By Shengqin Zhang, Yousef Mohassab, Feng Chen, Hong Yong Sohn, Mohamed Elzohiery, Amr Abdelghany

The kinetics of hematite concentrate reduction by mixtures of hydrogen and CO of various compositions has been investigated as part of the development of a flash ironmaking process at the University of Utah. This process produces iron directly from iron oxides concentrates by the gas-solid flash reaction based on the partial oxidation of natural gas, resulting in a significant reduction in energy consumption and greenhouse gas emission. The reduction kinetics of hematite concentrate of an average particle size 21.3 μm by the above mentioned gases in the temperature range 1423 to 1623 K (1150 to 1350 ºC) was investigated. Hematite concentrate particles can be reduced to > 90% by any of these reductants in several seconds of residence time typically available in a flash reactor. The activation energy ranged from 214 kJ/mol for hydrogen to 231 kJ/mol for CO.

Jan 1, 2016

By Michael J. Nicol

This paper summarizes some of the results of a study of the reactions involved in the Caron leaching process and identifies the roles of the major dissolved species in the kinetics of dissolution of iron alloy particles formed during reductive roasting. Using rotating disk electrodes and synthetic leach solutions, the reduction of water with the evolution of hydrogen was found not to occur on a dissolving iron surface under typical leach conditions. It has been established that the oxidative dissolution is governed primarily by a reaction involving reduction of Co(III) to Co(II) ions. The reduction of oxygen was also found to make a significant but largely indirect contribution to the kinetics of the dissolution process. The dissolution rates of various iron-nickel-cobalt-copper alloys which simulate the dissolving alloy particles in a Caron plant were measured in synthetic leach solutions under aerobic and anaerobic conditions. The initial dissolution rates of iron, nickel and the iron alloys were found to increase in the presence of thiosulphate, whereas the thiosulphate had a negative effect on the dissolution rates of cobalt and copper. It is shown that the eventual passivation of the iron occurs sooner in solutions rich in Co(II) ions. Whilst these conditions are present in the quench slurry, on-site measurements have shown that due to the very high concentration of reduced dissolved species, passivation does not occur until the slurry is strongly aerated. In the light of these fundamental findings, options for optimizing the rate of dissolution and minimizing the extent of passivation of the iron and iron alloys are discussed. Keywords: Ammonia, leaching, alloy, kinetics, passivation.

Jan 1, 2004

By Ruirui Wei, Yanhui Liu, Fangqing Yin, Meilong Hu

In China, Basic Oxygen Furnace (BOF) slag is traditionally used as an aggregate for civil engineering, for road engineering and fertilizer. In order to make full use of BOF slag, the experiments of BOF slag with high temperature roasting has been carried out and the phase transformation is studied. The BOF slag from Chongqing Iron & Steel is roasted in the electric muffle furnace at three different temperature. The influences of the high temperature roasting on change the phase composition of BOF slag was characterized by XRD. The results revealed that SFCA was produced at the high temperature in air atmosphere and melting temperature of slag was lowered. Therefore, if the BOF slag which treated by roasting was utilized in the sintering process, it is advantageous to improve the sintering strength and the formation of the liquid phase and reduce fuel consumption in the sintering production process.

Jan 1, 2015

By M. C. Ruiz

The conventional pyrometallurgical methods to treat copper sulfide concentrates include generally, one or more oxidizing steps where the formation of SO2 gas can not be prevented. From the economical point of view and the nature of some of the processes in which SO2 is produced, its complete capture is not feasible; therefore an important fraction is released to the atmosphere as fugitive emissions. In this research, the reduction of chalcocite was studied in the presence of lime as an alternative method, which overcomes the pollution problems related to SO2 emissions. The effect of temperature, time, concentration of carbon and CaO on the reduction rate were studied. Among these variables, temperature affects most the reduction rate. Conversions over 95 % can be obtained in less that 20 minutes at temperatures over 1000 ° C. The measured partial pressures of the gaseous components indicated that the chalcocite reduction proceeded through the gaseous intermediate species CO, C02, and the overall kinetics was controlled by the Boudouard reaction. The kinetic model In(1-X)= kt fits well the experimental data. Apparent activation energy of 3 14 kJ/mol was calculated for the temperature range of 900 0C-1050 °C.

