Search Documents

By R. M. Brick

EDUCATIONAL benefits for veterans of World War II have largely removed one of the two former barriers to a college education for everyone, namely financial means and intellectual capacity. This latter limita¬tion has not kept privately endowed institutions from increasing 50 to 100 percent in size of student body, even after applying moderately rigid entrance standards. Growth of some land-grant universities, which cannot well exercise such restrictive judgements, has been even greater. After a weary board of admissions, subject to student, alumni, faculty, and even political pressures, has admitted double the former number of freshmen, the university's worries really begin: to find laboratory, classroom, and instructional facilities. If this were a one- or two-year problem, the answer would be simple: double up, hold night classes, particularly of laboratories, rent space, and have instructors work 24 class or contact hours a week instead of twelve (it takes usually two to three hours of outside work by the instructor for one hour in class). However, most engineering school faculty men are worn out now from four to five years of "accelerated" (frequently downward!) programs and they couldn't continue teaching in a way satisfactory to their own consciences on

Jan 1, 1947

By Louis D. Huntoon

SHORTLY after publication of the article in the July, 1924, issue Of MINING AND METALLURGY, entitled "Canada as a Gold Producer," requests were received to determine the ownership of production. Advices have also been received that considerable discussion has taken place on the same questions both in Canada and Great Britain. The author is indebted to R. H. Coates, Dominion Statistician, and George C. Bateman, Secretary, Ontario Mining Association, for the following figures and takes this opportunity of expressing his appreciation. There have been no statistics compiled as to ownership of production. Statistics were compiled as of Dec. 31, 1921 relative to the distribution of stocks, bonds and "other securi¬ties" in industrials, agriculture excepted, throughout the Dominion, and "distribution of ownership of securities issued by mining companies incorporated and operating in Ontario" for the same year. Stock registration does not necessarily represent actual ownership' as large blocks may be endorsed and not transferred; neither does registration actually represent production. When the charts are studied individually and collectively one cannot help but be impressed with the fact .that in the mineral industry of Ontario and the Dominion at large, Canadian registration predominates, the United States registration is about half that of Canada, and Great Britain is about half that of the United States. When the nickel-copper industry is excepted the British registration falls to a very low percentage. Since Dec. 31, 1921, British capital has commenced to flow into mining enterprises in Ontario and it has been already rewarded by the discovery of valuable ore deposits.

Jan 1, 1925

By A. P. Young, F. C. Holden

IN many of the early investigations of the aging of titanium alloys, it was observed that the retained beta phase could be aged to a high hardness without an apparent change in microstructure; moreover, in some alloys it was found that even a very rapid quench produced beta having an anomalously high hardness. What appeared to be hard beta phase was designated as "beta prime," to distinguish it from the softer normal retained beta phase. Frost and co-workers'.' demonstrated that the increased hardness is caused by the formation of a metastable phase, omega, which can be identified from its X-ray diffraction pattern. This reaction also has been studied by Brotzen, et a1.,3 and the structure of the omega phase has been published by Silcock, et al.," and by Austin and Doig.3 The X-ray diffraction analysis by Austin and Doig indicated that omega is low in alloy content, approaching the composition of the stable alpha. The aging process proceeds by the path Thus, overaging results in the formation of alpha and the ultimate disappearance of omega. This is accompanied by a decrease in hardness and a recovery of ductility. The present work represents a study of the aging process in a high-purity Ti-6.4 Mn alloy, in which optical and electron microscopy, X-ray diffraction, and hardness data were correlated. The specimens, 1/8-in. sections cut from 1/4-in.-diam rod, were heated in argon to a temperature just into the beta field (810°C), held for 1 hr, and water-quenched. The aging samples were heated in air for 1 hr at 300 to 500°C. The specimens were ground and mechanically polished, finishing with alternate etching and polishing on a slow-speed wheel to remove disturbed metal from the surface. The surface finally was swab-etched, rinsed with tap water, and air-dried. The etchant used was an aqueous solution containing 1 1/2 pct HF and 3 1/2 pct HNO3. This procedure is identical with that used for preparing metallographic specimens, except that the optimum degree of final etching required for electron microscopy may vary from that used for light microscopy. Metal replicas, backed with silica, were prepared from plastic strip-pings for examination with the electron microscope. Complete details of the procedures used for preparing these replicas are available elsewhere." Fig. 1 shows a comparison between the structures revealed by the electron microscope and those obtained by conventional light microscopy. Hardness and X-ray diffraction data are listed in Table I. No evidence of a second phase is apparent in the optical micrographs for the as-quenched sample, or for the specimens aged at 300 or 400°C; fine alpha particles can be seen in the specimen aged at 500°C. In the electron micrographs, visible equiaxed pocks appear in the as-quenched specimen, and, with increasing density, in the samples aged at 300 and 400°C. After aging at 500°C, the structure becomes markedly coarser and develops an oriented appearance of a second phase, coincident with the appearance of visible alpha particles in the light micrographs. These observations are confirmed by X-ray diffraction and hardness data. In these specimens, aged for 1 hr, the intensity of the omega pattern increases to a maximum at the 400°C aging temperature, corresponding to maximum hardness and the maximum density of pocks in the electron micrographs. At this point the beta phase shows a definite enrichment in Mn. At 500°C, little or no omega re-

