By R. A. Grange, H. M. Stewart

Man.; steel parts may crack if quenched directly into a bath near room temperature, but not if quenched at a temperature just above the range where martensite forms and then allowed to cool slowly to room temperature. This latter procedure, which is the basis for such modern hardening techniques as "martempering" and "isothermal quenching," may entail some sacrifice in depth of hardening but very little, if any, in intensity of hardening. In planning such treatments, it is necessary to know the upper limit of the martensite range, and often desirable to know the proportion of martensite that would form on cooling to any lower temperature; furthermore, the tendency of a particular steel to crack when quenched is unquestionably associated with the temperature range of martensite formation, and consequently knowledge of this range aids in selecting the optimum composition for a given application. Certain puzzling phenomena associated with the properties of quenched and tempered steel may be at least partly clarified as the manner in which martensite forms is more fully understood. Information on the temperature range of martensite formation, particularly with respect to how much martensite results from quenching to a given temperature, is lacking for most commercial types of carbon and low-alloy steel. These considerations led us to study martensite formation in 14 carbon and low-alloy steels. The resultant data may be directly used in the following ways: (I) for selecting the lowest quenching temperature at which no martensite will form; (2) for selecting the highest quenching temperature at which virtually all marten . site will form, thereby avoiding quenching to an unnecessarily lower temperature with attendant danger of cracking; and (3) in producing a mixture of tempered martensite and bainite, which in high-carbon steels has been found to possess somewhat better ductility than tempered martensite, yet does not require the full transformation time necessary for a completely bainitic (austempered) structure. PART I. OBSERVATIONS OF MARTENSITE FORMATION IN FOURTEEN CARBON AND LOW-ALLOY STEELS Transformation of austenite to pearlite or bainite can be conveniently studied by observing the change that occurs over a period of time at constant temperature; such studies are the basis of the isothermal transformation diagram (S-curve). This isothermal technique is not applicable to martensite formation, which occurs within a time interval too small to measure, at least by any ordinary means. For all practical purposes, therefore, martensite may be regarded as forming only during cooling and not during a period of time at constant temperature. As austenite is cooled below

Jan 1, 1947

By H. M. Stewart, R. A. Grange

Man.; steel parts may crack if quenched directly into a bath near room temperature, but not if quenched at a temperature just above the range where martensite forms and then allowed to cool slowly to room temperature. This latter procedure, which is the basis for such modern hardening techniques as "martempering" and "isothermal quenching," may entail some sacrifice in depth of hardening but very little, if any, in intensity of hardening. In planning such treatments, it is necessary to know the upper limit of the martensite range, and often desirable to know the proportion of martensite that would form on cooling to any lower temperature; furthermore, the tendency of a particular steel to crack when quenched is unquestionably associated with the temperature range of martensite formation, and consequently knowledge of this range aids in selecting the optimum composition for a given application. Certain puzzling phenomena associated with the properties of quenched and tempered steel may be at least partly clarified as the manner in which martensite forms is more fully understood. Information on the temperature range of martensite formation, particularly with respect to how much martensite results from quenching to a given temperature, is lacking for most commercial types of carbon and low-alloy steel. These considerations led us to study martensite formation in 14 carbon and low-alloy steels. The resultant data may be directly used in the following ways: (I) for selecting the lowest quenching temperature at which no martensite will form; (2) for selecting the highest quenching temperature at which virtually all marten . site will form, thereby avoiding quenching to an unnecessarily lower temperature with attendant danger of cracking; and (3) in producing a mixture of tempered martensite and bainite, which in high-carbon steels has been found to possess somewhat better ductility than tempered martensite, yet does not require the full transformation time necessary for a completely bainitic (austempered) structure. PART I. OBSERVATIONS OF MARTENSITE FORMATION IN FOURTEEN CARBON AND LOW-ALLOY STEELS Transformation of austenite to pearlite or bainite can be conveniently studied by observing the change that occurs over a period of time at constant temperature; such studies are the basis of the isothermal transformation diagram (S-curve). This isothermal technique is not applicable to martensite formation, which occurs within a time interval too small to measure, at least by any ordinary means. For all practical purposes, therefore, martensite may be regarded as forming only during cooling and not during a period of time at constant temperature. As austenite is cooled below

Jan 1, 1947

By W. W. Simpson, W. L. Staker, R. G. Sandberg

The Bureau of Mines investigated selective extraction of Au and Ag from a low-grade Au ore containing Hg. Gold and silver were extracted from the ore in cyanide slurries, and Hg extraction was suppressed with sodium or calcium sulfide. Maximum Au extraction and minimum Hg extraction were obtained using solutions containing 17 kg NaCN/t of solution (0.34 lb NaCN/st). Increasing the cyanide concentration increased Hg extraction without increasing Au extraction. Mercury extraction from the ore was suppressed with 0.5-2.9 kg CaS/kg Hg (0.5-2.9 lb/lb) in the ore. Gold-to-mercury ratios of 100:1 to 400:1 were obtained in the leach solution, and on the activated carbon in a CIP circuit.

