Search Documents

By Xiang-dong XING, Zhen-yang wang, Xing-le LIU, Jian-Liang Zhang

Experiments were carried out by adding CaF2 as catalyst in a Ar atmosphere to study the isothermal reduction kinetics of vanadium titano-magnetite carbon composite pellets under high temperature in the range from1473 to 1673K. By analyzing reduction mechanism, it was found that the rate controlling step was gas diffusion, and the activation energy was 178.39kJ•mol-1 without adding any catalysts. Adding CaF2 of 3% to vanadium titano-magnetite carbon composite pellets can decrease the apparent activation energy of reduction, and the decrease extent was 14.95kJ•mol-1. In addition, temperature is an important factor influencing on reaction rate.

Jan 1, 2015

By Tailoka F.

Various metallurgical residues from iron and steel making processes have been treated by chlorination in excess air with hydrogen chloride gas generated from the combustion of scrap polyvinyl chloride (PVC). The residues include dust from both the electric arc and blast &maces, hydrocyclone overflow, zinc - lead blast furnace slags and dust rich in zinc and copper from copper refining. Chlorination is achieved either directly by mixing the residues with scrap PVC or indirectly in a two furnace system. In the latter, scrap PVC is combusted between 523 and 573 K in a horizontal furnace and the resulting gases are then reacted with metallurgical residues in a vertical furnace at 1166 to 1329 K. Gas chromatography, thermogravimetric measurements, XRD and AAS have been utilised to study the reactions. The recovery of non ferrous metals is as high as 80 to 90 % and only a negligible amount of iron is carried over. The optimum temperature for combustion is between 518 and 573 K. Above 600 K, the evolution of HCI is so fast that sufficient chlorination is not achieved. Analysis showed that no dioxins were present in the gases, the residues or the chlorides.

Jan 1, 1997

By Takao Mori

Novel rare earth boron icosahedral compounds are investigated as potential high temperature thermoelectric materials. REB50-type compounds and REB22C2N compounds were synthesized and the thermoelectric properties measured. Seebeck coefficients in excess of 200 V/K are observed at temperatures above 1000 K for the REB50-type compounds. Strikingly, n-type behavior was observed for REB22C2N. Up to now, non-doped B12 icosahedral compounds have all been p-type. The discovery of an n-type compound is extremely important in terms of the potential development of this class of compounds as viable thermoelectric materials. Low thermal conductivities of < 0.03 W/cm/K at room temperature was observed for these rare earth boron cluster compounds.

Jan 1, 2006

By Norihiro Murayama

The hydrothermal syntheses of zeolites from coal fly ash were carried out using NaOH and KOH as an alkali source. The cation exchange capacity (CEC) and the ion exchange selectivity were investigated for the zeolites synthesized by a hydrothermal treatment. The effective usage of the zeolite as a cation exchanger was considered from the viewpoint of engineering. Zeolite P, HS (hydroxysodalite) and K-CHA (potassium-chabazite) are mainly formed as zeolite species in NaOH or KOH solution at 393K. The zeolite P and K-CHA have a large exchange capacity as a cation exchanger. The cation exchange isotherms of various monovalent and divalent cations with various zeolites are investigated. The order of selectivity of the zeolites is as follows, NH4+> K+> Li+.For the divalent cation, the largest removal amount is obtained for Pb2+ in the low equilibrium concentrations below 0.2mmol/dm3, and almost perfect removal can be achieved for Pd2+. The order of selectivity of zeolites in low concentration is expressed in the following order; Pb2+> Co2+> Cd2+> Ca2+> Mg2+> Ni2+. Ii is considered the zeolites obtained from coal fly ash can be used as an excellent cation exchanger.

Jan 1, 2006

By Ho-Sang Sohn

Copper concentrate particles of 200 to 300 mesh size were fed from the top of vertical reaction tube of 2.8 cm ID and 2 m long with an O2-N2 gas mixture. The reaction tube was heated to 900 K to 1100 K. The residence time of the particles in the reaction tube was about 1 second. The copper concentrate particles were very rapidly oxidized and melted down during their descent in the reaction tube. The particle temperature were calculated by combining an un-reacted core model, mass transfer between gas and particles, and heat transfer between gas, particles and tube wall. The particle temperature reached its maximum within a distance of 60 cm from the top of reaction tube, and it attained at 2000 K at higher oxygen partial pressure. The most particles were melted at the oxygen partial pressure above 20 kPa. An appreciable amount of As, Sb and Pb in the concentrate particles was eliminated in the upper portion of the reaction tube and the rate of elimination are explained by the rate of mass transfer of volatilized species through the gas film on the particle surface and the variation of particle temperature during the descent.

