By R. W. Kraft, L. D. Graham

The process of' spheroidization, or more properly coarsening, of Al-CuAl,eutectic alloy specimens with various initial microstructures was studied by quantitative metallographic and X-ray diffraction techniques. By measuring the rale at which specimens with a very fine dispersion of phases (produced by quenching molten droplets of the alloy in water) coarsened it uias determined that the rate-controlling mechanism for coarsening was diffusion, probably of aluminum in the aluminum-rich phase. The lamellae in specimens with a high degree of microstructural and cr-ystallog/uphic anisotropy (produced hy unidirectional solidification of ingots) thickened during heat treatment by recession of the CuAl, platelets from jaulted regzons, yet the specinlens retained a very high degree of. anisotropy after prolonged heat treatments at a temperature within 8°C of the eutectic temperature. In such specimens the crystallographic orientation relationship between the phases remained constant and no change in the crystallographic substructure occurred. Based on these observations a model was developed for the coarsening—or rate of' thicken-ing—oj- the lamellar structures which predicts that the rate of decrease of interface area is proportional to the square of lamellar interface area. Experiments with degenerate and very coarse lamellar microstruc -tures preduced by extremely slow unidirectional solidification) indicate that initial microstructure is a most important factor governing the final micro-structure after heat treatment. The particle size and shape of dispersed phases are important parameters affecting the properties of a wide variety of two-phase materials. As is well-known, varietythe dispersed-phase particles tend to coarsen at appropriately high temperatures because the interface energy of the system is reduced by the concomitant reduction in interface area. The phenomenon of

Jan 1, 1967

By S. R. Goodman, Hsun Hu

The formation of secondary - recrystallization tex-tlires in cube-textured 18-8 stain less steel (Type 304) Ilas been studied at three temperatures. Prolonged annealing at 100°'C protluces a PredoninanGly (520) [OOZJ-type texture, which is related to the cube te.ture of the primary lnatrix by a rotation of approxivzately 22 deg around the [001] axis in the rolling direction. Annealing at 1200 or 1300°C facers the formation of the (123)[272/-type texture, which is related to the matrix texture by a [111] rotation of app.voxiniately 40 deg. These observations suggest that in the secondary recrystallization of cube-texlut-ed stainless steel an apparent actilation energy for growth is higher for grains related to the tncrtuix Og [111] rotations thun those reloted by [100] rotations. THE formation of secondary-recrystallization textures in cube-textured primary matrices of fcc metals has been studied widely by various investigators. For Fe-40 pct Ni alloys, Pawlek' and wassermann2 reported that the orientations of secondary grains were related to the cube texture by rotations of 30 and 38 deg around [001] in the rolling direction. However, Rathenau and custers3 found that, while in one Fe-48 pct Ni alloy, most of the secondary grains were oriented with respect to the cube-textured matrix by rotations around [001] of 26.5 deg, in another alloy of a different origin, the orientations of secondary grains were related to the cube texture by rotations of approximately 35 deg around a [lll] axis. Similar orientation relationships were also observed between the secondary grains and the cube-textured primary matrices of copper.4"a No attempt was made to differentiate these two types of orientation relationships; reorientation by either a [111] or a [100] rotation was considered to be equally favored. The present investigation consisted of a study of the secondary recrystallization textures in cube-textured stainless steel. It was noted that the secondary grains formed in stainless steel were considerably smaller than those of Fe-Ni alloys or copper. This offered the advantage that the secondary recrystallization texture could be determined by the texture-goniometer technique, and a more detailed study of the textural development during the course of secondary recrystallization could be made. The effect of annealing temperature on the formation of secondary-recrystallization textures was also investigated. MATERLAL AND METHOD It was shown earlier"-" that a strong cube texture can be obtained in 18-8 stainless steels by rolling at 800°C to produce the copper-type deformation texture, followed by annealing at 800" to 1000°C for recrystallization. To improve the cube texture for the present study, a commercial-grade 18-8 stainless steel (Type 304) was rolled at 800°C first to 5 mm (0.2 in.) thick plates. Three of these plates were then stacked and welded together along the edges into a sandwich assembly. After annealing at 900°C for 20 min: the assembly was finally rolled at 800'C to 90 pct reduction in thickness with reheats and end-for-end reversals after each pass. Only the central strip, which was reduced from 5.0 to 0.50 mm (0.7 in. to 0.020 in.) thick, was used. The chemical composition of the steel in weight percent was as follows: C, 0.06; Mn, 0.38: Cr, 18.71; Ni, 9.56: P, 0.011; S, 0.009; and Si, 0.39. The purpose of rolling the strip in a sandwich assembly was to prevent direct contact between the central strip and the rolls. It was observed earlier" that, when the strip was rolled at 800°C without being enclosed in a sandwich assembly, the cube texture obtained by subsequent annealing at 900" or 1000° C for recrystallization was largely confined to the central section of the strip, while most of the recrystallized grains formed in the surface section of the strip were not cube-textured. This was obviously due to the fact that the actual temperature at the strip surface during rolling, as a result of direct contact between the strip and the cold and massive rolls, was considerably lower than 800°C. By using a sandwich assembly for hot rolling, the cube texture obtained upon subsequent annealing for recrystallization was found to extend through the entire thickness of the strip. After rolling, the central strip was taken from the sandwich assembly. and cut into specimens. Prior to annealing. the specimens were etched to 0.25 mm (0.010 in.) thick. A tube furnace provided with a purified, dry argon atmosphere was used for annealing. Textures were determined by the reflection technique. using a Siemens automatic texture-goniometer and ZrOz-filtered MoKa radiation. With a time constant of 4 sec. the preferred orientation of the secondary grains could be measured satisfactorily by the integrated intensities. Both (111) and (200) reflections were measured, and corresponding pole figures were constructed according to the techniques described previously.10 The agreement between results deduced from these two reflections was excellent. RESULTS AND DISCUSSION Secondary-Recrystallization Texture due to Prolonged Annealing at 1000°C. Fig. 1 shows the primary-recrystallization texture of a specimen annealed at 1000°C for 30 min. A substantial improvement in both sharpness and intensity of the cube texture, owing to the present processing method, can be noted readily by comparing Fig. 1 with similar pole figures shown earlier in Refs. 9 and 11. Secondary recrystallization

