By D. F. Gibbons

THIS investigation was undertaken in order to gain further information on the mechanism of plastic deformation of iron at temperatures between room temperature and 77.2°K, and also to contribute to our understanding of the low temperature brittleness phenomenon that occurs in both the tensile and impact tests. It was decided to study as pure an iron as possible and to use the tensile test in order to simplify the problem as much as possible. Two series of iron were used throughout the investigation: iron A, obtained from the National Research Corp. and supplied as gas-free, high purity iron; and iron B, obtained from Fast' and produced by melting iron under purified hydrogen. Typical analyses of samples of both irons, after fabrication, are given in Table I. The main difference in composition of these irons is in their nickel and oxygen contents. Nickel has a very large solid solubility in iron. However, oxygen has an extremely small solid solubility. An attempt was made to reduce the oxygen content still further by remelting under purified hydrogen. This was successful in reducing the oxygen content to -0.0006 pct. However, no results on tests of this iron are included, since difficulty was encountered in fabricating the ingot. Wire specimens 1 mm in diameter were used for the investigation. The wires were produced from the ingots, as supplied, by cold rolling and swaging, with intermediate vacuum anneals at 700°C. Care was taken to reduce preferred orientation in the wires to a minimum by keeping the percentage of reduction in area between anneals of 30 to 40 pct. X-ray transmission photographs showed no indication of preferred orientation. The final grain size of iron A was 20 to 24 grains per linear mm and of iron B, 16 to 18 grains per linear mm. All specimens were tested in the decarburized and denitrided condition unless otherwise stated. The procedure was to pass hydrogen, saturated with water vapor at 26oC, over the specimens at 730°C for 2 hr. The specimens were quenched in iced water and then annealed in a vacuum of - 5x10-6 mm Hg for one day at 560°C to remove hydrogen. Higher temperatures were used for the vacuum anneal but this temperature was found to be quite satisfactory in removing hydrogen. The specimens were slow-cooled after the vacuum anneal. Where it is stated that the specimens were carburized, the specimens were given an identical decarburizing treatment and then carburized by passing hydrogen, saturated with pure n-heptane vapor at 0°C, over the specimens at 730°C. The specimens were then homogenized at 730°C for 2 hr in dry hydrogen. After the carburizing treatment the specimens were given the same vacuum anneal as for the decarburized specimens. The carbon content was determined from the maximum value of the internal friction carbon peak.2 Apparatus Fig. 1 shows a diagram of the tensile apparatus, with half the cooling coil removed. The cooling coil enabled temperatures from 200" to 77.2oK to be obtained. The apparatus was designed to fit a standard Tinius Olsen Universal tensile machine. The apparatus consisted of the rigid plate A which carried two carefully machined hooks H. These hooks attached the plate firmly to the moving crosshead of the tensile machine. The lower grip B was rigidly suspended from the plate A by three stainless steel rods. The upper grip C was joined to the upper grip of the tensile machine by the stainless steel rod E. The lower part of the apparatus was surrounded by a Dewar vessel, which was made a sliding fit inside the brass collar D. The specimen was held in a clamp which fitted into the grip, forming a ball and socket joint (see inset a). This was to attain as nearly pure

Jan 1, 1954

By LEE H. CORNELL

Drilling activity in Kansas during 1945 continued at an accelerated pace to meet the demands of war; 1810 tests were drilled as compared with 1856 tests the previous year, 1771 tests in 1943, and 1516 tests in 1942. During the year 31 new oil pools and 10 new gas pools were discovered. Of a total of 364 wildcats drilled, 323 were dry; and of 1446 tests drilled in pools, 825 were oil wells, 197 gas wells, and 425 dry holes.