Jan 1, 2006

By Othon do Rêgo Monteiro Neto

[The present study has investigated the extraction of copper from a chalcopyrite flotation concentrate using an adapted strain of Thiobacillus ferrooxidans and shake flasks, tank leaching and Warburg respirometer techniques. From the shake flask experiments, the activation energy and the frequency factor have been determined to be ?ka = 59.4 kJ and A = 3.3 x 105 S-1, respectively. The temperature coefficient was found to be Q10 = 2.2 in the range of 20 to 35°C. It was suggested that the reaction mechanism of chalcopyrite leaching by T. ferrooxidans involves the formation of an activated complex. whose thermodynamic values have been calculated to be ?G? = 92.1 kJ, ?S? -148.8 J K-1 and ?H$ = 47.8 kJ. The maximum volumetric oxygen mass transfer coefficient for the reactor leaching was found to be achieved by using an optimum air flow rate of 1970 cm min l at a rotational frequency of 1000 min-1. The highest copper extraction in tank (reactor) leaching experiment was 86.8% after 17 days of leaching, while in the sterile runs the corresponding copper extraction was only 40.1%. The copper extraction was suggested to be diffusion controlled. The power requirement of the aerated reactor was calculated to be Pg = 2.02 watts. During leaching, the oxygen saturation concentration was found to be C* = 6.70 mg dm-3. Using the gassing out method the critical oxygen concentration was assessed to be CCrit 0.05 mg dm 3. From the Warburg experiments, the kinetic parameters of the Monad equation were derived with a new evaluation technique to be Vmsp = 9.0 µm3 02 min-1 mg protein-1 and K = 7.4% pulp density for the effect of substrate concentration. The order of reaction and the overall reaction rate constant were determined from the modified van&apos;t Hoff plot to be n = 0.0 and k = 1.49 p dm3 02 min-1 mg Protein -1 for the chalcopyrite concentrate oxidation by T. ferrooxidans. On the basis of this experimental work, a preliminary flow sheet has been proposed for the bioextraction of copper from flotation concentrates.]

Jan 1, 1985

By F. E. Wagner, L. J. Cabri, Y. G. Safonov, N. S. Bortnikov, A. D. Genkin, J. Friedl, G. N. Gamyanin

"A multidisciplinary investigation (including INAA, SIMS, EPMA, and Mossbauer Spectroscopy) was used to characterize gold in four of the largest Siberian mesothermal sulfide gold deposits. These are the Olympiada (""'750 metric tons gold) and Veduga (estimated at 75-100 metric tons gold) deposits in the Enisei Mountain Range and the Nezhdaninskoye (z500 metric tons gold) and Sentachan deposits in the Verchoyansk-Kolyma area. It was found that some of the mineralization is refractory in all four deposits, largely due to the occurrence of ""invisible"" gold in arsenopyrite as well as within pyrite, but with a lesser concentration. The gold concentration and its distribution varies considerably both within and between arsenopyrite grains, with implications for processing options such as heap leaching. The ore most likely to be amenable to heap leaching is the oxidized ore of the #4 orebody of the Olympiada deposit, but further quantitative mineralogical investigations are recommended for this orebody's sulfide ore and for the ores of the Nezhdaninskoye deposit. Following a full mineralogical characterization, it is possible that economic viability will depend on a combination of pre-concentration with or without pre-treatment, followed by heap leaching of some tailings products.Acknowledgements· The Russian authors performed this study under an ""Eco res"" Project which was financially supported by the Ministry of Science and New Technology of the Russian Federation. C.J. Stanley wishes to thank John Spratt and Terry Williams for help with EPMA. F.E. Wagner acknowledges the Deutsche Forschungsgemeinschaft for a grant supporting the Mossbauer studies. L.J. Cabri is grateful to the following: M. Beaulne, D. Carson and J.H.G. Laflamme for technical support, K.E. Haque for technical comments, and D.M. Hausen and W. Petruk for editorial suggestions."