Jan 1, 1985

By R. F. Domagala, M. Hansen, D. J. McPherson

Iodide zirconium was combined with calculated amounts of nitrided zirconium sponge and arc melted to prepare alloys in the 0 to 6 wt pct N region. Annealing treatments were carried out at 21 temperature levels. Metallographic examination of the heat-treated specimens permitted construction of the binary phase diagram from 0 to 6 pct N. Features of the diagram include the peritectic formation of both a and ß solid solutions. The maximum solubility of nitrogen is 0.8 pct in 8 zirconium and 4.8 pct in a zirconium. An X-ray study of nitrided materials was made in the range 6 to 13 wt pct N region because serious nitrogen losses were experienced when attempts were made to arc melt these high nitrogen alloys. PHASE relationships in the Zr-N system have been determined. Due to the inability to retain nitrogen in nitrogen-rich alloys subjected to arc melting, definitive work was possible only in the range 0 to 6 wt pct (0 to 30 atomic pct) N. Sufficient complementary X-ray work was done to permit construction of the binary phase diagram up to 13.3 wt pct (50 atomic pct) N (ZrN). Small ingots were prepared by arc melting master alloys with enough zirconium to produce an alloy of the desired composition. Following pretreatment, alloys were annealed at temperature levels between 600" and 2020°C. Determination of the phase boundaries was then accomplished by metallographic evaluation of specimens quenched from the various temperatures. Incipient melting techniques were used to corroborate solidus curves, and X-ray diffraction was employed to study the nitrogen-rich region of the a + ZrN phase field. Materials Westinghouse Grade 1 iodide zirconium crystal bar served as the base material for this investigation. The as-received bars were lightly sandblasted, pickled in a 20 pct HN0-5 pct HF aqueous solution, rinsed in water and acetone, and dried. They were rolled to about 1/32 in. strip and acid-pickled, followed by water and then acetone rinses. The material was sheared to approximately 1/4 in. squares, cleaned with acetone, and stored for use. Pure zirconium nitride is not commercially available, according to correspondence with possible suppliers. A literature survey indicated that nitrogen may be introduced into zirconium metal by passing nitrogen or ammonia gas over zirconium at an elevated temperature. After considerable experimentation, a train was devised whereby high quality nitrogen was passed through a series of bubblers to remove the last traces of oxygen, through an H,SO, bubbler and a cold trap to remove moisture, and finally over zirconium within a resistance furnace. Hand-picked Bureau of Mines magnesium-reduced zirconium sponge proved more amenable to nitriding than the crystal bar. The nitrogen used was extra pure gas purchased from Linde Air Products Co. The first two bubblers through which the gas was passed contained a solution suggested by L. F. Fieser" as being ideal for removing the last traces of oxygen from nitrogen. The solution contains 20 g KOH, 2 g sodium-anthraquinone ,9-sulphonate, and 15 g NaHSO, dissolved in 100 ml water. It is blood-red and turns brown when contaminated with oxygen. A saturated lead acetate solution, next in the series of bubblers, removed any H2S which might have formed in the 0, removal stage. An H,SO, bubbler and cold trap removed moisture before the nitrogen was passed over the zirconium. The zirconium was contained in a stainless steel screen within a Vycor or quartz tube in a resistance furnace. Unreacted nitrogen passed out of the system through a mercury bubbler. A nitriding run was performed in the following manner: Zirconium was placed in the screen within the furnace tube. The unit was assembled, suitably clamped off, and evacuated to remove the air and moisture within the tube and that trapped by the zirconium sponge. The unit was flushed with nitrogen and evacuated twice. After nitrogen was allowed to pass over the zirconium for about 30 min, the furnace was turned on; several hours were required to reach temperature. The reaction was allowed to continue at temperature for about 4 hr and the screen was then withdrawn from the hot zone of the furnace by means of a Nichrome or Kanthal rod. The screen and its contents were allowed to cool at the end of the tube and were then removed. At 800°C no more than about 5 pct N could be introduced into the sponge zirconium. This material was designated M-1 (master alloy No. 1) and reserved for the preparation of alloys in the dilute nitrogen region. A second set of experiments was conducted at 1000°C; no more than 7.2 pct N could be introduced into the zirconium at this temperature. Enough material (M-2) of this nitrogen content was prepared to produce a second set of alloys to complement the first and to provide alloys in the 0 to 6 wt pct N range. It was hoped that a diffusion anneal plus a re-nitriding might yield a material of higher nitrogen content. The material containing about 7 pct N was therefore given a homogenization treatment at 1000°C for 6 hr under an argon atmosphere. It was

