Search Documents

By Yusuke Kimura, Ken-ichi Yamaguchi

"Secondary materials have long been processed at the S-furnace of the Mitsubishi continuous copper smelting and converting process at Naoshima Smelter and Refinery. Intensive recycling in the recent years has formed concerns that impurities in the secondary materials may cause drastic changes in the chemical properties of the CL-slag, which is separated from matte in the smelting stage. Among various impurities included in secondary materials, the authors have studied the influences of sodium oxides in the CL-slag because the behavior of sodium oxide has scarcely been studied with respect to the copper smelting slag. The examinations have been applied experimentally on the distribution between slag and matte of arsenic whose acidic characteristics suggest strong affinity to sodium-oxide of basic characteristics in silicate melts. The results have been discussed by thermodynamic evaluations and the results of pyro-tests at the commercial furnace.IntroductionAt Naoshima Smelter and Refinery, the existing line of the Mitsubishi continuous copper smelting and converting process has been operated since 1991. The Mitsubishi Process consists of three furnaces namely the S-, CL- and C-furnace as shown in Figure 1. In the S-furnace, copper concentrate and powdery secondary materials (scraps, sludges, etc) are charged through the top lances with oxygen enriched air. The other secondary materials of lumpy shapes are charged through the chute installed on the furnace roof. Charged materials are smelted by the reaction heat in accordance with the oxidization of copper concentrate. The mixed melt of matte and slag overflows through the launder into the CL-furnace, where the melt is separated into slag and matte by the difference of their specific gravity. Matte is siphoned out and sent to the C-furnace and converted to blister copper continuously. The CL-slag overflows continuously through the slag outlet to be water-granulated. Granulated slag is sold as a raw material used for the cement production and so on. Various secondary materials have been processed at the S-furnace of Naoshima Smelter and Refinery. Intensive recycling in the recent years has formed concerns that the chemical properties of the CL-slag may change drastically due to impurities originating from secondary materials. Among various impurities included in secondary materials, the authors have studied the influence of sodium oxide in the CL-slag because the impact of sodium oxide has scarcely been studied with respect to the copper smelting slag. The examinations have been applied experimentally on the distribution between slag and matte of arsenic whose acidic characteristics suggest strong affinity to sodium-oxide of basic characteristics in silicate melts."

Jan 1, 2012

By Yavuz Ali Topkaya, Aydin Rusen

"In this study, zinc and lead recovery from zinc plant leach residue obtained from Çinkur using hydrometallurgical methods have been investigated by laboratory scale experiments. Considering more than one million tons leach residue (LR) rich in Zn (12.43%) and Pb (15.51%) in the stockyard and environmentally hazardous, it is essentially necessary to process Çinkur LR. Zinc and lead have been recovered in two main stages. As a first step, Çinkur LR was releached by using hot sulphuric acid for zinc recovery. About 72 % Zn was recovered by using 150 g/l H2SO4 at 95 oC in 2 hours with a pulp density of 200 g/l. Secondly, for lead recovery brine (NaCl) leaching tests were performed on the secondary Çinkur LR obtained after acid leaching process. In brine leaching while lead recoveries up to 95 % could be attained at a low pulp density, the maximum recovery obtained was 84.9 % at a high pulp density (200 g/l) with 300 g/l NaCl concentration in 10 minutes at 95 oC. Introduction Zinc and lead have been known and used by humans since ancient times and also they are important nonferrous metals [1]. Zinc and lead have different properties thus they are used in various application areas, ranging from automobiles to construction, from batteries to textile. Zinc and lead deposits are widely distributed in the Earth’s crust. The principal ore mineral for zinc is zinc sulfide, Sphalerite (ZnS), and lead sulphide, Galena (PbS), is the main source of lead in the world [2].Although zinc is generally produced from sulphidic ores (ZnS) or concentrates by Roast – Leach – Electrowinning (RLE) in the world, in Turkey, zinc production is based on zinc carbonate ores (ZnCO3), and at the Çinkur plant zinc was produced from zinc carbonate from its establishment to 1997 due to high reserves of zinc carbonate in that region. Çinkur is the only plant in Turkey that produces Zn from primary ore containing ZnCO3 by Waelz – Leach - Electrowinning route [3]. However, due to depletion of local high grade ores, oxidized ore concentrates were imported from Iran after 1997, until this plant was shut down. Therefore, there are two different leach residues (LR) which are Turkish LR (TLR) and Iranian LR (ILR) in Çinkur stockpiles. It has been estimated that the total amount of leach residue is more than one million tons of which the major part is Turkish leach residue (TLR)."

