Search Documents

Jan 1, 1935

Jan 1, 1935

Jan 1, 1935

Jan 1, 1935

Jan 1, 1935

By C. A. Edwards

Jan 1, 1935

By Herman F. Kaiser, Charles S. Barrett, Robert F. Mehl

The copper-silver system presents several points of special interest in the study of segregate structures. The system is simple eutectic, with limited solid solutions terminal with the pure component metals. The extent of solid solubility decreases with decreasing temperature for both the copper-rich and the silver-rich alloys, thus offering a possibility for the formation of Widmanstätten figures and also a possibility for aging after quenching. In contrast to the structures studied previously the structures in this system are unique in their origin, for one terminal solid solution will precipitate the other, and vice versa. In most of the other systems for which crystallographic data on the precipitation (or transformation) process arc available, either intermetallic compounds or intermediate phases partake in the decomposition process; the absence of such phases thus distinguishes this system. The lattice structures of the two solid solutions are identical in type, differing in lattice spacing by approximately 10 per cent; because of this it seems difficult if not impossible to predict on the basis of present theory either the outward form of the precipitate or the lattice orientation relationships between matrix and precipitate. The eutectic temperature in the copper-silver system' is 779" C. At this temperature copper dissolves 4.3 atomic per cent (7.0 weight per cent) of silver in solid solution; this solid solubility decreases to zero at room temperature.² Silver at the eutectic temperature rctains 14.0

Jan 1, 1935

By Alden B. Greninger

Many recent contributions in the field of theoretical metallography have been concerned with crystallographic definitions or descriptions of various phenomena. The lattice orientation of the crystal being studied must be known before such definitions can be made. Practically all the metallic crystals used do not have crystal faces—other than the unknown "plane of polish"; hence resort must be had to other means of determining orientations. Some use has been made of etch-figures, slip bands, optical properties, etc., for this purpose; but for accurate results, and because of the fewer restrictions to their use, the various X-ray methods have been the most satisfactory.' The methods that have been used may be divided into two general classes: (1) oscillation methods, and (2) transmission Laue methods.² The disadvantages of these methods are numerous, chief among them being the time required to determine a complete orientation. No method proposed so far is wholly satisfactory for determining the orientation of a small macrograin within a polycrystalline aggregate.

Jan 1, 1935

By Alden B. Greninger

The study of mosaic structure of crystals1 has been confined until recently to the field of theoretical physics. Crystallographers, in general, have neglected the subject, although X-ray crystallographers constantly make use of formulas for intensities of X-ray reflection as modified by mosaic structure. Work on mosaic structure has centered chiefly on the task of proving or disproving the secondary-structure theory of Zwicky,² and very little attention has been paid to the visible imperfections of crystals. A. Goetz has been responsible for most of the supposed experimental confirmations of Zwicky's theory.3 On the other hand, Smckal,4 and Orowan,5 among others, maintain that there is neither theoretical nor experimental evidence to substantiate Zwicky's secondary structure. Lately the subject has been intensively investigated by Buerger,6 one of whose recent papers led to a symposium on mosaic structures.'

Jan 1, 1935

By John T. Norton, V.G. Mooradian

The diffusion of metal atoms into the crystal lattice of another metal and the assumption of regular positions to form a homogeneous alloy are some of the most fundamental phenomena of structural metallurgy. The mechanism of this process has been the subject of a great deal of study from many viewpoints, but the picture is still far from complete. It is generally believed that if one metal is to diffuse into another, the first must have some solubility in the second1. This means that the solvent must be able to accommodate the stranger atoms, either on points of its own lattice or in the interstices between, without losing its own crystal-lographic identity. It is also a general observation that cold-working is a distinct aid in the diffusion process, causing it to take place with greater rapidity at the same temperature or with the same speed at a lower temperature. There is considerable doubt, however, as to the real significance of the deformation in its effect on the diffusion mechanism. Several factors associated with the cold-working may be responsible for the increased diffusion rate. The plastic deformation causes a distortion of the solvent lattice, which may be an aid in the assimulation of atoms of another kind. There are many references2 in the literature that suggest that some distortion or "loosening" of the lattice is necessary for atomic migration and that diffusion cannot take place in the undis-torted lattice. On the other hand, it may be that the cold-working causes an increase in surface of contact between the two metals through fragmentation or provides a more intimate contact that is necessary for diffusion. If it is true that lattice distortion is an important factor in diffusion, it seems as if there should be some particular relation between

