By J. W. H. Clare

An equilibrium isotherm at 550°C is given for ternary alloys rich in aluminum containing 0 to 15 wt pct Cr and 0 to 20 wt pct Mn. Phases encountered are: aluminum solid solution; stable temary compound G; and MnAl8,. In addition, a limited number of alloys were annealed at 450°C to check for differences from the 550°C isotherm. These experiments limited the composition of the G phase at 550°C and further experiments established that the G Dhase is not stable above 590 ± 1 °C. RAYNOR and Little1 established several equilibrium isotherms using aluminum-rich alloys containing up to 5 pct of the elements chromium and manganese. These isotherms showed that, in addition to an a solid solution and the two binary intermediate compounds 8 and MnAl6, a stable ternary compound ex-isted in the system. This phase was called the G phase because of its ghostly appearance in micro-sections. Little, Raynor, and Hume-Rothery2 found a similar phase in binary aluminum-manganese alloys and, as a result of their experiments, concluded that the G phase was a metastable phase existing in the aluminum-manganese system. This phase was stabilized by the addition of chromium. The constitutional work of Raynor and Little,' although showing the existence of the G phase in the aluminum-chromium-manganese system, did not establish precisely the composition limits of the phase or the temperature above which the phase became unstable and disappeared from the system. The work described in this paper was undertaken to provide this information. An examination of the previous work' showed that an isotherm at 550°C would provide the required data regarding composition in the shortest possible time, as the (a + G) phase field narrows considerably at higher temperatures. The same work showed that the G phase ceased to exist between 580° and 595°C. A more precise estimate of the transformation temperature would therefore be obtained by annealing selected alloys at successively higher temperatures beginning at 580°C. EXPERIMENTAL PROCEDURE 1) Materials Used—The experimental alloys were prepared from four master alloys containing 15.00 w pct Cr, 15.28 wt pct Cr, 19.80 wt pct Mn, and 19.38 wt pct Mn which were made from super-purity aluminum, electrolytic chromium, and electrolytic manganese. The aluminum was of 99.996 pct purity, the principal impurities being copper, iron, and silicon. The chromium and manganese were 99.9 pct pure, the principal impurities being antimony, calcium, and magnesium. 2) Preparation of the Experimental Alloys—The alloys were prepared in 20-g quantities by melting together the requisite amounts of master alloy and aluminum in an alumina-lined crucible and, after thorough stirring with an alumina rod, cast into a cold copper mold to give ingots 1/4 in. in diam and 3 in. in length.

Jan 1, 1960

By P. Niessen, S. J. Bercovici

RECENTLY Aust et al.&apos; proposed a model of non-equilibrium grain boundary segregation based on a vacancy gradient induced uphill diffusion process of solute to grain boundaries. According to their proposal, solute atoms which are attracted to vacancies would, during the cooling of a sample, migrate with vacancies toward grain boundaries (vacancy sinks) and thereby enhance the solute concentration in boundary regions. For solute atoms which are not attracted to vacancies no such boundary solute enrichment would be expected. These concepts were given experimental support by boundary and bulk mi-crohardness measurements of various thermally treated dilute zinc and lead alloys and also doped aluminum oxide. The underlying assumption in their work was that solute enrichment in boundary regions is indicated by higher microhardness values. From thermodynamic considerations1&apos;2 it appears that the solid-liquid solute distribution coefficient (K), defined as the concentration of solute in the solid to the concentration of solute in the liquid at equilibrium, indicates whether attractive or repulsive forces exist between vacancies and solute atoms. K < 1 indicates a solute-vacancy attractions, K > 1 indicates no, or a repulsive, vacancy-solute interaction. This note is to report on observations of different grain boundary etching phenomena in high purity zinc alloys. These phenomena appear to depend on whether a K < 1 or K > 1 solute is present. In experiments designed to measure directly the solute enrichment in grain boundary regions, samples of zone refined zinc with 0.1 at. pct solute additions were cooled from 380°C at a rate of 3°C per min. A surface layer of approximately 50 was then removed from the samples by chemical polishing. The samples&apos; surfaces were then protected by a chromating treatment such that in a subsequent etch only grain boundary regions were dissolved. The dissolved regions were approximately semicircular troughs, 10 µ in width. The grain boundaries were usually in the middle, i.e., at the bottom, of this trough. For zinc containing the K < 1 solutes cadmium and aluminum, the grain boundary was always indicated by a ridge as shown in Fig. 1. For pure zinc, and zinc containing the K > 1 solutes copper and gold, a groove at the bottom of the trough indicated the boundary position, Fig. 2., To test if these different grain boundary etching behaviors were possibly connected with the segregation process discussed above, the Zn-Cd alloy was again heated to 380°C and quenched into brine. After surface protection and etching it was found that this specimen no longer exhibited the grain boundary ridges but rather grain boundary grooves as shown in Fig. 2. It would appear, therefore, that the boundary ridge is a consequence of a process occurring during the slow cooling of the samples. From absorption spectrophotometric analysis it was found that for slowly cooled samples containing K < 1 solutes, the solute/zinc ratios of the material from the boundary trough were consistently considerably higher than the solute/zinc ratios of the bulk alloys. This boundary region solute enrichment was not observed in quenched samples. It is concluded therefore, that the boundary ridge shown in Fig. 1 is directly or indirectly connected with nonequilibrium solute segregation.

