METALLURGISTS have been studying the chem-ical behavior of sulfur in steelmaking for many years in order to have a better control of the sulfur content of finished steel. During the refining period in the open hearth, molten steel is separated from a gas phase by molten slag. Chemical reactions occur principally at the slag-metal interface and at the slag-gas interface. A need for physical-chemical investigations of reactions between sulfur-bearing gases and steelmaking slags was recognized some time ago.'.' From the early work, it can be qualitatively concluded that increased sulfur content and low partial pressure of oxygen in the gas phase favor the passage of sulfur from gas to slag. Using radioactive sulfur S Koch and Fink' have demonstrated the rapid rate of exchange of sulfur between gas and slag in an open hearth furnace. Gurry and Darken and Darken and Shields (as reported by Derge and Marshall') have equilibrated lime-iron oxide slags with SO—O2 gas mixtures. The major conclusion from the reported results is that sulfur content increases with increasing lime content in lime-iron oxide slags equilibrated with a gas of high oxygen pressure (10-2). The data were interpreted as indicating the presence of SO, and S,O, ions. Richardson and Fincham' have conducted the most extensive experimental study of sulfur equilibria between gas and slag. Their results confirmed many of the conclusions drawn from calculations of Richardson" and Withers. Richardson and Fincham's data fitted very well into the sulfur scheme represented by the reactions 1/2 s2 (g) + (0) melt - 1/202(g)+ (S) melt [II 1/2 S, (g) + 3/2 O (g) + (0) melt - (SO,) melt. [2] At oxygen pressures greater than 10 to 10 they found that reaction Eq. 2 was predominant while reaction Eq. 1 was controlling at oxygen pressures less than 10." to 10.". The slag compositions and gas mixtures used in their investigations were different from those used in the present study. Wherever possible, comparison has been made between their results and these, and agreement is excellent. It is evident that the distribution of sulfur between slag and gas depends upon the oxygen pressure of the gas. In FeO slags, a change in oxygen pressure produces a change in ferric oxide content, and a knowledge of this equilibrium is a prerequisite to studies of sulfur distribution. The data are found in the work of Darken and Gurry" on the FeO system and the more recent experiments of Gurry and Darken" and of Larson and Chipman" on FeO slags containing lime and silica. The effect of oxygen pressure on the ratio Fe /(Fe" + Fe ), the so-called j-ratio, reported by these investigators will be used in interpreting the results which follow. Experimental Method The purpose of the experimental program was to determine the equilibrium sulfur content in slags exposed to gases of known oxygen and sulfur pres- sures. The slag compositions selected for study were from the lime-silica-iron oxide system. Additions of magnesia were made to some of the slags. Apparatus—The apparatus used by Larson and Chipman was modified slightly to accommodate the addition of SO2 to the gas mixtures. As in their work, slag samples of 0.5 to 2.0 g were held at temperature (lcc) in platinum crucibles under a steady stream of gas, 100 to 200 ml per min, for several hours and then rapidly lowered to the bottom of the furnace where they were quenched in mercury. Preparation and Analysis of Gas Mixtures—Mixtures of SO,-CO were prepared from Virginia Smelting Co. Extra Dry liquid SO, and Pure Co. CO,. After removing traces of water vapor with an-hydrone, the CO, was passed over graphite at 1200°C, at which temperature the conversion to

