Search Documents

Jan 1, 1922

By Zay Jeffries

It has been known for centuries that iron and steel could be hardened by cold hammering and that the metal could be restored to the normal condition by heating to a red heat arid cooling, either rapidly or slowly with nearly pure iron, but slowly with steels containing considerable carbon. The art of tempering steels is also very old. When a medium- or high-carbon steel is quenched from a cherry-red heat, the hardness is increased; this hardness can be reduced by heating to various temperatures below the lower thermal critical point,, which is near 700" C. The present paper will not consider these old and well known changes in iron and steel below the thermal critical range but will confine itself to the more unusual changes, some of which have been studied recently. Stromeyer,1 for example, In 1886, reports that both working steel and heat treatment of steel in the blue-heat range arc highly injurious. Recently, however, some metallurgists believe that the straiglltening of warped steel forgings at a blue heat produces a beneficial effect on the metal2 The Engineering Division of the National Research Council has constituted a committee on Physical Changes in Iron and Steel below the Thermal Critical Range, which has the following personnel: K. R. -Abbott, H. C. Boynton, William Campbell, J. V. Emmons, F. B. Foley, H. J. French, H. M. Howe, Zay Jeffries (chairman), F. C. Langenberg, J. A. Mathews, P. D. Merica, A. H. Miller, J. H. Nelson, G. A. Reinhardt, W. E. Ruder, H. F. Wood. This committee is studying several aspects of the physical changes in iron and steel. The results, reported in the literature and obtained by recent experimentation, will be given; this will be followed by a general theoretical discussion of the more important

Jan 1, 1922

By Daniel M. MacNeil, Carle R. Hayward, Raymond L. Presbrey

At the February, 1916, meeting of the Institute, a paper presented by Hayward and Raymond gave the results of a study on the effect of time in tempering medium-carbon steel, when the following conclusions were reached: It is not fair to consider the question settled when only three specimens were used for each treatment, but the results obtained indicate that for reheating quenched medium-carbon steel to temperatures below 500" it is only necessary to heat it through. Longer heating has little or no effect on the tensile strength, ductility, or hardness. At temperatures above 500°, increasing the time of treatment causes a slight falling off in hardness and tensile strength with a corresponding increase in ductility. In the discussion of the paper these conclusions were attacked and evidence was presented that seemed to throw doubt on their accuracy. The authors, however, showed that this evidence was based on high-carbon or alloy steels and no facts regarding medium-carbon steel were presented. During this study the heat treatment was carried out in a small electric resistance furnace. It held nine specimens, but when these were placed in the furnace the temperature was lowered to such an extent that 30 to 40 min. were required to reach the desired heat. The authors pointed to this as a weak point in the investigation and it seemed wise to supplement the research by work on similar steel but using a different method of heating. This has been done and the results are given in the present paper. The Rhode Island Tool Co. coöperated by furnishing the steel and turning the tensile specimens. The steel used in this investigation came in three bars 3/4 in. in diameter; analyses are as follows: Carbon. MaNGanese, Phosphorus, Sulfur Bar NUmber PeR Cent. Per Cent. Per Cent. Per Cent. 1 0.46 0.56 0.010 0.055 2 0.44 0.58 0.007 0.042 3 0.48 0.58 0.007 0.048

Jan 1, 1922

By H. J. French

At the request of a committee of the Engineering Division,' National Research Council, a study of the properties of boiler plate at various temperatures up to about 900' F. (482" C.) has been instigated. The following is a report of preliminary tests made on two grades of 1/2-in. plate and includes a description of the apparatus used in the determination of the proportional limit. Detailed reference to- the many published investigations in connection with the properties of steel at various temperatures will be omitted from this report. Suffice to state that results obtained for variation in tensile strength, elongation, and reduction in area with temperature are in substantial agreement with the effects now generally considered to be correct. Comparison of proportional limit values with results obtained by other investigators will be found in the conclusions. Materials Used The steels tested were $1/2-in. (12.7 mm.) open-hearth boiler plate of firebox and marine grades. The specified tensile strength and the analysis for each are shown in Table 1. In the manufacture of this material, a