Jan 1, 1997

By W. Petruk

A study was performed to determine whether mineral textures affect are breakage during grinding, and to establish a correlation between are breakage and mineral liberation. A base metal are from the Brunswick No. 12 deposit in New Brunswick, Canada was ground for different periods of time in a laboratory ball mill, and both the unbroken are and the ground products were studied by image analysis. Similar size distributions were obtained for material from the 15-minute grind in a laboratory ball mill (K. 0 67 pm), for the grinding circuit discharge from a commercial mill (K. 0 = 59-72 pm), and for pyrite grains in unbroken are (K,. = 74 pm). This similarity indicates that the 1S-minute grind separated weakly adhering pyrite grains along grain boundaries, and represents the limit of easy breakage for the are. At this grind (15 minutes) large discrete are mineral grains and weakly adhering interstitial fillings aIrong pyrite were liberated. On the other hand, the 15-minute grind neither separated rooderately bonded pyrite grains nor released rooderate1y bonded interstitial minerals from pyritei a 45-minute grind (K.. 31 pm) in a laboratory ball mill was required. For Brunswick No. 12 are, a 45-minute grind in a laboratory ball mill (Keo = 31 pm) is equivalent to regrinding in a commercial mill (K ?? Fl:$ 30 pm). Grinding beyond 45 minutes in the laboratory ball mill broke the are by fracturing pyrite across grain boundaries and by Chipping grain edges. Such intense grinding (longer than 45 minutes) did not markedly increase sphalerite liberation. In contrast, the intense grinding increased galena liberation because a significant proportion of the galena occurs as minute inclusions in pyrite. These findings show that ore breakage and coincident liberation depend upon size distributions, intergrowths, and mode of occurrence of the minerals in an ore.

Jan 1, 1988

By Shengqin Zhang, Yousef Mohassab, Feng Chen, Hong Yong Sohn, Mohamed Elzohiery, Amr Abdelghany

The kinetics of hematite concentrate reduction by mixtures of hydrogen and CO of various compositions has been investigated as part of the development of a flash ironmaking process at the University of Utah. This process produces iron directly from iron oxides concentrates by the gas-solid flash reaction based on the partial oxidation of natural gas, resulting in a significant reduction in energy consumption and greenhouse gas emission. The reduction kinetics of hematite concentrate of an average particle size 21.3 μm by the above mentioned gases in the temperature range 1423 to 1623 K (1150 to 1350 ºC) was investigated. Hematite concentrate particles can be reduced to > 90% by any of these reductants in several seconds of residence time typically available in a flash reactor. The activation energy ranged from 214 kJ/mol for hydrogen to 231 kJ/mol for CO.

Jan 1, 2016

By Yuanbo Zhang, Ruijun Wang, Qian Li, Zhao Jing, Guanghui Li, Zhengwei Yu, Chen Liu

The high content of sodium and potassium in sinter is harmful for blast furnace ironmaking. Reductive sintering technology can remove more alkali metals than conventional sintering process. In order to improve the removal ratios of Na and K, reductive sintering with both CO-containing flue gas circulation and carbon-bearing pellet was conducted in this study. Experimental results show that all indexes except the VSV and P were improved in reductive sintering with CO circulation. Flue gas circulation technique combined with carbon-bearing pellets were beneficial to reductive sintering, because it could maintain good sintering indexes and enhance the removal of Na, K. The best removal ratios of Na, K and reduction degree of iron oxides were 20.37%, 63.73% and 23.76%. In reductive finished sinter, silicate mineral becomes the important binder phase, and main iron mineral phases are wustite (FexO) and magnetite (Fe3O4).

