By Liming Wang

One of the steps in the extractive metallurgy of lead is a refining process called drossing. Hot dross is mixture of impurity compounds that form on the surface during the cooling of lead blast furnace bullion, and in Missouri, the main impurities are copper and sulfur. The slow cooling of bullion throws out of solution all other minor impurity elements (or their compounds) which are much less soluble at lower temperatures (mainly nickel, arsenic, iron, and zinc). The transfer of bullion from the blast furnace to the refinery and the subsequent hot drossing step cause fugitive emission of lead-containing fume and dust, which creates a plant hygiene problem. One cause of the emissions is the high vapor pressure of lead and its compounds during transmission of = 1000 °C bullion to the drossing kettle. Another cause is the lifting of dross dust during manual skimming of dross. The environmental problems associated with the traditional hot drossing process provided an incentive to investigate a new drossing process that avoids contact between plant air and hot bullion or dross. A key aspect of the process development was a detailed mineralogical examination of dross from two different bullions. The bullion samples were cooled at different rates, and the dross filtered out and examined. The morphology, phase identification, and composition of the dross was examined by optical and SEM microscopy. The principal dross phases were copper and cuprous sulfide, galena, a complex sulfide containing copper, nickel and lead, and speiss (containing nickel, cobalt, iron, copper, lead, and arsenic compounds). The copper was acicular, with nickel and arsenic in solid solution. The cuprous sulfide was largely digenite in a granular or dendritic form. A substantial part of the dross was solidified matte with a eutectic microstructure, consisting mainly of CU2S and PbS. Small particles (some of which had a eutectic microstructure) never floated to the surface of the lead during the slowest cooling rate, thus indicating that flotation of tiny matte droplets and dross crystals is exceedingly slow. The success in separating dross and lead by centrifugal filtration suggests its application in industry as a replacement for traditional hot drossing.

Jan 1, 1995

By J. Brent Hiskey

Recently basic concepts of semiconductor electrochemistry and solid-state electronic structure theory have been applied to the dissolution of mineral electrodes. In this paper, fundamental aspects of semiconductor electro- chemistry and interfacial charge-transfer processes are reviewed. Information regarding the electronic and semiconductor properties of chalcopyrite is summarized. The electrochemical response of chalcopyrite in acidic solution is analyzed in terms of initial dissolution processes. The initial charge- transfer reaction involves the consumption of holes. It has been shorn that Fermi level pinning is consistent with observed electrochemical and dissolution behavior. Semiconductor electrochemistry has proved helpful in explaining the formation of intermediate surface films produced during the initial stages of chalcopyrite dissolution

Jan 1, 1993

By James P. Bennett

EAF slag chemistry and its control have been recognized as important in producing quality steel at a low price for a number of decades_ EAF steel producers make lime and dolomite additions to furnaces, controlling the CIS ratios and sulfur pickup from the steel. Existing phase diagram data at 1600°C for CaO, MgO, FeO, SiO2, and Al2O3 was used to write a computer model optimizing slag chemistry for slag foaming and reduced refractory wear. The model, its development, and its use in an industrial steelmaking environment will be discussed along with how the model can improve energy efficiency. The importance of EAF mass balance to account for critical materials like Si in scrap and refractory wear using the model will also be emphasized_

Jan 1, 2003

By V. I. Lakshmanan

Wastes when produced can be reused or recycled prior to disposal. Industries that cause environmental concerns during manufacturing include primary materials and primary metals. Pollution prevention mechanisms to achieve waste reduction require new separation, reclamation, control and process simulation technologies. Substituting recyclables for virgin resources will reduce energy use, water pollution, air pollution, water use and mining wastes. Shrinking landfill space will spur new technologies for waste treatment and recycling. These situations hence offer opportunities for innovative flowsheets with appropriate separation technologies. Development of innovative flowsheets to treat recyclables offer unique opportunities for process/product development, obtain green products and hence market advantage. The paper will illustrate with selected innovative flowsheets to treat recyclables.

Jan 1, 1996

By Guanghui Li, Xuling Chen, Zhiyun Ji, Min Gan, Tao Jiang, Xiaohui Fan, Zhiyuan Yu

With the increase of proportion of biochar(without modified) replacing coke breeze, the physical strength of sinter decreases due to the faster burning speed of biochar. An investigation upon passivating biochar with boric acid was then conducted to strengthen sintering in this paper. A layer of thin film of B2O3 distributed in the surface of biochar was observed, which could reduce the contact between reaction gas and biochar. So the burning speed of biochar was decreased properly after passivation, and the combustion efficiency increased due to the inhibition of carbon gasification. The comprehensive effects of above changes could increase the maximum temperature of sintering bed, which facilitated to the mineralization of sintering mixtures. Eventually sintering indices got reinforced. Thus the indices of sinter as applying 40% passivated biochar were comparable with that of 100% coke breeze.