Jan 1, 1922

By Howard Scott

The great advances made in mechanical engineering during recent years through the use of alloy steels, as illustrated by the development of the airplane and automobile, may be ascribed primarily to the application of nickel as an alloying element. The ternary system iron-carbon-nickel has a wide industrial application and forms, further, thefundamental basis of the even greater class of the widely used quarternary steels such as nickel-chromium, nickel-silicon, and nickel-vanadium. As is not uncommon with such cases of virile growth in an industry, the application of the alloy steel in a largely empirical manner has outstripped its scientific development so that a fertile field for metallographic research still remains. In this field, the basic nickel steels require first consideration and are the subject of the present investigation, which is offered as a preliminary to the study of the more complex alloys of industrial importance Of the principal tools of metallography—microscopic examination, determination of mechanical properties, and thermal analysis—the last has developed much more slowly in its application to industrial needs so that the situation often exists that heat treatment operations are based on empirically determined temperatures; that is, temperatures deterrnincd without regard to the actual transformation characteristics of the alloy. This situation is undesirable as there is no uniform standard for comparison of results. It is due, outside the usual difficulties involved in temperature measurements, to the pioneer character of much of the published work; to the lack of definiteness of the Ac, transformation,1 particularly in low-carbon steels; to the failure to define operating conditions completely; and to the paucity of information correlating thermal characteristics with results of heat treatment.

Jan 1, 1922

By J. J. Thomas, J. H. Nead

This investigation was undertaken to determine, if possible, the relation between static and dynamic tensile tests as measured by the work required to break test specimens slowly, in a tensile testing machine, and rapidly, by means of a falling weight. It was hoped that the investigation would throw some light on the role played by ductility under different rates of application of load. In problems of design, it is usually assumed that the moduli of elasticity of all steels are equal; viz., about 30,000,000. The stress-strain diagram within the elastic limit is a straight line, as shown in Fig. 1, where OA is the curve of a hard steel and OB that of a soft steel. If the modulus of elasticity is constant, as assumed, the slope of the line OC

Jan 1, 1922

By John A. Mathews

During the prosecution of the aircraft-production program in 1917 and 1918, the writer visited many plants engaged in the manufacture of motors, planes and parts, in carrying out his duties as chairman of the Committee on Aircraft-engine Forgings. On several occasions, when the question of expansion was discussed, it was noted that there was confusion in the use of the terms: the true coefficient of expansion, a physical constant, and distortion in hardening. One engineer, referring to a steel shown in the accompanying table, stated that he could not consider it for crankshafts because of its excessive coefficient of expansion, while another steel, also Iisted in the table, was said to be especially good because it had no coefficient of expansion, since it came out of the oil bath perfectly straight. Many years ago one of our employees designed a new oil furnace; when asked what became of the products of combustion, he replied: "There ain't any, we burn them all up." While the coefficient of expansion is not without its effect in volume changes in hardened steel, it is not a determining factor in the matter of distortion and going out of shape. Irregular heating, uneven furnace bottoms, and carelessness in withdrawing the part from the furnace, as well as the manner in which the part enters the quenching bath are of greater moment. Generally speaking, also, steels of relatively low hardening temperature will distort less than those requiring higher hardening heats. The coefficient of expansion must be considered in engineering design most frequently when different metals or alloys are used in the same construction. For example, the difference of expansion between a steel crankshaft and an aluminum crank case might be of real importance and a steel with no coefficient of expansion would be much less desirable than one with the normal coefficient. About 15 years ago, the writer made many determinations of the coefficient of expansion at low temperature ranges, usually between 20' and 100" C. Among the materials tested were: Pure forged electrolytic iron, 11.73 parts per million for l° C.; cast aluminum (99.93 per cent. AI.),

