Jan 1, 1896

By V. G. Cawagdan, E. M. Sacris

The performance of the grinding circuit, from the initial stages of operation to the present, is discussed. The mill efficiency as measured by the Bond (Bond and Maxson, 1943) grindability data and the operating work index is presented. The objective was to produce a sand cyclone overflow containing not more than 6% 210 µm (+ 65 mesh). This has never been attained, even at low milling rates. Significant improvements in throughput were achieved by instituting equipment changes and process modifications within the grinding circuit. Grind improvements were achieved with enlargement of cyclone spigots, grinding at reduced densities, and decreasing the opening of the ball mill discharge. Additional grinding capacity was realized by converting the concentrate regrinding mill into a secondary ball mill. The previous 20% 210 µm (+ 65 mesh) grind improved to under 15% 210 µm (+ 65 mesh). The latest approach to solving the coarse grind problem is also discussed.

Jan 1, 1985

By H. Larson, J. Chipman

The ferrous and ferric oxide concentrations of slags, expressed as j = Fe+++/(Fe+++ + Fe++), have been established through gas-slag equilibrium at 1550°C in a range of oxygen pressure of 10-I to 10-9 equilibriumatm. The value of j is increased by basic additions (BaO, CaO, MgO, MnO) and decreased by acidic oxides (SiO2 and TiO2). Oxygen pressure is shown graphically as a function of composition for slags which are analogous to those at the slag-gas interface of the open hearth furnace. THE progress which has been made in recent years in understanding the chemistry of metallurgical slags has been based largely on studies of slag-metal and slag-gas equilibria. There is a considerable body of knowledge which is applicable to reactions occurring at the slag-metal interface in open hearth steelmaking. There is little information concerning reactions of the slag with the furnace atmosphere and hence little basis for an understanding of the transfer of oxygen, sulphur, or hydrogen between gas and slag. The oxygen pressure of the open hearth atmosphere is normally of the order of 10-1 to 10-3 atm which differs by several orders of magnitude from that of about 10" atm at the slag-metal interface. The chemical properties of the slag, for example, the ratio of ferric to ferrous iron and the ability of the slag to hold sulphur in solution, are greatly affected by changes in oxygen pressure. This investigation was undertaken to enlarge our knowledge of the effect of oxygen Pressure on steel-making slags. Using air or controlled mixtures of CO a CO2 a range of oxygen Pressures from 10.' to 10.' was covered. Review of the Literature There are only a few references in the literature which pertain directly to this investigation. The most important is that of Darken and Gurry1,2 on the system iron-oxygen. This work included the determination of the phase diagram of the system and also a study of the field of homogeneous melts and their oxygen pressures. Their apparatus and procedure were very similar to that used in this study. Iron oxide was melted in a platinum crucible under an atmosphere of CO2:CO, CO2:H2, H2O, CO2, air or O2 depending upon the partial pressure of oxygen desired. After equilibrium was reached, the sample was quenched and analyzed for ferrous and ferric oxide. By appropriate calculations these authors were able to determine the oxygen and iron activities in the various slags, heats of formation of the oxides of iron, and heats of solution of iron and oxygen in the liquid slags. In a subsequent paper' the same authors made a less thorough investigation of the effects of additions of lime and manganese oxide on the composition of iron oxide melts. Only a few experiments were made and those in a narrower range of temperature and oxygen pressure. Darken' has investigated the fusion temperature of iron oxide in contact with silica under various atmospheres. He found that the temperature changes from 1120° to 1447°C as the gas composition changes from CO2/CO equal to 20.8 to pure oxygen. A comprehensive paper by White" predates the work of Darken and Gurry. The decomposition of ferric oxide into oxygen and lower oxides of iron was studied from 1000° to 1650°C and under oxygen pressures from 2 to 76 cm of mercury. The effect of

