By Keizo Uematsu, Satoshi Tanaka, Nozomu Uchida, Yutaka Saito

"Effect of moisture content must be fully understood for controlling the granule compaction of ceramics. It changes the mechanical behavior of spray-dried granules applied for compaction process, and governs the structure and properties of .ceramics. To understand the time-dependent change in processing, the kinetics was examined for change of moisture content for granules placed in a die and the pressed compacts also. The results were explained in terms of apparent moisture diffusion coefficients. They varied non-linearly with the PVA content in the granules. The results were explained through the non-uniform PVA distribution in the granules.IntroductionMoisture must be controlled in compaction process to produce the green compacts having uniform structure. It affects glass transition temperature of binder and thus the deformation behavior of powder granules under an applied stress. Several studies [1-7] have clarified the effect of moisture content on the compaction behavior of granules and the structure of resultant compacts for both die pressing and cold isostatic pressing (CIP) of pre-formed compacts. In these studies, the moisture contents in the system were equilibrated with the humidity in the atmosphere before compaction. In practice, however, the moisture content in the system may vary with time if the relative humidity of surrounding atmosphere is different from what the granules were equilibrated previously. This is very likely case in real production processes. However, the kinetics of moisture change in the granules as well as in the pre-formed powder compacts have not been well studied. For controlling the microstructure in a system, it is necessary to fully understand the kinetics of moisture change and its relevance to packing structure of powders."

Jan 1, 2000

By Christoph Sagadin

Corrosion mechanisms between high melting synthetic ferronickel slags and refractory were investigated. The used slags were prepared by mixing and melting of specific oxides. Substrates of the applied refractory material and specimens of FeNi slags were heated in a hot stage microscope up to 1650 °C. The experiments were performed under a defined gas atmosphere of 60% CO and 40% CO2. A further examination of the formed phases between slag and refractory occurred by scanning electron microscope. The investigations indicate that the slag penetrates between magnesia grains and partly dissolves magnesia. Spot analyses show that iron diffuses into the magnesia grains, which transform to magnesiawustite, meanwhile SiO2 forms different types of olivine like forsterite and monticellite. Thermodynamic calculations confirm the formation of these phases. The combination of practical lab scale experiments and thermodynamic calculations should finally contribute to an improvement of the refractory lifetime and performance.

By René Winand

The paper gives a synthesis of research work performed in the department during the last ten years and dealing with cobalt , copper and manganese electrodeposition in chloride aqueous solutions. Special emphasis is given to electrocrystallization. For copper, properties of the electrolyte such as solubility limits, electrical conductivity and complex ions stability are discussed in connection with leaching, purification of the electrolyte, and metal recovery. When possible, kinetic parameters and probable electrode mechanisms are given. Problems that are still to be solved are also listed.

Jan 1, 1985

By Hebi Yin

A two-dimensional finite element solidification model was developed to simulate the transport phenomena occurring during laser deposition of AISI 410 stainless steel during the Laser Engineered Net Shaping (LENS®) process. The molten pool geometry and the distribution of temperature, solute concentration and velocity were calculated during deposition of a thin wall plate. An analysis of the simulations results revealed the importance of heat transfer by both conduction and convection as well as the roles of the driving forces for convection in the molten pool. The heat transfer and the flow pattern in the molten pool are considerably dependent on the travel speed of the laser beam. For the alloy and process parameters in the simulations, no significant macrosegregation was observed. The temperature-dependent properties and thermodynamic variables involved in solidification modeling were calculated using Thermo-Calc software. The results of this work contribute to the current understanding of transport phenomena in the molten pool of laser deposition processes.

Jan 1, 2008

By Bogidar V. Mihaylov

Bacterial oxidation of a low-grade sulfide gold ore was investigated in order to enhance leaching of gold. The experiments were carried out in columns using mixed cultures of Thiobacillus ferrooxidansisolated from the ore. Fractions with different screen analyses were oxidized in two regimes - one pass of the solution and circulating, solution. Constant temperature and flow-rate of the percolating solution were maintained during the experiments. A correlation between the concentrations of copper and iron in the solution leaving the columns and pH and Eh values was observed. The effect of bacterial activity was proved by means of thiourea and cyanide leaching of the oxidized ore.