Jan 1, 1967

By M. E. Straumanis, J. -P. Krumme

In basic ([KOH + KCl] with a total polarity of 2) or acidic (2N H2SO4) electrolytes and at anodic current densities of more thun 2 to 4 ma per sq cnz, n-type GaAs single crystals of lozo resistivity preferentially dissol~je forming etch tunnels with triangular or civc~ilay cross sections and of a width between 0.5 arid 5 p. These etch tunnels are oriented along any one of the four possible (111) directions of GaAs. However, their growth occurs only in one direction of a given (111) whick apparently is determined by the atomic sequence Ga —As (and not the rezlerse) in respect to an individual valence bridge in the crystal. It is concluded from comparison with the cubic lattice structure of GaAs that the etch tunnels represent macroscopic evidence for the tetrahedral bonds and their polar properties. If the anodic current density is increased the tunnel fomation results in the development of a fibrous surface layer consisting of GaAs. The latter separates frorn the substrate (in an anodic s~irface disintegration process) by the growth pressure of an As,0, filnz forming in the interior of the fibrous layer, 100 to 200 µ under the surface, at more than about 50 ma per sq cni. The fibrous GaAs film has the same crystallographic orientation as the substvate and represents a skeleton of the original crystal. Since the etch-tunnel density in a separated GaAs layer is about 108 c?n-', and the etch tunnels develop only along (111) in a given polar direction, it is assurraed tlmt the dislocations have no influence on the growth of these tunnels. ElECTROLYTIC treatment of smooth surfaces of poly- and single-crystalline GaAs at high anodic current densities causes the formation of porous surface layers.' This phenomenon suggests comparison with effects being observed with magnesium,' indium,, gallium,4 and aluminum5 and known as "anodic disintegration". The purpose of the present paper is to explore and to explain the reasons for the formation of such surface layers on GaAs and, in particular, to investigate the influence of the lattice polarity of this III-V compound semiconductor in the (111) direction on the anodic dissolution behavior. GaAs SINGLE CRYSTALS For the experiments described below GaAs single crystals from the Monsanto Co., St. Louis, Mo., were used. Their impurity levels were below 1 ppm and their dopant levels between 1 and 100 ppm. They were grown in (111) using the Czochralski or the gradient-freeze technique. The crystals had n-type conductivity and electric resistivities between 1 and 5 ohm-cm. EXPERIMENTAL The GaAs single-crystal rods were cut perpendicularly to (111) into wafers of about 1 mm thickness using a wire-blade crystal slicer and an aqueous slurry of Sic or a diamond saw. The orientation of the faces of these wafers were checked by Laue back-reflection patterns. If there was a deviation from (111) the faces were abraded under a certain angle using grinding paper and distilled water. The damaged surface layer was removed from each crystal by chemical etching with a mixture of 1HF:1HNO3: 1H20 or 2HF:1HNO3:2HAc (glacial). {110) faces were obtained by mechanical cleavage, producing surfaces which did not require a further treatment. The GaAs wafers were mounted using "alligator" clamps instead of soldered electrical contacts.' Only the bare crystal surfaces were dipped into the electrolyte. The clamps were coated with insulating wax to prevent any contact with the electrolyte. The experiments were carried out in aqueous 2 N H2so4,' or in an aqueous solution of KOH and KCl1 (1 mole KOH + 1 mole KCl in 1000 cu cm solution). Anodic current densities up to several hundred ma per sq cm were applied for periods between 30 sec and 2 hr. For the purpose of investigating the initial steps of disintegration the anodic current density applied never exceeded 20 ma per sq cm. The films which partially separated from the anodic surfaces under high-field conditions were treated with KOH to further their detachment by dissolving the As2O3 formed. The washed and dried films were pasted to strips of filter paper, and Laue pictures were made. The back-reflection patterns obtained were compared with those of the original anode surface before and after anodic dissolution. Furthermore, space reciprocal lattices7 were constructed from asymmetric rotation crystal patternsa which permitted the determination of the crystallographic orientation of the detached films of the corrugated anodic surfaces. The disintegration products were identified from assymmetric powder patterns.8 The polarity of the {111) faces was determined by chemical etching with mixtures of 1HF:1H2O2(30 pct): 2H2O or 1HNO3:2H2O. Different patterns on each of two inverse (111) sides appeared.'-l8 The correlation of these patterns to the Ga{111) or the As(111) side has already been established by the use of light figures,18-20 by X-ray diffraction near the absorption edges of gallium and arsenic,'lmZ4 and by LEED measurements.25 The geometric structure of these surfaces and the interior of the anodically attacked crystals were observed and photographed with a high-power microscope using oil immersion objectives up to magnification of X1720.

