By L. Evrard, S. Brouwer, E. Bosly, E. Boydens

"A partial desulfurization roasting process has been tested on a typical copper-zinc sulfide concentrate in a Nichols Herreshoff monohearth pilot furnace whereby the su!fµr is partially removed and iron is to a certain degree preferentially oxidized. The phase changes that occur in the particles during selective roasting at 650°C and 800°C over a range of residence times were investigated by the use of chemical analysis, optical microscopy, X-ray diffraction and electron microprobe analyses. The purpose of this work was to get an insight into the mineral assemblages formed by controlled oxidation roasting and to evaluate if this non traditional approach could be afterwards used to recover zinc, copper and iron by a physical separation method. IntroductionThere has been considerable interest over the years in improving extraction and processing procedures for recovering non ferrous metals especially from polymetallic ores containing copper, lead, zinc and iron sulfides with very fine intergrown phases. Complex sulfide ores, which represent considerable reserves and resources in copper, lead and zinc, as well as precious metals and sulfur, are difficult to treat by conventional physical processes, leading to impure concentrates at low metal recovery. Some methods that can be used to treat such ores were described by G. Barbery (1). Various metallurgical routes generally combining pyro- and hydrometallurgical methods have been explored to develop new processes to recover the metals from zinc-bearing sulfidic ores and concentrates (2, 3, 4). The feasibility of partitioning complex sulfide minerals to simpler phases in order to improve selective extraction of mineral constituents has also been investigated (5)."

Jan 1, 1999

By J. W. Lyman

The U.S. Department of the Interior, Bureau of Mines, investigated methods to recover valuable rare-earth materials from NdFeB magnet scrap. Although several processing techniques were evaluated" the best separation of rare earths from the NdFeB magnet ,scrap was obtained by sulfuric acid dissolution followed by precipitation of recyclable rare-earth salts. Both sodium and ammonium intermediate double-salt precipitates' that can be converted to a variety of useful neodymium products were investigated. The sodium system showed a neodymium recovery of 98 pct, while the ammonium system yielded 70 pct during double-salt precipitation. The iron-rich effluent following the rare-earth recovery was treated to produce sodium and ammonium iron jarosites that can be disposed of or converted to hematite. By following this new procedure, many materials handling and economic disadvantages found with fluoride or oxalate direct precipitation were avoided.

Jan 1, 1992

By Kuniaki Murase, Tetsuji Hirato, Koji Nitta, Yasuhiro Awakura

"The redox behavior of copper species in an ""ammonium imide"" room temperature molten salt was examined in order to clarify the applicability of the salt to the electroplating media of various metals. Trimethyl-n-hexylammonium bis(trifluoromethanesulfonyl)- amide (TMHA-Tf2N), having an electrochemical window of 5.6 V (50 °C), and corresponding copper(II) salt were synthesized. In TMHA-Tf2N media monovalent copper ion, Cu(I), was stable and Cu metal was oxidized, or corroded, in the presence of Cu(II) species. Cathodic electrodeposition of copper metal and anodic dissolution of it were, thus, one-electron reaction and their current efficiencies were almost 100%.IntroductionElectrodeposition of metals from aqueous solutions is an important soft process for manufacturing thin-film materials, surface finishing, and extractive metallurgy. However, the electrodeposition of base metals, such as zinc, chromium, and nickel, from aqueous media inevitably accompanies hydrogen evolution, which lowers the cathodic current efficiency of metal deposition. Since the electrodeposition of aluminium, titanium, and rare earths from aqueous media is actually impossible due to their largely negative redox potentials, nonaqueous media such as aprotic organic solvent and high-temperature molten salts have been employed for the electrodeposition of these metals. Room temperature molten salts (RTMS),1, 2) or room temperature ionic liquids, have also been developed as a promising electrolytes for the electrodeposition of base metals. In this field, chloroaluminates of alkylpyridinium or alkylimidazolium cation have been well investigated for aluminium3) or alluminium-alloy4-5) electroplating media. On the other hand, in order to avoid high hygroscopicity arising from the use of aluminium chloride, attempts have been made to combine the alkylimidazolium cations with fluorine-containing hydrophobic anions, e.g. BF4-,6) CF3SO3- (TfO-),7) (CF3SO2)2N- (Tf2N-),8) and H(HF)n-ions,9) and investigated for electrodeposition media.'°) Recently, a new series of RTMS consisting of tetraalkylammonium cations and Tf2N- anion, sometimes abbreviated as TFSI- anion, was found independently by MacFarlane et al.11, 12) and Matsumoto et al. 13) This type of RTMS, which is commonly named ""ammoniumimide"" salt, has a wide electrochemical window of ca. 5 V and, thus, the RTMS seems to be suited for practical application as a solvent for the electrodeposition process. In this paper, we report the electrochemical behavior of copper species in an ammoniumimide RTMS, trimethyl-n-hexylammonium bis(trifluoromethanesulfonyl)amide (TMHA-Tf2N)."

