Search Documents

By Toshiyuki Nohira, Eiichi Takeuchi, Tetsuo Oishi, Hideki Ono, Hirokazu Konishi

The Dy-Nd-Pr-Ni alloy sample was prepared by cathodic potentiostatic electrolysis at 0.65 V (vs. Li+/Li) for 1 h using a Ni plate in a molten LiCl-KCl-DyCl3-NdCl3-PrCl3 system at 723 K. The highest mass ratio (Dy/Nd+Pr) in the alloy sample was observed to be 50 at 0.65 V. Anodic potentiostatic electrolysis at 2.20 V for 12 h was conducted using the Nd-Fe-B magnet electrode in a molten LiCl-KCl system. All elements were almost dissolved from the magnet, and the original form of the magnet disintegrated. After anodic potentiostatic electrolysis at 2.20 V, cathodic potentiostatic electrolysis was conducted at 1.00 V for 5 h using a Mo plate in order to remove the dissolved Fe from the bath. Finally, cathodic potentiostatic electrolysis was conducted at 0.65 V for 12 h using a Ni plate. The mass ratio of Dy/Nd in the alloy sample was determined to be about 18.

Jan 1, 2015

By Huimin Lu, Liyuan Zhao, Zhijiang Gao

The aluminum matrix composite reinforced by graphene was successfully fabricated using high pressure torsion (HPT). With only 0.5wt% graphene, the grain size was reduced to 100nm while that of pure Al was about 500nm. The hardness of the composite increased from the center (64HV) to the edge (120HV) of the sample. Moreover, the tensile strength of this composite reached 197MPa, while that of pure Al was 157MPa. The enhancement in mechanical properties was induced by grain refinement, load transfer from the matrix to the reinforcement and dislocations piled up at the grain boundaries.

Jan 1, 2015

By Larry Twidwell, Ed Rosenberg, Courtney Young, Sean Dudley, William Gleason, Maureen Chorney

Experimental and industrially produced polystyrene and silica resins are tested for recovery capabilities of Rare Earth Elements (REE). Testing regimes being used are typical of resin analysis. Inductively Coupled Plasma-AES results indicate that preferential separation and recovery is possible in the adjusted pH range of2 to 10, solution conditions, and resin type. Testing conditions are resulting in structure modification of the composite resin as indicated by X-Ray Diffraction, Differential Scanning Calorimetry, Scanning Electron Microscopy, Mercury Porisometry, and density analysis. Resin modification indicates both surface and internal structure alteration outside of reported standard behavior of resins. Structural changes have ramification for both Rare Earth Recovery RER and traditional resin operations. Analysis shows that the resin uptake of REE can be manipulated for concentration. Further analysis with SEM work indicates that widespread surface and interior modification is taking place as resins load with REE. This modification is leading to pore rupture and particle breakage. Further investigation is being performed to determine the mode of breakage.

Jan 1, 2015

By Naiyang Ma

High zinc concentration in basic oxygen furnace (BOF) steelmaking offgas (OG) cleaning system solid wastes is one of the main barriers for recycling of the solid wastes in sintering – blast furnace ironmaking process. One of the possible solutions is to utilize zinc-free scrap in BOF steelmaking so that the BOF OG solid wastes will not be contaminated with zinc and can be recycled through sintering – blast furnace ironmaking. This paper describes a model for helping to decide whether to use zinc-free scrap in a BOF process. A model computing marginal price increment of zinc-free scrap is developed. The marginal price increment is proportional to value change of the BOF OG solid wastes after and before using zinc-free scrap, to ratio of BOF solid waste rate to purchased galvanized scrap rate, and to price of galvanized scrap. Due to the variations of consumption rate of purchased galvanized scrap and home galvanized scrap, iron ore price, landfill cost, and price of purchased galvanized scrap, using zinc-free scrap in a BOF process might be economically feasible for some ironmaking and steelmaking plants or in some particular market circumstances.

Jan 1, 2015

By N. G. Azeredo

This work dealt with the evaluation of engineering structural clay brick samples that were sintered at estimated temperatures of 700 and 800°C. They were collected in a red-brick plant in Campos dos Goytacazes, RJ, Brazil. From a lot, a sample already sintered in its kiln at 700°C were collected and also a sample from the same lot only dried by the air, which were then sintered at 800°C controlled temperature. The samples were subjected to Brazilian Standard tests (ABNT NBR 15270:2005) to determine their geometric, physical and mechanical properties. In order to be classified as structural clay brick it is required minimum 3.0 MPa for the characteristic compressive strength (fbk) to be suitable for up to five floors structural building applications. We also used the Weibull Probability Plot and Weibull Maximum Likelihood Estimation to evaluate distribution parameters in order to compare the results of compressive strength obtained in the tests.

