By W. L. Phillips

Single crystals of aluminum, brass, and copper oriented for (100) and (110) slip were extended at 25°, 400°, and 600°C in simple shear. Aluminum specimens oriented for nonoctahedral slip began to shear at a higher critical resolved shear stress than specimens oriented for octahedral slip. Parabolic stress-strain curves were obtained from zero strain. The initial rate of parabolic hardening was lower for specimens sheared on the (100) plane in a close-packed direction <110>, than for specimens sheared in a nonclose-packed direction <100>. metallographic evidence, however, showed that all slip traces could be explained in terms of (111) <100> slip. All attempts to cause nonoctahedral slip in copper and 70-30 a-brass single crystals were unsuccessful. Instead of shearing, the crystals bent, allowing {111} type planes to come into action. NONOCTAHEDRAL slip in aluminum has been reported under three different conditions: first, as the main mode of slip in tension experiments at elevated temperatures;&apos;-&apos; second, as the main mode of slip in direct shear experiments at room temperat~re; and third, as a minor mode of deformation, i.e., as cross-slip, in tension, shear, and bicrystal experiments at room and elevated temperatures."-l2 However, as far as the author knows, nonoctahedral slip has not been reported in either copper or 70-30 a-brass. The present study was undertaken to determine whether nonoctahedral slip could be obtained in aluminum, brass, or copper at room or elevated temperatures when the shear stress was approximately constant over the cross-section, a maximum at the center, or a maximum at the surface. EXPERIMENTAL PROCEDURE A detailed description of the crystal preparation and shearing apparatus has been given previo~sly. Cylindrical crystals 1/2 in. in diam and 8 in. long were grown from the melt in a temperature-gradient furnace. The aluminum contained 0.001 pct Zn, 0.001 pct S, and 0.001 pct Fe; the 70-30 brass contained 0.015 pct Pb, 0.001 pct Fe, 0.01 pct Ni, 0.02 pct Sn, and 0.005 pct Se; the copper was certified OFHC of 99.98 pct purity. All samples were electropolished prior to testing. The shear apparatus was a modified Bausch type. The strain sensitivity was 4 x lob4 Load was applied by clamping the rods attached to the shear plates in an Instron tensile machine. The rate of loading was 0.02 in. per min. In all cases a 1/8-in. gage length was used. For the tests performed at 400° and 600°C the shear plates, collars, and rods were made of stainless steel. These elevated-temperature tests were performed in an argon atmosphere. A) Aluminum at Room Temperature. Values of a and ß for the various slip planes and slip directions investigated are shown in Table I where a is the complement of the angle between the specimen axis and the slip direction, and ß is the angle between the specimen axis and the normal to the shear plane. The shear stress is a function of a (assuming ß - 0);10 when a is less than 27 deg, the shear stress on the slip plane for which the specimen is oriented has a maximum at the center of the crystal; at a = 27 deg the shear stress is constant across the slip plane; for a greater than 27 deg the shear stress is a minimum at the center. Fig. 1 shows the stress-strain curves for specimens cut from crystals 1, 2, and 5, which were sheared on the (010) plane in the [loll direction at room temperature. These three crystals have shear-stress distributions corresponding to the three dif-

Jan 1, 1962

PRESIDENT Willis McGerald Peirce New York City, N Y PAST PRESIDENTS D H McLaughhn, San Francisco, Calif L E Young&apos;, Pittsburgh, Pa VICE-PRESIDENTS A. B. Kinzell, New York, N Y H. W Thomas Ray, Arizona Philip Kraft, New York, N Y J L Gillsan Wilmington, Del M. L Haider, Toronto, Ont , Canada VICE-PRESIDENT and TREASURER Andrew Fletcher, New York, N Y

