THE following Officers, Directors, and guests were present: Herbert Hoover, A. R. Ledoux, Henry S. Drinker, Edwin Ludlow, Samuel A. Taylor, Charles F: Rand, William M. Corse, Arthur S.. Dwight, Glen H. Clevenger, L. W. Francis, F. G. Cottrell, Bradley Stoughton, Percy E. Barbour, E. P. Mathewson, Dorsey A. Lyon, Archibald Douglas, A. D. Flinn, RobertLinton, James F. Kemp, William Y. Westervelt, J. W. Richards, W. L. Saunders, George Otis Smith, Thomas T. Read, J..C. Murray, Ralph Arnold. A Committee on Mine Equipment was appointed composed as follows: Graham Bright, chairman, William Kelly, Howard N. Eavenson, R. E. Hobart, and S. P. Rumsey. B. D. Saklatwalla was added to the Committee on Miscellaneous Metals and W. Spencer Hutchinson was added to the Committee on Mining Geology. A revised budget for 1921 was approved. A petition duly signed to amend Section 1., of Article III of the Constitution, increasing the initiation fees from ten dollars to twenty dollars, was approved by the Board.

Jan 1, 1920

By H. R. Cooper, T. S. Mika

T. S. Mika (Department of Mineral Technology, University of California, Berkeley, Calif.) - Dr. Cooper's attempt to establish a correlation between process behavior and operational variables on the basis of a statistical analysis after imposing a reasonable process model is a very commendable improvement on the use of standard regression techniques. However, it must be recognized that the imposition of a model has the potential of yielding a poorer representation if its basic assumptions or mathematical formulation are invalid. It appears that at least two aspects of his treatment require some comment. First, the limitations on the kinetic law where xta represents a hypothetical terminal floatable solids concentration (cf. Bushell1), should be mentioned. Most current investigations2-9 appear to utilize the concept of a distribution of rate constants rather than a single unique value, k, to describe flotation kinetics. A distributed rate constant is certainly a more physically meaningful concept than that of a terminal concentration. The study of Jowett and safvi10 strongly indicates that xta is merely an empirical parameter, whose actual behavior does not correspond to that expected from a true terminal concentration. Rather than being a strictly mineralogical variable, as Dr. Cooper's treatment implies, it apparently represents the hydromechanical nature of the test cell as well as the flotation chemistry. The extension of batch cell kinetic results to full-scale continuous cell operation is a suspect procedure if the effect of such nonmineralogical influences on x,, remain unevaluated. There is evidence that introduction of a terminal concentration is necessitated by the inherent errors which arise in batch testing and are eliminated by continuous testing methods.' Possible lack of validity of the author's use of Eq. 1 is indicated by two unexpected results of the statistical analysis of his batch data. The first is the apparent corroboration of the assumption that the rate constant, k, is independent of particle size, i.e., of changes in the size distribution of floatable material. This assumption directly contradicts numerous results 2,4,11-l8 for cases where first order kinetics prevailed and ignores the phenomenological basis for the analysis of flotation in terms of a distribution of k's. It must be recognized that, if the rate constant is size dependent, the lumped over-all k would be time dependent; Eq. 1 would then no longer be valid. Cooper's x,, is determined by batch flotation of a distribution of sizes for an arbitrary period of time. If the size dependence of k is artificially suppressed, x,, will become a function of the experimental flotation time used in its determination. Upon reviewing the rather extensive literature concerning batch flotation kinetics, there appear to be few instances where constant k and x,, adequately adsorb variations in floatability due to particle size. The second surprising result is the low values of the distribution modulus, n, determined. Contrary to Cooper's assertion, most batch grinding (ball or rod mill) products yield values of n > 0.6, which increase as the material becomes harder.'' It is likely that the values of n = 0.25 and n = 0.42 for Trials 1 and 2, respectively, are completely unreasonable, and even the value n = 0.54 obtained for Trial 3 is unexpectedly low. Possibly, this indicates inherent flaws in the three trial models considered, in particular the assumed particle size independence of the rate constant, k. The above does not necessitate that Eq. 1 (and the terminal concentration concept) is invalid; it could constitute a good first approximation. However, the qualitative arguments used by Dr. Cooper in its justification are somewhat frail and require verification, particularly since much of the flotation kinetics literature is in opposition. Apparently, no effort was made to test these hypotheses on the actual data; in fact, since they pertain to a single batch test time, his data cannot be utilized to evaluate the kinetics of flotation. To evolve a control algorithm on the basis of this infirm foundation seems a questionable procedure. Another difficulty in his analysis arises in consideration of the froth concentrating process. As Bushel1 ' notes, for Eq. 1 to be valid it is necessary that the rate of recycle from the froth be directly proportional (independent of particle size) to the rate of flotation transport from the pulp to the froth, a restrictive condition." Harris suggests that it is more realistic to assume that depletion occurs in proportion to the amount of floatable material in the pertinent froth phase volume (treating that volume as perfectly mixed).12,21,22 The physical implications of

Jan 1, 1968

By W. L. Staker

The Bureau of Mines investigated selective extraction of Au and Ag from a low-grade Au ore containing Hg. Gold and silver were extracted from the ore in cyanide slurries, and Hg extraction was suppressed with sodium or calcium sulfide. Maximum Au extraction and minimum Hg extraction were obtained using solutions containing 0.34 lb NaCN/ton of solution. Increasing the cyanide concentration increased Hg extraction without increasing Au extraction. Mercury extraction from the ore was suppressed with 0.5 to 2.9 lb CaS/lb Hg in the ore. Gold-to-mercury ratios of 100:l to 400:l were obtained in the leach solution, and on the activated carbon in a CIP circuit.