Jan 1, 1922

By John A. Mathews

It is twenty years since the writer made his first molybdenum steels and others were making them commercially five years earlier but the prevailing opinion seems to be that molybdenum steels are new; from time to time the daily press speaks of important discoveries in Europe and intimates that American steel makers have much to learn in regard to alloy steels. The earlier experiments were largely confined to the use of relatively high percentages of molybdenum in tool steels and permanent magnet steels. Recent developments deal with the types of alloy structural steels used for airplane, automobile, and other engineering requirements; in these, the molybdenum content is usually less than 1 per cent. The earlier types generally have been unsuccessful commercially, but the newer types of steels are becoming of increasing importance. The war showed our dependence on foreign sources for alloying metals; molybdenum alone is widely distributed in the United States and seemingly abundant. Many deposits are not now of commercial interest, owing to location and relatively small amount of ore available, but other deposits are being developed and a stable source of supply seems well assured. In tool and magnet steels, it was early found that 1 part of molybdenum was equivalent to from 2 to 2.5 parts of tungsten. The permanent magnet steels investigated by Madame Curie,' in 1898, contained from 3.36 to 4.05 per cent. molybdenum; in 1902, Dr. E. L. French and the writer thoroughly tested steels containing from 2.0 to 4.0 per cent. These steels gave satisfactory tests for permanence, but were low in residual density and much more sensitive to hardening than the corresponding tungsten products. We discontinued work with them, therefore, and have no advice that such steels have been used commercially here or abroad. Prior to the development of the Taylor-White process and the modern high-speed steels, air-hardening steels were in general use. These were

Jan 1, 1922

By P. W. Bridgman

During the war, the Navy undertook the construction, under my direction, of an experimental gun embodying features designed to lessen the cost and time of production. These experiments were initiated after representations as to their desirability had been offered by myself, by the Naval Consulting Board, and by the National Research Council. The first drawings were made in June, 1917, and the experiment was completed in November, 1918. For the sake of clearness it will pay to recapitulate briefly the fundamental idea of gun construction. It is well known that if a hollow cylinder is subjected to internal fluid pressure, the maximum stress occurs in the inside layers, the outer parts carrying much less than their due share of the stress. This inequality of stress is more pronounced the thicker the walls of the cylinder. If such a cylinder is pushed to the elastic limit, failure in elasticity will take place long before the outer lagers have reached the limit of their capacity. Economical use of the material would demand, however, that all parts of the cylinder reach the limits of their capacity simultaneously. This may be brought about, at least in cylinders of not too great thickness, by producing in the inner layers an initial compression, and in the outer layers an initial tension. The effect of internal pressure is at first to relieve the compression of the inside layers, while increasing the tension of the outside layers. If the initial stresses are properly distributed, all parts of the cylinder will reach their elastic limits simultaneously, thus giving a cylinder of maximum strength for its weight. In gun construction as hitherto practiced, this initial distribution of stress is produced either by winding the inner tube with wire, a common English practice, or by shrinking hoops over the inner tube, which has been the standard American practice. Either process is long and expensive, particularly with the larger guns, 12- or 14-in., which require

Jan 1, 1922

By Frank E. Hall

The needs of the World War showed the necessity of a metal stronger than cast iron which would supplement the supply of steel. SO patriotic metallurgists were spurred to new efforts to improve the status of that half-breed of the metal world that had been, more or less erroneously, christened semisteel. As a result, it was developed that for certain purposes semisteel was superior to steel in the manufacture of shells. Steel, because of its greater strength and toughness, is able to carry a greater charge of explosive, weight for weight; consequently, a steel shell can be expected to cause greater destruction when used against fortifications or other inanimate objects, while semisteel, because of its comparative brittleness and its resulting greater fragmentation, is capable of inflicting more serious loss of life when used against opposing forces of men. Therefore, each has its proper place in the economy of war. For the present purpose, steel may be defined as a comparatively pure iron whose physical nature is modified by small amounts of carbon, silicon, sulfur, phosphorus, manganese, and possibly other rarer elements; while cast iron generally is limited to approximately 93 per cent. of iron, the remainder consisting of larger percentages of carbon, silicon, sulfur, phosphorus, and manganese. Semisteel may be defined as cast iron in which the carbon and silicon have been reduced to as low a point as is consistent with maintaining the nature of gray iron, and in which the remaining elements are adjusted so as to give the greatest strength. The fact that the addition of steel scrap, in varying percentages, is the means used to reduce the carbon, together with the fact that a considerable increase in strength results, is probably the explanation of the origin of the name semisteel. That ordinary grades of steel show from three to four times the tensile strength of cast iron is due to the fact that the crystals, or grains, of cast iron are interspersed with flakes of

