By K. Tangri, M. Chaturvedi

The addition of 0.5 wt pct Cu to Zr-2.5 Cb alloy increases the as -quenched hardness of the hexagonal martensitic a' phase, produced by water-quenching bccß-Zr phase, by about 35 pct. This strengthening has been attributed to the solid -solution hardening of the matrix. On aging ternary martensite, a' phase reverts to equilibrium a and Zr2Cu and ß-Cb precipitate out, mainly at the twin and grain boundaries, causing a secondary hardening of the matrix. COLD-worked Zircaloy-2 pressure tubes have been in use in power reactors for a considerable period of time. The search for a better material led to the development of Zr-2.5 wt pct Cb alloy which in the quench-aged condition develops 50 pct more strength than that of cold-worked Zircaloy-2, however, its corrosion resistance in water and steam in the temperature range of 316" to 400°C, in absence of neutron flux, is inferior to that of zircaloy-2.' Work carried out by Ells et al.1 and Dalgaard2 has shown that the corrosion properties of Zr-2.5 wt pct Cb alloy can be considerably improved by the ternary addition of 0.5 wt pct Cu. This paper is concerned with the effect of 0.5 wt pct Cu on the formation of martensitic a and its aging characteristics in a Zr-2.5 wt pct Cb alloy. MATERIALS AND EXPERIMENTAL TECHNIQUES Zr-2.5 Cb-0.5 Cu (referred to as the ternary alloy) and Zr-2.5 Cb (referred to as the binary alloy) alloys, supplied by the Chalk River Nuclear Laboratories of the AECL were used. The detailed chemical analysis is given in Table I. Cold rolling and swagging with frequent intermediate anneal of 1000°C were used for the initial fabrication of the alloys. All the heat treatments were carried out after the specimens were wrapped in zirconium foils and encapsulated in silica tubes under a vacuum of 5 x 10-6 mm of Hg. For optical metallography and hardness measurements specimens were mechanically and then chemically polished in a 45 pct HNOj, 45 pct HzO, and 10 pct HF solution. Hardness was measured on a Vickers hardness tester using a 10-kg load. For each specimen at least fifteen indentations were made in order to obtain a representative value. The phase identification and structural analysis were carried out using X-rays and electron diffraction techniques. Wires of 1.5 mm diam reduced to 0.12 mm diam by chemical etching were used for making Debye-Scherrer powder patterns using Cu Ka radiation in a 114.6 mm diam camera. Carbon extraction replicas were prepared by etching the specimens, after depositing a layer of carbon on the metallographic specimen, in one part HF and thirty parts ethyl alcohol. Thin films were prepared by electropolishing heat-treated 3/4 by 1/2 by 0.005 in. thick strips using a modified Bollman-Window technique. The 10 pct perchloric acid-90 pct methyl alcohol bath was kept at -50°C and polishing was done at 5 to 10 V. The thinned specimens were washed in ethyl alcohol at -30º to -40°C and dried between filter papers. Replicas and thin films were examined in a Phillips 300 G electron microscope. For resistivity measurements thin strip specimens 0.02 by 0.3 by 10.0 cm long were used. The potential leads were spot welded to the specimens in order to maintain a fixed length for the initial and the final resistivity measurements. The resistivity was measured by a Kelvin bridge in a temperature controlled room. The temperature was maintained at 72º ±1°F and the accuracy of the resistivity measurements was 0.03 µa-cm. RESULTS As-Quenched Structures. In order to produce a homogeneous matrix to study the precipitation reaction the solution-treatments of both the alloys were carried out in the -field region. From the Zr-Cb phase diagram due to Lundin and cox3 ß/a + ß phase boundary for Zr-2.5 wt pct Cb alloy is 820°C. Ells et al.1 have reported this boundary for Zr-2.5 Cb alloy containing 1100 ppm 0 to be at 920°C. Also, the addition of 0.5 wt pct Cu reduces this temperature by 50°C. Therefore, the solution-treatments were carried out at 1000°C to ensure that the alloys were in ß-phase region. The soaking time was 1 hr and the specimens were water-quenched. The as-quenched hardness of the binary alloy was 245 Vpn whereas, that of the ternary alloy was 330 Vpn. The X-ray diffraction studies indicated that the as-quenched structure of both the alloys consists of martensitic hexagonal phase a', with a c/a ratio of 1.591, and some retained ß-Zr. The presence of a' phase was further confirmed by thin film electron microscopy. Electron micrographs of typical ß-quenched structures of the ternary and the binary alloys are shown in Figs. 1 and 2, respectively. Fig. 3 shows the diffraction pattern from an area similar to that shown in Fig. 1. Although, the as-quenched hardness of the ternary alloy is about 35 pct greater than that of the binary alloy, the structure of both the alloys seems to be the same. The matrix of both alloys is heavily twinned and shows very few dislocations. Furthermore, there is no evidence of any precipitation taking place in either of the two specimens during quenching from the solution-treatment temperature. Aging Behavior of Martensitic a'. The aging kinetics of the ternary alloy were followed by resistivity and hardness measurements. The as-quenched values