Jan 1, 1959

By C. R. Knopp

Gas-oil relative permeability ratio is an important relationship in oil reservoir predictive calculations. A correlation has been developed from 107 gas-flood k/k tests on Venezuelan core samples. The correlating parameter is based on restored-state water saturation tests and' is applicable to both consolidated and poorly consolidated sandstone reservoirs. Data of the correlation show that there are no distinguishah1e differences between the mass-data groupings for the two c1assifications A procedure is recommended for running .sufficient relative. permeability analyses to compute a geometric mean of the sample group. The geometric mean is more representative of the total core, and probably the entire reservoir. For example, while only one in four of the k,,/k,., test curves agreed closely with the resultant correlation of this report, the geometric mean curves of the 16 suites (three samples or more). showed good agreetment ill three cases out of four. INTRODUCTION The gas-oil relative permeability ratio is an important, fundamental relationship in most oil reservoir predictive calculations. Predictive calculations are made to estimate future reservoir production characteristics and ultimate oil recovery. The k1,/k2, relationship is specifically needed to relate the surface gas-oil ratio to the reservoir oil and gas saturation, and to calculate the relative movement of these phases within the reservoir whenever some of the more complex driving mechanisms are present. Laboratory k1/k2, tests are not generally run as a routine analysis. Consequently, k1/k2 data often are not available when needed because the cost of laboratory work could not be justified or the need for such data had not been properly anticipated. When laboratory k1/k2, data are available, they are often very difficult to interpret. For example, wide divergence is sometimes shown in a family of k1,/k1, tests representative of the producing horizon in a single well. With these considerations in mind, a study was made to determine if a relationship might exist between the k1,/k2, curve and some other simple laboratory test criteria. The most probable k1/k2, curve correlation for Venezuela described in this paper is the result of the investigation. The presented correlation defines the most probable gas-flood k,,/k,, curve through the medium of air-water capillary displacement and centrifuge water saturation tests. The laboratory procedures of these tests are. relatively simple, and inexpensive; test data should be. widely available- from routine analysis. DATA AVAILABLE, LABORATORY METHODS The report correlation utilized 107 gas-Hood k1/k2, tests run on sandstone cores of Venezuelan reservoirs. Table 1 is a general tabulation of data pertinent to the tests, while Table 2 summarizes the data. Thetests include 96 from Western Venezuela and 11 from Eastern Venezuela. Eighty-two- of the 107 test samples were sandstones that varied from poorly consolidated to-unconsolidated; 25 were consolidated. The average sample porosity was 26.7 per cent and the average permeability was 1,121 md; these values typify the better sandstone reservoirs of' Venezuela. The Welge gas-flood technique,' based on fundamental Buckley-Leverett frontal displacement theory, was introduced in about 1952 and is widely accepted in the industry. The laboratory procedure is relatively simple, rapid, and can be performed on small core samples. While there have been some minor variations in sample preparation and laboratory procedure in the tests used for the correlation, these tests can be generally summarized as follows. The core sample was first sol vent-extracted and dried. Connate-water saturation was restored by the oil-flushing or evaporation-blow down methods. At the beginning of gas flood the hydrocarbon pore volume was completeiy saturated with the test oil phase. Unsteady-state gas-oil displacement then began with the injection of nitrogen or helium. while the displaced oil and gas phases were incrementally metered at the out-flow face. From the test data, the k,,/k,, curve was calculated by the Welge method.' The individual oil and gas relative permeabilities were also calculated." CORRELATING PROCEDURES In attempting to establish a basis of correlation, we found that broad mid-range sections of 105 of the 107 k,,/k,, test curves could be closely duplicated by a straight line. Only two curves did not show a degree of linearity in this region. Correlation-curve definition parameters were subsequently developed from this observation of consistent mid-range linearity. Possible correlating variables were limited to the physical properties measured on core samples that (1) were widely available as common test data and (2) could be easily and cheaply obtained through future laboratory work. The more obvious possibilities were porosity, permeability and

Jan 1, 1966

By E. J. KENNEDY

FEBRUARY 15-18 will be the outstanding dates of the month for members of the A. I. M. E., for then the 141st Meeting of the Institute is to be held in the Engineering Societies Building, at New York. What with 41 technical sessions, the Annual Business Meeting at 4 o'clock Tuesday afternoon,, two sessions of the Section and Division delegates, minor committee meetings, and the many luncheons and dinners, the Dinner-Smoker, Informal Dance, President's Reception and the Dinner-Dance, the opportunity will be limited to do- more-than cast sheep's eyes at New York's other multitudinous attrac¬tions until the meeting is over. The technical program is diverse but well organized. The sessions are almost equally divided among the four days, with ten on Monday, Tuesday, and Wednesday, and 11 on Thursday. The meeting opens Monday morning with registration. Be sure to attend to this detail. Failure to do so may have its repercussions at the meeting and throughout the year.