Jan 1, 1984

Jan 1, 1885

By F. Claisse, R. Angers

Self-diffusion in iron has been measured during rapid a-r transformations using a variant of the Kryukou and Zhukhovitskii diffusion method. The study was performed by thermally cycling iron foils (1 to 6 cpm) through the transformation (=910°C). Some foils have been subjected to over 1000 cycles and some have spent more than 15 pct of their total diffusion time in the process of transformation. The experimental results show that the a-r transformation has no measurable effect on self-diffusion in iron. The study is completed by a quantitative analysis of mechanisms which can affect the diffusion rate during the transformation. The analysis confirms the experimental results. SINCE diffusion is an important factor in many solid-state transformations, it is of interest to study how it is affected by the stresses generated during these transformations. Clinard and Sherby1'2 were the first to make a study along these lines. They measured diffusion coefficients in Fe-FeCoV couples subjected to slow thermal cycling (1.5 cph) through the a-r transformation range. They found an enhancement of diffusion by a factor of about two. The purpose of the present paper is to report measurements of the self-diffusion coefficient of iron during much more rapid thermal cyclings (1 to 6 cpm) through the a-r transformation (-910°C). These more rapid cyclings produce higher strain rates during the transformation and should emphasize any possible influence of transformation upon diffusion. EXPERIMENTAL Iron foils, 25 to 35 µ thick, were cold-rolled from 99.92 pct pure iron and annealed in pure helium for 2 hr at 870°C; the resulting grain diameter was about 150 µ. Specimens 0.5 by 8 cm were cut from the foils and I7e55 was vapor deposited on one of their surfaces. A 38 gage alumel-chrome1 thermocouple was spot welded in the middle of one of the specimen long edges, Fig. 1. Two 38 gage chrome1 wires were also spot welded along the same edge on each side of the thermocouple; they were placed 2.5 cm apart and used for electrical resistance measurements. In order to prevent twisting and crumpling, the specimens were pinched between two quartz plates 0.1 by 1 by 7 cm and the assembly was close fitted into a 1 cm ID quartz tube. Four holes were drilled through the tube to let the 38 gage wires out: these were connected to the recording equipment by means of extension wires. 20-gage nickel wires fixed at both ends of the specimens were used to thermally cycle the foils by Joule heating. The above described device was placed in a 2.7 cm ID quartz tube which in turn was placed in a tubular furnace. Either a pure helium atmosphere or circulating hydrogen was used during the experiments. Specimens were subjected to thermal cycles between a minimum temperature To and a maximum temperature Tm at rates ranging from 1 to 6 cpm. This was obtained by maintaining the furnace at a constant temperature near the minimum temperature To and periodically passing an electric current through the specimen. Cooling was achieved by heat losses to the surroundings. The forms and periods of cycles were varied from one specimen to another; however, each specimen was subjected to one type of cycle only. The temperature and electrical resistance variations of the specimens were recorded as a function of time. The temperature curves were used for diffusion calculations while the electrical resistance curves were used to monitor the transformation and to determine its starting point and its approximate duration. Diffusion was measured by the method developed by Kryukov and zhukhovitskii3 and modified by Angers and Claisse.4,5 In this method a metallic foil is coated on one side with a radioactive isotope and the activity is measured periodically on both sides during the diffusion anneal. The following equation then holds: where: I1 Activity on the surface on which the deposit is made. I, Activity on the opposite surface. t Diffusion time. B Constant. D Diffusion coefficient. d Foil thickness including the deposit. G(t) A function of time; it is a second order correction term which is given graphically in Refs. 4 and 5. The diffusion coefficient D is found by plotting ln[(Il - I2)/(I1 + I,)] -G(t) against t; the resulting slope m leads to an accurate calculation of D through Eq. [2]. The effect of the a-r transformation on diffusion is expressed by the ratio DT/DU where:

Jan 1, 1970

By J. R. Cahoon, W. V. Youdelis

FOR the diffusion of copper in silver-rich alloys, there have been only two previous investigations, that of Seith and Peretti in 1936, and that of Sawatzky and Jaumot2 in 1957. Seith and Peretti obtained a value of 24.8 keal per g-atom for the activation energy of diffusion whereas Sawatzky and Jaumot obtained a value of 46.1 keal per g-atom. Admittedly, Seith and Peretti used relatively high concentrations of 2 at. pet Cu and polycrystalline diffusion couples, while Sawatzky and Jaumot investigated tracer diffusion in single crystals of silver. The difference in the results, however, seems too large to attribute solely to solute concentration, as a change of over 20 keal per g-atom in the activation energy suggests a change in the mechanism of diffusion. Therefore, in the present investigation the diffusion coefficient for copper in polycrystalline Ag-2 at, pet Cu alloy is re-established using conventional sandwich-type diffusion couples and electron-probe microanalyses, and the results are compared with those of the previous studies. The diffusion couples were prepared from high-purity silver (99.999 pet) and high-purity copper (99.999 pet). The silver disks, 1/4 in. long and 4 in. in diam, were machined from an ingot which had been solidified in a dynamic vacuum of 10-3 mm of Hg to eliminate oxygen absorption which otherwise would result in copper oxide precipitation in the weld zone. The alloy disks of similar dimensions were machined from an alloy ingot (nominal composition 2 at. pet Cu) which had been unidirectionally solidified to obtain a predictable solute concentration,3 and homogenized for 1 week at 800°C. Sandwich diffusion couples were made by pressure welding an alloy disk between two silver disks in an induction heating coil. The couples were diffusion-annealed at temperatures of 800°, 756°, 699°, and 630°C in tube furnaces in which the temperature was controlled to better than ± l°C. The diffusion couples were examined metallographically for weld defects, and couples showing even minute defects at the weld interfaces were rejected. Concentration penetration curves were established using an A.R.L. Microprobe analyzer. CuKO radiation was counted and converted to concentration using 0.5 and 1.0 wt pet Cu chemically analyzed standards. Initially, four continuous profiles were obtained, and averaged to obtain the final diffusion curve. The initial analysis was performed commercially and the welds were not located with respect to the profile. Therefore, the results were rechecked by the authors using the Mellon Institute A.R.L. probe. In the latter case, concentrations were obtained at 10-µ steps for four different traverses, and then averaged to obtain

