By J. A. Herbst, G. E. Agar

Beginning with the second paragraph in the second column of page 148, this paper should read: The Reynolds number in Fig. 6 was calculated from the inlet diam and it is evident from the graph that above NR = 5000 the value of K2 is as it should be, a constant. The data10 shown in Fig. 7 was obtained for fluids flowing in pipes of diam D with sharp edged orifices of diam d. To be consistent with the representation in Fig. 6 the Reynolds number was calculated with the orifice diam d. These two sets of data show similar patterns and the variation in the orifice coefficient C is believed to account for the variability of the cyclone coefficient K2. The values of C given in Table IV are derived from K2 by conversion of units. C more nearly represents an equivalent orifice coefficient for a cyclone. Armstrong1' showed that data reported by Chaston 12 and Elcox13 yielded values for C of 0.24 and 0.27, re- spectively, Dahlstrom's4 data gives a value of 0.22. As a consequence of the variability of the cyclone coefficient some caution must be exercised in substituting for Q in the split size equation.

Jan 1, 1967

By John T. Eastlick

The Banner mining district is about 70 miles northeast of Tucson in the southern part of Gila County, Arizona. Production from the district, valued at about $26 million, is chiefly from copper-silver-lead zinc ores. The stratigraphic section consists of Precambrian conglomerates, quartzites, dolomites, and limestones, Cambrian quartzites; Devonian limestones; dolomites, and shales; Mississippian limestones; Pennsylvanian limestones and shales; and Cretaceous volcanic and sedimentary rocks. Deformation of these rocks presumably started near the end of the Cretaceous, and extended into the late Tertiary. The sedimentary rocks were folded, faulted, and intruded by fine grained diorite, quartz mica diorite, and dacite porphyry. At least four distinct stages of mineralization are recognized. In the first stage of contact metamorphism and the second stage of hydrothermal alteration, favorable zones were prepared for ore deposition. Metallization occurred in three of the mineralizing stages. Magnetite, pyrite, and hematite were deposited near the end of the second stage of hydrothermal alteration. The third stage included the main deposition of sphalerite, chalcopyrite, bornite, and galena. In the fourth and final stage, minor amounts of sulfide minerals were deposited with a late anhydrite and quartz gangue. The ore deposits in the form of veins and veinlets, pipes, irregular massive replacements, and bedded replacements are localized by the extent and distribution of metamorphic and hydrothermal alteration, by the proximity to the intrusive contacts, and by the effects of structural development. Oxidized ores of copper, lead, and zinc constituted the principal production of the district prior to 1940, but, for the most part, supergene enrichment was of minor economic importance. The ore bodies of the district are in the mesothermal class of deposits, occurring as normal metasomatic replacement and vein types.

Jan 1, 1968

By R. A. Deju, R. B. Bhappu

The basic structural unit of all silicate minerals is a tetrahedron with a silicon atom at the center and four oxygen atoms at the corners. The oxygen-silicon distance is about 1.6 & and the oxygen-oxygen distance about 2.6 &. The different types of oxygen-silicon frameworks in the various silicates are based entirely on the combinations of the tetra-hedral oxygen-silicon groups through sharing of oxygen atoms. In recent years, infrared spectroscopy has permitted estimation of the ratio of the ionic character of the oxygen-silicon bond to be a few times that of the oxygen-carbon bond and the ratio of electro-negativity of the two bonds has also substantiated this finding. On this basis, it is generally accepted that the oxygen-silicon bond is the strongest one occurring in silicate minerals. As the oxygen-silicon ratio increases from quartz to the olivines, a greater percentage of the oxygen bonding power is available for bonding to cations other than silicon. Hence, with an increasing oxygen-silicon ratio, there is increasing oxygen-to-metal bonding. Upon the fracturing of a silicate mineral crystal, the oxygen-metal bond, which is almost entirely ionic in character, should break more easily than the stronger oxygen-silicon bond, resulting in a greater number of unsatisfied negative forces on the surface. If, then the mineral is immersed in a liquid containing hydrogen ions, these negative forces should tend to be neutralized by hydrogen ions from solution, resulting in a change of the pH of the solution. An increase in the degree of adsorption of hydrogen ions is to be expected as the oxygen-silicon ratio in the crystal structure increases. This study attempted to correlate the oxygen-silicon ratio for various representative silicate minerals to the adsorption of hydrogen ions. Experiments to determine the effect of surface area on this adsorption and to investigate the effect of surface iron were also conducted. It is believed that such studies of the surface properties of silicate minerals will supply pertinent information about their behavior in froth flotation systems. EXPERIMENTAL PROCEDURE Ion Exchange: Carefully selected, hand-picked samples of the minerals investigated were dry-crushed in a ceramic ball mill and sieved to obtain a minus 100 plus 200-mesh sample. The sized samples were then run through the electro-magnetic separator to remove any iron-bearing particles. A 10-g sample of each mineral was placed in 100 ml of freshly deionized water previously adjusted to a pH of 3.50 with HCl. The beaker containing the sample and the water was placed under a bell jar from which the air was displaced at once by nitrogen gas from a tank. All experiments were carried out in a nitrogen atmosphere. The sample and solution were stirred gently but continuously during the entire experiment, the stirring speed being kept about the same for all runs. Changes in pH were followed with a Beckman Zeromatic pH meter and recorded on a