Jan 1, 1991

By Orion Ciftja, Arjan Ciftja

"The directional solidification method is routinely used to produce polycrystalline silicon, an important material for the photovoltaic (PV) industry. The form of the solid-liquid interface during solidification has considerable influence on the material quality. The dissolved impurities and the solid inclusions above the solidification front affect the interface and may cause interface breakdown. We investigate the effects of pushing and engulfment of silicon carbide (SiC) particles by the solidification front during directional solidification of silicon. We employ a 12kg directional-crystallization furnace to cast the molten silicon. We use upgraded metallurgical grade silicon with low concentrations of metallic impurities (< 5ppm) and a high content of carbon (700 ppm) present as SiC particles. Samples from the cast polycrystalline silicon ingots are investigated by light microscope. The expected interaction of impurities with the solidification front is investigated theoretically using empirical models. The data obtained from the models are in good agreement with the experimental results.IntroductionDirectional solidification is a well-known method for producing multi-crystalline silicon for the PV industry. In this method a planar front, achieved during solidification, results in a clearly defined interface between the solid and the liquid phase. The solubility of major impurities is higher in the liquid than in the solid phase. Therefore, directional solidification will work as a purification process where the impurities are retained in the liquid phase [1]. Apart from the process of removing the dissolved elements in molten silicon, the directional solidification plays also another role. It will interact with the solid particles that may be present in the melt. When a liquid containing an insoluble particle is solidified, three distinct interaction phenomena are observed: engulfment of particles, continuous pushing, and entrapment [2]. The term “engulfment” is used to describe incorporation of a particle by a planar interface, and the term “entrapment” is used for particle incorporation by a cellular or dendritic interface (see Figure 1) [3]."

Jan 1, 2014

By Hiroshi Nakajima, Kotobu Nagai, Toshihiro Hanamura

"Low carbon ferritic steel bars with ultra-fine grain structure was developed through a warm rolling for the first time by the present authors. They show better low temperature toughness than conventionally hot-rolled plates. Hence, the brittle fracture surfaces in Charpy tests were examined in terms of the effective grain size of fracture, compared with those of conventional QT steels. The ductile-to-brittle transition temperatures were in good accordance with those for the QT steels if referred to the effective grain size of fracture: · However, the size was a few times that of the ferrite grain. This means the grain refining is not yet fully utilized from the viewpoint of low temperature toughness. The anisotropy of· the impact properties and the annealing effect of highly dislocated structure on the toughness are also discussed in the present paper.IntroductionFor structural materials, both high strength and good toughness are required. Well-known approaches for obtaining better toughness for steels are as follows:1) Grain refining2) Addition of Ni3) Thin plate effect by cracking parallel to the rolling direction prior to crack propagation4) Contribution of metastable austenite.Among them, only the grain refining can raise the strength and improve the toughness. And it is well known that the finer the ferrite grain size, the lower the ductile-to-brittle transition temperature. For example, in the case of 0.11 carbon steel, the transition temperature decreases linearly to in d 1/2 [1 ]. However, these have been told in the regime of coarse grain size that is larger than 10 µm in diameter. There ~as .been no study dealing with the low temperature toughness in the regime of ultra-fine grain size with a diameter in the order of 1 µm."