Jan 1, 1932

By Hugh P. Tiemann

The desirability of employing the centigrade scale for the measurement of temperatures is becoming more and more recognized in this country, particularly in view of the fact that this scale is used almost exclusively in technical papers and publications—exclusively in those published in French or German. There are, however, a large number of factories and laboratories which still employ the Fahrenheit scale. It therefore frequently becomes necessary to convert one into the other and the accompanying chart (Fig. I) has been found very convenient for this purpose. The formulas for conversion follow: (1) °F. = 9o /5+ 32 (2) oC = 5 (oF - 32 ) (1) 100° C X 9 900/5 =180 .'. 180 + 32 = 212° F. 5 (2) 5 (212° F - 32) = 5 X 180 =100o C 9 9

Jan 1, 1916

By J. B. Seabrook

The accompanying Fig 1 is a graphical scheme of intermediate accuracy for expediting interconversions of mol, weight, and volume percents. This chart consists of a family of curves of mol or atomic or volume percent plotted against weight percent, each curve in the family providing for a certain ratio of molecular or atomic weights or densities. Thus, the whole range of variations is presented in a very familiar format, and the conversion is effected simply by choosing the proper curve and reading off the required values. An entire series of conversions for a given binary system can be found by following the appropriate curve. It is interesting to examine the analytical geometry of the plots. The curves, which must fit into a square and all join at the 0 and 100 pet points, may be shown to be hyperbolas with their centers on the extension of the diagonal of the square which they intersect. Multiplying out the expression x A atomic fraction of A = y = ------ where x is the weight fraction of A, and A and B are atomic weights, we get xy+A/By- A/Bxy=x Upon rotating and translating axes and avoiding imaginaries, it is found that the angle of rotation is —45°, the origin moves upv2/2 units andv2/2(A/B+1/A/B-1) units to the right, and the standard form is Thus the curves are equilateral hyperbolas, their centers are units away from their intersection with

Jan 1, 1950

By E. J. Dulis, G. V. Smith

AS reported several years ago,' nitrogen may be taken up from the atmosphere by austenitic Cr-Ni steels during creep or creep-rupture tests. This was indicated by chemical analysis and by the appearance of a new microstructural phase, or phases, tentatively identified as chromium nitride (S), at the surface or at the intergranular cracks associated with fracture. The nitrogen pickup was observed to be dependent on time, temperature, and deformation. In a more recent investigation, a sample was obtained in which there was sufficient of the precipitate to suggest that it could be readily identified by X-ray diffraction. This sample had been taken from a 1/4 in. diam creep-rupture specimen of annealed, type 304L stainless steel of the following initial composition: C, 0.03 pct; Mn, 0.65; P, 0.010; S, 0.019; Si, 0.54; Cr, 19.50; Ni, 12.02; N, 0.031; and Al, 0.005. The specimen had ruptured after 10,470 hr at 1500°F (2000 psi). In this case nitrides were distributed across the whole section of the sample, Fig. 1. The precipitate occurred both at the grain boundaries and within the grains; the latter precipitate had in some cases the appearance of pearl-ite, and in others was distinctly Widmanstatten. Chemical analysis of the sample after test showed 0.64 pct "soluble" nitrogen (soluble in 1:1 hydrochloric acid: water) and 0.18 pct "insoluble7' nitrogen (insoluble in the hydrochloric acid solution but dissolved by fuming sulphuric acid). For identification of the precipitate by X-ray diffraction, the matrix in the surface layer of the specimen was dissolved by prolonged attack in an alcoholic solution of picric and hydrochloric acids. The appearance of the specimen surface after such etching is shown in Fig. 1c. The diffraction pattern of the surface-concentrated precipitate was obtained with a recording spectrometer in both the forward and back-reflection regions (the latter by adapting a special fixture to the conventional X-ray unit). The observed X-ray diffraction lines, Table I, show the presence of Cr,N and CrN; the agreement with interplanar spacings calculated from reported data2,3 is quite good. Since it has been suggested' that CrN dissolves only in concentrated sulphuric acid, whereas Cr2N dissolves in dilute hydrochloric or sulphuric acids, an effort was made to distinguish between the two nitrides. This proved possible, inasmuch as etching in a dilute solution of hydrochloric acid gave a sample in which microscopic examination showed that much of the Widmanstatten-pearlitic precipitate within the grains had been eaten out, leaving the grain boundary precipitate in relief, and which, when examined by X-ray diffrac-