Jan 1, 2000

By Florian Kongoli

The so-called "fayalite" slag, despite problems associated with it, is the most widely used slag in copper smelting processes. Thirty years ago, in order to overcomes some drawbacks of this slag a new "calcium ferrite" slag was proposed especially for continuous copper converting. Since both slags have strong and weak points depending on the field of their application about 8 years ago another new "ferrous calcium silicate" slag was proposed that is expected to solve the drawbacks of each slag. This new slag is defined as mainly consisting of FeOx, CaO and SiO2 as its main components but it can practically have several combinations of these constituents. In order to determine the best area of this slag for possible industrial application the quantification of phase relations is an important subject. In this paper the work carried out by the authors in quantifying through an original physical model the phase relations, liquidus surface, liquidus regions, behavior of solid phases and the effect of minor components is reviewed. Several special compositions of this slag have been identified and discussed for possible applications in the industrial practice.

Jan 1, 2006

By Bryn Harris

Chesbar Resources Inc.1 is developing a nickel-cobalt laterite project in Guatemala, Central America, by applying existing atmospheric chloride technology to a known resource. The tropical laterite project has an inferred resource of 133 million tonnes grading 1.51% nickel, which represents ~20% of Chesbar?s land holdings in Guatemala. Within its boundaries, the Sechol area has a measured resource of 14 million tonnes grading 1.46 % nickel and 0.08% cobalt, and an indicated resource of 23 million tonnes grading 1.34% nickel and 0.08% cobalt. Notwithstanding the impressive overall resource, the company has taken an innovative approach to a laterite project and is concentrating on El Inicio, a high-grade starter pit with five million tonnes grading 2.1% nickel and 0.08 % cobalt. The process flowsheet is based on atmospheric chloride leaching in a slightly acidic magnesium chloride brine, solution purification by recycled magnesia, precipitation of a mixed nickel/cobalt hydroxide intermediate product, and lixiviant regeneration by modified pyrohydrolysis technology. Initial results suggest that >90% of the contained nickel and cobalt in the non-magnetic fraction of the feed can be recovered, with <5% of the iron leaching. A metallurgical scoping study has established preliminary capital and operating costs for a production facility at a proposed rate of 20,000 tonnes per year of nickel as the intermediate mixed hydroxide. A preliminary assessment of producing a magnesium oxide by-product has also been carried out. This paper reports on the current development of the project and highlights the advantages of working in a chloride medium at atmospheric pressure and slightly elevated temperatures.

Jan 1, 2003

By W. K. Choi

Stainless steel exposed to wet environments at ambient temperature is subject to the formation of a surface biofilm. Depending upon the prevailing environmental conditions (dissolved oxygen, pH, Eh, concentration of cationic/anionic species), the biofilm may stimulate corrosion through formation of differential aeration zones and concentration cells. Corrosion significantly impacts the United States economy, since on a yearly basis, corrosion induced losses are estimated to be over $200 billion. A large portion of this corrosion is imputable to bacterial activity, and basic information is needed for a better understanding and control of the biocorrosion phenomenon. The present study has investigated the influence of Thiobacillus ferrooxidans in the corrosion of American Iron and Steel Institute (AISI) 304, 316 and 416 stainless steel samples. The formation of biofilm and microstructural changes on the surface of stainless steel samples and their weldments were assessed by microscopic examination, and the changes in the mechanical properties by stress-strain measurements. The significance of the results will be discussed.