Jan 1, 1951

By E. O. Kirkendall

The investigation reported herein was undertaken to obtain data to supplement those presented in an earlier paper,l particularly for longer times at a higher temperature. This information may further develop our knowledge of the mechanism of diffusion in substitutional solid solutions. Diffusion of solute atoms interstitially dissolved is not difficult to visualize: it can take place without much disturbance of the solvent atoms. The mechanism of diffusion of solute atoms substitutionally dissolved is not so easily understood. Many theories have been advanced. Rosen-hain,2,3 Frenkel,4 Smekal,5 Langmuir,3,6 Steigman, Shockley and Nix,&apos; and Johnson8 all proposed theories to explain diffusion. Langmuir&apos;s proposed mechanism consisted of a simple cyclic interchange of atoms involving an interchange in lattice positions of four or more atoms. This mechanism, accepted by the author at the time of his previous publication,1 and apparently quite generally accepted, required a net exchange in positions of both solute and solvent atoms in equal numbers. In other words, the rate of diffusion of the solvent and solute atoms would be the same. That this cyclic interchange in lattice positions of solute and solvent atoms in equal numbers is the only true mechanism of diffusion is denied by the evidence presented in this paper. Experimental Procedure This modification of similar procedure1 will be outlined briefly. The method consisted of the following steps: I. A pure Muntz metal (60.6 per cent Cu, 0.1 per cent total impurities) that was almost all beta brass at 780°C. was chosen. 2. The brass was turned between centers in a lathe to a diameter of 0.5965 inches. 3. After the brass was cleaned, it was electroplated with pure copper to a diameter of about one inch. 4. The sample was heated slowly to 400°C. under reduced pressure and held at that temperature for 4 hr. to remove occluded gases. It was then cooled to room temperature. 5. The sample was heated to 780°C. ± 3°C. and held at that temperature for different lengths of time; then quenched. Samples were cut off each time after quenching. Metallographic samples 1/4 in. thick were removed at I hr., 6 hr., 24 hr., 96 hr. and 701 hr. After 96 and 701 hr. samples of about I in. were removed for X-ray analysis. 6. The metallographic samples were polished on the cross section and photomicrographs were taken. 7. The I-in. samples were polished and etched on both ends. With the aid of a microscope each was carefully mounted in a four-jaw chuck in a lathe, so that they could be accurately bored for an arbor. 8. Turnings were taken for each X-ray sample. After each set of turnings, the sample was heated in an oil bath for about 1/2 hr. at 300°C. It was then etched in 25

Jan 1, 1942

By E. O. Kirkendall

The investigation reported herein was undertaken to obtain data to supplement those presented in an earlier paper,l particularly for longer times at a higher temperature. This information may further develop our knowledge of the mechanism of diffusion in substitutional solid solutions. Diffusion of solute atoms interstitially dissolved is not difficult to visualize: it can take place without much disturbance of the solvent atoms. The mechanism of diffusion of solute atoms substitutionally dissolved is not so easily understood. Many theories have been advanced. Rosen-hain,2,3 Frenkel,4 Smekal,5 Langmuir,3,6 Steigman, Shockley and Nix,&apos; and Johnson8 all proposed theories to explain diffusion. Langmuir&apos;s proposed mechanism consisted of a simple cyclic interchange of atoms involving an interchange in lattice positions of four or more atoms. This mechanism, accepted by the author at the time of his previous publication,1 and apparently quite generally accepted, required a net exchange in positions of both solute and solvent atoms in equal numbers. In other words, the rate of diffusion of the solvent and solute atoms would be the same. That this cyclic interchange in lattice positions of solute and solvent atoms in equal numbers is the only true mechanism of diffusion is denied by the evidence presented in this paper. Experimental Procedure This modification of similar procedure1 will be outlined briefly. The method consisted of the following steps: I. A pure Muntz metal (60.6 per cent Cu, 0.1 per cent total impurities) that was almost all beta brass at 780°C. was chosen. 2. The brass was turned between centers in a lathe to a diameter of 0.5965 inches. 3. After the brass was cleaned, it was electroplated with pure copper to a diameter of about one inch. 4. The sample was heated slowly to 400°C. under reduced pressure and held at that temperature for 4 hr. to remove occluded gases. It was then cooled to room temperature. 5. The sample was heated to 780°C. ± 3°C. and held at that temperature for different lengths of time; then quenched. Samples were cut off each time after quenching. Metallographic samples 1/4 in. thick were removed at I hr., 6 hr., 24 hr., 96 hr. and 701 hr. After 96 and 701 hr. samples of about I in. were removed for X-ray analysis. 6. The metallographic samples were polished on the cross section and photomicrographs were taken. 7. The I-in. samples were polished and etched on both ends. With the aid of a microscope each was carefully mounted in a four-jaw chuck in a lathe, so that they could be accurately bored for an arbor. 8. Turnings were taken for each X-ray sample. After each set of turnings, the sample was heated in an oil bath for about 1/2 hr. at 300°C. It was then etched in 25