Jan 1, 1935

By Arthur Phillips, R. M. Brick, A. J. Smith

A previous publication1§ has described the effect of quenching stresses on the lattice parameter values of high-purity aluminum-copper alloys particularly with reference to the solution and precipitation of CuAl². A similar study has been made of the aluminum-rich aluminum-magnesium alloys. Attention has been directed in the present investigation to the magnitude of the quenching stresses as affected by the specimen size and shape, the number of solute atoms and the quenching rate. The effect of cooling stresses in causing plastic defomation or cracking has been considered in relation to the physical properties of the alloy On reheating alloys in the two-phase field, the time required for precipitation to occur has been observed in connection with the degrec of supersaturation, the rate of diffusion of the solute atoms as a function of the comparative atomic radii, degree of strain, temperature of reheating and grain size. A few qualitative comparisons on the relative effect of these factors have been drawn between the aluminum-copper alloys and the aluminum-magnesium alloys. Strain in Solid-solution Alloys A 10 per cent magnesium alloy ill the form of chill-cast bars was furnished by the Aluminum Company of America through the courtesy of L. W. Kempf. Additional alloys were prepared using alllminum (99.95 per cent Al) and high-grade magnesium. The alloys listed in Table 1 were melted in an Acheson graphite crucible under a flux of fused MgCl², CaC12, NaCI. Chill-cast rods were sealed under vacuum in Pyrex glass, homogenized several days at 450' C., air-cooled and machined to rods of from 1/8 to ¾-in. dia. Metal powders taken from these rods with a fine-toothed saw were again sealed under vacuum in

Jan 1, 1935

By Russell W. Dayton

The metallurgical polarization microscope has been utilized in several researches in the last few years, thus attaining a fair degree of prominence, but little has been written in a manner suitable to a metallurgist concerning the theory of this instrument. In this investigation the theory was carefully studied, and the results are presented here in a detailed manner, yet as simply as possible. The theory is discussed with particular reference to the three chief functions of the instrument: (1) determination of anisotropy; (2) effect of strain; and (3) identification of inclusions. Each of these is investigated experimentally, with especial attention to the mechanism of producing any effect. Where possible, the discussion is supplemented by photomicrographs. The instrument used had numerous defects as a polarization microscope; these and their remedies are discussed. In the microscopic study of transparent mineral sections (chalcography) the use of polarized light has aided tremendously in the identification of a mineral. The determination of strain in transparent substances (photoelasticity) by the use of polarized light has lately become a commercial process, used in testing finished glass articles. The success of the use of polarized light with opaque materials has not been so great. The magnitude of the effects obtained is much less than that of the corresponding effects with transparent materials, and the mechanical difficulties are much greater. Königsberger,"' i in 1909, was the first to apply polarized light to the microscopic study of opaque substances; Endell and Hanemann(2) were the next, in 1913. In 1919 and 1920, Wright(3,4) prepared two papers on the subject. In the first he developed the detailed mathematical theory from the viewpoint of the electromagnetic theory of light, and in the second described the various methods in use, giving improvements of his own. Schwarz(5)