Jan 1, 1999

By D. K. Panda

The behavior of single drops with gas evolution at the interface is of interest because this is one of the important reactions that occur in oxygen steelmaking vessels, where a large amount of iron-carbon drops are dispersed in an oxidizing slag. The carbon dissolved in these drops, reacts with the slag to form CO, which is evolved as a gaseous phase. A room- temperature model was used to study the nature of this type of reaction including the effect of various factors such as viscosity and the presence of surface active impurities. Experiments were done for reacting drops over a wide size range to observe various regimes of behavior. Large single drops were levitated in a counter current flow to produce a sufficiently long residence time to allow the study of the various stages in the reaction. The emphasis of this work was to obtain photographic evidence of a high quality to describe all possible modes of behavior, and so a lot of effort was given to developing and perfecting experimental techniques.

Jan 1, 1994

By Norihiko Fukatsu

In order to use effectively the previously reported new sensing system for hydrogen and oxygen potentials in molten copper, the criteria of the potentials for getting sound castings have been determined in the laboratory experiment. The copper melt equilibrated with a given hydrogen and an oxygen potential was rapidly quenched in the crucible. The relations between the holding potentials and the gas porosity in the solidified sample were investigated by measuring the density of the sample and microscopic observations. It was found that the defects of the gas porosity became the maximum at the potentials where the dissolved amount of hydrogen and oxygen was in the mole ratio 2: I. The samples having the density more than 99% of the theoretical value were obtained in the higher oxygen and lower hydrogen potential region or in the lower oxygen and higher hydrogen potential region. The criteria thus determined were examined by comparing with the measured potentials in the practical easting machine. In tough-pitch copper casting, the problem due to gas porosity was found to be serious when the hydrogen potential increased. In the oxygen-free copper casting, the evolution of hydrogen was found not avoided. The gas porosity in the casting, however, was found eliminated when the oxygen potential was kept at a low value.

Jan 1, 2003

By Eoghan T. M Doyle

Oxide mixtures of nickel (NiO), cobalt (COO) and chromium (Cr203) were prepared with graphite in stoichiometric amounts and the powder mixtures were compacted to produce cylindrical pellets. The composition of chromium oxide in these mixtures were varied. Pressed pellets were reduced in a flowing stream of argon-4% hydrogen gas (500 ml/min). Both slow and rapid heating methods were adopted to raise the temperature of a pellet during reduction of oxides to form superalloy powder. The reduction temperature was varied between. 1523 and 1623K. The effect of heating rate and niobium oxide addition on the microstructure of the superalloy produced was studied by using ordinary light and scanning electron microscopes. New phases formed as a result of reduction were identified by X-ray powder diffraction technique. The mechanism of reduction of oxides together with the microstructure of NiCrCo alloy are discussed. The thermodynamics of formation of ternary alloy phase is elucidated on the basis of binary phase equilibria and Gibbs free energy of mixing data for the constituent alloy compositions.

Jan 1, 1992

By P. C. A. Maia, J Alexandre, F. A. J. Saboya, A. R. G. Azevedo, G. C. Xavier

"This work shows the characterization of clay and the granite waste by-product from the sawing process of the granitic blocks, used as raw material for brick ceramic. Besides, shows the degradation of the ceramic material obtained with different by-product contents in the waste after lab test degradation, is investigated. The clay is obtained from mine use areas of ceramic industry in Campos-RI and the waste is originating from of the area of Cachoeiro-ES, an important center of decorative stone in Brazil. The mixes were made by the addition of 0% up to 10% of the waste in the raw material. After drying and firing up to 900°C, obtained prismatic pieces were considered intact. Physico-mechanical properties were obtained from wet and drying tests in laboratory considering 50 and 150 cycles. The results showed that the use of powder byproduct has a considerably influence on the weathering and strength of the material.IntroductionThe ornamental rocks and coating defines the most promising areas of business in the mineral sector [l]. In this context, the Espirito Santo appears as the main Brazilian state in production and export of ornamental rocks, representing 47% of national production [2] which in tum is one of the economic sectors most representative of this State, due of its transport logistics and port vocation that facilitates the export of such products.It is estimated that the state of Espirito Santo there are approximately 1,200 companies dedicated to the activities of ornamental rock by providing 20,000 direct jobs [ 1]. These mobilize support activities, such as companies that provide machinery, equipment and supplies for industries, including service providers for maintenance.However, the production of rocks produces about 15,000 tons of granite waste/month [3] only in the municipality of Cachoeiro ltapemirim-ES. This is justified by the presence of more than 500 extraction industries, cutting and processing of stone, with about 900 looms, waste generators.According to [4], there is great potential for the use of granite waste in red ceramics introduced for the manufacture of bricks, blocks structural ceramics. and other ceramic products, especially when evaluated on exposure to weathering."