Jan 1, 1957

By J. Chipman, G. G. Hatch

One of the important functions of the iron blast furnace is the desulphur-ization of pig iron before it enters the steelmaking furnaces. However, the increasing concentrations of sulphur in the metallurgical coke, source of approximately 90 pct of the sulphur present in the blast furnace charge, and demands for higher rates of production within recent years have increased the need for greater desulphurization within the iron blast furnace. Furnace operators are beginning to look for desulphurizing agents other than blast furnace slag to accomplish the desired degree of desulphurization. A considerable amount of work has been done on desulphurization outside the furnace with soda ash, calcium carbide and various synthetic slags. Whether the desulphurization of pig iron is accomplished wholly inside the furnace or partly inside and the remainder outside, will be determined by the economics involved. Regardless of which is the case, it is believed that it is necessary to have a better understanding of the physical chemistry of desulphurization by blast furnace slags. To this end, it is the object of the present investigation to attempt what is believed to be the first equilibrium study of the distribution of sulphur between liquid pig iron and a wide range of blast furnace slag compositions. Review of Literature There is a considerable amount of information in the literature concerning the desulphurizing power of iron blast furnace slags, the solubility of various sulphides in the slags, and the effect on desulphurization of temperature, of elements dissolved in the liquid iron, and of viscosity. However, there is nothing to indicate that the equilibrium distribution of sulphur between liquid iron saturated with carbon and iron blast furnace slags has been studied experimentally. Wentrupl has made probably the most detailed study of the desulphurization of pig iron to date. He considered that there are three distinct aspects involved, namely: 1. Desulphurization within the blast furnace (by lime and manganese). 2. Subsequent desulphurization by manganese. 3. The effect of subsidiary reactions on the desulphurization by manganese. The experimental work carried out by Wentrup was devoted mainly to obtaining a better understanding of how desulphurization by manganese was accomplished in the mixer and the ladle. Particular attention was given to the part played by carbon, silicon, and phosphorus associated with manganese in the iron, and the effect of temperature on desulphurization. The experimental results indicated that desulphurization by manganese is purely a process of crystallization of manganese sulphide. The addition of silicon to iron melts containing 3.5 pct carbon and less than 0.5 pct manganese had no noticeable effect on desulphurization, but with 1-2 pct manganese the silicon additions improved the desulphurization. Additions of phosphorus also resulted in improved desulphurizati011 by manganese, but the effect was not as marked as in the case of silicon. It was also found that desulphurization by manganese was further improved by lowering the temperature. In order to explain desulphurization inside the blast furnace, Wentrup considered the system iron, sulphur, calcium, oxygen, manganese. (silicon). The distribution of sulphur between the metal and slag was represented by the following equation: (SS) _ (S)Fe + (S)Ca + (S)Mn .... [S] = [s] [1] The parentheses and the brackets represent the equilibrium concentrations in weight per cent of the slag and metal constituents, respectively. Since FeS D (FeS) _ (FeS) (S)Fe LfeS - [FeS] [S] [2] (CaO) + S e (FeO) + (S)Ca _ (FeO)(S)Ca. (S)Ca _ (CaO) Kl = (CaO)[S] [S] ~K1(FeO) [3] Mn + S D (S)Mn (S)Mn (S)Mn K' = [MnpT "1ST = *lIMnJ !4) Substitution of Eq 2, 3, and 4 into Eq 1 resulted in if = L- + *> (Sol + K^ (S) [51 Eq 5 was used to calcu1;lte -f^j and [S] at 1480°C for slags containing 30-50 pct lime, 0.1-2.5 pct iron oxide, 0-26 pct silica, 2 pct sulphur and iron analyzing 1.5 pct manganese. The value for LFaB at 1480°C was found to be equal to 4.5, based on the experimental work of Bardenheuer and Geller.2 The results of the calculations are shown in Table 1. Although the slags are hypothetical and do not represent the range of compositions found in ordinary blast furnace practice, the calculations indicate that lime is effective in controlling desulphurization only if the iron oxide and silica contents of the slag are kept low. Schenck3 did not claim K1 to be a true equilibrium constant, but an empirical value which varied with the silica content of the slag.