Jan 1, 1970

By AIME AIME

The XCVIIth meeting of the Institute for the reading and discussion of papers will be held at Spokane, Wash., beginning Monday, Sept. 27, 1909, as already announced in Special Circulars of May 8 and Aug. 14, 1909, and in the Bulletins for June, July, and August. The meeting will be preceded by a tour through Yellow stone Park and visits to Butte and Anaconda, and will be followed by visits to the Coeur d&apos;Alene district, to the Alaska-Yukon-Pacific Exposition at Seattle, to the mining- and smelting-plants near Salt Lake, and to the iron- and lead- and zinc-plants at Pueblo. The special train for the party&apos; will leave Chicago, September 16, and return about October 12. Details of the itinerary are given later in this announcement. The Secretary of the Spokane Local Committee is Lyndon K. Armstrong, 615 Hyde Block, Spokane, Wash., to whom should be addressed all inquiries concerning local matters. The control of the papers and proceedings will remain in charge of the Institute office, as usual. It is greatly to be desired, both in behalf of the Institute and in recognition of the many courtesies to be extended on the trip, that the excursion party be made larger. Exceptional facilities to visit the many mines and smelters have been freely provided; and members are requested to make all reasonable effort to attend the meeting at Spokane and participate in the excursions. For those who cannot join in the entire trip, it may be possible to provide special Pullman accommodations after leaving Yellowstone Park. In order to make the necessary arrangement, however, the names of members and guests contemplating this partial trip should be sent at once to Theodore Dwight, 29 West 39th Street, New York City. The general cost of the trip per member will be $300, which includes transportation, berth, and meals for the entire trip from

Sep 1, 1909

By Gerhard Bockstiegel

Kuczynski&apos;s formula has been derived for the case of nonspherical particles. TWO formulae of Kuczynski&apos;s type have been derived, one describing the increase in tensile strength, the other describing the progress of shrinkage of a powder compact. It has been strength,shown that the exponents of all three formulae each contain two magnitudes of different physical characters, viz, the geometrical factor a and the kinetic factor ß. The interrelationships between the three exponents are stated. SOME years ago Kuczynski1 experimentally showed that the radius, x, of the area of contact between very small spherical metal particles and a metallic block is related to the time of sintering, t, by the following equation x = constant tk [11 where k has the value 1/5 or 1/7. Assuming that the metal particles were perfect spheres and the metallic block was perfectly flat, he derived the foregoing equation from theoretical considerations of the process of material transport in metals, and he showed that exponent k is different for different mechanisms of transport, e.g., k = 1/2 for viscous flow (according to Frenkel2), k = 1/3 for evaporation and condensation, k = 1/5 for volume diffusion, and k = 1/7 for surface diffusion. From this Kuczynski concluded that the mechanism of transport was either volume diffusion or surface diffusion, depending on whether the value of k, as found in his experiments, was 1/5 or 1/7. Subsequently. Cabrera8 corrected Kuczynski&apos;s calculations with regard to surface diffusion, showing that the theoretical value of exponent k is 1/5 for both volume and surface diffusion. He supposed that the different experimental values of k were due to slight differences in the shape of the metal particles. An exponential relationship similar to the aforementioned was found by Okamura, Masuda, and Kikuta,4 Masuda and Kikuta, and Takasaki8 when studying the rate of shrinkage on powder compacts during sintering. The authors measured the shrinkage by means of the fraction w = Vp — V./Vp — V,,,, where V,, is the volume of the green compact, V, is the volume of the sintered compact, and V,,, is the volume of the compact in its densest state. This fraction, w, they found, is related to the time of sintering, t, by the equation w == constant tm. [21 Further, Bockstiegel, Masing, and Zapf7 observed that the tensile strength, s, of sintering iron powder compacts can also be related to the time of sintering, t, by an equation of the foregoing type, i.e., s = constant tn. [3] For exponent n the values 0.28 (S=2/7) and 0.35 ( 2/5) were obtained, and the authors pointed out that there might exist a simple interrelation between exponent n as found in their experiments and exponent k in Kuczynski&apos;s equation. The authors supposed that 2k = n, since the strength of adhesion between a metal sphere and a block (as in Kuczyn-ski&apos;s experiments) must approximately be proportional to their contact area, p. x2. Theoretical Considerations This paper is an attempt to correlate the fundamental experiments of Kuczynski&apos;s type with the results obtained with powder compacts as represented by Egs. 2 and 3. In particular, the paper is to show how the rate of sintering is influenced by the geometry of the sintering particles and by the type of material transport. As the geometry of particles conglomerating in a powder compact is very complex, some simplifying assumption has to be made, of course, in order to adapt the problem to mathematical treatment. In the following paragraph a suitable simplification is introduced, and Kuczynski&apos;s formula is derived for the case of nonsphcrical particles. Relation Between Area of Contact and Sintering Time—As the face of contact between two particles in a sintering powder compact is not necessarily a circle (as in the case of spheres sintering to a block), Kuczynski&apos;s formula is modified as follows: Let the perimeter of the face of contact be described by means of polar coordinates R, 4, as shown in Fig. la, so the area of contact, f, is determined by f= 1/2 . S112p[R(Æ) ]2 dÆ [4] Then, let the two particles be intersected by a plane perpendicular to area f. The intersection is shown in Fig. lb. According to the nomenclature in this figure, the distance, h, between the surfaces of the two particles is a function of T and Æ: h = h(r,Æ). For the particular case of spherical particles, as in Kuczynski&apos;s theory, this function becomes: h = constant r2. It shall be assumed here that in the close neighborhood of their

