By Nobuaki Sato

The electrical conductivity, k, of pure and sodium doped sulfur melts was measured with and without ultrasonic waves at temperatures ranging from 140 to 340'C by the two probe method using an ultra high resistance meter. The k value of the pure sulfur melt with irradiation jumped at around 170°C by an order of 102 after which it mouutuniocally increased from 10-5 to10-4 A' 1 cm-1 with an increase of the temperature. The addition of the sodium metal to the sulfur melt was found to cause a larger jumping in the K value. The k value increased with the increase of Na proportion in the melt. For a 10mol% Na doped sulfur melt it was as high as max ~30 A 1cm -1 above 180 C under the irradiation of of ultrasconics.

Jan 1, 2003

By C. M. Acuña

At the Chuquicamata Division of Codelco-Chile high arsenic concentrates are produced, which at the smelter are processed via the Outokumpu Flash Furnace and Teniente Converters to obtain copper mattes. In the case of the Teniente Converters the production of matte grade near white metal composition is a common practice since the eighties and provided in the pyrometallurgical route no appropiate measures are taken, penalties have to be paid because of arsenic content in the anodes. During smelting huge volume of slag is produced and elimination of arsenic by slagging at this step is not economically attractive. Although during fire refining is possible to eliminate arsenic by use of mixtures of calcium and sodium carbonates this alternative is expensive, takes long process time and decreases the lifetime of the refractory lining. In spite of these facts a reasonably way to control arsenic in metal, and therefore in the anode, is taking, action in the converting step. The effects of oxygen and arsenic content in metal, arsenic in white metal and basicity index of the slag upon the distribution coefficient of arsenic between metal and slag were investigated at pilot and industrial levels. The best results are obtained for metals around 7,000 ppm oxygen and 0.3 basicity index slag, which results in a 5.7 distribution coefficient for a 5,800 - 7,100 ppm arsenic content in white metal, 18%-24% CaO slag at 1473 - 1523K. Furthermore, no significant/visible refractory wear has been realized.

Jan 1, 1999

By J. J. Talja

An investigation of oxidation of various nickel concentrates was carried out using differential scanning calorimetry (DSC). The aim of this study was to determine the ignition temperature and investigate other oxidation behavior of various sulfide-based nickel concentrates. Variables in the experiments were mineralogy, particle size and partial pressure of oxygen with temperature increasing linearly at 25 K/min from 323 to 1023 K (50-750 °C). The igni¬tion temperature was determined to represent the starting point of rapid oxidation. The reac¬tion enthalpies of the concentrates were determined and the amount of heat generated up to various time were used to calculate the extent of reaction. Mineralogical changes at various stages of oxidation were also investigated. For this purpose a second set of DSC-experiments were carried out in which each experiment was interrupted at a desired temperature between 673-873 K. From these tests the weight loss of samples were determined and changes in the individual constituent of sulfide minerals were analyzed. For pentlandite-based Ni-concentrates the ignition temperature was 705-710 K (approximately 435 °C). Pyrite was the first sulfide to oxidize. Reactivity of the violarite-based concentrate was greater than those of the pentlandite-based concentrates. The stoi-chiometry of pentlandite changed before ignition because of preferential oxidation of iron. Rapid oxidation of the pentlandite mineral occurred at about 823 K (550 °C). By 900 K about 90 % of the iron in pentlandite was converted to hematite, and NiS containing some iron was formed.

Jan 1, 1994

By Liu Zhonghua

Hydrogen reduction of cobalt sulfide (Co9S8) was experimentally investigated in the temperature range 813-1053 K. The results revealed that the reaction kinetics can be described by the shrinking core mod¬el in chemical control regime at low temperatures, it is of first order with respect to hydrogen concentration, and the reaction activation energy is 67.4 kJ/mol. The SEM second electron images of the samples before and after experiments showed that the swelling of the sample above 973 K is due to the formation of metallic cobalt whiskers.

