By Jonkion M. Font

An expression for the distribution ratio of arsenic between slag and copper matte or liquid copper was developed by both, an extension of the Reddy-Blander model for deriving a priori the arsenic capacity, and by a relationship between the arsenic capacity and the arsenic distribution ratio. In this study, the a priori arsenic capacities in the FeO-SiO2, CaO-SiO2, MgO-SiO2, FeO-CaO-SiO2, FeO-FeO1.5-CuOo.5-MgO-SiO2, FeO-FeO1.5-CuO0.5-CaO-MgO and FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slags were calculated at 1573 K. The a priori arsenic distribution ratio between the FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slag and copper matte (L s/m as), and between the FeO-FeO1.5-SiO2 or FeO-FeO1.5-CuO0.5-CaO-MgO slag and liquid copper (L s/Cu as) were calculated. The model calculated data are found to be in good agreement with the reported experimental data. The availability of reliable thermodynamic data for slag components and impurities in the slag-matte-metal system is essential for the accurate prediction of impurity capacities and distribution ratio data. The arsenic distribution ratio model developed here, can be extended for prediction in multi-component slags and mattes or liquid metal, and thereby may lead to the development of new slag systems for the efficient removal of arsenic in the copper smelting, converting and refining processes.

Jan 1, 2003

By Zhuo Sheng

We have designed a high-temperature Raman micro-furnace and cell that is suited for the electrochemical process study of the NO3 − in molten NaNO3– KNO3 (fraction of NaNO3 50 wt%) salt. During the cycle voltammetry and constant potential electrolysis process, the Raman laser beam was focused near the electrode; subsequently, the Raman spectra are obtained and the reduction process of NO3 − is analyzed. In the CV cathodic scan process, the new peak attributed to the ν1 mode of NO2 − emerges, and the peaks assigned to superoxide ions (O2 −) and peroxide ions (O2 2−) are not found. In the constant electrolysis process, the peaks at 1130 and 800 cm−1 appear when the potentials are between −2.0 V and −3.2 V (vs. Pt). The results show that when the NO3 − is reduced in molten the NaNO3–KNO3 mixtures, the reduction product O2− cannot stably exist, and O2− will react with NO3 − to form of superoxide ions (O2 −) and peroxide ions (O2 2−).

By Denise Crocce Romano Espinosa, Andrea Moura Bemardes, Jorge Alberto Soares Tenorio, Daniella Cardoso Buzzi, Tatiana Scarazzato

"In copper plating processes, a fraction of raw materials are incorporated to the final products, while other portions are discarded as effluents. In this study, the application of electrodialysis (a membrane treatment process) was studied for treatment of wastewaters from cyanide-free strike baths, in order to reuse the components of this bath: copper and HEDP. The synthetic solutions studied consider 1 % of ion concentration of the bath used in this process, simulating the rinsing waters to be discarded. The electrodialysis allowed a percentage extraction up to 73% of copper ions and 72% of HEDP from the effluent. Complexes formation between the acid and copper indicates the possibility of recovery of components in the same compartment, obtaining a concentrated solution of these substances that can be reinserted in the process, for compensating drag-out losses. A diluted solution is also obtained, that can be reused as water in rinsing tanks.IntroductionIn metal finishing industries, contaminants in wastewater and the type of treatment required are determined according to the type of operation [l]. Generally, electroplating industries employ conventional wastewater treatments, e.g. oxidation of cyanide and chemical precipitation. This stage promotes reactions with soluble compounds to produce an insoluble precipitate, removed by physical separation. The sludge is dried by press-type filters [2].In this manufacturing sector, part of the raw materials are discarded as hazardous waste. The cost of discarded compounds and the treatment and disposal of waste may compromise profit margins. In addition, water consumption per unit of production stimulates the development of methods able to recover and reuse the largest possible amount of water [3].In some plating processes, cyanide-based substances are used as complexing agents and as raw materials in form of metal salts [4]. However, the toxicity associated with cyanide has been promoting research for the development of new raw materials in plating processes.A study conducted in Brazil [4] evaluated the modification of a commercial cyanide-free bath for processes of copper coating on Zamak. In the performed study, a new alkaline copper bath was formulated using l,hydroxyethane-1,1-diphosphonic acid (HEDP), an organic compound known for forming stable complexes with metal ions.As results of the study, the operational conditions and the formulation of a bath to obtain adherent, uniform and bright layers were established (Table I) [4]."