Jan 1, 1942

By H. R. Gardner

The heat treatmmt of plutonium was studied using the Jominy end-quenching technique commonly used for determining the hardenability of steel. Plutonium specimens were end-guenched from temperatures in each of the ß, y, d, d&apos;) and E phases. One series of specimens with a low-iron content, 165 pprn Fe, and another gvoup with a high-iron content, 678 pprn Fe, were used in order to study the effect of a Pu-Pu,Fe eutectic network on the hardness and micro-structure. Hardness traverses indicated no significant variations in hardness with either cooling rate or quench temperature. Metallographic studies indicated major effects on microstructure. Grain size was found to vary markedly with quenching temperature and cooling rate. It was determined that the Pu-PueFe eutectic network could be modified extensively by heat treatment, including spheroi -dization in the y phase and 6 phase below 413°C. An unidentified spheroidal inclusion was observed to go into solution in the delta and higher temperature phases. 1 HE element plutonium is unique among metals in that it has six allotropic forms in the solid state.&apos; These have been designated&apos; as the a, ß, y, d, d&apos;, and phases. The respective phase transformations occur at approximate temperatures of 122", 210°, 319°, 450°, and 480°C with a melting point at 640°C. With this number of phase transformations it becomes pertinent to consider the effect of heat treatment and cooling rate in the various phases on the microstructure and hardness of plutonium. To determine; the effect of a wide range of cooling rates, the Jominy end-quenching technique was applied to cylindrical plutonium specimens. In addition, since the presence of iron in amounts greater than 500 pprn is common in plutonium and results in a network of the Pu-Pu6Fe eutectic, it was decided to study heat treatment effects on two bomb reduced plutonium buttons with different iron contents. A low iron button containing 165 ppm Fe and a high iron button containing 678 ppm Fe were selected for this comparison. EXPERIMENTAL PROCEDURE Experimental Material. The cylindrical bars for Jominy quenching were cast from button stock in vacuo in MgO coated graphite molds. Metal pouring temperature was approximately 950°C and the molds were preheated to 300°C. The castings were machined to 0.5 in. diam. by 2.5 in. long cylinders. Chemical analysis and density data for the two groups of Jominy specimens containing different iron contents are presented in Table I. Except for iron, heats 19-12-1 and 20-2-1 are comparable within the limits of analytical accuracy. Representative specimens from the low-iron and high-iron bars were taken for metallographic examination. The low iron specimen was found to have extensive microcracking, Fig. 1. In addition, numerous unidentified spheroidal inclusions were present, Fig. 17. The average grain size of the low-iron plutonium is 0.068 mm, Fig. 4. In the high-iron plutonium, a Pu-Pu6Fe eutectic network is prominent, Fig. 7. The average size of the network is 0.100 mm. Unidentified spheroidal inclusions were also common in the high-iron plutonium. The average grain size of the high-iron plutonium is 0.036 mm. Experimental Technique. A Jominy end-quenching fixture was fabricated for glove box use. A 2.5 in. water height was used with an orifice of 0.250 in. ID. The orifice to specimen distance was maintained at 0.5 in. Annealing temperatures of 160°, 265°, 400°, 465°, and 535°c were chosen for the study of the effect of quenching from ß, y, d, d&apos;, and e phases on microstructure and hardness. During quenching, cooling curves were obtained from the Jominy specimens at distances from the quenched end of 1/16, 1/8, 3/8, 3/4, 1-1/4, and 2 in. Cooling rate calculations were made from the cooling curves for temperature intervals of 100° to 110° 160" to 170°, 330" to 340°, 420° to 430°, and 490° to 500°c. These temperature intervals were chosen

Jan 1, 1962

By William E. Ford, Edward Salisbury Dana

In their action upon the senses a few minerals possess taste, and others under some circumstances give off odor. 444. Taste belongs only to soluble minerals. The different kinds of taste adopted for reference are as follows: 1. Astringent: the taste of vitriol. 2. Sweetish astringent: taste of alum. 3. Saline: taste of common salt. 4. Alkaline: tast&apos;e of soda. 5. Cooling: taste of saltpeter. 6. Bitter: taste of Epsom salts. 7. Sour: taste of sulphuric acid.

Jan 1, 1922

COUNCIL OF SECTION DELEGATES Jack A. Criehton. Chairman Allen T. Cole. Vice Chairman M I. Signer, Secretary EXECUTIVE COMMITTEE W. C. Leonard, North Pacific W. K. Beck, Cleveland W. W. Leonard, Southwest Texas

Jan 1, 1952

By Zay Jeffries

Rearmament superimposed on buying sprees by the public, caused a general shortage of metals in 1911. and the rare metals were no exception; they also shared with the more common metals the uncertainty of future demand. In general, the apparent undersupply of metals is a favorable condition for the realization of sleeping possibilities of the rare metals, especially if the supply can he made sufficient to take care of the possible new demand. Many changes in metal usage in 1941 were forced because of shortages. When such changes are in the direction of the economic trend there is a speeding up in the tempo of the inevitable change, but when the forced changes are against the economic trend they are likely to be shortlived. In any event, the latter is not a solid foundation on which to build a future business.