Jan 1, 1967

By J. A. Fellows, Earnshaw Cook, Howard S. Avery

HEAT-RESISTANT alloys of the higher nickel and chromium ranges have been empirically developed through the practical experience of the past two decades to a position of significant industrial importance. Few quantitative metallurgical data have been published, however, that could be related directly to engineering specifications and design. Inadequate information led to the inauguration, in 1934, of a research directed toward a better understanding of the properties and performance of these steels at temperatures between 1400° and 2000°F. Investigation was concentrated upon the 26 per cent Cr:12 per cent Ni type, which owes its extensive application to an excellent combination of economy, strength and surface stability at elevated temperatures. The requirements of the oil-refining industry have been prominent in influencing the scope and evolution of the program. Creep strength at the maximum allowable deformation ranges has been employed to evaluate the merits of these alloys. Permissible elongation rates vary from 1.0 per cent in one million hours for turbine blades to 1.o per cent in ten thousand hours for tube supports and heating-furnace equipment. Throughout this paper, the limiting creep stress (L.C.S.) for a given temperature has been defined as the stress that will produce a uniform elongation rate (stage II) of one per cent in ten thousand hours as extrapolated from rates per hour or tests of less than two thousand hours duration. Certain current specifications require a minimum L.C.S. of 1600 lb. per sq. in. at 1800°F., of 3600 lb. per sq. in. at 1400°F., and include a tensile acceptance test at room temperature, after aging for 24 hr. at 1400°F., as a measure of embrittlement in service. An elongation of 4 per cent is considered satisfactory for general use, while a minimum of 9 per cent is prescribed on occasion. Many differences of opinion concerning the properties and performance of these alloys appear to result from their sensitivity to unappreciated variations of chemical analyses which, for example, may change their L.C.S. from 3500 to 350 lb. per sq. in. at 1800°F. Within broad chemical limits, it is possible to balance the six or more important elements present to attain desirable properties with a number of different combinations. One method for adjusting the composition has been described under the sponsorship of the Alloy Casting Institute,1 in which, by maintaining a substantially austenitic* alloy, optimum creep strength and minimum tendency to embrittle after aging are expected. Unless, however, the limits are undesirably dose, it has not been possible to ensure a moderate range of strength and of ductility by any chemical specification alone. There is a definite need

Jan 1, 1942

By Earnshaw Cook, J. A. Fellows, Howard S. Avery

Heat-resistant alloys of the higher nickel and chromium ranges have been empirically developed through the practical experience of the past two decades to a position of significant industrial importance. Few quantitative metallurgical data have been published, however, that could be related directly to engineering specifications and design. Inadequate information led to the inauguration, in 1934, of a research directed toward a better understanding of the properties and performance of these steels at temperatures between 1400° and 2000°F. Investigation was concentrated upon the 26 per cent Cr:I2 per cent Ni type, which owes its extensive application to an excellent combination of economy, strength and surface stability at elevated temperatures. The requirements of the oil-refining industry have been prominent in influencing the scope and evolution of the program. Creep strength at the maximum allowable deformation ranges has been employed to evaluate the merits of these alloys. Permissible elongation rates vary from 1.0 per cent in one million hours for turbine blades to I .o per cent in ten thousand hours for tube supports and heating-furnace equipment. Throughout this paper, the limiting creep stress (L.C.S.) for a given temperature has been defined as the stress that will produce a uniform elongation rate (stage 11) of one per cent in ten thousand hours as extrapolated from rates per hour for tests of less than two thousand hours duration. Certain current specifications require a minimum L.C.S. of 1600 lb. per sq. in. at I800°F., of 3600 lb. per sq. in. at 1400°F., and include a tensile acceptance test at room temperature, after aging for 24 hr. at 1400°F., as a measure of embrittlement in service. An elongation of 4 per cent is considered satisfactory for general use, while a minimum of 9 per cent is prescribed on occasion. Many differences of opinion concerning the properties and performance of these alloys appear to result from their sensitivity to unappreciated variations of chemical analyses which, for example, may change their L.C.S. from 3500 to 350 lb. per sq. in. at 1800°F. Within broad chemical limits, it is possible to balance the six or more important elements present to attain desirable properties with a number of different combinations. One method for adjusting the composition has been described under the sponsorship of the Alloy Casting Institute,' in which, by maintaining a substantially austenitic* alloy, optimum creep strength and minimum tendency to embrittle after aging are expected. Unless, however, the limits are undesirably close, it has not been possible to ensure a moderate range of strength and of ductility by any chemical specification alone. There is a definite need

