By Matti J. Saarivirta

The relative machinabilities of the precipitation-hardenable Cu-0.9 pct Cr, Cu-0.25 pct Zr, and Cu-0.9 pct Cr-0.25 pct Zr alloys are improved from 18 to 80 pct by 0.75 to 1.25 pct Pb. The Lead also improves the tensile strength, hardness, ad resistance to softening of the Cu-Cr and Cu-Cr-Zr alloys. When the alloy containing 0.7 to 2.2 pct Cr, 0.10 to 0.25 pct Zr, 0.75 to 1.25 pct Pb, and balance copper is solution-annealed at 1000°C (1830°F) and then aged at 525°C (Y75°F), tensile strength of 65,000 psi, 16 pct elongation, 62Rb hardness, and 84 to 87pct IACS electrical conductivity are obtained. The copper base Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys have high electrical and thermal conductivities, high strength and resistance to softening at elevated temperatures, but their machinability is poor, i.e., close to that of the pure copper. In the manufacture of various components such as welding electrodes or electrical and thermal conductors it is ofter desirable that the alloy have good machinability for high production rates and long tool life. Thus, alloys that combine these properties may be used not only for existing applications, but for new ones where good machinability is a requirement. This investigation was undertaken to improve machinability without impairing other desirable characteristics of the Cu-Cr, Cu-Zr, and Cu-Cr-Zr alloys. These commercial alloys contain about 0.4 to 1.2 pct Cr, 0.10 to 0.25 pct Zr, and balance copper. Lead was selected as an element that should improve the machinability and possibly other characteristics of the alloy. WORK PROCEDURE This investigation began with a study of the effect of lead on the hardness, tensile strength, electrical conductivity, and machinability of the binary alloy containing 0.10 to 1.30 pct Cr and balance copper. This was followed by an investigation of the effect of lead on the Cu-0.1 to 0.4 pct Zr and Cu-Cr-Zr alloys. The alloys were made from initially oxygen-free copper and for comparison some castings were made from phosphorus-deoxidized Lake Copper. Commercially pure chromium, zirconium, and lead were used for alloying. In melting the chromium was added to molten copper at 1400°C (2550°F), the heat held for 15 min at temperature, and the temperature then lowered to 1350°C (2460°F) when the other elements were added. The alloys were held for 15 min at this temperature and cast into a cast-iron mold. One-kilogram, 3-in.-diam castings were made. An argon cover was maintained during melting and casting to prevent oxidation. The chemical compositions of the alloys are shown in Table I. The micro structure and properties of the alloys were studied in the cast and wrought conditions prior to and after various solution-annealing and heat-treating cycles. The relative machinability was determined as a function of the lead content and compared with the free-machining Cu-lpct Pb alloy. To determine the machinability, 13/16-in.-diam cast specimens were cut by a machine hack saw using a constant cutting speed of 50 fpm, a fixed feed force, and a new blade for each alloy specimen. Molybdenum highspeed steel saw blades, 0.032 in. thick with 14 teeth per in., were used in all tests. No cutting fluid was used. Five tests were made on each specimen and the average elapsed time per test was taken as a measure of the relative machinability for that alloy. The variation of cutting time for each alloy was less than 110 pct.