Jan 1, 1953

By Oscar H. Hershey

COMPLAINT has been made that in the literature of economic geology the work of the "company or practical" mining geologists does not get enough attention. I propose to attempt to overcome this com¬plaint in reference to one important lead-mining district, that of the Coeur d'Alene in northern Idaho. Furthermore, I will assume that the reader is not so much interested in the geology of the district as in the methods of application used and incidents that have arisen in the work. All the important discoveries of ore in the Coeur d'Alene were made without benefit of geology. Certainly I would not claim the reputed discoverer of the Bunker Hill mine as a fellow geologist. It appears also that the mines were operated quite successfully for many years without geological specialists, though doubtless certain properties were visited at long intervals by such men as Waldemar Lindgren. It was known that the ores occur in quartzite, graywackes and slates as stated by J. R. Finlay in 1903. (TRANS., VOL. 33.) He described the ore as occurring in typical fissure veins that occupy fault-planes of indeterminate displacement. The Bunker Hill lode was based on a definite fissure with the mineralization all on the hanging-wall side, extending as far as 300 ft. from the fissure.

Jan 1, 1933

By H. Reiss

The zone-melting process in which redistribution of solute in a solid bar is effected by the passage of a molten zone is considered mathematically. Simple approximate techniques are developed for computing the manner in which redistribution occurs as molten zones continue to pass. The introduction of the "zone-melting flux" provides valuable insight into the nature of the phenomenon, as well as a central mathematical theme in terms of which the process can be discussed. Curves are presented for typical and general cases. AN extremely efficient purification technique was described recently by Pfann.1 Known as zone refining, it consisted of the slow passage of a series of molten zones, produced by external heaters, through a long solid ingot of the substance to be purified. Equations were given for the maximum separation attainable, and a numerical computation method was described for obtaining the concentration in the ingot after a given number of zone passes. The present paper offers an interpretation of the physical nature of zone melting in terms of a transport process in which formal diffusive and convec-tive flows occur. This interpretation, in addition to providing insight into the physical nature of the process, also provides a basis for its mathematical treatment. From this basis, useful equations are developed for the solute concentration in the ingot as a function of the number of zone passes. These are applicable particularly where large numbers of passes are necessary and where numerical computational methods might be laborious. All considerations will deal with the limiting form of the process, described by Pfann,' in which: 1—Diffusion in the solid is considered negligible. 2—Mixing in the liquid is supposed, complete. 3—The distribution coefficient, k, measuring the ratio (at equilibrium) of solute concentration in the solid to that in the liquid is supposed, independent of composition. In general, this paper will be concerned with a bar of uniform (actually unit) cross section, ex- tending in the x-direction from x = 0 to x = L, where L may be infinite. Zone melting is a transport process, and as such must admit of interpretation in terms of a flux of transported quantity. However, the progress of operation is not measured in units of time but in terms of the number of completed zone passes. Consequently, the zone-melting flux will be a rate, per unit pass, rather than per unit time. The description of this flux and the examination of its properties is given below. Zone-Melting Flux Fig. 1 represents an intermediate stage of the nth pass. Concentration C is plotted against distance, x. The molten zone with its back at the point x and front at x + I moves in the direction indicated by the arrow. As it moves, it leaves behind the nth