Jan 1, 1970

By J. J. Gilman, T. A. Read

S URFACE effects in the cleavage of brittle crystals have been known for some oftime,1, 2 but our knowledge of surface effects in the plastic deformation of crystals is of relatively recent origin. In 1936, Roscoe9 eported his observations comparing oxidized and clean cadmium crystals. He found that cadmium crystals 1/2 mm in diam when covered by an oxide film less than 1200 atoms thick had critical shear stresses about twice those for clean crystals. This effect is anomalous in that it cannot be caused by the inherent shear strength of a normal oxide film. Either an interaction between the film and the crystal causes the large increase in strength, or the oxide film has an abnormal mechanical strength. Several authors since Roscoe have studied surface effects in crystal plasticity. A complete review of the literature will not be presented, but most of the results may be summarized as follows: 1—The critical shear stress for slip is increased markedly by very thin oxide films on zinc4 and cadmium crystals;" ' also, the entire stress-strain curve is raised by an oxide coating;3,4 both effects increase with decreasing specimen radius. 2—Surface active substances such as oleic acid destroy the hardening effect of oxide films.4, 6-8 The time required for the reduction of the hardening effect to begin increases with the viscosity of the solvent4~ 3—There has been dispute in recent years about the effects of surface active substances themselves on plastic deformation. Rehbinder, Lichtmann, and Maslenikov9 state that surface active substances reduce the strength of metal monocrystals markedly and increase the number of slip lines per unit length at a given strain. The effect varies with orientation for tin crystals being smallest for x, = 0, largest for x, = 45", and intermediate as x, + 90°.10 Several workers claim to have disproved the results of Rehbinder')"." but Rehbinder and Lichtmann9 have defended themselves and Masing with his collaborators" has confirmed some of Rehbinder's results. 4—Immersion of metal specimens in electrolytes such as sodium chloride reduces their strength12,13' and subsequent cathodic polarization increases the strength reduction. For noble metals, the strength reduction occurs for both anodic and cathodic polarization," increasing with increasing polarizing voltage. 5—Electroplated copper coatings effect the creep rates of zinc monocrystals. Poly crystals are not affected." 6—Immersion in dilute acid destroys the hardening effect of an hydroxide film. When an acid solution is applied to a steadily creeping crystal, the creep rate jumps to a very high value and then drops gradually to a steady value which is higher than the initial steady rate.*' " If the hydroxide film to be removed is very thin (about 100A thick), the creep rate does not change measurably, but a small rapid strain-increment is observed when dilute acid is applied." 7—Crystal plasticity depends on specimen dimensions. This was observed by Lichtmann and Ven-stroml" for monocrystalline tin and by Andrade and Kennedy" for polycrystalline lead. 8—Immerson of copper crystals in mercury has no effect on their stress-strain curves.'" 9—Bombardment of creeping cadmium crystals with a particles which penetrate the surface to only 0.005 mm may increase their creep rates as much as five times.''' The experiments which will be described in this paper pertain to: (a) the effect of a crystal's shape on its plastic deformation, and (b) the effect of metallic surface films on plastic deformation. For the work pertaining to (a), crystals of zinc, tin, and lead were grown which had various shapes. These were tested in simple tension. Macroscopic rotations about the tension axis which are unpredicted by the classical theory of slip were observed, and serrated edges were observed in tin crystals. For the work pertaining to (b), the effects of evaporated and electrodeposited films of copper, nickel, gold, and zinc on the mechanical properties of zinc, tin, and lead crystals were determined. The films influenced both slip and twinning of the crystals in creep and tensile tests. Experimental Details Chemically pure zinc, tin, and lead were used in this investigation. The zinc was 99.999t pct pure;

Jan 1, 1953

By R. Taggart, D. H. Polonis, W. C. Gallaugher

In the Ti-Cu system, the a' phase can be produced over a wide range of alloy composition witJwut the retention of measurable amounts of the ß or ? phases. This paper reports on the decomposition of this hexagonal martensite phase front the standpoint of solute corzcentratiorz, tempering temperature, and coherency strain condition. The mechanism of precipitation during tempering comprises localized precipitation which is followed by discontinuous precipitation if sufficient coherency strains are present. The localized precipitation process in hypoeutectoid alloys is described by the generalized Johnson-hiehl equation and an activation energy of 46,000 cal per mole. In hypereutectoid alloys the corresponcEing activation energy is 51,000 cal per mole. The rate-controlling process has been proposed as the difision of copper along a' platelet interfnces. SEVERAL investigations have been reported concerning the kinetics of decomposition of the mar-tensitic a' phase in titanium binary alloys.' In the Ti-Mo system,' two modes of a' decomposition have been observed in the presence of /3 phase; one of these involves the precipitation of fine a from a', and the other involves diffusion across the a'-ß interface. In studies of the Ti-Cr system, Rostoker2 did not detect the formation of TiCr2 during tempering. In Ti-Ni alloys,3 the intermediate phase Ti2Ni has been found to precipitate directly from a' along the interfaces between plates. With the exception of the study of Ti-Ni alloys the previous investigations of tempering phenomena in substitutional martensites are mainly qualitative and do not present a detailed description of the precipitation processes. The following limitations restrict the correlation of the microstruc-tural processes and reaction kinetics during tempering in most binary-alloy systems. 1) A mixture of at least two phases characterizes the constitution of quenched alloys. 2) Difficulties have been encountered in obtaining uniform structures throughout quenched samples. 3) The reaction products, and in particular their morphology. have not been clearly resolved. 4) The martensitic a' phase forms over only a limited composition range for most titanium-base binary alloys. Gomez and polonis4 showed that the Ti-Cu system provides an excellent basis for investigating the tempering of a' over a range of composition without the complication of retained P or the transition w phase. In the present work the effects of solute concentration, tempering temperature, and coherency strain conditions are considered with reference to the over-all precipitation process in quenched alloys of the Ti-Cu system. Both microstructural observations and kinetic data are correlated to define the rate-controlling processes which govern the observed localized and discontinuous precipitation reactions. An earlier paper5 was devoted to a discussion of the modes of heterogeneous nucleation of Ti2Cu from the martensitic a' structure. The present paper will therefore emphasize the progress of the tempering reaction beyond the initial stages. EXPERIMENTAL METHODS The Ti-Cu alloys for this study were prepared by conventional arc-melting procedures. Chemical analysis revealed that the alloy buttons contained approximately 0.02 wt pct 0, 0.04 wt pct N, and within 0.1 wt pct of the intended copper concentration. The progress of the tempering reaction was followed by means of electrical-resistance measurements utilizing a Kelvin double bridge, microhard-ness readings with a 400-g load, and X-ray dif-fractometry patterns to reveal line-broadening effects. Metallographic specimens examined at magnifications greater than X1000 were shadowed with germanium to reveal fine structural details. Direct carbon replicas were prepared for the electron-microscopy studies. EXPERIMENTAL RESULTS Property Changes. The changes of microhardness that accompany the precipitation of Ti2Cu from a' are shown in Figs. 1 and 2. As the solute concentration increases the peak hardness, for a given tempering temperature, increases. In alloys of given composition the time to reach the peak hardness agreed with the time to attain maximum X-ray diffraction peak breadth, as shown in Fig. 3. The maximum hardness and the maximum line breadth increased with lower tempering temperatures, and the time to reach the maximum also increased. The a' peaks broadened during the initial stages of tem-