Jan 1, 2014

By G. S. Hill

A large amount of the stereological error associated with liberation studies can he eliminated by assessing areas instead of linear intercepts. The presentation of a simple geometrical model as a stereological 'worst case' allows calculation of the worst possible grade/recovery curve for a given assemblage of areas. The true results are expected to lie in the window between this worst case and the hest possible case, represented by uncorrected data. The width of this window typically corresponds to an error margin of about 5% grade at a given recovery. An indication of where the data lies within the range of possible grade/recovery results may he obtained from a qualitative analysis of the locked section complexity. Assemblages consisting of texturally complex locked sections (ie. containing many mineral nuclei) are likely to exhibit minimal stereological bias and therefore will tend to lie close to the uncorrected side of the grade/recovery window.

Jan 11, 2011

By J. L. Jambor, H. W. Nesbitt

Oxidative dissolution of pyrrhotite and pyrite is largely responsible for the sulfate-rich waters of the vadose zone in the Waite Amulet tailings. Although the shallowest of the sulfate-rich waters are of the Fe-SO4 type, they change to Mg-SO4-type, near-neutral waters within 1-2 m of the tailings surface. Phyllosilicates and amphiboles are the only minerals present in sufficient quantity to ameliorate the amount of acidity produced. X-ray diffraction and microscopic studies of bulk sample indicate that quartz, chlorite, talc, amphiboles, magnetite, albite, and micas are the major and minor non-sulfide minerals, but their variations with depth do not give clear indications of depletion in the vadose zone. Mineralogical and bulk chemical compositions of the tailings confirm that Fe2O 3 has accumulated in large quantity in the vadose zone, with the Fe having been derived from Fe sulfides. When the effect of Fe2O3 is accounted for, the bulk compositions suggest that SiO2 is slightly more abundant in the vadose zone than in the saturated zone. This may be the result of residual enrichment of siliceous minerals such as quartz and albite in the vadose zone. Weathering of the tailings since the cessation of deposition in 1962 has resulted in a well-defined zone of sulfide depletion and secondary sulfate-mineral development. Although some silicate dissolution is indicated by pore-water compositions, the role of silicates in providing neutralization seems to have been minimal. The contribution by silicate minerals in laboratory tests of neutralization potential may be excessive relative to that in natural settings.

Jan 1, 1999

By Tsutomu Yamamura

The electrolytic reduction mechanism of rare-earth chlorides such as LaCl3, CeCl3, NdCl3, ` SmCl3 and DyCl3 in alkali chloride baths has been investigated in NaCl, KCI and eutectic LiCI- KCI by means of electrochemical transient methods. The thermodynamic behaviors of rare-earth containing species have been discussed in the frame of Electrode potential - P02- diagram. Low current efficiency found in the case of Nd electro-winning has been attributed to the dissolution of Nd into the bath. The analyses of electrochemical measurement required the elucidation of the effects of the factors such as under-potential deposition, metal dissolution, moisture and oxygen partial pressure.

Jan 1, 2003

By V. A. Luganov

During the treatment of raw materials containing arsenic and antimony, problems in the distribution of these elements in the process products occur. In a number of cases in processing of copper-bearing materials, it is possible (or necessary) to obtain speiss. The purpose of the present research is to study the theoretical aspects and analyze the technological possibilities of producing copper-bearing speiss and the subsequent electrometallurgical processing with copper extraction as well as arsenic and antimony utilization. Copper arsenide (Cu3As) and copper antimonide (Cu3Sb) are the main components of the speiss. A thermodynamic analysis of the electrochemical oxidation of Cu3As and Cu3Sb, carried out using Pourbaix diagrams, showed that in a pH range from 0 to 2, oxidation potential 0.45-0.55V, ions of copper and arsenic and antimony trioxide are in the equilibrium. The kinetic study has shown, that with an increase in the polarization potential, the dissolution process changes from chemical to diffbsion control. An increase in temperature stabilizes the electrolysis process due to dissolution of arsenic trioxide forming on the anode. Electrolysis of speiss using a cathode diaphragm with the solution pH = 1-2, current density 150-200 A/m2 and temperature 60-70°C makes it possible to obtain cathode copper with a current efficiency of 95-96% and to remove the arsenic from the process during the electrolyte cleaning process. The arsenic content in the cathode copper did not surpass 0.002%. As the result of the research, a technological flowsheet for copper-lead speiss processing was developed. At the present time this technology is undergoing pilot testing.

