Search Documents

By John P. Goheen

Considerable work has been done in developing a pyrometer to measure the temperature of molten brasses, bronzes, and aluminum in the crucible. On account of the high melting points and the amount of zinc and sulfurous fumes given off from molten brasses, the conditions are somewhat severe for a thermocouple of standard design; but satisfactory results are obtained with a portable pyrometer, 3 ft. (0.9 m.) of connecting lead wire, and a special 5-ft. nickel-nickel chromium thermocouple, composed of rods 1/4in. (6.35 mm.) in diameter. The lower 12 or 24 in., as desired, may be made detachable so that new tips may be connected at little trouble or expense. The portable instrument need not be of the extreme high-resistance type, as the movable parts of the galvanometer of a lower resistance instrument may be better constxucted to withstand the continuous handling such an instrument receives. Platinum-platinum rhodium thermocouples, protected with porcelain and graphite tubes, have been used, but the lag in registering the temperature is too great. It has been found that the range of temperature for various brasses is as follows: Red brasses...............2200-2250" F. (1205-1234" C.) Yellow brasses............2250-2400" F. (1234-1318' C.) Bronzes..................2300-2550" F. (1260-1400" C.) A recent test with a portable pyrometer having a range of 2600" F. with a bare 1/4 in. heavy exposed couple 5 it. long and a handle attached at the upper end showed that the temperatures of molten aluminum under varying conditions in an oil-fired crucible furnace and one of the Simplex type were as follows: CRUCIBLE, OIL-FIRED FURNACE SIMPLEX FURNACE Temperature of metal in furnace....... 1540" F. (837" C.) 1530" F. (834" C.) Temperature in ladle after skimming at furnace......................... 1480" F. (805" C.) 1440" F. (784" C.) Temperature in ladle after skimming at floor near mold................... 1440" F. (784" C.) 1430' F. (778" C.)

Jan 1, 1923

By John P. Goheen

Considerable work has been done in developing a pyrometer to measure the temperature of molten brasses, bronzes, and aluminum in the crucible. On account of the high melting points and the amount of zinc and sulfurous fumes given off from molten brasses, the conditions are somewhat severe for a thermocouple of standard design; but satisfactory results are obtained with a portable pyrometer, 3 ft. (0.9 m.) of connecting lead wire, and a special 5-ft. nickel-nickel chromium thermocouple, composed of rods 1/4in. (6.35 mm.) in diameter. The lower 12 or 24 in., as desired, may be made detachable so that new tips may be connected at little trouble or expense. The portable instrument need not be of the extreme high-resistance type, as the movable parts of the galvanometer of a lower resistance instrument may be better constxucted to withstand the continuous handling such an instrument receives. Platinum-platinum rhodium thermocouples, protected with porcelain and graphite tubes, have been used, but the lag in registering the temperature is too great. It has been found that the range of temperature for various brasses is as follows: Red brasses...............2200-2250" F. (1205-1234" C.) Yellow brasses............2250-2400" F. (1234-1318' C.) Bronzes..................2300-2550" F. (1260-1400" C.) A recent test with a portable pyrometer having a range of 2600" F. with a bare 1/4 in. heavy exposed couple 5 it. long and a handle attached at the upper end showed that the temperatures of molten aluminum under varying conditions in an oil-fired crucible furnace and one of the Simplex type were as follows: CRUCIBLE, OIL-FIRED FURNACE SIMPLEX FURNACE Temperature of metal in furnace....... 1540" F. (837" C.) 1530" F. (834" C.) Temperature in ladle after skimming at furnace......................... 1480" F. (805" C.) 1440" F. (784" C.) Temperature in ladle after skimming at floor near mold................... 1440" F. (784" C.) 1430' F. (778" C.)

Jan 1, 1923

[*DAVID THOMAB ...................... 1871 *R. W. RAYMOND .1872-1874 *A. L. HOLLEY ....................... 1876 *Asurn 8. H~WITT ................... 1876 *T.ST~RYHUNT ..................... 1877 *ECKLBY B. COXB .1878-1879 *WILLIAM P. BHINN .................. 1880]