Jan 1, 2016

By C. O. Bounds

The magnetic properties of (NdDy)15Fe78B6 sintered magnets have been evaluated using powder prepared by Inert gas atomization. The atomized powder had a particle size distribution from 1 to approximate 1000 microns. The as atomized powders have been sieved into, coarse, intermediate, and fine fractions; magnetic properties were evaluated for the as produced powder and each fraction. A B, of 11.7 kG, a Hci of 11.0 kOe and a BHmax of 32.5 MGOe was -obtained on a sintered magnet made from the as-atomized powder. The magnet made from coarse powder exhibited a slightly higher B, of 12.1 kG, while that from fine powder showed a decrease in B, to 11.2 kG. Hydrogen decrepitation has been utilized to study its effect on the magnetic properties. Finally, cast ingots with a definite columnar structure have also been used to compare the magnetic properties of magnets of the same nominal, composition but of different alloy preparation process. Hydrogen decrepitation does not appear to improve the magnetic properties of magnets made from thin cast ingots. However, it does show a significant improvement in the Hci of magnets made from the atomized powders. Possible causes for the differences in the magnetic properties on magnets made from each process have been discussed in the paper.

Jan 1, 1992

By Jiang Diao, Yong Qiao, Xuan Liu, Tao Zhang, Bing Xie

Adding CaO into the vanadium extraction converter is an effective way to decrease the dephosphorization burden in subsequent steelmaking process. The crystallisation process of spinel is one of the most decisive factors in the subsequent extraction. The theoretical calculation results show that the temperature of the peak total crystallization rate will decrease 5K with basicity increasing 0.1. The relation between cooling conditions and grain size of spinels is also discussed. It is found that low cooling rate and high basicity benefit spinel crystal growth. And the non-isothermal crystallization kinetics results indicated that the restriction factors of spinel growth is that solid crystals accept new components from liquid-solid interfacial. While the sample was cooled down to 1250 (1523K) at cooling rate of 5K/min, the crystal growth is consistent with Ostwald coarsening grew up law, and controlled by diffusion of particle.

Jan 1, 2016

By Xiangwen Wang

Electrochemical measurements associated with the electrowinning of lead metal from concentrated brine (NaCI) - lead chloride (PbCI,) electrolytes at temperatures in the range 328 to 353°K (55 - 80°C) were conducted. The electrodeposition of lead metal onto a lead rotating-disk electrode may be described by the electrodic reaction: {PbCl 4 2 + 2e- = Pb° + 4Cl-} The deposition-overpotential requirements are low (approximately 41mV per decade of current density - Am+), with a corresponding high exchange current (approximately 0.018 A.cm2). The diffusion coefficient of the electroactive PbC142- species in a 3.5 NaCl electrolyte at 353°K was insensitive to the total PbCI, concentration (0.01 to 0.1M), and its value was found to be (1.21*0.1)~10-5 cm2Is with a temperature-sensitivity coefficient (E,/R) of approximately 1.98x103K-1 (328OK(T<353OK).

Jan 1, 1993

By Catherine Cai

A granular sorbent, prepared by gel-coating polyethyleneimine (PEI) on high surface area silica followed by crosslinking with a low-molecular weight diepoxide, has significantly higher uranium capacity, greater salt tolerance, and faster kinetics than the commercial resin Dowex 21K. Though having lower U(VI)/Fe(III) selectivity than Dowex 21K, the gel-coated PEI affords much higher sorptions of both U(VI) and Fe(III) and also their separation by selective stripping with acid.

Jan 1, 1999

By Norihiro Murayarna

Hydrothermal synthesis of K type zeolite was carried out by using coal fly ash as a raw material and KOH as an alkali source. The change in various physical properties of the obtained zeolite, such as the kind of zeolite crystal, cation exchange capacity, surface structure of zeolite and particle size distribution were investigated through the overall reaction of zeolitization. The reaction mechanism of K type zeolite from coal fly ash was investigated from these results in this study