Jan 1, 1957

By J. D. Ridge

The geologic setting and mineral relationships of seven European massive sulfide deposits that more or less conform to the bedding of the largely noncal-careous sedimentary rocks and/or bedded volcanics in which they are found are considered here. These orebodies consist largely of massive beds or lenses of sulfides usually surrounded by halos of disseminated sulfides and distorted by tectonic activity. The formations containing these deposits have been metamorphosed in varying degrees at times subsequent to their lithification. The ore-forming process is thought to be essentially volcanic, with the ore constituents being brought to the shallow-water site of deposition through tectonic fissures from magma chambers at depth as gases or relatively concentrated hydrother-mal solutions. Certain European ore deposits of base metal sulfide have previously been considered to be of hydro-thermal or magmatic origin, but today a number of European mining geologists consider them to be syngenetically produced. In an effort to provide American geologists with some idea of the reasons behind this change in thought, the geological settings of seven of these deposits have been studied. These are: Ldkken, Meggen, Rammelsberg, Ergani-Maden, Outokumpu, Boliden and Roros. These deposits lie in bedded rocks that have undergone metamorphism from causes not universally agreed upon; most of the formations were originally shales, and may have been intercalated with limey and occasionally quartzitic beds, volcanic tuff, agglomerate, extrusive lavas and usually basic intrusives. Deposits of the conformable type, however, are not confined to these rock types but may be in calcareous and associated igneous rocks or almost entirely in volcanics. These deposits may be closely associated in space with igneous rocks that, again, are usually basic types. Although the ages of the enclosing rocks range from mid-Precambrian (Boliden and Outokumpu) to Eocene (Ergani-Maden), the bulk of them are Paleozoic, with two (Meggen, and eammelsberg) being upper middle Devonian and two (LØkken and RØros) being Cambro-Ordovician. Geographically, two are in West Germany, four in Scandanavia and one in Turkey. Of the seven deposits, six are mined for copper, with three of these also producing zinc, and two lead; one is mined for zinc and minor lead. In the discussions of the seven conformable deposits that follow, I have attempted to present as uniform a treatment as their varying characters will permit. For each deposit, I have considered the stratigraphy of the area, its major structural characteristics, the form of the orebodies, their mineral content, and the origin of the ore. In the last of these subdivisions, I have presented only the viewpoint of those who believe the ores to have been formed by syngenetic processes, processes that went on at the same time as those which produced the beds that enclose the ores but that are not, in the deposits in question, thought to have been sedimentary in the strict sense of the term. The materials of which these orebodies are composed, it is suggested, did actually collect by falling through sea water to the floor of that portion of the sea in which they accumulated. The ore constituents, however, are believed by a considerable number of European geologists to have been added to the sea water from intratelluric sources, probably igneous magma chambers, as exhalations — hydrothermal solutions or volcanic gases. The effect of the encounter with sea water on these ejected gases or water-rich vapors was to precipitate their potentially solid constituents with great rapidity; they were deposited so quickly, in fact, that the amounj of normally accumulated mechanical or chemical sediment deposited over the same period of time was essentially negligible. The ores formed in this manner, however, are generally interbedded with normal sediments or with lava flows, or with any combination of these two types of rock-forming materials. Such departures as these deposits may have from their original mineral content and attitude are thought to be directly related to the degree of dynamic or static metamorphism that they may have undergone after their accumulation. I have not attempted here to present alternate hypotheses to that of so-called exhalative sedimentation although, of course, such exist and, in my

Jan 1, 1963

By A. Satter

Studies of wellbore heat transtnission during the injection of a hot fluid, as either gas or liquid, have appeared in he literature. The present investigation takes into account the effect of condensation, which is of practical sig-nificance when considering steam injection operations. Calculation procedures are given for superheated and for saturated and undersaturated steam. Effects of injection rate, time, pressure, temperature and depth of a well on heat losses have been analyzed. The benefits of using a packer are discussed. Also presented are correlations for estimating heat losses involved during injection of saturated steam. INTRODUCTION Studies of wellbore heat losses during the injection of a hot fluid have appeared in the literature. Ramey' has presented a useful solution for calculating temperature of a heated gas as a function of depth and injection time. Ramey and others have also presented solutions for the hot liquid case.'. ' No method is available to take into account the effect of condensation, which is of practical significance when considering steam injection operations. This paper presents a method of estimating the quality of a condensing fluid as a function of depth and time. The approach is basically the same as that used by Ramey. The following injected fluids and conditions are considered in this study: 1. Injection of superheated steam A. Decrease in temperature until cooled to the saturated state B. Condensation until condensed completely into hot (saturated) water 2. Injection of saturated or undersaturated steam; condensation until condensed completely into hot (saturated) water. Although this investigation does not include cooling of water after steam is completely condensed, Ramey's solution for the hot liquid case can be used for this purpose. The effects of various process variables on heat losses During the injection of steam into a well are investigated. THEORY QUALITY OF CONDENSING STEAM Predicting the behavior of condensing steam flowing down the injection wellbore requires an estimate of the quality of steam, i.e., the mass fraction of vapor in the mixture. Let us divide the total depth of the injection well into several segments which might be, but do not have to be, of equal magnitude. Consider condensation within a given depth interval AZ, the bottom of which is located at a depth Z from the surface (Fig 1). The following equation, derived in the Appendix- relates the quality of steam at the bottom of an interval to that at the top of the interval:

Jan 1, 1966

By D. H. Gieskieng

THE advent of curved jaw crusher wearing plates made an approach other than segmental layout analysis desirable for prediction of capacities. For some time it had been known that the drawing board capacities of crushers using these plates had to be considerably modified by complicated experience factors to achieve agreement with results. Because these apparent capacities could be readily increased severalfold by minor crushing chamber shape changes, it was necessary that the utmost precaution be taken in predicting capacities of jaw plates modified for nonchoking, special wear characteristics, or any other reason. To this end the laboratory and field tests outlined by the author in a previous paper1 were made on Blake-type jaw crushers. The results of these tests were summarized in a simple first degree equation applicable to crushers using either straight or curved jaw plates. This equation first outlines the maximum capacity potential of a given crusher, then reduces this figure in accordance with installation circumstances by means of a realization factor. It was found subsequently that this equation, with the addition of an eccentric throw factor, is applicable to standard types of single-toggle or overhead eccentric jaw crushers as far as maximum capacity potential is concerned. However, these crushers have realization factor curves somewhat different from those outlined for the Blake type. While this paper is concerned principally with standard type single-toggle crusher capacities, the evaluation of data obtained with these machines is simplified by comparative reduction to the 10 x 7 in. Blake-type equivalents upon which the summary of the preceding paper was made. Convertibility of data from one type of crusher to the other also tends towards confirmation of both. The agreement of these data is sufficient to be considered complimentary. Consequently the feed factors, f, previously reported for Blake crushers are slightly adjusted to an average with the single-toggle crusher results. Blake-type equation: C = f.d.w.y.t.n.a.r [I] Single-toggle type equation: C = f.d.w.y.t.n.a.e.r [21 where C is the capacity in short tons per hour through the crusher, f is a feed factor, dependent upon the presence of fines in the feed, and the surface character of the jaw plates used. Values of f : Smooth Plates Corrugated Plates With normal fines 0.0000414 0.0000319 Fines scalped out 0.0000368 0.0000252 Large pieces only . 0.0000312 0.0000215 d is the apparent density of the broken product in pounds per cubic foot. (If the true specific gravity of the feed is known, 40 pct voids may be assumed and d becomes 37.4 times sp gr). w is the width of crushing chamber in inches. y is the openside setting of the crusher, in inches. In the case of corrugated jaw plates it is measured from the tip of one corrugation to the bottom of the valley opposite. t is the length of jaw stroke in inches at the bottom of the crushing chamber. It is the difference between open and close-side settings. n is rpm, or crushing cycles per minute, a is the nip-angle factor. It is unity for 26" and 3 pct greater for each less nip-angle degree. A nip-angle of 20" has an a value of 1.18, and an angle of 30" has an a value of 0.88, see Fig. 1. r is the realization factor. It is unity for perfectly uniform choke feeding and usually less for actual operating conditions according to the method of feeding used and the probabilities of hang-ups involving the size of feed and crusher opening. Approximate values are given by the curves in Fig. 2. These values are further reduced by intermittent feeding, e is the throw or diameter of gyration of the single-toggle crusher eccentric in inches. As evident in Fig. 1A, variation of feed size will generally have little effect on nip-angle if both jaw plates have flat areas. Jaw plates having continuous curvature, as in Fig. 1B will have different nip-angles, depending upon the size of feed. For test work as described in this paper this effect was accounted. For general compilation of capacities for average feeds it is suggested that the nip-angle be taken at the various settings computed, at an arbitrary level, such as is indicated in Fig. 1C. Data Evaluation To bring the Blake and single-toggle type crusher capacity test results to common terms for evaluation, all data are converted to terms of 10 x 7 in. Blake-type performance at conditions of 100 lb per cu ft, 10 in. chamber width, 250 rpm, 0.65 in. stroke, 3-in. openside setting, and 18° nip-angle. (The nip-angle of the 10x7 in. Blake is 18° at 3-in. setting.) The single-toggle crusher performances are also divided by the eccentric throw to bring this effect to unity. As outlined,' laboratory and field tests made on Blake-type crushers ranging from 10 x 7 in. to 60 x 48 in. were summarized along the foregoing conditions of speed, stroke, etc. This resulted in groups of data which correspond to feeds with fines, feeds

Jan 1, 1952

By C. O. Rison

HIGH explosives, particularly nitroglycerin, have been used in torpedoes for the purpose of shooting oil and gas wells for more than 60 years. The early history of the oil industry in Pennsylvania is not clear as to who actually torpedoed the first well, although in 1865 the Roberts Torpedo Co. procured a patent covering the process. Gunpowder was first used, although nitroglycerin was substituted shortly afterwards. Wells are shot for the purpose of increasing the flow of oil and gas A shot-hole in the producing horizon, with its contributory fissures and fractures, increases the area of and stimulates drainage into the hole. The shot-hole also acts as a collecting basin from which the oil is pumped. As a rule, hard or close-grained sands or limes are shot, other more or less porous and soft formations usually do not require shooting. and might be injured by blasting. Shooting is also resorted to in mechanical trouble such as straightening crooked holes, sidetracking pipe or tools, and for severing frozen strings of casing or drill pipe. Explosives arc also used sometimes to extinguish oil or gas-well fires although that work, which involves unusual conditions and methods, does not properly come within the classification of oil-well shooting. Some Factors to Be Considered in Shooting Wells Although nitroglycerin has been used extensively for more than half a century in shooting oil and gas wells, there is still a great deal of uncertainty as to the proper method of shooting or the amount of explosive required to produce best results in a particular formation. The possibility of shooting unproductive or cavey formations above or below the productive horizons, shooting into lower water, destroying casing seats, and the splitting or collapsing of casing strings, are factors that require consideration. The engineering departments of a number of the larger oil companies are making a study of methods of shooting, and the amounts of liquid nitroglycerin or other explosives required in shooting various productive