Jan 1, 1946

By Didyk M. Marko, Vásquez Ñ. Gregorio

INTRODUCTION The Salvador Division of Codelco Chile is an important copper molybdenum production center, located 1,200 km north of Santiago and 124 km east of the Pacific Ocean, in the foothills of the Andes Range. El Salvador Mine produces by block caving 8,600,000 t of ore with a content of 1 .l0% Cu and 0.02% Mo, from a copper porphyry ore body. The geology of the ore body shows a great heterogeneity as to rocks, grade distribution, ore height and undercutting levels. This has resulted in a variety of designs for the productive units (blocks) and in the mineral handling systems. Up to now, 4 systems have been employed: grizzly and intermediate haulage; slusher drifts with intermediate ore pass and haulage; slusher drifts with scraper loading directly into trains; and, LHD. On the other hand there is a marked dispersion in the final results from each block mined out. We report here the conclusions reached after analyzing the data gathered on the mining of 163 depleted blocks, representing a total production of 102,000,000 t, with an undercut area of 340,000 sq m. The final results of each block, characterized in terms of tonnage and fine cop- per recovery, were studied as a function of a number of design, geological, and operational parameters. BASIC CONCEPTS Indices of Efficiency In order to evaluate the final result of each block, or group of blocks, the following indices of efficiency were defined : Tonnage Recovery (TR) . It is the ratio between the ore tonnage extracted and the in situ tonnage estimate for each block or group of blocks. Grade efficiency (E) . It is the ratio between the Cu mill feed grade and the in situ Cu grade estimate for each block or group of blocks. Grade efficiency is numerically equal to the ratio between fine copper recovery (FR) and tonnage recovery (TR) . Figure 1 shows the final results for 163 mined out blocks, in terms of tonnage and fine copper recovery. Different grade efficiencies are also indicated. The marked dispersion in the final results of mined out blocks must be stressed since it greatly incides in mine planning. It must be kept in mind that an eventual concentration of low overall efficiency in the blocks during a given period (e.g., one year) will make it necessary to bring into production new blocks over the standard development schedule. It is worth noting that the final results in the 163 mined out blocks corresponding to a production of 102,000,000 t of ore with a mill feed grade of 1.445% were obtained from an ore estimate of 93,000,000 t and a grade of 1.671% Cu, which represents 110% tonnage recovery and 86% grade efficiency. Parameters Studied The following parameters are considered in this study: Geological Parameters. These parameters depend exclusively on the geological and geotechnical features of the ore body. IN SITU GRADE: The initial estimate of the block grade. Four copper grade categories were considered : (a) lower than 1.3% ; (b) 1.3 to 1.6%; (c) 1.6 to 2.0%; (d) higher than 2.0%. The overall initial in situ estimate of the ore body was 1.6% Cu. IN SITU TONNAGE: Initial tonnage estimate of the block. Four categories are considered: (a) below 500,000 t; (b) 500,000 to 1,000,000 t (c) 1,000,000 to 1,500,000 t; (d) over 1,500,000 t. CONTACTS SLOPE: Since up to 4 rock types can be found in a block, resulting in a corresponding number of contacts, a horizontal con- tact was defined as that which forms an angle of less than 45" with the horizontal and a vertical contact that which forms an angle of more than 45" with the horizontal. GRADE DISTRIBUTION: As in rock types, horizontal and vertical grades were defined. ORE HEIGHT: The distance measured between the undercut level and the top of ore. Four categories are considered: (a) less than 60 m; (b) 60 to 100 m; (c) 100 to 150 m; (d)over 150 m

Jan 1, 1981

By Nicholas J. Grant, Noboru Komatsu

Metallographic and X-ray studies were made of oxide dispersion strengthened Cu-12 vol pet SiO2 and Cu-3.5 vol pet Al2O3 alloys following time exposures at temperatures approaching the melting. point of the matrix metal. Changes in hardness, oxide particle size and crystal structure were studied to determine the time-temperature stability of these alloys. An interpretation of the mechanism of oxide agglomeration is proposed. One of the most striking features of dispersion strengthened metal-metal oxide alloys is their stability at elevated temperatures, both with respect to recrystallization and maintenance of mechanical properties after exposure at high temperatures. A small amount of work has been done on the re-crystallization phenomenon in dispersion hardened metal-metal oxide alloys'l and several theoretical treatments have been advanced regarding the stability of these alloys by Lenel and Ansell,8 and by Grant and his co-workers.9, 10 This paper reports on metallographic and X-ray studies following various heat treatments of Cu-AI2D3 and Cu-SiO2 alloys at elevated temperatures and the effect of subsequent cold work on the recrystallizalion temperature. An interpretation of the recrystallization behavior of this type of alloy, based on the decomposition and agglomeration of oxides, is proposed. EXPERIMENTAL PROCEDURE Cast ingot bars of copper-1.59 pet Si and Cu-0.77 pet Al, 7/8 in in diam, were annealed in argon for 80 hr at 1000CC for homogenization. The homogenized rods were machined into fine chips and ball milled. Milled particles in the range minus 20 to plus 60 mesh were separated for internal oxidation. The internal oxidation was accomplished by the same method used by Preston and Grant,9 except that the oxidalion temperature for the Cu-Si alloy was 750°C, and for the Cu-A1 alloy was 800°C. These powders were then hydrogen-reduced at 450°C, compacted in a copper container, evacuated at room temperature to 0.04 µ, and sealed for extrusion. They were extruded at 1400°F (760°C) with a ram speed of 55 in. per min for an extrusion ratio of 15.6 to 1 to give a rod 0.38 in. diam by about 3 ft long.