Jan 1, 1946

By P. Payson

INTERGRANULAR corrosion in corrosion-resistant chromium-nickel steels has been widely discussed in the last few years. So far as the author knows, nothing has been published which definitely shows that this tendency can be eliminated, although suggestions have been made that a remedy is possible if certain specifications are satisfied. Strauss, Schottky and Hinueber1 suggested an increase in chromium content to an extent that would prevent the impoverishment of chromium on carbide precipitation sufficient to cause impaired corrosion resistance in the matrix. Pilling2 suggested an increase in nickel, so that the stability of the austenite matrix would be increased. Aborn and Bain,3 say that "intergranular attack-may be eliminated by preventing carbide precipitation (e. g., by lowering the carbon content or somehow raising its solubility) or by precipitating it permanently under conditions which will not remove chromium from solid solution so drastically at any points." In a later paper Aborn and Bain4 state that many different metallic elements, tungsten, vanadium, copper, aluminum, molybdenum, titanium and zirconium, have been added in small per-centages to increase the stability of these alloys, but that it has been reported that according to the copper sulfate test these added elements act only to retard the intergranular corrosion, and that increased nickel and chromium contents have similar effects. Newell5 showed that the lower the quenching temperature before reheating, the less severe was the intergranular attack.

Jan 1, 1932

By Gordon E. Agar, David M. Hopstock

This paper describes the procedures and results of a series of experiments conducted to determine the depressing effect of sodium, calcium and magnesium ions on the amine flotation of quartz. It also presents an analysis of the experimental results by the electrical double layer theory. The flotation of quartz with primary amines has been practiced on a large scale in the phosphate industry for many years. Some glass sand —and recently iron ore — has also been treated by this flotation technique. These applications have been highly successful and demonstrate that a complete mastery of all the details of an operation is not needed to achieve an economic success. There are times, though, when it becomes important to recognize, both qualitatively and quantitatively, the effects of some previously ignored variables. The effects of cations on the amine flotation process, particularly those ions that contribute to water hardness and abound in sea water, are a case in point. In conjunction with the development of a cationic flotation reagent for separating quartz from apatite, it became necessary to quantify the influence of calcium and magnesium on the separation. In order to strengthen and broaden current understanding of the flotation process, the results were interpreted by means of the electrical double layer theory. THEORETICAL BACKGROUND Assume that, given the same equipment, procedure, and time, the recovery of quartz by amine flotation is a function of only the adsorption density of aminium ions in the Stern layer, i.e., that for any given adsorption density there exists only one recovery percentage. By the Stern-Grahame treatment of the electrical double layer,'-' for any ionic species in a solution in equilibrium with quartz,

Jan 1, 1969

By C. S. Matthews, J. L. Mahaffey, W. M. Rutherford

This paper gives results of an experimental study of the sweep efficiency of a miscible displacement in a five-spot. The study was carried out in a parallel-plate glass model in which effects of diffusion were scaled at or near the molecular diffusion level. The experiments show that very early breakthrough (25 to 35 per cent of pore volume (PV) injected) may be expected in miscible floods because of the unfavorable viscosity ratio. However after 1 PV of displacing fluid is injected, the sweep rises to a reasonable value (50 to 60 per cent). Photographs show that small slugs of less than 10 per cent of PV tend to dissipate before breakthrough. A minimum slug size of 15 per cent of PV would appear to be necessary even in a relatively homogeneous formation. Presence of a slug whose viscosity is inter-mediate between that of oil and gas increases the sweep efficiency of the oil-gas system. In a typical system the sweep at breakthrough rose from 26 to 37 per cent of PV for a 25 per cent slug. The increase in sweep brought about by use of a large slug could well pay for the extra deferment cost of the additional slug material. INTRODUCTION Most miscible displacement processes involve the displacement of oil with fluids of much lower viscosity and density. The displacement process at these adverse viscosity and density ratios is dominated by instability phenomena, i.e., viscous fingers and gravity tongues. These phenomena have highly adverse effects on oil recovery. Although a number of laboratory studies have been made to determine the effect of adverse viscosity ratios on five-spot sweep patterns,l,2 the scaling of diffusion effects is uncertain. In the series of scaled model studies reported herein, an attempt was made to scale diffusion. Model studies of miscible displacements in which molecular diffusion predominates are per-mitted by controlling the parallel plate spacing which reduces convective mixing to arbitrarily small levels. To decide how this scaling relates to any particular Geld displacement necessitates an estimation of diffusion effects for the natural rock being considered and conditions under which displacement will be conducted. The approach normally taken is to extrapolate data obtained from stable miscible displacements performed in the laboratory, such as those presented by Brigham et al.3 The validity with which such an extrapolation can be applied to an unstable flow system has yet to be established. If this approach is accepted, a family of oil recovery curves can be generated for a single viscosity ratio based on Brigham's observation that the magnitude of the dispersion coefficient is dependent, among other things, upon specific rock properties. Objective of our test was to define the lower limit of this range by presenting the case where dispersion effects were reduced to the molecular diffusion level in both the transverse and longitudinal directions.