Jan 1, 1999

By Patrick R. Taylor

In the search for the development of more "environmentally friendly" and more intensive waste disposal approaches to meet more and more stringent environmental regulations, thermal plasma-based processes? are considered one of the most promising alternatives to well-established technologies such as incineration. This paper presents an overview on the research and development status of thermal plasma-based waste remediation technologies. The properties of thermal plasma are described. Due to its unique feature of high-energy intensity and super high temperature, thermal plasma is particularly capable of destroying organic-containing wastes. Its potential and promising application to waste remediation may include: treatment of incinerator ashes; metallurgical dusts (especially, electric arc furnace dust); medical wastes; radioactive wastes; and other Resource Conservation and Recovery Act (RCRA) listed hazardous wastes. Many research institutes and vendors have been involved in the development of thermal plasma-based waste treatment-technology encouraged by the cleanup programs supported by the Environmental Protection Agency (EPA), the Department of Energy (DoE) and the Department of Defense (000). More recently, thermal plasma-based waste treatment technologies (sometimes called plasma-enhanced pyrolysis) are focused more and more on not only just destroying organic wastes but also on how to practically, and economically recover energy contained in the organic waste materials in addition to the recovery of metals in order to offset the high operating costs.

Jan 1, 2003

By Moto Goto

Today, Pierce-Smith converters, coupled together with various types of smelting units, are used in most of the world's smelters. However, due to the "batch" processing nature, and problems associated with fugitive emissions during the transfer of melt and blowing stages, this arrangement will unlikely be adopted in future smelters. Modern day alternative processes include the Mitsubishi Process, Outokumpu Flash Smelting and Flash Converting Process, the Noranda Process, and the Ausmelt Process, but only the Mitsubishi Process is a "truly continuous" smelting and converting operation, producing a constant flow of blister without tapping, and is economically proven by long term commercial operations. This paper reviews recent advances in modern continuous converting technologies, with a special section devoted to operation of the "first standalone Mitsubishi C-furnace" coupled together with a Noranda Reactor, at Port Kembla Copper Pty. Ltd. in Australia.

Jan 1, 2003

By Selvin Yesilay, Guray Kaya, Bekir Karasu, Asli Cakir

"In this investigation, the wastes of Eti Maden Kirka Boron Company of Turkiye were evaluated in the production of diopside and anorthite-based glass-ceramic glazes suitable for porcelain tiles fast and single-fired under industrial conditions. First of all, high wear resistant frits were produced with the use of concentrator and derivative borax wastes. Second of all, pre-engobed porcelain tile bodies were coated with the standard and newly produced frit-based glazes and industrial fast single-firing was employed. Final products were undergone to the certain standard tests to determine their Vickers hardness, wear resistance, thermal expansion coefficient values, gloss and coloring parameters. The micro-structures and phase formations of the fired glazes were also studied. Consequently, it was confirmed that the utilization of borax solid wastes in fast single-fired porcelain tile glass-ceramic glazes is possible. Introduction Porcelain tiles were introduced at the end of 1980s by Friandre, one of the leading Italian porcelain manufacturers. The American National Standard Specifications for Ceramic Tile defines porcelain tiles as: dense, smooth, impervious (with water absorption value less than 0.5 %) and stain resistant [1]. The excellent technical performances for ceramic tiles, such as mechanical, wear, frost and chemical resistance that make their use possible in indoor and outdoor building applications [2-3]. In the last decade, the growth rate of the global production of porcelain tiles increased more than those of other ceramic products; in fact, the technical properties of porcelain tile, coupled with even more improved aesthetic appearance, gave it a prominent role on the tile market [2]. Glass-ceramics are composed materials of one or more crystalline phases immersed in a residual glassy phase [4-5]. Glass-ceramic technology is based on controlled nucleation and crystallization of bulk glass [6]. The concepts of controlled crystallization of glass designate the separation of a crystalline phase from the parent glass in the form of tiny crystals. Their growth rate and final size are controlled by a suitable heat treatment [7]."