Jan 1, 1950

By J. Chipman, G. G. Hatch

T. ROSENQVIST*—It is a pleasure to see the excellent way in which the experimental part of this work has been handled. There seems to be little doubt that the distribution data obtained corresponds most closely to thermodynamic equilibrium under the prevailing reducing conditions, namely equilibrium with graphite and one atmosphere CO pressure. The desulphurization curves in Fig 10 show the same general feature as the curves given by Holbrook and Joseph, but the distribution ratios are from 20 to 40 times greater—undoubtedly due to a closer approach to true equilibrium. In the theoretical discussion, the authors calculate a theoretical distribution (S) ration -jg-. which they find to be about 50 times greater than the experimental. The deviation is so great that the basis for their calculation needs a more thorough examination. The authors base their thermodynamic calculation on free energy expressions where diluted solutions of FeS and CaS are used as standard states. (The activity coefficient in diluted solutions is taken to equal unity.) Such a standard state will change when the nature of the solvent is changed. Taking the free energy of the reaction [FeS] ? (FeS), Eq 2, which is derived from the distribution of sulphur between an iron and a FeO-melt, it is very unlikely that the free energy of this reaction will be the same for a distribution between pig iron and a calcium silicate slag. Therefore a more fundamental basis for the thermodyuamic calculations seems needed, where all thermodynamic equations are referred to unambiguously defined standard states. The most natural standard states for CaO and CaS are the pure solid substances at the same temperature. As standard state for sulphur in iron, pure liquid FeS can be used. This rules out Eq 2 [FeS] ;=s (FeS) because ?F° = 0. The standard equation will then be: FeS, + CaO6 + Cgraph ?Fei + CaS8 + CO. vFo1773 = 25,000 cal It would be more universal and also simpler to refer the escaping tendency of sulphur in liquid iron to the corresponding H2S/H2 ratio which can readily be determined experimentally. As standard state a gas mixture H2S/H2 = 1/1 can be used. (This corresponds at the temperature of liquid iron closely to one atmosphere S2 vapor.) Thus the standard equation for the sulphur reaction can be formulated as follows: H2S0 + CaO3 + Cgraph ?H2o + CaS8 + COg The standard free energy of this reaction has been calculated from the best available data to AF°m3 = —35,000 cal. This gives for the equilibrium constant at 1500°C Now, the solubility of CaS in blast furnace slags has been determined by McCafferey and Oesterle* and corresponds at 1500°C to about 10 pet S (varying somewhat with the composition of the slag.) If the activity of CaS is assumed linear between 0-10 pet as curve 1, (see Fig 11), then acaO = 0.1 (S); (S) being wt. pet sulphur in the slag. For a diluted solution of sulphur in an iron melt saturated with carbon, the ratio H2S/H2 is, according to Kitchener, Bockris and Liberman,f about 0.01 [S], [S] being wt. pet sulphur in iron. Substituting these values in the expression for Kp we find The value 2.103 is only 4 times greater than the experimental coefficient found by Hatch and Chipman, but the value is very sensitive to a small error in AF°. A better agreement with the experimental distribution coefficient can be obtained if one assumes the activity of CaS to run like curve 2 (Fig 11). This (S) will give a lower theoretical W, value, a value which varies with (S) exactly as Hatch and Chipman learned. Such a shape of the activity curve, which corresponds to a positive deviation from Raoult's law, is actually to be expected from the fact that liquid silicate and sulphide phases usually show incomplete miscibility. A closer agreement between experimental and theoretical data can not be expected before we have more complete data for the individual activities of CaS and CaO in the slag. The activities acaS and Ocao referred to the solid phases as standard states, are exact defined quantities contrary to the somewhat undefined expression "free lime," and they are independent of any theory for the constitution of liquid slag. J. CHIPMAN (authors' reply)—The authors wish to thank Mr. Rosenqvist for his very interesting and useful thermodynamic addition. Curve 2 of his figure offers the needed basis for explaining the increase in the ratio (S)/[S] with increasing sulphur content. Attention is called to an error in the printed paper: Fig 2 and 3 are reversed. M. TENENBAUM*—In the figures showing the relationship between excess base and sulphur distribution (Fig 6, 7 and 9) the slope of the curve tapers off in the negative basicity range. Somewhat the same thing is observed with open hearth slags. In that case, the fact that some sulphur distribution between slag and metal is obtained with negative basicity is interpreted as indicating some dissociation of the lime silicate compounds whose existence in oxidizing basic slags has been used to explain various observed phenomena with regard to other slag-metal reactions. In the case of the blast furnace slags, the reduced slope of the sulphur distribution curve with decreasing excess base is attributed to the amphoteric effect of alumina. Has the possibility of other explanations been investigated ?