Jan 1, 1942

By J. A. Fellows, Earnshaw Cook, Howard S. Avery

Heat-resistant alloys of the higher nickel and chromium ranges have been empirically developed through the practical experience of the past two decades to a position of significant industrial importance. Few quantitative metallurgical data have been published, however, that could be related directly to engineering specifications and design. Inadequate information led to the inauguration, in 1934, of a research directed toward a better understanding of the properties and performance of these steels at temperatures between 1400° and 2000°F. Investigation was concentrated upon the 26 per cent Cr:I2 per cent Ni type, which owes its extensive application to an excellent combination of economy, strength and surface stability at elevated temperatures. The requirements of the oil-refining industry have been prominent in influencing the scope and evolution of the program. Creep strength at the maximum allowable deformation ranges has been employed to evaluate the merits of these alloys. Permissible elongation rates vary from 1.0 per cent in one million hours for turbine blades to I .o per cent in ten thousand hours for tube supports and heating-furnace equipment. Throughout this paper, the limiting creep stress (L.C.S.) for a given temperature has been defined as the stress that will produce a uniform elongation rate (stage 11) of one per cent in ten thousand hours as extrapolated from rates per hour for tests of less than two thousand hours duration. Certain current specifications require a minimum L.C.S. of 1600 lb. per sq. in. at I800°F., of 3600 lb. per sq. in. at 1400°F., and include a tensile acceptance test at room temperature, after aging for 24 hr. at 1400°F., as a measure of embrittlement in service. An elongation of 4 per cent is considered satisfactory for general use, while a minimum of 9 per cent is prescribed on occasion. Many differences of opinion concerning the properties and performance of these alloys appear to result from their sensitivity to unappreciated variations of chemical analyses which, for example, may change their L.C.S. from 3500 to 350 lb. per sq. in. at 1800°F. Within broad chemical limits, it is possible to balance the six or more important elements present to attain desirable properties with a number of different combinations. One method for adjusting the composition has been described under the sponsorship of the Alloy Casting Institute,' in which, by maintaining a substantially austenitic* alloy, optimum creep strength and minimum tendency to embrittle after aging are expected. Unless, however, the limits are undesirably close, it has not been possible to ensure a moderate range of strength and of ductility by any chemical specification alone. There is a definite need

Jan 1, 1942

By C. S. Barrett, D. F. Clifton

THE transformation that occurs in lithium and its solid solutions containing magnesium1,2 is similar in many respects to other diffusionless transformations of the martensitic type. This general similarity makes it desirable to investigate the transformation curves in detail. The current interest in the phenomenon of stabilization in martensitic transformations has created a need for a careful appraisal of possible stabilization effects in both cooling and heating transformations in lithium alloys. The effect of prior heat treatment on the temperature at which transformation begins and the effect of various temperature cycles in partially transformed alloys also merit attention. Limited data on some of these features were presented previously,' but the present studies have been made with improved apparatus, in which erratic fluctuations were smaller than in the earlier work, and include many independent determinations of certain critical observations. Material and Methods Geiger counter X-ray spectrometers were used: a Norelco instrument, original model, and a General Electric XRD-3. The low-temperature specimen holder has been described elsewhere." Specimens 10 mm in diam and 1.5 mm thick were held in firm contact with a copper block which was attached to the lower end of a stainless steel tube that extended up to a reservoir of liquid nitrogen. A heating coil on the tube permitted a controlled temperature gradient along the tube, so that desired temperatures and rates of heating and cooling could be obtained by controlling the heating current. The specimen was surrounded by an atmosphere of evaporated nitrogen in an insulated chamber having double cellophane windows. The temperature of the specimen was read by a thermocouple imbedded in it close to the irradiated area; the specimen could be held at constant temperature within 1°C for long periods. The body-centered cubic 200 reflection near 8 = 26" was used as the index of the amount of b.c.c. material present; occasional checks were made using the most suitable line of the low-temperature phase, the close-packed hexagonal 110 line near 8 = 29". Copper radiation was used throughout. A continuous record was made of the reflected intensities on a strip chart recorder, both when the peak intensity of a line was being followed and when the lines were being scanned at constant temperature. On the continuous recordings of peak intensity, periodic checks were made on the background intensity between the lines, and on the setting of the spectrometer for maximum intensity. The lithium-base solid solution containing 12.4 atomic pct Mg (33.3 wt pct) that had been used previously' was chosen, as it had a transformation range at relatively high temperatures, so as to permit wide temperature cycling within the range. Just prior to use a pellet was cut from the ingot,