Jan 1, 2008

By E. Almendras de Siegel

Pyrometallurgical processes have the thermodynamic capability of treating complex and dirty ores and concentrates to produce high purity metals and inert slags. Modem pyrometallurgical processes are environmentally sound and competitive with other processes. However, there is still a need for sensors and other practical tools that permit a rapid evaluation of the performance of these processes. In order to contribute to satisfying this fundamental requirement, the authors developed the IDENT.LA software that permits the automatic mineralogical analyses of inorganic materials, including the final and intermediate products of pyrometallurgical processes. The technique allows determining the grain size distribution of mineralized inclusions, the surface relations between metallic phases, and conducting modal analyses of the essential phases that are present in the samples. Three basic automatic operations are performed: creating a representative image of the sample; identifying the metallic and non-metallic phases; and measuring the features of the resulting image. The results are used to evaluate the performance of pyrometallurgical and other processes. In this paper, the authors discuss the application of the technique to a sample of slag from a slag cleaning process that uses a carbonaceous reductant. In this case, process performance impacts not only on the efficient reduction of the slag magnetite and on copper recovery but also on the quality of the process off-gas. The mineralogical analysis of the slag is a valuable tool in assessing process performance and in recommending changes of operating conditions.

Jan 1, 1999

By Yong .. Jun Wu

Laminated ceramics have received widely scientific and commercial attention because their properties, such as mechanical properties and electrical properties, can be tailored by adjusting the structure, thickness and composition of the different layers. For example, ferroelectric Bi4Ti3O12 (BIT) which has a positive temperature coefficient of dielectric constant (,E) can be used to modify the negative tE of typical microwave dielectric ceramic BaNd2Ti4O12(BNT), However, BaNd2Ti4O12/Bi4TiO12/Bi4Ti3O12/BaNd2Ti4O12 (BNT/BIT/BNT) laminated ceramics could not be prepared by the general method because the optimal sintering temperature of BaNd2Ti4O12 ceramic (around 1350°C) was much higher than that of Bi4Ti3O12 ceramic (around 1100°C). In this research, a new method of spark plasma sintering (SPS) combined with post-sintering was successfully proposed to prepare BNT/BIT/BNT laminated ceramics. It was divided into three steps. In first step, the BaNd2Ti4O12 ceramics were prepared by conventional sintering method. In second step, the calcined and pre-pressed Bi4Ti3O12 powders were sandwiched between BaNd2Ti4O12 ceramic pellets and spark plasma sintered at 900°C for 10min to synthesize BNT/BIT/BNT composite ceramics. In the last step, a post-sintering was employed to reoxidize the partially reduced BNT/BIT/BNT composite ceramics. The results of scanning electron microscopy (SEM) and electron probe microanalysis (EPMA) showed that BNT layer and BIT layer were well bonded and no significant interfacial infiltration between them was observed. The sandwiched BNT/BIT/BNT ceramic with 10.7% BIT in volume has a dielectric constant of 92.85, a low dielectric loss of 01068 and a small temperature coefficient of dielectric constant of 35 ppm/°C at MHz.

Jan 1, 2003

By Berndt Moeller

Mercury-cell chlor-alkali production plants generate mercury contaminated wastewater streams from which mercury must be precipitated and filtered, resulting in a sludge containing 2% mercury (designated KI06) that cannot be landfilled in the United States without treatment. REMERC is a chemical treatment process used to recover 99% of the mercury from wastewater sludge generated at these plants. The process uses leaching to oxidize mercury compounds to mercuric chloride, washing and filtration to separate mercuric chloride from the treated sludge, and cementation to reduce the mercuric chloride to metallic mercury. Mercury not recovered in cementation is recycled to the wastewater process for precipitation and filtration. Treated sludge contains less than 260 ppm total mercury and 0.2 ppm TCLP, meeting the USEPA low mercury subcategory specifications that allow landfill disposal. REMERC uses readily available chemicals, is straightforward to control and inexpensive to operate, has no mercury emissions to air, and recovers metallic mercury. REMERC enabled significant cost savings including lower solids disposal costs, recovery and reuse of metallic mercury in the chlor-alkali process, and ability to treat non-wastewater sludge. No new EPA permits were required. REMERC was shown to be a viable process for recovery of metallic mercury from K106 designated sludge.