Jan 1, 1942

By J. E. Campbell, A. W. Wesner, M. Pobereskin

This paper summarizes the results of an investigation sponsored by The Coates Steel Products Company. The objective was to determine the relative effects of certain chemical and physical properties on the wear resistance of grinding balls when grinding cement. In making this study, a number of types of balls were used in both dry and wet grinding in commercial ball mills. The radioactive-tracer technique was used in separating the test balls from the rest of the mill charge and in sorting the different types of halls that were all tested at the same time for each of the grinding operations. PROCESSING OF GRINDING BALLS In order to determine whether the properties of grinding balls, namely, composition, microstructure and hardness, can be related to the rate of wear, the halls used in this study were selected to represent various combinations of these properties. It was recognized that the mechanism of wear was not the same in the wet mill as in the dry mill. Therefore, the types of balls tested in each of the two environments were not necessarily the same. However, all of the types of balls evaluated in the dry mill were tested simultaneously for one time period, while those evaluated in the wet mill were tested simultaneously for three different time periods. All of the test balls were separated from the charge when the mill was dumped. All of the balls were of 0.940-inch diameter when charged, and all but the regular production balls were finish ground to this size to eliminate the decarburized surface layers. The steels and processing methods used, as well as the micro-structures and hardness levels of the balls, are described as follows: Regular production forged SAE 1095 steel balls were used in both the wet and dry mills. They were forged to a nominal diameter of 0.940 inch and quenched in oil from the forging temperature. Each retained a partially decarburized surface layer from the forging bar stock; the maximum depth of this layer was about 0.030 inch and the decarburization was negligible where the ball was sheared from the bar. The hardness at the surface was 40 to 46 Rock-well C in the partially decarburized area and 57 to 62 Rockwell C in the areas not decarburized. The hardened zone extended to a depth of about one-third of the radius. Below the decarburized layer, the hardened zone consisted primarily of hard as-quenched martensite with varying amounts of retained austenite. This structure changed to fine pearlite at a depth of about one-third of the radius. In order to eliminate the effect of the decarburized layer, a set of production balls of SAE 1095 steel was forged to about a 1-inch diameter, quenched in oil from the forging temperature, and ground on ball-bearing grinding equipment to a 0.940-inch diameter to remove the decarburized layer. The balls&apos; hardened zones were similar to those in the previous set. The hardness of the finished surfaces was 52 to 60 Rockwell C. A slight amount of decarburization apparently remained after the removal of about 0.030 inch from the surface. Balls of this type were tested in the dry mill only. Another set of forged SAE 1095 steel balls of 1-inch diameter was heated to 1500 F and quenched

Jan 1, 1961

By H. Papazian, Robert A. Lad

SINCE it can be shown both theoretically&apos;&apos; : and experimentally that disordered Cu3Au has a greater internal energy than the ordered alloy, it might be expected that its chemical reactivity would be greater. Experiments were initiated&apos; to test this hypothesis. This note will describe some recent results obtained in the study of the rates of corrosion of ordered and disordered polycrystalline Cu3Au by aqueous FeCl., The work of Robertson&apos; has indicated that the attack by such solutions is intergran-ular and highly orientation dependent. It was of interest to see whether the order-disorder effect was great enough to overcome the variations from specimen to specimen which would arise from this type of attack. The polycrystalline alloy specimens (0.020 in. wire, 1¾ in. long) were preannealed in ½ atm H, at 700°C for 2 hr. The subsequent heat treatments to produce order and disorder were performed in M atm He. Disordered specimens were obtained by heating at 450°C for 2 hr and quenching in water. Ordered specimens were produced by heating for 2 hr at 450°, furnace cooling to 380°, and soaking at 380°C for 80 to 90 hr. Room temperature was reached by cooling to 150" at a rate never exceeding 7" per hr, and water quenching from 150°C. The specimens so produced exhibited electrical resistivities characteristic of the two states; of the order of 11.27x10 ohm-cm for the disordered, and 4.28x10 ohm-cm for the ordered specimens. The corrosion rates were studied at 30°C in ferric chloride solutions of several concentrations (?,¼, 1.5, and 1 molar). The specimens were attached to a stirrer during the tests. Tests were interrupted at intervals, and the specimen weight change was determined after washing and drying. Analysis of the solutions showed that the attack was limited to the copper. The higher corrosion rate for the disordered alloy, as illustrated in Fig. l, is typical of the results obtained. The effect of variation in ferric chloride concentrations is indicated in Table I for typical specimens. The variations in the ratio of reactivity for disordered and ordered specimens at the different concentrations are within experimental error, and the best value is estimated to be near 1.4. The experimental variation was due in part to the mode of attack, as mentioned, and in part to the fact that films were formed on the specimens under some conditions. Electron diffraction patterns of the films were very complex and indicated the presence of metallic iron, as did chemical analysis. In an attempt to eliminate the difficulties arising from the mechanism of attack, single crystal specimens were used. A greater reaction rate was again measured for the disordered specimens, but the reproduci-bility was no better than that for the polycrystalline metal. This would indicate that film formation was primarily responsible. It was concluded that the reaction with aqueous ferric chloride served to demonstrate that the reactivity of disordered Cu3Au is greater than that of the ordered alloy. However, the difficulties with film formation did not permit determinations of a precision great enough to warrant extension of the study to partially ordered alloy systems.