Jan 1, 1968

By H. E. Cline, T. H. Alden

A study zvas made of rate-sensitive plastic deformation and superplasticity in alloys of lead and tin. These alloys (lead, PO-19 pct Sn, Sn-38 pct Pb, Sn-2 pct Pb, tin) were extruded, aged at room temperature, or melted and resolidified to produce a variety of ~nicrostrnctures. Flow stress us strain rate data were obtained frorn tension tests for strain rates between 10-6 and 1 min-1. The curve log o .us log £ was S-shaped jor fine-grained materials and approxinzately linear for coarse-grained nzaterials. At constant grain size, the behavior was relatively insensitive to conposition. High rate sensitivity (d log o/d log k) and superplasticity occurred at intermediate strain rates in fine-grained materials and are believed to be associated with a transition with strain rate in the mode of plastic flow. This transition was shifted to higher strain rates with increasing temperataire or decrensing grain size. The high rate rneclzanisrn is presunzed to be slip, while rnetallographic evidence sug-gests that the low rate lnechanism is pain boundary sliding. PEARSON' discovered that extruded eutectic alloys of Pb-Sn and Bi-Sn could be elongated as much as 2000 pct in tension. The ability for stretching decreased with aging time or annealing to increase the grain size. At high strain rates, or if the material was in the cast condition, normal ductility was observed. Following deformation of the extruded Pb-Sn eutectic at low rates, Pearson observed an equiaxed granular structure on an initially flat surface, while rapid straining produced elongated grains. He attributed the large deformation in the extruded alloys to the persistence of extremely small grains to a temperature sufficiently high for inter granular flow. Avery and backofen2 measured the strain rate sensitivity of the flow stress, m = d In old In 6, in the Pb-Sn eutectic and established a correlation between m and the tensile elongation. In the extruded eutectic alloy the strain rate sensitivity was 0.1 to 0.2 at rapid rates and the elongation was small, while at low rates m increased to 0.4 to 0.6 and superplastic elongation was observed. They also noted a grain size effect. In the case of the cast Pb-Sn eutectic the strain rate sensitivity remained at 0.1 over the range of strain rates of their experiment (3 x 10"3 to 2 min-I). These authors suggested that diffusional (Nabarro-Herring) creep was the mechanism by which deformation occurred at low strain rates, while climb-controlled creep occurred at high rates. Two predictions of this model are that, at low strain rates, the strain rate sensitivity approaches 1, i.e., Newtonian viscosity, and that the strain rate at constant stress varies as D/L2, where D is the coefficient of self-diffusion and L the grain size. More recently, a mechanical and microstructural investigation of the dilute superplastic alloy, Sn-5 pct Bi, has been done.3 The results show that the high strain rate sensitivity is associated with a transition with strain rate of the mechanism of plastic flow. At low strain rates, grain boundary sliding and its associated accommodation processes were evident, while at high strain rates quasi-uniform slip was concluded to be the dominant deformation process. The following experiments were performed to extend our knowledge of the phenomena of superplasticity to a larger range of strain rates, compositions, temperatures, and microstructures in the Pb-Sn alloy system. The question of why a cast structure does not exhibit viscous behavior although it appears to have a fine microstructure2 was investigated.

Jan 1, 1968

By O. Mellgren, A. M. Gaudin, P. L. De Bruyn

In the January 1956 issue: TP 4137B. Adsorption of Ethyl Xanthate on Pyrite. By A. M. Gaudin, P. L. de Bruyn, and Olav Mellgren. P. 65. Since P. L. de Bruyn is now a member of the AIME, the word "associate" should be removed in describing his status. The address of the third author, Olav Mellgren, should read: 74-2 Chingola, N. Rhodesia. P. 68, second paragraph, last line: the word "300-fold" should be replaced by "3000-fold." Also in the January 1956 issue: TP 4158B. Energy Transfer by Impact. By R. J. Charles and P. L. de Bruyn. The authors wish to express their disapproval of the omission of the abstract from the article, since they believe that an abstract fulfills a very important function in every paper.

Jan 1, 1957

By D. E. Trout, W. R. Hibbard

Previous investigations have shown that the cold rolling textures1n2 and the drawn wire textures3 of copper change their secondary components after the addition of about 1 pct aluminum and 5 pct zinc, but do not change after the addition of as much as 30 pct nickel. However, few data are available on compression textures. Barrett4 reports from unpublished work with E. L. Layland that compression rolled copper develops a texture which is predominately (110) in the compression plane with a secondary spread to (113) and weaker spread to (100) as shown in Fig 1. However, 70-30 alpha brass similarly treated develops a texture again predominately (110) in the compression plane and with a weak secondary spread to {113} but with moderate (111) secondary intensities illustrated in Fig 2. Experimental Procedure Specimens of the compositions shown in Table 1 remaining from a previous investigation3 were annealed to a grain size of 0.090 mm average diam and machined to cylinders 0.20 in. diam and 0.20 in. high. Cylinders were compressed 90 pct reduction in height between lubricated steel blocks in a tensile machine. Glancing X ray photo-grams using copper K-alpha radiation were taken at an angle of 0 degrees to the compression surface. (111), (002) and (220) rings were analyzed to define the textures shown in Table 1. The results are in agreement with Barrett4 as to types of textures and are essentially in agreement with previous work1,2,3 as to the effects of composition. In the wire study3 it was reported that the 4.99 pct zinc alloy had a brass-type texture, while the data in Table 1 indicate a copper-type texture for compression. The wire specimen of the 4.99 pct zinc alloy was re-examined by X rays and it was established that the [loo] component still exists in the wire axis. Therefore, Table 2 of Ref. 3 is in error and should indicate a double [ill], [loo] copper-type texture for this alloy. This correction results in complete consistency with regard to compositional effects, namely that copper and its alloys containing up to approximately 1 pet aluminum, 5 pct zinc and at least 30 pct nickels develop a copper-type texture and more concentrated copper-aluminum and copper-zinc solid solution alloys will form a brass-type texture. Summary Compression textures developed in copper and its alpha solid solution alloys of aluminum, nickel and zinc are essentially the same types as those re- ported by Barrett4 with compositional effects occurring at approximately the same percent additions as previously reported for rolled sheet182 and drawn wire.3 The Scovill Manufacturing Co., Waterbury, Conn., furnished the copper and brass alloys, performed certain chemical analyses and supplied laboratory facilities where needed. References 1. Brick, Martin and Angier: Tram. A.S.M. (1943) 31, 675. 2. Dahl and Pawlek: Zlsch. Melall. (1936) 28, 266. 3. Hibbard and Yen: Trans. AIME 175, 126. Melals Tech.. Feb. 1948, TP 2334. 4. Barrett: Structure of Metals, mc- Graw-Hill (19421, 386.