Jan 1, 1955

By H. R. Peiffer

Hardening of soft metals can be accomplished by dispersing finely divided hard particles in them. The dispersing of finely divided alumina in silver in the presence of oxygen yields a high strength material which is unusual in that its mechanical properties above the melting point of the continuous Ag-O alloy matrix are similar to other solids. The tensile strength is studied for two of these alloys, one of which contains 15 pct by weight alumina and the other 20 pct by weight alumina. The average fracture strengths above 960°C of these alloys were found to be 0.4 x106 dynes per sq cm and 3.8x106 dynes per sq cm respectively. The strengths appenred to be independent of temperature above 960° C. The creep behavior of the 20 pct alumina material was studied above 960°C. The initial creep rate, 6 , of this material can be represented by where s is the applied stress and E the activation energy for the process. This energy is of the order of 1.7 to 2.1 ev. HARDENING of soft metals by the addition of finely divided, hard particles has resulted in the production of materials with excellent creep resistance and with inhibited recrystallization.' It has been demonstrated that such composites have useful strength up to temperatures very near the melting point of the soft metals, but one might expect that the strengthening by the dispersed particles ceases to be of importance above the melting point of the softer phase. This, however, is not so.2 In this paper the strengthening of a liquid Ag-O solution by the presence of dispersed alumina is discussed and experimental data concerning the mechanical properties of such a material at temperatures above 960°C presented. EXPERIMENTAL PROCEDURE Specimens were prepared using powder metallurgical techniques. Finely divided silver oxide was mixed in the appropriate proportions with "Linde B" alumina. For these experiments the specimens contained 15 or 20 wt pct alumina in pure silver.* These alloys were used in these experiments since they were the ones that could be handled readily enough to yield experimental data. Silver oxide was used in preference to silver because it is readily available in a very finely divided form and because the presence of excess oxygen in the silver is important to the properties2 of the material. The powders were mixed wet, using alcohol as the medium, in an ordinary food blender until a uniform mixture was obtained. They were then dried and heated to reduce the silver oxide to silver. Only a fraction of the finely divided silver remains unoxi-dized upon removal from the oven since the finest particles of silver oxidize immediately upon contact with air. The remaining fine silver served as a binder during pressing. The mixture was then pressed at 20 tons per sq in. into shoulder-grip (reduced section 1/4 in. by l/4 in. by 1 1/4 in.) and rectangular bar specimens (l/4 in. by 1/4 in. by 2 in.). The green specimens were heated very rapidly in a globar furnace to 1000°C, held at temperature untic they had reached theoretical density and then furnace cooled. The strength of the two compositions at temperatures above 960 °C was determined by pulling shoulder grip specimens inside a furnace mounted on a tensile machine. Specimens were gripped by means of wires wrapped around the shoulders of the specimen. Temperatures were measured by means of a chro-mel-alumel thermo-couple placed in the vicinity of the specimen. Control of temperature (within ±°15C) was accomplished by means of a Weston Recorder-Controller. Before loading, specimens were held at temperature for approximately 15 min in order to insure uniform specimen temperature. The low loads were measured by a special load cell designed by Baldwin Lima Hamilton. All testing was performed on a FGT testing machine of the same com-pany. Creep studies were performed in bending utilizing rectangular specimens of the 20 pct alumina alloy. Specimens supported at both ends by knife edges of inconel were placed in a globar furnace, heated quickly to temperature, and the deflection of the beam measured optically as a function of time. The weight and size of the specimen were predetermined and the maximum stress on the beam calculated from

Jan 1, 1962

By Alan J. Strauss

The Group IV elements germanium, tin, and lead form nine 1:1 compounds with the Group VI elements sulfur, selenium, and tellurium. This paper reviews the properties of the pseudobinary solid solutions formed by these compounds, including the extent of mutual solid solubility, temperature-composition phase diagrams, transport properties, deviations from stoichiometry, optical properties, and energy band structure. Particular emphasis is placed on the Pbl-xSnxTe and Pb1-xSn,Se alloys with rocksalt structure, because of current interest in these malerials for generating and detecting infrared ,radiation. ThE Group IV elements germanium, tin, and lead form nine 1:1 compounds with the Group VI elements sulfur, selenium, and tellurium. Some of the physical and electronic properties of these compounds, including their melting points1-8 and energy gaps,4'9-12 are listed in Table I. Four compounds (SnTe, PbS, PbSe, and PbTe) have the cubic rocksalt (Bl) structure. At room temperature GeTe has a rhombohedra1 structure closely related to the B1 structure, into which it is transformed at about 400°C. Four compounds (GeS, GeSe, SnS, and SnSe) have the orthorhombic B29 structure. In samples which have not been intentionally doped with impurities, the electrical conductivity is due primarily to electrons or holes produced by the ionization of donor or acceptor lattice defects associated with deviations from stoichiometry. Undoped samples of PbS, PbSe, and PbTe may be either n type or p type, depending on whether they contain excess lead or an excess of the Group VI element, respectively, but only p-type samples of the other compounds have been reported. This paper will review the properties of the pseudo-binary solid solutions formed by the nine 1:l compounds. The topics to be considered include the extent of mutual solid solubility, temperature-composition phase diagrams, transport properties, deviations from stoichiometry, optical properties, and band structure. Particular emphasis will be placed on the Pb]-xSnxTe and Pbl-xSnxSe alloys with B1 structure, which are promising materials for generating and detecting infrared radiation in the 8 to 14 µm atmospheric window and beyond. MUTUAL SOLID SOLUBILITY The extent of mutual solid solubility in the pseudo-binary systems has been investigated for fourteen of the eighteen ternary systems (in which the two terminal compounds have a common element) and for nine of the eighteen quaternary systems. In most cases, X-ray diffraction measurements made at room temperature were used to determine the structure and lattice parameter(s) of the phase(s) present in samples of various compositions prepared by freezing from the melt. In many investigations, including the extensive studies of Krebs and co-workers,13'14 the samples were annealed at elevated temperatures before X-ray measurements were made. In some cases, metallographic examination and thermal analysis have also been employed. The results for the ternary and quaternary systems are summarized in Tables II and III, respectively. (The original references should be consulted for the annealing temperatures.) The solubility of one compound in the other is at least 5 mol pct in all cases, and is often much larger. Complete solid solubility has been observed in all systems so far investigated in which the terminal compounds have the same structure, although in the PbS-PbTe system complete solubility is limited to elevated temperatures. Thus complete solid solubility occurs in five systems where both compounds have the B1 structure (SnTe-PbTe, PbS-PbSe, PbS-PbTe at temperatures above 805°C, PbSe-PbTe, and SnTe-PbSe) and in three where both compounds have the B29 structure (GeS-SnS. GeSe-~n~e-, and SnS-SnSe), as well as in two involving GeTe and a compound with B1 structure (GeTe-SnTe and GeTe-PbTe). On the basis of thermal analysis data, complete solid solubility at sufficiently high temperatures has also been reported for the GeSe-GeTe2 and SnS- pbS22 systems. This seems unlikely, however,

