By Xueming Lv

The rotary kiln-electric furnace (RKEF) process is the main method for producing ferronickel from nickel laterite ore. However, this process is energy intensive as it involves several high temperature steps. Therefore, a novel process is proposed to directly produce ferronickel from nickel laterite ore by semi-molten reduction, which is expected to be realized in a rotary hearth furnace (RHF). The RHF process is able to shorten the flow sheet, decrease the reaction temperature as well as reduce energy consumption. In this study, the influence of basicity on reduction of nickel laterite ore was investigated. The results showed that it is possible to produce the ferronickel nugget directly at 1400 °C when the quaternary basicity [(mCaO + mMgO)/(mSiO2 + mAl2O3)] was fixed at 0.60. Under this experimental condition, the grade and the recovery ratio of nickel reached 11.53% and 98.59%, and the grade and recovery ratio of Fe were 84.16% and 68.72%, respectively.

By A. C. Neiva

An energy-dispersive x-ray fluorescence spectrometer was assembled with the aim of analysing alloys and corrosion products of artistic, ethnological and archaeological pieces. The spectrometer is semiportable and consists basically of an 60kV/1.5mA X-ray tube with W anode and a Si-drift X-ray detector with Peltier cooling, with no need of liquid nitrogen. It was used for the analysis of the alloys and occasional corrosion products of several metallic pre-Hispanic pieces of the Museum of Ethnology and Archaeology of the University of São Paulo. Special care was taken to account for the contribution of spurious radiation from both the Pb primary collimator and the Zr detector collimator. The main components of most alloys were Au, Ag and Cu, but Pb, Ca, Fe and other elements were also identified. The characterization of the alloys and corrosion products is important for the subsequent conservation of the collection.

Jan 1, 2006

By Qingzhu Li

The brewing industry byproduct, spent grain (SG), was evaluated for its ability to adsorb Ag(I) from aqueous solutions. Ag(I) adsorption was dependent on solution pH, contact time, adsorbent dose, initial Ag(I) concentration and temperature. The kinetic data were well described by pseudo-second-order kinetic model, indicating that chemical adsorption was the rate-controlling step. The equilibrium data followed Freundlich isotherm rather than Langmuir isotherm, suggesting heterogenity of the adsorption sites on spent grain. Ag(I) desorbed from Ag(I)-loaded spent grain was also evaluated in this study. HCl, NaOH, Na2S2O3 and ultrapure water were chosen as eluants and desorbed Ag(I)-loaded spent grain for 30min, Ag(I)-loaded spent grain desorbed in 0.1M Na2S2O3 exhibited higher elution efficiency as compared with other eluants. The results indicated that application of spent grain for adsorption and recovery of silver from aqueous solutions was feasible.

Jan 1, 2009

By Miguel N. Herrera

The electrochemistry of coal pyrite is relevant to coal desulfurization by chemical or bacterial leaching, flotation and oil agglomeration. The electrochemical behavior of polished and etched Upper Freeport and Pittsburgh coal pyrite samples was investigated from pH 1.0 to 10.5. The open-circuit potentials decreased with increasing pH, as expected, but were well above the thermodynamic stability region of pyrite, and decreased with time. Cyclic voltammetry revealed behavior highly sensitive to pH and scan rate (2.0 and 20.0 mV/s). The behavior on the first cycle was always substantially different from that on subsequent cycles. The anodic and cathodic reactions were correlated with the Eh-pH diagram for the Fe-S-H20 system to identify the reactions occurring at different pH values. There was also evidence that the buffers used to maintain basic pH values are themselves electrochemically active, which should be considered in interpreting many earlier electrochemical studies of sulfide minerals.

Jan 1, 1994

By J. N. Hartley

Samples of ash from the May 18, 1980, eruption of Mt. St. Helens Were collected from several locations in eastern Washington and Montana. The optical microscope and the combined scanning electron microscope with energy dispersive x-ray microprobe were used to determine the composition and mineralogical characteristics of the samples. In addition, a quantitative image analyzer was used to examine the particle size distribution, and x-ray diffraction was used to identify major minerals. Both polished sections and ultra thin sections (less than 5 ~m in thickness) were prepared to study the mineralogical characteristics. The use of ultra thin sections provided access to microstructural detail. Mineralogically, the samples ranged from almost totally glassy to almost totally crystalline. Crystal-line samples were dominated by plagioclase feldspar (andesine) and ortho-pyroxene (hypersthene) with smaller amounts of titaniferous magnetite and hornblende. Nearly all the samples contained from less than 1 to 3 wt% free crystalline silica (quartz, trydimite, or cristobalite).