Jan 1, 1957

By S. R. Goodman, Hsun Hu

A study has hem made of the formation of annealing textures in an 18-8 austenitic stainless steel (Type 304L) from various deformation textures obtained by rolling at different temperatures. When the deformation texture is a mixture of the ferritic type and the brass type owing to the pres -ence of both martensitic ferrite and retained aus-tenite in the specimen, recrystallization takes place by the growth of the existing austenite phase. In a previous report,&apos; it was shown that the rolling texture of austenitic stainless steel (Type 304L) changed gradually from the brass type to the copper type with increasing temperature of deformation above 200°C. These changes are similar to those in high-purity silver2,3 and electrolytic copper;4 a brass-type texture is favored at low rolling temperatures, whereas a copper-type texture is favored During the course of rolling -texture transition from the brass type to the copper type, the subsequent recrystallization textures change accordingly. The orientation relationship between the annealing textures and the various rolling textures, being consistent with previous observations on various fcc metals, can be described as [Ill] rotations of approximately 25 to 40 deg. Carhide precipitation may influence the annealing textures. at high rolling temperatures. Furthermore, the annealing textures in high-purity silver5 and electrolytic copper4 were found to depend entirely on the prior deformation texture. From a copper-type rolling texture a strong cube texture will form upon recrystallization, whereas from a brass-type rolling texture the annealing texture will be quite different from the cube orientation. In an earlier comm~nication,6 the formation of a strong cube texture in 18-8 austenite stainless steels (Types 304 and 304L) was reported briefly by the authors. The present paper constitutes the results of a complete study of the annealing textures obtained from a

Jan 1, 1965

By A. U. Seybolt

Experiments on both suljidation and hot corrosion have been carried out using ternary Ni-Cr-X alloys and commercial nickel-base superalloys. It has been shown that lhere are certain micro structural similarities between sulfidation using H,S/H2 mixtures and hot corvosion using Na,S04 in "crucible" experiments or hot corrosion tests using a flame tunnel apparatus. It is proposed that two key processes in the hot cowosion process are: 1) formation of chromium sulfides which deplete the alloy matrix, and 2) oxidation which can be accelerated because of chromium depletion. Other processes play an important role in the hot corrosion process, such as accelerated oxidation attack due to the presence of a N& S04 or N&SO,- NaC2 film which inhibits the formation of a protective external oxide scale. However, this latter phenomenon was not studied in this work. THE term hot corrosion has come to mean a combination of sulfur and oxygen attack on nickel-base or cobalt-base superalloys used as gas turbine blades or partitions. This attack can be initiated by any combustion process in air involving fuel containing sulfur if the sulfur level is sufficiently high. Levels of 5 pet SO2l for example, in the combusting gas have been observed to produce hot corrosion attack on nickel-base alloys. The important immediate corroding medium in aircraft gas turbines, however, has been established to be Na2S04, formed from reaction between NaCl from sea air and sulfur in the fuel.&apos; The Na2S04 concentrates the sulfur sufficiently so that superalloy parts heated in the range 1400" to 1900°F can become sulfided by reducing the Na2S04 film which forms on the parts, and this reaction allows sulfur to gain access to the alloy. The sulfur thus released diffuses into the superalloy and forms primarily chromium sulfides of various compositions, but frequently Cr2S, has been identified. Figs. 1 and 2 show the morphology typical of hot corrosion of a cobalt-base superalloy X-45 (25 Cr, 10 Ni, 7.5 W, 0.25 C) and a nickel-base alloy, Udimet 500 (19 Cr, 19 Co, 4 Mo, 3 Ti, 2.9 Al, 0.07 C). Both alloy samples were subjected to the same hot corrosion conditions: 616 hr at 1600°F in a combusted 2.9 pct S distillate oil containing 125 ppm Na as NaC1. It will be noted at once that the nickel-base alloy is much more severely attacked. The depth of corrosion is much greater and the number and size of the sulfides present are much greater. Both alloys show a duplex oxide scale, which is more noticeable in the X-45 alloy. The external scale is probably a spinel in both cases, with CrQ3 lying next to the alloy. Many investigators1 -"ve been concerned with hot corrosion phenomena, but there has been a lack of unanimity of opinion as to the details of the hot corrosion mechanism. More than one definition of hot corrosion is possible. Some investigators con- sider as a measure of hot corrosion only the weight gain due to an accelerated oxidation. However another point of view is that the total depth of affected alloy may be used as a measure. While it is recognized that surface oxidation attack is greatly accelerated by the presence of salts like Na2S04 or Na2S04-NaC1 mixtures, sulfur penetration into the alloy also undoubtedly produces very important effects. The region of sul-fide penetration which is so prominent in Fig. 2 is one of the outstanding characteristics of hot corrosion. For highly stressed parts, such as first-stage buckets, this sulfur-penetrated region can be more significant in mechanical property loss than the reduction of cross section produced by the formation of the massive external scale. In addition, evidence will be presented that this sulfided region can be less resistant to subsequent oxidation attack. Since it appears that the sulfided region below the surface oxide scale plays an important role in the overall corrosion process,