Jan 1, 1954

By Harvey Brooks

Jan 1, 1963

By R. L. Smith, J. L. Rutherford

ALTHOUGH considerable effort has been devoted toward the determination of the mechanical properties of pure metals, it is extremely difficult to compare the results of such work. This is because of differences in method and type of test, grain size, heat treatment, and purity of material. There is very little information on the properties of most of the high melting point reactive metals with purities greater than 99.9 pct. Previous evidence concerning the tensile properties of unalloyed metals show that: body-centered-cubic metals are brittle at low temperatures; face-centered-cubic metals remain ductile; some hexagonal metals remain ductile, others become brittle. It may be that traces of impurities decrease the low temperature ductility of the body-centered-cubic lattice. This would suppose that a body-centered-cubic lattice free from impurities would exhibit nearly the same ductility as a face-centered-cubic structure. The present investigation has been an evaluation of the tensile properties of zone refined iron in order to determine whether higher purity material than that previously evaluated behaves differently. Experimental Procedure In this investigation, high purity iron was zone purified using the floating zone method.' The starting stock was obtained from two sources. The first,

Jan 1, 1958

By R. S. Dean

THE first attempt to establish an equilibrium diagram of the lead-antimony series was made by Roland-Gosselin1 in 1896. This investigation classified the system as a purely eutectiferous one, with the eutectic at 12.5 per cent. antimony and 228° C. In the next year, Stead2 placed the eutectic temperature at 247° C. The error in temperature made by Roland-Gosselin, however, has been perpetuated in the literature with a remarkable degree of persistency; this value was accepted by Campbell (1902), and Ewen (1910),3 and will be found in the last edition of Desch's3 Metallography (1922). Gonterman's investigation, made in 1907, was the most complete one available at the time the present investigation was started. He concluded' that the system was a simple eutectiferous one and placed the eutectic at 13 per cent. antimony and 247°C. Other investigations by Tammann (1907),5 Garbow (1909),6 Rudolfi (1910),7 Loebe (1911),8 and Leroux (1913)9 added little, if any-thing, to Gonterman's diagram. A number of investigations have been made of physical properties of the alloys. The electrical conductivity of the series was studied by Matthiessen (1860)10 and by A. W. Smith (1921);" the thermoforce by Rudolfi (1910),12 and Pelabon (1923);13 the specific heat by Durrer

Jan 2, 1926

ALABAMA Alabama City.-Eddy, L. Altoona.-Cain, J. America.-Foreman, J. T. Anniston.-Foster, R. N. Ashland.-Sturdevant, J. C. Bessemer.-Ball, E. M. Calhoun, F. W. Maschmeyer, W. L. McKenzle, W. C., Jr. Birmingham.-Abbott, C. E. Aldrich, T. H. Aldrich, T. H, Jr. Ashton, J J.

Jan 1, 1923

Jan 1, 1923

By C. A. Zapffe

BOTH the foundryman and the theoretical metallurgist are now generally agreed that the anomalous "rising" or "bleeding" of certain ferrous castings of killed metal is primarily attributable to hydrogen. How and why the phenomenon occurs, however, have not been made clear. The following discussion is intended to harmonize foundry experience with metallurgical theory so that the foundryman may possibly improve his ability to prognosticate whether a certain casting may bleed or not. BLEEDING, RISING, AND PIPING The "rising" to be discussed here is not to be confused with the action in rimming ingots as a result of the carbon-oxygen reaction, although a conclusion will be drawn that may apply to the art of controlling the rimming action. Only killed metal is considered, which includes both steels and irons. In Fig. I, three killed, chill-cast ingots are shown: a porous ingot whose evolution of gas during late stages of solidification has ejected metal through the top; an ingot in which moderate gas evolution during solidification has lifted the mushy central metal, i.e., it has "risen"; and, third, a sound ingot with good piping characteristics. The first type is referred to as "bleeding," and generally infers that a solid skin had first formed through which the liquid metal later erupted. There is no fundamental distinction between bleeding and rising in reference to killed metal.* POROSITY Hydrogen appears as a cause of bleeding because the gas evolution simultaneously leaves a porosity of a type traceable to hydrogen. Twenty years ago, Melmoth1 noted that killed steel that rose unexpectedly in the mold, if returned while liquid to the furnace and heated further under a reducing lime slag, would again rise in the mold; but that if the ingot were allowed to solidify and was then remelted no rising occurred. A critical quantity of the responsible gas is therefore removed by the rising action. Melmoth associated rising with high silicon (0.7 to 0.9 per cent) and concluded that silicon increased gas absorption. Because silicon is a strong deoxidizer, oxygen must, therefore, be eliminated from consideration of the three common gases in steel-oxygen, nitrogen, and hydrogen. Butterworth2 later decided that pinhole porosity was caused by gases dissolved in the metal and that hydrogen was obtained from steam in the mold. Allen's classical work on copper castings,3 soon followed by