Jan 1, 2008

By Susanne Pignolet-Brandom

Reflected light microscopy scanning electron microscope energy dispersive spectroscopic analysis and backscatter electron image and electron microprobe chemical analysis have been used to study lead sinter and lead blast furnace slag. These studies provide invaluable information on the phases present their intergrowths, and their chemical composition. Such information increases the understanding of the nature of pyrometallurgical processes and the behavior of minor elements during these metallurgical processes.

Jan 1, 1987

By Adegbenjo Adewale Oladapo, Ibitoye Simeon Ademola, Ladiipo Olufemi Akinbiyi, Adegbola Adekunle Amos, Adeboje Taiwo Bode, Raji Fatai Olasunkanmi

The combined effects of the addition of Silicon (Si) as alloying element and low temperature annealing on the tensile properties of 70/30 brass with Nickel (Ni) and Iron (Fe) contaminants is investigated in this paper. Melts of cartridge brass were made to which 0, 0.5, 1, 2, 3 and 4 wt % of Si was added. These were sand cast into rods of 600 mm by 10 mm diameter and were thereafter machined into standard tensile test samples. Some of these samples were annealed in a muffle furnace at temperatures of 250, 300, 350, 400 and 450 oC respectively and the others were used as control. Subsequently, all the heat treated and non heat treated samples were subjected to tensile tests on a Hounsfield Extensometer and the load – extension plots retrieved were analyzed. Microstructural characterizations of the samples were carried out using Accu-Scope Optical Microscope. The results showed that cartridge brasses subjected to alloying and annealing treatments had improved tensile and yield strengths. However, the tensile properties were increased and maintained within acceptable limits at stress relieve annealing temperatures.

Jan 1, 2015

By R. N. Reddy

The Pseudo capacitance of layered type Mn02 electrode material for electrochemical capacitors (EC's) was investigated. MnO2 was synthesized in our laboratory. Mn02 was prepared from heating of KMn04 at 300°C in air. Cyclic Voltammetry (CV) experiments were carried out using three electrode system, Saturated calomel electrode as reference electrode, platinum mesh as a counter electrode, and MnOz composite material mounted in a platinum mesh used as a working electrode. Two kinds of composite working electrode materials were used, one was mixture of MnOz and 25 wt% acetylene black, while the other was MnOz, 25 wt% acetylene black and 25 wt% carbon. All the experiments were carried out at 25OC. A maximum specific capacitance of 130 Fig and 118 Fig were observed at the scan rate of 2 mV/s and 20 mV/s respectively in 1M KC1 for composite electrode made with carbon. Results obtained in this study are compared with that of other electrode materials.