Jan 1, 1992

By R. Padilla

A thermogravimetric study has been conducted to follow the decomposition and volatilization of arsenic from enargite concentrate in nitrogen and slightly oxidizing atmospheres. Temperature has a large effect on the rate of volatilization of arsenic. Fractional volatilization of arsenic as high as 98% were obtained in less than 60 min at 650°C in nitrogen atmosphere, while in slightly oxidizing atmosphere the same volatilization could be achieved in 30 min. It was found that arsenic volatilizes as sulfide in nitrogen atmosphere and as 4xture of sulfide and oxide in atmospheres containing 1% oxygen. By using the pore blocking and the first order kinetic models, apparent activation energies of 213 and 200 kJ/mol for the temperature range of 780 - 900 K and 205 and 184 kJ/mol for the temperature range of 900 - 985 K were determined for enargite and copper concentrate, respectively.

Jan 1, 1997

By Leiting Shen

The thermodynamics of tungsten ore decomposition in mineral acid and alkaline solutions were studied. The published thermodynamic data of tungsten minerals were collected and assessed. The Gibbs energies of CaWO4 (−1538.43 kJ/mol), FeWO4 (−1053.91 kJ/mol), MnWO4 (−1206.08 kJ/mol), H2WO4 (−1003.92 kJ/ mol), and Na2WO4 (−1455.58 kJ/mol, aq) at 25 °C were adopted in the calculation using HSC software. The results show that CaWO4 is decomposed more readily in Na2CO3 solution than in NaOH,while FeWO4 andMnWO4 aremore reactive inNaOH solutions. Froma thermodynamic point of view, tungsten ore decomposes easily in acid solutions despite most ΔGo T increasing slightly with temperature. Oxidizing Fe2+ to Fe3+ in acidic solutions facilitates decomposition of FeWO4, and the reaction of CaWO4 in H2SO4 solution occurs more easily than in other mineral acids, due to the formation of sparsely soluble CaSO4. The results fit well with the experimental data and industrial experience previously reported in the literature.

By Anjali Talekar

Low temperature heat capacities of pentaerythritol [PE: C(CH2OH)4], pentaglycerine [PG: (CH3)C(CH2OH)3], and 2-amino-2-methyl-1,3-propanediol [AMPL: (NH2)(CH3)C(CH2OH)2]have been determined by adiabatic calorimetry from 3 K to 300 K. To the best of our knowledge, this is the first reported heat capacity measurement below 280 K for PE and AMPL. The Debye temperatures for these organic crystals have also been determined and compared with other alcohol derivatives of neopentane.

Jan 1, 2006

By Guohui Zheng

The ever increasing quantities of solid wastes generated by various industries are at the source of the growing need for proper waste disposal methods. Thermal treatment of combustible wastes is a proven technology which permits the reduction of hazardous material having to be landfilled. However, this method is not universally applicable to waste disposal. For example, the transferal of heavy toxic metals into the thermal remediation products is a major issue of public concern. This paper focuses on the analysis of morphology changes from solid sludge to ash which is a product of the sludge combustion. The morphological parameters analyzed were particle size and external surface. They were determined using Jeol 840 Super Probe. The experiments were conducted in a computer-controlled high-temperature combustion system consisting of the thermogravimetric furnace coupled with Fourier transform infrared spectrometer (TGA-FTIR). Sludge particles were made of complex fibers trapped in the aluminosilicate matrix. At low temperatures, up to 680 K, the solid residue looked similar to the initial sludge. Between 680 K and 1180 K the sludge underwent intensive burning and steadily changed into powdered ash. At the temperature of 1050 K the ash was composed of separate, flat flakes with sizes ranging from 5 to 20 um. At 1470 K the flakes aggregated into large particles. The surface observed at 1670 K was a mixture of mullite crystals. Such structure could result from the solidification of the ash material after its melting. Morphological changes influenced the distribution of metals in the solid residue. For example, Cr was concentrated in small aggregates. Such distribution should allow for recovery of valuable metals from the solid waste residue.

Jan 1, 1996

By W. G. Davenport

Chapter 6 examined autotherrnal smelting of pure chalcopyrite concentrate with 50 mass% O2-50 mass% N2 blast. It showed that production of 1500 K products with this blast requires: 181 kg of pure oxygen 337 kg of air per tonne, of concentrate. It also showed that the grade of matte produced with this blast is 58% Cu. This chapter re-examines autotherrnal smelting by asking: (A) WHAT COMPOSITION BLAST (MASS% 02 -MASS% N2), 298 K, WILL AUTOTHERMALL Y PRODUCE 65% Cu MATTE 1500 K FROM PURE CHALCOPYRITE CONCENTRATE? (B) HOW MUCH PURE OXYGEN AND AIR WILL BE NEEDED? These are important questions for flash? smelting because furnace operators usually want to send specific composition matte to converting. This chapter shows how a specified matte can be produced autotherrnally with 298 K oxygen-air blast. Later chapters show how it can be done with hot blast, hydrocarbon combustion, different concentrates etc.