Jan 1, 1967

[ ]

Jan 1, 1938

By R. Ehrlich, F. E. Crane

A consolidated porous medium is mathematically modeled by networks of irregularly shaped, interconnected pore channels. Mechanisms are described that form residual saturations during immiscible displacement both by entire pore channels being bypassed and by fluids being isolated by the movement of an interface within individual pore channels. This latter mechanism is shown to depend strongly on pore channel irregularity. Together, these mechanisms provide an explanation for the drainage-imbibition-hysteresis effect. The calculation of steady-state relative permeabilities, based on a pore-size distribution obtained from a Berea sandstone, is described. These relative permeability curves agree qualitatively with curves that are generally accepted to be typical for highly consolidated materials. In situations where interfacial effects predominate over viscous and gravitational effects, the following conclusions are reached. 1. Relative permeability at a given saturation is everywhere independent of flow rate. 2. Relative permeability is independent of viscosity ratio everywhere except at very low values of wetting-phase relative permeability. 3. Irreducible wetting-phase saturation following steady-state drainage decreases with increasing ratio of nonwetting- to wetting-phase viscosity. 4. lrreducible wetting-phase saturation following unsteady-state drainage is lower than fir steady-state drainage. 5. Irreducible nonwetting-phase saturation 101lowing imbibition is independent of viscosity ratio, whether or not the imbibition is carried out under steady- or unsteady-state conditions. Experiments qualithtiveIy verify the conclusions regarding unsteady-state residual wetting-phase saturation. Implications of these conclusions are discussed. INTRODUCTION Natural and artificial porous materials are generally composed of matrix substance brought together in a more or less random manner. This leads to the creation of a network of interconnected pore spaces of highly irregular shape. Since the geometry of such a network is impossible to describe, we can never obtain a complete description of its flow behavior. We can, however, abstract those properties of the porous medium pertinent to the type of flow under consideration, and thus obtain an adequate description of that flow. Thus, the Kozeny-Carmen equation, by considering a porous medium as a bundle of noninterconnecting capillary tubes, provides an adequate description of single-phase flow. With the addition of a saturation-dependent tortuosity parameter in two-phase flow to account for flow path elongation, the Kozeny-Carmen equation has been used to predict relative permeabilities for the displacement of a wetting liquid by a gas. 1-5 It has long been recognized that relative permeability depends not only on saturation but also on saturation history as we11.6,7 Naar and Henderson8 described a mathematical model in which differences between drainage and imbibition behavior are explained in terms of a bypassing mechanism by which oil is trapped during imbibition. Fatt9 proposed a model for a porous medium that consisted of regular networks of cylindrical tubes of randomly distributed radii. From this he calculated the drainage relative permeability curves. Moore and slobod,10 Rose and Witherspoon,11 and Rose and Cleary12 each considered flow in a pore doublet (a parallel arrangement of a small and large diameter cylindrical capillary tube). They concluded that, because of the different rates of flow in each tube, trapping would occur in one of the tubes; the extent of which would depend upon viscosity ratio and capillary pressure. They limited

Jan 1, 1970

By David Sinclair

THE dimensions and shapes of mine structures may at present be determined by (1) field experience, (2) structural calculations, and (3) barodynamic tests.§ None of these, however, provide information as to the stresses, their direction and distribution in a mine structure. For the design of pillars, the placing of openings relative to working places such as gangways, haulage levels, etc., this information is desirable. Photoelastic methods provide this and, while relatively new, their appli-cation in all engineering fields is assuming increasing importance. This paper, therefore, will present the method with a few applications to mining, and with sufficient reference for further study by the reader. PART I THE PHOTOELASTIC METHOD The photoelastic method of stress measurement determines the stress distribution in a two-dimensional model by optical means. It makes use of the fact that when a piece of isotropic transparent material, such as glass, celluloid, or Bakelite, is stressed and viewed in polarized** light a picture is seen which indicates by its color bands of light, or fringes, the magnitude of the stresses, their direction and their distribution.