Jan 1, 1968

By J. W. Spretnak, R. Speiser

IT has been suggested that boron in steel may form a film entirely around the austenite grain and that this film is responsible for the boron hardenability effect. In this connection, it is of interest to examine some of the ramifications of the concentration range of boron usually employed in hardenable steels, namely 0.0005 to 0.003 pct in a grain size range of ASTM grain size No. 1 through No. 10. The ratio of the iron to boron atoms and the number of unit cells of y iron per boron atom are listed in Table I. Even at the highest concentration considered, there are 1600 unit cells of y iron per boron atom, assuming a uniform distribution of boron. To investigate the possibility of the boron film formation, the number of boron atoms required to cover the grain surface completely must be calculated. With some transition elements, boron crystallizes in sheets composed of equilateral hexagons very much like graphite.' The selected value for the length of a side is 1.80Å. A simple calculation shows that two boron atoms cover an area of 8.4x l0 -16 sq cm. Table II lists the number of atoms of boron required for the formation of the monatomic film and Table III lists the number of boron atoms per grain. The hypothetical cases of 100 pct and 10 pct adsorption are calculated (all boron atoms in a grain and 10 pct of all boron atoms in a grain are located at the grain surface respectively). In Table 111, all combinations of grain size and composition below and to the left of the solid line (100 pct adsorption) and the dashed line (10 pct adsorption) are excluded as to the possibility of covering the grain surface with a continuous boron film. Thus, even for 100 pct adsorption, the smaller grains can form the film only at the higher concentrations. For the best case, grain size No. 1 and 0.0030 pct B, the required degree of adsorption is 3.9 pct. The above calculations deal only with the number of boron atoms required to form a monatomic film and do not take into account the mechanism of concentration of boron at the grain surface and the possible limitations to the extent of this concentration at a constant temperature, as for example in the austenitizing process. The question next arises as to how this surface concentration can occur during an isothermal treatment. Such surface enrichment of boron must occur through the phenomenon of surface adsorption, i.e., the concentration of solute atoms in solid solution in the vicinity of the surface without precipitation. A solute atom will tend to concentrate at the grain boundary if it reduces the interfacial tension. The possibility of adsorption effects involving both boron and carbon in iron has been discussed.' In general, the tendency for a sol-

Jan 1, 1954

By Zay Jeffries

A SURVEY of rare metals and minerals for the past year places uranium as one of two partners, the other being the neutron, in what historians will probably say is the greatest discovery in physics at least during the year and probably for a consider- ably longer period. The uranium atom has been made to divide into parts somewhat after the style of reproduction of the amoeba. When an amoeba divides into two parts, however, it produces two amoebae substantially alike and each substantially like the parent: furthermore, there is no considerable change of energy when this happens. When the uranium atom divides it yields other atoms such as barium and krypton with the complete destruction of the original uranium atom but with the liberation of a tremendous amount of energy. This will be discussed more at length later.

Jan 1, 1940

By ROBERT. RICHARDS

I. INTRODUCTION The object of this paper is to enlarge the field of settling velocities treated by me in my former papers, Close Sizing Before Jigging, and Sorting Before Sizing.' There seemed need of work both on coarser and on finer sizes. Messrs. A. Sidney Warren and M. L. Nagel undertook the investigation for the coarser sizes, from 12.85 mm. down to 2.05 mm. diameter. Their work, because of the closer spacing and because of the increased number of observations and consequent stronger averages, called for a revision of the former work. Messrs. G., A. Barnaby and Ralph Hayden undertook this part of the work, from 2.49 mm. down to 0.28 mm., which is near the limit of sifting. Their work covers the ground much more minutely and comprehensively than the former papers. There remained to be covered the portion of the field too fine for investigation with the sieves. This part, covering the range of grains from 0.48 to 0.03 mm., was undertaken by Mr. E. S. Bardwell. For it he used the elutriation method. II. THE FIRST, OR COARSEST, SECTION OF THE FIELD. The first desideratum in this investigation was a series of sieves for sizing the sands preparatory to making the tests. It became necessary, therefore, to decide on a sieve-scale for this purpose. A sieve-scale is a series of sieves in which the dimensions of the holes of the successive members form a series increasing by a. definite ratio. There are three natural sieve-scales : 1, progressing by doubling the width of the hole for each suc-