Jan 1, 2002

By Carlos Maurício Fontes Vieira, Sergio Neves Monteiro

"A ceramic body traditionally used to produce bricks and roofing tiles with kaolinitic clays was reformulated by the addition of sand and illitic clay. The objective was to obtain a ceramic product with better technological properties. Specimens were made by uniaxial press-molding at 20 MPa and then fired at 850, 900 and 950°C. The determined technological properties were: linear shrinkage, water absorption and flexural rupture strength. The results showed that both sand and illitic clay contribute to reduce the water absorption of the industrial clayey body. With respect to the flexural behavior, it was observed that the incorporation of sand decreased the mechanical strength. On the other hand, the illitic, incorporated in an amounts of 30 wt.% contributed to increase the mechanical strength of the clayey ceramic.IntroductionCeramic bodies industrially fabricated in the county of Campos, north of the State of Rio de Janeiro, in Brazil, are still empirically elaborated using a mixture of local clays. These clays are predominantly kaolinitic mineral in nature, associated with high plasticity and elevated weight loss during the firing stage. Due to the excessive plasticity of the ceramic bodies, dimensional defects, which occur after drying and firing are usually obtained. Moreover, the kaolinitic nature and the presence of aluminum hydroxide (gibbsite) confer a refractory behavior to the local clays, which impairs sintering during the firing operation. In the case of clay ceramic products for civil construction, this results in greater porosity associated with elevated values of water absorption and low mechanical strength [1,2]. To avoid these problems, it is necessary to reformulate the ceramic body composition. The addition of both non-plastic materials to reduce plasticity and fluxes to condition the refractoriness is a possible alternative.As an alternative to reduce the plasticity of clayey ceramics sand, which is predominantly constituted of silica, can be used. The incorporation of sand in amounts of up to 25 wt.% to a clayey ceramic body used for roofing tiles fabrication was studied by Vieira et al. [3]. In that work specimens were prepared by extrusion and fired at 850°C. The results indicated that in the pre-firing stages the sand improved the workability of the investigated clayey ceramic body and facilitates the drying stage. It was also observed that the incorporated sand significantly improved the physical and mechanical properties of the clayey ceramic after firing. On the other hand, the apport of flux oxides could be done by the use of illitic clays that have a higher amount of alkaline oxides in comparison with the kaolinitics clays."

Jan 1, 2013

By Jeffrey Shepherd, Scott R. Smith, Eduard Guerra

"Electrochemical and spectroscopic evidence for the dissolution of a Au electrode by meso-2,3- dimercaptosuccinic acid (DMSA) from an acidic LiCl04 electrolyte is presented. Near the potential of zero charge, DMSA was determined to form a stable layer on the metal surface but at more anodic polarizations, DMSA was displaced from the metal through an oxidative process. The anodic displacement of the layer from the electrode resulted in a small amount of Au that was detected in the electrolyte using atomic absorption analysis. The extent of Au dissolution, was monitored while holding the potential of the electrode for 24 hours at the thermodynamic Eo/H,O in LiCl04 electrolytes containing 10 mM DMSA. This routine resulted in detectable quantities of a soluble Au-DMSA complex in the electrolyte and the greatest leaching was observed at a pH = 2.0. At room temperature, the leaching rate was stable at 10.9 µg cm·2 hr·' however, upon increasing the temperature to 50.0°C, the rate of Au dissolution increased yielding an average rate of extraction of 40.1 µg cm·2 hr- 1. Interestingly, after the first 12 hours of leaching at 50.0°C, the leaching current decreased dramatically suggesting surface passivation which prevented further Au extraction. The implications of this process in the industrial leaching of Au will be discussed.IntroductionThe use of cyanide in the industrial process of leaching Au from ores has raised concerns regarding both operational safety and environmental issues surrounding the disposal of spent leaching eftluents in tailings ponds. Depending on the chemical nature of the processed ore, the spent solutions that are released into the tailings ponds can contain toxic cyanide, either dissolved or complexed with different metals and may pose serious risk to wildlife as well as freshwater contamination to nearby water systems. Because of these issues, some recent studies have focused on the exploration of more environmentally-friendly molecules to selectively leach Au with appropriate kinetics. However, to effectively leach Au into an aqueous solution, a suitable ligand that reacts to form a stable chemical bond with Au is needed to form soluble Au complexes that can be later recovered [I]. Recently several sulfur bearing alternatives have been shown to leach significant quantities of Au in aqueous solutions. These include thiourea [2], thiocyanate [3], and thiosulphate [4]. However, alkylthiols are also known to quickly form a stable covalent Au-S bond [5], but have been relatively understudied in term of their ability to leach Au in solution, even though some short chain thiols are water soluble and relatively nontoxic."