Jan 1, 2001

By Byung-Su Kim

The recovery of elemental sulfur from sulfur dioxide has important implications for coal- burning power plants and nonferrous metal smelters. The thermodynamic analyses showed calcium sulfide to be suitable for recovering elemental sulfur from sulfur dioxide. At the temperatures of 1023 to 1153 K under the sulfur dioxide partial pressures of 5.0 - 60.1 kPa, elemental sulfur from sulfur dioxide was recovered by its reaction with calcium sulfide. The kinetics of this reaction were measured at the same conditions using a thermogravimetric analysis technique. This reaction scheme would be attractive if the coproduct calcium sulfate can be reduced to regenerate calcium sulfide. This is the topic of another paper. At 1073 K under the sulfur dioxide partial pressure of 25.8 kPa, 48 % of the original calcium sulfide was converted to calcium sulfate in an hour. Under the same conditions, 55 % of the regenerated calcium sulfide were converted to calcium sulfate in an hour even after third regeneration.

Jan 1, 1999

By Jie Li, Shu Yang, Zhongliang Tian, Xun Hu, Yanqing Lai, Shaolong Ye

The electrolyte with high solubility for Sc2O3 is very important to realize the preparation of Al-Sc master alloy by the molten salt electrolysis. The solubility of Sc2O3 in K3AlF6- Na3AlF6-AlF3 melts is determined with an isothermal saturation method. The effects of KR (ratio of K3AlF6 to K3AlF6+Na3AlF6), the concentration of Al2O3 and the temperature on the solubility of Sc2O3 are also investigated. The results indicate that the solubility of Sc2O3 in K3AlF6-Na3AlF6-AlF3 melts increases and then decreases with KR increasing. The solubility of Sc2O3 is 8.698 wt.% in (K3AlF6-Na3AlF6)(KR25%)-18 wt.%AlF3 melts at 940℃. The effect of temperature on the solubility is little, and the values are 8.575 wt.% and 8.762 wt.% respectively when the temperatures are 930℃ and 960℃. The solubility decreases from 8.809 wt.% to 7.058 wt.% as the concentration of Al2O3 increases from 1.5 wt.% to 5.0 wt.% at 950℃.

Jan 1, 2015

By Yang Cui

The partition ratios of lead and antimony between liquid copper and MgO saturated Cu2O-CaO-SiO2 flux and their removal rate by using CuCl-based flux were measured between 1423 K and 1573 K. For Cu2O-CaO-MgOsatd. system, the partition ratio of Pb was not affected by the CaO content at 1573 K, while that of Sb increased with increasing CaO content. The maximum value was 160 at the CaO content of 15.4 mass%. For Cu2O-CaO-SiO2-MgOsatd. system, two liquid phases of calcium silicate rich phase and Cu2O rich phase were observed at 1573 K. The partition ratios of Pb and Sb between calcium silicate phase and liquid copper depended on the (mass%CaO)/(mass%SiO2) ratio. When the (mass%CaO)/(mass%SiO2) ratio increased, the partition ratio of Pb decreased and that of Sb increased. For CuCl flux, the removal of Pb from liquid copper at 1473 K was possible, and a relatively low concentration could be reached. Moreover, most of lead as metal chloride vaporized from flux. For the removal of antimony from liquid copper at 1423 K, it was difficult by CuCl flux, and the removal ratio was approximately 20% for 75 minutes. However, the addition of CaO or Na2CO3 to CuCl flux was relatively effective to remove antimony, and the concentration of antimony reached a relatively low value after 15 minutes by using CuCl-CaO or CuCl-Na2CO3fluxes. Moreover, a small part of antimony as chloride vaporized from flux.