Jan 1, 1935

By C. H. Mathewson, A. U. Seybolt

As is well known, many questions affecting the properties and uses of a metal cannot be answered without careful consideration of the state of purity realized in the various operations of preparation, refining, or special treatment that have brought the product to its final state. The occurrellce of an impurity in minute quantity offers no guarantee that its effect will be inconsiderable because dissolved substances often modify the properties of a metal quite out of proportion to their concentration. In such cases the determination of solid solubility must be accepted as a problem of considerable difficulty, requiring the use of especially purified materials and methods not ordinarily used in the metallurgical laboratory. This aspect of the equilibrium between metals and their oxides is especially important and a search for fundamental data reveals little except conflicting opinion even concerning the systems of common occurrence and interest. Rhines and Mathewson1 in 1934 studied the solubility of oxygen in solid copper by annealing to equilibrium in air and gave reasons for the failure of other methods, notably the ordinary procedure of heat-treatment followed by microscopic examination, to yield reliable results. In this paper, a similar study has been made of the solubility of oxygen in cobalt. The simple theory of this method is outlined below. Conditions of Equilibrium between a Metal and Dissolved Oxide at Different Temperatures and Pressures The general conditions of equilibrium in any system are conveniently summarized in a projection of the triple curves of the P, T, X space

Jan 1, 1935

By C. M. Tucker, K. R. Van Horn, W. P. Sykes

Recent investigations of the molybdenum-carbon alloys have been reported by Becker and Ebertl,‡ Westgren and Phragmén2, T. Takei3, and H. Tutiya4. Takei3 studied the Mo-C system by employing metal-lographic and X-ray methods, and the other publications described the determination of the crystal structure of the molybdenum carbides. In exploring this system by a technique previously applied to the tungsten-carbon series5, the results of Takei were confirmed with two definite exceptions; i.e., first the composition of the eutectic, and second the nature of the carbon-rich intermediate phase. Consequently, a more thorough examination of the molybdenum-carbon constitution was initiated in an effort to correlate the data supplied by the microstructures, diffraction patterns and chemical analyses. Metallographic Investigation A briquette of molybdenum powder when heated in a carburizing atmosphere at 1500" to 1600" C. for several hours develops the carbon-rich layer shown in Fig. 1. The carburization was accomplished by placing the briquette in a carbon tube, which was heated in the hydrogen atmosphere of an alundum muffle wound with tungsten resistor. While the macrostructure indicates two distinct shells, and suggests the possibility of two carbon-rich phases, no evidence of this condition could be detected by the microscope, which revealed but one high-carbon constituent. This carbide forms next to the molybdenum as a relatively dense, light-colored zone (Fig. 2) which passes abruptly into an outer layer of spongy texture. As will be noted later, only one intermediate phase was observed in the X-ray photograms prepared of different locations in the carburized zone. The metallographic structure at the inner border of the shell, reproduced in Fig. 3, shows a marked porosity accom-

Jan 1, 1935

By Clair Upthegrove, E. S. Rowland

The widespread interest in the alloys of beryllium with copper is due principally to the fact that certain compositions show very favorable precipitation-hardening characteristics and are, in fact, the stronges nonferrous alloys known at the present time. Investigations have been conducted by Masing and Dahl and others on the physical characteristics of ternary beryllium alloys, in an attempt to produce precipitation hardening effects with a smaller amount of beryllium than that required in the binary copper-beryllium alloys (2.0 to 2.5 per cent Be). The results of these investigations show that ternary alloys of beryllium with Cu-Sn, Cu-A1 and Cu-Zn, among others, exhibit promising improrcmc~nts in physical properties after precipitation-hardening treatment and, while the increases in properties obtained are not as high as those reahzed from the binary copper-beryllium alloys, excellent properties arc obtaincd with beryllium contents averagirlg about one-half the amount reqnired in the binary alloys. This paper presents the results of an investigation of the equilibriun relations of certain alloys containing copper, tin and beryllium. The alpha-phase boundary of the ternary system is given for alloys containing from 0 to 1 per cent beryllium. The equilibrium conditions beyond the alpha-phase boundary are presented for alloys containing up to 32 per cent tin and 1 per cent beryllium. The data were collected by means of quenching experiments, microscopic examination and thermal analysis The results of some powder-method X-ray determiniations on the alloys, conducted by Mr. William Mikulas and Prof. Lars Thomassen at the University of Michigan, are used as evidence in this paper. The con