Jan 1, 1929

By R. W. Gurry

IN the course of a series of measurements of the rate of diffusion of carbon in austenite at about 960°C. (1760°F.) and 1110°C. (2030°F.), it became necessary to determine carbon concentration when austenite is saturated with graphite, because of indications that the hitherto accepted value of the solubility of graphite in this temperature range is too low. Specimens of carbonyl iron were saturated at temperature in a hydrogen-toluene atmosphere which was in equilibrium with graphite. The carbon content of the steel was measured either by combustion or by the loss of weight after substantially complete decarburization in an atmosphere of hydrogen saturated at room temperature with water vapor. The absence of carbide or graphite as a phase at temperature was demonstrated by microscopic examination of saturated specimens that had been drastically quenched. The mean result of concordant measurements is that gamma iron saturated with respect to graphite contains 1.39 per cent carbon at 957°C. (1755°F.) and 1.89 per cent at 1110°C. (2030°F.). These two values, plotted along with what appears from the literature to be the best value (0.69 per cent) at the iron-graphite eutectoid temperature (738°C. or 1360°F.), yield a curve that is almost linear, and which, continued upward through a short interval, leads to a limiting solubility of 1.98 per cent at the iron-graphite eutectic temperature 1135°C. (2075°F.) instead of the commonly accepted value of about 1.7 per cent. EXPERIMENTAL PROCEDURE The samples of carbonyl iron, with the exception of those for microscopic examination, were cylinders 3.8 cm. long, 0.475 cm. in diameter. They were placed in a graphite holder and suspended in a vertical furnace, the temperature of which was controlled precisely by means of the resistance of the platinum winding.1 In the empty furnace the range of temperature over a distance of 4 cm. at the heat center was 9°C. (16°F.) but at a given location the temperature remained within ±0.5°C. (0.9°F.); it was measured by inserting a platinum-rhodium couple calibrated at the melting point of palladium, 1555°C. Since the presence of the sample probably improved the uniformity of temperature, it was decided to consider the average temperature of the sample to be 3°C. lower than the maximum measured in the empty furnace with the same setting of the controller. Data were obtained in the vicinity of two temperatures, 960°C. (1760°F.) and 1110°C. (2030°F.). The samples for microscopic examination, 2.2 cm. long, 0.475 cm. in diameter, were suspended individually on pure iron wire; for these no temperature correction was applied. The carburizing gas passed into the furnace was dry, oxygen-free hydrogen saturated at room temperature with

Jan 1, 1942

By Charles S. Barrett

Metallurgists are making use of the stereographic projection to a steadily increasing extent. In the last five years no less than 20 papers in American metallurgical journals alone have employed the stereographic projection; recent books on physical metallurgy, plastic deformation, X-rays and their applications, and crystal structure use it. Mineralogists have used the stereographic projection for many years in the description of symmetry classes and crystal planes, for it presents an accurate, easily understood plot of any angular relations in crystals with all unessential features eliminated (such as the accidentally determined size and shape of crystal faces). In metallography and physical metallurgy the projection is much used for the analysis of markings appearing on polished grains: slip lines, twins, cracks, structures formed by precipitation, magnetic-powder patterns, etch pits, etc. Data from certain types of X-ray photograms are most conveniently analyzed by its use, particularly those for determining the orientation of single crystals or the preferred orientation of grains in an aggregate. Calculations of how to tilt or cut a crystal parallel to a certain crystallographic plane or to reflect X-rays from a certain plane are rapidly carried out. It has been adopted almost universally to the exclusion of other methods by those studying the deformation of metallic crystals, save where the accuracy required is greater than a few tenths of a degree. Any directional property in a crystal or polycrystalline material can be shown on a stereographic projection; for example, the modulus of elasticity, yield point, etc. It has been repeatedly called to our attention that there is need of an elementary explanation of the principles and methods of stereographic projection, covering all the common applications in the field of metallography and physical metallurgy. The following contribution is an attempt to fill this need. The description of each method is supplemented with references to publications in which the method has been used. For convenience to the reader, these illustrative references are chiefly in American journals, particularly the publications of the American Institute of Mining and