Jan 1, 1962

By Harold R. Bradford

EXPANSION initiated during and after the war has placed industrial plants in new areas and increased reduction and manufacturing facilities in communities already established. With added expansion interest has grown in possible area contamination from waste products. Evolved flue waste contains many chemical contaminants that may or may not cause concern; however, atmospheric pollution has always been a problem to industrial communities. For some time effects attributed to small quantities of compounds of fluorine in various waste gases have been studied by industrial, medical, agricultural, and associated interests.1'2 Aside from an article by Churchill, Rowley, and Martin in 1948," little has been published on the subject of fluorine in coal except by foreign investigators. The first indication of fluorine compounds in coal was noted in England in 1934 by R. Lessing,4,5 who found that the presence of fluorine in Midland and West County coals was definitely established by etching of glass and by severe corrosion of porcelain fillings in a gas works scrubber. Etching of glass in a direct contact annealing kiln initiated research, and in 1944 four papers were published by H. E. Crossley,6-9 giving results of investigations of fluorine in coal of England by the Fuel Research Board, Department of Scientific and Industrial Research. These investigations studied methods of determining fluorine, the quantities present in various coal deposits, the geographical distribution of fluorine in British coals, occurrence of fluorine in minerals associated with coal, amounts of fluorine compared to other constituents of coal, the nature of fluorine compounds, and industrial significance of fluorine in coal. It was shown that British coals contain from 5 to 200 ppm of fluorine, which is probably present as fluorapatite [Ca10F2(PO4)6], often written as [3Ca3P2O8.CaF2]. The fluorapatite is intimately associated with shale in some coals and can often be separated from these coals along with the shales. H. E. Crossley8 also reported no correlation between the amounts of chlorine, sulfur, or ash and the amount of fluorine in different coals. He found, however, a relationship between the content of fluorine and phosporus in many British coals. Thus it should be possible to anticipate likely fluorine-rich coals from existing data giving phosphorus content. Behavior of the fluorine compounds of coal was compared with that of 12 fluoride-phosphate minerals in sink-float separations and solvent ex-

Jan 1, 1958

By David J. Dunn

At a time when mill availability is at a premium, production costs are rising, and lead time for mill liner casting is a year or more, mill liner design is an important factor in ore grinding. Testing and selection of the optimum liner profile for a given set of mill operating conditions can improve mill capacity, reduce liner wear rate, and lengthen liner life. The mill liner that grinds best, lasts the longest, and costs the least is a necessity for economic mill operation. After testing four mill liner profiles for 3.96 X 3.65-m (13 x 12-ft) overflow ball mills, Climax Molybdenum Co. found that an improved design increased mill tonnage by 2.72 t/h (3 stph) while reducing finish grind by 1.7% minus 100-mesh, reduced liner wear rate, and almost doubled liner life.

Jan 12, 1976

By Lawrence H. Van Vlack

DISCUSSION, H. L. Burghoff presiding C. S. Smith (University of Chicago, Chicago)—The author is to be congratulated on his valuable contribution to the extremely meager absolute data on interface energies in metallic systems. It is interesting to note that the ratio between a and r iron boundary energies is approximately the same in the quaternary alloy with silicon, carbon, and sulphur as in the binary Cu-Fe alloy. A value for the copper grain boundary energy can be obtained from the author's data, Tables IV and VI, by utilizing the energy ratios of the following pairs of interfaces: copper-sulphide/copper, copper y iron, y iron/y iron, y iron/ copper, and copper/copper. This gives a value of 595 erg per sq cm for the free energy of the copper grain boundary. Despite this circuitous route and the assumption that the y iron boundary is identical in alloys with and without sulphur and does not change between 1105" and 100O°C, this figure is in remarkably close agreement with other values of the copper boundary energy, obtained by equilibration against lead and against the free copper surface. It therefore appears either that impurities do not greatly affect the grain boundary energies or that boundaries in even nominally pure metals are already sufficiently contaminated so that further change has little effect.

Jan 1, 1952

THE following employment items are made available to AIME members on a nonprofit basis by the Engineering Societies Personnel Service, Inc., operating in cooperation with the Four Founder Societies. Local offices of the Personnel Service are at 8 W. 40th St., New York 18; 100 Farnsworth Ave., Detroit; 57 Post St., Son Francisco; 84 E. Randolph St., Chicago 1. Applicants should address all mail to the proper key numbers in care of the New York office and include 6c in stomps for forwarding and returning application. The applicant agrees, if placed in a position by means of the Service, to pay the placement fee listed by the Service. AIME members may secure a weekly bulletin of positions available for $3.50 a quarter, $12 a year. MEN AVAILABLE Sales Engineer, 37, seven years experience Europe and Latin America both in underground work and administrative and sales work; speaks fluent Spanish, Portuguese, French. Desires responsible position preferably export in U. S. M-692. Superintendent, 46, married. Experience covers mining and metallurgy as mining engineer and as general superintendent; metallurgy of leaching, flotation, cyanidation; development, construction, operation. Presently available. Prefer U.S.A. M-693-333-E-1-San Francisco. Mine Manager, Superintendent, Consultant, 61, married. Design and erection of mining and mill plants-examinations. Many years as superintendent, manager, consultant, designer and builder of mining plants, flotation mills, concentration mills. Available one month's notice. Prefer U. S. but foreign acceptable if good climate. M-695-4211-E-9-San Francisco.