Jan 1, 2003

By K. Morsi, S. K. Kassegne, K. S. Moon, A. Numula

"Current Activated Tip-based Sintering (CATS) is a new process for the powder-based manufacturing of macro, micro and possibly nano-scale features and shapes. CATS enables the selective sintering of powders by localizing current activation conditions through an electrically conducting small tip (either in the stationary or moving mode). This paper presents preliminary experimental results on the CATS of reactive mixtures of Ni/Al powder to form nickel aluminide intermetallics. Preliminary investigations on the effect of current on the reaction characteristics are discussed.IntroductionSpark Plasma Sintering (SPS) has been the subject of intense research over the past decade [1,2, 3,4,5,6]. The process boasts remarkable advantages which include ultra fast heating rates (hence by-passing low temperature non-densifying sintering mechanisms), considerably lower sintering temperatures and shorter sintering times than achieved in conventional sintering. The process is however limited to the generation of simple geometries on the macro-scale. Recently three of the authors conducted work on a novel process ""Current-activated tip-based sintering (CATS)"" [7], where electric current is passed through a conducting tip that is placed or allowed to travel over a powder bed/compact to locally sinter powders. lD, 2D and 3D micro-scale sintered shapes can be generated with the possibility of 3D rapid prototyping on the macro/micro or nano-scale. Although CA TS of single phase powders has been conducted, the CATS of reactive powders has not yet been investigated.The Ni-Al phase diagram contains five intermetallic compounds, AhNi, AhNh, AlNi, AhNi5 and NhAl. Out of these intermetallics, NiAl and NhAl have received the vast majority of scientific and industrial interest [8]. NhAl can be formed by reaction synthesis, where nickel and aluminum reactant powders are heated to a reaction ignition temperature at which the reactant powders are converted to the intended intermetallic product. The reaction is exothermic which gives rise to considerable compact self heating, thus instantaneously raising the compact temperature by several hundred degrees which facilitates sintering [8]. Applying and electric current locally would not only provide for a rapid local reactive sintering, but would generate a number of intriguing scientific investigations. For example, of interest would be, how would the reaction propagation and microstructural/phase evolution be affected by the temporal and spatial temperature and current distributions."

Jan 1, 2011

By Boxun Lu, Juan Wei, Kun Chen, Wanlin Wang, Lejun Zhou

"Slag system is an indispensable part during the continuous casting process, and playing various important roles like absorbing inclusions, modifying heat transfer rate, preventing oxidation of molten steel, etc. to ensure the smooth process and excellent slab quality. However most slags contains more than 8% fluorides which tend to introduce a series of environmental and health problems. This study involves the research of the removal of fluorine through the chemical composition optimization. Through the studies of CCT, DHTT, XRD and SEM, it has been successfully founded that the crystalline phase of Ca11Si4B2O22 discovered in this study shows very similar crystallization property as Cuspidine (Ca4Si2O7F2), which is the most important crystalline phase in the current fluorine bearing slags. Moreover, the optimized free/low fluorine slag shows the opportunity to replace conventional high-fluorine mold slag for casting medium carbon steels that is regarded as the bottleneck of green slag development for continuous casting.IntroductionMold flux has been widely used in continuous casting to control heat transfer, lubricate the strand, absorb inclusions, provide insulation and prevent oxidation of the molten steel[1-3]. It usually contains fluorides, like CaF2, NaF etc., which are used to control the viscosity and solidification temperature of mold fluxes [4-5]. However, the presence of fluoride leads to corrosion of equipment, serious environmental pollution (toxic volatiles and water pollution), and high processing cost of cooling water[6-7]. Therefore, the study of low or free fluorine mold flux is of interest and attracts worldwide attention.S. Y. Choi et al. [4] used B2O3 as a substitute for cuspidine in steel B2PB2) however, B2O3 content was extremely high (up to 30 w%). Other studies have investigated F-free mold flux by adding or optimizing components as MgO, Li2O, B2O3 et al[8-11]. However, most of these focused on the melting and viscosity issues or for low or ultra-low carbon steels, where crystallization tendency is not significantly strong. Very few studies regarding to the development of low/free Fluorine mold flux for casting medium carbon (MC) steels have been conducted, due to the difficulty of the crystallization and heat transfer control without the formation of cuspidine."

Jan 1, 2014