Jan 1, 2012

By Jiangtao Li, Zhongwei Zhao, Xingyu Chen, Xuheng Liu

The method of ultrasonic-assisted leaching was used to extract vanadium from the stone coal, with alkali as leaching reagent. The effects of ultrasonic power, concentration of alkali, reaction temperature, liquid-solid ratio and reaction time were investigated, respectively. The optimal ultrasonic leaching condition for vanadium extraction is as follows: ultrasonic power 230W, concentration of alkali 5%, liquid-solid ratio 3:1, reaction temperature 90℃ and reaction time 1h. The leaching rate of vanadium reaches 76.4% under the optimal condition, which is 12.2% higher than that of non-ultrasonic leaching. The reason on enhancing the leaching rate of vanadium by ultrasonic leaching was discussed. It is indicated that the ultrasonic cavitation can increase the surface area of mineral, which is beneficial to facilitate the reaction rate. Keywords: stone coal; vanadium; alkaline leaching; ultrasonic

Jan 1, 2014

By W. Drummond

The cooling of smelter gases by air dilution, adiabatic evaporative cooling and indirect heat exchange is discussed with reference to the ,process, to the subsequent cleaning of the gas and to the use of the heat extracted from the gas. The method of reducing the effect of acidic ,sulphide formation on the corrosive properties of the gas and the dust and the development of surface cleaning mechanisms are discussed. The development of indirect recuperators using air, water or steam cooling, made 'possible by the control of surface fouling is traced. The application of the modern Waste Heat Boiler to the new sulphide smelting processes is discussed with respect to the natural and forced circulation concepts. Case histories are presented to illustrate mistakes made with respect to designs produced without recourse to sensitivity analysis and without an appreciation of "worst process conditions".

Jan 1, 1992

By W. Riekehof

The paper explains required practice and equipment for capturing airborne fumes and particulates in hot-dip zinc galvanizing plants. An economic and technical comparison of enclosure and tank rim suction options is presented. The paper also compares the performance of various filter media in filtering fumes, to determine the effect of changes in flux as well as changes in filter finishlcoating methods. This includes a recommendation for how to achieve the best result with respect to pressure loss and cleaning behavior of the filter.

Jan 1, 1992

By Martin J. Hansel, Jan Bäckström

Starting from historic perspectives on converting at the Rönnskär Smelter, the continuous developments of refractory practice is described. In the development the joint efforts of operators and suppliers of refractory have lead to significant achievements. This paper comprises the development of the converting process and the refractory lining as well as future prospects regarding operation and refractory lining design, especially in the face of equipment and raw material availability. 81

Jan 1, 2009

By S. Katz, V. Stanek, K. L. Moore, E. D. Larsen, D. E. Clark, P. E. King

"Cupola melting is a complex physical and chemical process having a number of nonlinearities which make conventional process control difficult. In addition, sensors for both inputs and outputs of interest to the foundry operator are often difficult or impractical to apply in a production situation. The present work is an effort to control the process using both intelligent and conventional control techniques as appropriate. Neural networks are used as an inverse process model in a cascade, feedforward controller in conjunction with a finite difference model of the cupola. A separate implementation of the neural net serves as a stand-alone visualization tool; it can operate on a laptop computer and is a useful tool for the cupola operator. IntroductionThe goal of the present work is to develop a controller to improve the efficiency of cupola melting. Although cupola melting as a process has a long history, automatic control has been elusive because the process has been poorly understood. The purpose of this four-year program, which has been underway for about six months, is to develop a controller for the cupola process using intelligent and conventional control methods.The Cupola ProcessThe cupola furnace [1,2] is one of the oldest processes for making cast iron, and is still the dominant method. It takes the form of a water-cooled vertical cylinder, as large as 4 m in diameter and 20 m tall. The charge consists of scrap metal, alloying ingredients, limestone, and coke, which serves as fuel; it is composed by weight and fed through doors near the top of the cupola. Air, usually heated and often enriched with oxygen, is blown in near the bottom through tuyeres extending a short distance into the interior of the cupola. As the coke is consumed, the charge drops and melts. A continuous flow of iron emerges from the bottom of the furnace, at rates as high as 100 tons per hour, and. is transferred to casting lines in the foundry. The exhaust gases are drawn from the top of the cupola, where they are processed to meet pollution standards."