Jan 1, 2000

By Jingbo Liu, Zhimin Wang, Wenchao Li

"IntroductionThe advantages of non-stoichiometric perovskite material are highlighted in many papers[l]and many of this family of materials are well-suited to integration into microsensor devices. Among them, barium titanate is the most promising due to it's piezoelectric, pyroelectric, dielectric properties. Through modification, BaTiO3-based materials can be utilized in many kinds fields, such as surface wave probe; pholoconducting devices, field-effect transistor, permanent memory permanent storage, and ultrasonic transducerl2-3l. In this Paper, a series of BaTiO3-based polycrystals were synthesized by sol-gel processing which appears to be a very promising method for the manufacture of ceramic, because it offers significant advantages such as high purity, chemical homogeneity, controlled particle sizes of ceramics, and lower processing temperatures [4]. In a sol-gel process, alkoxides of the constituent elements show different reactivity toward water so that the preparation of multi-component homogenous system is difficult. In the experiment, inorganic salt was substituted for some of the alkoxides. Acetic acid which is employed for the solvent and catalyst, acts as donor ligand to titanium alkoxide and controls, the hydrolysis polycondensation reaction. Taking these aspects into consideration, we select the system Ba(OAc)2, , La(OAc)3, Ti(O11Bu)4 and acetic acid which is used as both solvent and homogeneous catalyst for the first time.ExperimentalA series of La3+-doped BaTiO3-based nano-crystals were prepared with sol-gel technology using various parameters. The precursor solution was prepared in the presence of barium acetate, lathanium acetate, and titanium tetrabutoxide monomer in butyl alcohol. According to the flow chart (fig. I.), Ba(OAc)2, La(OAch dissolved in the glacial acetic acid (0. lmol/40ml) in a three-neck flask were mixed with a solution of titanium tetrabutoxide monomer in butyl-alcohol(l 7ml/20ml) at room temperature and under constantly, vigorous stirring conditions. In most cases, the resultant solution was golden yellow and stable in the air. To this precursor solution, containing Ba, La, Ti in the desired ratio, water was added incrementally for hydrolysis under continuous stirring until sol was formed. After aging for more than 2 hours, sol was transformed to gel at room temperature. If heated during aging, the gel was formed in a shorter time. The wet gel was allowed to dry at 50°C for more than 10 hours. The dried gel was transparent or light yellow. In order to obtain BaTiO3-based nano-crystals, the amorphous dry gel was calcined at 600°C, 700°C, 800°C, 900°C, 1000°C respectively[5]. The ceramic humidity sensor was formed through the cold-pressed, aged, capsulated routes. The dried gels were crushed in an agate mortar and then pressed into discs of ? 1.5 X l.5mm (l.5mm diameter and l.5mm thickness), then held at about 16.5 MPa pressure for 3 min [6]. The disc was sintered at 1350°C and 1400°C for I hour respectively. During the processing, an Ag-Pt electrode was inserted in the sensor [7]. (See the flow chart.)"

Jan 1, 2000

By Steven C. Torma

The present article reviews some of the technologies available for recycling high-energy yield explosives loaded projectiles. These activities lead to reduction of military ammunition stockpiles and their conversion into commercial and industrial applications. The recycling technologies involve dismantling and separation of ammunition components into recyclable metals, plastics, paper and explosive materials. The metal 1 ic components will be sent to smelters, where they will be converted to products that can be used in a variety of industries, such as construction, automotive, housing and so on. Plastics and paper will be recycled and reused. Explosives will be recycled to be used for industrial purposes in the mining industry. Propellants (ammonium nitrate and ammonium perchlorate) can be ground to small particle size and treated to be used in the agricultural industry as fertilizer. In addition, some of the excess explosive material recovered in the demilitarization process may be incinerated to produce energy for steam production for heating purposes, or for production of electricity. Furthermore, this article reviews the developments in the bioremediation of explosive contaminated soils and industrial effluents.

Jan 1, 1994

By Junhong Noh, Kug Sun Hong, Jung-Kun Lee, Bo Ding

"The photocatalytic splitting of water into H2 and O2 by oxide nanoparticles has received much attention. However, the full potential of photo-catalysts for efficient hydrogen generation out of water has not been fully realized yet due to unresolved limitations including the low electrical conductivity and ineffective carrier extraction. Here, we report composite oxide materials consisting of 1-dimensional (1-D) transparent conducting oxide (TCO) core and TiO2 shell. Highly conductive ITO nanowires were grown on a flexible SUS mesh as a core component. The photoelectrodes consisting of these 1-D nanocomposites have increased carrier mobility due to the TCO core, while the TiO2 shell provides the photocatalytic functionalities. In addition, the built-in-potential at the interface between TCO core and the TiO2 shell improves the collection of charge carriers from TiO2 to TCO. These factors altogether contribute to increasing the photocurrent of the device under light.I. IntroductionPhotocatalytic behavior of semicondcutors has been extensively explored since it was discovered in TiO2 in 197Os. When TiO2 is exposed to UV light, the light is absorbed and electron/hole pairs are generated in the conduction and valeence bands. Holes in valence band will oxide/mineralize pollutant target directly or indirectly (via mediator hydroxyl radical). If the adsorbed A is O 2, O 2 will react with electron from conduction band to generate hydroxyl radical as described in the second set ofreactions. The photocatalytic reaction is schematically explained in Figure 1.Photoelectrochemical (PEC) cells using the photocatalytic reaction have attracted emerging interest as a potential route to convert solar radiation into useful forms of energy by reaction such as water splitting to generate hydrogen1 or the reduction of carbon dioxide.2 Another application ofphotocatalysis is water splitting and CO2 reduction, both of which utilize the electrons that are optically excited to the conduction band. 3•4 For this purpose, the conduction level of the semiconductor should be higher than hydrogen production level (EHZ1HZO) while the valence band should be lower than water oxidation level (Eo21112O). Electrons and holes will be generated on the semiconductor site, and holes generate O 2 at semiconductor site, while electrons will migrate to counter electrode to execute reduction forming H2. In addition to that, materials should be chemically stable to resist photocorrosion and have long lifetime of electron/hole pairs. TiO2 is a suitable material from the viewpoint of band arrangement and chemical stability requirement"