Jan 1, 1940

By Frederick Laist

I. INTRODUCTION The new slime-concentrating plant at the Washoe Reduction Works, Anaconda, was put into operation during March, 1914. This plant, which has a capacity of 26,000,000 gal. of slime pulp carrying 2,500 tons. of solid matter per day, consists of Dorr thickeners and Anaconda multiple-deck slime concentrators.' This plant is the culmination of a great deal of experimental work extending over a considerable period of time, which work will be described briefly in the following pages.

Jan 8, 1914

By C. H. Samans, G. F. Tisinai, J. K. Stanley

The addition of nitrogen (0.10 to 0.20 pct) to Fe-Cr-Ni alloys of simulated commercial purity results in a real displacement of the u phase boundaries to higher chromium contents. The effect is small for the (Y + s)? boundary, but is pronounced for the (y + a +s)/(y + a) boundary. Although there is an indication of an exceptionally large shift of the n boundaries to higher chromium contents, especially in steels with nitrogen over 0.2 pct, the major portion of this apparent shift results from the fact that carbide and nitride precipitation cause "chromium impoverishment" of the matrices. The effect of combined additions of nitrogen and silicon to the Fe-Cr-Ni phase diagram is demonstrated also. Nitrogen can nullify the effect of about 1 pct Si in shifting the (y + o)/? phase boundary to lower values of chromium at all nickel levels from 8 to 20 pct. NItrogen can nullify this U-forming effect of about 2 pct Si at the 8 pct Ni level, but not at the 20 pct Ni level. The alloys studied were in both the cast and the wrought conditions. There are indications that the u phase forms more slowly in the cast alloys than in the wrought alloys if both are in the completely austenitic state. The presence of 6 ferrite in the cast alloys accelerates the formation of U. Cold working increases the rate of o formation in both cast and wrought alloys. THE major improvement in Fe-Cr-Ni austenitic alloys in recent years has been in the addition or removal of minor alloying elements to facilitate better control of corrosion resistance, sensitization, and heat resistance. One shortcoming of the austenitic Fe-Cr-Ni alloys, which never has been completely circumvented, is their propensity toward u formation. In the AISI-type 310 (25 pct Cr-20 pct Ni) and type 309 (25 pct Cr-12 pct Ni) steels, sufficient amounts of u phase can form, if service or treatment is in a suitable temperature range, to cause severe embrittlement. Also, there is a growing conviction that this phase may be contributory to some unexpected decreases in the corrosion resistance of certain of the 18 pct Cr-8 pct Ni-type steels. The present paper discusses the effect of nitrogen additions on the location of the (r+u)/d and the (y+a+u)/(y+a) phase boundaries in the ternary Fe-Cr-Ni system, for cast and wrought alloys of simulated commercial purity, and in similar alloys containing up to about 2.5 pct Si. The objective is to define compositional limits for alloys which will not be susceptible to u formation when used near 1200°F (650°C). An excellent review of the early studies of the u phase in the Fe-Cr-Ni system has been compiled by Foley.1 Rees, Burns, and Cook2 have determined a high purity phase diagram for the ternary system, whereas Nicholson, Samans, and Shortsleeve3 are- stricted themselves to a portion of the simulated commercial-purity phase diagram. Both groups of investigators show almost an identical position for the commercially significant (y+u)/y phase boundary. Further comparison of the work of the two groups indicates that, below the 8 pct Ni level, the commercial alloys have a decidedly greater propensity toward u formation than the high purity alloys. The two groups of workers agreed that both the AISI-type 310 (25 pct Cr-20 pct Ni) and the type 309 (25 pct Cr-12 pct Ni) steels are well within the (y+~) region and that the 18 pct Cr-8 pct Ni-type alloys straddle the U-forming phase boundaries. Nicholson et al.3 showed, in addition, that these boundaries shift toward lower chromium contents if greater than nominal amounts of silicon or molybdenum are added. The effect of nitrogen on the location of the s phase boundaries in the Fe-Cr-Ni system has not been known with any certainty. In 1942, an approach to this problem was made by Krainer and Leoville-Nowak,' but at that time they apparently were unaware of the slow rate of s formation in strain-free samples and aged their samples for insufficient times, e.g., 100 hr at 650°C (1200°F) and 800°C (1470°F). For this reason, it would be expected that their (y+ u) /y boundary would be shifted toward lower chromium contents (restricted ?-field) when equilibrium conditions were approximated more closely. Procedure for Studying the Alloys The alloys used were prepared in the following way: Heats of 200 lb each were melted in an induction furnace. A 5 lb portion of each heat was poured into a ladle containing an aluminum slug for de-