Jan 1, 1993

By Kenneth N. Han

Thermodynamic and kinetic aspects of nickel and cobalt leaching from metals. minerals and ores in various media have been reviewed and discussed in this paper. A kinetic model developed to delineate the leaching mechanisms for these metals has been discussed in view of experimental observations. The current review also includes the dissolution behavior of nickel and cobalt from various minerals such as oxides, sulrides. ocean floor manganese nodules, and laterites. A particular emphasis has been extended to similarities and differences of the dissolution behavior of these two metals in various media. The leaching of nickel as well as cobalt metal in acidic solutions and arnmoniacal solutions exhibits in most part mass transfer controlling. although at some pH&apos;s, chemical controlling or mixed controlling mechanisms seem to prevail. The leaching of nickel and cobalt from oxides in acids and ammoniacal solutions. on the other hand, can be described best by chemical controlling mechanisms.

Jan 1, 1993

By Riyad N. Ahmad-Bita, Shadia J. Ikhmayies

"SnO2:F/CdS:In structures were prepared by the spray pyrolysis technique on glass substrates at a substrate temperature Ts = 450°C. NH4F and HF were both tried as the sources of fluorine in the precursor solution of SnO2:F. A comparison between the properties of structures obtained by using the two doping compounds was performed. X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmittance measurements were used to characterize the films. The structures prepared by using HF as a fluorine source were found to have more ordered crystal growth, larger grain size and sharper absorption edge. From the inspection of the first derivative of the absorbance it is expected that more interdiffusion on the SnO2:F/CdS:In interface takes place in the structures made by using HF. These results confirm that these films are better as forecontacts for CdS/CdTe solar cells.IntroductionThin film CdS/CdTe solar cells built in the superstrate geometry rely on transparent conducting oxides (TCOs) to make the front contact The investigation of combined CdS-TCO films has recently been developed owing to the great interest of better understanding the effect of these bilayers on the absorbers [1]. Usually SnO2 is utilized as a front contact for these solar cells. Optimizing the properties of the SnO2/CdS structures is an important step on the way to get high performance CdS/CdTe solar cells.There are different methods to prepare SnOz thin films, such as reactive sputtering [2], evaporation [3], chemical vapour deposition [3, 4], dip coating [5] and spray pyrolysis [6-9]. At the same time CdS thin films can be prepared by different techniques such as chemical bath deposition [10], thermal evaporation [11], screen printing [12] and spray pyrolysis [7, 13]. However, the spray pyrolysis technique is a very low cost and simple technique that enables intentional doping and getting large area and uniform thin films [14]. For these reasons it is choused to prepare SnOz and CdS thin films in this work. To improve the properties of these compound semiconductors, SnOz was doped with fluorine and CdS was doped with indium where such doping is well known for these compounds."

Jan 1, 2012

First, a classification of the various primary sources of feed materials for the production of cobalt is presented from a mineralogical point of view : sulfides, arsenides, sulfo-arsenides and oxide minerals. Each of these cate- gories will be characterized by its behaviour towards concentration methods, taking account of the presence of the associated minerals of other metals and of the nature of the gangue minerals. Then, for each category of cobalt bea- ring ores, typical flowsheets of treatment will be presented and discussed and the characteristics of the cobalt concentrates produced will be under- lined having in view their subsequent processing by pyro - and (or) hydrome- tallurgical methods.