Jan 1, 1969

C. H. MATHEWSON, Chairman SAM TOUR, Past-chairman W. A. SCHEUCH, Vice-chairman T. S. FULLER, Vice-chairman W. M. CORSE, Secretary-Treasurer 810 Eighteenth St., N. W. Washington, D. C. Executive Committee J. L. CHRISTIE ARTHUR PHILLIPS E. H. Dix, JR. GUY C. RIDDELL W. M. PRIRCE J. WALTER SCOTT&apos; A. J. PHILLIPS&apos; H. M. WILLIAMS EL M. WISE

Jan 1, 1932

By J. W. Hickman, E. A. Gulbransen

In a previous paper&apos; the authors have investigated the structure of the oxide films formed on most of the metals that make up the alloys of this study. The metals were studied in order to provide basic information on the structures, both physical and chemical, of the oxide films and to determine how these structures are effected by the temperature, time of oxidation, and surface preparation. It was felt that an understanding of the physical and chemical structure as well as the stability of the oxide film might furnish clues as to the nature of the reaction process and the protective quality of the film. The oxidation of the metals was studied over the temperature range 300&apos; to 7o0°C. except for copper, wherc the range selected was 100&apos; to 500°C. The results of these studies were presented in graphical form as existence diagrams of the oxides on a time-temperature scale. For some of the metals the existence diagrams were simple and showed few chemical transitions, but there were numerous cases where the physical state of the oxide surface was a function of time and temperature. In general the physical state of the oxide surface changed with increasing temperature so as to increase the sharpness of the diffraction patterns and to cause orientation effects to be more pronounced. Deviatiois in lattice Darameters from X-ray values were noted. In general these deviations were of positive nature and may be due to solid solution of the metal in the oxide lattice. This effect might be expected in thin oxide films. In a study of the oxidation of alloys containing two or more metals, there may arise the complicating factor of identification of the oxides formed. A thorough understanding of the oxides formed on the pure metals, therefore, was, essential before investigation of the oxidation of alloys. In this paper it is our purpose to present a study of the following problems: 1. The existence diagrams of various alloys. 2. The effect of the structure of the alloying metal on the existence diagram of iron. 3. The effect of the percentage of chromium on the oxides formed on Fe-Cr alloys. 4. The relationships, if any, between the oxides formed and the protective quality of the oxides. The following alloys are included in this study: alloys of iron with body-centered cubic, face-centered cubic and other metals, 13 Cr-Fe, 18-8 stainless steel, K4²B, Nichrome V, Hipernik, Inconel, Stellite "²I," Refractaloy, Kovar, mild steel, a series of Cr-Fe alloys and a series of Co-Fe alloys. Since many of the commercial alloys in this list contain more than two metals, various complicating factors in the identification of the oxides formed may arise.

Jan 1, 1947

By E. A. Gulbransen, J. W. Hickman

In a previous paper&apos; the authors have investigated the structure of the oxide films formed on most of the metals that make up the alloys of this study. The metals were studied in order to provide basic information on the structures, both physical and chemical, of the oxide films and to determine how these structures are effected by the temperature, time of oxidation, and surface preparation. It was felt that an understanding of the physical and chemical structure as well as the stability of the oxide film might furnish clues as to the nature of the reaction process and the protective quality of the film. The oxidation of the metals was studied over the temperature range 300&apos; to 7o0°C. except for copper, wherc the range selected was 100&apos; to 500°C. The results of these studies were presented in graphical form as existence diagrams of the oxides on a time-temperature scale. For some of the metals the existence diagrams were simple and showed few chemical transitions, but there were numerous cases where the physical state of the oxide surface was a function of time and temperature. In general the physical state of the oxide surface changed with increasing temperature so as to increase the sharpness of the diffraction patterns and to cause orientation effects to be more pronounced. Deviatiois in lattice Darameters from X-ray values were noted. In general these deviations were of positive nature and may be due to solid solution of the metal in the oxide lattice. This effect might be expected in thin oxide films. In a study of the oxidation of alloys containing two or more metals, there may arise the complicating factor of identification of the oxides formed. A thorough understanding of the oxides formed on the pure metals, therefore, was, essential before investigation of the oxidation of alloys. In this paper it is our purpose to present a study of the following problems: 1. The existence diagrams of various alloys. 2. The effect of the structure of the alloying metal on the existence diagram of iron. 3. The effect of the percentage of chromium on the oxides formed on Fe-Cr alloys. 4. The relationships, if any, between the oxides formed and the protective quality of the oxides. The following alloys are included in this study: alloys of iron with body-centered cubic, face-centered cubic and other metals, 13 Cr-Fe, 18-8 stainless steel, K4²B, Nichrome V, Hipernik, Inconel, Stellite "²I," Refractaloy, Kovar, mild steel, a series of Cr-Fe alloys and a series of Co-Fe alloys. Since many of the commercial alloys in this list contain more than two metals, various complicating factors in the identification of the oxides formed may arise.