Jan 1, 1981

By P. N. Anyalebechi

The effects of application of steady and pulsed electric current on the cast microstructures of ingots of a 7050 type aluminum alloy have been experimentally investigated over a solidification rate range of 0.1-10 K/s. This involved the application of an electric current of 465-930 mA/cm2 of melt surface area to laboratory-size ingots solidified in a unidirectional manner. Within the ranges of electric current density and solidification rate investigated, the applied electric current reduced the average dendrite, grain, and second-phase particle size. It also made the size distribution of the second-phase particles more uniform. The mechanism for the observed refinement of the cast microstructure by the applied electric current is not well understood. The potential effects of heat-induced local convections, shear stress-induced fragmentation of dendrites, increased temperature gradient due to Joule heating and the thermal and constitutional supercooling engendered by Peltier, Thompson, and Joule heating are discussed.

Jan 1, 2009

By Jie Li, Shu Yang, Zhongliang Tian, Xun Hu, Yanqing Lai

The purity of the electrolyte has an important influence on the content of the impurities in electrodeposited silicon. In this paper, effects of electrolysis temperature, current density and the time on the concentrations of two important impurities: phosphorus and iron in the electrolyte were investigated during the purification of Na3AlF6-10%K2SiF6-AlF3 melt. It was observed that the concentrations of P and Fe in the electrolyte decreased with the electrolysis temperature, current density and the electrolysis time increasing. X-ray fluorescence (XRF) of the electrolyte shows that the concentrations of P and Fe decrease from 4.2ppmw to 1.3ppmw and 204.0ppmw to 42.6ppmw, respectively. The removal rates of P and Fe are 69.08% and 79.12% when the electrolysis was performed for the duration of 3 hours and at a current density of 20mA·cm-2 while the operating temperature was 1225K.

Jan 1, 2015

By M. Z. Mubarok

Effect of single addition of a lignin-based biopolymer additive, DP 2782, at various dosages as well as in combination with thiourea on cathode polarization during copper deposition was investigated by performing potentiodynamic and galvanostatic measurements using a potentiostat. The result of electrochemical measurements was compared with the behaviour of cathode deposition with glue and thiourea additives. Surface micro-appearance of the copper deposit after 1 h galvanostatic scan under current density of 330 A/m2 and various additive type and dosage was evaluated by scanning electron microscopy (SEM) examination. It was found that the addition of 2.5 mg/l biopolymer gave sufficiently polarizing effect of copper deposition. SEM examination of the cathode surface after galvanostatic scan revealed that the combination of the biopolymer with thiourea (2.5 and 3.5 mg/l) resulted in a compact deposit which is comparable with that resulted from the test with glue and thiourea.

By Felipe Daroch, Maria C. Ruiz, Rafael Padilla

Copper concentrates with high arsenic contents must be pretreated before conventional smelting to prevent environmental pollution with arsenic compounds. In this work, experimental results concerning the selective removal of arsenic and antimony from copper concentrates are presented. The process consists of an alkaline digestion using concentrated NaHS-NaOH solutions to transform the arsenic and antimony sulfides into soluble compounds. A water leaching follows the digestion to dissolve the arsenic and antimony, leaving clean copper sulfide solid residues. The laboratory scale tests were carried out using a copper–arsenic concentrate with 15.05% As and 1.42% Sb. The results showed that the most important digestion variables were temperature and concentrations of NaHS and NaOH. Over 97% of arsenic and 92% of antimony could be removed in 10 min of digestion using 8.9 M NaOH and 100% excess of NaHS at 80 °C. The subsequent water leaching was performed at 80°C for 20 min.