Jan 1, 1965

By J. B. Newkirk, W. G. Martin

Oxidized cobalt powder is known to have a magnetic hysteresis loop which is asymmetric with respect to the magnetization axis. The experiment described herein shows that the orientation relationship between the basal plane of hexagonal cobalt and the oxide which forms upon it at 400°C is {111}ux//{100.1 }co <110>ux//<11.O> This orientation relationship allows a magnetic interaction between the antiferromagnetic oxide and the ferromagnetic substrate which could account for the offset hysteresis loop. Oxidized nickel powder has a symmetrical hysteresis loop and so is apparently not influenced by any magnetic interaction between metal and oxide. The orientation of the oxide (cubic) was found to be identical with that of the nickel substrate when the oxide forms on a polished surface parallel with {111} Ni. IN 1956 W. H. Meiklejohn and C. P. Bean discovered that fine particles of cobalt which had been prepared in a certain way have a magnetic hysteresis loop which in a strong field is asymmetric relative to the magnetization axis.&apos; The cobalt powder exhibited this unusual magnetic property only after it had been oxidized in air or oxygen; it lost the shifted hysteresis loop when the oxide was reduced in hydrogen. X-ray and neutron diffraction&apos; experiments showed the presence of cobaltous oxide (COO) and hexagonal cobalt in samples exhibiting the biased hysteresis loop and specifically showed no indication of any other compound with the exception of mercuric oxide.* The magnetic hysteresis loop becomes symmetrical above the Nee1 temperature (paramagnetic state) of COO. Therefore, it was concluded that the anomalous magnetic behavior is associated with the influence of cobaltous oxide upon the metallic cobalt. It has been proposed that crystallographic coherency may exist between the cobalt and a plane of some antiferromagnetic material which has unbalanced spin distribution and sufficient magnetic anisotropy to hold its spin in the direction which existed when the specimen was cooled. COO has these properties. Therefore, Roth&apos; has suggested that cobaltous oxide may form with a {111} plane parallel and coherent with the basal plane of the hexagonal cobalt metal and proposed that, as consequence of the antiferromagnetic interaction between COO and the underlying cobalt, the magnetization direction in oxidized fine Co particles may be ro-lated from the easy c-direction.2 Such a relationship, he proposed, would explain the observed magnetic effect in oxidized cobalt powder. The main purpose of this study was to determine the orientation relationship, if any, between the basal plane of cobalt and the oxide which forms upon it. Attempts to produce a film of COO which was strong enough to be handled were not successful. However we did succeed in making a film of CoCo2O, which was strong enough to be removed from the cobalt substrate and mounted on an electron-microscope grid. Because of the close structural similarity of COO and CoCo2O, we believe the orientation relation found for CoCo2O, on cobalt probably also holds for COO on cobalt. The epitaxial relationship of NiO and Ni also was investigated. To date no shifted hysteresis loop has been observed with nickel powder. However, the similarity of atomic array in cobalt and nickel leads to the prediction that a {111} of NiO may be parallel with a (111} of nickel. Experimental Method Cobalt-Cobalt Oxide—A coarse-grained specimen of a (hexagonal) cobalt was prepared by allowing a large crystal of fee cobalt to transform slowly at 400°C. The crystal was then cut to expose a surface parallel with the basal plane. A back reflection Laue X-ray photograph showed that the 00.1 plane was within 2" of the cut surface. The surface was mechanically polished and then electro polished in 85 pet orthophosphoric acid after which the crystal was held for 30 min at 400°C in air. During this heat-treatment the surface darkened slightly due to the oxide film which formed. The film was not thick enough to give an X-ray diffraction pattern, even by a glancing-angle technique. Glancing-angle electron diffraction was not possible either, owing to the interference of the electron beam with the high magnetic fields which exist at the 00.1 surface of the cobalt. However, it was possible to make an electron-diffraction photograph of the oxide film by stripping it from the cobalt substrate using the method described later. By maintaining reference marks carefully, it was possible to preserve the orientation relationship between the stripped film and the substrate on which it was formed. The oxidized surface of the crystal was first covered with a 1 pet solution of collodion (cellulose nitrate) in amyl acetate. When the film was dry, small rectangles were scored on the surface with a needle point. The specimen was then repolished

Jan 1, 1959

By H. R. Thresh

An oscillational vis cometer has been constructed to measure the viscosity of liquid metals and alloys to 800°C. An enclosed cylindrical interface surrounds the molten sample avoiding the free surface condition found in many previous measurements. Standardization of the apparatus with mercury has verified the use of Roscoe&apos;s formula in the calculation of the viscosity. Operation of the apparatus at higher temperatures was also checked using molten lead. Extensive measurements on five different samples of zinc, of not less than 99.99 pct purity, indicate i) impurities at this level do not influence the viscosity and ii) the apparatus is capable of giving reproducible data. The variation of the viscosity ? with absolute temperature T is adequately expressed by Andrade&apos;s exponential relationship ?V1/3 = AeC/VT , where A and C are constants and V is the specific volume of the liquid. The values of A and C are given as 2.485 x 10-3 and 20.78, 2.444 x 10-3 and 88.79, and 2.169 x 10-3 and 239.8, respectively, for mercury, lead, and zinc. The error of measurement is assessed to be about 1 pct. Prefreezing phenomena in the vicinity of the freezing point of the zinc samples were found to be absent. AS part of an over-all program of research on various phases of melting and casting nonferrous alloys, a systematic study of some physical properties of liquid metals and their alloys was undertaken in the laboratories of the Physical Metallurgy Division.1,2,3 The most recent phase of this work, on zinc and some zinc-base alloys, was carried out in cooperation with the Canadian Zinc and Lead Research Committee and the International Lead-Zinc Research Organization. One of the properties investigated was viscosity and the present paper gives results on pure zinc; the second part, on the viscosity of some zinc alloys, will be reported separately. Experimental interest in the viscosity of liquid metals has virtually been confined to the past 40 years. The capillary technique was already established as the primary method for the viscosity of fluids in the vicinity of room temperature; all relevant experimental corrections were known and an absolute accuracy of 1 to 2 pct was possible. Ap- plication of the capillary method to liquid metals creates a number of exacting requirements to manipulate a smooth flow of highly reactive liquid through a fine-bore tube. Consequently, the degree of precision usually achieved in the high-temperature field rarely compares with measurements on aqueous fluids near room temperature. However, the full potential of the capillary method has yet to be explored using modern experimental techniques. As an alternative, many investigators in this field have preferred to select the oscillational method. Unfortunately, the practical advantages are somewhat offset by the inability of the hydrodynamic theory to realize a rational working formula for the calculation of the viscosity. In attempting to overcome this restriction many investigators have employed calibrational procedures, even to the extent of selecting an arbitrary formula for use with a given shaped interface. However, where calibration cannot be founded on well-established techniques, the contribution of such experiments to the general field of viscometry is questionable. A critical appraisal of the viscosity data existing for pure liquid metals reveals a somewhat discordant situation where considerable effort is still required to establish reproducible and reliable values for the low-melting point metals. The means of rectifying this situation have gradually evolved in recent years. Here, the theory of the oscillational method has undergone major advances for both the spherical and cylindrical interfaces. The basic concepts of verschaffelt4 governing the oscillation of a solid sphere in an infinite liquid have been adequately expressed by Andrade and his coworkers.5,6 Employing a hollow spherical container and a formula, which had been extensively verified by experiments on water, absolute measurements on the liquid alkali metals were obtained. The extension of this approach to the more common liquid metals has been demonstrated by culpin7 and Rothwel18 where much ingenuity was used to surmount the problem of loading the sample into the delicate sphere. Because of the elegant technique required to construct a hollow sphere, the cylindrical interface holds recognition as virtually the ideal shape. On the other hand, loss of symmetry in one plane increases the complexity of deriving a calculation of the viscosity. The contributions of Hopkins and Toye9 and Roscoe10 have markedly improved the potential use of the cylindrical interface in liquid-metal viscometry. The relatively simple experi-