Jan 1, 2014

By Young-Geun Park

A new decarburization model for the RH system was constructed for calculating the decarburization reaction using a three-dimensional fluid dynamics program. The entire fluid flow in the RH process was calculated by evaluating the shape and volume of the plume zone, formed by Ar gas blown through multiple nozzles on the wall of the snorkel. On the basis of this fluid flow, the decarburizaiton reaction was calculated through establishing the decarburization reaction model, which considers the thermodynamics, reaction kinetics, and the decarburization sites (Ar bubble surface, bath surface, and the CO bubble fomtation at inner sites). The results from this model were compared with a real RH operation results with good agreement. Because it is possible to predict the carbon concentration at various conditions using this model, it may be useful in increasing the decarburizaiton rate. Key words : RH process, plume zone, decarburization, Ar bubble surface, bath surface, inner site, circulation flow rate.

Jan 1, 2001

By X. J. Wu

Effects of various factors such as diaphragm materials, composition of electrolytes and current density on copper electrowinning from cupric chloride solutions was investigated. It is found that the crux of this process is to prevent the dissolution of copper by cupric ion and the formation of suspended CuCl precipitate. A process with high difference of copper concentrations between the feed solution and the spent electrolyte was selected. With this process, in which the feed solution contains 90 g/dm3 [Cu"], 3M NaC1, and 10mg/dm3 bone glue, and the spent electrolytes contains 10 g/dm3 [Cul, a very smooth and dense copper cathode can be produced with current efficiency above 93% and energy requirement less than 1.7 kwh/kg Cu at 25°C with N2 sparging. If a slightly higher energy requirement is permitted, smooth and dense copper cathodes can be produced at the current density up to 800 A/m2 with the identical solutions.

Jan 1, 1991

By Onder Guney, Erdem Demirkesenm

"In this study, the crystallization behavior and thermal expansion coefficient of a lithium disilicate (LS2) based glass-ceramic derived from SiO2-Li02-AhO3-K2O-ZrO2 system was investigated by using x-ray diffraction (XRD), high temperature x-ray diffraction (HTXRD), differential thermal analysis (DTA) and dilatometer techniques. Analytical reagent grade chemicals were chosen as raw materials for preparing glass batches. Nucleation and crystal growth heat treatments were planned according to DTA results. The amounts of the amorphous and crystalline phases developed during the heat treatments were determined by quantitative XRD. XRD results of crystallized samples showed simultaneous formation of lithium silicate (LS) and quartz in the early stage of the crystallization followed by formation of lithium disilicate (LS2) at higher temperatures. The thermal expansion coefficients of glassceramics were also measured depending on the applied heat treatments.IntroductionSignificant developments occurred in all ceramic materials provide the fabrication of high quality dental implants [1]. Glass ceramic based dental restorations like dental inlays, crowns, bridges and veneers are becoming increasingly popular with their reliable and durable performance [2,3]. In addition to their advanced functional properties, glass ceramic implants especially lithium disilicate glass ceramics also face the esthetics expectations of patients and dentists and in this way they are starting to take the place of metal based restorations today [1,3,4,5]. Lithium disilicate glass-ceramics derived from multicomponent glass systems have some superior mechanical and optical properties comparable to natural teeth [ 6]. In restorative dentistry, mechanical characteristics of biomaterials play very crucial role in order to resist the masticatory forces occurred during biting and chewing [7] According to three point bending test results of Roland, flexural strength of the lithium disilicate glass-ceramics were 400±40 MPa and their fracture toughness (K1c) are approximately 3,3 MPa m112 [2,6]. In addition to high mechanical strength, aesthetic appearance is another important prerequisite as material for dental restorative applications. Translucency and light transmission of the LS2 glass ceramics mimic enamel. Moreover, opacity of the material can also be adjusted depending on the restoration types [2,6, 7]. These superior properties of the LS2 glass ceramics are directly related with chemical composition of the base glasses and controlled crystallization heat treatments [ 4, 7]. The aim of the present work is to determine the effect of heat treatment schedules on the crystallization behavior and thermal expansion of the LS2 glass-ceramics."