Jan 1, 1969

By E. S. Machlin

THE function of this paper is to present certain results based on the fact that the strain energy arising from the solution of out-of-size solute atoms into the solid matrix is free energy and not internal energy, and that this strain energy is almost wholly shear strain energy as Zener1 pointed out. One natural consequence of this fact is an expression for the excess entropy of mixing due to the strain energy. Also, a derivation of the integral molar free energy of mixing partitioned to strain energy will be made using the model of Lawson2 and thermodynamics. This derivation has the advantage of showing in a simple way the assumptions involved in Lawson's treatment. The excess entropy of mixing partitioned to strain energy can be derived in two ways. The first way makes use of the fact that the strain energy is almost wholly in the form of shear strain energy. In this case, as Zener1 pointed out, the change in entropy due to the addition of shear strain energy is to a first approximation given by ?S/?? p,T = - ?lnµ/?T p,? Hence, the excess entropy of mixing partitioned to strain energy will be given by Sx ? = ?S/?? p,T Gx ? = - ?lnµ/?T p,? Gx ? where, Gx ? is the relative integral molar free en- ergy partitioned to strain energy; S is the entropy; is the shear strain energy; µ is the shear modulus; T is the absolute temperature; p is the pressure; and ? is the shear strain. Zener,1 as well as others, has pointed out that the shear strain energy stored in a compressible isotropic solid due to the insertion of an off-size incompres-sible sphere into a spherical hole in the solid, is approximately given by 2/3 µ/O (O°I - O)2 where a is the volume of spherical hole and no , is the volume of sphere. If we now consider the introduction of one mol of such spheres into an infinite volume of solid, then the relative partial molar free energy excess due to strain energy alone is GM ? = 2/3 µ/v (v ° 1 - v)2 where v is the molar volume of solvent and v°1, is the molar volume of pure solute type 1. Let us consider that these spheres are the two types of atoms in a binary solution, then there will be a similar relation for solute 2. The total relative integral molar free energy excess due to strain is then, to the approximations stated above GM ? = GM ? x1 + GM2 ? x2 = 2/3 µ/v [(v ° 1 - v)2 x1 + (v ° 1 - v)2 x2]. Lawson's relation for the strain energy can be de-

Jan 1, 1955

By Donald L. Katz

FIFTEEN years ago Dr. Manning published a paper in "Petroleum Development and Technology" on '.Fundamental Research Relating to Petroleum." He tabulated for several industries "the proportion of their present success which can be fairly attributed to the application of information and processes obtained by scientific research," giving petroleum a score of 7 compared to 100 for the electrical and coal-tar industries. Today the petroleum industry as a whole and the producing groups both have raised their score beyond the majority and are climbing toward the top. Present practices are being developed both by fundamental research and the application of the research method in field operation.

Jan 1, 1941

By C. H. Li, R. J. Stokes, T. L. Johnston

A portion of the Ni3Cr-Ni3Al phase dzagram has been investigated, including the precipitation of 1 (Ni3Al) as well as the existence of ordered Y (Ni matrix), Extensive metallographic studies by electron microscopy have been carried out and X-ray diffraction diagrams have been taken at both elevated and ambient temperatures, No long-range ordering of the phase was found above 893°C (1639°F) in the compositional range investigated. The high rate of formation of the ordered ?1 phase upon quenching has been confirmed, a phenomenon which up to the present Lime has retarded the understanding of this phase diagram, Specimens with controlled amounts of ?1 exhibited up to a six-fold improvement in yield and creep strength compared with single-phase Ni-Cv-A1 alloys. MOST of the important high nickel heat-resistant alloys are related to the nickel-chromium-aluminum system. One of the important functions of the aluminum, often accompanied by titanium, is to produce a precipitate of the very fine ?1 phase (Ni3A1, X) where X may be Ti, Cr, or other elements. A number of investigators1-" have demonstrate the presence of y' in these alloys but most of their materials contained large amounts of other elements resulting in appreciable amounts of con- fusing phases such as carbides. Further clouding of the precise role of y' has been the suspected existence of an ordering reaction in the y matrix itself, ro-3,12-17 It appeared from these investigations that aluminum in Ni-Cr alloys would raise the ordering temperature of the matrix from 540°C at NisCr to 1300°C at Ni,Al. In support of this possibility, the matrix phase in the parallel Ni-Fe-A1 system is ordered to very high temperatures.1 OBJECTIVES OF THIS RESEARCH From this survey of the literature it appeared desirable to conduct an investigation of the simple Ni-Cr-A1 system using the alloys of the highest available purity to avoid the complication of foreign phases and thereby isolate the structures in the Ni-Cr-A1 system. Procedures were developed to study ? - ?o and ? - ?1 equilibria. Preliminary mechanical tests at elevated temperatures were also conducted.