Jan 1, 1965

By B. B. Rath, Hsun Hu

In wedge-shaped bicrystals of zone-refined aluminum it is observed that (111) pure tilt boundaries migrate under the driving force of their own inter-facial free energy. The boundary velocity is a power function of the driving force. The driving force exponent decreases with decreasing angle of misorien-tation. For example, at 64O°C, the exponent decreased from 4.0 for a 40 deg to 3.2 for a 16 deg tilt boundary. An evaluation of the driving force acting on the boundaries during their motion indicates that for low driv-forces, up to about 2 x l03 ergs per cu cm, the velocity is relatively independent of misorientation, whereas at higher driving forces a 40 deg tilt boundary exhibits the highest velocity. The measured activation energy for boundary migration approaches that for bulk self-diffusion at low driving forces, decreasing from 33 to 27 kcal per mole as the driving force is increased from 1 x l0 to 5 x l03 ergs per cu cm. These results are compared with current theories of grain-boundary migration. In previous experimental studies of grain boundary migration the driving force has been limited to a difference in stored energy across the boundary. This stored energy has been introduced into the crystal either by prior deformation1-3 or by grown-in lineage structure. A part of the energy stored in the deformed crystal is released by recovery either prior to or concurrently with grain boundary migration, thus introducing an uncertainty as to the magnitude of the driving force responsible for grain boundary migration. The grown-in lineage structure, though thermally stable during annealing, neither provides conditions under which different levels of energy may be stored in the imperfect crystal nor provides a control of orientation difference across the migrating boundary of a growing grain. Furthermore, because of variation in the lineage structure, it is difficult to determine accurately the energy stored in the imperfect crystal. Several investigations of grain boundary migration during normal grain growth have also suffered from difficulties in estimating the driving force because of uncertainties in the principal radii of curvature.~ In the present investigation the velocity of pure tilt boundaries in zone-refined aluminum bicrystals of selected orientation (40, 30, and 16 deg around the [Ill] tilt axis) has been measured in the absence of a dislocation density difference across the moving boundary, thus eliminating the previous experimental difficulties. The driving force for boundary migration is derived from a gradient of the total interfacial free energy of the migrating boundary in wedge-shaped bicrystals. A similar method was attempted by Bron and Machlin in a study of grain boundary migration in silver. However, they found that one of the crystals was deformed and consequently the motion of the boundary was partly due to a difference of stored energy across the boundary. The observed behavior of boundary velocities as affected by the driving force is examined in the light of the predictions of the current theories of grain boundary migration.7"10 The effect of boundary misorientation on velocity is compared with the theory of " which is based on a dislocation core model for high-angle boundaries. EXPERIMENTAL METHOD Seed-oriented bicrystals of zone-refined aluminum, 2.5 cm wide, 0.5 cm thick, and 12 cm long, containing tilt boundaries with a common (111) axis, were grown from the melt in the direction of this axis. Spectro-graphic analysis, reported earlier,&apos;&apos; indicated the purity of the crystals to be 99.999+pct. Three such bicrystals containing 16, 30, and 40 deg tilt boundaries were used. Wedge-shaped specimens were prepared from these bicrystals by spark cutting followed by electrolytic polishing. The angle of the wedge was usually 40 deg and the specimens were usually 0.25 cm thick. The intercrystalline boundary was located within 0.2 to 0.5 cm from the tip of the wedge. Fig. 1 shows a section of an oriented bicrystal containing an outline of a wedge-shaped specimen. The crystallographic directions shown in Fig. 1 represent the orientation of one of the crystals (the larger section of the bicrys-tal); the orientation of the other crystal differs only by rotation around the common [lil] axis. The parallel faces of the wedge always corresponded to the common (171) planes in both crystals, whereas the orientation of the side faces varied, depending on the misorientation angle. The bicrystal orientations were determined

Jan 1, 1970

By Fred Chappell

Pyrophyllite, a hydrous aluminum silicate, physically similar to talc, receives its name from the Greek word Pyr, for fire and phyllite, a rock or stone. Firestone refers to its first recorded use as firestones or hearthstones. Composition and Properties Pyrophyllite is an aluminum silicate A12O34SiO2H2O (alumina 28.3 pct, silica 66.7 [ ] pct, water 5.0 pct) (Table 1). Vanderbilt1 gives pH value of pyrophyllite as 5.6 to 8.4. Pyrophyllite is usually white or cream, though it may be found in shades of pale green, pale yellow, buff or light gray, and in darker shades and other colors principally due to oxidation of contained iron minerals. It is opaque to translucent in thin sections. Its hardness is 1 to 2 in the Mohs scale. Its specific gravity is 2.8 to 2.9. Its luster is pearly to dull; it is recognized chiefly by its micaceous structure and cleavage, and its soft greasy feel. Two other varieties occur, one in which there are radiated needles in the crystalline form, and there is also a massive homogeneous structure found. Fine grinding reduces pyrophyllite to fiat plates or scales but aggregates of minute foliated plates may be formed.1 Distribution of Deposits Pyrophyllite is found in metamorphic rocks throughout the world but it is only in comparatively recent years that it has assumed much commercial importance. The principal