Jan 1, 1957

By K. E. J. Rapperport, C. S. Hartley

The only slip system observed in zirconium crystals deformed at 77", 575", and 1075OK was (1010) [1210] with a critical resolved shear stress in tension of 1.0 kg per sq mm at 77°K; 0.2 kg per sq mm at 575 °K; and 0.02 kg per sq mm at 1075 OK. The active twin planes were {1012}, (1121}, (11221, and (11233) with varying temperature dependence. A detailed analysis for the slip direction using Laue spot asterism is appended. NeARLY all metals of the hexagonal close-packed structure exhibit basal slip, i. e.,(0002)<1120>- type slip. This is true of magnesium,&apos; zinc,&apos; cadmium,3 beryllium,4 titanium,= yttrium,6 and rhenium.Many of these such as titanium 5&apos;8-&apos;0beryllium,4&apos;" magnesium, and zinc13&apos;14 display other slip modes even at room temperature, and nearly all have been reported to slip on other systems under particular loading or temperature conditions of testing. As is shown in this paper, basal slip was not found at any of four test temperatures from 77" to 1075°K in hexagonal close-packed zirconium under the simple loading conditions of tension and compression, even though in one case the resolved shear stress on the inactive (0002) <llgO> system was twenty-five times higher than the critical resolved shear stress on the active (1010) [1210] system. This result is consistent with prior studies on the active deformation processes in zirconium deformed at room temperature. &apos;&apos;-I7 SPECIMEN PREPARATION A) Material—The zirconium used in this work was of two types: 1) as-deposited reactor grade crystal-bar, and 2) arc-melted and forged reactor grade crystal-bar. Typical chemical and spectrographic analyses of these materials as received, and after hydrogen removal and crystal growth are given in Ref. 17. Crystals of type 1) above have the letter prefix (A) and those of type 2) have the prefix (B) throughout this paper. B) Crystal Growth— he zirconium was machined into rectangular parallelepipeds about 0.2-in. scl in cross section and 2 in. iong. These were hand polished through 4/0 abrasive paper, electropolished, given a hydrogen removal anneal, and subjected to long-time anneals at 840 °C in vacuo to produce usable crystals.&apos;7 A second technique used to obtain large crystals was to cycle the samples two or three times between 1200" and 840°C, allowing them to remain at the higher temperature for about 4 hr and at the lower temperature for 5 days.17 These techniques yielded some grains which occupied the entire cross section of the bar and were as long as 3/4 in. C) Orientation Determination—After the growth of large crystals by thermal cycling, the samples were repolished with extreme care through 4/0 abrasive paper and electropolished. Metallographic examination after polishing showed the surfaces to be free of visible deformation traces. Standard Laue back-reflection X-ray techniques were used to find the crystallographic orientations of selected large grains with respect to a specimen face and edge. Fig. 1 shows the stereographic projections of the stress axes for the crystals used. The sharpness of the spots on the Laue photographs indicated that the crystals were of good quality. EXPERIMENTAL METHODS Nine crystals were deformed in tension at 77"K, nine in tension and five in compression at 300°K in previous tests,17 fifteen in tension at 575"K, and eleven in tension at 1075°K. All specimens were stressed by load increments. After a predetermined load was applied, the specimen was removed from the loading appratus and metallographically examined for deformation traces. An attempt was made to initially stress each bar so that some crystals slipped a small amount and others not at all. This was done to bracket the critical resolved shear stress. One bar of special orientation (B-11) was repolished and annealed at 1075°K for 1 hr after lower temperature deformation, before final deformation at 1075°K. In the other bars the loading by increments, followed by metallographic examination, was continued until the surface distortion would interfere with analysis, or until fracture. One example of a crystal pulled to fracture is shown in Fig. 2. This photograph shows a crystal (B-14C) which was pulled at 1075°K and failed by slip on two (10i0) planes. The approximate orientation of this crystal is illustrated in the figure. Specimens were deformed at 77°K in liquid nitrogen on a tensile machine using an insulated bucket with an internal hook to accept a clamped specimen.