Jan 1, 2015

By Bhagyadhar Bhoi, Chitta Ranjan Mishra, Hara Prasanna Mishra

"In the Sukinda Valley of Orissa, India, the total quantity of nickel ore reserves comprising of both lateritic and chromite over burden(COB) have been estimated at around 231 million tonnes containing 0.3 to 0.9% Ni. While mining of one tonne of Chromite ore, around 6-7 tonnes of chromite over burden are removed. These overburden materials are disposed as waste materials, which causes lot of environmental hazards and ecological imbalance. India imports a large amount of nickel and ferro-nickel to meet its growing demands in various sectors. For import substitutions, efforts have been made to produced ferro-nickel from the lean deposits of nickel bearing lateritic ores/ chromite over burden materials by reduction roasting followed by magnetic separation and then the nickel rich magnetic fraction is smelted to produce ferro-nickel. It has been possible to produce ferro-nickel of grade varying from 4-25% nickel.IntroductionDuring mining of chromite ore, large quantities of overburden materials are being generated. The materials amount to approximately 10 million tones per year contain around 0.3-0.9% Ni, 0.02-0.06% Co, 20-50% Fe and 4-9% Cr2O3 depending upon the location and the depth of the mine. These materials presently do not find any application for the extraction of nickel due to lack of a suitable technology. The materials are also unsuitable for ferro-nickel making because of their very high iron to nickel ratio. The country is seriously looking for a suitable technology to utilize these resources as its entire domestic requirements of nickel is met though imports. In this connection, a systematic approach has been made at the Institute of Minerals and Materials Technology, Bhubaneswar to develop a process for ferro-nickel making from this indigenous resource."

Jan 1, 2011

By P. Heald-Wetlaufer

Doubly polished sections (i.e., sections polished on both sides) allow insights into complex paragenetic relationships, the interpretation of which is essential to understanding ore-forming processes. Alternate viewing of these optically superior sections in transmitted and. reflected light facilitates the recognition and definition of growth zones in ore and gangue minerals and the interpretation of postdepositional changes, such as hydrothermal leaching and replacement. Many such observations would escape detection by conventional petrographic methods. Our procedure for preparing doubly polished sections has evolved during the past 20 years and incorporates many standard procedures. Studies from such diverse districts as Creede, Colorado, Hokuroku, Japan, and the Upper Mississippi Valley zinc-lead district, southwestern Wisconsin, demonstrate the value of observations from doubly polished sections in constructing genetic models. The advent of doubly polished sections represents a major advance in the study of ore deposits and they should be a standard tool in every ore petrology laboratory.

Jan 1, 1982

By R. W. Lawrence

A method by which it is possible at an oxidation potential below 680 mV SHE to achieve quantitative conversion of sulphide sulphur to elemental sulphur instead of sulphate in a biological leach of chalcopyrite and bornite has been investigated. The process chemistry, biological phenomena and process flowsheet options are discussed. Several copper concentrates have been evaluated and have been found to be amenable to th process. Results to study the progression of chalcopyrite decomposition during the leach are presented and mineralogical factors affecting the requirement for silver addition are discussed. A chloride addition method for improving silver recovery is described. The results of a small scale continuous leach test have demonstrated that continuous operation can be carried out with high copper extraction and stoichiometric conversion of sulphide sulphur to elemental sulphur.

Jan 1, 1985

By Andrew Case

The Port Nickel facility in Braithwaite, Louisiana, is known for pioneering hydrometallurgical processes for the 'separation and recovery of nickel, cobalt and copper. Ten years ago, in 1985, a new CRI-MET process for the recovery of molybdenum, vanadium, nickel, cobalt and alumina from spent catalysts was developed and implemented. Spent- catalysts from the petroleum industry consietute the majority of feed. These are not only a valuable-source of metals, but due to EPA regulations are frequently classified as hazardous under RCRA. Molybdenum and vanadium are selectively leached in an oxidative hydrothermal step. Alumina is then extracted in a caustic digestive leach. The unique technology produces four primary commercial products l molybdenum trioxide, vanadium oxide, aluminum trihydrate and nickel-cobalt concentrate. This paper discusses the process, modifications. during ten years of operation, and the relationship of these modifications to the future of the catalyst recycling business.