Jan 1, 1950

The October meeting of the Mining and Geological Society, Lehigh University, was held in the Eckley B. Coxe Mining Laboratory, and was called to order at 8:15 p. m., by President R. L. McCann. After the reading of the minutes of the previous meeting, a short business session was held, for the purpose of electing a Vice-President to succeed G. S. Borden, who has left college. Nominees for the office were: H. J. Sloman, P. S. Justice, L. Sargeant. Dr. F. F. Hintze, of the Geology Department, was elected a member of the Advisory Committee, which now consists of the President-

Jan 12, 1916

By C. Laird, C. E. Feltner

An investigation into the effect of a material's slip character on its high strain fatigue properties has been carried out using copper and Cu-7.5 wt pct A1 as representative wavy and planar slip mode materials, respectively. In copper, the constant term and exponent in the Coffin-Manson equation, ?EpNf1/2 = const, are unaffected by the temperature of testing or the history of the metal. On the other hand, in Cu-7.5 wl pcl Al, while the exponent is invariant, the constant is increased with respect to copper and increased further with decrease in temperature. The life in Cu-7.5 wt pct A1 is double that of copper at room temperature and about four times at 78°K. Fractoflaphic studies indicate that these diffevences in life are associated with the early stages of cracking. In copper, severe surface rumpling provides crack nuclei at pain boundaries independent of' testing temperature or the history of the metal. In Cu-7.5 wt pct Al, the planar slip mode of deformation prevents grain boundary folding; crack nucleation is therefore mainly transgranular and the increase in life with respect to copper is associated with a prolonged linking-up stage of such transgranulay cracks. At the lower temperature the increased difficulty of cross slip inhibits multiplication of trans-granular cracks and retards the linking-up process, giving a further enhaancement in life. It is expected that such behavior will be found general in materials of wavy and planar slip mode, respectively. STAGE II crack propagation in high strain fatigue takes place by a repetitive process of crack tip blunting in the tension part of a fatigue cycle followed by resharpening of the crack in the compression part.1-3 This mechanism has come to be called the "plastic relaxation process".3 At very high strains (lives to failure less than 103 cycles), most of the life of a specimen is spent in crack propagation by the plastic relaxation process.4,5 Since the differences in the cyclic strain hardening behavior of metals and alloys are comparatively small in this strain range,6,7 the amount of blunting at a crack tip depends primarily on the applied strain amplitude. The rate of crack propagation in this life range is therefore nearly constant with respect to material and temperature of testing. In the longer life portion of the high strain fatigue range (l03 to 103 cycles to failure), a considerable fraction of the lives is spent in crack initiation and Stage I growth. Grain boundaries have frequently4,5,8 been found to be the sites for this growth which is also associated with a surface folding process.4'5 Such folding behavior may also be general in any material having a grain structure and capable of plastic deformation. It has therefore been suggested475 that the universality of the Coff in-Manson law,9'10 constant,* where ?Ep is the plastic strain range and Nf the number of cycles to failure, is reflected in the approximate invariance of both the crack initiation and propagation behavior. It happens that, in most investigations of the phenomena associated with failure,4,5,8 materials with a wavy slip mode have been used as vehicles for the studies, or else "normally" planar slip mode materials have been tested under conditions giving rise to wavy glide deformation, e.g., stainless steels cycled at high temperature.'' The purpose of the present investigation was to determine whether or not different cracking phenomena would occur when the slip mode of a material is planar and if the associated life to failure would be different than that of a wavy slip

Jan 1, 1968

By S. F. Willey

Difficulties encountered in justifying replacements for overage mobile mine equipment at the Gay mine are common to most mining operations. More critical management reviews, resulting from ever rising capital expenses, increased such difficulties. These increased difficulties are especially apparent to those who are primarily operators and are not statisticians, mathematicians or computer men. The Gay mine is located 17 mi east of the town of Fort Hall in southern Idaho. This open pit operation annually supplies the J. R. Simplot Co. and the FMC Corp. with 1.5-2.0 million tons of phosphate ore. Stripping ratios average approximately three bank cubic yards of waste per ton of ore mined. The mobile mine equipment fleet consists of ten 24-cu yd scrapers; twenty-one 30-50-ton end-dump trucks; four 3%-4%- cu yd shovels; fifteen dozers in the D-8 and D-9 classes; and three road patrols. Equipment replacement is based on the results of evaluations made on individual units.