Jan 1, 1955

By D. J. McAdam

As shown in three recent papers by the author, in two papers by McAdam and Mebs, and in a paper by McAdam, Mebs, and Geil," the technical cohesive strength of a metal, in any particular state as regards mechanical treatment and heat-treatment, cannot be represented by a single stress value, but must be represented by a diagram with the principal stressest as coordinates. Each point on the boundary of such a diagram represents a technical cohesion limit. The technical cohesive strength thus comprises an infinite number of technical cohesion limits, each representing fracture under a specific stress combination. Moreover, neither the yield strength1 nor the ultimate strength can be represented completely by a single stress value, but must be represented by a diagram with the principal stresses as coordinates. All combinations of the principal stresses may be classified in three groups as illustrated by Fig. I. Fig. Ia shows three typical stress combinations with no two principal stresses equal. The magnitude of each principal stress is indicated qualitatively by the length of the arrow. Arrows pointing away from the cube indicate tensile stresses; arrows pointing toward the cube indicate compressive stresses. Typical stress combinations with two principal stresses equal are illustrated in Figs. rb and Ic. Such stress combinations would be produced by subjecting a cylinder to combinations of uniform axial and radial stresses. The uniform radial stress may be resolved into two equal principal stresses. with the mutually perpendicular directions rotatable around the axis of the cylinder. Fig. ib shows stress combinations with Sz equal to The greatest principal stress is in the axial direction, and the stress combination tends to cause either absolute or relative increase in length.* Fig. u shows stress combinations with S2 equal to St. The greatest principal stress is in the radial direction, and the combination tends to cause either absolute or relative decrease in length. The complete representation of either technical cohesive strength, yield strength, or ultimate strength generally requires a three-dimensional diagram. When two of the principal stresses are kept equal, however, the strength of a metal may be represented by a two-dimensional diagram with the coordinates representing the axial and radial stresses.6-II In this paper, attention will be confined almost entirely to stress combinations with two of the prin-