Jan 1, 1969

Charles Mather MacNeill, President of the Utah Copper CO. and of the Chino Copper Co., and a life member of the Institute since 1899, died at his home in New York on March 17, after a very brief illness with pneumonia. Mr. MacNeill was born at Oak Park, Ill., in 1871, and began his connection with mining enterprises immediately after graduating from high school, his first position being that of cashier with the Pueblo Smelting and Refining Co. He later went to Aspen, Colo., as manager of the Holden lixiviation plant. In 1893, he went to Cripple Creek as manager of the Lawrence Reduction Works, in which Mr. Holden and the late Capt. J. R. DeLamar were large owners. It was at this plant that Mr. Jackling became associated with him. The plant was destroyed by fire and, early in 1894, Mr. MacNeill became associated with Messrs. Spencer Penrose and Charles L. Tutt in a plan to finance and erect a chlorination plant at Colorado City, Colo., for the treatment of Cripple Creek ores. This plant was erected and was known as the Colorado-Philadelphia Reduction Works. Mr. MacNeill was general manager of the plant, Mr. Tutt having been president and Mr. Penrose, secretary and treasurer. The plant was very successful and was expanded, hally being reorganized under the name of the United States Reduction & Refining Company. Late in 1903, or very early in 1904, D. C. Jackling called the attention of Messrs. MacNeill and Penrose to the copper properties in Bingham Cañon, Utah, which have since become the main properties of the Utah Copper Co. After extended examinations and milling tests, these properties were bought, Mr. MacNeill becoming president of the Utah Copper Co., Mr. Penrose, secretary-treasurer, and Mr. Jackling, general manager. Mr. MacNeill remained president of the company to the time of his death. Mr. MacNeill was also a director, a member of the executive committee, and was largely interested in the Ray Consolidated Copper Co.; he was also president and a member of the executive committee of the Chino Copper Co. He had a variety of other mining interests, but the ones mentioned were distinctly the meost important. He was a director

Jan 1, 1923

Charles Mather MacNeill, President of the Utah Copper CO. and of the Chino Copper Co., and a life member of the Institute since 1899, died at his home in New York on March 17, after a very brief illness with pneumonia. Mr. MacNeill was born at Oak Park, Ill., in 1871, and began his connection with mining enterprises immediately after graduating from high school, his first position being that of cashier with the Pueblo Smelting and Refining Co. He later went to Aspen, Colo., as manager of the Holden lixiviation plant. In 1893, he went to Cripple Creek as manager of the Lawrence Reduction Works, in which Mr. Holden and the late Capt. J. R. DeLamar were large owners. It was at this plant that Mr. Jackling became associated with him. The plant was destroyed by fire and, early in 1894, Mr. MacNeill became associated with Messrs. Spencer Penrose and Charles L. Tutt in a plan to finance and erect a chlorination plant at Colorado City, Colo., for the treatment of Cripple Creek ores. This plant was erected and was known as the Colorado-Philadelphia Reduction Works. Mr. MacNeill was general manager of the plant, Mr. Tutt having been president and Mr. Penrose, secretary and treasurer. The plant was very successful and was expanded, hally being reorganized under the name of the United States Reduction & Refining Company. Late in 1903, or very early in 1904, D. C. Jackling called the attention of Messrs. MacNeill and Penrose to the copper properties in Bingham Cañon, Utah, which have since become the main properties of the Utah Copper Co. After extended examinations and milling tests, these properties were bought, Mr. MacNeill becoming president of the Utah Copper Co., Mr. Penrose, secretary-treasurer, and Mr. Jackling, general manager. Mr. MacNeill remained president of the company to the time of his death. Mr. MacNeill was also a director, a member of the executive committee, and was largely interested in the Ray Consolidated Copper Co.; he was also president and a member of the executive committee of the Chino Copper Co. He had a variety of other mining interests, but the ones mentioned were distinctly the meost important. He was a director

Jan 1, 1923

By H. LeRoy Scharon

The electrical resistivity method was utilized at 245 road cuts and structure sites over the 166 miles of the Philadelphia and Western Extensions of the Pennsylvania Turnpike System. Varying geologic structures and rock types afforded an excellent academic study of the method as well as a practical application to modern highway engineering.

Jan 4, 1951

PRESIDENTS DAVID THOMAS 1871 R W RAYMOND 1872 R W RAYMOND 1873 R W RAYMOND 1874 A L HOLLEN 1875 ABRAM S HEWITT 1876 T STERRY HUNT 1877 ECKLEY B COXE 1878 ECKLEY B COXE 1879 WILLIAM P SHINN 1880 WILLIAM METCALF 1881 RICHARD P ROTHWELL 1882