Jan 1, 2011

By Sergio Neves Monteiro

The efficiency by which an applied load is transmitted through the composite structure depends on the strength of the interface between the matrix and the second phase. In fiber reinforced composites, the interfacial shear stress plays a major role in the composite capacity to support the applied load. This interfacial stress can be obtained by means of pullout tests using the fiber embedded to a certain length in a socket of the matrix material. In the present work, pullout tests were performed to evaluate the interfacial shear stress of ramie, a relatively strong natural fiber, reinforcing polyester matrix composites. The general result permitted to calculate a critical length for the ramie fiber embedded in polyester resin. From this critical length, the value of the interfacial shear stress was calculated. An interpretation of this result together with SEM observation displayed a relatively weak bond between the ramie fiber and the polyester matrix.

Jan 1, 2010

By Olga Karabelchtchikova

Keywords: Multipass grinding, Residual stress, Retained austenite, X-ray diffraction The study investigated residual stresses behaviors and their superposition effect in D2 dies for thread-rolling applications. A nested factorial experiment was applied to test hypotheses that the residual stresses profiles change due to combination of heat treatment and multipass grinding operations, and that certain patterns can be derived due to the memory relationship between pre-existing and final residual stresses distributions. The amount of the retained austenite along with residual stresses in variation with depth was measured using x-ray diffraction technique. Statistical analyses indicate that the proposed hypotheses hold. Residual stresses distributions as well as tensile peak location were found to be significantly influenced by the treatment parameters used. Unique characteristic patterns in the residual stresses profiles were observed due to multipass grinding technique across all experimental conditions. This finding suggested a plausible memory relationship between the cutting passes, and the causes of the foregoing results are further proposed and discussed.

Jan 1, 2005

By P. G. West-Sells

Recovery of gold from thiosulfate leachates can be accomplished by adsorption of the gold thiosulfate complex by a strong base resin. Two of the most significant impurities that can decrease this gold adsorption are tetrathionate and trithionate, which are produced as oxidation products of thiosulfate during gold leaching. This paper investigates gold adsorption on a strong base resin (Purolite A500C) as a function of the concentration of these impurities. It is shown that concentrations of tetrathionate and trithionate as low as 150 mg/L can decrease gold loading by an order of magnitude, and that of the two ions, tetrathionate has a stronger detrimental effect. The resin and solution gold concentration profiles were successfully fit using a Freundlich isotherm, which further shows the strong effect of tetrathionate. To counteract the decrease in gold adsorption by tetrathionate, a novel process was proposed. Sulfite was added to the solution to oxidize tetrathionate to trithionate, and a nitrogen blanket was added to ensure that no further oxidation of thiosulfate could take place. It is shown that by incorporating this process, gold adsorption was doubled from both synthetic and real gold thiosulfate leachates.

Jan 1, 2003

By Guo Xian Jian

In this paper, an alternative process to recover the value metals from polymetallic gold ore by FeCh leaching was proposed. In the process, gold was recovered by direct cyanidation from the leaching residue, the isolative electrolyte in chloride solution was selected to recover lead, the cementation with copper powder was used to recover silver and the solvent extracting was applied to recover copper and zinc. The total recovery of gold, lead, copper, silver and zinc in the process is 90.8%,96.05%,84.3%,81.98% and 54% to the bullion of gold, lead and silver and sulfate of copper and zinc, respectively. The process conditions selected for FeCh leaching are the temperature of 104°C, leaching time of 6 hours, Fe3+ content of 140 g/l and stoichiometry of FeCl3.