Jan 1, 1942

By W. E. Forsythe

WHEN measuring ordinary temperatures, the instrument is generally placed in very close contact with the body the temperature of which is desired. However, if the temperature of the source is continually raised, a point is soon reached where no known substance will, in general, remain constant in any of its temperature-measuring properties if placed in direct contact with the source. Also, it is occasionally necessary to measure the temperature of a source that 'is so small or so situated that it would be very hard to bring the measuring instrument into direct contact with the source. When these conditions exist, advantage is taken of the well-known fact that all bodies, when at sufficiently high temperatures, send out radiation in amounts readily measurable. This radiation has been found to be related to the temperature. The temperatures of very hot bodies have probably always been judged by the color, or the brightness, of the light given off. With practice, one can estimate probably within 50° to 100° C. of the correct value. However, if judgment is left to the eye alone, very much larger errors are sometimes made, due to

Jan 9, 1919

By C. R. Fettke

In 1914, the officials of the Brundred Oil Corpn., faced with the problem of introducing new methods to increase production in the old and nearly depleted pools of Venango County, became interested in the Smith-Dunn (Marietta) process which was at that time being tried out in southeastern Ohio and which was already yielding very encouraging results. A license to use the process in Pennsylvania was secured from the owners of the patents. These patents were later declared invalid. The method was first used in Pennsylvania on a property consisting of about 434 acres, of which 300 are productive, at Hamilton Corners, 15 miles northwest of Oil City, in Cherry Tree and Oakland Townships, Venango County. The producing horizon is the First Sand of the Venango Group. A small oil pool was opened up in this vicinity in 1904. By July, 1916, when the compressed air was first introduced to restore pressure, the production had dropped to a point where it was no longer possible to continue profitable operation. From that time until March, 1927, over 100,000 bbl. of oil have been recovered from the tract. The property is being operated at present by the Brundred Oil Corpn. and LUX. The 1926 production, amounting to 10,650 bbl., was only 400 bbl. short of the maximum reached during any year of the 10-year period that the process has been in operation. Inasmuch as the Hamilton Corners pool is the first one in Pennsylvania in which the Marietta process was tried out, and the one in which it has been longest in continuous operation, considerable interest attaches to the results obtained. Through the courtesy of H. D. Brown and W. J. Brundred, officials of the Brundred Oil Corpn., all their data on this operation were made available to the writer in connection with an investigation of rejuvenation methods in the State for the Pennsylvania Geological Survey. Stratigraphic Position of the Producing Sand The producing sand at Hamilton Corners is encountered at depths of from 364 to 560 ft., depending on the location of the well and the topog-

Jan 1, 1928

NORTH AMERICA. CANADA Canadian Army Overseas. Ball, H. D. Bridges. C. Butterill, H. J. If. Ladner, F. E. Lane, H. C. Alillar, W. A. ALBERTA Calgary.-Chonette, W. C. Clark, L. At. Corbett, C. S. de Hart, J. B. Dingman, C. W. Fath. A. E. Fulton. J. If. Cray, J. G. Johnson. R. V. McCutchin, J. A. *Slipper, S. E. Vin Buckirk H. A.