Jan 1, 2015

By I. Gaballah

Cadmium is toxic to plant, animals and humans. The council directive of the European Communities No 8315 13lEEC has fixed an upper limit of 200 ppb for the release of cadmium in industrial effluents. The conventional method of neutralization/prccipitation ( NIP ) is inefficient to reach this limit. The objective of this study is to test the efficiency of the trees modified bark to remove cadmium cations from industrial effluents after the conventional treatment by NIP. Laboratory scale tests with synthetic solutions show that the cadmium removal depends upon pH and initial concentration. About 99.9 %, 99 % and 96 % of the metal are removed from synthetic solutions containing 10, 100 and 1000 ppm respectively. Pilot plant trials ( 1 m3 ) with an industrial effluent bearing about 500 ppb of cadmium lead to the almost complete elimination of the cadmium ( final concentration is lower than the analytical detection limits < 20 ppb ).

Jan 1, 1994

By O. P. Pandey, Rama Arora, Gurmel Singh, Suresh Kumar

The tribological behavior of Dual Particles Size (DPS) rutile reinforced LM13 alloy composite was investigated under varying applied pressure from 125 kPa to 625 kPa at a constant sliding speed of 1.6 m/s. In the present studies, 15 wt.% of rutile particles of different sizes (50-75 μm and 106-125 μm) are reinforced in the Al-12Si alloy (LM13) by liquid metallurgy route. Microhardness of the prepared samples was measured in different phases. Microstructure, wear mechanism and surface morphology of the wear surfaces and debris was observed under optical and scanning electron microscope. The change in wear behavior has been explained with reference to the observed EDS analysis of the wear track and debris. However, an interesting change in wear feature, mild to severe wear transition at critical pressure was noticed in wear behavior of the composite. The Al-DPS composite has immense potential to be used as a component material for tribological applications.

Jan 1, 2015

By Alan P. Prosser

The heap leaching of gold ores by cyanide solution was simulated by computer program. The program uses only basic m1neralogical and chemical data; no process testwork data, such as column leach results, are required. The simulation can be used to forecast the consequences of various changes before and during the testwork, design and operation stages of a particular ore-process system. Also, data about the state of different parts of the heap at various times help create an understanding of what is happening. The effects of mineralogical and process variables on the overall performance of the ?heap leaching process are illustrated. Comparisons are made to column leach tests and production data. The potential of the simulation strategy is discussed for making better use of operating experience and for suggesting specific research objectives. It has become clear that more attention should be paid to other metals that dissolve in the solution.

Jan 1, 1989

By Haydar Güneş

In this study, a hydrometallurgical process was evaluated for the recovery of Nd from a Nd-Fe-B magnet. Each leaching test was performed at the solid (weight) to liquid (volume) ratio of 1:50 and was mixed at 400 rpm at ambient temperature. The effects of 3 different acids (HCl, HNO3, and H2SO4) on the extraction of Nd were investigated and H2SO4 was found to be more effective than other acid solutions. Under the optimal conditions, pregnant leach solution was produced with H2SO4 for subsequent Nd precipitation testing. Each precipitation test was carried out using 100 mL of feed solution mixed at 600 rpm at 25°C. NaOH and H2C2O4 were used for Nd precipitation. The highest Nd was precipitated as Nd2(C2O4)3, 10H2O with C2H2O4 at 20 min.

A study of iron-removal from copper leachate by limestone precipitation followed by direct eltctrowinning of copper has been conducted. The influence of the process parameters: amount of precipitant, contact time, temperature, agitation intensity, solution acidity, and initial iron concentration on iron-removal was investigated. The effects of electrowinning time, cell voltage, solution acidity and temperature on electrowinning of copper were also investigated. The leachate contained 1.20 g/l cu2+ and 7.41 g/l total iron at pH 2.27. After contacting with 14 g/l precipitant for 2 hours, 97.5 % of the iron was attenuated and 98.4 % of the copper was recovered. With the following electrowinning conditions: 3 lead anodes, 3 stainless steel cathodes, 2.5 V, 39.41 A/m2 and 10.7 g/l H2S04, copper recovery-was 98.4 %. Purity of copper powder produced was greater than 99.0 %.