Jan 1, 1996

By Cang Daqiang, Li Yu, Liu Xiaoming, Zong Yanbin

"Utilization of high-quality heat in melting slag is a great challenge for iron and steel industry. In the paper, a new method is put forward to concurrently utilize heat and slag by converting the melting slag directly into high valued materials, slag glass-ceramic. A glassceramic with a higher basicity of 0.7 than traditional basicity of 0.45 was prepared from steelmaking slag in order to utilize more hot melting slag. Effects of Alz03 on its crystallization processes were researched by XRF, DTA, XRD and SEM. Results show that Alz03 in glassceramic would have great effected on its property. When the Alz03 content ranges within 12%-15%, glass-ceramics with basicity of0.7 could reach the best performances. The change of dominant phase in glass ceramics from akermanite and wollastonite to akermanite and gehlenite would significantly degrade its mechanical property. An increase of Al2O3 content leads to a rise of the viscosity and crystallization activation energy of the glass, while results in increasing sintering temperature and crystallization temperature of glass, which contributed to its fully crystallization and densification process.IntroductionSteel slag is a by-product under a process of converting iron to steel at above 1600°C, and 0.1-0.15 ton molten steel slag would be discharged for producing per ton of steel in the process. The discharged steel slag at 1600°C has heat of 68 kgce/t. In 2012, China's steel output reached 716 million tons, and produces about 100 million tons of steel slag and 68,000 tee of heat in it [1,2]. But at present, utilization of both slag and its heat at 1600°C is a great challenge for iron and steel industry.Dry granulation of melting steel slag by air and then recovering the heat of the hot air are a traditional technology which have not yet been put into practice for very low heat conductivity of the slag and low efficient of heat exchange among the different processes [3,4]. Therefore, a new method for high efficient utilization of both steel slag and its high temperature sensible heat is put forward [5,6], which is on-line reducing and extracting iron from molten steel slag and then directly preparing glass-ceramic by use of the residual molten slag."

Jan 1, 2014

By T. T. Chen

Raw anode slimes consisting primarily of PbSO4, AgCuSe, Cu3Se2, Cu2-x Se, Cu2O, CuSO4.5H2O, Sn arsenate and Sb-Bi-As oxide are batch-leached with electrolyte-O2 to dissolve Cu. During this process, Cu2O and CuSO4.5H2O are solubilized and the Cu in the selenides is leached with the formation of Ag2Se and Se. A small amount of Cu remains in the Ag2Se, Sn arsenate and Sb-Bi-As oxide. The decopperized slimes are repulped in Na2CO3 solution to convert most of the PbSO4 to NaPb2(CO3)2(OH). The Sn arsenate and Sb-Bi-As oxide partly react, but the Ag2Se is not significantly affected by the Na2CO3 solution. The NaPb2(CO3)2(OH) intermediate phase is dissolved in acetic acid to leave a final product consisting of Ag2Se, Se, Sn arsenate and Sb-Bi-As oxide, together with small amounts of PbSO4, NaPb2(CO3)2(OH) and various gangue constituents.

Jan 1, 1993

By M. Wu, A. Kharicha, A. Ludwig

"The droplet formation during melting of a 400 mm diameter electrode is simulated with a multiphase-MHD approach. The computational model includes a layer of slag and a layer of liquid steel. A VOF approach is used for the interface tracking and a potential formulation is used for the electric and the magnetic field. The Lorentz force and the Joule heating are recalculated at each time step in function of the phase distribution. The first results provided by this model are presented.IntroductionThe Electro-Slag-Remelting (ESR) process is an advanced technology for the production of components of e.g. high quality steels [ 1-9]. An alternating current (Figure 1) is passed from a conventionally melted and cast solid electrode through a layer of molten slag to the baseplate. Because of the electrical resistivity of the slag, Joule heating is generated and the slag transfers this energy to ingot and mould surfaces and to the melting electrode tip. The molten metal produced in the form of droplets passes through the slag and feeds a liquid pool from where directional solidification takes place. The slag and the ingot are contained in a water cooled copper mould. As also the baseplate is water cooled, a heat flow regime is imposed that gives controlled solidification, and this results in improved structure characteristics of ESR ingots.This process involves two liquids, a liquid metal and a liquid slag. Each liquid is subject to a phase change due to melting and/or solidification. From a fluid dynamic point of view, the ESR process is clearly a multiphase process, with free interfaces (slag/pool, gas/slag), and with a mixed area (slag and falling steel droplets) [ 10-15].Physically, the development of the heat and mass transfer at the slag/droplet interface is important for the final ingot quality, composition and cleanliness. Visual observations of the droplet formation just under the electrode being melted is almost impossible. Due to the presence of high temperatures, opacity of the materials, and the presence of the mould it is not possible to directly observe the behaviour the slag/pool interface. Although usually assumed flat [1-9], a previous work [10] using a Volume of fluid (VOF) model has shown that the interface shape between a layer of slag and steel layer in a cylindrical cavity is highly coupled with the distribution of the electric current. A full scale simulation of the ESR process using a VOF model has shown that the shape of the pool interface is likely to be non flat."