Jan 1, 1952

By B. Ramaswami

INTERNAL oxidation occurs readily in silver due to the rapid diffusion of oxygen in silver.' It has a marked effect on creep in polycrystalline silver2 and raises the critical resolved shear stress in single crystals of silver.3 However, the effect of oxygen on the work-hardening parameters of silver is not known. It is the aim of this paper to describe the effect of internal oxidation on the work-hardening characteristics of single crystals of silver and an Ag-0.1 at. pct A1 alloy. The materials used were: 99.99 pct Ag from Handy and Harman and 99.993+ pct A1 from Alcoa. Single crystals, 6 mm by 6 mm in cross section of silver and Ag-0.1 at. pct A1 of mo.5 orientation, i.e., the orientation with the Schmidt factor m = 0.5. were grown by the Chalmers technique.4 One set of specimens, referred to herein as oxidized specimens, was annealed at 940°C for 24 hr in a muffle furnace, in air, and furnace-cooled to room temperature. Another set of specimens, referred to as nonoxidized specimens, was annealed in oxygen-free helium at 940°C for 24 hr and furnace-cooled over a period of 7 hr to room temperature. The annealed single crystals were tested at room temperature in a floor-model Instron testing machine. The results are presented in Figs. 1 and 2. A

Jan 1, 1965

By E. J. Westerman

Prealloyed powders of nickel-base superalloys were sintered to almost theoretical density in short sinterilzg times. It was ascertained that the rapid densification was caused by a small amount of liquid phase at the grain boundaries, which apparently ovriginated by incipient melting at temperatures considerably below those at which macroscopic melting of the compacts occurred. An increase in the quantity of liquid phase present during sintering-, caused by an increase in the sintering temperature, increased the densification rate, but resulted in a decrease in the room temperature tensile propevties. NICKEL-base superalloys, which presently comprise an important group of high temperature alloys, are difficult to fabricate by the forging, casting, and machining operations presently used. As it was felt that fabrication by powder metallurgical techniques might offer advantages in the production of super-alloy parts, a basic investigation of the most important process in the sequence of powder metallurgical operations, the sintering process, was undertaken on Rene 41, Udirnet 500, and Nimonic 90 and 100 powders. These alloys age harden by the precipitation of the ? Ni, rA1,Ti) phase. Nickel-base superalloys of the Nimonic type have been fabricated by powder metallurgical methods, and their mechanical properties reported in detail.' Other alloys for high temperature service which have been fabricated by powder metallurgical methods include a Co-base alloy of the Vitallium type;2,3 alloys with a Co-Ni-Fe-Cr base;4 stainless steels;5'6 Cr-W-Co alloys;" and a Co-base alloy, X-40.8 METAL POWDERS The superalloy powders investigated were: a) a prealloyed at.omized Rene 41 powder; b) a prealloyed atomized Udirnet 500 powder; c) a prealloyed atom-

Jan 1, 1962

By W. F. Chiao, R. B. Gordon

Tile sharp-yield point found in magnesium crystals in the solulion-treated and aged condition is studied by dislocation internal-friction experiments. The results show that the sharp yield is not file to the sudden release of pinned dislocations hut is movc likely due to the rapid multiplication of an initially small number of dislocations. Recovery or the dislocation internal friction after deformation is also studied. This yecovery results from the re-pinning of dislocations by a solute, presumably nitrogen, which moves with a relatively small activation energy. SHARP-yield points, when they occur, are a striking feature of the stress-strain curve generated during a tensile test. Although commonly associated with steel, sharp yielding has been found in a variety of metallic and nonmetallic crystalline materials. In particular, sharp-yield points have been found in zinc"' and cadmium3 containing nitrogen. With this background, Geiselman and Guy4 investigated the tensile properties of magnesium single crystals containing nitrogen to see if sharp yielding also occurs in this system. They found that sharp yields did indeed occur in solution-treated and aged specimens tested at elevated temperature but were not able to give conclusive proof that the sharp yield was caused by nitrogen, a yield drop being observed even in their purest crystals. Sharp-yield points have also been found in various polycrystalline magnesium alloys.7'8 In the study of the sharp-yield phenomenon it is desired to observe the behavior of dislocations in the earliest stages of the deformation process. Internal-friction experiments are useful for this purpose because dislocation damping is sensitive to the mobility of free-dislocation segments. At low strain amplitudes the damping, A, due to the the forced vibration of dislocation segments of average length L is ? =KAL4 [1] where A is the dislocation density and K, if the applied frequency is well below the resonant frequency of the dislocation segments? is a constant for the sample under observation.5 Dislocation damping, because of the fourth-power dependence on L, is particularly sensitive to the creation of free-dislocation segments during deformation. Since sharp yielding is associated with the sudden release of pinned-dislocation segments, marked changes in the dislocation damping are expected at the yield point.6 The use of the dislocation-damping observations to help elucidate the incompletely understood mechanism of yielding in magnesium is the primary objective of the experiments reported here. PROCEDURE Many investigations have shown that very marked and rapid changes occur in the dislocation damping of of a deformed material as soon as the straining is stopped.5 It was quite essential, then, for the purpose of this investigation, to make the damping measurements during the deformation of the samples. This can only be accomplished through the use of the ultrasonic-pulse method. In this method traveling sound-wave pulses are used and, in contrast to resonating-bar methods, only the sample ends are set in vibration. Thus, the sample can be gripped along its sides in the tensile-test machine without disturbing the damping measurements. In the pulse method, the decrease in the amplitude of a sound pulse is measured as it travels back and forth through the sample. If A is the amplitude after traversing a distance x and A. is the initial amplitude, A=Aoe-ax [2] and a is called the attenuation. It is commonly measured either in units of cm-I or as db per µ sec. The observed attenuation in a metal sample is due to a number of causes. These include scattering by grain boundaries and impurity particles, thermo-elastic damping, diffraction effects, stress-induced ordering of solute atoms, and dislocation damping. The total observed attenuation in a given sample usually cannot be resolved into these various components, but changes in a due solely to changes in dislocation damping can be accurately determined, provided the experiment is arranged so that all other sources of damping are held constant. It is desired to reduce the extraneous sources of attenuation to a minimum and for this reason the experiments are done on single crystals of high purity. Magnesium crystals offer the further advantage that, when properly oriented, only a single set of slip planes is active during deformation. Crystal Preparation. The method of sample preparation is similar to that of Geiselman and Guy.4 The starting material was high-purity, sublimed magnesium rod supplied by the Dow Chemical Co. Melting under Dow 310 flux was used to reduce the nitrogen content of the starting material: the fluxing was done under an argon atmosphere and the