Jan 1, 1937

By H. Kahata, I. Iwasaki, Y. Takahasi

A combined process of segregation roasting-flota-tion or magnetic separation was developed to recover nickel from lateritic iron ores and oxidized nickel ores. An ore was mixed with a halide, such as sodium or calcium chloride, and a solid reductant, and roasted, whereby the nickel content was segregated out as discrete metallic particles. Either by magnetic separation, or by flotation using a sulfhydryl collector together with a heavy metal salt as an activator, the metallic nickel could be concentrated, Effects of such variables as the types and amounts of the halide and solid reductant addition and of the roasting conditions were extensively investigated. The concentration results on several types of ores from Japan, the Philippines, and New Caledonia are presented. Laterite is a residual product of rock decay in tropical and subtropical regions, and consists mainly of hydrated oxides of iron and alumina. Those derived from serpentine sometimes become enriched in nickel, cobalt, and chromium contents. Oxidized nickel ores are of the similar origin, but their nickel as well as silica contents are higher due to gamierite-type silicates. Apparently, nickel enrichment is more pronounced in the transition region between the surface layer of iron laterite and the underlying serpentine. Iron laterites often contain over 50% iron, and their reserve is reported to exceed 22 billion tons, corresponding approximately to 20% of the world iron ore reserve.1 It is readily apparent, therefore, why the iron laterites have attracted much attention of the steel industry as a potential source of iron ores. Numerous attempts to remove nickel and chromium as byproducts, have been reported in literature.' Worldwide discoveries of high-grade iron ore deposits in recent years have inevitably lessened the interests in iron laterites. However, in view of the tremendous potential for their gross value and supplies of nickel, cobalt, chromium, and alumina along with iron, the problem remains as a challenge. Much of the chromium in laterites is present in the form of relatively coarse particles of chromite, and various classification methods have successfully been applied for its removal.2,3 The nickel, however, is intimately associated with limonite, and ordinary concentration techniques are totally ineffective. Much attention has, therefore, been given to hydro-metallurgical or pyrometallurgical means. Yet, all the known processes appear to have limitations either economically or for the use of products as iron raw materials due to a high residual content of nickel. Some attempts have been made to pre-roast laterites or oxidized nickel ores, particularly with sulfidizing agents, and to remove nickel either by magnetic separation,' or by flotation.4 It is apparent that any such concentration process would require grain growth of nickel during roasting for effective separation. Oxidized copper ores are reported to be concentrated by the segregation roasting-flotation process,5 in which the ores are roasted with a chloridizing agent and a carbonaceous reductant in order to promote the growth of metallic copper through repeated cycles of copper chloride volatilization and its reduction on the solid reductant surfaces. Examination of a vapor pressure-temperature diagram of various metal chlorides indicates that a separation of nickel from iron may be effected by a similar process. In fact, the segregation roasting of laterites was reported to increase the extraction of nickel by the ammonia leach process, as compared to the ordinary reduction roasting.6 In the present article some of the preliminary experimental results of the segregation roasting, followed by either flotation or magnetic separation, on laterites and oxidized nickel ores are reported. The effects of various parameters in the roasting as well as in the concentration steps are discussed. MATERIALS AND METHODS An oxidized nickel ore from Thio, New Caledonia, and three laterites from Homonhon, the Philippines, Wakasa and Miyagawa, Japan, were selected for the

Jan 1, 1967

By H. C. Johnson, J. K. Elliott

One of the primary requirements for successful operation of an enriched gas-drive project is to control the composition of injection gas. This can become a serious and difficult problem, particularly in cases where the enrichment material is being furnished from a number of field -produced gas streams. It is possible to effect control of the injection gas composition through frequent or continuous sampling; however, this can be extremely costly and, in many cases, impractical due to laboratory requirements of time. Another alternative would be to provide a calculation technique which would be flexible and sufficiently accurate to predict composition of the liquid and gas streams of interest at any point in the system. The purpose of this paper is to discuss a technique that was used successfully on an operating enriched gas-drive project for developing information which could be used for controlling composition of the injected gas. FIELD OPERATIONS The particular field (hereafter called Example field) in the example operation being discussed is composed of four oil reservoirs (A. B, C and E) and one gas condensate reservoir (D). Casinghead gas from the oil reservoirs and gas from the gas condensate reservoir are gathered through a field gathering system as shown in Fig. I for injection into Reservoir C. The gas mixture which is recovered from the five reservoirs for injection purposes is composed of gases liberated in 19 individual separators, each operating at a separate temperature and pressure. PROPOSED CALCULATION TECHNIQUE It is well known that vapor-liquid equilibrium calculations in general use throughout the petroleum industry can be used to predict reliably the phase behavior of hydrocarbon mixtures, particularly at pressures less than 1,000 psig. It is then a simple matter to account for the material on a ComPonent basis by m''ing flash and material balance calculations at each separation point in a hydrocarbon system. Accordingly, it was proposed to use vapor-liquid equilibrium and material balance cal- culations with a medium-sized electronic digital computer as a basis for developing a control procedure for use in controlling injection gas composition in the enriched gas-drive project. Although the approach is a simple one, the numerous vapor-liquid equilibrium calculations involved make the problem laborious; in this particular case, it would have been impractical to make sutficiently complete analysis without the aid of digital computing equipment. SAMPLING AND VERIFICATION OF CALCULATION PROCEDURE To obtain representative gas and liquid stream samples and to provide a quantitative measure of overall system Performance for comDarative purpLses, a thorough test of the field and plant system was conducted in the summer of 1957. Oil production at each battery was sta-