Jan 1, 1935

By Harry Seltz, J. C. DeHaven

InteRmetallic compounds are formed in many binary metal systems. Some compounds are stable to their melting points, and others decompose at lower transition temperatures. Even those of the first class are dissociated in the liquid state, as indicated by the continuous form of their solubility curves at their melting points1. While the lattice structures of some of these compounds have been determined, their thermodynamic properties have not been investigated. In this paper is described the determination of the free energy and heat of formation of the compound CdSb, which is of the first class mentioned above, melting congruently at 455' C. This compound shows a rhombic structure, and the lengths of the edges of the elementary cell containing four molecules are: a = 6.52, b = 8.60, c = 4.16 A.' There are three possible methods of determining the free energy of formation of a compound of this type. The first method, applying the third law of thermodynamics, requires the measurement of its heat capacity preferably to liquid hydrogen temperatures, and a calorimetric determination of its heat of formation. The second method involves the study of the equilibrium of the compound in some gas reaction, such as: CdSb + CO² = CdO + CO + Sb From the known free energies of formation of CdO, CO² and CO the free energy of formation of CdSb could be calculated. The third method measures the electromotive force of a galvanic cell in which the cell reaction is the reversible formation of the compound from the elements. The first method is generally applicable, but requires elaborate experimental equipment. The second method can not be used for compounds melting at low temperatures, owing to the difficulty in establishing equilibrium. The electromotive force method, therefore, seemed to offer

Jan 1, 1935

By C. S. Smith, E. W. Palmer

For several years an investigation has been in progress in the research laboratory of The American Brass Co. to determine the thermal and electrical conductivities of most copper alloys of commercial importance and several of scientific interest. This paper contains such data on the binary alloys of copper with silicon, aluminum, manganese and nickel, and on a large number of ternary or more complex alloys. Some interesting general relationships between the thermal and electrical conductivities for all copper alloys at all temperatures are pointed out. The data for the copper-zinc, copper-phosphorus and copper-tin binary systems have already been published1,2 † except for the electrical conductivity at 200" C., which is given in the appendix of this paper. Literature on Thermal Conductivity of Copper Alloys The papers referred to above contained a summary of the figures available in 1929 for the thermal conductivity of copper alloys. There is given in Table 1 herewith a selection of the data that have appeared since that time. The measurements of Hanson and Rogers3 are particularly interesting since they cover a series of alloys in the alpha solid solution range and show the effect of heat-treatment. Their alloys were tested as annealed castings, and are not therefore directly comparable to the worked alloys measured in the present investigation, although the difference is small. Bailey's determinations4 were carried out on the alloys used by Lees6 in 1906, and extend his results to higher temperatures. It is most unfortunate that the alloys were not analyzed, for the approximate compositions given are hardly sufficient identification of the material. It is equally to be regretted that neither Hanson and Rogers nor Bailey give data for the electrical conductivities of their samples. Sager6, using the heat-wave method of King, determined the thermal conductivity of copper, nickel and four alloys of the two metals. His results are included in Table 1.