Jan 1, 1960

By S. S. Cole, H. Sigurdson

The melting points of mixtures of titanium dioxide and other titanates have been reported to a limited extent as binary systems and some results have been reported in conjunction with silicon dioxide. The limited data indicated that a low melting zone might exist in a ternary or quarternary system of CaO-MgO-TiO2-Al2O3, since the eutectics reported in the binary systems of MgO.TiO2-TiO2, Al2O3TiO2-TiO2 and CaO.TiO2-TiO2 were of about equivalent composition of TiO2. The importance of a low melting region with a high titanium oxide value in the developing of high titanium slags is fully appreciated by metallurgists. A comprehensive study was undertaken to establish basic information on low melting titanate mixtures. Compounds in the System CaO-MgO-TiO2 -Al2O3 Preparation of the titanates of CaO, MgO and Al2O3 confirmed reported data that the following compounds could be formed under oxidizing conditions in solid state reactions: CaO.TiO2, 2MgO.TiO2, MgO.TiO2, MgO-2TiO2 and Al2O3.TiO2. Under oxidizing conditions it was not possible to react MgO with TiO2 in mol ratios higher than 1:2 without having unreacted TiO2 in the product, nor was it possible to form calcium or aluminum titanates with a higher mol ratio of CaO and A12O3 to TiO2 than 1:1. By fusing mixtures of Al2O3-TiO2 and MgO-2TiO2 together a series of solid solution products were obtained, which showed an MgO-2TiO2 X ray diffraction pattern shifted to smaller inter-planar spacings. Range of Investigation Data in the literature1 indicated that these titanates had melting points which ranged from 1645 to 1860°C. Since the purpose of the study was primarily to provide useful data for smelting titaniferous ores, the work was restricted to the zone of the system which would include the crystalline phases present in the slags. The explored limits were bounded by CaO.-TiO2-MgO.TiO2-TiO2in the base plane. The system was extended to a fourth component Al2O3-TiO2 since many titaniferous ores contain appreciable amounts of A12O3. In the quarternary system CaO-TiO2-MgOTiO2-TiO2-Al2O3TiO2, a tetrahedron was used to represent graphically the components, with one component at each point of the tetrahedron. In the base plane, mixtures were pre- pared to represent fairly uniform changes of composition over the desired range expressed on a mol percent basis. Al2O3-TiO2 was brought into the system in increments of 10 mol pct up to 40 pct. Mixtures were then made up for each of the Al2O3-TiO2 planes. The ranges employed were then represented by five planes cutting the tetrahedron at 10 mol pct Al2O3-TiO2 intervals. Choice of Equipment Although it was necessary for all smelting work to be done in a strongly reducing atmosphere, it was decided that all melting point determinations should be done under oxidizing conditions. This decision was prompted by the fact that TiO2 reduced to lower oxides in a reducing atmosphere with consequent changes in melting points. The use of a micropyrometer and a platinum strip furnace for work of this type is adequately described in the literature.2 With modifications, equipment was selected which provided a fairly rapid method of determining melting points of refractory oxides. The final assembly, which was used, consisted of a platinum strip furnace and a Leeds and Northrup disappearing filament optical pyrometer attached to a special telescope which magnified the sample about 20 diam. The furnace assembly consisted of a platinum strip 0.005 X 0.3 X 2.2 in. mounted on brass posts on a refractory base. This was enclosed in a black steel shell which had a 2-in. opening at the top for purposes of sighting the telescope. The platinum strip was in series with two 0.04 ohm nichrome resistors connected to the secondary of a 2 kw transformer which supplied 17 volts. The current to the primary was varied

Jan 1, 1950

By K. BRUCE DAVIDSON

-The North Central Texas area includes the following counties in Railroad Commission of Texas District 7-B: Brown, Callahan, Coleman, Comanche, Coryell, Eastland, Erath, Fisher, Hamilton, Haskell, Hood, Jones, Lampasas, Mills, Nolan, Palo Pinto, Parker, S

Jan 1, 1946

By G. E. Pellissier, P. H. Salmon Cox, B. G. Reisdorf

Banding that occurred in plates rolled from the early production heats of 18Ni(250) maraging steel is described and related to the segvegation of certain alloying elements (nickel, molybdenum, titanium), the extent of which was quantitatively evaluated by means of electron-microprobe analysis. The effect of banding on mechanical properties is discussed, with particular reference to observed directional differences in plane-strain fracture toughness of plates. It is shown that banding originates as interdendritic segvegation during ingot solidification and persists in some degree through normal soaking and hot reduction to plate. The results of the study showed that heating sections of small laboratory-cast ingots at 2200°F for 4 hr was sufficient to markedly reduce microsegregation and to considerably improve mechanical properties. Hot rolling of 7-in.-thick ingot sections to 1/2-in.-thick plate effected a similar reduction of microsegregation, but resulted in even greater increases in ductility and toughness than that obtained by homogenization treatment alone. DURING the past few years, considerable attention has been directed towards the low-carbon, high-alloy maraging steels and in particular towards the 18Ni-8Co-5Mo-0.4Ti alloy. The steels of this group, having an excellent combination of high strength and toughness, have a number of advantages over their more conventional medium-carbon low-alloy, quenched-and-tempered counterparts. In the annealed condition, the maraging steels are in the form of a ductile marten-site; aging at a relatively low temperature, typically 900°F for 3 hr, increases greatly the strength through the precipitation of intermetallic compounds. One problem in the early production heats of maraging steel was that the finished plate frequently displayed a banded structure. Previous work on other steels1-&apos; had established that banding in wrought products is either a direct or an indirect consequence of chemical segregation, which occurs during solidification and persists to some extent through normal thermal and mechanical treatments. For example, Smith and others: in a study of low-alloy steel, were able to correlate the severity of banding in the wrought product with the degree of interdendritic segregation of nickel and chromium in the as-cast ingot. The effect of banding on the mechanical properties of steels is usually considered to be detrimental, although there is only limited evidence to suggest that a marked improvement in properties can be obtained with less heterogeneous structures. Comparison of the longitudinal and transverse tensile properties of banded and of homogenized 4340 steel showed that only the transverse ductility was improved by homogenization, but even then the improvement was not commercially significant.&apos; Conversely, homogenization of through-the-thickness tension specimens of quenched-and-tempered steel plate, containing 1.47 pct Mn, increased the strength by as much as 10 pct and the tensile ductility by at least a factor of twos5 This improvement was related to the elimination of manganese-rich bands, which also are one of the factors responsible for cold cracking in the heat-affected zone of metal-arc welds.7 In the present study the nature and severity of banding in early commercial 18Ni(250) maraging steel plate and in laboratory-melted 18Ni(250) maraging steel plate was determined. The effects of banding on plane-strain fracture toughness and the effects of thermal homogenization treatments on the strength, tensile ductility, and toughness of 18Ni(250) maraging-steel as-cast ingots and rolled plate were evaluated. In addition, the effects of hot deformation by rolling on the mechanical properties of ingots were determined. 1) STUDIES OF BANDING IN EARLY PRODUCTION PLATE The chemical composition of the steel (A) used in this part of the investigation is shown in Table I. Banding was not clearly evident in either as-rolled or annealed* plate, but annealed and agedc** plate had a banded structure. The typical banded condition, Fig. 1, consists of layers of unetched austenite (white) and dark-etching martensite in a light-etching martensitic matrix. X-ray diffraction measurements showed that this steel contained more than 6 pct austenite. An electron-probe X-ray microanalyzer (using a focused beam of electrons) was used to determine the composition of the bands and of the material between the bands with respect to the main alloying elements— nickel, molybdenum, titanium, and cobalt. The recorded X-ray intensities were converted to concentration values with the use of a standard of similar composition. To facilitate probe positioning, all analyses were conducted on specimens that had been given a light etch. The influence of this etching on the analytical results was negligible; analyses made on the identical area before and after etching yielded essentially the same concentration values. The results of the electron-microprobe analyses at selected points revealed that the layers of austenite and adjacent dark-etching martensite contained greater amounts of nickel, molybdenum, and titanium than did the surrounding matrix, Table 11. The austenite layers