Jan 1, 1922

By Henry M. Howe, W. P. Barba

When this country went into the war, but two concerns, The Bethlehem Steel Co. and The Midvale Steel and Ordnance Co., knew how to make steel fit for great cannons and at these concerns there were relatively few men who knew the whole art. Fortunately, certain of these men put their knowledge at the service of the Government, and proceeded to instruct the metallurgists at the arsenals and at various steel works. Doctor Howe, then chairman of the Engineering Division of the National Research Council, suggested that this work might be facilitated, and the number of effective gun-steel makers thereby increased, if a detailed description of the best practice could be written, giving the reasons for the various steps, and issued with the endorsement of a committee composed of those who were evidently the most competent authorities. It was thought that something would be gained by clarification of the subject, and something by the eminent authority of the members of the committee. To that end, the Engineering Division appointed a committee, consisting of the gentlemen whose names follow, to mention on1y those who retained their connection with it. At this time there were serious difficulties in the manufacture, for the Government. of aircraft and high-speed engine crankshafts, of certain ordnance forgings, and of shells for both the Army and Navy. This Committee was asked to study and report upon these, with a view to betterment of practice. There were indications that the source of some of the difficulties went back to the melting of the steel and the production of the ingot. Hence, the committee first studied steel melting and ingot production, in order to guide the wartime manufacturers to an even larger percentage of useful production from the steel initially melted. Committee on Steel Ingots W. P. Barba, chairman, Ordnance Dept., U. S. A. (formerly Vice Pres. & Gen. Mgr., Midvale Steel Co., Philadelphia). George K. Burgess, Chief of Division of Metallurgy, U. S. Bureau of Standards, Washington, D. C. Henry M. Howe, Then Chairman Engineering Division, National Research Council.

Jan 1, 1922

By Wm. R. Webster

This is a contribution for the proposed new discussion on the physics of steel. The former discussion on the subject started with the consideration of five papers presented at the Chicago meeting in 1893, and continued for several years. The Suggested Lines of Discussion, prepared by Doctor Howe, covered a wide field and added greatly to the success of the work. Naturally, the first step in a new discussion will be to remodel and bring up to date the old Suggested Lines of Discussion so as to embody all the important advances in the metallurgy of steel that have a bearing on the physics of steel and keep the papers and discussions within the field of work undertaken. This paper will be devoted to the practical application, in rolling steel, of the effects of carbon, phosphorus, and manganese on its tensile strength, with some suggestions on further research work. Dr. J. E. Stead, in his paper Influence of Some Elements on the Mechanical Properties of Steel,' gave a complete review of all that had been done during the past thirty years. He gave full credit to all investigators who worked on these lines, also their results, with his views on same, and in many cases his own results. All of this data and much new valuable information were put in convenient shape for reference and study. To do this required a great deal of work, which is fully appreciated by the steel manufacturers and investigators. The variations in the values given by the different investigators for the increase of the tensile strength of steel for each 0.01 per cent. of carbon, phosphorus, and manganese were largely due to the steels they worked on, the large or small variations in the amount of the elcments present, and the omission to take into consideration all the factors, from the blast furnace through to finished rolled material, that affect the character of the steel. For instance, a poorly made dirty steel requires considerably more carbon to give the same ultimate strength than a well-made clean steel with the same phosphorus and manganese content.