Jan 1, 1999

By K. C. Mills, P. N. Quested, A. P. Day, R. F. Brooks

"Methods have been developed to measure the physical properties of molten materials relevant to the fluid flow in high temperature processes. Data for the densities, viscosities and surface tensions of Al-, Ni- and Fe-based alloys are compared with (i) values for the pure metals and (ii) estimated values obtained from models making use of chemical composition of the alloy. Experimental values for metallurgical slags are also given and compared with estimated values.1 IntroductionPhysical property data has proved very useful in improving process control and product quality. For instance, in the continuous casting of steel the viscosity (TJ) of the mould flux is important since it determines (i) the optimum casting conditions, nVc = 2.5±1 dPas (m min-1) where V c is the casting speed and (ii) the level of slag entrapment (which leads to inclusions) in the metal. Thus data for properties like viscosity are exceedingly useful in understanding the process and the problems encountered and the causes of defects and problems.Another interesting development which has helped to increase our knowledge of processes and improve process control and product quality is the development of mathematical models of the fluid and heat flow in the process. These models have been developed to the stage where one of the prime requirements is for good physical property data for the industrial materials involved. Recently, Oxley [1] has shown that the use of reliable, experimental, property values for the commercial alloy in a commercial software package produced a significant improvement in the prediction of casting defects. Thus reliable property data are required for liquid metals but also for (i) liquid slags since many processes involve the use of a slag to refine and protect the metal or to lubricate the mould and (ii) refractories, sand and investment moulds."

Jan 1, 1999

By Yuri Gelfgat

"This paper presents some results of the investigation of the steady magnetic field influence on hydrodynamics and heat/mass transfer in processes of semiconductor single crystal growth (Si, Ge, InSn). The investigation employed mathematical and physical simulation techniques of relevant processes and full-scale experiments on growth facilities. A number of additional MHD phenomena have been found generated in the melt due to the rearrangement of flow pattern, the formation of specific convective cells, and the origin of MHD boundary and shift layer.IntroductionMagnetohydrodynamic (MHD) means of creating forces by contact-free methods in liquid conducting media have been widely used in the production of volume semiconducting single crystals. The goal of this method is to control convective transfer processes in the melt volume and on the crystallization front [1-3]. This is due to the sufficiently high conductivity of semiconductor melts (s = 104 /106 O1m-1 ) and an obvious relationship between the hydrodynamics in the melt and at interfaces and the conditions of formation of single crystals and their quality [ 1].All types of MHD effects rest upon the generation of volume electromagnetic forces in the melt by various means as well as on the possibility to direct them arbitrary in space and to adjust easily their absolute values. Fig. l presents different means how to implement MHD phenomena during single crystal growth. It should be emphasized that in all the modifications given in Fig. l additional energy introduced into the melt cannot influence directly the crystallization process since it is incomparable to the energy of molecular forces. Both the influence and efficiency of MHD means are determined solely by the change of motion, heat and mass transfer characteristics."

Jan 1, 1998

By Dai Yongnian

"The feasibility to vacuum distillation of a crude metal or an alloy was discussed. The equilibrium relationship between vapor phase and liquid phase in A-B system - - - - - PA/PB =BAa*/b has been derived. The separation coefficient, BA = rAPA/(rBPB) is a judgment criterion. By calculation PA/PB, the equilibrium composition diagram of vapor phase and liquid phase was drawn. By use of the equation derived by M. Olette, the relationship among the volatilization amounts of various impurities in a crude metal (yi) was further solved. 1-(X/100)= C =(1-Y1/100)1/02i . From yi value obtained in practice, 2i, Pi and then can be calcu-lated. The correct volatilization order of various impurities was obtained. These results can be applied to determine the practical conditions (temperture, vacuum degree, type of distilla¬tion furnace, times of distillation and control of product composition) in distillation of a crude metal or an alloy.INTRODUCTIONRefining and separation of various impurities from nonferrous crude metals by vacuum distillation have many the advantages of high metal recovery, impurities recovered in metallic state, flowsheet simplified, good enviromental protection, low operation costs and in complex equipment. So in recent years this method has been adopted widely.Vacuum distillation has also been studied and used in separation of various elements from non-ferrous alloys and the area of its application is being extended rapidly.At this situation, some problems have been put up: What kind of impurities can be removed from crude metals? What kind of alloys can be separated by vacuum distillation? In present paper, attemps have been made to answer these problems and combine with practical results to analyse some valuable data obtained from testwork on vacuum distillation of crude tin and Pb-Sn alloy."