Jan 1, 2011

By Du Sichen, S. Seetharaman, Wei Liu

"The viscosities of two-phase mixtures are of great importance in the modelling of the fluid flow in metallurgical processes. For example, in steel making and refining, the intimate mixing of metal droplets in the slag phase requires a consideration of the effective viscosities for the mixture. The present work was aimed at an understanding the phenomena underlying the viscous flow in a two-phase mixture with widely differing viscosities.Emulsions of silicone oils of known viscosities (345mPa.S and 1010mPa.S at 293K) with small amounts of water evenly distributed in the same were prepared by subjecting the mixture to uniform stirring using a magnetic stirrer. The viscosities of these emulsions were measured at constant temperature by rotating cylinder method using Brookfield Digital Rheometer. The uniformity of the preparation of the emulsions was confirmed by the reproducibility of the results. Th7 measured viscosities were generally found to be independent of the torque under the experimental conditions so that the two-phase mixture could be considered as a Newtonian liquid. The variation of viscosities with temperature and the effect of addition of a surface-active substance were also studied in this work.The measured viscosities were found to be· higher than those of both pure water and silicone oil. The experimental viscosities were found to increase with increasing concentration of water. The influence of surface tension on the viscosities was examined by adding surfaceactive agent to the mixtures. The result is discussed and compared with theoretical models developed by Einstein, Taylor and Oldroyd."

Jan 1, 2000

By Katsunori Yamaguchi

Secondary materials, that contain relatively high concentrations of platinum group metals, (PGMs) are treated in copper smelting process. The PGMs lost in the slag is increasing with increasing quantities of scrap treated amount. To determine the portion of the PGMs chemically dissolved and that associated with the mechanically trapped matte in the slag will be a key factor to improve the recovery of those metals. An experimental study was carried out to determine the distribution of palladium between the FeOx–SiO2 slag and the liquid Cu2S–FeS matte at 1573 K and a fixed partial pressure of SO2 of 0.1 atm. It was found that the distribution ratios are around 10−3 for platinum and palladium. The distribution ratios show a tendency to increase when the grade of matte is increased above 60 mass% Cu. In addition, the solubility of platinum in FeOx–SiO2 slag equilibrated with a pure palladium and the Pd-Cu alloy was determined at 1573 K and the range of oxygen partial pressure from 10−9 to 10−7 atm. The solubility of palladium in the slag tends to increase with increasing oxygen partial pressure and activity of CuO0.5 in the slag.