Jan 1, 1988

By R. Boom, B. Kraaijveld, H. Kuntzel, Y. Meteleva-Fischer

"Alloying refining with rare earth elements followed by acid leaching was examined for the potential of upgrading of metallurgical grade silicon. Microstructure study of silicon alloyed with small additions of rare earths showed behavior relatively similar to the influence of calcium addition. After alloying with neodymium the phosphorus content was detected in various intermetallic silicides containing neodymium and iron. The content of lanthanum and neodymium in refined silicon was by several times lower than that of aluminium and calcium. Alloying with lanthanum and neodymium at smaller additions than calcium reduced the phosphorus content down to the same level. The efficiency of lanthanum and neodymium in removal of boron and phosphorus at the 1-2 wt% of their additions and their low solubility in silicon make the alloying with these metals followed by acid leaching an attractive option for the refining route of metallurgical grade silicon up to solar grade.IntroductionA striving for a cheap ""green"" energy directs the research interests in silicon solar cells towards new efficient refining routes for metallurgical grade silicon (MG-Si, -98% purity). The silicon price determines up to high extent the solar module's price, so that cheap and efficient metallurgical process is awaited. The research challenge is to fulfil the purity requirements of solar grade silicon (SoG-Si, 6N) by competing with the energy-consuming and environmentally unfriendly Siemens process. Most difficult impurities to remove are boron and phosphorus, so technologies dedicated to their efficient removal attract an attention of industry and academia.Alloying refining (also known as solvent refining) is one of the most promising refining options, which is based on a principle of solid-liquid extraction using limited solubility of impurity elements in solid silicon [ 1]. Various elements were proposed for alloying refining: aluminium [2], calcium [3], tin [4], iron [5], copper [6] etc. The attractiveness of the alloying refining is in decreasing a melting point of the metal mixture and an affinity of the alloying element to the most harmful impurities, especially to boron and phosphorus. However, the difficulties are still faced due to self-solubility of the alloying elements, their low affinity to boron and/or phosphorus, silicon losses and necessity of removal of the silicide impurity phases in an additional step, using acid leaching [7], fractional melting [ 8] etc."

Jan 1, 2013

By Ryosuke O. Suzuki

A combined process of electrolysis of CaO in the molten CaCl2 and of calciothermic reduction, so-called OS process, was applied to prepare metallic vanadium directly from V2O3. The fine metallic powder containing 1860 mass ppm oxygen was obtained using 0.5mol%CaO-CaCl2 melt for 10.8 ks at 1173 K. The oxygen level did not decrease further even when twice electricity was applied. Because the metallic vanadium could be electrochemically deoxidized to the level of 10 ppm oxygen from 1.48 %, the large amount of by-product, CaO, due to reduction and the large surface area of the fine particles are the reasons of high oxygen content in the reduced powder.

Jan 1, 2006

By John Hanna

The University of Alabama Mineral Resources Institute (MRI) has developed a unique process for selective fatty acid flotation of carbonate gangue from sedimentary apatites (francolite) in the pH range of 4-6, without collector conditioning of the pulp. The process, which does not require an apatite depressant, was modified to beneficiate a high MgO siliceous phosphate matrix from South Florida. The modified process includes two flotation stages, one for carbonate removal, as mentioned above, and the other for phosphate recovery from the siliceous gangue. The selective flotation separation of the carbonate and phosphate from siliceous constituents of the matrix at various pH levels and collector dosages are discussed. In the carbonate flotation stage, about 70% of the MgO was rejected in the froth, and the phosphate flotation stage produced concentrates analyzing about 31% P20S&apos; 0.7% MgO and 4% acid insolubles. The overall P20S recovery in the two stages is about 85%.