Jan 1, 1968

By E. T. Turkdogan

This is a compilation and a critical review of the data on the Fe-Ca-0 ternary system. Using the results on the reductiorz-equilibria, an oxygen potential diagram is drawn for the greater part of the system. A number of univariant systems and invariant points, not determined experimentally, are evaluated by making use of the theorem on univariant curves intersecting at an invariant point. The formation of solid solutions and ternary compounds and the crystal structures of some of the phases in the composition-diagram are given for a feu! temperatures. DURING the past thirty years there has been a continued interest in the study of the Fe-Ca-0 system. A detailed literature survey made by white1 in 1943 indicated that further work was required to clarify the phase relationships; in fact, the work carried out in the subsequent years, reviewed by Burdese2 in 1954, made a valuable contribution to a better understanding of this subject. Most of the data were obtained by the step-wise reduction of mixtures of iron oxides and calcium ferrites. However, there is some uncertainty about the phase relationships in this system, arising mainly from insufficient use of thermodynamic concepts in the construction of phase diagrams. In this paper an attempt is made to establish the invariant points from the available data. OXYGEN POTENTIAL DIAGRAM Schenck and coworkers3,4 were the early investigators who studied part of this system by the step- wise reduction method and suggested the formation of two ternary compounds, CaO.FeO.Fe2O3 and 2Ca0.5Fe0.2Fez03, the latter being referred to as point X. They also deduced from their results that the phases Y (8.74Ca0.32.5Fe0.8.74Fe2O3 and Z (2.02CaO-97.98FeO) were formed near the w?stite corner of the system. Martin and voge15 postulated the existence of the compounds CaO.9FeO and 4Ca0.3Fe3O4; the former is very close to the composition of point Z and the latter to that of CaO.FeO-Fe2O3. The most valuable contribution to the presen knowledge on this system was made by Cirilli and Burdese6-8 who showed by X-ray and chemical anal yses that there were two ternary compounds, CaO-Fe0.Fe2O3 and CaO.3FeO-FezO3; the former is the same as that suggested by Schenck et al. and the latter is close to their point X. The results of Cirilli and Burdese show that the phases Y and Z postulated by Schenk et al. are solid solutions of calcium oxide in w?stite. In most of the above-mentioned reduction-equilibria measurements carbon monoxide-carbon dioxide mixtures were used and in a few cases hydrogen-water vapor mixtures were employed. Using the

Jan 1, 1962

By J. B. Hess, R. L. Dietrich

In the mechanical twinning of magnesium on the {1012} planes the crystal-lographic deformation is such that, in the direction of the hexagonal axis [0001], twinning is possible only undef tension stress, while in the directions perpendicular to the hexagonal axis, twinning is possible only under applied compression. Thus in extruded magnesium and magnesium alloys where the extruded textures are best described as either [1010] or [1120] fibers,&apos; the basal planes are all nearly parallel to the extrusion axis and such material is susceptible to ( 1or2 ) twinning by compression in the direction of the extrusion axis. In order to explain the results of cyclic stressing in alternate tension and compression upon the tangent elastic modulus in such material, Dorn and Thomsen2 have postulated that, following twinning under applied compression, a retwinning or un-twinning occurs as a result of residual microtensile stresses immediately upon removal of the applied compressive force. Recently, Carapella and Shaw4 have used this supposition of untwinning in magnesium in discussing their results on indentation hardness and on cold drawing of MI sheet. In trying to confirm this hypothesis by suitable direct experiments, the authors have been unsuccessful in detecting any evidence whatsoever that untwinning follows the release of applied compression and are forced to conclude that this hypothesis is improbable or, at least, that the quantity of material involved is small. For the experiments, small cylindrical specimens 0.040-in. diam. X 0.120- to 0.140-in. long were etched from 0.0625-in. extruded rod. The ends of the specimens were accurately faced off parallel in a jeweler&apos;s lathe. The compression jig was simply an ordinary set of micrometer calipers with an anvil interposed between the spindle and the specimen. The anvil was free to move axially but restrained from rotating so that the rotation of the spindle would not introduce a twisting stress on the specimen. With this arrangement the compressive strains could be estimated to 0.0001 in. and X ray pinhole photographs could be taken with or without load as required. Fig I is the pattern of an uncompressed specimen of AZ3I alloy, showing the approximate [1010] extrusion fiber. The X ray beam is normal to the extrusion axis; in this position it is particularly sensitive in detecting twinning if one directs his attention to the diffraction ring from the basal plane. Since twinning on (1072 planes produced an 86" reorientation of the crystal lattice, the original basal reflections occur at the 3 and 9 o&apos;clock positions while the (0002) reflections from any twinned material will occur at the 6 and 12 o&apos;clock positions. Fig 2 shows the same specimen compressed 3.0 pct, photographed while still under load. This strain has been just enough to produce a detectible amount of twinning and the sensitivity is roughly indicated by the fact that no alterations were produced in the intensities or maxima of the other diffraction rings. A strain of