Jan 1, 1961

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members and guests who registered at Institute headquarters during .the period Jan. 10 to Feb. 10, 1915: N. H. Emmons, 2d, Dover, Mass. R. 0. Hocking, Redruth, England. Paul W. Gaebelein, Cornucopia, Ore. G. H. Carnahan, New York, N. Y. H. D. Kinney, Easton, Pa. W. A. Wilson, Salt Lake City, Utah. W. D. McDougall, New York, N. Y. H. V. Winchell, Minneapolis, Minn. Kirby Thomas, New York, N. Y. Mrs. H. V. Winchell, Minneapolis, Minn. V. T. Lawshe, Newark, N. J. Keijiro Nishio, Tokyo, Japan. Henry S. Stebbins, who has been connected with the firm of Oglebay, Norton & Co., Cleveland, since 1892, has resigned to accept a position with M. A. Hanna & Co. of the same city. E. L. Newhouse has been chosen First Vice-President of the American Smelting & Refining Co. in place of the late Barton Sewell.

Jan 3, 1915

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members and guests who registered at Institute headquarters during the period Sept. 10 to Oct. 10, 1914: James D. Mooney, Akron, Ohio. J. Kojima, Ashio Copper Mine, Japan. Bernard A. Wilkinson, Guadalajara, H. Starkweather, Cripple Creek, Colo. Mexico. S. S. Langley, New York, N. Y. A. B. Parsons, Candor, N. C.. J. H. Warder, Chicago, Ill. Arthur Feust, Santo Domingo, Nicaragua. Lloyd T. Buell, Butte, Mont. G. B. Marshall, New York, N. Y. George R. Rogers, Gowganda, Canada. Henry Krumb, Salt Lake City, Utah. H. 0. Hammond, Douglas, Ariz. Herbert S. Kohlberg, El Paso, Texas. Percy E. Hohne, El Oro, Mexico. Wilbur L. Cross, Jr., Glen Carbon, Pa. Percy E. Barbour, Candor, N. C. Thomas H. Leggett, formerly-in charge of the mining interests of the American Smelting & Refining Co., has resumed practice as consulting engineer with offices in the Singer Building, New York, N. Y.

Jan 11, 1914

(Members are urged to send in for this column any notes of interest concerning themselves or their fellow-members.) Members and guests who registered at Institute headquarters during the period April 1 to 15. William B. McKinley, New York, N. Y Collier Cobb, Chapel Hill, N. C. C. W. Goodale, Butte, Mont. E. P. Fleming, Guayacan, Chile. D. C. Brown, San Luis Potosi, Mex. Albert Sauveur, Cambridge, Mass. W. H. Rettie, Yonkers, N. Y. H. M. La Follette, La Follette, Tenn. Mark B. Kerr, San Francisco, Cal. E. Fleming L&apos;Engle, New York, N. Y. H. W. Turner, San Francisco, Cal. H. Garlichs, St. Louis, Mo. Frank M. Leland, Mackay, Idaho. Henry Hay, London, England. Sir Robert Hadfield, London, Eng. Edward J. Way announces that his agreement as consulting engineer in South Africa for the Anglo-French Exploration Co., Ltd., having terminated, he will engage in professional consulting work with headquarters at 135 Cullinan Buildings, Simmonds St., Johannesburg, South Africa.

Jan 5, 1914

By Hal T. Morris

The main Tintic mining district in central Utah has produced approximately 13,500,000 tons of ore, containing silver, lead, gold, copper, zinc, and other metals, valued at more than $315,000,000. More than 90 per cent of this ore has come from large, irregular ore bodies that have replaced folded and faulted limestone and dolomite strata. Of lesser importance are replacement veins that chiefly cut contact-pyrometasomatized carbonate rocks and fissure veins that cut altered intrμsive bodies and volcanic rocks. The district is in the west-central part of the East Tintic Mountains, a north-trending fault-block range near the eastern margin of the Great Basin. The consolidated sedimentary rocks exposed at the surface and in mine workings are miogeosynclinal deposits more than 10,000 feet thick that range in age from late Precambrian to Late Mississippian. They are folded and strongly faulted and are partly overlain by volcanic tuffs and agglomerates and by extensive flows of porphyritic and vitrophyric quartz latite, latite, and trachyandesite of Eocene age. All of these rocks are locally concealed beneath thick alluvial deposits of Pliocene and Quaternary age. The Eocene and older rocks are cut by dikes, sills, and small stocks of porphyritic quartz monzonite, monzonite, and latite, which are genetically related to the ore deposits. The district is inactive except for the production of halloysite clay and for minor leasing activity and exploration ventures. Several exploration targets remain untested.