Jan 1, 1951

By Frances Hurd

WHEN 60:40 brass is heated to 825° C., given a drastic quench to obtain the beta solid solution, and reheated, various changes take place in the structure. Reheating at 200' C. causes a fine, granular, sorbitic structure to appear which has been considered alpha solid solution. These particles coalesce at higher temperatures of reheating, and at 470° C., the alpha forms twins. A further study of these transformations was considered worth investigating.

Jan 1, 1927

By D. W. McGlashan, K. N. Mcleod

IN the use of free bubbles with precise temperature control and continuous pH measurement, the contact angle apparatus differs from all previous equipment. Experimental procedures differ sharply from the captive bubble method1,2 of introducing the gaseous phase in the three-phase system. When freed from the tube and captured by a solid surface, a bubble more closely conforms to the spherical ideal set up by the usual mathematical analysis of surface free energy or surface tensional relationships of the forces involved. The assembled equipment, Fig. 1, departs from the usual contact angle apparatus in providing: 1) water circulation for fixing temperature, 2) instruments to measure and record pH during testing, and 3) a system for producing and using free bubbles. The apparatus allows testing over a broad range of closely controlled conditions, and the use of free bubbles gives contact angles independent of operator manipulation, which was unavoidable in the older captive bubble method. A bubble released below the specimen rises through the liquid and contacts the mineral. If the mineral is gas-avid the bubble adheres, developing a finite contact angle. Reaction cells (1), 2x33/8x5 3/16 in. ID, are of pyrex glass 5 mm thick. To prevent optical distortion, the sides are optical flats and are planed parallel to within five wave lengths of light over the entire surface. Special cement is required to withstand chemical attack and thermal shock. The cell is placed in a thermal jacket (2) made of welded aluminum. A water seal for the optical ports is made by using O-rings tightened against the flats of the cell by fine-threaded and adjustable ports, Fig. 2. In-flow water is discharged downward from a manifold located near the bottom of the cell jacket. Water overflows the weirs at each end of the cell jacket, discharging from both sides to a collecting manifold (24). A hose (26) leads the overflow water to the thermal-conditioner well (4), which is recessed to accommodate a reaction cell and two beakers (150 ml). Both the thermal jacket and the thermal-conditioner well are insulated to minimize the effects of temperature differentials. Water, discharging from the thermal-conditioner well, returns to a thermostat bath and pump (3), from which it is pumped to the thermal jacket. The thermostat bath permits temperatures to be adjusted from 1" or 2°C to 80°C and will maintain the selected temperature within 0.2ºC. An electrode support (22) groups the four electrodes (8) so that they fit conveniently into the reaction cell, Fig. 2. This assembly holds the glass electrode, the calomel electrode, the temperature-

Jan 1, 1957

By Henry Hibbard

AT THE beginning of a Henry M. Howe lecture it seems fitting to refer to Howe's great contributions to steel metallurgy, and particularly to the literature thereof. Most of my predecessors in this role have been able, from their association with him, to give direct testimony as to his great services; but although connected with him for years in a business way, I am less familiar with what might be called his academic side, except as .it is embodied in his utterances, written and oral. Howe was adept in his genial way in extracting information in any line which, at the time, was of interest to him. In a technical lecture one expects as a rule new knowledge-something about recent advances relating to the subject. On this occasion, however, I will ask you to go back with me to the primary department of steel lore, as the title of my lecture shows, to review the more fundamental features in that field for the purpose of seeking some gaps which we can fill and so give the subject renewed interest. In thus going back one must inevitably repeat many familiar facts, but that seems to be necessary in order to reach a clear understanding of the unrecorded matters. The full interpretation of a steel analysis is at present unattainable, though much progress toward that end has been made. The ultimate analysis, giving the percentages of the five commonly determined elements, does indeed usually give a fair idea of what the steel is, and is ordinarily enough, with knowledge of its history and physical condition, to enable it to be assigned to some purpose or use for which it is reasonably suitable. But discrepancies arise. Every maker and every user of steel knows, from at least occasional examples in his own experience, that the ultimate analysis is insufficient by itself to enable one to tell positively, from its interpretation, either the mechanical properties of the steel or its adaptability to the purpose for which it was made. Further, if, while having the specified composition, it is abnormal or unsatisfactory, why it is so. Good, bad and indifferent steels may have substantially the same ultimate analysis.