Jan 1, 2015

By Dan Wang, Qian Xu, Guangshi Li, Xionggang Lu, Xingli Zou, Zhongfu Zhou, Hongwei Cheng, Changyuan Lu

The preoxidation of the ore has a profound significance to the concentration, separation and purification of nickel and copper from the lean complex ore. In this paper, the natural Ni-Cu sulfide mineral samples under the elevated temperature condition in air were investigated, as well as under isothermal condition at 600 oC in air. The mineralogical characterization was studied using XRF, ICP and the Rietveld method. The oxidation behavior and the element migration of the Ni-Cu sulfide ore were studied by XRD, SEM-EDS and TG. The XRD Rietveld method was successfully developed in the phase identification and quantification of this complex ore powder sample. The oxidative intermediates (Cu/Ni-ferrite) were detected by XRD, and the process of the element migration was obviously revealed by the line scans using SEM-EDS. It is the preoxidation of this mineral that provides guidance for the extraction of valuable metals from low-grade Ni-Cu sulfide ores in the future.

Jan 1, 2015

By Jilai Xue, Jun Zhu, GermainKouma Ndong, Luxing Feng

High-temperature corrosion behaviors of Fe-Ni-Cr alloy as inert anodes for aluminum electrolysis have been studied. The effect of anodic overpotential on layer growth of anodic surface is specially considered. The corrosion layers on the anodes tested were analyzed using XRD and SEM-EDS to provide a fundamental understanding of the layers growth at metallic anode surface. The dissolution of the scale layers on the metal anode occurred with low overpotential, while AlxM3-xO4 spinel phase within the scale layers was found with an increased overpotential. A mixture of multiple MyO layers existed on the anode substrate. The results may be useful for understanding and controlling the corrosion behaviors of Fe-Ni-Cr anode for potential application in aluminum electrolysis.

Jan 1, 2015

By Pedro A. Netto, Sergio N. Monteiro, Foluke S. de Assis, Rômulo L. Loiola, Frederico M. Margem

Banana fibers are among the lignocellulosic with great potential for use in polymer composites, such as the variety from the Musaceae family, due to its low density and good mechanical properties. In this work, epoxy matrix composites incorporated with continuous and aligned banana fibers were tested for their flexural behavior. Specimens with up to 30% in volume of fibers were bend-tested until rupture. The results showed an increase in both the composite mechanical strength and the stiffness with incorporation of these fibers. A fractographic analysis by SEM examinations a moderate adhesion mechanism between the banana fiber and the epoxy matrix. This mechanism is apparently responsible for the improved performance of the composites.

Jan 1, 2015

By Mao Chen, Tim Evans, Zhixing Zhao, Weidong Zhang, Baojun Zhao, Dongqing Wang

High temperature softening behaviours of iron blast furnace feeds (sinter, lump and pellet) have been determined under conditions simulated to the blast furnace. The industrial samples were packed with sandwich structure (coke / ore / coke) in graphite crucibles and 30 CO / 70 Ar gas mixture was blowing directly through the bottom of the crucibles. The displacement and temperature were continuously recorded simultaneously to construct the softening curves. Separated quenching experiments were also carried out at selected temperatures under the same gas atmosphere. The temperatures were selected corresponding to the turning points of the softening curves. The phase assemblages and composition of each phase in quenched samples were analysed by Electron Probe X-ray Microanalysis (EPMA). The proportion of the liquid formed at temperature was obtained from the backscattered electron images. The deformation characteristics of these complex multi-phase materials are shown to be related directly to the phase assemblages of the samples and the microstructures. FactSage was also used to assist the predictions of liquid / solid fractions and their compositions.