Jan 1, 1910

By J. A. Herbst, K. Rajamani, Y. C. Lo

In spite of potential theoretical and economic advantages of large-diameter ball mills, many manufacturers elect not to build them owing to what is perceived as an excessively large design risk. This is because traditional predictions for mill scaleup to large diameters are not always accurate. Alternative methods of analysis and scale-up are required. Recent studies have shown that detailed population balance models which account for important grinding subprocesses (grinding kinetics, material transport, and classification) are capable of predicting the performance of small- and intermediate-diameter mills (up to 4.3 m, or 14 ft) from small-scale batch tests. These same models are used in the current study to predict the performance of a "borderline "large ball mill (4.7 x 5.5 m, or 15 x 18 ft) at Asarco's Sacaton operation, a ball mill (5 x 5.8 m, or 16.4 x 19 ft) at Kennecott's Chino operation, and one of the world's largest ball mills (5.5 x 6.4 m, or 18 x 21 ft) at Cities Service Pinto Valley operation. Model parameters required for scale-up have been estimated in a 380-mm-diam (15-in.-diam) batch mill. Predictions are compared with the results of detailed plant sampling in the three plants. For the Sacaton and Chino operations, the error of the predictions was found to be less than 2.5%, while the corresponding error for the Pinto Valley operation was less than 2.7%. It is concluded that proper representation of the major subprocesses of grinding in the model equations is the key to achieving accurate scale-up. Of special importance is the need to account for the size distribution of the grinding media and the influence of the size distribution environment in the mill on grinding kinetics.

Jan 1, 1986

By Charles M. Means

A thoroughly modern coal-handling system has been installed at the Pittsburgh Terminal H. H. &. Coal Co.'s new No. 8 shaft, or Cover-dale mine, about 11 mi. (17.7 km.) from Pittsburgh on a spur of the Montour R. R. The Pittsburgh scam, which is the one worked, is reached at a depth of 342 ft. (104 m.). Power is delivered to the mine at 22,000 volts over a transmission line of the bow-arrow type of construction. A private telephone line connecting the various mines and the main office in Pittsburgh is carried on the same poles. The high-tension line is brought to an outdoor, step-down, transformer substation, where three 833-kv.-a., single-phase, 60-cycle, oil-insulated, self-cooled transformers reduce the potential to 2300 volts. The transformers are protected by electrolytic, aluminum-cell lightning arresters, horn gaps, and choke coils. High and low-tension busses, together with fuses, choke coils and air-break horn-gap switches with thcir remote-control operating mechanism are mounted on a substantial structural-steel tower 25 ft. (7.6 m.) in height. Mine Substation The transformer substation is adjacent to a. pressed-brick building that houses direct-current substation equipment together with switchboards, etc., for the control and distribution of power. This building also contains the hoist for the men and supplies. Main Switchboard The 2300-volt circuit is carried underground in a conduit from the transformer substation to an oil switch in the substation and supply hoist building. This is the main switch controlling the 2300-volt busbars mounted back to a twelve-panel black-slate switchboard. From the switchboard, 2300-volt circuits are carried to transformers feeding the street and house lighting systems and to other transformers furnishing power for the elevator and lighting circuits in the store building. Other 2300-volt circuits run from this switchboard to the main hoist building, fan house and auxiliary or man-and-supply hoist. High-tension wiring,

Jan 1, 1922

AT the Non-ferrous Metallurgy session on Wednes-day afternoon, R. M. Roosevelt, vice-president of the Eagle-Picher Lead Co., presided. The paper "Sug-gested Improvements for Smelting Copper in the Rever-beratory Furnace," by G. L. Oldright and F. W. Schroeder, was presented by. Mr. Oldright. It was brought out that lessening of dusting of the charge would increase the life of the arch at present operating temperatures, but will not allow much higher tempera-tures to be used unless dusting can be entirely elim-inated. The best opportunity for improving rever-beratory practice lies in the use of still higher tempera-tures but this requires the development of refractories superior to those now used. There was an interesting discussion of the facts brought out. The paper. on the "Formation and Decomposition of Zinc Ferrite," by