Jan 1, 1945

Jan 1, 1913

By R. D. Pehlke, J. V. Gluck, R. L. Louvet

A study has been made of the effect of small additions of bismuth on the activity of zinc in dilute solution in molten tin. Free-energy interactions have previously been determined between zinc and various third elements where the solvents were molten bismuth or molten lead.'-4 In both of these solvents, the activity of zinc exhibits a strong positive deviation from ideal behavior (at 550°C y° for zinc in lead is 11.4 and for zinc in bismuth is 3.0). The present work, using tin as the solvent, is an extension to a case where the positive deviation is considerably diminished (y°Zn at 550°C is 1.63). Several previous investigators have studied the Zn-Sn binary system; however, little data is available in the range below 0.1 mole fraction zinc.5= Previous high-temperature galvanic cell studies in the Sn-Zn-Bi ternary system included the determination by Gluck and Pehlke of interactions in the bismuth-rich corner1 and separate investigations of the central region by Oleari and Fioriani6 and by Ptak and Moser.7 Yokokowa et al.8 conducted Knudsen effusion studies in the central region; however, their experiments at 625°K were conducted somewhat below the present experimental temperature range. Their results indicated an increase in zinc activity with the addition of bismuth. The present series of experiments was conducted in galvanic cells represented as follows: Zn Zn++ in LiCI-KC1 eutectic Zn + Bi in Sn (pure reference (fused salt electrolyte) (molten alloy) standard) The experimental apparatus. a multi-electrode system employing alumina crucibles and contained in a Vycor tube under a helium atmosphere, has been described previously, as have been the experimental procedures, precautions, and the methods of data reduction.1-4,- The experimental measurements were made over the range from 450° to 650°C. Between thirty and forty measurements were made in each run. The linearity of the electromotive force vs temperature relations was verified by linear regression techniques. The correlation coefficients exceeded 0.99. The experimental results summarized in Table I include the interpolated electromotive force at 550°C and the temperature dependence of electromotive force. Only results from stable and consistent cells containing more than 0.025 mole fraction zinc are reported. Attempts to run cells at 0.01 or 0.02 mole fraction zinc were not satisfactory. This is attributed to the closeness of the free energies of formation of the chlorides of tin and zinc. Calculations employing Wagner and Werner's criteria for displacement reactions10 indicated that reduction of the zinc content to 0.01 mole fraction places the cell near the borderline concentration for a 1 pct error in measured potential. The compositions shown in Table I are the actual weighed-in amounts. Previous experience has indicated that compositional changes during the running of a stable cell are negligible.' Over the range of compositions studied for the binary alloys, the activity coefficient of zinc was essentially constant indicating that Henry's law is followed to 0.05 mole fraction zinc. The temperature, OK, de-

Jan 1, 1969

By W. H. Bassett, C. H. Davis

ALTHOUGH brasses and bronzes have been made for ages, a systematic study of their physical properties has been carried out only during the years of the present century. Among these properties may be included those which are to be detected by means of microscopic examination; in other. words by the science of metallography. The earlier workers in this field, both in this country and abroad, gave their attention to steel. When the senior author explored the situation in 1902, there was little encouragement to be found in undertaking the study of the non-ferrous alloys. A start was made, and the metallography of the brasses and bronzes, as well as of the copper-nickel-zinc alloys developed materially under his direction. Annealing experiments were begun in 1902, and in the succeeding years the effect of temperature, and the influence of previous working, on the grain size of brass were studied. The conclusions so well known and widely published today were largely reached during those earlier years. . In 1905 the first complete annealing series were made. By this it is meant that brass and copper sheet, 5 B & S Nos. hard, was machined into tensile test specimens, then annealed under accurate control for 30 min. at temperatures up to the melting point of the material. Various determinations were made, including tensile strength and elongation in 2 in. There rapidly followed similar series on all of the copper-zinc alloys from 100 to 60 per cent. copper, on the bronzes, cupronickels, and on copper-zinc-nickel alloys. At this point there was published by Grard, in October, 1909,1 the very comprehensive and complete work on the tensile properties of cartridge brass, 90-10 copper-zinc, and electrolytic copper. The excellent photomicrographs in that paper illustrated the changes in structure produced by cold rolling as well as by annealing at different temperatures, but where Grard's work was confined to copper and to two alloys, the investigations in this laboratory have been over the entire fields of the commercial copper-zinc alloys, copper-tin alloys, representative copper-nickel and copper-nickel-zinc alloys as well as aluminum bronzes and others of a more special nature.

Jan 1, 1928

By H. N. Eavenson

In a discussion in the Transactions of the Institute (vol. Xl, page 835 et seq.) the writer gave some data about the explosions of gas and dust in the coal mines of the United States, Canada, and Mexico…