May 1, 1907

By J. E. Harris

The metallic elements, beryllium, calcium, cerium, lithium, manganese, titanium, vanadium and zirconium are used in metallurgical practice in relatively small percentages for the purpose of improving the physical properties of various alloys. No important uses for any of these elements have thus far been developed either in the pure form or in alloys of which they constitute the major constituent.

Jan 1, 1935

By L. L. Wyman

SINCE the observations of Heyn,1 relative to the embrittlement of copper after having been heated in hydrogen, this subject has received considerable attention from later investigators. The published works of Archbutt2 and of Bengough and Hill3 give the reasons for this embrittlement-the formation of steam by the reaction between cuprous oxide and hydrogen. From Ruder,4 Pilling,5 Moore and Beckinsdale,6 Bassett and Bradley,7 and from Smith8 can be obtained quantitative data concerning the action of hydrogen and other reducing gases on copper samples having various oxygen contents. This problem has been discussed from a practical standpoint by Fuller9 who calls attention to some of the instances of this embrittlement encountered in the manufacturing field. The examples he cites may be considered typical cases of copper embrittlement which were incident to the process of manufacture. In many cases, such difficulties are overcome by changes in the manufacturing process.

Jan 1, 1931

By Clyde E. Williams

THIS review of the progress made in iron and steel metallurgy during the past year is confined to developments in this country. It attempts to give examples to illustrate progress made rather than to appraise results. As a result of the gradually diminishing supply of rich iron ores and of predictions made as to the probable life of the iron-ore reserves of the Lake Superior District, attention of iron and steel executives was directed to the question of beneficiation of iron ores. Laboratory and plant-scale experimental work was conducted on the wash ores .of Minnesota and an investigation, was, begun on the Old Range low-grade ores.

Jan 1, 1931

By Charles L. Mantell, Kurt Straler

The hydrogen reduction of Cr2O3 to chromium metal was found to be feasible at very low water-vapor concentrations, corresponding to dew points of -38° to -24°C, over a temperature range of 1130" to 1490°C. Hydrogen reduction under these conditions was predicted by the calculated equilibrium curves which also indicated that CrzOs is reduced directly to chromium without forming the intermediate oxide, CrO. This reduction path was confirmed by X-ray diffraction analysis. The percent reduction of Cr2O3 at each reaction temperature was constant with time, suggesting an inhibiting effect of water vapor. A small increase in the residual water-vapor concentration of a single temperature, 1490°C, strongly retarded the rate of reduction This effect was expressed by an empim'cal equation which indicated a direct relationship between "distance from equilibrium" and the rate of reduction. me effect of temperature over the range of 1130" to 1490°C was expressed in an Arvhenius plot of log rate vs reciprocal absolute temperature. From this curve the apparent enthalpy of activation was found to be 29,600 cal. Based on the hypothesis that the rate of reductiun is contvolled at the oxide-metal interface, an over-all rate equation consistent with the experimental data and the thery of absolute reaction rates was formulated. A simplification of this expression to an Arrhenius equation was justified by the overriding effect of temperature on the rate of reaction for the minimum water-vapor concentration range. MOST of the metals in Subgroup V1 of the periodic table can be prepared commercially by direct reduction of their oxides by hydrogen or carbon monoxide, at temperatures considerably below the melting points of both the metals and their oxides. Chromium is an exception, being generally reduced from its ore, Cr2O3 . FeO, by silicon in an electric arc furnace which operates above the melting point of the Fe-Cr alloy or above the melting point of chro- mium if a chromium oxide be the starting material. In reduction of chromium oxide by hydrogen, either reduction does not occur at all or the rate of reduction is extremely slow. Theoretical considerations based on the high, exothermic, free energy of formation of Cr2O3 compared to the oxides of the other Subgroup VI metals, molybdenum, tungsten, and uranium, would also suggest a slow rate of reaction and a high activation energy. Interest in the direct gaseous reduction of fine-powdered ores in fluidized beds was considered justification for examination of this reaction. In order to develop a basis for a continuing study of the commercial feasibility of the direct gaseous reduction of chromite, a study of the kinetics of the reduction of Cr2O3 with hydrogen was undertaken. To the authors' knowledge no accurate kinetic data for this reaction have been obtained. Neither has an activation energy been determined nor has an attempt been made to establish a mechanism of reaction. LITERATURE Maier10 compared the data of I. Y. Granaat,6 H. von Wartenburg and S. Aoyama, and G. Grube and M. Flad7 with that derived from calorimetric and ther-modynamic properties for the equilibria for the reduction of Cr2O3 with hydrogen. These results, plotted as the log of the equilibrium constant vs absolute temperature for the reduction of Cr2O3 and the intermediate oxide, CrO, to chromium, show agreement between the differently derived data. In both cases the equilibrium constants were extremely low. Maier showed that, over a temperature range of 1000° to 2000°K, Cr2O3 is more readily reducible than CrO. Granat assumed that CrO was preferentially formed from Cr2o3 above 1100°C. Grube and Flad's analysis of their reaction products in the 895" to 1000°C range indicated the coexistence of only Cr2O3 and chromium. The hydrogen reduction of the other Subgroup VI metals, molybdenum, tungsten, and uranium, shows that reduction of the higher oxide proceeds through all of the intermediate oxides before being reduced to the metal. Since evidence pointed to an anomaly in the reduction behavior of Cr2O3, the authors investigated the reduction path of Cr2Os.to chromium. This was done theoretically with more recently available free-energy data and experimentally by X-ray diffraction analysis. This work reinforces Maier's conclusion.