Jan 1, 2006

By Kenji Monden

"The creep properties of tin-based lead-free solders Sn3.0AgO.5Cu and SnO.7CuO.1Ni and lead solders 10Sn90Pb and 50Sn50Pb were investigated at temperatures between 298 K and 398 K. The creep-rupture time decreases with increasing initial stress and temperature. The analysis of the solder creep curves uses the Omega method. The creep rate E is expressed by following formula: 1n ? = 1n ?0 + O?, where ?0 and O are experimentally determined. The parameter Eo increases with increasing initial stress and temperature. The activation energy for ?0 is 108 kJ/mol for Sn3.0Ag0.5Cu and 85 kJ/mol for SnO.7CuO.INi. These energies suggest that the lattice diffusion of tin is dominant. The energy of 1OSn90Pb is 37 kJ/mol and that of 50Sn50Pb is 67 kJ/mol. The creep-rupture time is calculated using the parameters, ?0 and O. The calculated creep-rupture time is in good agreement with the measured creep-rupture time.IntroductionLead-free solders are replacing traditional tin-lead solders as part of a major trend toward protecting the earth's environment. However, tin-lead solders are currently needed for a high temperature range. Since creep is the main deformation mechanism in solder joints, understanding a constitutive model for creep and examining creep data for solders are important for reliability analysis of solder joints. A steady-state creep equation is generally used for solders [1,2], and it supposes that the secondary-, or minimum-, creep rate occupies the entire creep life. However, secondary creep accounts for only about 15 % to 40 % of the entire creep life for solders. Thus, the equation may not represent the entire creep life."

Jan 1, 2012

By Mariana H. Staia

Thermodynamic calculations based on the free energy minimization method were performed for the system Ti-Fe-Mn-0-C1-C in order to evaluate the chemistry associated with the chlorination of an ilmenitic concentrate using CCl4. In the calculations various weight ratios of FeTi03/ CC14, a , were considered, which varied between 0.32 to 0.98 at temperatures ranging from 673 K to 1273 K , at atmospheric pressure. The results obtained indicated that the operating conditions for a process in a packed bed reactor, which implies the chlorination of both Fe and Ti, are 0.39 < a < .49 at T 1173 K.

Jan 1, 1993

By Haotian Xue

A new process to extracted antimony directly from stibnite concentrate by reductive sulfur-fixation smelting in sodium molten salt has been presented. The influences of sodium salt content and composition, ferric oxide addition, temperature and time was investigated, respectively. The optimum conditions was determined as follows: W????: ??concentrate=40%, W??alt: ????concentrate =88.75%, WFe2O3 :Wconcentrate =55.13%, W??aCl: ????alt=40%, 1123K, 1h. Under above-mentioned optimum conditions, the average direct recovery ratio of antimony can reach 91.48%, and the main chemical composition of obtained crude antimony is Sb 94.31%, Fe 4.436%, Pb 0.502%, Au 0.0236%. In comparison to traditional antimony pyrometallurgical process, the smelting temperature of present process is reduced from 1423~1473K to 1123~1173K. During the smelting operation, SO2 emision can be avoided completely due to sulfur-fixation as FeS. Furthermore , S0 can be obtained when the molten slag is handled by water leaching with conditions of 323K, L/S=5/1, 2h.

Jan 1, 2014

By Y. K. Rao

In the carbonyl process for the refining of crude nickel CO(g) reacts with nickel in the 310-370K range producing nickel tetracarbonyl, Ni(C0)4(g). Iron and cobalt impurities also form gaseous carbonyls but their partial pressures are low. The carbonyl is led to a decomposer plant wherein the gas disproportionates in the 500-600K range depositing pure metal on nickel pellets that move countercurrent to the gas-flow. This system serves to illustrate the fundamental principles involved in the vapor phase mass transport of elements, against temperature-gradient, under the influence of chemical potential gradient. Unlike in the crystal growth, the source is at a lower temperature (say 350K) whereas the seed is in the hot-zone (say 550K) of the closed ampoule-type reactor. By assuming virtual gas-solid equilibria in the end zones, with diffusion of gaseous species between them acting as a slight perturbation, the quasi-steady- state mass-transport rates are computed for a range of CO-pressures and temperatures.

Jan 1, 1993

By José C. Escobedo B.

A kinetic study of nitrogen dissolution in a. electromagnetically stirred Co-Cr-Mo alloy bath was made. The experiments were carried out at 1693, 1723 and 1743K of temperature, with a nitrogen pressure of 0.67 atm. The mass transfer coefficients were obtained, finding that their values increase as temperature grows. The true kinetic constants were calculated. It was found that at 1693K of temperature, the kinetics of the nitrogen dissolution process is controlled by a mixed mechanism involving both transport processes and chemical reaction, while at 1723 and 1743K of temperature, the kinetics is controlled only by transport processes mechanisms.