Jan 3, 1928

PRESIDENTS DAVID THOMAS 1871 R W RAYMOND 1872 R W RAYMOND 1873 R W RAYMOND 1874 A L HOLLEN 1875 ABRAM S HEWITT 1876 T STERRY HUNT 1877 ECKLEY B COXE 1878 ECKLEY B COXE 1879 WILLIAM P SHINN 1880 WILLIAM METCALF 1881 RICHARD P ROTHWELL 1882

Jan 1, 1910

By William Klement

THIS note reports the results of some attempts to metastably extend the primary solid solubilities of tin, antimony, and silicon in silver by rapidly quenching these binary alloys from the melt. The procedures employed for alloy preparation, quenching, and Debye-Scherrer X-ray diffraction measurements have been described elsewhere. The lattice parameters obtained for the fcc structures in Ag-Sn and Ag-Sb alloys are presented in Fig. 1, together with the results of Owen and Roberts.4 Alloy compositions are believed to be within ± 0.2 at. pct on the basis of negligible weight losses during preparation and reproducibility of the lattice spacings. Diffraction lines from hcp phases were also detected: the relative visual intensities of the fcc (200) and hcp (10.2) lines were estimated as shown in Table I. The intensities were m for the (200) and w for the (10.2) in a quenched 13.6 at. pct Sn alloy: a lattice spacing for the fcc structure could not be reliably obtained, however. As seen from Fig. 1, the lattice parameters vary linearly with composition up to 8., at. pct Sb and 13." at. pct Sn, respectively, which may be compared with the maximum equilibrium solid solubilities5 of 7.2 at. pct Sb and 11.5 at. pct Sn, respectively. The presence of the hcp phases, which were found together with the fcc phases, is a consequence of the competition1,3 in the nucleation and growth processes during solidification. Both the fcc and hcp phases must be of the same composition for those alloys in the range where lattice parameters increase linearly with solute concentration. Despite much effort with quenched alloys of several silicon concentrations, it has not been possible to obtain lattice spacings of sufficient precision to establish the variation of lattice parameter with composition or the maximum metastable solid solubility: the equilibrium data5 suggest little primary solid solubility of silicon in silver. For alloys containing less than 16 at. pct Si, the Si (111) diffraction line was not observed. For alloys containing 10 to 25 at. pct Si, faint low-angle lines were detected and these could be indexed as the (10.0), (00.2). and (10.1) reflections of an hcp structure with a = 2.87 + 3A. c = 4.52 ± 3A, and c/a = 1.57 ± 2. The 16 at. pct Si alloy was quenched to, and examined at. liquid nitrogen temperatures without any change observed in the proportion of the hcp phase. These experiments were jointly supported by the Atomic Energy Commission and Office of Naval Research under a program directed by Professor P. Duwez. The assistance of H.-L. Luo and A. Abu-Shumays is acknowledged. as is the support afforded

Jan 1, 1965

By F. F. Sharpless

ON Saturday evening, Sept. 9, a small party of Institute members, their wives and friends, left New York to attend the Fall Meeting of the Institute at San Francisco. In this party there were: President and Mrs. Arthur S. Dwight; Mr. and Mrs. George D. Barron; Mr. and Mrs. H. J. Stehli; N. S. Spencer and Miss Spencer; the Secretary and Mrs. F. F. Sharpless. They were joined at Chicago by E. F. Eurich, and by Mr. and Mrs. R. L. Baldwin and daughter. Our party was met at Chicago by Mr. and Mrs. L. V. Rice, Mr. and Mrs. A. D. Terrell and W. F. Boericke, who constituted themselves an impromptu entertainment committee and proceeded to carry out a delightful little program. We were taken to the Lake Shore drive, where a stiff wind off the lake refreshed us after a sultry day on the train, and on our return to the city saw Chicago illuminated with all its brilliance of electricity. We were entertained at dinner at the Drake Hotel. In spite of being two hours late getting into Omaha, we were right on the dot at Denver on Tuesday morn-ing. Horace F. Lunt came to the hotel soon after breakfast, and told us that a trip to the mountains had been planned. Having learned the number in the party, he began to gather up his automobiles for a 10 o'clock start.