Jan 1, 1994

By Dmitri Goljandin, Jaan Kers, Xiangjun Zuo, Lifeng Zhang, Priidu Peetsalu

"In this paper, the mechanical milling of the electronic wastes was carried out. The metal parts and plastic parts were roughly separated. The final plastic powder size could be as small as ~100 µm. Then the pyrometallurgical recycling Printed Circuit Boards (PCB) was executed. The mechanisms of thermal degradation and combustion are investigated using TG/DTA and MS. Some chemical powders, such as Na2CO3, NaHCO3, NaOH and CaCO3 are used to control the exhausted toxic gas such as Br2. Introduction Waste electric and electronic equipment (WEEE), or electronic wastes (E-wastes), has been taken into consideration not only by the government but also by the public due to their hazardous material components [1-3]. From the point of material composition, electronic wastes can be defined as a mixture of various metals, particularly copper, aluminum, and steel, attached to, covered with, or mixed with various types of plastics and ceramics [4]. Precious metals have a wide application in the manufacture of electronic appliances, serving as contact materials due to their high chemical stability and their good conducting properties. Platinum group metals are used among other things in switching contacts (relays, switches) or as sensors to ascertain the electrical measurand as a function of the temperature [5]. Table 1 [6] gives examples of the metal composition of different electronic scraps from literatures. Additionally, non-ferrous metals and precious metals content have gradually decreased in concentration in scraps. The value distributions for different electronic scrap samples are shown in Table 2 [6], where the metal price data are from London Metal Exchange (LME) (Octoebr 2007). It can be seen that for cell phones, calculators, and printed circuit board scraps, the precious metals make up more than 70% of the value, for TV boards and the DVD player they still contribute to about 40%. This indicates that the major economic driver for recycling of electronic waste in industry is from the recovery of precious metals. Behind the precious metals come copper and zinc, while Al, Pb, and Fe are less value. Recycling of electronic waste is an important subject not only from the point of waste treatment but also from the recovery aspect of valuable materials."

Jan 1, 2008

By Wan Pu

Chrysotile asbestos samples from different mines have been studied by SEM and TEM, including high resolution electron microscopy, to find reasons for differences in physical properties of different types of asbestos fibres. The results show that the inner diameters of fibre tubes and the lattice images of fibres are different for soft and hard asbestos fibres. These differences are related to temperatures and geochemical conditions during the growth of chrysotile asbestos.