Jan 1, 1947

WILLIAM L SAUNDERS, President GEORGE H PEGRAM, 1st Vice-president ALFRED D FLINN, Secretary J V W REYNDERS, 2d Vice-president JACOBS LANGTHORN, Treasurer HENRY A LARDNER Assistant treasurer Finance Committee House Committee GEORGE H PEGRAM, Chairman ; ALFRED D FLINN. Chairman J VIPOND DAVIES FREDERICK F SHARPLESS BANCROFT GHERARDI JOHN H DUNLAP WILLIAM L SAUNDERS CALVIN W RICE W F M GOSS, ex-officio F L HUTCHINSON

Jan 1, 1923

By L. A. Roe, E. A. Elevatorski

Wollastonite, named after William H. Wollaston, an English chemist, is a calcium metasilicate, CaSiO3; CaO: 48.30%, SiO2: 51.70%. It has a short history as an industrial mineral. The earliest production of wollastonite is reported to be from a deposit near Code Siding, located north of Randsburg, CA. At this locality small tonnages of wollastonite were quarried during 1933-34 and 1938-41, and processed into mineral wool. This operation was largely experimental and virtually no United States production was again reported until the 1950s when a large deposit near Willsboro, NY, was developed by the Cabot Corp. A processing plant was placed onstream in 1953, with nearly continuous production to date. It is currently operated by NYCO, a division of Processed Minerals, Inc. Since 1958, wollastonite deposits in the Little and Big Maria Mountains of Riverside County, and in the Panamint Range of Inyo County, both in California, have operated intermittently for production of both ornamental and commercial wollastonite. During 1980, the United States was the major producing country, furnishing about 75% of the world&apos;s output. Current production comes from Finland, Mexico, India, and Kenya. Small amounts have been shipped intermittently from the USSR, New Zealand, Republic of the Sudan, Republic of South Africa, and Namibia (South-West Africa). The principal use of wollastonite is in the manufacture of plastics. Other uses are for paints, ceramics, adhesives, fluxes, glazes, thermal insulation board, and refractory products. Mineralogy Pure wollastonite, CaSiO3, has the composition of 48.3% CaO and 51.7% SiO2. However, it is seldom found in the pure state due to the ease with which it takes into solution the metasilicates of manganese, magnesium, iron, and strontium. Predominantly, wollastonite occurs as a contact metamorphic deposit forming between limestones and igneous rocks. Commonly associated minerals are garnet, diopside, epidote, calcite, and quartz. It has a specific gravity of 2.8 to 3.0, and hardness of 4.5 to 5 on Mohs&apos; scale. When pure, it has a brilliant white color, but with impurities it may be grayish or brownish. Luster is vitreous to pearly. Melting point of wollastonite is about 1540ºC. Wollastonite occurs in coarse-bladed masses, rarely showing good crystal form. It is usually acicular or fibrous, even in the smallest of particles. The most unique property of crushed and ground wollastonite is its cleavage. Fragments of crushed wollastonite tend to be needle-shaped, imparting a high strength, and this property is the basis for many of its uses. The fiber lengths are commonly in the ratio of 7 or 8 to 1, length to diameter. The average diameter of wollastonite is 3.5 µm. Some crystals of wollastonite fluoresce under short-wave or longwave ultraviolet light, or both, with colors ranging from yellow-orange to pink-orange. Specimens may also show phosphorescence. The acicularity of wollastonite is a property of considerable importance to the marketplace. The plastics industry makes utilization of high aspect ratio grades of wollastonite (20:1) for reinforcing thermoplastics and thermoset polymer compounds. The naturally high pH of 9.9 (10% water slurry) is a prime property to the coatings industry. The coatings industry uses milled grades of wollastonite as a pH stabilizer in interior and exterior PVA and acrylic latex systems. Processed wollastonite can have a G.E. brightness of 90 to 93. Chemically, wollastonite is inert and this property makes it useful as a filler and reinforcing agent. There are two polymorphs of calcium silicates: wollastonite, a low temperature form, and pseudowollastonite, a high temperature

Jan 1, 1983

NORTH AMERICA. CANADA Canadian Army Overseas. Ball, H. D. Bridges. C. Butterill, H. J. If. Ladner, F. E. Lane, H. C. Alillar, W. A. ALBERTA Calgary.-Chonette, W. C. Clark, L. At. Corbett, C. S. de Hart, J. B. Dingman, C. W. Fath. A. E. Fulton. J. If. Cray, J. G. Johnson. R. V. McCutchin, J. A. *Slipper, S. E. Vin Buckirk H. A.