Jan 1, 1928

By B. A. Wilcox, A. H. Clauer

The tensile and creep deformation characteristics of fiber reinforced composites have been studied, primarily at room temperature. The matrix was an alloy of Mg-14 wt pct Li-1 wt pct Al (LA141A alloy) and the reinforcing fiber consisted of continuous wires of a high strength precipitation hardening stainless steel (AFC-77 alloy). The ultimate tensile strength and strength-to-density ratio of composites were much improved over that of the mmix, both at room ternperatwe and up to 200°C. Creep studies at room temperature revealed logarithmic weep behavior for wires and composites and steady state creep for the nonreinforced matrix. It was concluded that creep of the fibers controlled composite creep. The instantaneous logarithmic weep rate of the composite, 6, was related to the average tensile stress on the fibers, where n = 3.4. Mg-Li alloys are the lightest structural metals commercially available, e.g., the alloy LA141A (Mg-14 wt pct Li-1 wt pct Al) is 27 pct less dense than beryllium Although Mg-Li alloys have moderate tensile strengths at normal strain rates and ambient temperature, their creep strength is relatively poor, even at room temperature. Reinforcement by fibers offers a means of increasing the tensile strength as well as overcoming the limitations of low creep strength. With a proper choice of reinforcing filament, composites could be designed with higher strength-to-density and modulus-to-density ratios than the matrix alloy. This communication reports a study on the tensile and creep characteristics of alloy LA141A reinforced with continuous wires of a high-strength precipitation hardening stainless steel (AFC-77 alloy). The matrix has a bcc structure, with possible precipitates of AlLi and MgLi2A1,3 and is ductile at room temperature Stainless steel wire was chosen as the -reinforcing filament since previous work at Battelle4 showed that a good bond between wire and matrix could be produced in this system. For all volume fractions of reinforcing wire, the theoretical composite strength-to-density ratio is greater than that of the matrix and the modulus-to-density ratio is somewhat lower than that of the matrix. EXPERIMENTAL PROCEDURES The 0.004-in. diam AFC-77 wire was obtained from two suppliers: National-Standard Co.* and Crucible 0.13 Si, 0.18 V, 0.011 P, 0.012 S, balance Fe. In the as-received condition, wires from both sources had room-temperature ultimate tensile strengths of 585,000 to 590,000 psi with approximately 2 pct total elongation and 40 pct reduction in area. Composite preparation was accomplished by the vacuum infiltration technique. This involved placing the continuous wires in a mild steel tube (1/8-in. ID), capping one end of the tube with a sheet of the matrix alloy, and evacuating the other end of the tube. When the capped end was placed in a crucible of the molten matrix alloy and held for 31/2 min at 70O°C, the liquid metal was drawn up the tube approximately 7 to 8 in. A cross-sectional view of a typical composite is shown in Fig. 1. This preparation technique promoted excellent bonding between the matrix and wires, and porosity was rarely observed. Test specimens for both creep and tension studies were prepared by machining off the steel tube. Tensile tests on the wires and composite specimens were made in an Instron using a cross-head speed of 0.01 in. per min. The composite specimens had no reduced section and were held in self-tightening grooved serrated grips. Most of the specimens broke in the effective 1-in. gage section. Even though several tests fractured in the grip section, their ultimate strengths were essentially the same as those of specimens which fractured in the gage section. Creep specimens of the composite were gripped in a similar manner, and

Jan 1, 1970

ALABAMA Aldrich -Thomas, D A Altoona -Cain, J Anniston -Cowie, L K Walmsley, W N White, H E Ashland -Sturdevant, J C Bankhead -Connaway, M B Bessemer-Ball, E M McKenzie, W C, Jr Mitchell, F R Morgan, C Thompson, N E Birmingham -Abbott, C E Adams, J H