Jan 1, 1915

By R. J. Wasilewski

The resistivity of single crystal and of polycrystalline metal has been determined between 77° and 1500°K. At comparable purity, the resistivity of the poly crystalline metal differs from that calculated from the axial resistivity values. The observed anisotropy is briefly discussed. A zone refined titanium rod was obtained from F. J. Darnell.1 The hardness of this material varied between 52 and 64 Bhn, indicative of its high purity. Single-crystal specimens were cut out from a few large grains, elongated predominantly along <1120>. Resistance measurements were taken with specimens immersed in liquid nitrogen, solid CO,, and acetone, and at ice point, and then recorded continuously between room temperature and 1200" to 1250°C, throughout at least one full heating and cooling cycle at a rate of l° to 3°C per min. Four probe measurements were taken using spot-welded Pt wire 0.003 in. in diam as potential terminals, and the electromotive force drop was determined poten-tiometrically. A standard resistance, in series with the specimen, served to determine the dc current (generally about 80 ma) in the circuit. In order to eliminate spurious thermal electromotive forces, the circuit polarity was automatically reversed at 5-min intervals, and the mean of the two adjacent readings taken as the true electromotive force value. The discrepancy between the readings at reversed polarities was generally of the order of a few µ v, as all the spot-welded joints were contained within a volume of some 5 mm cube. The relative resistance (R T/R 273o) variation with temperature is tabulated below, and shown in Fig. 1, as measured during the first heating run. The discontinuous drop in resistance, corresponding to the a — ß transformation, started for both initial orientations at 1170°K; i.e., some 15°K above the accepted value of 882°C (1155°K). Judging by the temperature ranse of transformation—some 30°K for the single crystal and 20°K for the polycrystal-line specimen—this difference is believed caused by the solution of the oxygen present initially on the surface of the specimens. The general trend of the resistance vs temperature shown in Fi,;. 1 is in qualitative agreement with that previously reported for polycrystalline titanium metal. 2,3 Significant anisotropy is, however, indicated by the crossing over of the curves for <1120> and <0001> orientations at 273°, 650°, and 1000°K. This difference is most startlingly shown in Fig. 2, where instantaneous temperature coefficients (l/R273 x dR /dT) are plotted for both the first heat-

Jan 1, 1962

By B. J. Nelson, F. N. Rhinos

Studies upon the rates of oxidation of copper alloys containing small quantities of the alloying elementsl,2 have shown that steady growth of the scales at predictable rates is limited to a small concentration range and to oxidation at temperatures above 600°C., whereas unpredictable and erratic oxidation behavior is found with alloys containing larger additions and at low temperatures. The latter effect appears to be associated with modifications in the geometric disposition of the oxides. At low concentrations of the baser elements in copper, simple oxidation behavior is typified by the formation of two distinguishable zones of oxidation: (I) a subscale composed of discrete particles of the oxide of the alloying element embedded in substantially pure copper and (2) an external scale composed of cuprous oxide (with a very thin layer of cupric oxide on the outside) containing particles of the alloying element distributed throughout, but most profusely near the metal surface (see Fig. 2, top). Where this type of structure obtains, the process of oxidation is believed to be implemented, and its rate controlled, by the diffusion of the reacting elements through a&apos; continuous matrix phase; i.e., through the alpha (metallic) phase of the subscale and alloy and through the cuprous oxide of the external scale. Copper is presumed to diffuse outward through the cuprous oxide layer to the external surface, where it reacts to form more cuprous oxide.3 Oxygen is delivered at the oxide-metal interface in the form of cuprous oxide, which may either react with the alloying element to deposit its oxide at the inner limit of the external scale or dissolve in the pure copper that remains at the surface of the metal after it has become depleted in its oxidiza-ble alloying elements. Both oxygen and the alloying element are pictured as diffusing through the metal, the oxygen inward and the alloying element outward. Where the two diffusion streams meet in sufficient concentration the oxide of the subscale is precipitated. If the oxygen pressure in the surrounding atmosphere is just below the pressure necessary to maintain cuprous oxide undecomposed, no cuprous oxide can be formed; some of the oxide of the alloying element may form upon the external surface, if its decomposition pressure is below that of cuprous oxide, and a normal sub-scale appears. This condition is achieved experimentally by enclosing the alloy with cuprous oxide together with an excess of copper. At temperatures from 600°C. downward, the precipitated oxides tend to accumulate at the grain boundaries of the alpha phase where a relatively small volume establishes a partial barrier to the diffusion of the reactants- Similarly, large volumes of Precipitated oxides tend to deposit in various patterns that may be expected to