Jan 1, 1965

By J. H. Mallery, J. H. Keeler

THE crystal structure of Zral, the compound richest in zirconium (91.03 pct Zr by weight) in the system Zr-Al, has been found to be ordered face-centered-cubic. This compound is of particular interest, since it is encountered as the precipitated phase in potentially useful zirconium-rich alloys. It forms peritectoidally from body-centered-cubic zirconium and Zr,Al at about 975°C. The Zr-A1 constitution diagram has been reported by McPherson and Hansen.' For the primary determination a 100 g ingot was prepared by arc-melting in a water-cooled copper crucible under purified argon. The raw materials were crystal-bar zirconium (a purity of better than 99.7 pct) and spectroscopically pure aluminum. The ingot was double melted, examined metallographi-cally, and found to be quite uniform as shown in Fig. 1. The hardness of the as-cast button was VHN 390 to 445. A 20 mil diam specimen was prepared from annealed (900°C) filings of Zr,Al. The specimen was mounted in a 5 cm radius powder camera and an 8 hr exposure was taken using copper radiation with a nickel filter. The structure of the compound Zral was found to be ordered face-centered-cubic of the Cuau type, with an a,, value of 4.37220.003A. Its calculated density is 5.976e0.013 g per cu cm. The relative intensities for the lines were calculated using the formula 1+cos2 20 I oc----------------- • p • /F7 sin2 0 cos 0 1 + COS' 20 where----------------is the Lorentz polarization fac- sin2 0 cos 0 tor, p is the multiplicity factor, and F is the structure factor. The X-ray data are given in Table I. The compound has exhibited plasticity when present as particles in a matrix of a zirconium. During hot working at about 900°C, the compound has been found to deform plastically to the extent that some of the particles exhibit a length-to-width ratio greater than 4:1 as shown in Fig. 2. In answer to the discussion of ref. 1, McPherson and Hansen pointed out that the compound may be cold rolled and reduced as much as 33 pct. Zr,Al has also been found2 under certain conditions to precipitate in lamellar form at grain boundaries of the a phase of hexagonal-close-packed zirconium. Acknowledgment This work was carried out under Contract W-31-109-Eng 52 for the United States Atomic Energy Commission.