Jan 1, 1944

THE translators wish to record their appreciation of the help given by many individuals with whom they have discussed various details of the work. They are particularly indebted to Mrs. Anne Noble McKeachie, who initiated their collaboration; to Miss Cora Adamson, who spent many hours in making an accurate copy of a much-mutilated &st draft of the translation; and to the Yale University Library which gave access to its excellent collection of books on all aspects of the history of the sciences. The reader will share with the translators their obvious indebtedness to Mr. Carl P. Rollins, Mr. James W. Boyden, and the staff of the Printing-Office of the Yale University Press. The publication of this translation by the American Institute of Mining and Metallurgical Engineers has been made possible by a grant from the Seeley W. Mudd Memorial Fund, administered by a committee composed of Harvey S. Mudd, H. DeWitt Smith, and George Otis Smith. The translators are gratified that their work has been judged to fall within the scope of this Fund, which was established for the advancement of the sciences of mining and metallurgy by the encouragement of research and the dissemination of knowledge, and especially for the furtherance of such activities as might benefit the younger members of the profession. While Biringuccio's book would scarcely serve as a dependable text for the young mining student or metallurgist, it can give him a sense of his membership in a long-standing and honorable profession and enable him better to see his own work in true perspective. It is hoped that this English edition of a sixteenth-century Italian work will be read by the practicing metallurgist as well as by those who have already found pleasure in exploring the past of their profession. A man always feels more at home in a foreign country with men of his own craft than in his birthplace with those of different interests: As in space, so in time, and the modem metallurgist who may be unmoved by the literary and artistic Renaissance will quickly appreciate the spirit of that exciting period as he talks shop with Biringuccio on a visit to mine, smelter, forge, and foundry; as he sees in different forms the very furnaces and machines whose operation and response he knows so well; and as he discusses with this engineer of four centuries ago such topics as the best kinds of fuel or refractory for a given operation, and the importance of adequate supplies of power and material.

Jan 1, 1942

By E. H. Mohr

At the McGill concentrator of the Nevada Consolidated Copper Co., all flotation operations have been carried out in Forrester cells since November, 1926. In respect to cost of operation, the new cell has proved to be superior to the Callow, which it supplanted, and its incorporation in the flow sheet has resulted in a marked improvement in the metallurgy. Before citing the advantages of the new machine over the old, it should be explained that the Forrester has not only replaced the Callow, but it has made possible the elimination of a number of tables as well. When Callow cells were in use, table concentration preceded flotation. The ball mill pulp was elevated, by means of air lifts, to roughing Wilfley tables situated two floors directly above the flotation floor. On an intermediate floor were additional tables which cleaned the concentrate from those above. The finished table concentrate constituted approximately 60 per cent. of the total mill production, and contained about 40 per cent, of the recovered copper. The table tailings were returned to the classifiers, the overflow from which went to the flotation cells and the oversize to the ball mills. As soon as the Forrester cells were installed, this tabling operation was discontinued. The ball mill pulp now discharges into the classifiers direct, without the intermediate tabling. It was impracticable to ernploy the present flow sheet when Callow cells were in use, for the reason that unless the great,er part of the heavy mineral was first removed, it accumulated on the mats and adversely affected the flotation operation. By tabling ahead of flotation, it was practicable to maintain the concentrator at 10 to 20 per cent. greater capacity (depending up on the pyrite contnt of the ore) than was possible by flotation alone. This was due to the necessity for finer grinding in the latter case. Even though the table conecntrates contained only 6 to 8 per cent'. copper content, the low smelting costs made it advantageous to operate at high mill capacity, at the cost of low grade of product. Standard Section equipment With the old flow sheet, a standard section consisted of four ball mills and classifiers, one air. lift, 20 roughing tables, 10 cleaner tables, 12 primary