Jan 9, 1972

By R. E. Ogilvie, N. L. Peterson

DURING the past few years there has been considerable effort devoted to the understanding of radiation effects on materials. The concept of the Frenkel defect and other lattice defects suggests that radiation may alter the rate of many metallurgical phenomena, especially those which are diffusion controlled. In 1953 R. R. Coltman and T. H. ~lewitt' found an appreciable effect on the ordering rate of Cu,Au due to fast neutron bombardment. Since then several rather comprehensive theories have been proposed on radiation enhanced diffusion in solids.2"4 If the energy of the radiation is above the threshold energy for the removal of atoms from their lattice sites, Frenkel defects will be produced. These defects can be produced uniformly throughout a relatively thick specimen by high-energy X-rays permitting bulk property studies without the limitation of sample dimensions. In this work high-purity arsenic containing 30 ppm of impurities was allowed to diffuse from the gase- ous phase at 700°C into single crystals of p-type germanium containing 0.1 ppm of indium. As the arsenic diffuses into the P-type germanium, an n-type layer will form in the diffusion zone. At the p-n junction the concentration ratio of the arsenic to the indium is constant. Experimental Procedures—The germanium specimens, 10 mm by 10 mm by 5 mm, were polished and etched to a mirror finish. The specimens were then sealed off in a vycor glass capsule at 3 x 10"5 mm Hg pressure with a sufficient amount of arsenic powder to produce a one-half atm pressure of arsenic at 700°C. Specimens were annealed at 700°C without radiation. The diffusion coefficient determined from these samples agrees within 8 pct of previous work done by Fuller.' Three specimens were given diffusion anneals at 700°C in a small tube furnace centered beneath the target of a 2-mev Van de Graaff generator. The specimens when in the furnace were 10 cm directly below the target of the generator. These specimens were irradiated continuously during the diffusion run with the Van de Graaff operating at 2 mev with a tube current of 225 to 250 pamp. The intensity of the x-radiation at the surface of the specimen inside the furnace was approximately 4.5 x l05 roentgens per hr. The temperature was controlled within m2°C by a chromel-alumel thermocouple throughout this work with no observed temperature change due to the radiation. By careful lapping, the samples were polished at an angle of 5 deg to the diffusion zone, giving a XI0 increase in the visible diffusion zone. The location

Jan 1, 1960

By D. S. Tomalin, D. F. Stein

The effect of reducing oxygen to low concentrations on the fracture of high-purity iron single crystals has been examined at 78° and 20°K. It is found that iron single crystals grown by the strain-anneal method usually contain a few occluded grain boundaries which may become embittled in the presence of oxygen, thereby nucleating cleavage fractures. High purity with respect to interstitial elements was found to inhibit twinning and evidence is presented for an orientation dependence of the resolved yield stress. Deformation occurred by slip rather than twinning at both temperatures of testing with elongations of as much as 9 pct at 20°K. THE fracture properties of iron single crystals have been observedl-3 to be a function of temperature, orientation, and purity. Allen, Hopkins, and McLennan1 demonstrated that at 78°K iron single crystals became increasingly brittle as the tensile axis approached the (001) pole of the stereographic unit triangle. Iron crystals with the tension axis near a (001) pole were completely brittle and orientations near the (011)-(111) boundary were very ductile, achieving a 100 pct reduction in area prior to fracture. Later work of Biggs and pratt2 and of Edmondson3 demonstrated that by reducing the carbon content of the single crystals the transition between brittle and ductile failure at 78°K could be shifted to orientations nearer the (001) pole. Ed-mondson went further and pointed out that any mechanism which tended to increase the yield strength of the iron (i.e., carbon addition, pre-strain) also increased the tendency for brittle behavior at 78°K. Thus by a reduction of carbon content Biggs and Pratt were able to obtain ductile behavior to within 20 deg of the (001) pole, and Ed-mondson was able to obtain ductile behavior to within 26 deg of the (001) pole. Edmondson's material had a total interstitial content (carbon, oxygen, and nitrogen) of approximately 60 ppm and, although Biggs and Pratt reported no analysis, indications were that their iron contained comparable impurities. Stein, Low, and seybolt4 purified iron single crystals to a total carbon, oxygen, and nitrogen content of approximately 20 ppm. They observed a lowering of the yield stress with this increased purity, and thus one might have expected an observation of increased ductility. Although they tested specimens of orientations which the previous workers had indicated should be ductile, the crystals failed at a 78°K in a brittle manner with little elongation. Stein noted,' however, that about 90 pet of the failures could be traced in origin to occluded grains. Allen et al.1 and Edmondson3 do not report examination of their cleavage surfaces, but Biggs and pratt2 reported that microscopic examination of the cleavage surfaces of many of their specimens revealed the presence of small occluded grains. Honda and cohen6 and Keh7 have also observed the initiation of fracture at occluded grains in iron single crystals. Therefore, the additional complication of occluded grains must be considered in studying the properties of iron single crystals and the origin of fractures determined if the ductility exhibited by the crystals is to be considered meaningful. Various investigators8-12 have studied the effects of impurities on grain boundaries in high-purity polycrystalline iron. Rees and Hopkins10 showed that the addition of oxygen to low-carbon (0.002 pet) iron weakened the grain boundaries, causing a shift from transcrystalline to intercrystalline fracture and a progressive decrease on the brittle-fracture stress with increasing oxygen content. In addition, it has been shown by Low and Feustel11 that the addition of carbon to polycrystalline iron containing oxygen eliminated grain boundary brittleness. Thus, oxygen can embrittle grain boundaries in high-purity polycrystalline iron, but the addition of an appropriate amount of carbon can eliminate the oxygen-induced brittleness. The oxygen content (19 ppm) of the iron "single crystals" employed by Stein el al. was large enough to suspect impurity effects at the occluded grain boundaries. Allen et al.1 Biggs and pratt,2 and Edmondson3 may have masked any occluded grain problem in their specimens considering the relatively high carbon levels they employed. stein13 demonstrated that the addition of as little as 0.9 ppm C to previously purified (less than 5 x 10-3 ppm C) "single crystals" would increase the elongation from a few percent to more than 20 pet at 78°K and the fracture was not associated with grade boundary initiation.