Jan 1, 1988

By Ning Wang, Bing Xie, Hong-Yi Li

"Compared to traditional sodium roasting, calcified roast inhibits chlorine pollution. A vanadium extraction technique based on a calcified roast is especially suitable for vanadium slag with high calcium content. In this report, V205was extracted from vanadium slag by calcified roast followed by acid leaching and hydrolysis precipitation. In optimized conditions, the high silicon low vanadium slag was roasted at 850'C for 2 hours without CaO addition. The roasted materials were leached with 35 % H2SO4 in liquid/solid ratio of 5:1 (mL/g) at 95OC for 4 hours. The extraction of vanadium was as high as 97.66 %. These results are instructive to V2O5 production in industry.IntroductionVanadium slag is produced in converter, sodium salt roasting is the commonly used technique to extract vanadium. In sodium salt roasting, vanadium slag is roasted with sodium salts including sodium chloride and soda as additives, followed by leaching with acidic or basic solution [1]. However, in this process chloride reacts to produce corrosive gases including HC1 andCl2- SO2 and SO3 can also corrode equipment severely and are also an environmental contaminant. The low melting point of sodium salts leads to fusion agglomeration, which blocks vanadium oxidation and thus decreases the extraction rate of vanadium. A large amount of sodium salts consumed as roasting additives increases the production cost. Moreover, sodium salt roasting requires low CaO content in vanadium slag. When the CaO content increases to 1%, V2O5 extraction can amount to 4.7%-9% [2]. For vanadium slag with high CaO content, the sodium salt roasting technique leads to low vanadium extraction rate."

Jan 1, 2012

By W. Y. Kim, K. H. Song, K. Nakata

"The present study was carried out to evaluate the mechanical properties of friction stir welded Inconel 600/SS 400 lap joints. In this process, friction stir welding (FSW) was performed at a tool rotation speed of 200 rpm and welding speed of 100 mm1min, and argon gas was utilized to prevent surface oxidation during the welding. Application of FSW notably decreases the grain size of Inconel 600 alloy from 20 µm in the base material to 8 ~ in the stir zone. However, the grain size of SS 400 in the weld zone was slightly coarsened, when compared to the base material. Also, the hooking in the advancing side and the intermetal1ic compounds (M7C3) in the weld interface between Incone1 600 and SS 400 were well formed. These intermetallic compounds and hooking were effective to increase in mechanical properties such as tensile and peel strengths.IntroductionFriction stir welding (FSW), applicable welding process at solid state, has several advantages in defect suppression such as blow hole, segregation and cracking which mainly occurs in fusion welding [1, 2]. Notable grain refinement in the stir zone due to FSW can expect the outstanding increase in mechanical properties of the welds. In constructing the chemical and power plants, Ni base superal10ys have been used in many parts, moreover, fusion welding as construct method, such as gas tungsten arc welding, electron beam welding and laser welding, has been mainly used [3-5]. However, fusion welding has a limit in an increase in chemical and mechanical properties in the welds. Lately, Ni base superalloys to which FSW applied have been reported with notable enhancement in mechanical properties, which resulted from refined grains in the welds [6-10]. These researches showed the possibility in applying the FSW, directly."

Jan 1, 2012

By Tao Li

The development of DP(Dual Phase) steels and TRIP(Transformation Induced Plasticity) steels has received much attention in recent years due to their high strength and simultaneous good ductility, which provides the potential for weight reduce and resource savings on certain components in automobile or other industries. So a controlled rolling process was simulated in the present study by thermomechanical simulator (Gleeble 1500) for producing DP steels on a kind of low carbon steel containing a small amount of Si and Cr. F+M dual phase microstructures have been obtained during continuous cooling processes of a wide cooling rate range from 10°C /s to 60°C /s. The grain size of the dual phase steel developed can be refined to less than 5 m through the mechanism of deformation induced ferrite (DIF) transformation. The ultrafine ferritic grains are equiaxed with high-angle boundary, and the martensite islands of an average size less than 5m disperse uniformly in the ferrite matrix. The ultrafine martensite islands not only inhibit the growth of ultrafine ferritic grains and improve the bonding of F/M interface, but also increase remarkably the strain hardening rate in the processing of the present Dual-Phase steel. As a result, the tensile strength of ultrafine grained Dual-Phase steel reaches higher than 1000 MPa. The result shows that an ultrafine grained Dual-Phase steel of low carbon and low alloy is promised to exhibit desired F+M microstructure by means of this new TMCP process.

Jan 1, 2006