Jan 1, 1956

By Rex E. Cheek, Donald E. Menzie

The fluid mapper, a model relatively new to the petroleum industry, was used to study the effect of various mobility ratios on the areal sweepout efficiency for two typical spacing patterns. The experiments indicated the areal sweepout for the five-spot pattern varied from 51.8 per cent at a mobility ratio of 0.093 to 89.1 per cent for a ratio of 24.4. In the direct line-drive pattern, the areal sweepout varied from 58.7 per cent at a mobility ratio of 0.089 to 92.0 per cent at a ratio of 24.8. The fluid mapper may prove useful to determine quickly the effective areal sweepout for any well spacing. INTRODUCTION The effect of the mobility ratio on the areal sweepout efficiency during primary depletion of a water drive reservoir and during secondary recovery operations has recently become more widely recognized The mobility ratio, M, is defined as: _ kjp (displaced fluid) k/u (displacing fluid) where k = effective permeability u = viscosity When the displacing fluid is miscible with the displaced fluid, the permeabilities are equal and the mobility ratio may be expressed as a ratio of viscosities: u (displacing fluid) u (displaced fluid) The mathematical analysis for calculating the areal sweepout efficiency with mobility ratio other than unity is quite tedious.5,11 An experimental method by using a potentiometric model2 in a step-wise manner and in using an X-ray shadowgraph model3,12 with continuous fluid flow has been published. Several types of models have been used to study oil and gas reservoir performance. These models may be classified as physical, electrolytic, potentiometric, X-ray shadowgraph, and fluid mapper. The X-ray shadowgraph and fluid mapper are models relatively new to petroleum engineering and have not been used extensively for specific applications. The theory of the fluid mapper indicates it may be adapted to a study of areal sweepout efficiencies for various mobility ratios as well as other complex problems in petroleum engineering. The use of the model and results obtained when using displacing and displaced fluids of equal densities but different viscosities are discussed. FLUID MAPPER DEVELOPMENT H. S. Hele-ShawV eveloped a fluid mapper model based on the hydrodynamic theory. This theory is that in the steady flow of a viscous fluid between horizontal parallel plates spaced a very small distance apart, the effect of viscous shear is of such magnitude in the vertical plane that the motion in the horizontal plane is practically undisbrted streamline flow. Techniques developed by Hele-Shaw were not expanded and no additional developments in fluid mapper models were forthcoming until A. D. Moore, University of Michigan, published a series of papers starting in 1949, which describe the construction of a flexible and inexpensive model'h nd the fluid mapper technique for the solution of certain problems.' The essential components of the fluid mapper as developed by Moore are::.ln 1. A base slab. made of dental stone (calcium sulphate and water). which is shaped to represent the prototype. 2. Plate glass slightly larger than the slab and spaced

Jan 1, 1956

By Robert M. Betts

The Cornucopia district is situated in northeastern Oregon 25 miles from the Snake River branch of the Oregon Short Line R.R. and 75 miles northeast of Baker City, in the Wallowa Mountains. The formation is principally granodiorite, which has intruded much older rocks locally known as greenstone, and which are probably altered schists. In the upper horizons of the veins, greenstone is found as inclusions in the granitic mass. Both of these formations have been cut by numerous basalt, aplite, and porphyry dikes. Veins of the district are the result of faulting and the consequent crushing of the wall rock. The ore has been deposited irregularly along these faults and formed a lenticular type of vein. The ore varies in width from a few inches to 20 ft.; the average stoping width is about 5 ft. As the basaltic dikes are subsequent to the ore deposition, they are at times a hindrance in development and mining operations; on the other hand, a dike which has followed a vein as a line of least resistance often serves as a good mall in place of the crushed, rather loose granite. The veins generally strike northeast-southwest and dip about 35" to the west. Orebodies are from 100 to 300 ft. in length and about the same in height. The lenses are irregular; inclusions of wall rock are common in the ore and are a factor in reducing the grade. The ores are quartz, carrying some free gold near the surface, but the metals for the most part are in iron sulfides, sometimes associated with chalcopyrite. The gold and silver are in a mechanical combination with the iron, which requires find grinding to liberate them. The ratio of silver to gold is 5 to 1, by weight. Development The Cornucopia Mines Co. owns, and operated until 1920, two mines and two mills of 100 tons capacity each. The sustained high costs and labor shortage, however, necessitated the abandoning of the Union mine, the oldest in the district. Two crosscut tunnels were then started, first, to cut the Last Chance vein at a much lower horizon and, second, to prospect two parallel veins. The ore from the Last Chance vein will go to the old Union mill and the ore from the new veins to the Last Chance mill.