Jan 1, 1923

By C. E. Lesher

Two processes for agglomerating fine sized ores with low temperature coke are described. One process (Orcarb) agglomerates ores with limited amounts of carbon; the other (ore-carbon pellets) pelletizes fine sized ores, using low temperature cokes as the binder. Data are presented on the products obtained when taconite, magnetite, and hematite concentrates and several titanium oxide ores were used. REDUCTION of finely divided oxide ores has long been a major metallurgical problem. Various methods of agglomerating, notably briquetting, sintering, nodulizing, and pelletizing, have been developed and are in industrial use. Carbon is the usual reducing agent for oxide ores and attempts have been made to agglomerate fine ores with coking coal in order to get the metallurgical advantages of intimate contact and increased particle sizes suitable for subsequent smelting or reduction.1-3 For the past three years, research has been in progress on two processes for combining fine sized ores with reactive carbon in the form of low temperature coke. By one process, designated Orcarb, the ore is coated with coke carbon in amounts limited to that required for reduction and the result is an appreciable but limited increase in product particle size over that of the original ore. The second process, called ore-carbon pellets, produces pellets of fine ore bound by low temperature coke. The first objective was to develop a process for combining an oxide ore with only enough carbon for its reduction, the amount being that derived from the simple reduction equations. The carbon (that amount theoretically required for the reduction of the oxides in an agglomerate with ore), calculated to CO, ranges from 10 pct for zinc calcines Or phosphate Ores to 21 pct for rutile and 26 pct for silica. The carbon required for reducing iron oxides falls between the extremes—10 and 26 pet' When the carbon in the agglomerate is low temperature coke, reduction by hydrogen may be expected to take place, thus modifying the calculated carbon require- ment. On the other hand, in practice, an excess of reducing agent over that required in theory is normally used. Screen sizes of three iron ores on which the greater part of the experimental work was performed are given in Table I. Most of the testing was done with Freeport (Renton Mine) coal, but Pittsburgh and Elkhorn bed coals were also used. The first objective was to agglomerate the ore with sufficient low temperature coke to provide carbon for reduction, i.e., in the range from 10 to 25 pct. This was accomplished by preheating the ore, mixing with pulverized coking coal, and completing the coal carbonization in a plain steel rotating retort. The pilot retort, as it is now constituted, is shown by diagram in Fig. 1 and photograph, Fig. 2. Ore is fed into the upper kiln by a screw; it is heated to 900° to 1100°F by direct flame and it is then discharged into an insulating hopper from which it goes

Jan 1, 1956

By Oliver S. North

Reserves of perlite rock in the western section of the United States are immense. A geological report prepared for the Union Pacific RR showed proved tonnage of over 400 million tons in southern Nevada alone. Yet the perlite industry is not large, and most of the mines are relatively small. There are indications that perlite processing, thus far largely in the hands of relatively small com¬panies, is becoming concentrated in a few large companies. For economic reasons the bulk of perlite sold in crude form has come from three or four pro¬ducers, although many individual operators have sold small quantities to limited lists of purchasers. Perlite is one of ultra-lightweight aggregates. Owing to its outstanding qualities as an aggregate, variety of uses, and ultimate economy of use, it has enjoyed considerable popularity in this country in recent years. Marked foreign interest also has been evinced in this material.

Jan 2, 1955

By C. E. Lesher

Two processes for agglomerating fine sized ores with low temperature coke are described. One process (Orcarb) agglomerates ores with limited amounts of carbon; the other (ore-carbon pellets) pelletizes fine sized ores, using low temperature cokes as the binder. Data are presented on the products obtained when taconite, magnetite, and hematite concentrates and several titanium oxide ores were used. REDUCTION of finely divided oxide ores has long been a major metallurgical problem. Various methods of agglomerating, notably briquetting, sintering, nodulizing, and pelletizing, have been developed and are in industrial use. Carbon is the usual reducing agent for oxide ores and attempts have been made to agglomerate fine ores with coking coal in order to get the metallurgical advantages of intimate contact and increased particle sizes suitable for subsequent smelting or reduction.1-3 For the past three years, research has been in progress on two processes for combining fine sized ores with reactive carbon in the form of low temperature coke. By one process, designated Orcarb, the ore is coated with coke carbon in amounts limited to that required for reduction and the result is an appreciable but limited increase in product particle size over that of the original ore. The second process, called ore-carbon pellets, produces pellets of fine ore bound by low temperature coke. The first objective was to develop a process for combining an oxide ore with only enough carbon for its reduction, the amount being that derived from the simple reduction equations. The carbon (that amount theoretically required for the reduction of the oxides in an agglomerate with ore), calculated to CO, ranges from 10 pct for zinc calcines or phosphate ores to 21 pct for rutile and 26 pct for silica. The carbon required for reducing iron oxides falls between the extremes—10 and 26 pct. When the carbon in the agglomerate is low temperature coke, reduction by hydrogen may be expected to take place, thus modifying the calculated carbon require- ment. On the other hand, in practice, an excess of reducing agent over that required in theory is normally used. Screen sizes of three iron ores on which the greater part of the experimental work was performed are given in Table I. Most of the testing was done with Freeport (Renton Mine) coal, but Pittsburgh and Elkhorn bed coals were also used. The first objective was to agglomerate the ore with sufficient low temperature coke to provide carbon for reduction, i.e., in the range from 10 to 25 pct. This was accomplished by preheating the ore, mixing with pulverized coking coal, and completing the coal carbonization in a plain steel rotating retort. The pilot retort, as it is now constituted, is shown by diagram in Fig. 1 and photograph, Fig. 2. Ore is fed into the upper kiln by a screw; it is heated to 900" to 1100°F by direct flame and it is then discharged into an insulating hopper from which it goes