Jan 1, 1968

By G. L. Smit

The Buffelsfontein Gold Mining Company is situated in the Klerksdorp district of the Province of the Transvaal in the Republic of South Africa, approximately 100 miles west of Johannesburg. Gold production commenced in January 1957 and Uranium treatment of residue slimes as a by-product started in July 1957. The mining property is 5435 mining claims in extent, the equivalent of 7988 acres or 12.5 sq miles. The mine was initially exploited by the Pioneer Twin Shaft System, consisting of a 26-ft diam down-cast shaft and a 22 ft-diam up-cast shaft, sunk in the north-west area of the mine to cater for the hoisting and ventilation requirements for a milling rate of 150,000 tons per month. To exploit the Eastern zone of the property and assist in increasing production to 200,000 tons milled per month, it was decided to sink a further Twin Shaft System consisting of a 28-ft diam downcast shaft and a ventilation up-cast shaft -22-ft in diam, both monolithic concrete lined — 200 ft apart and 5300 ft deep. This paper deals with the sinking and commissioning of these Eastern Twin Shafts. This was achieved by one sinking crew within a period of 20 months. A) PLANNING 1) Siting: The Eastern Shaft System was sited in the north-east area of the property, 12,000 ft east on strike from the Pioneer System. (Fig. 1). Initially the system was sunk to the 5300 ft elevation to conform with the original Pioneer Shaft System. On completion a sub-vertical main shaft will be sunk to the 8000 ft elevation in the immediate vicinity, and subsequently the surface ventilation shaft will be deepened to this elevation by raising from level to level and sliping to full size. The exact positions of the shafts were chosen after: a) underground development had located certain known water bearing zones, and b) geophysical and topographical surveys had been carried out. The shafts passed through the following geological succession: Surface to 4430 ft - Dolomites of the Transvaal System 4430 to 4470 ft - Quartzites and conglomerates of the Black Reef Series of the Transvaal System. 4470 to 4470 ft - Diabasic Lava of the Venters-dorp System (Ventersdorp Contact Reef at base). 4470 to 5250 ft - Quartzites of the Elsburg Series of the Upper Witwaters-rand System. The shafts were sited to ensure that the least possible water would be encountered during sinking, and this contributed to the rapid rate of sinking. 2) Duties: a) The 22-ft diam ventilation shaft was designed to up-cast 1,400,000 cfm of air (0.060 density) against a resistance of 22 in. water gauge. b) The main shaft was designed to handle 160,000 tons hoisted per month as well as the men, material and down-cast ventilation to serve this tonnage. The 284 diam main shaft is equipped with streamlined buntons spaced at 15 ft centers set in pockets which were left during sinking. There are six compartments, four of which are sewed by two dual purpose hoists, hoisting either, twedeck man cages or 13-ton bottom discharge skips. The other two compartments are served by a single purpose winder hoisting double deck cages accommodating 60 men per deck. (Fig. 2). 3) Timing: Permanent equipment was ordered well in advance to insure continuity in the operation. Development underground reached the shaft positions before the start of sinking operations. From this development, boreholes were drilled into shaft positions to drain off water in the vicinity of the shafts. To ensure complete co-ordination of effort, all relevant data, as well as the allocation of responsibility, were made known to all persons and departments concerned. 4) Models: The extensive use of scale models during the preliminary planning stages proved most useful in deciding on design such as buntons, bunton pockets and guide cleats, and complex layouts concerning loading, spillage and pumping arrangements. (Fig. 3). These models also proved invaluable in determining the walling routine. Normal working conditions could

Jan 1, 1964

By A. J. W. Schwandt

Magmont is a venture jointly owned by Cominco American Incorporated of Spokane, Washington and Dresser Minerals, Division of Dresser Industries, Houston, Texas. Cominco American assumed direction of the operation in 1961 and completed exploration, preproduction planning and development, and is now the operating partner managing the operations. The plant has a rated capacity of 4200 tpd and produces in excess of 60,000 tons of lead per year. [ ]

Jan 1, 1970

[Trans. No. Place Date Vol. Page 1. Wilkes-Barre, Pa.* May, &apos;71.. 1 3 2. Bethlehem. Pa Aug., &apos;71.. 1 10 8. Troy, N. Y Nov., &apos;71.. 1 1S 4. Philadelphia, PaFeb., &apos;72.. 117 5. New York, N. Y.*May: &apos;78.. 120 5. Pittsburgh, PaOct., &apos;72.. 125 7. Boston, MassFeb., &apos;78.. 128 8. Philadelphia, Pa.* May, &apos;78.. 2 3 9. Easton, POct., &apos;78.. 27 10. New York. N. YFeb.. &apos;74.. 2 11]