By Tsembel Darjaa, Toru H. Okabe, Yoshiaki Umetsu

"With the purpose of extracting molybdenum and rhenium from molybdenum sulfide concentrate; .electrolysis of slurry, solvent extraction and ·precipitation operations were carried out. The slurry of the concentrate in 10 mass% NaCl aqueous solution was continuously circulated into a vertical type 10 stack bipolar electrolytic cell consisted of carbon electrode disks, and, the concentrate was dissolved by electrochemically generated oxidizers at 313 K. The current efficiency for molybdenum dissolution was 73 % after 10 hours electrolysis, and the leach solution was found to contain 0.2 mol/l of molybdenum and 4x10-5 mol/l rhenium. This result shows the dissolution is more than 8 times faster than that obtained using a single cell. The leach solution from electro-oxidation was then subjected to a solvent extraction for rhenium which is then recovered as sulfides. After rhenium separation, molybdenum was precipitated by pH adjustment, and solid MoO3 (H2O)x crystals, free of sulfate, were obtained from the leach solution containing large amount of so42-.IntroductionIn the past, electro-oxidation using a bipolar cell was applied for leaching molybdenite concentrate and ores at U. S. Bureau of Mines [1-3] and also at Bhabha Atomic Research Center [4]. In· these previous studies, Moebious type bipolar cells, in which electrode plates were vertically inserted into the free surface of the electrolyte, were employed and its effectiveness was demonstrated.Recently, the present authors studied on leaching of Mongolian molybdenite concentrate, and the effectiveness of leaching of the concentrate by electro-oxidation in alkaline and acidic NaCl solutions was demonstrated [5]. The leaching reaction during the process can be explained by the 18 electron transfer reaction of molybdenite (MoS2) with the oxidizers produced in-situ by electrolysis of NaCl aqueous solution. Further investigation was made with respect to various process parameters for electrooxidation such as pH, pulp density and temperature of the slurry, and the dissolution behavior of minor elements such as iron, copper, and rhenium [6]. Solubilities of molybdenum in the leach solution at, various temperatures and pH .was · studied, and feasibility of molybdenum recovery by hydrolysis of molybdenum species was demonstrated. By adjusting the pH of the leach solution, molybdenum oxides or hydroxides free from sulfate were successfully obtained from the solution containing large amount of sulfate ion. Rhenium present in the concentrate at a level of several tens of mass ppm was found to dissolve into the leach solution, and co-precipitate with the molybdenum compounds. Rhenium in the leach solutions, therefore, has to be recovered before precipitation of molybdenum, otherwise it is lost in the precipitate."

Jan 1, 2000

By Peter Olubambi, Babatunde Obadele, Oluwagbenga Johnson

"The microstructure and corrosion behaviour of titanium carbide (TiC) reinforced duplex stainless steel matrix surface composites synthesized by laser melt injection technique was investigated. The surface melting operation was conducted using a 4.4 kW CW Nd:YAG laser with laser power of 1.5 kW, scanning speed of 0.4 to 1.0 m/min, beam size of 3 mm and argon shield gas flow rate of 4 L/min. The morphologies and microstructures of the coatings examined using field emission gun scanning electron microscope (FEGSEM) revealed homogeneous distribution of fine precipitates of TiC in the matrix, while X-ray diffraction (XRD) analysis confirm no phase change. TiC addition to the steels significantly increased hardness value to about 547 Hv0.1 but slightly decreased the corrosion resistance of the steels in 3.5% NaCl possibly due to the intergranular carbide coating that prevented chromium from forming continuous passive oxide layers.IntroductionComposite materials evolve from the idea of combining two basically dissimilar materials with different physical and mechanical properties to arrive at a product whose final properties are superior to those of the individual components [1]. Metal matrix composites (MMCs) are receiving much attention and are the focus of intense research and development worldwide for aerospace, automotive and other applications because of their excellent combination of ductility and toughness of the metallic matrix with high hardness and strength of carbides reinforced in the matrix [2]. Surface modification techniques such as laser, thermal spray, plasma spray, chemical vapour deposition have been use to fabricate MMCs. Laser melt injection (LMI) is a surface modification technique known since the 1980s [3] has been used to improve surface properties of metallic alloys such as aluminium, titanium and steels [4-6]. It involves the lateral injection of carbides, ceramics and cermets blown by a gas stream into a liquid metallic pool, created by laser irradiation of the top surface of the base material."

Jan 1, 2012

By Arpad E. Torma

The identification and characterization of lithographic iron and sulfur oxidizing bacteria in the 1940' s. opened up new possibilities and challenges for the mining and metallurgical industries. These were exploited during the 1950's and' 1960's, when it was demonstrated' that mining wastes and complex unused mineral resources could be economically treated by bacterially assisted heap and dump leaching processes?. During the 1970's this technology grew into a more structured discipline called "biohydrometallurgy". In the l980's efforts were devoted to the identification of a variety of organisms involved in naturally occurring leaching processes. Further efforts dealt with the elucidation, of leaching mechanisms; the leach ability of nickel, coban, zinc, and precious metals; the desulfurization of coal; and diverse biosorpion phenomena. The application of genetic engineering techniques for the improvement of microbial performance was also initiated?. Current trends in biohydrometallurgy include improvement of many of the techniques noted above, as well as application of leaching. technolog.ies to. environmental remediation scenarios. These activities afford considerable opportunities for research in the 1990's. For example, bioremectiation of abandoned mining and processing sites requires development of new and economically viable technologies capable of removing low concentrations of toxic metals from high volumes of solid and/or liquid wastes.