Jan 1, 1956

By John T. Cumberlidge, Frederic M. Chace

Nickel-bearing saprolite developed during the early Tertiary over a northeast trending ultramafic body of Jurassic age near Riddle in southwestern Oregon. The principal nickel mineral is garnierite, but other complex nickel minerals may be present. There are two main ore bodies, an upper (older) one associated with the Klamath peneplain, and a lower (younger) one on the Sherwood peneplain. Saprolite constitutes the bulk of the ore and was probably derived from peridotite and dunite through chemical decomposition by downward percolating meteoric groundwater. Decomposition took place by net loss of MgO, SiO2, and Fe without a change in volume. Faults and joints provided permeable zones which localized saprolite development, and faulting may have helped preserve some ore from loss by erosion. Garnierite-chalcedony boxwork ore was deposited by meteoric groundwater along faults, joints, and at the level of former water tables. Boxwork ore is entirely supergene, the chemical constituents having been derived from higher in the soil profile. The saprolites show evidence of both supergene and residual enrichment in nickel. Red and yellow soil occurs as a capping over saprolite and boxwork, and was derived from them by chemical and mechanical decomposition. The present deposits are probably truncated remnants of a formerly thicker and much more extensive deposit which probably included laterite at the surface. The deposits started to form in the early Tertiary due to deep chemical weathering under sub-tropical to warmtemperature conditions. Early Tertiary ero~ion surfaces of low relief probably contributed to the predominance of chemical weathering over mechanical erosion. Alteration under present climatic conditions favors the formation of soil from saprolite rather than the formation of new saprolite from peridotite.

Jan 1, 1968

By B. W. Levinger

THE system Ti-CI- has been studied by several investigators." ' Though titanium and chromium are completely miscible at high temperatures, an intermediate phase of the approximate atomic proportions TiCr, has been identified at various compositions between 60 and 68 wt pct Cr. The structure of this phase was established as the cubic C15 (MgCu2) type with 24 atoms per unit cell and a lattice parameter 6.929 kX.2 During a study of the ternary system, Ti-Mo-Cr,5 the existence of a high temperature modification of the TiCr, phase was discovered. In a series of alloys annealed at 1300°C and containing from 60 to 70 wt pct Cr and 5 pct Mo, a new phase was present which did not correspond to either ß solid solution or TiCr,. By trial, the new phase was identified to be of the hexagonal C14 (MgZn2) structure with 12 atoms per unit cell. Further work showed that the hexagonal structure was. in fact, also present in binary Ti-Cr alloys quenched from high temperatures. To make the identification more certain, the intensities of the various reflections were calculated assuming a composition TiCr2 and C14 structure. Table I lists reflection planes, interplanar distances, calculated intensities, and a comparison of these values with the lines of a binary Ti-Cr alloy (66 pct Cr) annealed for 20 min at 1385°C and water quenched. Since high angle lines were more diffuse, the correspondence between visually observed and calculated intensities was not as good at these angles. Lattice parameters were computed to be a = 4.922 kX, c = 7.945, c/a :- 1.614. The corresponding interatomic distances are: titanium to titanium distance, 3.00:, kx, chromium to chromium distance, 2.43, kX, titanium to chromium distance, 2.88,, kX. These compare to 3.00, 2.45, and 2.87 kX in the cubic phase, respectively.' The atomic positions in the C14 structure are as follows: Titanium 1/3, 2/3, Z; 1/3, 2/3, 1/2: 2/3, 1/3, i; 2/3, 1/3, (1/2-z); Chromium 0, 0, 0: 0, 0, 1/2; 2x, 2, 1/4; 232, x, %; X, 22, 1/4; X, 2x, 3/4; x. x, 1/4; x, x, 3/4; The values of x and z were calculated for the alloy mentioned and found as follows: z — 0.061, x = 0.165. The values assumed in the intensity calculations were those for an ideal close-packed lattice or z = 1/16, x = 1/6. Work in the Ti-Mo-Cr system indicates that y2 the hexagonal modification of TiCr2, is the stable phase above 1300°C, while y1 with the cubic structure is stable below 1000°C. X-ray examination of a number of alloys annealed at intermediate temperatures showed that the hexagonal and cubic phases can coexist. Alloys quenched from 1000°C and annealed at 1100" and 1200°C showed small amounts of y2 at the higher temperature. A considerable amount of y, seemed present, however, in cast alloys annealed at 1100°C. It further appears that there is a small but definite solubility range for both phases in the ternary system. Acknowledgment The results of this paper represent work carried out in conjunction with a project sponsored by Watertown Arsenal, Contract No. DA-11-022-ORD-272. References 'M. K. McQuillan: Journal Inst. Metals (1951) 79, p. 379. 2 P. Duwez and J. L. Taylor: Trans. ASM (1952) 44, p. 495. W. J. Van Thyne,. H.. D. Kessler, and M. Hansen: Trans. ASM (1952) 44, p. 974. 1 F. B. Cuff, N. J. Grant, and C. F. Floe: Trans. AIME (1952) 194, p. 848; Journal of Metals (August 1952). Unpublished Research, Armour Research Foundation. "H. J. Wallbaum: Ztsch. Krist. 103, p. 391.