Jan 1, 1946

APPROXIMATELY 26 percent of the total ore production to date from the largest single deposit of copper-bearing material in the world was mined during the war years, 1942 to 1945, at Chile Exporation Company&apos;s great open-pit mine at Chuquicamata, Chile. About 18 percent of the total waste removed during the life of the mine was handled in the same period. The total of ore and waste represents approximately 24 percent of the total material that has been excavated from the pit. This is more than was removed in the first fourteen years of operation from 1914 through 1927. The pit at Chuquicamata is 17/8 miles long, 1/2 mile wide, and has a present vertical extent of 817 ft between the top of the highest bench and the lowest bench being worked. However, when

Jan 1, 1948

By Kenneth K. Humphreys

INTRODUCTION What is automation? Why automate? Webster&apos;s New Collegiate Dictionary defines automation as "the automatically controlled operation of an apparatus, process, or system by mechanical or electronic devices that take the place of human organs of observation, effort, and decision." This definition gives an implied answer to the second question, "Why automate?" Automation, automatic control devices, and process control equipment receive their justification in supplementing or replacing manpower, which results in decreased operating costs. In the past, processes were operated with the minimum amount of instruments needed merely to guide operators. Processes were manually con- trolled by the operator on the basis of simple temperature, pressure, flow, and level indications on a panel. Today the tendency is to design a new plant to operate in a fully automatic manner according to a preset pro- gram utilizing a minimum of manpower. In addition to this direct cost reduction in manual labor, increased equipment capacity results from uniformity of flow and uniform control of process variables. This control eliminates or minimizes surges and permits equipment to be operated at or near its ultimate capacity and, for a given material throughput, permits the use of smaller process equipment. Automatic control, therefore, be it in the field of coal processing or in any industrial field, is simply a problem of economics. Control equipment is justified in terms of its contribution toward increasing productivity, increasing profit margins, or producing a new and salable product at a profit. Instruments and control devices can be divided into two general groups: (1) units which measure and (2) units which both measure and control a process variable.

Jan 1, 1979

By J. F. Smith, J. E. Davison

The heat capacity of CaMg2 was measured over the temperature interval, 4.8° to 287°K, by the technique of low-temperature adiabatic calorimetry. Heat content measurements were performed with a drop calorimeter over the temperature interval, 273" to 673°K. From these data the thermodynamic functions, (FT - H0)/T, ST - So, and & - Ho, were evaluated. A third-Law calculation of the standard entropy of formation of CaMg2 yields a value of -0.25 * 0.06 cal per (°K g-atom) , and the free-energy function derived from this study when combined with existing equilibria data yields a value for the standard enthalpy of formation which is in agreement with direct calorimetric enthalpy measurements. The accompanying paper&apos; shows that the enthalpy of formation of CaMg2 has been determined with good precision by three different calorimetric techniques.&apos;-= TWO independent determinations of the Gibbs free energy of formation of CaMg2 have also been made; both determinations were based on vapor pressure measurements, being in one case hydrogen vapor pressures over ternary Ca-Mg-H alloys4 and in the other case magnesium vapor pressures over binary Ca-Mg alloys.5 The present determination of heat capacity of CaMg2 below room temperature and of the heat content of CaMg2 above room temperature was undertaken to provide supplementary data. These data are useful in their own right but can in addition be used to evaluate an entropy of formation for CaMg2 which, because of the interrelation of free energy, enthalpy, and entropy, can be used as a check of the self-consistency of the composite of the presently available information. LOW-TEMPERATURE HEAT CAPACITY The heat capacity of CaMg2 was measured over the temperature interval 4.87° to 286.64°K in an adiabatic calorimeter. The physical details of the calorimeter and the experimental procedure for measuring the heat capacity of a specimen have been adequately described by Gerstein et a1.6 The source and purity of the calcium and magnesium are described together with the methods of sample preparation and chemical analyses in the accompanying paper.&apos; Results of chemical analyses of the material which was used in the present investigation are shown in Table I. These analyses show that, on the basis of the published phase diagram,7 the heat capacity sample contained a slight excess of a calcium while the heat content sample contained a slight excess of magnesium. However, in both cases the excess was small, and X-ray diffraction patterns showed reflections which were without exception attributable to CaMg2. The sample which was used for heat capacity measurements weighed 69 g while the sample container and addenda weighed 132 g. The sample was in the form of annealed powder, 50 to 60 mesh, and was sealed into the sample container under 0.1 atm of helium. Copper fins inside the sample container facilitated thermal equilibrium of the powdered Sample. Time intervals of the order of 10 min were required for thermal equilibration, and such times are normal for this calorimeter regardless of the form of the sample. The observed heat capacities were corrected for the small excess of a calcium through use of the heat capacity values tabulated by Hultgren et a1.8 The corrected heat capacities are tabulated as a function of temperature in Table II. The free-energy function and the absolute entropy of CaMg2, which were calculated from the experimental heat capacity data, are listed in Table 111. A smooth curve was fitted to a plot of the experimental values of the heat capacity and in only two instances above 30°K did the plotted points deviate from the curve by more than 0.2 pct. Below 10°K the deviation of several of the points was as much as 50 pct. These large percentage deviations were attributed to the small value of the heat capacity and to the low sensitivity of the platinum resistance thermometer in this temperature range. The deviations in the region of 10°to 30°K were less than 5 pct. Although the percentage deviations of some of the low-temperature measurements are large, the actual value of these deviations is small since the magnitude of the heat capacity in that temperature range is small. The error in the value of the third-law entropy at 298.15°K was estimated to be less than 0.01 cal per (°K g-atom). A value of -0.25 ±0.06 cal per (°K g-atom) was obtained for the standard entropy of formation at 298.15°K from the relation:

Jan 1, 1969

By E. C. Burke, W. R. Hibbard

Plastic deformation in magnesium single crystals was studied by tensile tests at room temperature utilizing an improved preparation and testing technique. Consistent critical resolved shear stress values for basal slip were obtained. The advent of pyramidal slip at room temperature was rationalized upon the basis of grip constraints. A bend-twinning hypothesis was advanced as an explanation of mechanical twinning which occurs as a complex stress-relief mechanism. INVESTIGATIONS of the plastic deformation of magnesium have been limited to the determination of the fundamental kinetics which may be summarized as follows: 1—Twinning on the {102).l 2— Slip on the (001) plane in the [loo] direction at room temperature.&apos; 3—Slip on the {101) or {102) plane in the [loo] direction above 225°C." 4—Critical resolved shear stresses for basal slip in tension at room temperature of 83 g per sq mm with a variation from 57 to 127 g per sq mm." Bakarian&apos; studied the compression of thin wafers of magnesium single crystals and classified the components of the deformation mechanisms as follows: 1—The Basal field: (001) at an angle of less than 20" to the compression surface. Fracture along {101} or slip on (001) followed by {101} fracture. 2—The prism field: (001) at an angle greater than 60" to the compression surface. Twinning on the {102) generally occurring during the early stages of loading, basal slip in the areas of original orientation and (001) slip within twins. 3—The central field: (001) at angles greater than 20" but less than 60" to the compression surface. Slip on the (001). 4—The critical resolved shearing stress for {101} slip above 225°C was 400 g per sq mm. Observations of mechanical twins in hexagonal close-packed metals have been summarized by numerous investigatorsb-&apos; emphasizing a lateral or rotational atomic adjustment, in addition to the pure twinning shear, and the importance of reorienting the basal plane to a position more favorable for continued slip, rather than the resulting small dimensional changes. Criterion for the operative twinning planes has not been clearly established. Schmid and Boas hurmised that an energy condition related to the atom movements is the determining factor. MillerQ bserved that twinning stresses in zinc crystals decreased as the amount of prior deformation increased. Preparation of Specimens Magnesium single crystals % in. in diam x 8 in. long were grown from the melt under an argon atmosphere in a gradient furnace similar to that described by Jillson." Magnesium containing 0.018

Jan 1, 1953

By Desio S. Oddone, Mark C. Malamphy, Irnack C. Do Amaral

Most igneous rocks, and particularly those of the basic type, contain relatively high percentages of magnetite and other iron oxides, which give them moderately high magnetic susceptibilities and make them responsible for an important percentage of the magnetic anomalies observed during the course of geophysical surveys by the magnetic method. The irregular form and high susceptibility of the igneous rocks make them readily polarizable and the position and strength of the magnetic poles formed are not always explicable by theoretical calculations of anomalies due to certain assumed forms in the normal magnetic field of the area under study. During the last four years our field work has permitted us to make detailed observations of anomalies due to igneous rocks in all the states of south Brazil. The form and position of the igneous rock at some places were fairly accurately known, which made it possible to calculate theoretical anomalies and compare them with the observed data. Some of the data we obtained have been published and additional cases are now awaiting publication. In this paper, we will present a few specific cases where the geology is moderately well known and which we believe to be of considerable value as representing typical magnetic anomalies in the south magnetic hemisphere, where the inclination of the magnetic field is very low. Although the vertical intensity is negative in the Southern Hemisphere, we have adopted the convention of plotting increase in intensity (negative) as a positive anomaly; i.e., above the x axis. This convention facilitates comparison with anomalies in the north.