Jan 1, 1965

By P. T. Carter, A. B. Murad, H. B. Bell

The distribution of manganese and oxygen between molten iron and FeO-MnO-SiO2 slags not saturated with SiO2 has been determined and used to calculate activities of MnO and SiO2 in MnO-SiO2 slags. These were found to be intermediate between the corresponding activities in FeO-SiO2 and CaO-SiO2 slags. THE equilibrium constant for the reaction between molten iron containing manganese and slags containing FeO and MnO, namely: FeO(slag) + Mn = MnO (slag) + Fe(1iquid) is most conveniently represented by: (MnO) Kmn== (FeOHMn] [Fe] is omitted, since for dilute solutions of manganese in iron, afe is approximately constant. When activities are used for (MnO), (FeO) and [Mn], Kmn is a true equilibrium constant and will apply to all types of slags, but when weight percentages are used, the values obtained for Kmn for different slags vary considerably. The equilibrium between iron containing manganese and relatively pure FeO-MnO slags has been investigated by several workers;1-4 the most recent investigation reported is that of Chipman, Gero, and Winkler.4 Their results, corresponding to slags containing up to 4 pct SiO2, were represented by the equation: 6440 log KMn = +2.95 In this case both slag and metal may be assumed to be ideal solutions, therefore the values of Kmn so derived represent the true constant for the manganese reaction. As the molecular weights of MnO and FeO are almost equal, weight concentration of these oxides may also be used in the above expression. Acidic oxides such as SiO2 and P2O5 affect the activities of FeO and MnO differently, so that when total concentrations by weight of FeO and MnO are used in the above expression for Kmn the values obtained are no longer constant. These will be denoted by K'mn. Körber and Oelsen5 investigated the manganese reaction using silica-saturated iron-manganese-silicate slags and found: 7940 logK'mn =3.172 This corresponds to Kmn values much higher than those obtained for pure oxide slags. The results of Körber and Oelsen, and Chipman, Gero, and Winkler are summarized in Table I. In the present investigation it was decided to study the manganese reaction using iron-manganese-silicate slags not saturated with silica, and which fell mainly between the orthosilicate join 2FeO . SiO2 - 2MnO.SiO2 and the FeO-MnO side of the ternary system FeO-MnO-SiO2. It has been shown" that the phases present in solidified slags of this part of the diagram are (FeO, MnO) and (2Fe0.Si02, 2Mn0-SiO,) solid solutions. Such an investigation would be of interest in deoxidation and also gives information on activities in liquid slags. This equilibrium has not as yet been investigated successfully. Hilty and Crafts7 attempted to examine this reaction in a rotating crucible furnace, but were unable to obtain suitable slag samples. In the present investigation one series of experiments was carried out in a rotating crucible furnace, because the success of Taylor and Chipman8 with such a furnace in their study of oxygen distribution between molten iron and (CaO, MgO) — FeO-Si0, slags suggested that it would minimize contamination of the slag by the crucible material. A second series was carried out using a wire-wound resistance furnace. Rotating Crucible Furnace Experiments In all cases the metallic charge consisted of 800 to 1000 g Armco iron containing 0.02 pct C, 0.03 pct Mn, and traces of Si. Manganese and silicon additions consisted of electrolytic manganese (99.9 pct)

Jan 1, 1953

By S. D. Strauss

The marketing of nonferrous metals and of the ores and concentrates from which these metals are recovered is a fascinating trade, international in character, sensitive to every change in the economic tide, and complex in its organization. Each individual metal has its own marketing mechanism; no two are exactly alike. The differences sometimes are a matter of tradition rather than of necessity, but usually they have developed because of the very nature of the problems of producing or consuming the individual metal. This description, because of limitations of space, can do no more than indicate the major aspects of the trade and touch lightly on the marketing structure of each metal. The dictionary states that a market is a "meeting of people for selling and buying." In the case of nonferrous metals this meeting may occur on a half-dozen different occasions between the time the ore has been first mined and the time the refined metal is available for use by industry; or it may not occur at all until after the metal itself has been rolled, drawn, stamped, cast, or forged into a useful semifabricated shape. To illustrate: A Chilean miner may sell his small ore production to a custom mill, which produces concentrates that are sold to an ore dealer, who finances shipments of the concentrate to a custom smelter, which buys them for conversion into blister, to be subsequently refined into electrolytic copper (sometimes by a refinery having no corporate ties with the custom smelter) and sold. Conversely, aluminum production is mostly by integrated concerns that mine bauxite, convert it to alumina, smelt that to produce aluminum, and then fabricate that into semifinished or even finished products before title to the material changes hands for the first time. Some nonferrous ores are not converted into metal at all but are sold by the miners or dealers directly to the ultimate consumers. A good example would be chrome ores used by the chemical industry. And of course a substantial part of the commerce in nonferrous metals is in scrap, which is the reconversion into useful form of metals that have long since been mined and smelted. Thus, one-third of all the lead used in the United