Jan 10, 1922

PRESIDENTS DAVID THOMAS 1871 R W RAYMOND 1872 R W RAYMOND 1873 R W RAYMOND 1874 A L HOLLEN 1875 ABRAM S HEWITT 1876 T STERRY HUNT 1877 ECKLEY B COXE 1878 ECKLEY B COXE 1879 WILLIAM P SHINN 1880 WILLIAM METCALF 1881 RICHARD P ROTHWELL 1882

Jan 1, 1910

By Ralph Smith

DEVELOPMENT of the lime industry in Ste, Genevieve County began in a crude way in 1840. According to information furnished by the Missouri Bureau of Geology, in the early days small vertical kilns built of stone were used, and wood was the fuel. Modern development began in 1904 when one company introduced steel shells lined with firebrick. Within a few years two more companies erected similar plants, and in 1925 a fourth company began operations. Thus there are today four lime companies at Ste. Genevieve, all operating at high capacity and with a gradually increasing production. GEOLOGY The limestone of Ste. Genevieve County, which has the chemical composition and purity required for lime burning, is the upper 80 or 90 ft. of Spergen formation. The Missouri Bureau of Geology, in its geological map of Ste. Genevieve County, gives the Spergen formation a total thickness of 160 ft., but only the upper portion is pure enough for lime burning, with an average raw-stone analysis of 98.7 per cent CaCO3; 0,35 Si02; 0,3 R203; 0.35 MgCO3; 0.3 SO3. The Spergen, one member of the Meramac group, Iowa series, of the Mississippian system, underlies an area approximately 12 miles long north and south, by 5 miles wide east and west (Fig. 1) in Ste. Genevieve County. The entire eastern two-thirds of Ste. Genevieve County is sedimentary, the formations dipping gently toward the east on an average grade of about 4 per cent, or 2 ½ °. Thus the outcrops of the various sedimentaries run approxi-mately north and south. A line running west from Ste. Genevieve crosses the outcrops of the sedimentaries, ranging from the top of the Mississippian to the Ozarkian geological system in a space of 12 miles. Thus with the gentle dip of 2 1/2° the 160-ft. thickness of the Spergen formation stretches out in its outcrop so that it is approximately one mile

Jan 1, 1938

By J. L. Huiatt, D. G. Foot

The Bureau of Mines devised a direct flotation method for treating low-grade carnallite (KCl*MgC12*6H20) and sylvinite (a mixture of KC1 and NaCl) ores characterized by a high content of water-insoluble impurities. The procedure consists of flocculation-depression of the insoluble slimes; decomposition leach (carnallite only); potash rougher, cleaner, and recleaner flotation; and final product leaching. The technique eliminates the necessity of removing the water-insoluble slimes by mechanical or flotation desliming. Laboratory results demonstrated that the direct flotation procedure, when compared with conventional techniques, yielded equivalent or improved flotation results with equal or less reagent consumptions. The direct flotation method recovered 81.6% of the solid phase KC1 from camallite ore and 79.7% of the KCl from sylvinite ore in final products containing 60.5 and 60.9% K2O, respectively. A flowsheet incorporating the described flotation procedure is presented.