Jan 1, 1964

By S. R. du Toit, W. J. Oberholzer, M. I. Watson, D. G. Krige

The objectives, essential features and implications of the 'random' and 'deterministic' types of ore value surfaces are examined as well as the basic requirements for a satisfactory prediction model. The 'random' method used on the South African gold mines and based on observed auto-covariance patterns is briefly discussed as well as its justification in preference to the 'deterministic' approach. Various mathematical models for auto-covariance patterns are examined for the one-dimensional case. It is also shown that these patterns as estimated for ore values in certain mines agree closely for various sizes of ore unit. In two case studies the variations in gold, uranium and ore thickness covariance patterns are examined and compared with certain geological features established independently from sedimentological studies.

Jan 1, 1969

By Lee Morris, Charles E. Lawall

This paper represents the results of a study to determine the source, mode of occurrence and conditions influencing the flow and liberation of large volumes of inflammable gas in the Pocahontas No. 4 coal bed in southern West Virginia. A study of this kind is of interest in connection with mine ventilation, because in the removal of gases from coal mines it is very important to know the origin, the occurrence and laws of gas flow. The study was started in April, 1931, and the data and observations were obtained throughout a period of 15 months of field work. Geology The country where this study was made is mountainous and rugged; great cliffs, precipitous slopes and deep narrow gorges are found throughout the area. The outcropping rocks consist of stratified layers of sandstone, shale, limestone and deposits of coal of Carboniferous age. The Pottsville series of the Pennsylvanian, lying at the base of this period, cover the greater portion of the area. A stratigraphic section of the Pocahontas group of the Pottsville series is shown in Fig. 3. The older rocks outcrop in the extreme southeastern part of the area, but are under drainage in the central and northern parts due to the gradual northwest dip of the strata. The structure has a general northeast-southwest trend (Fig. 1). North of Dry Fork anticline the strata have been only slightly disturbed by movements of the earth's crust; it is now a long monocline. Southeast1 of Dry Fork anticline the strata are warped into great arches and deep troughs and are broken by overthrust faults. All of this folding is probably the result of the intense folding associated with the formation of the Appalachian Mountains. Pocahontas No. 4 Coal Bed The Pocahontas No. 4 bed, lying approximately 550 ft. above the base of the Pottsville series, is one of the thickest and most gassy coal beds in