Jan 1, 1995

By Do-Hyeong Kim, Tae-Jung Kim, Seung-Yeon Won, Jong-Jin Pak, Min-Kyu Paek

Liquid iron alloys containing V, Mo, and Ni can be produced by the carbothermic reduction of spent catalysts used in petrochemical industry. Thermodynamics of carbon in these alloy melts is important for refining these alloys. In the present study, the carbon solubility in Fe-V, Fe-Mo, Fe-Ni, Fe-V-Mo, Fe-V-Ni, Fe-Mo-Ni and Fe-V-Mo-Ni alloy melts of various compositions was measured at 1873 K. The temperature dependency of vanadium effect on carbon solubility in liquid iron was also measured in the temperature range from 1823K to 1923K. The additions of vanadium and molybdenum significantly increased the carbon solubility in liquid iron alloys while nickel decreased the solubility. The experimental results were thermodynamically analyzed using Lupis’ relation at constant activity to determine the first- and the second-order interaction parameters of vanadium, nickel and molybdenum on carbon at carbon saturated condition. Using thermodynamic parameters determined in the present study, the carbon solubility in Fe-V-Mo-Ni alloy melts of various composition were accurately predicted and verified experimentally at 1873 K.

Jan 1, 2014

By Hong Yong Sohn

A thermodynamic and experimental investigation has been performed to develop a new process for converting sulfur dioxide to elemental sulfur by a cyclic process. The most promising new process is a cyclic reaction scheme involving calcium sulfide and calcium sulfate. In this process, the reaction between sulfur dioxide and calcium sulfide produces elemental sulfur vapor and solid calcium sulfate. The latter is reduced by a suitable reductant such as hydrogen to regenerate calcium sulfide. &apos;Experimental results showed that up to 60 % of calcium sulfide powder was converted to calcium sulfate in 10 min at 1153 K under a sulfur dioxide partial pressure of 25.8 kPa. More than 95 % of nickel-catalyzed calcium sulfate powder was converted to calcium sulfide in 20 min at 1123 K under a hydrogen partial pressure of 86.1 kPa, water vapor being the only gaseous product. Sulfur dioxide-containing streams from certain new sulfide smelting plants contain much higher partial pressures of SO2. The rate of the first reaction is expected to be accordingly higher than in the test conditions reported in this paper.

Jan 1, 2002

By Phillip B. Messersmith, Emmanuel P. Giannelis

"A versatile in-situ polymerization approach is described for the synthesis of polymerceramic nanocomposites consisting of two-dimensional layers of mica-type silicate (MTS) within polymer matrices. Functionalized, organically modified mica-type silicates (OMTS) were used to promote delamination/dispersion of the host layers and initiate polymerization of organic rrionomer. Epoxy nanocomposites prepared in this manner exhibit substantial modulus reinforcement at low silicate loadings. The water vapor permeability of the poly(?-caprolactone) nanocomposite containing 4.8% silicate by volume was reduced by nearly an order of magnitude compared to pure poly (?-caprolactone).IntroductionPolymer matrix nanocomposites are a relatively new class of materials with dimensions typically in the range of 1-100 nm.1 In general, because of the ultrafine phase dimensions involved, nanocomposites exhibit new and improved properties when compared to their micro- or macrocomposite counterparts. We as well as others are currently investigating the design, synthesis and characterization of polymer-ceramic nanocomposites. Our effort, in particular, has focused on the use of mica-type silicates (MTS) with various thermoplastic and thermosetting matrices.2-5MTS's belong to the general family of 2: 1 layered silicates. Their crystal structure consists of layers of two silica tetrahedral sheets fused to an edge-shared octahedral sheet of either aluminum or magnesium hydroxide. Stacking of the layers leads to a regular van der Waals gap or interlayer.6 Isomorphic substitution within the layers generates negative charges that are counterbalanced by cations residing in the interlayers. Although the natural forms of MTS's usually contain hydrated Na+ or K+ ions, ion exchange reactions with organic cations (e.g. alkylammonium ions) can render the normally hydrophilic MTS's organophilic."

Jan 1, 1994