Jan 1, 1954

By R. C. Philp, Allan Gibb

INTRODUCTION. THE term matte is applied to smelting-products so extremely diverse in composition and physical properties that it appears impossible to devise any generic formula to represent, chemically, the manner in which the varied proportions of the almost unlimited possible constituents combine with each other. Mattes produced in copper-smelting, in distinction from those produced in smelting-operations in which the recovery of copper is secondary to that of other metals, cover a narrower range in composition. The copper-content of such mattes vary from 20 to 80 per cent., and even this range is much smaller in general practice since it is found advantageous, when possible, to produce mattes with about. 50 per cent. of copper in the first operation. Further, it is unusual that arsenic or antimony occurs in copper-ores in sufficient proportions to form arsenides or antimonides in such quantities that they will separate out from the furnace-products, as is common in lead-smelting. Generally, the mattes produced in copper-smelting are composed mainly of copper (usually greater than 35 per cent.), iron and sulphur, the remaining elements being usually in proportions sufficiently small to allow of their treatment as impurities, rather than as essential constituents of the mattes. In modern practice of smelting copper-ores in blast-furnaces the tendency is to approach pyritic smelting as nearly as pos¬sible, the furnaces being low and the air supplied being largely in excess of that required for complete combustion of the carbonaceous fuel. Hence the atmosphere of the blast-furnace thus used is usually oxidizing or Dearly neutral? and, as a consequence, the reduction of metallic iron that was a necessary evil of former practice is of unusual occurrence in operations where the main object is the recovery of copper. Hearth-accre-

Nov 1, 1905

By H. C. Rickaby

BY August 1944 Canada expects to be shipping 56 percent hematite ore from its new Steep Rock iron mine, via Port Arthur on Lake Superior, to the steelmaking centers in Canada and the United States. This is indeed welcome news to steel men, especially if they operate open hearth furnaces, as the Steep Rock ore is a high-grade lump and will be valuable as charge and feed ore. But better news is the fact that this first big producer of high-grade hematite ore in Canada, since the exhaustion of the Helen mine in the Michipicoten area north of Lake Superior in 1918, has a proved ore body of 16,757,000 long tons and a probable ore body of 14,000,000 long tons, thus giving an over-all total of 30,757,000 long tons and assuring production for a number of years to come.

Jan 1, 1943

By E. L. WOOD

IN ATTEMPTING to summarize briefly the reconstruction of the Hecla plant since the fire, three important facts must be held in mind; namely: a hurry-up job with the shadow of an insurance company in the background; restriction of working space in the narrow Burke Canyon; and building two-thirds of the plant on a filled area. Construction work was carried on without interruption through the winter season. These adverse conditions have contributed many obstacles not ordinarily encountered in mining work. The first problems immediately after the fire were organization and policy; the-former to create an efficient construction crew out of a mining organization; the latter to determine the type and extent of surface plant to be built. The new crew was organized from a nucleus of mine employees, 25 per cent. of the old crew remaining for construction work. Permanent fireproof buildings were decided upon, the general arrangement of the new plant to be similar to the old one as far as possible, at the same time enlarging it 100 per cent. in anticipation of the demands which would be made upon it when the Star Mine began operating. Cleaning up the wreckage was a big job, the extent of which is indicated by the fact that 30 carloads of scrap iron and steel were moved off the property. In re-establishing transportation facilities at the plant, a previous disadvantage of a steep grade on the high line was obviated by excavating 1600 yd. of solid rock; the fire having destroyed all town buildings below, made this work possible.

Jan 1, 1924