Jan 1, 1964

By Arnulf Muan, Klaus Schwerdtfeger

Equilibrium ratios C02/C0 of a gas phase coexisting with selected phase assemblages of the system Fe-Mn-0 have been determined in the temperature range 1000" to 1300°C. The oxygen pressure for the "hfnO" +hfn30, equilibrium and for the "(Fe,hTn)O" + (Fe,Mnh 0* equilibrium at high manganese contents has been determined by electromotive force measurements using stabilized zirconia as a solid electrolyte. The notstoichometry 01' "hTnO" and of "(Fe, iM1z)O" solid solutions has been determined by ther-mog-/avi?netry and by wet-chemical analysis. The data obtained are used to derive activity-composition relations in "(Fe,hfn)O" and (Fe,Mn),O4 solid solutions. WUSTITE "FeO" and manganosite "MnO" form a continuous series of solid solution at high temperatures,' and so do magnetite Fe304 and the high-temperature, cubic modification of Mn304 (Ref. 2) (high hausmannite, -1170). The oxides "FeO" and "MnO" are cation-deficient phases.495 The nonstoi-chiometry of "(Fe,Mn)O" solid solutions has been studied by Engell and ~ohl' at two selected C02/C0 ratios at 1250°C. The two oxide end members of the spinel solid solution, FesO4 and Mn,04, however, are known to be close to stoichiometric under the experimental conditions used in the present investigation.''' The oxygen pressures of "(Fe,Mn)07' solid solutions in equilibrium with iron have been determined by Schenck and coworkers,8 by Foster and welch," and by ~n~e1l.l' The two former groups equilibrated the condensed phases in C02-CO atmospheres of lmown compositions, whereas Engell" used a galvanic cell with stabilized zirconia as a solid electrolyte. The results of these investigators are not in good agreement. Activities of FeO in manganowiistite as calculated from the results of Foster and Welch show ideal behavior, those of Engell yield a pronounced positive deviation, and those of Schenck et 01. show a moderate positive deviation from ideality. In the present work oxygen pressures for the iron + manganowiistite and manganowustite + spinel equilibria and the nonstoichiometry of manganowiistites have been measured. The data were used to calculate activities in the manganowiistite and spinel solid solutions. EXPERIMENTAL METHODS The COz/CO ratios at which manganowustite and iron are in equilibrium were determined by thermo-gravimetric and quenching methods. Experimental details are described in a previous publication.'2 In the thermogravimetric technique, incipient reduction of manganowiistite pellets to metallic iron was observed as a break in the weight vs log COZ/CO curve. In the quenching technique, manganowiistite samples were partially reduced to metallic iron, or the metallic iron of manganowustite + metallic iron mixtures was partially oxidized to manganowustite, in atmospheres of constant C02/CO ratios. After quenching the composition of the oxide phase was determined by X-ray lattice parameter measurements and comparison with a standard curve obtained from oxide solid solutions of known compositions. The nonstoichiometry of "MnO" and "(Fe,Mn)07' solid solutions was determined by chemical analysis of samples equilibrated in C02-CO atmospheres and quenched to room temperature, as well as thermo-gravimetrically by reducing (Fe,Mn),04 or Mn304 to manganowiistite or manganosite. The equilibrium between manganowiistite and (Fe,Mn),04 was measured thermogravimetrically by reducing (Fe,Mn),04 solid solutions having composition in the range of %„ l(NFe +NM) from 0 to 0.63. No experiments could be performed with this technique at higher manganese contents, because the equilibrium C02/C0 ratios are too large for accurate control. An additional difficulty arises at the higher manganese contents due to the strong increase in oxygen content of the manganowustite phase with increasing log Py near the manganowiistite-spinel boundary. Consequently a sharp break in the weight loss vs log C02/CO curve cannot be observed at the phase boundary. At high manganese contents of the manganowiistite, e.g., (NMn/(NF~ + NMn) > 0.9, electromotive force measurements with stabilized zirconia as a solid electrolyte were made to determine the equilibrium oxygen partial pressure. Experimental details are described in a previous paper.* Mixtures of "(Fe,Mn)O" and (Fe,Mn),04 were pressed to pellets, and the oxygen pressure of the equilibrated samples was compared to that of Ni + NiO mixtures in the cell The composition of the manganowiistite in the equilibrated two-phase mixture was determined by lattice parameter measurements and comparison with known standards. The oxygen pressure for the Ni + NiO equilibrium was taken from available data.l3~l4 No reliable results were obtained with the electromotive force technique on iron-rich oxides. The electromotive force drifted strongly with time in this composition range. An additional difficulty arises from the partial de-

Jan 1, 1968

By William E. Ford, Edward Salisbury Dana

The monoclinic Wolframite Group and the tetragonal Scheelite Group are included here. Wolframite Group WoIframite (Fe,Mn)W04 a : b : c = 0.8300 : 1 : 0.8678 B = 89' 22' Hiibnerite MnW04 048362 : 1 : 0.8668 89' 73' WOLFRAMITE. Monoclinic. Axes a : b : c = 0.8300 : 1 : 0.8678; B = 89' 22'. mm"', 110 A 1TO = 79" 23'. ay', 100 A 101 = 62' 54' at, 100 A 102 = 61" 54'. $', 011 A 011 = 81" 54'. Twins: (1) tw. axis c with a (100) as comp.-face; (2) tw. pl. k (023), Fig. 449, p. 171. Crystals commonly tabular (1 a (100); also prismatic. Faces in prismatic zone vertically striated. Often bladed, lamellar, coarse divergent columnar, granular. Cleavage: b (010) very perfect; also parting (1 a (100), and 11 t (102). Fract,ure uneven. Brittle. H. = 5-5.5. G. = 7.2-7.5. Luster submetallic. Color dark