Jan 1, 1935

By L.W. Eastwood, Arthur E. Bousu, C. T. Eddy

The recrystallization and grain-growth phenomena of cold-worked metals have considerable industrial importance because of their role in the fabrication of metals. For this reason, and because of the general academic interest in the subject, these processes have received considerable attention since the time of J. E. Stead's paper1 on The Crystalline Structure of Iron and Steel. There are considerable differences of opinion regarding the theory of recrystallization and grain growth and also differences in the observation of the modus operandi of the processes themselves. The value of many of the existing quantitative data on grain growth is decreased by the failure to distinguish between the grain sizes just after complete recrystallization and those resulting from coalescence. For this reason also, the value of the diagrams of stable grain sizes, like those produced by Bass and Glocker2 and Czochralski3, is lessened in so far as an interpretation of the facts of recrystallization is concerned. It is hoped that the data presentcd in this paper will help to clarify and to simplify the facts relating to recrystallization, and at the same time will show that some of the present-day conceptions are untenable. A paper on the theory of recrystallization, with additional data, will be completed in the near future by the writers. Since the literature on the subject has been adequately and frequently reviewed, the only referenccs to it in this paper will be those necessary in the discussion of the data presented.

Jan 1, 1935

By W. A. Mudge, Paul D. Merica

One of the most prominent features of our present-day industrial development is the ever-increasing demand put upon materials of construction. Engineering ingenuity, within the past 25 years, has been unusually active, and in some fields at least engineers frankly say that engineering design has progressed as far as the limitations imposed by the properties of the present materials of construction will permit. Consequently, they are today demanding improvement in their working materials and seeking new ones, through the aid of which the present limitations of design may be overcome. The activity of this search is evident in all fields, but it is particularly so in that of structural materials required to be resistant to corrosion. The corrosion resistance of metals and alloys is never absolute and all-inclusive; a particular alloy will withstand some corrosive conditions well and fail utterly under others. Furthermore, other properties, physical and mechanical, required in conjunction with corrosion resistance vary considerably for different commercial applications. One wants a soft, ductile sheet metal resistant to atmospheric corrosion; another, a high-strength alloy resistant to sulfuric acid. The last decade has witnessed active and definite progress in the development of high-strength, corrosion-resisting alloys. In June, 1924, a symposium by the American Society for Testing Materials, on Corrosion-resistant, Heat-resistant and Electrical-resistance Alloys, disclosed no less than 60 commercial alloys the properties of which were described as being suitable for industrial service where corrosion resistance was a feature. Today the number of these alloys has been doubled, at least. In addition, economy in design and construction through decreased weight has given considerable impetus to the improvement of alloys of which the mechanical propprties may be improved by heat-treatment.

Jan 1, 1935

By T. E. Kihlgren, N. B. Pilling, E. M. Wise

Systematic data are presented on the relation of composition of nickel silvers to color, tarnish resistance, hardness and liquidus temperatures, for alloys containing up to 30 per cent nickel and 50 per cent zinc, further modified at certain nickel and zinc contents by 0 to 8 per cent of tin and 0 to 10 per cent of lead. Attention has also been directed, using a still more limited range of alloys, toward a study of tensile properties and such casting properties and characteristics as fluidity, shrinkage and pressure tightness. In some of these, rather broad ranges of composition are dealt with; in others, it has been expedient to focus attention on the Federal Specification 20 per cent nickel silver casting alloy, WWP-541. Introduction The demand for an alloy essentially white in color, which could be cast and worked by simple methods and which possessed strength and corrosion-resisting properties superior to the usual brasses, led to the discovery and early use of cupronickel alloys containing zinc, and sometimes tin, lead and other metals. This type of alloy was generally known as 'German silver until the war, when the term "Nickel Silver" became generally accepted. The element principally responsible for the white color of the alloy and for its strength and corrosion resistance is nickel, which may constitute from 8 to 30 per cent of the alloy. The functions of the other elements will be described later. The manifold uses of nickel silver are largely due to its color, corrosion resistance, ease of casting, fabrication, joining and rather moderate cost. In many instances the alloy is finished by grinding and polishing while in others it may be finished with a silver or nickel plus chromium plate. Electroplates applied to a nickel silver base behave more satisfactorily than those applied to the softer and less resistant alloys, and owing to the white color of the underlying metal the article will retain a pleasing appearance despite local failures of the plating.

Jan 1, 1935