Jan 1, 2012

At the present time, cyanide is the most widely used reagent to extract gold from its ores and concentrates. However, its use in mining has become the focus of intense attack by various groups throughout the world; as a consequence, a renewed effort has been launched to find suitable alternative lixiviants to recover gold. Chlorination was the most popular process to extract gold, before it was rendered obsolete with the advent of the cyanidation process at the turn of the last century, not least because it required the use of potentially hazardous and costly chlorine to oxidize/complex the gold. The PLASTOL® process, originally designed to recover the platinum group metals (PGM?s) from their ores and concentrates, provides an alternative to cyanide for gold ores. The process generates oxidizing conditions in the autoclave capable of forming the AuIII ion, and gold chloro-complexes result from the addition of small quantities (~5-10 g/L) of sodium chloride to the autoclave. The principles of the PLASTOL® process are briefly described, and several applications of the process to gold concentrates are presented. Various options available to recover gold from PLASTOL® leach solutions are also discussed.

Jan 1, 2003

By R. Winand, M. Degrez, C. Temmerman

"The influence of the copper electro crystallization inhibitors (mainly thiourea, gelatin and chloride ions) is studied in a new fully automatic pilot plan. This paper describes the conception and the building of this plan. The new approach is to reproduce the experimental conditions observed in the industry with the three additives present simultaneously in the electrolyte and secondly to study the influence of a slight modification of the concentration of one inhibitor, the others being present in the electrolyte with their industrial nominalconcentrations.1. INTRODUCTIONDespite the fact that gelatine, thiourea and chloride ions have been used in copper electrorefining for a long time, precise knowledge concerning their influence on the cathode deposit, metallographic structure and associated properties is still lacking.Many authors studied the influence of each additive separately, or of two added at a time. Only a few authors studied the combined influence of the three additives added simultaneously. The general conclusion that can be drawn is that the combined influence is far from that forseen from the influence of each additive separately, or even from two additives used at a time. Moreover most of the experiments described in the literature were performed by adding all additives at once initially. It is however, well known that gelatine looses a great part of its activity during the first half hour due to degradation by sulfuric acid (as shown by the cathode overpotential drop). Thiourea is rapidly replaced by a number of degradation mole,cules and complex ions including cations from the solution, changing even the equilibrium between Cu, Cu(I) and Cu(II).Chloride ions are consumed by precipitation.A number of successive research projects [1-9] led pregressively to the concept that, in order to obtain reproducible results representative of industrial cathodes, it was necessary to simulate as far as possible industrial conditions. It was essential that all additives were added continuously during the electrolysis, with, as consequence, a continuous bleed.The purpose of this paper is to describe the concept of a new fully automatic pilot plan for copper electrorefining and to present the first results."