Jan 1, 1995

By Patrick R. Taylor

Sub-micron sized boron carbide powders have been synthesized in a non-transferred arc thermal plasma reactor. Precursors for this synthesis are boric acid or boron oxide powders and methane. The powders produced were characterized in terms of size, shape and purity. Methods to increase the purity of the product were evaluated and included hot water leaching to remove unreacted oxides and controlled temperature, air roasting to remove excess carbon. Theoretical results are also presented on the thermodynamics and mechanisms of the synthesis reactions.

Jan 1, 1994

By J. L. Johnson

Remediation of small-arms firing ranges is being investigated by the Naval Civil Engineering Laboratory and the U.S. Bureau of Mines. Scheduled closures of military installations, as well as the management of active ranges, require the development of methodologies for heavy metals removal to prevent their entering the surrounding environment. The impact berms contain high concentrations of metals, and the soil and vegetation surrounding the berms were found to have slightly elevated levels. The heavy metals characterized are in the form of whole bullets, a wide size distribution of free fragments, smeared lead on the surface of the soil grains, and very finely attached particles. Gravity beneficiation can remove liberated metal contamination effectively. Weak acetic acid leaching shows promise in lowering the final metal contamination to allow the soil to pass the Environmental Protection Agency's (EPA) Toxicity Characteristic Leaching Procedure (TCLP) criteria.

Jan 1, 1991

By Dao Su, Ganghua Fu, Xuling Chen, Yufeng Guo, Min Gan, Tao Jiang, Xiaohui Fan

"The sinter quantity and quality of limonite in the magnetite and hematite sintering models were studied and compared. For the sintering of magnetite, the results showed that the increase of limonite improved the permeability of sinter mixture, increased the sinter quantity and quality. The sinter strength and productivity were decreased when the proportion of limonite exceeded 50%. The appropriate proportion of limonite was 40%-50%. For the sintering of hematite, the sinter quantity and quality were first maintained at the same level thereafter declined, more obviously when the proportion of limonite exceeded 40%. The amount of calcium ferrite increased whose shape changed from acicular to leaflike and block gradually with the proportion of limonite increased from 0% to 80%.IntroductionWith the fierce competition of domestic and overseas iron markets in the twenty-first century, cheap ores such as limonite are used to be sintering raw materials to cut the costs of sinter and pig iron for steel making, and boosts the competitiveness of steel companies [1, 2]. In addition, as the reserve volume of hematite of high grade is reducing year by year, the usage amount of limonite in sintering are expanding in major domestic and international sintering plant [3, 4]. Sintering can be divided into two types, majoring in concentrates and fine ores, according to the different types of raw materials. The sintering characteristics of limonite in the two types above have been studied and compared in this paper, which makes a significant sense for the research of limonite sintering properties and guidance of ore proportioning in sintering plants."

Jan 1, 2012

By Joseph Bloch

The hydriding of bulk metals and alloys is a gas-solid reaction in which a hydride product layer is initially nucleated adjacent to the gas-solid interface and continues to grow until a complete transformation of the parent (a) phase into the hydride phase. The combination of measurements of the overall hydriding kinetics of samples having defined shapes and dimensions, together with examinations of partially hydrided samples, enables the presentation of the reaction rate in terms of an appropriate reaction model. A common and important type of topochemical development of the hydride in bulk metals and alloys involves a hydride layer formed on the metallic surface. The continuity of the layer can affect the reaction rate. The rate of hydrogen absorption in a sample, in the presence of a hydride layer, is usually analyzed using a model combining several sequential steps in which the hydrogen is transferred from the gas phase into the reaction site. Coupling the flux equations across the layer under proper steady state conditions, results in a complex rate equation in which the steady state rate of hydrogen absorption (proportional to the hydride layer velocity) is expressed in terms of the pressure, temperature, the rate constants of the sequential steps and the critical concentrations of hydrogen in the hydride. Generally, the rate constants of the individual microscopic processes are comparable in magnitude, so that the overall rate is not controlled by any of the specific sequential steps. However, there are two limit cases related to the first stage, the adsorption, for which the general rate equation is much simpler, namely, the fast and the slow adsorption approximations. Using this limit cases, equations are derived for the steady state hydriding rate of a given system. These equations provide means to anticipate the pressure dependence of the steady state absorption rate under low pressures, close to Peq and under very high pressures. At the low pressure regime both the fast and slow absorption cases yield linear pressure dependence. For the very high pressure range, it is found that the rate become independent of the applied pressure. The rate is given then by a combination of the individual rate constants of the system and the critical hydrogen concentrations. The model is shown to apply in several real cases, such as ZrCo, LaNi5 and titanium.