Jan 1, 1989

By C. E. M. Meskers, U. Boin

"The increasing use of coated magnesium in consumer products results in creation of coated Mg scrap during product manufacture and after End-of-Life product treatment. Currently this material is generally not recycled, leaving a material resource unused. Closure of the magnesium cycle in a sustainable manner is necessary. In order to do so, the effect of coatings on the recycling process has to be quantified, predicted and minimized. For this purpose metrics have been developed, based on first principles supported by detailed understanding of the recycling process. The developed 3D metric enables quantitative assessment of the recyclability and links coating design, product design and recycling to each other in a visual manner. The parameters that form the metric can be measured and predicted, hence an engineering basis for Design for Sustainability of coated magnesium is provided.IntroductionEvery product progresses through the four phases of the product life cycle depicted by figure 1. In each phase residues are created. Their amount and composition is largely determined by the complex material combinations created/invented during product design in the manufacture phase. Compared to the ideal cycle the magnesium cycle is far from closed (fig. 2). Most noticeable is absence of the link between the EoL phase and raw materials production. A closed cycle only exists for class 1 scrap, which goes from the product manufacture phase directly to production from industrial material and returns to the manufacture phase as magnesium alloys. The four problematic streams are marked by ???. Coated semi-products are present in two of the four residues, namely in rejects and collected scrap. When these semi-products are recycled the amount and composition of the dross and salt slag residue is affected as well.During product design selection of the coating takes place, fixing the coating character¬istics and properties from this moment on for the rest of its life cycle. The choices made in the manufacturing phase are therefore critically linked to the recyclability of coated semi-products as well as the sustainability of the magnesium cycle as a whole. Sustainable closed life cycles, in which the quality of materials is preserved and residue creation and resource depletion are minimized, can be attained by selecting the appropriate alternative during product design. To realize this the effect of design choices on the life cycle and more specific the recycling process has to be known and quantified."

Jan 1, 2008

By Erik Olsson, Gunilla Hyllander, Stefan Schuster, Lena Sundqvist Ökvist, Maria Lundgren, Michael Hensmann, Olavi Antila

"Residual materials from the integrated steel plant itself or other sources often contain valuable compounds of e.g. C and Fe. Dust and sludge have to be agglomerated to be able to recycle to the blast furnace (BF) via top-charging. By injection of the materials, preparation methods in terms of e.g. drying and/or screening only, can be used. Alternative carbon materials (ACM) in terms of BF dust and sludge have been successfully injected up to levels of 60 kg/tHM in the LK.AB Experimental Blast Furnace (LKAB EBF®). Efficiency in recovery of valuable compounds as well as the behavior of undesired elements have been evaluated and are discussed.IntroductionTraditionally, recycling of steel in-plant fines is made via the sinter plant and blast furnace route. Steel plants operating with 100% pellet as ferrous burden and have no sinter plant. There are limited areas for land fill and costs are caused for preparation of landfills and deposit fees. Very fine paniculate dusts or sludges cause decreased productivity and increased coke rate in the sinter plant, and therefore other ways for recycling must be considered. Injecting them into the BF could be an economically and technically feasible alternative. Additionally, as the materials contain valuable compounds of e.g. C and Fe."

Jan 1, 2012

By René Winand

A new process was studied at large laboratory scale at Université Libre de Bruxelles, under contract with Metallurgie Hoboken-Overpelt. A two cathodes (1m long ; 0.2 m high) channel cell was used at 2000 A/m2, with an electrolyte flow rate up to 1.8 m/sec. The main results may be summarized as follows : cathodes are electro¬refined grade in analysis ; metallographic structure and surface roughness are kept under control up to 1.3 cm (one side deposits) ; silver in cathode is controlled by CI and Br ions in solution ; organics must be used at very low concentrations (in the range of 0.1 mg/1, with a consumption of about 0.01 mg/lh).

Jan 1, 1987

By Gaballah I.

Elimination of arsenic, mercury and zinc from synthetic solutions containing H;\A.sD4. HgCI2 and ZnCI2 using modified barks was investigated. The pH range was varied from ?1 to 10. The initial concentrations of individual element were 10,100 and 1000 ppm. More than 99 % of mercury and 65 % of zinc cations were removed by the modified bark .. In this case, the modified bark reacts as a cation exchanger leading to the release of &apos; two protons for every HgII or ZnII fixed by this material. About 30 % of arsenic was eliminated from the solution. This &apos;low efficiency could be attributed to? the presence of arsenic ,as. anion. Decontamination of a treated industrial effluent containing 4 ppm of ion? metals was performed on a pilot plant scale by the modified bll(k. More than 70&apos;% of these ion metals were eliminated.