Jan 1, 1928

By P. J. Burkhardt, L. V. Gregor

The oxidation kinetics of single-crystal silicon has been investigated using extremely dry oxygen as the oxidant. Two techniques were used. The first involved a flow system with which incremental thickness measurements were made. This sytem provided an oxygen ambient at atmospheric pressure which had a moisture content of less than 0.1 ppm of water. The second technique involved measuring the change in volume of oxygen with time in a closed system. A temperature range of 900O to 1200 "C and a pressure range of 20 to 760 Tory were covered. Both techniques showed that a simple parabolic rate law holds only at the higher temperatures. At lower temperatures, the data up to 5000Å can be fitted well to a linear-parabolic equation. The two constants in this rate equation are examined in terms of a physical model. The parabolic portion of the low-temperature oxidatLon fits along the high-temperature curve of an Arrhenius plot. The parabolic rate constant for the flow-system technique can be expressed by k = 2 x 10-9 exp (L 31 kcalRT) sq cm per sec. The manostatic technique gave k = 1 x 10-exp (- 23 kcalRT) sq cm per sec. By extending the thickness range to over 104. a rate law of X = At seems to fit all of the data better than the linear-Pavabolic law. Here the exponent n increases from 0.518 at 1150 V to 0.637 at 900°C. PASSIVATION of silicon planar devices through thermal oxidation is of such great importance that considerable effort has been devoted to the study of the process.17 Much of this work involves hydrothermal oxidation, in which H2O is the oxidant: whereby H2 is produced. It has been proposed that the reaction proceeds by the formation of Si-OH groups and hydroxyl diffusion through the film to react with the silicon surface. Thus, the silicon oxide layer probably contains residual hydrogen in some form after oxidation in H2O and it has already been established that hydrogen has a marked effect on the electronic properties of oxide-passivated silicon surfaces. Silicon is oxidized by oxygen at elevated temperatures; but the rate of oxide formation is considerably lower than that for 0." By using dry O2 as the sole oxidant, the presence of residual hydrogen is presumably avoided. At present, the mechanism of thermal oxidation by dry O2 is a matter for conjecture, and the presence of small amounts of H2O was reported to have a marked effect on the rate of oxide formation10 (perhaps on the electronic properties of the surface, as well). Hence, this study of the kinetics of silicon oxide growth in 0, was undertaken: 1) to determine the oxidation rate at atmospheric pressure in a system designed to exclude rigorously all traces of H2O in the ambient 0,; 2) to obtain oxidation-rate data in situ in dry O2 by means of a continuous monitoring of the amount of 0, consumed during oxide growth. These objectives are complementary—the first assesses what effects (if any) are obtained by excluding H2O from the reaction, and the second expands this information while at the same time avoiding the uncertainty inherent in relying upon incremental measurements of oxide growth to furnish kinetic data. EXPERIMENTAL PROCEDURE The conventional silica open tube in a resistance-heated oxidation furnace is subject to sources of trace H2O, even after the input O2 is thoroughly dried and the outlet gas stream is passed through a trap to prevent

Jan 1, 1967

Jan 1, 1923

[NORTH AMERICA ALASKA Anchorage.-Strandberg, H. Chlchagoff.-Russell, J. C. College.-Barber. R. J. Dorsh, J. B. Fox, E. F. Joesting, H. R. McAnerney, J., M. Douglas.-Cahill, W. E. Fairbanks.-Beistline, E. H. Crawford, J. D. Earling, R. B. Greves, J. H. Harris, Q. P., Jr. Henton, H. M. Herbert, C. F. Hester. W. B. Hopkins, J. E. Kreitlow, E. J. MacDonald, D., III March, J. P. Mathews, T. C.]

Jan 1, 1940

Jan 1, 1909

By C. W. Pritchett

Several years ago, during a trip from Jojutla to Huauatla, in the abate of Morelos, Mexico, I was told by my guide of the ruins of an old smelter near by, and my curiosity was excited to such an extent that I went out of my way several miles to see them. I found them very interesting; and, as I fortunately

Jan 1, 1902

By J. V. Emmons

It has long been known that the outside skin of tool steel frequently exhibits properties widely different from the interior of the mass.

Jan 1, 1915