Jan 1, 1934

By O. W. Simmons, L. W. Eastwood, C. M. Craighead

Binary alloys of titanium with silver, lead, tin, nickel, copper, beryllium, boron, silicon, chromium, molybdenum, manganese, vanadium, iron, and cobalt were studied. One-half-pound ingots of the alloys were prepared in an arc furnace, employing a water-cooled copper crucible, an argon atmosphere, and a water-cooled tungsten electrode. The half-pound ingots were fabricated by forging at 1700°F in air to 1/4-in. slab, followed by hot rolling at 1450°F to 0.060-in. sheet. Tensile properties, minimum bend radii, hardnesses, response to heat treatment and aging treatment, and phase relationships were determined for these alloys. EARLY in 1947, as one phase of the evaluation of materials for Air Force Project RAND, Battelle successfully arc melted Bureau of Mines titanium and obtained a few basic properties of unalloyed titanium and several titanium-base alloys. The low density, excellent resistance to corrosion, and high tensile properties of these materials stimulated a great deal of interest among metallurgists and designers seeking better materials of construction. As a result of this early work, Battelle, under contract with the Air Materiel Command, Wright-Patterson Air Force Base, has continued extensive studies of titanium alloys. The result of the first year's work is described in three papers. The present one deals with binary alloys, the second with ternary alloys, and the third paper with quaternary alloys. Melting Method The arc furnace for melting titanium and other refractory metals was developed at Battelle Institute under Air Force Project RAND. During the present work, considerable improvement has been made in the design and operation of this furnace for making small ingots of titanium and titanium alloys. The improved furnace design is illustrated by fig. 1, which shows a cross-sectional view with the dimensions of various parts and their relationship to one another. The essential features of the furnace are the inert argon atmosphere, the water-cooled copper crucible, and the water-cooled tungsten elec- trode. The melting crucible is formed by spinning 0.064-in. annealed copper sheet. A groove for an O-ring seal is spun into the flange of the crucible. A fiber gasket between the crucible flange and the water-cooled brass cover provides electrical insulation. The brass cover is fitted with a sight glass, an opening for the water-cooled electrode, and a tube through which the material is charged. Direct current is used for melting, with the positive electrical terminal connected to the water jacket and the negative terminal to the electrode. A typical heat is made in the new furnace as follows: Approximately, 0.20 lb of titanium under 2 mesh per in. and the alloy addition, if any is to be used, are placed in the bottom of the crucible. The cover is clamped on the crucible so that the O-rings make a tight seal. The remainder of the charge is placed in a glass bottle, and this is connected by a rubber hose to the charging tube of the furnace. The crucible and the charge are evacuated with a mechanical pump to a pressure below 50 mm of mercury, or less if desired, and held at this reduced pressure for 5 min. Hot water is circulated through the jacket during the evacuation period to assist in outgassing the crucible. Following the evacuation, tank argon of 99.92+ pct purity is flushed through the crucible for 5 min and then adjusted to give a positive pressure of 1 to 2 psi. During subsequent operation, an argon pressure regulator introduces only enough argon to compensate for the small leakage which occurs through a mercury trap. Re-evacuation and reflushing the melting chamber with argon produced a negligible reduction in contamination. Two 550-amp generators, connected in parallel, constitute the power source. Normally, about 800 amp are used for melting alloys which are not extremely refractory. The generators are set for 90 v open circuit and 200 amp. The arc is struck and the electrode is withdrawn to produce an arc of 23 to 26 v. This voltage is maintained while the electrode tip is moved slowly around a circle 1 in. smaller than the diameter of the ingot. The current

Jan 1, 1951

By Edwin S. Sperry

Metals differ widely in their behavior under the cuttingtool. Some, like iron or steel, require a slow speed and light feed, a tool shaped differently from that used for other metals,

Jan 1, 1898

By B. C. Allen

Liquid surface tensions of copper and 18 Group IV-A to VIII transition metals (Ti, Zr, Hf, V, Cb, Ta, Mo, W, Re, Ru, Rh, Pd, Os, Ir, Pt, Fe, Ni. Co) have been measured by the static pendant-drop and dynamic drop-weight methods on the same rod sample. The drops were formed by electron-bombardment heating in high vacuum. Application of necessary corrections enabled determination of surface tensions to k2 pct and agreement between methods to * 1 to 4 pct for all the metals studied. Evidence is presented that the liquid surface was well screened by metal vapor, suggesting negligible adsorption of gaseous impurities and that the surface tensions measured are characteristic of the metals involved. Correlations between liquid surface tension and melting point, molar volume, heat of vaporization, and atomic number are presented and discussed. Temperature coefficients of surface tension were calculated using Eötvös' law. SURFACE tension and interface energies of metals are the result of incomplete atomic coordination resulting in a force perpendicular to the boundary, tending to minimize its area. These energies are important in many phases of metallurgy, including microstructure, sintering, joining, electronic emission, and lubrication, which in turn affect many physical and mechanical properties of metals. Liquid surface tension refers to the interface between the liquid and its own vapor or nonreactive atmosphere, and is considered a physical property of the liquid. Since equilibrium shapes can be readily obtained with liquids, the units of surface tension (force per length) and interface energy (energy per area) are interchangeable. Thermo-dynamically, the surface tension ?LV is given by the change in free energy F with surface area A at constant pressure P, temperature T, and composition N: for commercially important refractory metals, vanadium, columbium, tantalum,13,14 molybdenum,14 and tungsten,l5 and none for the rare platinum-group metals and rhenium. Measuring the surface tensions of transition metals is difficult because of their high reactivity and melting points. Of the many techniques available,16-18 the pendant-drop 19-21 and drop-weight methods17,22 are considered superior because they can be modified to eliminate persistent sources of contamination such as supports and capillaries necessary in the popular sessile drop, capillary rise, and maximum-bubble-pressure techniques. The necessary modification is to melt a drop on the tip of a vertical rod, which provides support through a solid of the same composition.13,15 The object of the work was to study the surface-tension behavior of copper and transition metals, having reasonably low vapor pressures. Liquid surface tension of each pure metal was systematically determined by using a combination of the static pendant-drop and dynamic drop-weight methods on the same rod. Liquid drops were formed by electron-bombardment heating in high vacuum. EXPERIMENTAL WORK As indicated in Table I, the metals studied were high purity and generally were obtained in rod form. The exceptions were titanium and zirconium, which were machined from crystal bars, and molybdenum (tot 11, osmium, and ruthenium, which were sintered and arc cast into rods. All the metals were ground or swaged to desired sizes between 1- and 7-mm diam, and centerless ground round and smooth to a finish better than 50 µ in., rms. Each rod was thoroughly cleaned with steel wool, degreased, acid etched, and dried. In a typical run, the rod was vertically clamped in a modified floating-zone electron-bombardment furnace designed after Calverley23 and Carlson.24 The specimen was outgassed and maintained positive at several kilovolts in a dynamic vacuum of 10-5 to 10-7 mm. The bottom end was enclosed by a tantalum pillbox and heated by electrons emitted from a hot concentric tungsten filament mounted on a movable bracket. The bombardment power was slowly raised until melting was observed. Power requirements ranged from 30 w for copper to 1300 w for 4-mm tungsten. The stabilized and out-gassed drop of near-maximum size was photographed at 4. 1X on panchromatic film at desired time inter-