Jan 1, 1944

By F. N. Rhinos, B. J. Nelson

Studies upon the rates of oxidation of copper alloys containing small quantities of the alloying elementsl,2 have shown that steady growth of the scales at predictable rates is limited to a small concentration range and to oxidation at temperatures above 600°C., whereas unpredictable and erratic oxidation behavior is found with alloys containing larger additions and at low temperatures. The latter effect appears to be associated with modifications in the geometric disposition of the oxides. At low concentrations of the baser elements in copper, simple oxidation behavior is typified by the formation of two distinguishable zones of oxidation: (I) a subscale composed of discrete particles of the oxide of the alloying element embedded in substantially pure copper and (2) an external scale composed of cuprous oxide (with a very thin layer of cupric oxide on the outside) containing particles of the alloying element distributed throughout, but most profusely near the metal surface (see Fig. 2, top). Where this type of structure obtains, the process of oxidation is believed to be implemented, and its rate controlled, by the diffusion of the reacting elements through a&apos; continuous matrix phase; i.e., through the alpha (metallic) phase of the subscale and alloy and through the cuprous oxide of the external scale. Copper is presumed to diffuse outward through the cuprous oxide layer to the external surface, where it reacts to form more cuprous oxide.3 Oxygen is delivered at the oxide-metal interface in the form of cuprous oxide, which may either react with the alloying element to deposit its oxide at the inner limit of the external scale or dissolve in the pure copper that remains at the surface of the metal after it has become depleted in its oxidiza-ble alloying elements. Both oxygen and the alloying element are pictured as diffusing through the metal, the oxygen inward and the alloying element outward. Where the two diffusion streams meet in sufficient concentration the oxide of the subscale is precipitated. If the oxygen pressure in the surrounding atmosphere is just below the pressure necessary to maintain cuprous oxide undecomposed, no cuprous oxide can be formed; some of the oxide of the alloying element may form upon the external surface, if its decomposition pressure is below that of cuprous oxide, and a normal sub-scale appears. This condition is achieved experimentally by enclosing the alloy with cuprous oxide together with an excess of copper. At temperatures from 600°C. downward, the precipitated oxides tend to accumulate at the grain boundaries of the alpha phase where a relatively small volume establishes a partial barrier to the diffusion of the reactants- Similarly, large volumes of Precipitated oxides tend to deposit in various patterns that may be expected to

Jan 1, 1944

By C. A. Stickels

In a recent paper, Held1 showed that rolling conditions can have a marked effect on the volume fraction of surface texture produced in low-carbon steel. This variation in rolling texture is reflected in the recrys-tallization texture and affects the plastic properties of the annealed sheet. The fact that roll friction can influence the surface deformation texture in iron and steel has been known for some time;&apos;= but the magnitude of the effect has never been shown quite so clearly before. The analogous effect during wire drawing has been recognized for many year.4 Dillamore and Roberts5 examined surface textures in warm- and cold-rolled aluminum and copper. They found that when a surface texture was present it could be described as the interior texture rotated about the transverse sheet direction. The angle of rotation was a function of the type of lubrication, the amount of reduction per pass, and the temperature of rolling. The purpose of the present note is to show that surface textures in cold-rolled iron can also be described as interior textures rotated about the transverse sheet direction. Vacuum-melted electrolytic iron* was straight- rolled 90 pct at room temperature in a two-high rolling mill with 5-in.-diam rolls. Two rolling procedures were used: a) no lubrication with reductions of about 0.035 in. per pass, and b) heavy lubrication with lano-line and reductions of about 0.002 in. per pass. The final sheet thickness was 0.030 in. (110) pole figures were determined by transmission through specimens taken from the sheet surface and sheet midplane. The surface texture of the sheet cold-rolled according to procedure a is shown in Fig. l.* The shapes of the low-intensity contour lines indicate that the texture can be described as a partial fiber texture with a (110) fiber axis normal to the sheet. The approximate range of orientstions present is (011)[211] — (0ll)[100] — (011)[211]. This range of orientations is what one would obtain by rotating the interior texture 90 deg about the transverse sheet direction. The intensity of (110) and (222) reflections from planes parallel to the surface was measured after removing metal from the surface by chemical polishing. The surface texture here was confined to the outer

Jan 1, 1968

Jan 1, 1882