Jan 1, 1940

By Irnack C. Do Amaral, Mark C. Malamphy, Desio S. Oddone

Most igneous rocks, and particularly those of the basic type, contain relatively high percentages of magnetite and other iron oxides, which give them moderately high magnetic susceptibilities and make them responsible for an important percentage of the magnetic anomalies observed during the course of geophysical surveys by the magnetic method. The irregular form and high susceptibility of the igneous rocks make them readily polarizable and the position and strength of the magnetic poles formed are not always explicable by theoretical calculations of anomalies due to certain assumed forms in the normal magnetic field of the area under study. During the last four years our field work has permitted us to make detailed observations of anomalies due to igneous rocks in all the states of south Brazil. The form and position of the igneous rock at some places were fairly accurately known, which made it possible to calculate theoretical anomalies and compare them with the observed data. Some of the data we obtained have been published and additional cases are now awaiting publication. In this paper, we will present a few specific cases where the geology is moderately well known and which we believe to be of considerable value as representing typical magnetic anomalies in the south magnetic hemisphere, where the inclination of the magnetic field is very low. Although the vertical intensity is negative in the Southern Hemisphere, we have adopted the convention of plotting increase in intensity (negative) as a positive anomaly; i.e., above the x axis. This convention facilitates comparison with anomalies in the north.

Jan 1, 1940

By John Freeman

THE tensile properties of steels at elevated temperatures have been studied by numerous investigators,1 primarily for the purpose of determining their suitability for structural uses. Tests with this objective have been confined largely to the temperature range of approximately 20° to 500° C., because of the rapidly decreasing tensile strength at the latter temperature. Tests have also been extended to higher temperatures for the purpose of determining the most suitable forging range. This temperature range is also of theoretical interest. The phenomenon of increased tensile strength and decreased ductility in the so-called "blue-heat" range, approximately 200° to 300° C., is well known. It was suggested to the Bureau early in 1926 that a study of the properties of rail steels in this temperature range might prove of interest in relation to the studies of transverse-fissure failures in rails. There were available from another investigation3 several new rails from several different heats made to approximately the same specification requirements, the complete manufacturing histories of which were known. It was decided to determine, at least in the preliminary series of tests, only the ultimate tensile strength, elongation and reduction of area, because of the difficulty, time and cost involved in determining the proportional limit and yield point at elevated temperatures.

Jan 1, 1930

By E. E. Donath

Application of the coal hydrogenation process for the production of chemicals is described. It has been estimated that a plant to produce 31,090 bbl per day of chemicals and fuels would cost $326,- 000,000. These products would consist of 6.1 pct by weight tar acids, 50.8 pct aroma tics, 16.4 pct LPG, and 26.7 pct gasoline. THE coal hydrogenation process is well known as a means for the production of liquid fuels from coal. In this paper the possibilities of the coal hydrogenation process as a source of chemical raw materials will be discussed. The recovery of chemicals from coal hydrogenation products necessitates some modifications and additions to the equipment used for the production of fuels. The conversion of coal into liquid fuels such as gasoline requires two steps: liquid phase and vapor phase hydrogenation. Intermediate oils obtained in the liquid phase contain oxygen and nitrogen compounds, especially aromatic compounds, since the coal itself is composed mainly of cyclic compounds. These oils are the raw material for the separation of high molecular weight aro-matics and of tar acids and tar bases. The relative amounts of heavy and middle oil—boiling above and below, e.g., 325°C—can be influenced by temperature, residence time, and catalyst of the liquid phase hydrogenation. In the vapor phase hydrogenation a solid bed catalyst is used to convert the intermediate oil from the liquid phase operation into hydrocarbons of the gasoline boiling range. Essentially pure hydrocarbons with a low content of sulphur, oxygen, nitrogen, and olefines are obtained. Depending mainly on the catalyst, the high ring compound content of the liquid phase oil can be preserved and gasoline rich in aromatics obtained. However, with other catalysts, these ring compounds can be split into gasoline with a high content of isoparaffins.&apos; Again, depending on the operating conditions, products of varying boiling range can be obtained. Selection of catalyst and operating conditions therefore makes possible the production of different grades of motor fuel and also variations in the relative amounts of benzene, toluene, and xylene when aromatic hydrocarbons are produced. The schematic flowsheet, Fig. 1, shows the main steps of the coal hydrogenation process, and the product streams used for the recovery of chemicals are indicated. In the liquid phase hydrogenation stage, coal is made into a paste with recycle heavy oil. The coal paste is mixed with hydrogen and preheated at a pressure of 300 to 700 atm in heat exchangers and preheaters. The coal paste and hydrogen enter high pressure converters where the liquefaction of coal, conversion of the high boiling liquid materials initially obtained, into intermediate oils is performed at a temperature around 470°C. The reaction products enter the hot catchpot in which lower boiling oil vapors are separated from the residue containing unreacted coal, ash, and heavy oil. This residue, usually called H.O.L.D. (heavy oil let down), is processed to separate solid and liquid material. By thermal treatment of the residue, e.g., a coking process, distillate oil is obtained, which can be recycled as part of the pasting oil. This stream is rich in polynuclear aromatics and can be, and has been, used for the recovery of such material. The oil vapors and hydrogen from the hot catchpot are cooled in heat exchangers and a cooler, and the condensed oil is separated from the recycle hy-

Jan 1, 1953