Jan 1, 1963

By Paul A. Filteau

Asbestos ranks among the leading minerals produced in Canada. It is also mined in Russia, Rhodesia, South Africa, Cyprus, Italy, the U.S.A., Japan, China and several other countries. The most abundant variety, chrysotile, and also the most valuable form of asbestos produced, makes up 90% of the world's supply. In Canada, chrysotile is found in the provinces of British Columbia, Ontario, Newfoundland as well as in Quebec, the latter accounting for almost 90% of all the fibre produced in this country. A number of developments emerging this year could make 1968 a record production and export year for Canada's asbestos mining industry. Asbestos fibre consumption in increasing in the U.S., Canada, up 10% to date this year, Japan and in Latin America. Demand in Western Europe is again on the upswing, following a cut-back last year. As a result, shipments from Canadian mines for the first eight months of this year reached some 916,968 tons versus 873,402 in 1967, an increase of 43,566 tons or 5%. Indications are that Canadian asbestos production will for the first time ever top 1.5 million tons in 1968.

Jan 1, 1969

By Harold Roast

THE object of this investigation was to compare the arsenical antimony-lead alloy with some of the regular bearing-metal alloys. With this end in view, the following tests were made: 1. Chemical analyses to show the composition. 2. Thermal analyses. 3. Macroscopic examination of fractures. 4. Microscopic examination. 5. Tensile tests. 6. Crushing tests. 7. Scleroscope tests. 8. Brinell tests, at temperatures from 80° to 400° F. Tests 3 to 8 were conducted on both sand-cast and chill-cast specimens. For the purposes of this paper the alloys have been numbered from 1 to 6; their composition is as follows: LEAD, ANTIMONY, TIN, COPPER, ARSENIC, NUMBER PER CENT. PER CENT. PER CENT. PER CENT. PER CENT. 1 82.64 12.95 4.40 0.01 none 2 27.54 9.94 59.87 2.65 none 3 77.65 20.75 none 0.13 1.47 4 82.95 16.85 none 0.20 none 5 83.78 15.35 none 0.05 0.82 6 0.15 7.87 84.13 7.85 none The analysis, in the case of the antimony, was made by solution in sulfuric acid and titrated with permanganate. For tin, the ferric-chloride method was used; for copper, the alkaline separations, and the thiocyanate methods; for arsenic, volatilization of arsenic and titration with iodine. The lead, with the exception of alloy 6, was taken by difference.

Jan 2, 1922

By F. X. Tartaron

This article is a continuation of a previous paper by the writer in which Kick's Law was stated to be a part of comminution theory. ln the present paper, a broadening of ideas is attempted in order to state a general theory. The word "general" is employed because the new theory includes all previous laws and generalizations which are considered to be essentially correct. These ideas are combined into a coherent whole and the general theory can be expressed by the equation In the author's previous paper on comminution, ' the equations developed were based on Charles' equation of exponents a-n +1 = 0. 2 This paper is divided into two parts, designated as First Approach and Second Approach. In the First Approach, the equations of the previous paper are utilized, with Charles' equation of exponents being necessary. In the Second Approach, a separate and independent method is used to derive the same conclusions as in the First Approach, but without the use of Charles' equation of exponents. Holmes accepts the theoretical foundation of Kick's Law as sound but denies that the law as such operates in comminution. His idea is that Kick's Law requires homogenous matter whereas the presence of cracks, flaws and cleavage planes, which predominate in the coarser particles, makes matter unhomogene-ous. This explains why there is no experimental evidence to support Kick's Law. However, since the basis of the law is theoretically sound, all experimental evidence must be viewed as emanating from it. This requires modification of current comminution equations to fit this concept. Holmes makes the modification by changing the constant exponent n in the general energy equation used by Charles (E = - JCdx/xn) to a variable exponent r. The writer asserts that Kick's Law operates in comminution without modification but it does not