Jan 1, 1962

By R. C. Rastogi, F. F. Aplan

The goal of this study is to evaluate the coal flotation process and the interaction of the chemical (reagent) and hydrodynamic (machine, operational) variables as they affect yield, flotation of various sized particles, and sulfur and ash rejection. Coal flotation is found to follow a first order process with the coal floating much faster than either pyrite or ash. This circumstance may be used to achieve gangue rejection during flotation. When floated with MZBC, cresol, or pine oil frothers, coal floats in the size sequence: 108 pm ( - 65 mesh), 589 x 808 pm (88 x 65 mesh), and 1.17 mm x: 589 pm (14 x 18 mesh). However with a substantial amount of fuel oil collector, all particles tend to float roughly in proportion to their content in the feed. An increasing aeration rate was found to be the most important variable in increasing the coal flotation rate. This increase in flotation rate, unfortunately, is also accompanied by an increase in the flotation rate of the pyrite. The rejection of pyrite during coal flotation is best accomplished at low aeration rates, low frother concentrations, and low impeller speeds.

Jan 1, 1986

By Robert J. White

Strong's equation for calculating bottom-hole pressure reduction due to gas cutting of drilling mud is corrected, resulting in a simpler equation which is easier to use. Use of the equation is illustrated by examples. It is shown that reduction of weight of a 10 lb/gal mud by 50 per cent at the surface due to gas cutting produces only n 3 per cent decrease in hydrostatic head at the bottom of a 5,000-ft well. It is also shown that at the surface 5 volumes of air per volume of mud are required to reduce the apparent mud weight from 8.5 to 6.5 lh/gal in a 3,000-ft well. Illustrative graphs are included to show the effect of various degrees of gas cutting on apparent mud weight at depths of 2,000, .5,000 and 10,000 ft and to show variation of apparent mud weight, with depth for a 100 lb/cu ft (13.37 lb/gal) mud gas cut to 90 lb/cu ft (12.03 lb/gal) at the surface. INTRODUCTION In 1938, Strong' published the following equation for calculating reduction in bottom-hole pressure due to gas cutting of drilling mud h = 1/D [p + pn/100 In p + p(1-n/100)/p(1- n-100)] where: h = depth in feet P = pressure in atmospheres at depth h due to mud column only D = hydrostatic pressure in atmospheres of a col-umn of uncut mud 1 ft high p = back pressure at well-head (in atmospheres) n/100 = fraction by volume of gas in mud at well-head at back pres-sure p This equation was recently found to contain an error due to an incor-rect expression for variation of vol-ume fraction of gas with pressure. Values calculated by the original equation are close to the correct values for small percentages of gas for which it was derived but become increasingly erroneous as the gas content increases and are completely unusable at the very high gas con-tents employed in aerated mud. DERIVATION The nomenclature used is the same as in Strong's paper. The pres-sure dP exerted by a lamina of thickness dh at a depth h ft is ex-pressed by Eq. 1 where x = volume fraction of gas at depth h dP = D (l - x)dh . . . (1) When we express x in terms of the wellhead per cent gas n, the well-head pressure p and the pressure P at depth h, the result is Eq. 2. x = (np/p+p)/(100-n) + (np/P + p) When this is substituted in Eq. 1 and rearranged to separate the var-iables the result is dh = 1/D [dp + np/100-n dp/(P + p]. Integration between appropriate lim-its results in or if the wellhead is open so that p = 1 atm and we rearrange Eq. 4, the result is loss in head = hD — P = n/100-n In (P + 1) ...(5) Eq. 5 can be solved easily by successive approximation using hD as a first approximation for P on the right-hand side and calculating a first value for loss in head. This can then be used to get a new value of P using the left-hand side of the equation. Values converge very rap-idly even for quite large values of per cent by volume gas n. EXAMPLES The effect on bottom-hole pressure of 50 per cent gas cutting of the mud in a 5,000-ft well using 10 Ib/ gal mud will be calculated, we have: h = 5,000 ft 10 X 7.48 144 X 14.7 = 0.0353 atm/ft hD = 176.5 atm n = 50 Substituting these values in Eq. 5 and using hD as a first approxima-tion of P on the right, we have, approximate loss in head = 50/50 In (176.5 + 1) = 2.30 log 177.5 = 5.17 atm. We calculate a new value of P as follows:

Jan 1, 1958

By Thomas T., Read

E DUCATION for the mineral industry was at first a single comprehensive curriculum, but it was early recognized that the main basis of mining is physics, while that of metallurgy is chemistry. The first school to offer curricula leading to degrees in mineral industry education in the United States (1853) had separate ones in mining and metallurgy. The Columbia School of Mines (the first really successful one) had only a single curriculum when it opened in 1864, but within a few years had so reorganized its work that it offered curricula in mining, metallurgy, geology, chemistry, and civil engineering. Interest in the metallurgy or geology curricula was slight at first, and for the next 30 years the great majority of Columbia students took the mining curriculum, probably partly because it contained nearly as much geology as the geology curriculum, practically all the metallurgy, and most of the chemistry, and partly because of the degree awarded for it. Other schools kept their mining curricula equally broad, and as late as 1900-1910 men were graduating as mining engineers who were practically as well prepared to make geology or metallurgy their life work, as they were for mining. Gradually, however, the subject matter of mining geology and metallurgy became so enriched through research and development that separate curricula in them became worth while; their progressive development is the subject of another chapter. Mining curricula also began to be somewhat diversified, and schools in areas where coal mining was of outstanding importance began to offer options in coal mining, the earlier curricula having been chiefly aimed at metal mining. The petroleum industry began its meteoric rise about the same time as mineral instruction in this country, but little more of applied science attended its birth than had attended such ancient practical arts as copper and iron

Jan 1, 1941

By Charles Macdonald

WROUGHT-IRON eye-bars for bridges and roofs, designed upon what is known as the pin connection system, have been successfully manufactured in this country for some years. The most approved methods employed have been the hydraulic upsetting process, and by die-forging under a hammer. In upset eyes the fibre of the iron is necessarily much distorted ; and in bars of considerable size, this disturbance seriously impairs the strength of the connection. Mr. Collingwood, in discussing my paper on "Proportions of the Heads of Eye-bars," read before the American Society of Civil Engineers, Jan. 21st, 1874, submitted sketches of certain bars intended for the anchorage of the East River bridge, which had been exposed to the action of sulphuric acid a sufficient length of time to thoroughly cleanse the surfaces, and expose the condition of the fibre. These sketches are here reproduced for the purpose of illustrating the effect of this methpd of manufacture. In Figs. 1, 2, and 3, it will be observed that the fibres at A, and E, have been folded back upon themselves and otherwise twisted and disturbed, in a manner not calculated to inspire confidence in the integrity of the connection. To compensate for this defect, a large excess of metal is thrown into the eye; but a method of manufacture which involves such a necessity, even although it be the one giving the best results thus far, all things being considered, is far from being perfect.

Jan 1, 1879

By F. N. Flynn

- Introductory IN 1882, The Arizona Copper Co. Ltd., acquired producing copper mines at Metcalf and Morenci (locally called Longfellow). Metcalf is situated a distance of 7 miles, and Morenci a distance of 6 miles from the general office of the company at Clifton, Ariz. A reduction works with five blast furnaces was built in the center of the town of Clifton in 1884 and operated until January, 1914. Concentration of oxidized ores was begun in 1890-1891, in a mill built adjoining the smelter, and in October, 1893, a leaching process was started for treating tailings from the oxide mill. A sulphide concentrator with 300 tons capacity was built at Clifton and started treating chalcocite ores in July, 1896. This was the first mill to treat low-grade copper-sulphide ores successfully. Another concentration mill for sulphide ores was erected at Morenci in 1900. The, sulphide mills are now being remodeled to treat ores by concentration and flotation, with a capacity of 4,000 tons at Morenci and 500 tons at Clifton. The leaching plant has not been running since September, 1914. The average yearly production from this company's mines and reduction works from 1885 to date has been: Pounds 10 years ended 1894 6,864,902 10 years ended 1904 20,439,614 10 years ended 1914 : 32,665,905 Part of year 1915, to Sept. 12 30,206,106 4 months of 1916, to June 15,964,840 June, 1916...: ? 4,900,000 Construction on a new smelting plant was started in February, 1912, and finished in February, 1914. In the Transactions, vol. 49, E. Horton Jones published "Unit Construction Costs from the New Smelter of the Arizona Copper Co., Ltd:," which fully describes the construction of this plant, with details of costs.

Jan 9, 1916