Jan 1, 1925

By T. V. Philip, Paul A. Beck

IN a previous note1 it was pointed out that the available information suggests a distinct correlation between the occurrence of the CsCl-type ordered structures formed in equi-atomic binary alloys of transition elements and the location of the components in the periodic table. A definite increase in the bond strength between unlike atoms, as compared with that between like atoms, is indicated when, in binary alloys of iron group elements, the other component is changed from chromium to vanadium or tantalum, to titanium. Laves and Wallbaum,2 eported a CsCl-type ordered structure for the stable intermediate phase at the equi-atomic composition in the Ti-Fe system (and also in the Ti-Ru and Ti-Os systems). On the other hand, Tagaya, Nenno, and Nishiyama8 found no ordering of this kind in the body-centered-cubic solid solutions in the Cr-Fe system. It was concluded' that the occurrence of a CsC1-type ordered phase of intermediate stability may be expected in the V-Fe system. Preliminary results were described: suggesting that at least some degree of order does exist in the equi-atomic alloy VFe, annealed at 1200° C and quenched in cold water. Using CrK radiation, at least one weak superlattice line was found in the X-ray diffraction pattern which could be indexed as (100). and which disappeared, as expected, when FeK radiation was used. It was found more recently that the impurity phase (presumably VN), previously giving rise to additional X-ray diffraction lines and thus preventing definite indentification of the (111) superlattice line,' can be eliminated by preparing the alloy by arc melting in a helium atmosphere. The alloy specimen melted in this manner had clean surfaces and showed very littte, if any, nitride phase in the microstructure after annealing in vacuum at 1250°C and quenching. The relative intensity of the (100). superlattice line with CrK radiation was greatly increased and, in addition, a fairly strong (Ill) , superlattice line and even a detectable (210) , super- lattice line was obtained, when the powder produced by filing from the 1250°C annealed and quenched specimen was reannealed in vacuum at 625°C for 1 hr. By using a cellulose acetate film as a filter in front of the photographic film in order to absorb the soft radiation resulting from air fluorescence, the background intensity could be reduced considerably in relation to the intensity of the diffraction lines. All three superlattice lines, (100),, (111)., and (210)a, disappeared, as expected, when a radiation other than CrK, was used.1 For the powder reannealed at 625ºC, the strongest lines of the s pattern also appeared weakly, indicating that during an: nealing at 625°C a small amount of transformation took place from the body-centered-cubic to the u phase. However, since all superlattice lines to be expected in the 0 angle range used were actually very clearly present, it was evident that the high temperature body-centered-cubic phase had transformed into a CsCl-type ordered structure before much s phase could form. Reannealing filings for 1 hr at 700°C resulted in complete transformation into the u phase. After 1 hr at 650°C the transformation into IT was not quite complete, the strongest body-centered-cubic diffraction lines were still present, although fairly weak, and only the (100), super-lattice line was detectable (extremely weak). These findings not only confirm the previous conclusionsL as to the existence of a CsCl-type ordered structure in the Fe-V system, but they also indicate that this metastable ordered structure forms at about 600°C preceding the formation of the stable s phase, while at 1250°C the disordered body-centered-cubic phase is stable. The faint (loo) , super-lattice line previously observed in specimens quenched from 1200°C was probably due to the fact that the quenching of the powder in an evacuated fuse:! quartz capsule was not fast enough to prevent completely the ordering reaction on cooling. The present results conform with the suggestion that the A-B bond, in relation to the A-A and B-B bonds, increases in strength from CrFe to VFe to TiFc. It is, therefore, of interest to compare the measured values of the average atomic diameter for these three alloys with the corresponding average atomic diameters calculated from the atomic radii of the elements concerned. ASSUming A-B contacts

Jan 1, 1958

By A. Andreas

New Mexico retained its position in 1938 as the sixth largest oil-producing state, with a total production of 35,510,176 bbl. This was 2,875,598 bbl. less than the 1937 production of 38,485,774 bbl., or a decrease of 0.077 per cent, which was caused by the lack of pipe-line facilities and storage at the pipe-line terminals. The production for Lea County (excluding Maljamar) was 32,926,788 bbl.; for Eddy County (including Maljamar) was 2,225,411 bbl.; and for northwestern New Mexico (San Juan and McKinley Counties), 357,977 bbl. The average daily nonmarginal well allowable for Lea County on Jan. 1, 1938, was 65 bbl. At the close of the year it was 49 bbl. The average daily pipe-line runs for domestic consumption were less than the state allowables recommended by the United States Bureau of Mines. There was a demand for Artesia crude for foreign export, which if included in the daily production for New Mexico would be slightly in excess of the daily production recommended for New Mexico by the Bureau of Mines. The daily average production for the year was 97,329 barrels. There were 622 completions in the state, of which 520 were oil wells; 16 hydrocarbon gas wells; 5 carbon dioxide gas wells, and 81 dry holes. Of the dry holes 38 were in or near-by proven fields and the remainder, 43, were wildcats. Five new fields were discovered in New Mexico during 1938, three in Lea County and two in Eddy County. Southeastern New Mexico Lea County.—The Monumcnt field was the largest producing field in Lea County, with 9,440,334 bbl., and was closely followed by the Eunice field with 8,872,335 bbl. The Hobbs field was third with 5,010,414 bbl. The greatest activity in Lea County was in the Vacuum pool, with 129 completions, of which 126 were oil wells and three were dry holes. The Texas Company completed its Corbin NO. 1 in the KW 1/4 SW1/4 sec. 10, T. 18 S., R. 33 E. in August. This well was drilled to a depth of 5118 ft. in a white sand, encountering salt water. It was plugged back to 4315 ft, and pumped 43 bbl. of 36" gravity oil in 12 hr. It was approximately 6 miles southwest of the closest production in the Vacuum