Jan 1, 2002

By A. Jakobsson

Studies of the rate of interdissolution in oxide systems in the solid state are of importance in materials processing through the powder-metallurgical route. As there is a need for following the rate of the such reactions continuously, a new method based on high temperature X-ray diffraction was developed. Mechanical mixtures of the oxides were placed in a high-temperature X-ray diffraction unit and the changes in the intensity and position of the peaks with highest intensity for both the components were followed as functions of time. A suitable theoretical model has been developed in order to interpret the experimental data and evaluate the diffusion coefficients. The method was applied in the case of the system MgO-NiO. The results obtained are compared with those obtained by another new method, based on solid-state galvanic cell technique with calcia stabilized zirconia electrolyte, developed in the Department of Theoretical Metallurgy. The advantage of the present techniques to monitor the progress of the reaction continuously make them suitable for computer control of such processes.

Jan 1, 1995

By Jerold L. Johnson

Remediation of small-arms firing ranges is being investigated by the Naval Civil Engineering Laboratory and the U.S. Bureau of Mines. Scheduled closures of military installations, as well as the management of active ranges, require the development of methodologies for heavy metals removal to prevent their entering the surrounding environment. The impact berms contain high concentrations of metals, and the soil and vegetation surrounding the berms were found to have slightly elevated levels. The heavy metals characterized are in the form of whole bullets, a wide size distribution of free fragments, smeared lead on the surface of the soil grains, and very finely attached particles. Gravity beneficiation can remove liberated metal contamination effectively. Weak acetic acid leaching shows promise in lowering the final metal contamination to allow the ,soil to pass the Environmental Protection Agency's (EPA) Toxicity Characteristic Leaching Procedure (TCLP) criteria.

Jan 1, 1993

By Gary K. Elliott

Many industrial processes generate hot waste gases which contain particulate pollutants. Conventional clean-up techniques suffer limitations either because collection efficiency is low or because the gas must be cooled before treatment. thereby increasing costs and preventing energy recovery. The application of increasingly stringent environmental legislation to the non-ferrous metallurgical industry is presently illustrating these conventional technology limitations. Low density ceramic media allow filtration to ta,ke place at 'high temperatures and are now rapidly becoming accepted In many industries. This paper reviews experiences with a proprietary low density ceramic filter element. CerafH. It includes consideration of the structure, composition. typical operating and case studies with particular reference to non-ferrous metallurgical furnace applications.

Jan 1, 1992

By A. K. Kyllo

A study has been carried out on the dusts from Hudson Bay Mining and Smelting's Flin Flon copper smelter. The aim of the work was to determine the mechanisms of dust formation and the deportment of the various constituents. The work concentrated on the copper converters, but the electrostatic precipitators and baghouse also clean the reverberatory furnace off gas, so some mixing will have occurred. The dust composition was found to vary with distance from the furnace, and to be made up of three major components: solidified droplets, unreacted flux, and condensed particles. The solidified droplets were formed from material ejected from the converter during blowing, while the flux was blown out of the converters immediately after charging. The condensed particles contained the majority of the lead and zinc, as well as the volatile impurities. There was also a significant soluble content of the dusts, increasing with distance from the furnace. The condensed material may be separated from the remainder by a simple washing and sizing technique.

Jan 1, 1996

By Shun Myung Shin, Kang Jeong, Kyoungkeun Yoo, Jin Koo, Dong Hyo Yang, Soo Sohn

"The optimum discharging condition to dismantle the batteries without explosion was investigated to recycle the lithium primary batteries, which could be exploded by heating too much or crushing. The 3 waste lithium primary battery cells were discharged with 500 cm3 of 0.5 kmol·m-3 sulfuric acid. Fe concentration and pH increased rapidly after 3 days at 35? and after 1 day at 50?. Chromium concentration increased by 4 days at 35? and 2 day at 50?and then decreased, and nickel concentration was very low. Because Li concentration increased gradually, Li became dissolved after the dissolution of cover material. When the discharged batteries were shredded, the batteries discharged at 50°C were not exploded and those discharged during 3 days at 35°C were exploded. This result shows that the waste batteries could be stabilized within 1 day at 50°C and 4 days at 35°C. Introduction Lithium has some advantages for battery e.g. it is the lightest metals and also has the highest electrochemical potential at 3.04V[1]. For over thirty years lithium primary batteries became famous for their performance in various applications such as IT, medical, and military[2,3]. They gained a reputation for their long shelf life, constant voltage, wide operating temperature range, and low self-discharge characteristics[3-5]. World primary lithium battery market was expected to grow from $820.6 million in 2003 to $1,1355.3 million in 2010 (http://www.frost.com, Frost & Sullivan)[2-4]. The lithium primary batteries have very various sizes and components. Lithium batteries are made with lithium metal as anode active material and non-aqueous solvent as electrolyte. As cathode active material, various kinds of materials were used such as manganese dioxide (nominal voltage, 3.5V), thionyl chloride (3.6V), and carbon monofluoride (3.0V). In Korea, 50 % of the spent lithium primary batteries must be recycled because spent lithium primary batteries have been listed in EPR (Extended Producer Responsibility) of the enforcement degree of the act on the promotion of saving and recycling of resources. However, the batteries have been landfilled since there is no economic method to recycle the batteries in Korea[2,3]. When the batteries were heated too much, charged, pierced, over discharged, or short-circuited, the batteries explode because lithium reacts violently with water or air and because contents such as lithium, electrolyte, and sulfur become flammable by high temperature[4]. Therefore, it is so difficult to recycle safely the spent lithium primary batteries."