Jan 1, 1997

By N. Ono, H. Fujiwara, S. Otsuka-Yao-Matsuo, T. Omata

"The electrical conductivity and the oxygen release and uptake of sintered indium tin oxide (ITO) upon heating and cooling under the condition that P(O2)/P*=4.9X10-4 (P* = atmospheric pressure), :when P(O2) was approximately 50Pa, were simultaneously measured by using a closed-system oxygen-gas analyzer. A large increasing in -the electrical conductivity - upon the· oxygen release detected in 1130<T<1273K was observed. Quantitative relationship between the number of oxygen atom released from ITO and the conduction electron density in ITO was studied. The release of one oxygen atom agreed with the generation of two conduction electrons, i.e., the efficiency-carrier-generation for the oxygen release from the ITO was almost one. The oxygen atom released must be originally at the quasi-anion site in the C-type rare-earth lattice, i.e., the 16c site in the space group of Ia3, as an interstitial excess oxygen, Oi"". It was concluded that the mechanism of conduction carrier generation and compensation upon SnO2 doping into In2O3 can be expressed by the defect equation, 2SnO2-2Sn1n +2(1-z)e'+zOi""+3O0 x+(l-z)/2O2, and that the oxygen release bringing the increase in the electrical · conductivity can be expressed by the equation, Oi""-1/2O2+2e'.IntroductionThin films of SnO2-doped In2O 3 (generally designated as ITO, for indium tin oxide), which have high optical transparency for visible light and high electrical conductivity, have been used as transparent electrodes for liquid crystal and electrochromic displays. It is well known that the electrical conductivity of ITO depends on the content of SnOi-dopant and oxygen. However, a reliable relationship between electrical conductivity and the absolute oxygen content in ITO has yet to be reported. The elucidation of such a relationship is one of the important clues for realizing extremely highly conductive ITO electrodes."

Jan 1, 2000

By Per Anders Eidem, Merete Tangstad, Jens Davidsen

"During excavations of submerged arc furnaces producing silicomanganese, silicon carbide (SiC) has been found. Contributing to the size of the inactive area of the furnace, the active area of the furnace where reactions occur will decrease, thus reducing the potential for pre-reduction in the furnace.This work studied the formation of SiC from the liquid-solid reaction between slag, metal, and metallurgical coke. Slags and metals with different levels of silica (S1O2) and silicon (Si) have been studied. The slag and metal has been heated together with coke, and the samples investigated by microprobe. The results show that SiC was formed on the coke particle through reactions with both slag and metal. For the metal, the carbon most likely diffused through the SiC to react with Si in the alloy. SiC formation with slag is likely to go through the reduction of Si02 to Si.IntroductionToday, Silicomanganese (SiMn) is produced in submerged arc furnaces (SAF) by reduction of S1O2 and manganese oxides, mainly with metallurgical cokes. Typically, the tapped metal has a silicon content of 17 - 20 wt.%. To achieve higher levels of Si, the metal can be refined by adding off-grade silicon metal, yielding low carbon SiMn. [1]. What is believed to be SiC that has been found during dig-outs of SiMn furnaces producing high silicon alloy. It is possible that excess amounts of SiC in the furnace cause operational problems, since SiC will occupy furnace volume. As SiC accumulates, the active volume of the furnace will decrease, increasing the flow of material and gas in the active areas of the furnace. Formation of SiC is inevitable, so it is desired to keep the formation as low as possible. To be able to control the formation of SiC, one has to understand the basic mechanisms."

Jan 1, 2012

By S. Ferlay

"The main purpose of the ZIMA VAL project (Label EUREKA EU1367 and LIFE ENV/F/000278) is to demonstrate industrial scale recovery and recycling of the main components of used dry batteries (zinc, manganese dioxide, mercury, and stainless steel) into high added value products. The originality of the ZIMA VAL process resides in:1- the use of hydrometallurgy2- alkaline treatment implementation (highly selective) for zinc and mercury3- electrochemical recovery of high quality products.4- the recycling of all the battery components (zinc, mercury, manganese dioxide, stainless steel) ·5- low operating and investment costs.The process consists of physical classification, mechanical dismantling, hydrometallurgy and electrochemistry. The purpose of the demonstration plant in FALAISE (Calvados - France) is to define the technical and technological parameters of an industrial unit for the treatment of 2400 tonnes per year of used batteries."

Jan 1, 2000

By Taiping Lou

The coarsening process of precipitates in non-equilibrium systems was studied, and then a physical model of coarsening was proposed. The coarsening process of CaO&apos;TiO2 in MgO-TiO2-Al2O3-SiO2-CaO-CaF system was investigated. It is shown that the coarsening process by the model predicting is agreed with the experimental results.