Jan 1, 1995

By Wang Yun-yan

In order to examine the adaptability and the kinetics of leaching different gold ores in alkaline thiourea system, six kinds of gold concentrate and/or calcine with different physical and chemical properties were chosen as objects. The leaching behaviors in alkaline thiourea system with high stability, acidic thiourea system and alkaline cyanide system were compared. Changes of phase, surface appearance, particle distribution and specific surface area of six kinds of gold ores before and after leaching were studied in virtue of modern analytic techniques, e.g., XRD, SEM, and so on. The results indicate that alkaline thiourea solution can be used to leach gold ore, for oxidized gold concentrate removed arsenic by microbe pretreatment(4#) the leaching rate of gold is up to 82.68%, such conclusion overthrows the parlance reported that pH value must be less than 1.78, or gold can not dissolve in thiourea solution. Chemical components and phase are related to gold leaching rate, different gold ores are fit for different leaching system, and alkaline thiourea solution is suitable for the pretreated oxidized gold ores with low content of sulfur and in which the main phase was SiO2, phase almost does not change after leaching basically. Generally speaking, when leaching in alkaline thiourea solution, surfaces of gold ores with glaze change greatly to ones with coarseness, distinct trace and holes of corrosion. Particle size decrease and specific surface area increase of gold ores after leaching in alkaline thiourea solution with high stability except gold concentrate of Zhongyuan gold smelter(5#).

Jan 1, 2006

By Rainer Schmid-Fetzer

"Isothermal solidification can be used to form strong bonds at low temperature which remain solid at much higher temperatures. The exploitation of this principally known technique for new high temperature processing steps and applications in electronic assemblies is the aim of this study. Three basically different variants of this bonding process are given. A comprehensive metallurgical screening is performed and the feasibility of binary material systems is given on a quantitative scale. Very attractive systems are spotted that have never been studied before. Detailed examples for the realization of bonding with complex ternary and multilayer systems are given. A highly innovative example is the chip stack or wafer to wafer bonding of unmetallized Si or SiC at 250°C. The proposed bond remains stable above the melting point of Si and enables entirely new semiconductor manufacturing steps. An improved die bonding process was proposed and verified experimentally.1. IntroductionIsothermal solidification can be applied to form strong bonds at relatively low temperature which remain solid at higher temperatures. The general principle of this type of joining processes is illustrated in Fig. 1. An interlayer of a low melting component, Lo, is provided as a foil or a thin film coating between the high melting joint components, Hi. The assembly is heated under moderate pressure to the bonding temperature, T 8 , and a liquid filler forms, either because the melting point of Lo is exceeded or due to a eutectic reaction between Lo and Hi. This molten filler initiates a rapid interdiffusion or reaction diffusion between Lo and Hi and the subsequent approach to an equilibrium state results in isothermal solidification. The solid phases formed at T 8 in the joint region exhibit a remelt temperature above T8 •"

Jan 1, 1996

By Akira Yazawa

Oxidic dissolution loss of metal in slag is discussed thermodynamically in terms of oxygen potential, activity coefficient and equilibrium constant. To understand basic principle, regular solution model is applied for model calculation of the activity behaviour of metal oxide in FeO-SiO2-CaO slag, and effects of slag composition, temperature, and basicity of oxide on dissolution loss are demonstrated. As: a simplified but practical conclusion, the dissolved metal loss in slag is inversely proportional to activity coefficient of metal oxide, and also to FeO content in slag when amount of slag is taken account.

Jan 1, 1994

By M. C. Esposito

Seven pyrite samples purified from coal sources and one ore source pyrite (for comparative purposes) have been characterized by chemical and mineralogical analyses, inherent floatability, apparent specific gravity, surface area, semiconductor type, optical anisotropy, dissolution and oxidation rate. The data clearly demonstrate that pyrites from various coal sources differ not only from ore pyrite but from each other as well.

Jan 1, 1987