Jan 1, 1944

By H. D. Kessler, F. A. Crossley, J. J. Rausch

The titanium-rich corner of the system Ti-AI-V has been studied to determine the phase relationships in the temperature interval 600° to 1200°C. Metallographic examination of long time isothermally annealed specimens was the principal method of investigation. TWENTY-SIX alloys in the region 1 to 22 pct A1 and 2 to 11 pct V, and the temperature range 600° to 1200°C, were studied as part of a program on phase relationships and transformation processes of titanium alloy systems. Experimental Procedure Preparation of Alloys—Materials used in the preparation of alloys were high purity Bureau of Mines sponge titanium (103 Bhn), 99.7 pct pure V chips obtained from the Electro Metallurgical Div., union Carbide and Carbon carp., and 99.71 pet pure A1 in the form of granulated shot from Aluminum cO. Of The alloy ingots, weighing l5 g, were melted in a nonconsumable tungsten electrode arc furnace un-

Jan 1, 1957

By D. V. Edmonds, C. J. Beevers

Tensile tests were carried out on a! titanium containing 850, 1250, and 2700 ppm 0, and up to -500 ppm H. The tests were performed at -196", -78", 20°, 150°, and 300°C at a strain rate of -1.0 x 10??3 sec-1. Increasing oxygen content, increasing grain size, and decreasing test temperature resulted in enhanced embrittlement of the a titanium by the hydrogen additions. Metallographic observations showed that this can be correlated with the influence of these parameters on the introduction of cracks into the a! titanium by fracture of titanium hydride precipitates. CRAIGHEAD et al.1 reported that the hydrogen content normally found in commercial-purity a! titanium (60 to 100 ppm) was sufficient to cause a substantial lowering of the impact strength, and they attributed this embrittling effect of hydrogen to the precipitation of titanium hydride. Lenning et al.&apos; found that in commercial-purity a titanium there is an almost complete loss of impact strength at about 200 pprn H, which is approximately half the value needed to eliminate the impact strength of high-purity a titanium. They also showed that the presence of 3000 ppm hydrogen reduces the room-temperature tensile ductility of commercial-purity material to a value of the order of 10 pct; the corresponding hydrogen concentration for high-purity titanium is over 9000 ppm. It thus appears that the detrimental effect of hydrogen on the mechanical properties of commercial-purity titanium becomes evident at much lower hydrogen contents than for high-purity titanium. The main difference between the two types of a titanium might be expected to be the higher level of interstitial impurity in the commercial-purity grade. Jaffee et a1.3 studied the influence of temperature and strain rate on the hydrogen embrittlement of high-purity and commercial-purity ! titanium. In general, the behavior was the same for both materials; embrittlement was enhanced by decreasing temperature and increasing strain rate. Recent results from tests on commercial-purity a titanium containing 850 ppm O and varying amounts of hydrogen up to -500 ppm showed that the degree of embrittlement by hydrogen is intimately related to the fracture characteristics of titanium hydride precipitates.4 The present paper considers the interrelationship between the mechanical properties and micro-structural features of commercial-purity a! titanium containing 850, 1250, and 2700 ppm 0 and varying amounts of hydrogen up to -500 ppm. 1. EXPERIMENTAL PROCEDURE Three types of commercial-purity titanium supplied by IMI* were used in the investigation, and for the *Address: Witton, Birmingham 6, United Kingdom. purpose of this paper are designated Ti 115, Ti 130, and Ti 160. The principal impurity elements are given in Table I. The material was received in the form of 12.7 mm diam bars having a fully recrystallized structure. Tensile specimens with a round cross-section of 4.5 mm diam and a gage length of 15.2 mm were machined from the bars. In order to develop the same grain size (mean linear intercept of grain boundaries) in each of the three types the specimens were annealed under a dynamic vacuum of <10?5 mm Hg, Table 11. Specimen hydriding was carried out in a modified Sieverts apparatus;&apos; hydrogen was taken into solution at 450°C and after holding the specimens at this temperature for 24 hr they were furnace-cooled to room temperature at an average rate of -100 C deg per hr. By this method nominal hydrogen contents of 0, 50, 100, 250, and 500 ppm were introduced into specimens of Ti 115, Ti 130, and Ti 160 (100 ppm (wt) -0.5 at. pct). The actual hydrogen contents were calculated from the weight differences obtained by weighing the specimens before and after the hydriding treatment. Tensile tests were carried out at temperatures of -196", -78", 20°, 150°, and 300°C on a 10,000 kg In-stron machine at a nominal strain rate of -1.0 x 10-3 sec-1. Fractured specimens were sectioned in planes parallel to the tensile axis, mechanically polished to 0.25 µm grade of diamond paste, and then attack polished using a solution containing by volume 99 parts H2O, 1 part HF, and 1 part HNO3. Although the latter treatment unavoidably opened out cracks and voids visible after mechanical polishing, it did reveal the grain structure, titanium hydride morphology, and deformation twinning structure.

Jan 1, 1970