Jan 1, 1922

By H. E. Wheeler

The work described was carried out during 1917 and 1918 at the testing laboratory of Watertown Arsenal at the instigation of the Nitrate Division and later with the concurrence of the Cannon Section of the Ordnance Department, U. 8. A. The experiments follow three principal lines of work: First, the effect of nitrogen under pressure on steel containers of various compositions at a red heat; second, the effect of decomposing ammonia on various alloy steels, iron, and non-ferrous alloys; third, a new theory of the erosion of guns in respect to the effect of nitrogen in steel. Part I In the Haber process for the manufacture of ammonia from its elcnlents, it is necessary to have nitrogen and hydrogen of 1500 lb. per sq. in. (105.5 kg. per sq. cm.) at a temperature of 500 to 600' C. The steel containers for these gases gave trouble by failing without apparent cause. When the General Chemical Co. began to develop its method for the production of ammonia, it experienced the same difficulty and, knowing that the Haber process had solved the difficulty by the use of alloy steels, it made several small steel bottles of different compositions and kept them filled with these gases at this pressure and temperature until they failed. The time of service varied from a few days, for the plain steel casting, to two years for a chrome-vanadium forging. Four of these steel bottles were sent to this laboratory for investigation; they were a plain carbon-steel forging, a nickel-stee1 forging, a chrome-vanadium steel forging, and a chrome-steel forging. The time of service was as follows: plain carbon steel, 4 mo.; nickel steel, 6 mo.; chrome-vanadium steel, over 2 yr.; chrome steel, 4 mo. When these containers were cut open and the cross-section surface polished, they showed an inside zone with a different luster from the rest of the metal. Upon etching, this zone was almost unaffected while the rest of the steel etched normally.

Jan 1, 1922

By William J. Priestley

In the manufacture of gun forgings and other steel parts that, in service, are subject to sudden high stresses and shocks, it is most desirable to use steel possessing the greatest toughness and ductility possible without sacrifice of strength. In order to obtain this condition, it is necessary to procure steel that shows the highest possible elongation and reduction of area without lowering the tensile strength and clastic limit. Proper heat treatment of the steel can control this condition within certain limits. When heat treatment has failed to produce the desired results, metallurgists have used steels containing molybdenum, zirconium, vanadium, chromium, tungston, etc. The purpose of this paper is to describe a method by which these desired physical properties may be procured—by the elimination of certain impurities that inherently exist in steel made by the open-hearth process, and without the use of expensive alloys. Design of Gun Forgings In the manufacture of gun forgings, a certain elastic limit is fixed by the designer, and the walls of the gun arc made of the proper thickness, allowing a suitable factor of safety for the high stresses and sudden shocks that occur during gun firing. The clastic strength of the gun is about 1.4 times the stress set up at any point along the bore of the gun during firing with the maximum powder charge. As the stresses set up in the walls of the gun during firing are mostly "tangential," all physical tests are taken in this direction. Due to the length of the forgings, these tangential test bars are always taken at right angles and transverse to the direction of flow of the metal in forging. Furthermore, test bars taken across the grain of the metal will more frequently expose defects and foreign inclusions in the steel than will bars

Jan 1, 1922

By H. W. McQuaid, E. W. Ehn

It is usually assumed that chemical specifications are sufficient for steel to be used for case carburizing, and if the steel analyzes within the ordinary limits specified for steel for this purpose, no difficulty traceable to the steel used should be encountered in obtaining satisfactory results in the case carburizing and hardening. Much work has been done to determine the effect of various alloying elements on the rate of carbon penetration, etc. but, to our knowledge, little if anything has been published in regard to the effeet of the quality of the steel on the final results in the hardening of case-carburized steel parts. The writers believe that the structure of the case both before and after quenching is greatly affected by the actual condition of the steel itself as made, and that for good results in the case-carburizing and hardening departments, the steel should be of the best possible quality as regards non-metallic impurities. It is the purpose of this paper to prove that the presence of excess dissolved oxides in the steel, as made in the melting furnace, affects permanently the results obtained in carburizing and hardening and that it is possible that the presence of dissolved oxide call result in total unfit-ness of low-carbon steel for case hardening purposes. When races and rolls for roller bearings are made from a low-carbon steel, case carburized and hardened, it is of primary importance that the results of this treatment be of the highest quality. It is necessary, therefore, that in the case-carburizing work each detail be rigorously checked to avoid any defects which would cause the loss of much time and material. The case carburizing with which this paper deals was done in under-fired oil furnaces. The temperature of each furnace is controlled by means of a platinum platinum-rhodium thermocouple, in connection with a potentiometer indicator and potentiometer recorder. The temperature of each furnace is registered every 15 min. by an operator, who is continually checked by the automatic recorders.