Jan 1, 1983

By E. C. Burke, W. R. Hibbard

Plastic deformation in magnesium single crystals was studied by tensile tests at room temperature utilizing an improved preparation and testing technique. Consistent critical resolved shear stress values for basal slip were obtained. The advent of pyramidal slip at room temperature was rationalized upon the basis of grip constraints. A bend-twinning hypothesis was advanced as an explanation of mechanical twinning which occurs as a complex stress-relief mechanism. INVESTIGATIONS of the plastic deformation of magnesium have been limited to the determination of the fundamental kinetics which may be summarized as follows: 1—Twinning on the {102).l 2— Slip on the (001) plane in the [loo] direction at room temperature.' 3—Slip on the {101) or {102) plane in the [loo] direction above 225°C." 4—Critical resolved shear stresses for basal slip in tension at room temperature of 83 g per sq mm with a variation from 57 to 127 g per sq mm." Bakarian' studied the compression of thin wafers of magnesium single crystals and classified the components of the deformation mechanisms as follows: 1—The Basal field: (001) at an angle of less than 20" to the compression surface. Fracture along {101} or slip on (001) followed by {101} fracture. 2—The prism field: (001) at an angle greater than 60" to the compression surface. Twinning on the {102) generally occurring during the early stages of loading, basal slip in the areas of original orientation and (001) slip within twins. 3—The central field: (001) at angles greater than 20" but less than 60" to the compression surface. Slip on the (001). 4—The critical resolved shearing stress for {101} slip above 225°C was 400 g per sq mm. Observations of mechanical twins in hexagonal close-packed metals have been summarized by numerous investigatorsb-' emphasizing a lateral or rotational atomic adjustment, in addition to the pure twinning shear, and the importance of reorienting the basal plane to a position more favorable for continued slip, rather than the resulting small dimensional changes. Criterion for the operative twinning planes has not been clearly established. Schmid and Boas hurmised that an energy condition related to the atom movements is the determining factor. MillerQ bserved that twinning stresses in zinc crystals decreased as the amount of prior deformation increased. Preparation of Specimens Magnesium single crystals % in. in diam x 8 in. long were grown from the melt under an argon atmosphere in a gradient furnace similar to that described by Jillson." Magnesium containing 0.018

Jan 1, 1953

By John B. Pearse

IN order to get an idea as to the strength of steel rails, it will be well to review the tests to which iron rails have been subjected. In England, Mr. Ashcroft found that the best 80 pound rails broke under a 300 pound weight, falling 15 feet. In Germany the Society of Railway tyfanage1-s determined 011 and have long applied a test of 1000 pounds falling 101/2 feet, as the standard which all first-class iron rails must reach. In this country no inspection nor test is applied, but tests made show that iron rails fro; our most reliable makers, break under a G foot fall of a 1500 pound drop as an extreme test, most of those tested breaking under a far less test; some breaking with less than a 3 foot fall of the same weight. Everywhere where steel has been used, engineers have come to the conclusion that some test is required to show the regularity and strength of the product. As compared with iron, the tests which steel will stand are wonderful. After numerous experiments partially based on the experience of the rail-mill at Graz, belonging to the Southern Railway of Austria, the Society of German Railway Managers fixed upon a test of 2000 pounds falling 138 feet. They found that this test represented the steel which suited their necessities, and also found that with steel of otherwise average purity, this test represented about one-half per cent. of carbon, and made it a rule to take no steel containing under three-tenths of a per cent. of carbon, because it was too soft. They expressed a hope that a harder steel could soon be made tough enough to stand the same test. I n England, a test was adopted of 2240 pounds, falling 15 to 17 feet on the rail on heavy bearings. This test has been found satisfactory under heavy traffic on average road-beds, and has been invariably