By C. M. Wayman, J. F. Breedis

The crystallography of the martensitic transformation in the Fe-30 Ni alloy was reinvestigated. The scatter in the habit Plane as determined from measurements on the mid-rib plane was smaller than reported previously, and the orientation relationship was determined from a martensite plate having known direction cosines. From agreement with crystallographic theory and from observations of the morphnlogy of the martensite plates, it is suggested that the mid-rib plane represents the starting region of the transformation. THE crystallography of the martensitic transformation in the iron-nickel system has been the subject of many investigations.&apos;-7 However, for iron alloys containing approximately 30 wt pct Ni, a wide scatter in the reported habit planes exists. In only one instance has a Laue determination of the orientation relationship been made, but the habit plane of the martensite plate studied was not determined experimentally. Because the most successful thermodynamic and kinetic analyses8 of the martensite transformation have been based on Fe-30 Ni alloys, it was considered desirable to reinvestigate the crystallographic features of the transformation in this alloy. Lieberman9 suggested that the most significant information for use in a theoretical treatment involves the determination of all the crystallographic observables from a single plate of the product phase. This was first done in essence by Greninger and Troiano10 for Fe-22 wt pct Ni-0.8 wt pct C, and is the method followed in this investigation. Some theoretical approaches11-13 in describing the martensitic transformation consider the overall transformation distortion to be comprised of a Bain distortion, or lattice deformation (PI, which produces the structure change, and a lattice invariant deformation (G), such as twinning, which together leave the interface or habit plane un-distorted. The incorporation of a rigid body rotation (R) results in a transformation distortion (E) such that the interface plane is left both undistorted and unrotated. In matrix notation, E = RPG where the lattice invariant deformation has "taken place" in the austenite. Bowles and Mackenzie14-16 in formulating a theoretical approach proposed an adjustable scaler quantity, denoted as 6, which represents a uniform dilation in the interface plane. This dilation acts to adjust the lattice spacings of the parent and product structures at the plane of contact. Using the dilation parameter as a variable, these authors were able to account for a continuous variation of habit planes in steels along a curve in the stereogram between {225}A and {259}A. she invariant line strain14 of the transformation is 6 RP, and the corresponding transformation distortion is E/6.) With the dilation parameter known, the invariant line is computed as the triple coincidence of the habit plane, the shear plane of the lattice invariant deformation, and the initial Bain cone.14 The contraction axis for the Bain distortion can be taken9&apos;17 as [010]A, and the correct permutation of the habit plane indices used. Kelly and Nutting 18 have established the shear plane (of twinning) in the tetragonal martensite of Fe-22 Ni-0.8C to be {112)M by means of transmission electron microscopy. The reasonable shear system is then {112}M which is equivalent to {011}A <01l>A. The as-

Jan 1, 1962

By C. E. Lesher

Low-temPeRatUre carbonization needs no introduction to the literature on coal. This paper will attempt no review of that literature; it tells the story of the commercial development of one of the processes for carbonizing coal at so-called low temperatures, dealing with the technology and economics of the process rather than with the design of equipment. The process used is that covered by the patents of C. B. Wisner, with improvements and changes made by the Pittsburgh Coal Carbonization Co. The important and novel feature of the process is the phenomenon of making the product in ball form (Fig. 1). Melting coal dust into smokeless solid fuel in an apparatus as simple as a revolving cylinder of ordinary mild steel has been proved to be practical. Furthermore, it has been found that the process has a wide application, for by applying a knowledge of why and how this balling action is accomplished, the apparatus can be designed and adapted to treat any coal that has a certain minimum agglutinating property. The operating plant is 20 miles west of Pittsburgh, adjacent to the Champion preparation plant of the Pittsburgh Coal Co. The coal used is cleaned minus ?-in. or finer sizes. The products are low-tem-perature coke, tar and tar products. Present capacity is 7000 tons per month of low-temperature coke and 140,000 gal. of tar. There is no surplus gas for sale, and none of the light oils are stripped from the gas. The coke is marketed in two sizes, 1 to 2 in. and 1 to 6 in., through retail coal dealers for domestic consumption in hand-fired furnaces, and for fireplace fuel. The smaller size is bagged by dealers. Crude tar and many distillates and road tars are sold. Acknowledgments During the 10 years in which the work that is summarized in this paper has been under way, many have contributed time and effort, faithful service and fruitful thinking. Whatever success has attended

Jan 1, 1940

By C. E. Lesher

Low-temPeRatUre carbonization needs no introduction to the literature on coal. This paper will attempt no review of that literature; it tells the story of the commercial development of one of the processes for carbonizing coal at so-called low temperatures, dealing with the technology and economics of the process rather than with the design of equipment. The process used is that covered by the patents of C. B. Wisner, with improvements and changes made by the Pittsburgh Coal Carbonization Co. The important and novel feature of the process is the phenomenon of making the product in ball form (Fig. 1). Melting coal dust into smokeless solid fuel in an apparatus as simple as a revolving cylinder of ordinary mild steel has been proved to be practical. Furthermore, it has been found that the process has a wide application, for by applying a knowledge of why and how this balling action is accomplished, the apparatus can be designed and adapted to treat any coal that has a certain minimum agglutinating property. The operating plant is 20 miles west of Pittsburgh, adjacent to the Champion preparation plant of the Pittsburgh Coal Co. The coal used is cleaned minus ?-in. or finer sizes. The products are low-tem-perature coke, tar and tar products. Present capacity is 7000 tons per month of low-temperature coke and 140,000 gal. of tar. There is no surplus gas for sale, and none of the light oils are stripped from the gas. The coke is marketed in two sizes, 1 to 2 in. and 1 to 6 in., through retail coal dealers for domestic consumption in hand-fired furnaces, and for fireplace fuel. The smaller size is bagged by dealers. Crude tar and many distillates and road tars are sold. Acknowledgments During the 10 years in which the work that is summarized in this paper has been under way, many have contributed time and effort, faithful service and fruitful thinking. Whatever success has attended

Jan 1, 1940

By Edward H. Robie

PROBABLY nowhere in the United States or its possessions is mining development more active at present than in the Philippine Islands. Only a few years ago only one company was of any importance, the Benguet Consolidated. Now, five companies are paying dividends, five others have reached the producing stage, some seven others may produce this year, and a score or so are being actively developed. Gold production in 1933 was valued at about $8,000,000, last year at about $11,000,000, and this year an output valued at about $17,000,000 is envisaged. At the beginning of 1934 about 1750 tons of ore was being milled daily; at the end of the year, the tonnage was approximately 3400. In 1933 there were only thirteen Institute members in the Philippines; a year ago there were 27, and now there are 46. About fifteen thousand amen were employed in the mining industry last year, with mine payrolls amounting to $3,500,000. An immense amount of new machinery has been required. One difficulty has so far hindered gold-mine development to some extent-lack of adequate power. Each company therefore finds it necessary to generate its own power, and for this purpose diesel engines are generally adopted.