Jan 1, 1989

By Yong Hwan, Wang Jian-Jun, Cai Jiu-Ju, Chen Chun-Xia

"The quantity of residual-heat and its recovery in some Chinese sinter plants are investigated. The main factors affecting energy consumption are analyzed using exergy analysis combining energy level analysis. It is indicated that the “gradation recovery and cascade utilize” of discharged gas and sinter residual heat in different temperature is the direction and the available approach to reduce energy consumption of the sinter process. Taking an iron& steel enterprise as an example, the three-ranked scheme of residual-heat recovery is put forward: ?Part of the sinter gas is used for warm-up and dryness; ?The high-temperature part of the cooler and exhaust-heat boiler are actualized as a closed-circuit, which can produce high-quality steam to generate electricity. ?The waste air in low-temperature part is introduced to sintering machine to support combustion. According to the CDQ which can recover the coal heat, the assumption of pot-recovery is put forward to replace the belt cooler. The two equipments of residual-heat recovery are analyzed in the aspect of energy consumption and CO2 reduction.1. IntroductionEnergy consumption in sintering is only inferior to iron-making in iron& steel enterprises, accounting for 10%~20% of the total energy consumption. A lot of residual heat is produced during sintering, and mostly from the sinter ore and waste gas. Sensible heat of hot sinter ore and discharged gas have accounted for 60%[1] (equals to 40 kgce/t-ore), which are the key point of sintering waste heat recovery. Discharge gas of sintering is mostly composed of flue gas deriving from sinter bed’s combustion, and the content distribution of H2O and O2 and the temperature of the gas along the length of belt-type sintering are shown in Figure1[2,3]. Currently, the sensible heat of hot sinter ore is mainly recovered by circular cooler and cooled by blasting air: the temperature of cooled discharge gas brings down from 350? to about 100? along with the decrease of sinter ore temperature. It is significant to recovery and reuse the waste heat as 4000~6000m3 discharge gas per ton of ore can be produced"

Jan 1, 2008

By John G. Reid

When the paper "Operations at the Greenvale Nickel Project Mine and Refinery" was delivered at the 1st International Laterite Symposium in February 1979, the Yabulu Caron plant had been operating for four years and production had just stabilized. The design had been based closely on the Caron plant at Nicaro, Cuba, built in 1944, also by Freeport. Yabulu had 10 Herreshoff ore roasters and production in 1978 was 18,682 tonne nickel as impure oxide sinter and 763 tonne cobalt in a mixed sulphide with a cobalt to nickel ratio of 1 :2.5. In the 25 years since the 1st Symposium, two more roasters have been added, but dry ore processing rate has remained relatively unchanged at 2.4M Uyr to allow a lower feed rate per roaster with associated higher recovery. The ore source has changed from the domestic Greenvale mine to imports from New Caledonia, Indonesia and the Philippines. Nickel production between 1978 and 2003 has risen by 67%, cobalt has risen by 146% and the products have changed to high purity nickel compacts and "ChemGrade" cobalt salt. The plant changes that have contributed to the increased recovery, production and product value are discussed. Keywords: Caron, Yabulu, nickel, cobalt, ammonia

Jan 1, 2004

By Vladimir Lobanov, Pritchinm Alexander, Nikifor Ageev

"Sulfuric anhydride is one of the most voluminous technological emissions. The possibility of high-temperature SO2 oxidations without catalyst in presence of calcium-bearing filling materials (CaO, Ca(OH)2 and CaCO3) with obtaining of binding material on the basis of waterless calcium sulfate is studied. Due to application package HSC-4 the thermodynamic analysis of the specified interactions is made and following conclusions are drawn: 1) Reactions are feasible in the all range of investigated temperatures (400 – 1000 °?); 2) The best results should be expected at use of ???; 3) The heat of reaction does possible autogenous behavior of process. The researches have shown: 1) Practical possibility of the process; 2) SO2 oxidation without the catalyst is feasible in presence of ???, Ca(OH)2 and CaCO3; 3) The optimum temperature range is 600-800 °?; 4) The content of waterless calcium sulfate in a product reaches 48% that makes it possible to use as the binding material; 5) At excess of ??? the degree of SO2 collection is nearer to 100%. Introduction At processing of sulfide raw materials in metallurgical furnaces the significant amount of sulfur, mainly in the form of sulfuric anhydride is escaped. Rich gases (SO2>3 %) are used for the sulfuric acid or element sulfur production. Chemism of sulfuric acid manufacturing is based on catalytic high-temperature oxidation of anhydride. Poor gases of metal works (SO2 =2,5 %) and power combustion units (SO2 =0,5 %) after clearing discharge into the atmosphere. Commonly, to recovery of weak sulfuric anhydride the chemical and physicochemical methods are applied. A few chemical ways of recycling sulfur dioxide are applied practically. In a number of methods for SO2 recovery a pulp of metals oxides (magnesium, zinc, etc.) with formation of sulfites is used. In other case sulfuric anhydride is catch by weak sulfuric acid in the presence of an oxidizer (pyrolusite ore). Methods of absorption SO2 by solid sorbents, (carbon fibers, silica gels, zeolites) are known and put into practice. Regeneration of the saturated sorbents is realized by thermal decomposition or extraction. Obtained as a result high-concentrated solutions are a commercial product."