By S. S. Shen, M. J. Pool, P. J. Spencer

Heats of solution of gold and copper in dilute Au-Cu-Sn alloys have been determined using a liquid metal solution calorimeter. The self-interaction coefficient, Au - has been calculated at constant copper concentrations and n cu has likewise been determined at constant gold contents. Good experimental agreement is obtained between the interaction coefficients and nAu Cc thus demonsbating the reliability of the measured heat values. The measured data are compared with the Predictions of certain solution models. In previous publications,1,2 the results of calori-metric investigations of dilute Ag-Au-Sn and Ag-Cu-Sn alloys have been presented. The present work on the Au-Cu-Sn system concludes a program of studies of enthalpy interaction coefficients in dilute alloys of the Group IB metals with tin. Since the definition and derivation of an enthalpy interaction coefficient has been discussed previously,1,2 no restatement of this theory will be presented here. From the determination of the partial heat of solution of gold and copper in ternary alloys of various copper and gold contents, values of the interaction coefficients can be calculated. These coefficients give an insight into the various solute interactions that occur in the liquid solutions since changes in their magnitude and sign reflect bonding changes that are taking place in alloys of varying solute contents. EXPERIMENTAL Details of the design and operation of the liquid metal solution calorimeter used in this work may be found in a paper by Poo1.3 For the present studies copper of 99.999 pct purity was supplied by American Smelting and Refining Co., gold of 99.999 pct purity by A. D. Mackay, Inc., and tin of 99.99 pct purity by Baker Chemical Co. At the commencement of each series of experimental drops, a tin solvent bath consisting of between 70 and 90 g of the pure metal was inserted in the calorimeter. The weight of the bath was accurately determined and to it were added appropriate amounts of gold or copper to give alloys of the desired composition. For determinations of approximately 0.0015 g-atom samples of Cu were used and for measurements of ?HAu approximately 0.0025 g-atom additions of Au. The heat capacity of the bath was determined at regular intervals during a series of drops using tin calibration samples. Measurements were made of the heat of solution of copper in alloys containing a constant 0.01, 0.02, 0.03, and 0.04 mole fraction of Au, respectively, in order to determine ?HCu in each alloy, and the same mole fractions of copper were used to determine equivalent values for nAu at constant copper concentrations. The composition of the bath was maintained at the desired constant gold or copper content by making calculated additions of the appropriate solute throughout the experiments. The limiting values ?HAu in alloys of constant copper content and of %c, in alloys of constant gold content were studied as a function of the mole fraction of copper or gold respectively in order to determine and nCu. Heat content and heat capacity data used in calculating values of ?ºHAu and ?HCu at the experimental temperature of 720°K were obtained from Hultgren et a1.4 ' RESULTS AND DISCUSSION Determinations of ?HAu. The partial heat of solution of gold in pure tin as a function of gold concentration was determined in the previous study of dilute Ag-Au-Sn alloys1 and can be represented by the least-squares expression: ?HAu(l) =-8075 + 2413xAu [l] which is valid between XAu= 0.00 and xAu = 0.05. The standard error in the constant term, which represents the partial heat of solution of gold at infinite dilution in tin,?HºAu(l)is 35 cal per g-atom, while the standard deviation of the slope, which represents n Au is ± 619 cal per- agtom. Corresponding expressions for ?HAu(l) in alloys containing constant mole fractions of 0.01, 0.02, 0.03, and 0.04 copper were obtained from the data listed in Table I and are themselves given in Table II. Fig. 1 illustrates the partial heat of solution of gold as a function of its concentration in each of the alloys. For the four alloys of constant copper concentration, the values obtained for ?HºAU(l) (in order of increasing copper content) are -8141 i 36 cal per g-atom, -8210 ± 42 cal per g-atom, -8202 ± 46 cal per g-atom and -8268 ± 51 cal per g-atom. The corresponding values of the self-interaction coefficient, n Au, for these alloys are 3103 * 644 cal per g-atom, 2425 ± 676 cal per g-atom, 2574 * 717 cal per g-atom and 2523 ± 899 cal per g-atom. In Fig. 2 these values of n Au are plotted as a function of the copper content of the alloys and are seen to remain approximately constant within the experimental limits. The addition of increasing, small amounts of copper to dilute binary Au-Sn alloys thus has no apparent effect on Au-Au interactions in these dilute liquid solutions, although more exothermic values of ?HºAu(l) do result from an increase in the copper content of the alloys. Analogous behavior was observed with additions of silver to dilute Au-Sn alloys.' By

Jan 1, 1970

By R. L. Templin

THE increasing use of aluminum and its alloys in commercial fields has demanded a better understanding of their machining properties. This fact is exemplified by problems that have arisen in the automotive and airplane industries, but many in other fields might be cited. As pure aluminum and its alloys in their various commercial conditions show appreciable differences in their machining properties, it is not surprising that quite divergent solutions have been offered for the machining problems encountered. However, if the fundamental requirements of the most suitable cutting tools for these metals are understood, these machining problems lend themselves more readily to satisfactory solutions. Since the machining of free cutting brass and mild steel is understood by most persons accustomed to working these metals, it may serve our purpose better to first make a general comparison of the tools more commonly used in machining these metals with the tools most suitable for machining aluminum, then proceed to a more specific discussion of the individual stools.