Jan 1, 1939

By A. Andreas

New Mexico retained its position in 1938 as the sixth largest oil-producing state, with a total production of 35,510,176 bbl. This was 2,875,598 bbl. less than the 1937 production of 38,485,774 bbl., or a decrease of 0.077 per cent, which was caused by the lack of pipe-line facilities and storage at the pipe-line terminals. The production for Lea County (excluding Maljamar) was 32,926,788 bbl.; for Eddy County (including Maljamar) was 2,225,411 bbl.; and for northwestern New Mexico (San Juan and McKinley Counties), 357,977 bbl. The average daily nonmarginal well allowable for Lea County on Jan. 1, 1938, was 65 bbl. At the close of the year it was 49 bbl. The average daily pipe-line runs for domestic consumption were less than the state allowables recommended by the United States Bureau of Mines. There was a demand for Artesia crude for foreign export, which if included in the daily production for New Mexico would be slightly in excess of the daily production recommended for New Mexico by the Bureau of Mines. The daily average production for the year was 97,329 barrels. There were 622 completions in the state, of which 520 were oil wells; 16 hydrocarbon gas wells; 5 carbon dioxide gas wells, and 81 dry holes. Of the dry holes 38 were in or near-by proven fields and the remainder, 43, were wildcats. Five new fields were discovered in New Mexico during 1938, three in Lea County and two in Eddy County. Southeastern New Mexico Lea County.—The Monumcnt field was the largest producing field in Lea County, with 9,440,334 bbl., and was closely followed by the Eunice field with 8,872,335 bbl. The Hobbs field was third with 5,010,414 bbl. The greatest activity in Lea County was in the Vacuum pool, with 129 completions, of which 126 were oil wells and three were dry holes. The Texas Company completed its Corbin NO. 1 in the KW 1/4 SW1/4 sec. 10, T. 18 S., R. 33 E. in August. This well was drilled to a depth of 5118 ft. in a white sand, encountering salt water. It was plugged back to 4315 ft, and pumped 43 bbl. of 36" gravity oil in 12 hr. It was approximately 6 miles southwest of the closest production in the Vacuum

Jan 1, 1939

BRANCH COUNCILS MINING BRANCH R M Foose, Chairman (Industrial Minerals) Carroll A Garner (Coal) J V Beall, Eastern Secretary A B Cunmins (Industrial Minerals) R E O'Brien, Western Secretary E D Gardner (Mining, Geology, and Geophysics) Carroll F Hardy (Coal) Philip J Shenon (Mining, Geology, and Geophysics) R E Byler (Minerals Beneficiation) A C. Callen (Mineral Industry Education) Grover J Bolt (Minerals Beneficiation) R J Lund (Mineral Economics)

Jan 1, 1951

By O. K. Miniato, L. Massé, K. Nobe, J. S. Aronofsky, W. F. 213-000-000-016 Seyer

MUCH work has been done dealing with the effect of mechanical stress on electrode potential in an electrochemical system. The contradictory nature of the experimental results indicates the complexity of the problem although thermodynamic considerations show that a simple relationshir, should exist. In those systems where a gas was the electromotive active substance satisfactory agreement between theory and practice has been found. Des Coudres' found this to be so even when the active substance of the electrode, in this case mercury, was in the liquid state. In contrast, attempts to correlate theory and experiment for the solid state have met with a very limited success. The early workers in this field, Andrews,2 Walker and Dill3 used iron, certainly one of the most reactive of metals. Others have made use of less active metals such as copper and nickel. Recently Fryxell and Nachtrieb4 investigated the electrochemical behavior of gold and silver under both tensile and compressive stresses and concluded that it was doubtful whether true stress potentials could ever be measured. Much of the lack of success to measure the thermodynamic stress potential can be ascribed to the presence or formation of a complex film on the metal surface in contact with the electrolyte. Further, the theoretical stress potential is very small and therefore difficult to measure directly. Thus the calculated emf between a 24 B & S gage cold-drawn copper wire stressed with a weight of 1 kg and an unstressed portion of the same wire is only 2.60 X 10"7 volts. This is very small compared to that which can be produced by chemical reactions at the metal electrolyte interface which in turn can be so large as to mask completely the stress potential. Hence in this type of measurement all chemical side effects must be eliminated or reduced as much as possible. It was for this reason that the system copper-sodium chloride solution was selected for study. INSTRUMENTATION In the many preliminary experiments conducted, two major difficulties were encountered. The first was to measure the small electro-potentials to be expected and the second to obtain a suitable electrode surface. The conventional potentiometric method was found to be unsatisfactory for measuring the small emf expected. However, by using an L & N No. 2290 galvanometer having a resistance of 915 ohms consistent measurements were possible. The reference electrode was always the unstressed one made from the same sample of wire. The steady current flow was approximately 10-8 amp. Lewis and Randell5 have stated that for currents of the order of 10-8, if there is no sensible polarization, the measured emf may be taken as a reversible one. To check the galvanomenter readings an alternative method was devised to measure the potential difference between the wires. This involved a Liston-Falb d-c breaker amplifier model 10, an L & N k-2 potentiometer and a moving-coil galvanometer having a sensitivity greater than 0.1 µv (microvolt) per mm. To increase further the output voltage of the amplifier a d-c amplifier, model B. L.-932 was introduced into the circuit. This amplifier was in turn connected to a Brush recorder which had been calibrated previously by the test signals from the Liston-Falb instrument. These test voltages employed took into account the impedance of the input current. Unfortunately, this method had too low a sensitivity for measurement below 10 µv. Above this value the voltage agreed reasonably well with those obtained directly by the simple galvanometer method. The main advantage of the amplifier setup was that one did not have to wait until no deflection occurred on the galvanometer in the circuit when first exposing the wires to the solu-

Jan 1, 1959