Jan 1, 1922

By George R. Ensminger, E. Heaton Hemingway

During the past year, the Watertown Arsenal has been interested in the occluded gas and oxide content of certain ordnance steels in order to determine, if possible, whether some of the peculiar failures in their physical properties might not be traced to these causes. For the purpose of best accomplishing a study of this nature, it was decided to heat the various samples of steel in a vacuum for definite periods of time at high temperatures and carefully examine the quantity and composition of the gases evolved. By the use of a fused quartz tube fitted with a water-cooled, ground-glass stopper, it was possible to maintain a vacuum at a temperature of 1000" C. for 10 hr. without perceptible leakage being evidenced as measured by a McLeod gage. The silica tube was connected with an evacuating system so constructed that the volatilized gases could be removed from time to time and a low vacuum of 0.0002 to 0.0010 mm. of mercury continuously maintained. At no time during the period of heating or in the removal of the gases did the evacuated system come in contact with rubber stoppers or any rubber connections, making contamination from such a source, impossible. In other words, the only volatile products that could be: obtained must necessarily have come from the steel itself or from the glass and fused quartz system or from the mercury used as a sealing agent. In the carlier experiments, the steel treated was in the form of turnings, but this practice was discarded because the weight's of the turnings before and after being heated were widely inconsistent,, even when taken from the same piece of steel. This discrepancy developed largely through variation in the amount of metal volatilized with the gases; this metal could always be seen in the form of a ring where it condensed in the cooler portion of the tube in either the amorphous or crystalline condition. Because of the frequency in occurrence and the variation in the manner of deposition, this material was roughly analyzed and found to consist for the most part of iron. At the same time two samples of steel that had been

Jan 1, 1922

By Howard Scott, Henry S. Rawdon

The method of demonstrating the structure existing in a metal or alloy at high temperatures, by etching a polished sample after it has been heated to the desired temperature, is quite familiar to metallog-raphists. The usual procedure1 2 is to heat the specimen, previously polished for microscopic examination, to the desired temperature, in a neutral atmosphere (hydrogen or nitrogen), then admit the etching gas (chlorine, hydrochloric acid or similar gas) for a few seconds, and finally, after flushing out the etching gas with the neutral one, cool the specimen in the neutral atmosphere. The pattern produced by etching at a definite temperature is usually taken as a record of the microstructure prevailing at that temperature. It has frequently been pointed out that changes in composition of the surface metal occur during the preliminary heating in the neutral atmosphere, so that the appearance produced by the etching at high temperature may not exactly represent the condition of the interior of the specimen. To overcome this uncertainty, the heating has sometimes been done in vacuo,3 the etching gas being admitted when the desired temperature was reached, then pumped out and the specimen cooled in vacuo. The studies of Rosenhain, Humfrey, and other workers 4, 5, 6, 7, 8 dem-