Jan 1, 1922

By Thomas R. Mager

An in.t!estigation has been made of the equilibrium conditions at 1200°C in the reaction between hydrogen sulfide gas and sulfur dissolved in Fe-Si alloys From this the equilibrium constant, activity coefficient, and activity of sulfur in solution were calculated. A number of studies of the equilibrium of sulfur with iron and iron alloys have given closely agreeing results from which the activity and free energy of the dissolved sulfur may be found. Sherman, El-vander, and chipman1 discussed the significant researches of dilute solutions of sulfur in liquid iron prior to 1950, and the results of this study indicated that the relationship between the ratio of PH2S/PH2 in the environment and the percentage of sulfur in solution is not a linear one. Morris and williams2 studied the equilibrium conditions in the reaction between hydrogen sulfide gas and sulfur dissolved in liquid iron and Fe-Si alloys, and reported that silicon dissolved in iron has a pronounced effect on the equilibrium conditions. They found that the activity of sulfur in iron is increased by the addition of silicon. At a silicon content of 4 pet the activity coefficient of sulfur was about twice that for sulfur dissolved in pure iron. Sherman and chipman3 investigated the chemical behavior of sulfur in liquid iron at 1600°C through the study of the equilibrium: H2 + S = H2S; K = PH2S/PH2 . 1/as [1] From the known equilibrium constant of the reaction between H2, H2S, and S and the experimental data, the activity of sulfur in the melt was determined. They found that the activity coefficient of sulfur defined as fs = as/%s is increased by silicon and decreased by manganese. Morris4 and Turkdogan5 also reported that manganese decreases the activity coefficient of sulfur in liquid iron and iron-base alloys. A recent technique of sulfur analysis developed by Kriege and wolfe6 of the Westinghouse Research Laboratories permits an accurate sulfur analysis of 0.5 * 0.2 ppm in the range of 0.1 to 3 ppm, whereas in the range of 3 to 50 ppm the accuracy is ±1 ppm. This technique of sulfur analysis was utilized in this experiment. Previous unpublished data reported that sulfur analysis by the combustion technique was not accurate below 20 ppm. EXPERIMENTAL PROCEDURE Five 5-lb ingots of high-purity Fe-Si were prepared. Three of these ingots were prepared without the addition of manganese but with a variation of silicon contents from 2 to 4 pet. The remaining two ingots contained 3 pet Si with the addition of manganese. Ingots were made at each of three silicon levels: 2, 3, and 4 pet. No alloys were made with less than 2 pet Si since below approximately 1.8 pet Si the binary alloy exhibits a to ? transformation. The two additional ingots of 3 pet Si-Fe were made at each of two manganese levels: 0.20 and 0.50 pet. To minimize the effects, if any, of impurities on the activity of sulfur on Si-Fe, the best metals available were used for melting. All ingots were vacuum-melted in magnesium oxide crucibles. After obtaining samples for chemical analyses, the ingots were processed. This consisted of hot rolling and subsequently cold rolling the alloys. Each ingot was hot-rolled at 1000°C, reheating between every pass to minimize grain growth. All heating was done in a protective argon atmosphere. The slabs were hot-rolled to strips 50 mils thick. After hot rolling, all the material was pickled to remove the scale formed on the surface of the strip during hot rolling. The material was then cold-rolled to 12-mil strips. Single strips of the material used in this experiment were hydrogen-annealed at 1200°C for 16 hr in an alumina tube. Chemical analyses of strips M-1, M-3, M-4, M-7, and M-8 are given in Table I. Sulfur, silicon, and manganese analyses were made from the millings from the cold-rolled 12-mil strips. The oxygen analyses were made from slugs of the as-cast material. The hydrogen sulfide used in these experiments was supplied from cylinders containing a mixture of argon and 1 pet hydrogen sulfide. The parts per million of hydrogen sulfide were determined from the analysis of the exit gas of the annealing furnace during each anneal. The flow rate of hydrogen was approximately 1 liter per min in all anneals. The

Jan 1, 1964

By Carl J. McHargue

Mechanical twins were produced in electron-beam melted columbium by high-speed impact at room temperature and by slow or fast compression at -196°C. The composition plane of the twins was { 112} and the shear direction was <111>. Notches in the twin bands often corresponded to traces of {110) of the matrix and appeared to be untwinned regions. Markings within the twin bands were interpreted as resulting from {110} slip in the twins. THERE has been much work in recent years concerning plastic deformation by glide, and the dislocation theory relating to glide has reached a relatively high degree of development. On the other hand, there have been fewer studies of deformation by mechanical twinning, and understanding of this process is far from satisfactory. This method of deformation is of interest for at least two reasons. First, it provides a mechanism in addition to glide for the relief of stresses, and, in the bcc and hexagonal close-packed metals may result in significant amounts of plastic flow. Secondly, there is the possibility that twins may act as barriers for dislocation movement, resulting in pile-ups which could nucleate cracks. As might be expected, the bulk of the literature on mechanical twinning in the bcc metals is concerned with iron. A good summary of the work done prior to 1954 is contained in the book by all.&apos; Recently the refractory bcc metals have become increasingly important. Limited studies have shown that tantalum,2,3 molybdenum,4,5 vanadium,6,7 tungsten,&apos; and columbium9-11 deform by mechanical twinning under some conditions. Alloys of molybdenum with rhenium and tungsten with rhenium show extensive deformation by twinning at room temperature.I2-l4 Most of these studies have dealt primarily with mechanical properties at low temperatures or have shown the existence of twins, and there is only a small amount of information concerning the conditions under which they form. The subject of the present paper is the formation of twins under stress in columbium with a consideration of their morphology. EXPERIMENTAL PROCEDURE The material used for these studies was taken from an ingot of columbium which had been melted twice by the electron-be am-method. The analysis of the ingot was (in ppm): B < 1, C = 10, Fe < 100, The cast ingot contained very large grains, and it was possible to obtain single-crystal prisms which measured from ¼ to 3/4 in. on a side. A few experiments were conducted on polycrystalline plate which was prepared by rolling material from the same ingot at room temperature and annealing at 1000 in a dynamic vacuum of 10-6 mm Hg. This gave a plate in which the grains had an average diameter of 3 mm. After the specimens were cut from the ingot, the six faces were metallographically polished and elec-tropolished to remove all traces of cold work. Most of the observations were made on the surfaces of the deformed specirllens without further treatment. Occasionally, etching after deformation was desirable. In these cases, an etchant of the composition 50 parts H2O, 5 parts HNO3 25 parts HF, and 10 parts H2SO4 was found to delineate the twins very well. Unless considerable care was taken to ensure the removal of all disturbed metal left by the mechanical polishing, etching failed to reveal many of the features discussed in this; paper. The specimen&apos;s were deformed either by impact or slow compression at 77°K (liquid-nitrogen coolant), 198°K (dry ice and acetone coolant), and 298°K. The impact load was delivered by a hammer except in one case where the load was delivered by a bullet. Slow compression was carried out on a hydraulic testing machine equipped with a chamber to hold the coolant. EXPERIMENTAL RESULTS It has been generally believed that the conditions favoring the formation of deformation twins are large grains, low temperature, and impact loading. In fact, Barrett and Bakish2 found twins in tantalum only after impact deformation at 77°K, and Adams, Roberts, and Smallman10 observed twins in columbium only at 20 For these reasons, the initial experiments of this study used impact loading. Hammer blows caused many bands resembling twins in single crystals a.t 77" but not at 198°K. Only a few slip lines were observed on any of the single-crystal specimens of this study—essentially all the deformation occurred by twinning. The appearance of the twins on the as-deformed surface is shown in Fig. 1. Although both Figs. 1(a) and l(b) are photomicrographs of twins taken at the same magnification and from the same crystal, they are startlingly different in appearance. Fig. 1(a) was taken from the crystal face approximately perpendicular to the shear direction, whereas Fig. 1(b) was taken from

Jan 1, 1962