass properties. The developed models also offer utility in predicting the impact of discontinuities within the rock mass on rock strength and rock mass classification systems. Statistical analyses identified volumetric joint count, joint spacing, joint frequency, and rock strength as the most influential parameters. Moreover, the statistical analysis revealed varying degrees of correlation among different rock mass properties. While some properties demonstrated significant correlations suitable for modelling, others did not align well with any correlation model. The results highlight the need for a comprehensive approach to rock mass characterization, considering multiple factors beyond volumetric joint count. Geological complexities, including tectonic activity and weathering processes, may obscure direct correlations. These results emphasize the importance of empirical modelling and detailed site investigations for accurate assessment of rock mass quality and stability in the Himalaya.

Jun 10, 2024

By J. van Zyl, K. B. Le Bron, L. J. Gardner

Pillar design is a crucial aspect of underground mining engineering, as it directly impacts the safety, stability, and overall effectiveness of mining operations. In this paper we present a method to calculate pillar stability based on the strain criterion and pillar load inversion concept, which complements the empirical pillar strength formulae. Those formulae do not account for certain parameters that can affect the stability of the pillars, e.g. weak layers, changes in stress orientations due to mining, orebody dip, mining layout complexity, and the influence of regional stabilizing pillars. The approach presented here is not intended to replace the empirical method; rather, we suggest using it as the initial step in the pillar design process. This should be followed by iterative numerical modelling to study pillar behaviour, define pillar stability, and optimize the pillar design by considering site-specific and representative rock mass properties and criteria.

Jun 10, 2024

By W. W. de Graaf, M. J. Ntsekhe

Klipspruit Colliery is experiencing coal losses, which leads to a negative impact on coal production and subsequently loss in revenue. This study aimed to identify the possible causes of coal losses in the No. 4 upper and lower seams. The objectives were to identify potential sources of coal losses through a literature survey, to identify areas where the coal losses occurred, to determine factors affecting coal losses, and to identify the most cost-effective methods to reduce coal losses. Highwall losses, top-of-coal losses, and coal edge losses were identified as the major areas of coal loss at Klipspruit. These losses were mostly attributed to the drilling and blasting practises of the pre-split, interburden waste, and the coal seams. Recommendations include re-visiting the current pre-split design and the tolerances adopted for the interburden and coal seam drilling and blasting design. It is furthermore recommended that Klipspruit implement a continuous improvement plan for the drilling and blasting and refresher training for the blasting crew and operators.

Jun 10, 2024

By S. Moolla, R. Lynch, S. Brijraj

A reliable method to locate microseismic evets is an important objective for routine mine seismic monitoring. We developed an algorithm that can automatically and reliably locate an event from a single uniaxial trace. Signals created by microseismic events are recorded as seismograms that consist of direct P- and S-waves as well as the waves reflected off the underground excavations. We take advantage of the extra complexity these reflections introduce as they make the signal more unique. In our investigation we cross-correlated unaltered synthetic seismograms against trial waveforms created from a linear combination of appropriate waveforms from a library of numerically calculated strain Green’s tensors. We use a single uniaxial synthetic seismogram to invert for the source location, six moment tensor components, and frequency. The resulting cost functions are constructed as maximal correlations at each node in the mine grid through the true source x-planes. This function is maximized by differential evolution to simultaneously yield the source parameters. Sensitivity tests such as shifting the mine plans and altering the background velocities of the media are investigated to test the robustness of the method. We contaminate the data with 40% white noise to test the resolution against simulated real recorded seismograms. The method is demonstrated using synthetic data calculated with a realistic underground 3D velocity model.

Jun 10, 2024