Jan 1, 1949

By H. E. Cline, D. F. Stein

A fine lamellar structure with interlamellar spacings ranging from 0.I to 3.7 was Woduced by high-speed directional solidification and used to study the interaction of dislocations with an array of bimetallic bound-am.es. The tensile flow properties were measured at elevated temperatures and the results interpreted in terms of an image force model. As the width of the plates decreases the strength increases according to a Hall-Petch relation, suggesting pile -ups. Considerable strengthening was also observed at elevated temperatures. In recent years composites containing a strong but brittle phase and a ductile but weak phase have been studied extensively in the search for a high-strength material with adequate ductility.&apos; However, the strength of these composites has been limited to a volumetric average of the strengths of the component phases. In this paper we will show that a composite made by directional solidification of a Cu-Ag eutectic has strength properties that substantially exceed the strength of either of the metals in the composite, and an explanation for this increased strength will be presented. The Cu-Ag eutectic is a near ideal material to study for several reasons. The eutectic structure is made up of alternate plates of silver-rich and copper-rich phases with the same crystal structure.2&apos;3 In addition, the mechanical and elastic properties of silver4 and copper5 are known over a wide range of temperatures and the eutectic microstructure is stable to nearly the melting point.6&apos;7 Therefore, the properties of the eu-tectic are readily comparable to various theories involving the mechanical properties of copper and silver. The experiments consisted of producing directionally solidified Ag-Cu eutectic material, determining the structure and performing tensile tests at different temperatures and strain rates. EXPERIMENTAL A) Solidification and structure. A cylindrical ingot 2.2 cm in diam and 15 cm long was prepared from 99.999 pct pure materials and cast in argon. The ingot was placed in an alumina crucible and was direc-tionally solidified at 7 x 10"4 cm per sec in a Bridg-man apparatus in argon. Metallographic examination at both ends and along the length of the ingot showed a uniform structure that consisted of fine alternate plates of silver- and copper-rich phases. The plates were aligned parallel to the growth direction, as shown in the longitudinal section, Fig. 1, and were in small randomly oriented domains of parallel plates as viewed in a transverse section, Fig. 2. Four smaller ingots 0.175 in. in diam were solidified at speeds of 2Xlo-&apos;, 4.4 xlo-&apos;, 4.4 x 10-3, and4.4x10-4 cm per sec to produce a range of lamellar spacings. Replica electron micrographs were taken to resolve the individual plates as shown in Fig. 3. The copper-and silver-rich plates in the larger ingot were about

Jan 1, 1970

By A. Kaufmann, B. Cullity, G. Bitsianes

T0 determine the bulk of the phase diagram, techniques for melting, thermal analysis, heat treatment, metallography, and X-ray diffraction that have already been described were used.&apos; It proved difficult to get definitive results for most of the alloy system because of the large number of compounds, their high melting points, and their extreme brittle-ness which made metallography difficult. The final phase diagram, essentially as shown in Fig. 1, was issued with considerable trepidation.&apos; The phase relationships at the two ends of the system were defined with satisfactory accuracy. In the central region between U,Si, and USi, there was great uncertainty concerning the melting points and even the composition of the compounds. At the uranium end of the system, it is quite clear that a eutectic exists at about 985 °C and approximately 8 or 9 atomic pct Si. The a-to-8 transformation is not appreciably altered by silicon, but the 8-to-y transformation is raised to about 795°C. There is appreciable solid solubility in y-uranium, as demonstrated by the micrographs of Fig. 2. The occurrence of the E phase was not suspected at first, since the alloys as melted and furnace cooled gave no X-ray diffraction or thermal arrest indication of it. However, suitable metallography revealed a rim around each of the compound particles as shown in Fig. 3. Heat treatment above 600°C revealed that the rim was another phase which formed by peritectoid reaction between uranium and U,Si,. This reaction proceeds slowly and it is difficult to get it to go to completion. Consequently, there is some uncertainty concerning the exact composition of P and the exact peritectoid temperature. On the basis of various metallurgical studies, it was decided that the most probable composition for t was about 23 atomic pct Si. Metallographic examination shows the closest approach to a single phase at this composition. Likewise, density and hardness measurements of heat-treated alloys shown in Figs. 9 and 10 show a change in slope at 23 pct Si. This is revealed most clearly by plotting the difference in hardness or density between chill-cast and heat- treated alloys as shown in Fig. 4. Zachariasen2 was able to index the diffraction lines of P and to determine the arrangement of the atoms in the unit cell. He concluded that the composition must be US. However, it is felt that the metallurgical studies are reliable and that Zachariasen&apos;s X-ray work does not furnish positive proof that the P phase exists exactly at the stoichiometric composition U3Si. There are many instances in alloy systems where a phase does not occur at the composition dictated by the molecular structure. It is possible that the chemical analyses used in the present work were subject to some systematic error. This seems unlikely, however, since recent work in several laboratories seems to show excess compound at 25 atomic pct Si.

Jan 1, 1958

By Frank G. Miller, Ralph A. Seban

Problems relating to thermal methods of oil recovery have been given increasing attention during the past year. The nature of the physical and chemical processes underlying thermal recovery are not yet well understood. The need for pertinent basic information is recognized generally. One of the processes involved is the transfer of heat by conduction in oil reservoir rocks containing moving reservoir fluids. This technical note deals with heat conduction in a laboratory sand column filled with a moving hydrocarbon and therefore should be contributory to the presently inadequate fund of knowledge on thc over-all subject. In an analysis of the flow of vaporiziny propane through a horizontal column of sand, one of the present author9 demonstrated correspondence between thc measured values of pressure along the length of the column and those predicted by a theory which postulated that the enthalpy of the propane was invariable along the length of the column. This postulate way implied as a deduction from the principle of conservation of energy but the details of the deduction were not given. The specific purpose of this technical note is the presentation of these details both as an adjunct to the earlier analysis and to supply some additional details on the processes involved in this type of flow. Results disclose that rates of heat transfer by conduction, in the direction of fluid motion, generally would be small for systems of the type studied. FUNDARIENrAI. ENERGY EiQUAI-[ON The principle of conservation of energy may be applied to a section of the porous material on the basis that heat transfer, like fluid flow, is possible in the x direction only. Transfer of heat in the y and z di&apos;rections is prevented by suitable insulation or by taking the medium as infinite in directions perpendicular to the x axis. For steady state heat conduction and conditions of steady fluid flow the principle of conservation of energy specifies that any reduction in the enthalpy rate increases the flow of heat in the same proportion. Stated mathematically, dH KA 87 —- = - — - — U) * dx W dx........ Lvhere is the flow of heat in the positive x W dx direction. TEMPERATURE DISTRIBUTION IN DIRECTION OF FLOW The column of sand used in the previoi~sly described research is divisible into three different flow regimes. each of which may be analyzed independently. In the entrance region the liquid approaches the saturation state. A transition region is postulated following the transverse section at which the saturation state of the liquid is attained. In this transition region gas and liquid phases are both envisioned as present, with no vaporization occurring and with fluid movement restricted to the liquid. The upstream end of the exit region is at the transverse section of the column where the fraction of the pore space occupied by gas first becomes great enough for gas flow and where vaporization of the liquid begins. Fig. 1 indicates schematicaHy the thermodynamic processes undergone hv the fluid in the three flow regimes.