Jan 1, 2002

By S. N. Sinha

The distribution coefficients of lead and silver between copper and matte phases have been measured at two different temperatures. Experiments covered the ranges of 0.009-1.8, 0.07-0.13, and 0-11 wt pct lead, silver, and iron in matte, respectively. The distribution coefficients of lead have been measured at 1405 and 1505 K and correlated with lead and iron concentrations in metallic copper and matte. The values of the distribution coef¬ficient of lead between copper and iron-free matte, at infinite dilution of lead, have been determined to be 3.60 and 4,06 at 1505 and 1405 K, respectively. The distribution coefficient of silver between copper and iron-free matte is independent of silver concentrations and has been measured to be 2.13 and 2.21 at 1400 and 1500 K, respectively. For an iron-bearing matte, the distribution coefficient of silver has been correlated with iron concentration in the matte at both 1400 and 1500 K. From the measured values of distribution coefficients, the Raoultian activity coefficients of PbS and AgS0.5 in copper-saturated matte have been calculated. At infinite dilution, the following equations correlating the Raoultian activity coeffici¬ents of PbS and AgS0.5 with matte- composition and temperature have been obtained: log Y° PbS =1.515 + 1080/T 0.14 NFes lbS Fog YAgS = -0.074 - 425/T + 0.09 NFes. - 0.5

Jan 1, 1983

By G. G. Krishna Murthy

Interactions of wustite and hematite pellets with Fe-C melts were investigated experimentally by examining the effect of pellet size and bath temperature on the reduction rates of the pellets. Experiments were carried out in the temperature range 1473-1923 K. A flash X-ray equipment was used to obtain images of the melt surface during its reaction with an oxide pellet. The reduction rates were calculated using experimentally estimated time for complete reaction of a pellet, tR. The value of tR was determined employing gas mass flow rate, or pressure rise in the sealed furnace, versus time traces. The value of tR was the same for both wustite and hematite pellets of equal weight at or above 1723 K and it decreased with increasing melt temperature. But the reduction rate was substantially lower at temperatures below 1651 K, the melting point of wustite. The rates were defined as the rate of moles of oxygen removed from the pellet per unit area of bath free surface and it was found that the bath surface area affects the reduction rates. It was established that the overall reaction followed nth-order rate kinetics with the values of n falling between 0.3 and 0.4 for temperatures above the melting point of wustite. The apparent activation energy determined using the apparent rate constants obtained from the experimental data was 76.2 + 27.7 kJ/mol-O.

Jan 1, 1992

By Ray Y. Lin

This study explores the formation of sodium pyrosulfate in molten sodium sulfate resulting from dissolution of SO3 at temperatures between 1160 and 1250 K. Solubility of SO3 in Na2SO4 melts at temperatures between 1160 and 1250 K under gas mixtures of SO2, O2 and argon was investigated applying a thermogravemetric analysis (TGA) technique. The activity of Na2O in the melt was determined with a high temperature electrochemical cell (ECC). Results showed that the SO3 solubility in molten Na2SO4 increases with decreasing temperatures and increasing SO3 partial pressures. Enthalpy of SO3 dissolution in molten Na2SO4 was calculated to be -119 kJ/mol for infinite dilute solutions. Thermochemistry of Na2SO4-Na2S2O7 melts was analyzed based on information obtained from both TGA and ECC techniques. Detailed examinations of the earlier low temperature measurements in the Na2SO4-Na2S2O7 system along with data from this study reveal that the solution behavior between Na2SO4 and Na2S2O7 can be satisfactorily treated as regular with the interaction parameter, , being 2.7 kJ/mol. The phase diagram and the field of SO3 partial pressure has been generated with the thermodynamic calculation using a regular solution approach.

Jan 1, 2006

By José D. T. Capocchi

Viscosity of liquid lead, tin, and Pb-Sn alloys has been measured by the rotational viscometer method in the temperature range from 50 K above their respective liquidus temperature to 823 K. The results are accurate to within ±1.0 %. The variation of viscosity with temperature followed the Arrhenius-type equation µ = µo.exp(Q/RT). The composition dependence of the isothermal viscosity and the activation energy for viscous flow have not shown anomalous changes at the eutectic composition of the Pb-Sn system.

Jan 1, 2000

By W. G. Davenport

Chapter 10 showed that any given smelting task, e.g. production of 65% Cu matte, 1500 K, from CuFeS2, can be done with many different combinations of: blast%02 hydrocarbon fuel blast temperature. This chapter repeats the Chapter 10 calculations but reports the results in terms of the mass industrial oxygen mass hydrocarbon fuel blast preheat energy combinations that will produce 65% Cu matte, 1500 K, from CuFeS2 concentrate. It also determines the energy inputs equivalent to these combinations.

Jan 1, 2001