Jan 1, 2008

By Richard D. Hagni

Polished sections of pyrometallurgical intermediate products from a simulated commercial flash furnace were examined by reflected light microscopy, scanning electron microscopy-energy dispersive spectrometry and electron backscatter analysis, and microprobe analysis for phase and textural relationships. The smelter feed is a copper concentrate from a porphyry copper deposit. The concentrate consists primarily of chalcopyrite, bornite and pyrite with smaller amounts of covellite, chalcocite, molybdenite, magnetite, galena, and sphalerite. The flash furnace reactions for pyrite and chalcopyrite can be observed by reflected light microscopy. Reacted angular particles of pyrite exhibit successive rims of fibrous pyrrhotite and hematite or magnetite. Reacted angular chalcopyrite particles show successive rims of bornite, digenite, and chalcocite. Spherical particles, formed by the complete melting of former pyrite particles, consist of variable amounts of granular pyrrhotite with magnetite rims and minor hematite. Spherical particles, formed by the complete melting of former chalcopyrite particles, exhibit exsolution intergrowths with varying proportions of intermediate solid solution, bornite, digenite, and chalcocite and have rims of hematite, magnetite, and copper-iron spinel. Sphalerite and molybdenite do not show evident mineralogical reactions.

Jan 1, 1987

By lchiro Aoi, Hideo Nakae, Makoto Yoshida, Makoto Ishino

"The influence 6f gravity on the microstructure of unidirectionally solidified Cu-Pb monotectic, Ag-Si and Fe-C eutectic alloys is studied. In order to examine the influence of gravity in a lg environment, both the upward (opposite to direction of gravity) and downward (direction of gravity) unidirectional solidifications are carried out. The results are as follows: (1) For the upward solidified Ag-Si eutectic alloy, the eutectic Si continuously grows. On the other hand, in the downward solidified Ag-Si alloy, the Si grows discontinuously and disperses into the ex-Ag matrix. (2) No morphological difference in the eutectic growth is observed between the upward and downward solidified Fe-C eutectic alloys. (3) In the case of the upward solidified Cu-Pb monotectic alloy, a banded structure, which consists of Pb-rich layers and Cu-rich layers, is observed. However, such a banded structure -is not observed in the downward specimen. (4) The banded structure is not found in the upward solidified Cu-Pb-0.05 mass % Al and Cu-Pb-0.1 mass % Al alloys. In the Cu-Pb-0.05 mass% Al alloy, a fibrous -L 2 phase grows continuously parallel to the growth direction at low growth rate. Only 500 mass ppm addition of aluminum induces the morphological change of the monotectic L2 phase.IntroductionThe influence of gravity on the solidification of eutectic and monotectic alloys has been investigated in microgravity environments [l-9]. The purpose of these studies was to obtain a homogeneous microstructure of eutectic or monotectic alloys, most of which alloys tend to solidify with macro-segregation under gravity. However, in most of the previous experiments, e.g., in free fall systems, in aircraft or in space laboratories, the growth rate was too high to realize a planar solid/liquid interface. This would be due to the limited time for solidification. Thus, it was difficult to examine the influence of gravity on the planar coupled growth of the eutectic or monotectic alloy. In this study, both the downward U.D.S. (unidirectional solidification by gravity) and upward U.D.S. (opposite direction to gravity) are carried out in order to examine the influence of gravity on the coupled growth in a lg environment [l0, 11]. In the case of the downward U.D.S. using the current Bridgman method, the molten alloy must be confined between the crucible and the solid."

Jan 1, 2000