Jan 1, 2015

By Antoine Allanore, Guillaume Lambotte, Bradley R. Nakanishi

Current industrial methods used for rare earth element (REE) extraction involve: 1) ore enrichment, 2) separation of rare earth oxides (REOs), 3) chlorination or hydrofluorination, and 4) individual electrowinning of REEs from a molten halide electrolyte. The complexity of REE extraction is inherited from their electronic configuration. Recently, molten oxide electrolysis (MOE) has been used to produce reactive metals directly from their oxides, e.g. titanium. As a single-step alternative to processes 3) and 4), or laboratory has investigated rare earth extraction by MOE. A key challenge is to find a molten electrolyte more stable than REOs. One possibility is to use binaries of REOs directly as a solvent. We have, therefore, developed two experimental approaches for studying molten REOs at temperatures exceeding 2200oC. The present work reports the most recent experimental results obtained with La2O3-Y2O3. Those promising results demonstrate potential for operating with molten REOs and refine the underlying materials challenge for electrodes to enable metal recovery.

Jan 1, 2015

By Min Chen, Lei Xu, Weijun Huang, Shuai Zhang

For the purpose of extending the service life of MgO-C bricks used as linings of vanadium-extraction converters, the effect of Fe addition on properties of MgO-C bricks was investigated. The results showed the addition of Fe could effectively improve the sinterability of the oxidized layer of the MgO-C refractory at 1400°C due to the effect of FeO (formed by oxidation of Fe) on formation of MgO-FeOss and modification of the microstructure, and excellent corrosion resistance against vanadium containing slag was also obtained due to the increase of compactness of the oxidized layer and concentration of FeO in the oxidized layer. Consequently, it is considered that MgO-C brick by introducing the new phase of Fe is a favorable substitute of MgO-C refractory to be used as linings of vanadium-extraction converters.

Jan 1, 2015

By Lei Zhang, Shining Chen, Lina Wang, Pu Liu, Benquan Fu, Jiannyang Hwang

A PFS(polymeric ferric sulfate) coagulation-photocatalytic oxidation technology was used for advanced treatment of coking wastewater from secondary biological treatment. Effects of some key factors on TOC removal rate were investigated, and the results were compared with those of the common photocatalytic oxidation technology under the operating parameters of the photocatalytic oxidation defined. Single factor experimental results showed that TOC removal rate could reach 81%, when optimal operating conditions were as follows: TiO2 loading: 4.0g/L, irradiation time: 4h, initial pH is 5.1and PFS dosage:700mg/L. PFS coagulation and photocatalytic oxidation have synergistic effect, which is meaningful for highly efficient treatment of coking wastewater

Jan 1, 2015

By Jing Zhong, Yugang Li, Chen Yan, Shaoda Zhang, Qian Wang

Online surface quenching technology has been developed for the hot charging process to prevent the surface cracks in high strength low-alloy steel slabs. In this paper, a two-dimensional heat transfer model of surface quenching process was presented. This finite element model includes nonlinear thermodynamic properties, by which the slab temperature distributions were computed. The model predicted temperatures show reasonable agreement with the measurements. The effects of the water flow rate and slab movement velocity on temperature variation during the quenching and subsequent tempering process were investigated. The result shows that the temperature drop increases but the tempering temperature changes slightly with increasing water flow rate and decreasing slab velocity. Keeping the slab movement velocity at 1.2-2.1m/min and the water flow rate at 55-70m3/h, the slab surface experiences a temperature drop of 400-600 firstly, then recovers above 650, the quenching and energy-saving effect are remarkable.

Jan 1, 2015

By Junli Xu, Xianwei Hu, Kaiyu Xie, Liangxing Li, Zhongning Shi, Zhaowen Wang, Bingliang Gao, Aimin Liu

Al-Ti master alloys were prepared by aluminothermic reduction between the dissolved titanium dioxide and aluminum in cryolite melts at 960oC. The kinetic analysis by differential scanning calorimetry indicated that the apparent activation energy of the reaction of reducing titanium dioxide by aluminium is 22.3 kJ/mol, and the reaction order is 0.5. The products were analyzed by means of X-ray diffraction, X-ray fluorescence, scanning electron microscopy and energy dispersive spectrometer. Results from X-ray diffraction showed that the phase compositions of produced alloys are Al and Al3Ti. In addition, Al-Ti master alloys containing 2-6 mass% Ti were formed at different reduction time of 2-5h in aluminothermic reduction experiment.