Jan 1, 1963

By B. A. Rogers

ACCORDING to petrographic investigations, 1-4 cooled steel furnace slags contain a number of substances that have been shown to be ferro-magnetic5,6 and hence capable of undergoing appreciable changes of susceptibility with temperature. Since any alteration of the suscepti-bility of a constituent affects the average susceptibility of the sample, information concerning the nature of the substance should be deducible from its magnetic behavior. The possibility of obtaining information concerning slags in this way led to the construction of the apparatus to be described. FUNDAMENTAL PRINCIPLES OF APPARATUS The most convenient method of observing changes in mass suscepti-bility? with temperature is the one employed by Curie7 in his original investigation of the changes in magnetic properties of substances at elevated temperatures. As the method has been described frequently in the literature and in textbooks, only a brief review of the fundamental principles need be given here, but the particular arrangements used in the present work require a more detailed description.

Jan 1, 1939

By M. J. Marcinkowski, A. Szirmae, R. M. Fisher

Room -temperature hardness measurements obtained from single and polycrystalline samples of a 47.8 at, pet Cr-Fe alloy which were aged for various times al 500°C show a two-fold increase over that of the unaged alloy after annealing for 1000 hr. A detailed examination of the deformation markings in the neighborhood of the hardness imbressions reveals that twinning becomes an increasingly more important mode of deformation as aging proceeds. this observation is shown to be inconsistent with the Proposals that the transformation is eve of order-disorder On the other hand, the results are in agreement with previous observations of Fisher et al. of a coherent chromium-rich precipitate which forms in an iron-rich matrix as a result of a miscibility gap in this alloy system as proposed by Williams . Using the coherent precipitate hypotlzesis as a model, a detailed analysis of the various possible strengthening contributions to both the slip mid twinning stresses is made. In the case of' slip, lattice friction within the chromium-rich phase and the chemical energy associated with the interface between the two phases contribute about 60pet to the total strength. The contributions from coherency strains and modulus differences are thought to contribute the remaining 40 pet of the strength but are difficult to evaluate because of uncertainties regarding the flexibility of the dislocation line. All of the factors have nearly the same or else a smaller effect on the twinning stress in the aged alloy. Twinning is never observed in the unaged alloy because the twinning stress is much higher- than that for slip. With increased aging times, the various contributions to the total stress for both twinning and slip increase, but most of those for slip increase much more rapidly, so that, in the fully aged alloy, it surpasses the stress for twin propagation. When a twin is nucleated by the chance occurrence of an internal stress concentration during a test, the subsequent twin burst results in a low hardness reading. FeRNTIC Fe-Cr alloys from about 15 to 80 at. pet Cr content show considerable change in properties such as hardness, electrical resistivity, saturation magnetization, and so forth, after aging in the vicinity of 500°C.* The most marked change is a large increase in hardness accompanied by a sharp decrease in ductility, so the phenomenon has often been referred to as the 475°C (885°F) em-brittlement problem. Changes in microstructure are rather subtle and most investigators have not been able to observe any X-ray diffraction or metal-lographic changes during aging. There is little doubt that the phenomenon is inherent to the Fe-Cr binary system and is not directly related to the formation of a phase. Two distinct schools of thought have developed during the past decade concerning this problem. Masumoto, Saito, and sugiharal have concluded, from their own specific-heat measurements, that atomic ordering occurs in this temperature range. Pomey and Bastien2 have also attributed the changes in physical properties with aging in the neighborhood of 500°C to atomic ordering. In addition, Takeda and Nagai3 claimed to have found X-ray verification for superlattices corresponding to the compositions FesCr, FeCr, and FeCr3. However, all known attempts to observe superlattices in Fe-Cr alloys using neutron diffraction, which should be much more sensitive, have been unsuccessful. These have been reported by Shull et al.4 for 25 at. pet Cr, williams5 for 75 at. pet Cr, and Tisinai and samans6 for a 28.5 at. pet Cr. steel. The second and more prevalent opinion ascribes the 475°C embrittlement phenomenon to the formation of a coherent precipitate due to the occurrence of a miscibility gap in the Fe-Cr system below about 550°C. This latter concept was first indicated by the results of Fisher, Dulis, and Carroll,7 who were able to extract fine particles about 200Å in diameter from samples of 28.5 at. pet Cr steels aged from 1 to 3 years at 475°C. The extracted material was found to be nonmagnetic, to have a bee structure with a lattice parameter between that of iron and chromium, and to contain about 80 at. pet Cr. Williams and paxton8 and williams5 confirmed these results and first explicitly proposed the existence of a miscibility gap below the a region in the equilibrium diagram. Alloys aged within this gap

Jan 1, 1964