Jan 1, 1991

By M. Misra

The bacterium?Mvcobacterium Phlei has a demonstrated potential to be used for the flocculation of a variety of finely divided minerals. The microorganism possesses both hydrophobic surface and high negatively electrostatic charge. It can adhere to many mineral surfaces ?if the charge and hydrophobic interaction? between the microorganism and the minerals are favorable to adhesion. Experimental results showed that the dolomitic phosphate slime from Florida and fine hematite can be :readily flocculated from dilute suspension.. In the case of dolomitic phosphate slime, a consolidated sediment containing 24'-25 weight% :solids can be obtained from .a dilute slurry .in a short time. Sediments obtained from hematite flocculation are rather massive and more .consolidated than phosphate slime. Mycobacterium Phlei has a specificity for selective flocculation of hydrophobic fine coal particles from pyrite and ash containing minerals. Because of mutual hydrophobic interaction of coal and Mycobacterium Phlei, it was noticed that coal particles appear to be strongly held in the aggregate by adhesion or bridging of bacteria. However, Mycobacterium Phlei is not a good flocculant for either associated pyrite or ash present in coal.

Jan 1, 1991

By Dong Liang, Honggang Zhong, Zhenxing Yin, Qijie Zhai

"2507 super duplex stainless steel (SDSS) has been widely applied in a marine environment, attributing to its excellent pitting corrosion resistance and mechanical properties which are particularly determined by the nitrogen precipitation behaviors and volume fraction of ferrite. In this paper, various cooling rates were obtained by applying four different moulds with the common gating system. By which the influence of cooling rates on nitrogen precipitation behaviors and the ferrite fraction in cast 2507 SDSS was comparatively investigated. The results showed that nitrogen porosity could easily precipitate in cast 2507 SDSS under standard atmospheric pressure. The number of nitrogen holes increased with decreasing the cooling rates, and the holes mainly distributed in three zones, i.e. the interface between the horizontal and vertical columnar grains, top vertical columnar grains and the final solidification region. Additionally, higher ferrite fraction was obtained with lower cooling rates.IntroductionDuplex stainless steels (DSS) have a dual-phase microstructure consisting of ferrite (d) and aus-tenite (?). Due to the combined advantageous properties of d and ? phase, their application rapid-ly increased in industry [1, 2]. Super duplex Stainless Steel (SDSS) is the third generation of du-plex stainless steels, of which the alloy elements Cr, Ni and N content are higher than the stand-ard 2205 DSS. Because it has high contents of alloy elements, the SDSS has better mechanical properties, and its pitting resistance equivalent number (PREN) reached a point 43. Hence SDSS has been used in petroleum chemical industry, the marine equipment and harsh corrosion environments [3]. SDSS contains ferrite stabilizing elements, such as Cr, Mo and Si, and austenite stabilizing elements like Ni, Mn and N [4]. Many researchers have studied the effects of these elements on the stabilization of d and ? phase and the ratio of the two phases. High nitrogen con-tent is another prominent feature of SDSS. Nitrogen addition to SDSS is very effective for improving its mechanical properties [5] and corrosion resistance [6], such as pitting resistance in NOx environment. To increase the nitrogen content in steels, a lot of work had been done. N. Nakamura and S. Takaki [7] examined the behavior of nitrogen absorption in Fe-23Cr alloy powder by sintering in nitrogen gas atmosphere, they found nitrogen content easily up to 1.0 wt. %. Using devised NH3 gas injection system, W. Park et al. [8] successfully produced austenitic Fe–23.5Cr alloys containing over 3 wt. % of nitrogen. Further-more, W.P. Tong et al. [9] stated that nitrogen percent was extraordinary high (about 10 wt. %) in pure iron plate. However, the above methods are difficult to be applied to large-scale industrial production."

Jan 1, 2012