Jan 1, 2015

By Wenbo Luo, Jilai Xue, Tiepeng Li, Jun Zhu

Sodium silicate solutions for producing silica have been ultrasound treated to enhance the precipitation process in laboratory scale. Higher precipitation rate was found with ultrasound treated solutions than those without ultrasound. The obtained SiO2 powder products were characterized using XRD, SEM, BET and laser particle size analyzer. The particle size distribution and the specific surface area of the powder products varied with the power input level and the processing time of the ultrasonic treatment. The results indicate that the efficiency of the precipitation process can be improved optimally when the ultrasound is conducted into the solutions before the nucleation stage.

Jan 1, 2015

By Cheng Fang, Zhou Lie-xing, Peng Jin-hui, Guo Sheng-hui

This article discusses the behavior of temperature and microwave thermo gravimetric analysis characteristic of ammonium paratungstate in a microwave field. Experimental results show that when 12g of material is place in a microwave with 900W of power, paratungstate’s temperature rises at 70°C/min. This results in paratungstate’s temperature being 980°C after 14 minutes. Compared with thermo gravimetric analysis characteristic, former two-step process of paratungstate microwave calcined completed ahead of schedule, after two-step process reaction is more intense,Paratungstate warming is more rapidly, the reaction time is much shorter; According to XRD and SEM, the product is high purity, the crystal particle size is uniform, and the grain size is fine.

Jan 1, 2015

By Baozhong Ma, Qian Li, Yonggang Wei, Shiwei Zhou, Bo Li, Chengyan Wang, Hua Wang

The magnesium-rich nickel oxide ore (w (Ni) =1.09 %, w (MgO)=29.08 %) mixed with 6 % and 8 % anthracite were roasted at different temperatures. XRD and SEM/EDS techniques were utilized to characterize the phase and microstructure transformation of the ores. The results show that lizardite and chrysotile of raw ore were converted into forsterite and enstatite during reduction roasting process. Simultaneously, iron and nickel oxide were reduced and migrated from the initial magnesium silicate. Fe3Si were formed when the roasting temperature went up to 1300 ℃ and 1350 ℃, and a small amount of Ni was observed in it. Temperatures got too high were not benefit to the polymerization of ferronickel.

Jan 1, 2015

By Kexin Jiao, Zhijia Zhang, Jianliang Zhang, Zhengjian Liu

Carburization behavior of molten iron in blast furnace is an essential part of BF long campaign technology. Maintaining carbon content stable is an important prerequisite to ensure the high production of the blast furnace. In this paper, the important aspects of the research progress which mainly including the study of iron carburization at the upper and the lower parts of the blast furnace was reviewed. Indirect carburizing is the main way at the top of the blast furnace. The content of carbon in metallic iron increases with the reducibility of iron ore improved. The thermodynamics and kinetics conditions are good for carburization reaction to take place at the bottom of the blast furnace. Carbon content of molten iron increased by coke carburizing. Meanwhile, the drawbacks of the existing literature on iron carburization behavior were analyzed and new research directions of iron carburization were proposed in the future.

Jan 1, 2015

By Xuemei Zheng, Aiyuan Ma, Yonggang Zuo, Jinhui Peng, Shiwei Li, Libo Zhang

The effect of moisture content on the dielectric properties and microwave drying behavior of zirconium hydroxide was studied by using an open-ended sensor dielectric measurement system at the frequency of 2.45 GHz. The experimental results showed that moisture content can significantly influence the variation of dielectric properties. Dielectric constant, loss factor and loss tangent all increase with the increasing moisture content. Compared with the conventional drying method, the microwave-assisted drying method resulted in a substantial decrease (81.8%) in the drying time, and the drying effect was better at the lower power level of 600 W. This study offers the useful information on dielectric properties of zirconium hydroxide, which can be used for developing microwave drying applications in mineral processing and designing better microwave sensors for measuring zirconium hydroxide moisture content.

Jan 1, 2015

By Jong Hyeon Lee, Go-Gi Lee, Chang-Kyu Lee, Hong Youl Ryu, Sung-Koo Jo

This study deals with research on the reduction process of neodymium oxide by molten salt electrowinning. Neodymium fluoride and lithium fluoride electrolyte were used for feed stock of electrolyte and neodymium oxide was added as precursor. Cell current was confirmed that cell potential was applied as constant potential of 4.5V. Argon gas injection into the electrolyte was carried out to confirm convection effect on current efficiency. Applied current was gradually decreased without argon flow, but applied current was kept within a certain range with argon flow in electrolyte.

Jan 1, 2015