Jan 1, 1927

By B. Ramaswami

INTERNAL oxidation occurs readily in silver due to the rapid diffusion of oxygen in silver.' It has a marked effect on creep in polycrystalline silver2 and raises the critical resolved shear stress in single crystals of silver.3 However, the effect of oxygen on the work-hardening parameters of silver is not known. It is the aim of this paper to describe the effect of internal oxidation on the work-hardening characteristics of single crystals of silver and an Ag-0.1 at. pct A1 alloy. The materials used were: 99.99 pct Ag from Handy and Harman and 99.993+ pct A1 from Alcoa. Single crystals, 6 mm by 6 mm in cross section of silver and Ag-0.1 at. pct A1 of mo.5 orientation, i.e., the orientation with the Schmidt factor m = 0.5. were grown by the Chalmers technique.4 One set of specimens, referred to herein as oxidized specimens, was annealed at 940°C for 24 hr in a muffle furnace, in air, and furnace-cooled to room temperature. Another set of specimens, referred to as nonoxidized specimens, was annealed in oxygen-free helium at 940°C for 24 hr and furnace-cooled over a period of 7 hr to room temperature. The annealed single crystals were tested at room temperature in a floor-model Instron testing machine. The results are presented in Figs. 1 and 2. A

Jan 1, 1965

By O. N. Carlson, D. G. Alexander

THE hardness anisotropy of metals and alloys has been of increasing interest in recent years but silicon ferrite,1 niobium,2 and tungsten3,4 are the only bcc metals about which this type of information has been reported. This investigation was carried out on vanadium and chromium single crystals in an effort to determine to what degree the hardness variations observed in these metals are due to orientation effects and to compare their behavior with other bcc metals. In earlier work the authors had observed a small angular dependence in the Diamond Pyramid Hardness of single crystalline vanadium on the (100) plane but no anisotropic effects were noted on either the (110) or (111) planes. At the suggestion of R. G. wheeler5 it was decided to investigate this effect in greater detail using the more asymmetric Knoop indentor. The vanadium metal used in the study was prepared by the aluminothermic reduction of V2O5 followed by electron beam melting.6 The principal analyzed impurities were 230 ppm C, 230 ppm O, 65 ppm N, 90 pprn Al, Cr not detected, 50 ppm Fe, 60 ppm Ni, and 200 ppm Si. The chromium was an iodide-refined product obtained from the Chromalloy Corporation. Analysis of this material showed the following amounts of impurities present: 10 ppm C, 9 ppm O, 2 ppm N, 0.4 ppm H, 3 ppm Al, 2 ppm Ca, 2 ppm Cu, 20 ppm Fe, 1 ppm Mg, 0.3 ppm Mn, 1 ppm Mo, 3 ppm Ni, 10 ppm Si, and 1 ppm V. Single crystals of both metals about 1 cm in diam and 10 cm in length were grown by an arc-zone melt- ing technique.7 The chromium crystal was annealed at 1600°C for 6 hr in a purified argon atmosphere to remove any strains or inhomogeneities, but the vanadium was tested in the as-grown condition. The crystals were oriented by the Laue back-reflection method and then sectioned with a spark cutter into individual specimens with a (loo), (110), or (111) plane parallel to the crystal surface. They were mounted in Lucite and carefully ground to a flat surface. The vanadium specimens were then electropolished in a 6 pct perchloric acid-methanol mixture while the chromium specimens were mechanically polished on a Syntron vibratory polisher using an alumina abrasive. The orientation of each crystal was then rechecked by the back-reflection X-ray method. All of them were found to lie within 2 deg of the desired orientation with the exception of the (110)-Oriented chromium crystal which was within 4 deg. Microhardness impressions were taken at 10 deg intervals from the common (110) direction by rotating the crystal in the plane of the crystal surface. A Knoop indentor was used with a 400-g load on the vanadium crystals and an 800-g load on the chromium. The hardness values are averages of 6 impressions and standard deviations were calculated for each set of data. The values reported for the (111) plane of vanadium are based on from 10 to 15 measurements for each point. The microhardness results for vanadium and chromium are plotted as a function of the angular rotation of the long axis of a Knoop indentor from the (110)

Jan 1, 1970