Jan 1, 2008

By João M. S. Rodrigues

The use of sandblasting as a treatment method for conditioning anodes for zinc electro-winning was investigated and compared with conventional fluoride preconditioning. The anodes were made from two different lead-based alloys (Pb-Ag-Ca and Pb-Ag). Laboratory results showed that sandblasting and preconditioning both minimize lead contamination in the zinc and sludge generation. Sandblasting was found to have no aggravating effect on the anode corrosion. The sandblasting treatment was tested on Pb- Ag-Ca anodes on an industrial scale in the celJhouse of a local zinc producer. An unexpected finding of the large-scale tests was that the sandblasting appeared to strengthen the anodes, resulting in reduced warping during handling and operation.

Jan 1, 1996

By Shenghui Guo, Dongbo Li, Lijun Liu, Chengdong He, Jinhui Peng, Libo Zhang

In present study, partially stabilized zirconia (PSZ) was prepared by CaO doped fused zirconia heated by microwave furnace at the temperature of 1450 oC and holding time of 120 min. The XRD results showed that untreated fused zirconia mainly consists of crystalline compounds of cubic ZrO2 phase; while the roasted one mainly is composed of crystalline compounds of cubic ZrO2 phase and monoclinic ZrO2 phase. It is shown through the optimization of structures of two phases that structure of cubic ZrO2 and monoclinic ZrO2 reject each other, revealing its difficulty in forming coinciding interface and linkage of two phases being of Ca atom. Introduction Due to advantages of zirconia, such as high melting point, chemistry inertia, low heat transmission and so on. Zirconia is always taken as megathermal refractory material[1]. However, in the heating and cooling processes of pure zirconium oxide, martensitic transformation will take place associated with greater shear force and volume change, which severely limits the industrial application of pure zirconia in some areas. Such as: Refractory materials, grinding materials and high temperature insulation materials[2]. Through adding a certain amount of MgO, CaO, or Y2O3 stabilizer, etc.[3,4], the zirconia can change into fully stabilized zirconia, which exists in cubic phase. But this high purity fully stabilized zirconia cracks easily because of thermal stress. Therefore, the thermal shock resistance variation is one of the most important quality indicators of zirconia-based materials. According to the heat treatment, the fully stabilized zirconia can be changed into the partially stabilized zirconia (PSZ)[5], which exists in cubic phase and monoclinic phase and has superior mechanical properties, such as anti-heat, low thermal conductivity, large coefficient of thermal expansion and stability, as well as good wear resistance[6].

Jan 1, 2011

By S. Moussa

The formation of boron-doped nickel aluminides Ni3AI, (76 at. % Ni) from elemental powders by reaction synthesis using reactive sintering was studied. The process involves the mixing of elemental powders of nickel and aluminium with various wt % of boron up to 1 wt % boron. Nickel and Aluminium powders were mixed in the correct proportion to form the intended boron-doped nickel aluminide intermetallic. XRD, SEMI EDS, Image analysis and Archimedes principle; were used to study the effect of Boron addition on the final microstructure, bulk density, average grain size of as reactively-sintered nickel aluminides (boron-doped), compared with no boron addition. The results showed that at greater boron content than 0.3 wt %, a two-phase non-equilibrium microstructure of consisting of NiAI phase in NiJAI matrix was formed that have been primarily retained even after heat treatment for 5 hours at 1000 °C. Boron was present in solid-solution within both the NiAI and the Ni3AI (in greater amounts) phases.

Jan 1, 2001