Jan 1, 1935

By E. B. REESER

EFFICIENCY is the foundation on which the prosperity of this Nation must be built. Your organization and the members thereof are constantly thinking of Gays and means whereby greater efficiency may be developed. It is often said that this Nation has become great because of its almost up limited supply of raw materials at low production &apos;costs. This was undoubtedly true in the earlier years but today we face an entirely different situation. We have learned that nature has been very generous in supplying all parts of the world with ample resources of various kinds to meet the demands. This applies to practically all commodities but for the purposes of this discussion, we will limit our remarks to petroleum.

Jan 1, 1931

By T. C. Campbell

Copper is extracted from the Chuquicamata oxide ore by a hydro-metallurgical process. The ore is crushed to 3/8-in. sizing, and leached with a sulfuric acid electrolyte. Chlorine is precipitated. and the ferric iron reduced in the enriched electrolyte, after which the copper is recovered by electrolysis with insoluble Chilex and lead-antimony anodes, the spent electrolyte being returned to leaching. Cathodes are melted and refined in market furnaces and cast into commercial wire-bar and cake shapes. Sulfuric acid for the process is supplied by the brochantite in the ore. Water for washing the ore is advanced through the solution system and finally after cutting by electrolysis to from 6 to 16.0 grams per liter is completely stripped by the cuprous chloride method and run to waste. The cuprous chloride so obtained plus that resulting from precipitation of chlorine from strong solution is dissolved in ferrous chloride brine and the copper cemented on scrap iron. The cement so obtained is in part used to reduce ferric iron in electrolyte, and as it is of exceptional purity is also furnace refined and cast into an exceptional quality of fire-refined copper. Fig. 1 is flow sheet of the operation. The reduction plant is composed of seven divisions as follows: (1) crushing, (2) leaching, (3) tailings disposal, (4) dechloridizing, (5) sulfur dioxide treatment, (6) electrolytic tank house, (7) smelting and melting. A brief description of each of these divisions will be given. Crushing Ore that is frequently blocky and up to 5 ft. in section is crushed in four stages to 3/8-in. mesh. The first stage of crushing is called primary and the next three stages are known as secondary crushing. The first stage is accomplished with two 60-in. Superior McCully gyratory breakers by which the ore is broken to 9 in. The second coarse gyratory breakers crush the ore to 3-in. sizing. There are seven No. 10 McCully gyratories in this service, for one of which recently has been substituted a No. 7 cone crusher. The third and fourth stages of crushing are accomplished by fifty 48-in. disk crushers. In the third stage 14 disk crushers break the ore to 1 in., and in the last stage 36 disk crushers turn out the final product of 0.371-in. sizing. Reference to the flow sheets of Figs. 2 and 3

Jan 1, 1934

By George W. Bain

Methods of mining building stone of any sort are planned to produce as few fractures as possible, and present a strong contrast to methods of mining metallic ores, which must be crushed eventually and have fractures produced in as great profusion as possible. Shocks transmitted to a stone invariably make it more porous and more permeable and reduce its effective life, therefore methods of mining building stone involve as This building illustrates the fine detail of workmanship, unprotected sharp corners and thin edges, and tall narrow columns characteristic of marble structures. These features require exceedingly coherent stone, and preservation of these features for decades or centuries demands many special quarrying precautions to keep absorption to 0.14 per cent or less, a detail not essential to stone for coarser architectural types. few shocks as possible. This is singularly true for marble because marble structures are intended to have long life, greater delicacy of line, more gracefulness and fineness of sculpture than those made from any other structural material (Fig. 1). So that delicate lines may remain in almost perfect preservation for decades, or even centuries, it is important

Jan 1, 1938

By George W. Bain

Methods of mining building stone of any sort are planned to produce as few fractures as possible, and present a strong contrast to methods of mining metallic ores, which must be crushed eventually and have fractures produced in as great profusion as possible. Shocks transmitted to a stone invariably make it more porous and more permeable and reduce its effective life, therefore methods of mining building stone involve as This building illustrates the fine detail of workmanship, unprotected sharp corners and thin edges, and tall narrow columns characteristic of marble structures. These features require exceedingly coherent stone, and preservation of these features for decades or centuries demands many special quarrying precautions to keep absorption to 0.14 per cent or less, a detail not essential to stone for coarser architectural types. few shocks as possible. This is singularly true for marble because marble structures are intended to have long life, greater delicacy of line, more gracefulness and fineness of sculpture than those made from any other structural material (Fig. 1). So that delicate lines may remain in almost perfect preservation for decades, or even centuries, it is important

Jan 1, 1938