Jan 1, 1956

By Michael Hoch

The phase diagrams of binary systems of some of the transition elements of Groups IV, V, and VI were used to compute the partial free energies of these elements and the free energy of formation of their Laves-type compounds. From these data, isothermal sections of ternary phase diagrams were calculated and compared with experimental results. DURING the investigation of ternary and quaternary high temperature systems formed by the transition elements of Groups IV, V and VI, the binary phase diagrams for these elements available in the literature were studied. In this study, the free energies of formation of the compounds formed in these binary systems were calculated; these values were then used to determine the general shape of the ternary and quaternary phase diagrams. Above 900°C, the transition elements of Groups IV, V, and VI are all bcc and form only Laves-type compounds in binary systems. The investigation was based on the binary phase diagrams published by Hansen.1 The Cr-Nb system was constructed from the data of Elyutin and Funke.&apos; Several unpublished phase diagrams were taken from Schmidt&apos;sLo and English&apos;sl1 compilations. THE BINARY SYSTEMS valuations of the Thermodynamic Functions. Rostokers evaluated the boundaries of the (a + b) field in Ti-base alloys with a two-constant equation. The authors&apos; interest is mainly in the center of the diagrams; therefore the miscibility gaps in the Zr-Nb, W-Cr, Ta-Zr, Ta-Hf, and Ti-W systems were used to evaluate the thermodynamic behavior of the binary systems. Lumsden&apos;s4 Equations 29.2, 32.1, and 33.1, page 287, were used for the excess integral free energy FeX, and for the excess partial free energies Fx and replaces b and b replacesP in Lumsden&apos;s notation):

Jan 1, 1962

By Robert E. Hochscheid

The subject article appears in the February, 1978, edition of Mining Engineering, and on page 190 carries the statement, "As most operators know, in a Water-Only cyclone, ability to adjust the vortex finder is quite important due to the sensitivity of this type of operations to variance in feed conditions and having to take them apart to make this adjustment is always a nuisance." Our experience as a manufacturer and supplier of Water Only cyclones does not agree with the above statement, and we offer the following brief discussion. Our company finds that the sensitivity of the Water-Only cyclone is a function of the fineness of the coal being washed, with the sensitivity to vortex finder length being greatest for coals coarser than 3/4-in. and virtually insensitive to raw coal finer than 1 mm. For coals finer than 1 mm, we find that we can use the shortest standard vortex finder in either our 10- or 15- in. Water Only cyclone without exception. For coals 5/8-in. x 1 mm ceramic vortex finders of fixed length have been satisfactory in all cases following an initial testing period in which the length was determined. Coals coarser that 5/8-in. are more sensitive to the vortex finder length, and two installations handling coals coarser than 1-in. continued to experiment with vortex finders of various lengths long after the initial startup period. For coals of all sizes, final adjustment of product quality has been achieved by determining the optimum size of apex orifice, which is accessible and readily changed, if necessary. Comments above assume no unusual change in the coal being washed or the required quality of clean coal.

Jan 1, 1979

By L. M. Howe, J. Gordon Parr, E. Saarema

THE decreasing solid solubility limit at the titanium-rich end of the Ti-Cu constitutional diagram,&apos; Fig. 1, suggests the possibility that titanium-rich alloys may be age-hardenable. However, results obtained by Holden et al. reproduced in Fig. 2 show that after quenching from 790°C the age-hardening of an alloy containing 1.7 pet Cu is very slight, while a 0.8 pet alloy decreases in hardness, during heat treatment at 400°C. It was believed possible that powder samples of alloys might show different results from the lump samples used by Holden et al., since small particles are often more sensitive to diffusion processes than larger samples. Consequently, a 1.9 pet (by weight) Cu alloy was made by the technique of levitation melting," checked for homogeneity, and filings of 48-65 Tyler screen size were cut from it for aging experiments. The filings were helium-quenched (by a technique described previously)&apos; from 790°C, sealed in vacuo in silica tubes and aged at temperatures of 400°, 450°, and 500°C. Microscopic and X-ray examinations failed to reveal any structural changes during the aging process. This is not too surprising since early stages of precipitation do not usually manifest themselves in ways that are readily detectable by metallographic methods, and the extent of precipitation on overaging a 1.9 pet alloy is very small. However, hardness readings (taken on a Bergs-man micro hardness tester, using a 25 g load applied to a diamond indenter) do show a hardness peak at each aging temperature, Fig. 3. About a dozen readings were taken on each heat treated sample; the highest reading and the lowest reading were ignored and an average taken of the remaining values. In

Jan 1, 1957

By P. A. Toynbee, D. G. Wilson

The combustion performance of sub-bituminous slack coal is greatly improved by the removal of the smaller size fractions. Screening processes are not well suited to the size separation, at 1/8 in. or 1/16 in., with coals which are normally wet, and the use of an alternative size-separation device has been investigated. It is felt that this classifier might be applied equally well to other minerals in cases such as this, where precise size limits are not essential. Coal is dropped as a curtain onto a curved metal plate, shaped rather like a ski-jump. The smaller particles, slowed up in their free fall to the plate and also by contact with the metal, leave the plate with a lower horizontal velocity; they can be separated from the larger particles by virtue of their shorter trajectory. The principle of the classifier is obvious from the diagram (see Fig. 1) which shows also the positions, relative to the curved plate, of the point of coal feed and of the dividing plate which separates the streams of coal particles. The horizontal distance between the curved plate and the dividing plate is varied in the tests. It is designated in the general case, by X. Tests were carried out using slack coal with a free moisture content higher than that expected in any commercial operation. The results given in Table I. show the percentage recovery of upgraded product, and the cumulative screen analysis of both the upgraded and reject material, for three different positions of the dividing plate. The results show, for example, that the original coal can be upgraded, with a recovery of 80%, to reduce the minus 1/8 in. frac-

Jan 1, 1965

By Thomas T., Read

IT will be recalled that when educational instruction for the mineral industry began at Freiberg, at the beginning of the eighteenth century, the original aim was to organize and systematize the procedures previously followed by young men in gaining -familiarity with the technology then in use. There must have been many other ideas current, even then, as to just what a young man needed to learn in order to become capable of assuming &apos;responsibility for the supervision and direction of such technical work. The problem in Europe was decidedly different .from that in nineteenth-century America, because some of the European mines were actually owned and operated by the governing authority and the others were supervised, regulated, and taxed by it. The American problem was the e5cient performance of technical operations; the European one was regulatory supervision. It was natural, therefore, that in the development of educational processes in Europe stress was laid on those factors which conserved and protected the interests of the state. The study of mineralogy and geology, leading to correct judgments as to the workability and value of mineral deposits; assaying, which gave the means of quantitative measurements, as did surveying; chemistry, which furnished a better basis of understanding for assaying, mineralogy, and geology; and physics and mathematics, which are the bases for the understanding and efficient use of mechanical appliances, became the core of systematic instruction, for the mineral industry. It was early recognized that men could learn more than was already known about all of these subjects and education took on that dichotomy which still characterizes it; the teaching of established knowledge to the unlearned, and that of extending of the bounds of knowledge, now loosely termed research, which after two and a half centuries of work still shows

Jan 1, 1941