Jan 1, 1922

By Charles Y. Clayton

Cast-steel runners, while not interesting from a commercial standpoint, furnish valuable material for microscopic study. Folcyl found not only the usual ingot structure, but zones of Widmannstättian structure, which he explains as due to differential crystallization. The writer, in examining nickel-steel runners, found a type of pro-eutectoid ferrite that is unusual and most probably new. The runner in question was 8.75 cm. (3.5 in.) in diameter and analyzed at its center 2.69 per cent. nickel and 0.350 per cent. carbe a and at its edge 2.62 per cent. nickel and 0.359 per cent. carbon. Th macrostruc-ture, which is the usual type, is shown in Figs. 1 and 2, which are a cross-section and the longitudinal surface, respectively. Slight segregat'ion of ferrite can be seen near the center of the segment and at other points near the edges of polyhedral grains. Stead's reagent brings out the dendritic structure within the grains as shown in Figs. 3 and 4. This texture is what would be expected of such a steel. Figs. 5 to 10 show the peculiar swirls of pro-eutectoid ferrite, the finding of which prompted this paper. These swirls, or eddies, if such a term can be applied, occur in all parts of the runner and in all parts of the individual grains. The upper left-hand figure shows this ferrite at a grain boundary; the middle left-hand figure shows the inner portion of a grain; and the lower left-hand figure shows these swirls at the edge of a grain which is also the outer edge of the runner. Straight-lined ferrite associated with swirls is found in the areas of Figs. 11 and 12. The texture of the carbon-bearing constituent of the runner is shown to some extent in Fig. 12, the pearlite being very fine or sorbitic. Higher magnification does not bring out any new features either in the peculiar ferrite or in the pearlite. Figs. 13 and 14, at 240 diameters, show the curved and straight-lined ferrite.

Jan 1, 1922

By R. S. Archer

The proper representation of equilibria involving graphitic carbon in the constitutional diagram of the iron-carbon system is admittedly an unsolved problem, the complete solution of which will probably require the establishment of more experimental evidence than is at this time available. The object of this paper is to present the author's observations on some of the phenomena in question and his interpretation of this and other recorded evidence. The chief of the recently disputed questions upon which the author has experimental evidence concerns the occurrence of graphitization at temperatures below the Al point. In a paper1 presented at the September, 1919, meeting of this Institute, the following is found: "the results given would seem to indicate that the graphite eutectoid lies at a smaller value of carbon content than has been previously supposed. At least this is true unless there is either a marked formation of graphite eutectoid at these rates of cooling, or a decomposition of pearlite into graphite, both rather unlikely suppositions, but not impossible ones." In a discussion of this paper, H. A. Schwartz2 takes the position that the possibility of graphitization occurring below the A1 point is an open question, but that complete graphitization (to less than 0.10 per cent, combined carbon) commonly occurs above this temperature. Another opinion from the malleable castings industry is found in a recent paper3 by Touceda: "Also the carbide of iron can be broken up into its two soft constituents at the temperature referred to. This temperature is called the critical temperature, or critical range, and for air-furnace hard-iron castings it is in the vicinity of 1440" F. It is the

Jan 1, 1922

By W. T. Ober

the hammering effect acts only to a point 3 in. back from the cutting edge, and the hardening heat extends back only 1 in. from the cutting edge. Then, as a steel is taken from the fire, the grain condition is as shown in Fig. I. After the forging operation has been performed the condition shown by Fig. 2 exists. The heating operation to harden the cutting edge produces the effect shown in Fig. 3. The questions that naturally arise are: Will the cost of the extra heat treatment necessary to change this condition (annealing) be more than the saving that may be effected in the drill steel or will the extra heating be an economical as well as a wise thing to do? Is this condition necessarily detrimental to the maximum service of the drill steel? Can this annealing action be obtained in the hardening heat by heating more of the bit, say at least 5 in., to the hardening temperature but quenching only the end of the bit by a shallow immersion? Short Rock-drill Steels Reclaimed by Welding By W. T. Ober, Lynn, Mass. Experimental tests by the Thompson Company have shown that short lengths of rock-drill steels may be reclaimed by electric butt welding. The drills used in the experiments were hollow drills l1/4-in. in diametcr containing 0.95 per cent. to 1.05 per cent. carbon. The ends to be joined must first be ground off fairly square and the greater part of the rust, scale, etc. removed for 3 or 4 in. back in order to insure good electrical contact with the dies of the welder and countersunk, with an 80° countersink, approximately 1/4 in. The steels are then clamped in the copper dies of the welder, so that a length projects from the inside edge of each pair of dies equivalent to from one-half to three-quarters the diameter of the drill. The drills should also be brought into accurate alignment. The first step is to bring the ends into close proximity and then close the primary circuit of the transformer, slowly bringing the steels together until their ends lightly touch, when they will "flash," that is, minute

Jan 1, 1922