Jan 1, 2000

By P. R. Bruggink

"A quantitative tool has been developed to assess the impact of changes in recycling rates on the environmental impact of aluminum supply. It has been applied to the USA to forecast sources of aluminum scrap and to examine the impact of an increase in Old Scrap recovery on the USA supply system and the subsequent effect on the Life Cycle Impact of aluminum supply. The reported data for primary, secondary and import/export supply and product shipments for aluminum in the USA show a fairly good balance between supply and demand on average over the years. Therefore, it is reasonable to use the data, along with published estimates of average product lives, recycling rates and recoveries to draw conclusions about future aluminum scrap generation· and recovery. The Life Cycle Impacts of increasing post-consumer recovery rates to recover an additional 450,000 MT/yr (1 billion lb/yr) has been estimated using the model.The spreadsheet model upon which this work was based was developed in U.S. Customary units. Converting the figures to Metric units would have required converting the entire model and rebuilding the figures. I have chosen to leave the figures in U.S. Customary units. I apologize for any inconvenience this may cause."

Jan 1, 2000

By S. H. Castro

In 1997 Chile was the world&apos;s largest copper mine producer with around 3.4 million metric tomes of copper. Conventional technology (conminution-flotation- smelting-converting-electrorefining) for copper sulfide ores was used. For copper oxidized ores hydrometallurgical processes (heap leaching-solvent extraction- electrowinning) were employed. Consequently, the most important waste effluents include flotation tailings, gaseous emissions, smelter slags, acidic and alkaline wastewater, electrolytic sludges, solid residues from leaching, etc. The introduction of stricter environmental regulations are forcing the Chilean industry to minimise the generation of waste and promote cleaner production. Gas emissions such as SO2 and arsenic from smelters and process wastewater are the major problems at this stage. The environmental impact assessment of gas emissions in all six largest smelters namely Chuquicamata, Caletones, Potrenllos, Ventanas, Paipote and Chagres led to design a "decontamination plan." The implementation of this plan resulted in (i) the installation of sulfuric acid plants for SO2 abatement and (ii) the installation of electrostatic precipitators to remove arsenic oxides condensed from cooling gases. The aim of this paper is (i) to describe the type of waste associated to the various stages of the metallurgical processes and (ii) review the main abatement technologies used in medium and large size companies.

Jan 1, 1999

By Y. Y. Liu, H. M. Domanus, W. T. Sha

"Casting is fundamental to manufacturing of many types of equipment and products. Although casting is a very old technology that has been in existence for hundreds of years, it remains a highly empirical technology, and production of new castings requires an expensive and time-consuming trial-and-error approach.In recent years, mathematical modeling of casting has received increasing attention; however, a majority of the modeling work has been in the area of heat transfer and solidification. Very little work has been done in modeling fluid flow of the liquid melt. This paper presents a model of fluid flow coupled with heat transfer of a liquid melt for casting processes. The model to be described in this paper is an extension of the COMMIX code and is capable of handling castings with any shape, size, and material. A feature of this model is the ability to track the liquid/gas interface and liquid/solid interface. The flow of liquid melt through the sprue and runners and into the mold cavity is calculated as well as three-dimensional temperature and velocity distributions of the liquid melt throughout the casting process.IntroductionBower et al. (1), in their 1969 review of the evolution of some of the casting techniques, stated that:""The evolution of technology requires alternatives to be available so that choices can be made that lead to changes. The role of solidification science and other disciplines related to casting technology is to develop a better understanding of process and product, so that a wider range of alternatives is possible.Alternatives, whether from science or from invention, must lead to improvements in casting ""utility."" Utility, or economic advantage, must include consideration of total system costs, and final product value. The cost of materials, melt processing and finishing should be optimized with casting costs, since all are part of the production system. It is the favorable relationship between total processing costs and product value that makes a change in casting technology viable, but the best change is not possible unless technology has provided an understanding."""

Jan 1, 1986

Testing is in progress to address compatibility issues with regard to long term storage of plutonium in contact with two different intermetallic systems. The two intermetallic systems are: 1. dental amalgam, i.e., mercury plus silver alloy powder, and 2. liquid gallium alloy plus copper powder. Both of these are plasto-metallic materials that undergo a solidification reaction at room temperature. Each system is allowed to react in contact with both high-purity alpha plutonium and a delta stabilized plutonium alloy at varying temperatures in an argon atmosphere. Wetting characteristics and possible interaction will be studied metallographically in the post-mortem condition. Complete results including metallographic examinations will be presented.

Jan 1, 1995