Jan 1, 1950

By R. E. Boni, G. Derge

Application of surface tension measurements has been made to molten silicates in order to determine the effect of sulphur upon the surface tensions of synthetic blast furnace slags. In melts with the same molar ratios of AI2O3 + SiO2 to the basic oxides BaO, CaO, and MgO, the surface tensions increase in the order of oxides listed. Sulphur lowers the surface tensions of the basic BaO, basic CaO, acid BaO, acid CaO, and acid MgO slags in that order; and the concentration of excess sulphur at the slag surface increases in this same order of slags. The rate and amount of desulphurization of iron by these slags is favored by a low excess surface sulphur in the slag. IN a previous paper,1 the authors discussed the applications of surface tension measurements of molten silicates to problems of metallurgical interest. Of major importance is the aid that such studies lend to forming a working concept of slag structure. Since the ability of a slag to desulphurize metal depends strongly upon its composition,2"4 fundamental information about the structural differences between various slags which contain sulphur should aid the development of better desulphurizing media. For that reason, the present investigation concerns the effect of sulphur upon the surface tensions of synthetic blast furnace slags. Experimental Procedure , The maximum bubble-pressure method was used to measure the surface tensions of synthetic blast furnace slags in the temperature range 1300° to 1600°C. The method is based upon the equation which was developed by Schrödinger5 from a consideration of the forces of hydrostatic pressure and surface tension of a liquid which oppose bubble formation when a gas is forced through a tube immersed in the liquid. where y is the surface tension between argon and slag in dynes per centimeter; g is the gravitational constant, centimeters per second2; H is the manometer reading in centimeters; s2 is the density of manometer fluid in grams per cubic centimeter; S1 is the density of the medium in grams per cubic

Jan 1, 1957

By T. J. Whalen, S. M. Kaufman

Surface-tension measurements for liquid Fe-C-Co and Fe-C-Ni alloys were performed by the sesszle-drop technique at 1350o and 1425°C. Cobalt was shown to he more effective than nickel in lowering the surface tension of Fe-C alloys A minimum value for surface tension of 1640 dynes per cm was found in the Fe-C-Co system at a concentration of 1.5 pet C and 12pet Co. Analysis of these measurements in terms of adsorption and desorption behavior indicated that cobalt and nickel lower surface tension in Fe-C alloys by replacing carbon at the liquid-vapor interface. Comparison of results to date for Fe-C liquid alloys has shown that most substitutional-type elements having about the same atomic diameter as iron also have relatively the same influence on surface tension when present in dilute amounts. It has been shown previously that surface-adsorption behavior in liquid Fe-C ternary alloys is related to the manner in which the ternary addition affects the activity of carbon in the bulk solution.' Certain ternary additions, such as chromium, tending to decrease carbon activity cause adsorption of carbon and chromium to the liquid-vapor interface. Additions, such as silicon, increase the carbon activity, resulting in a desorption of carbon and an adsorption of silicon. Both cases were shown to cause a decrease in surface tension due to adsorption. It is the object of this paper, as part of the writers' continuing interest in the effect of alloying additions on the surface tension of Fe-C alloys, to present and discuss surface-tension data on solutions in the ternary systems Fe-C-Co and Fe-C-Ni. Available activity measurements for these systems in the solid state indicate a strong increase in carbon activity when either nickel or cobalt is added to Fe-C alloys.2, 3 EXPERIMENTAL PROCEDURE The alloy compositions used are shown in Table I. These alloys were prepared by vacuum melting in stabilized zirconia crucibles and then vacuum casting into cold-steel molds. The nominal analyses for the alloys used in this investigation are given in Table I. Surface tensions and densities were measured by the sessile-drop method4,5 in conjunction with the tables of Bashforth and bdams.' Specimens were prepared by slicing 1/4-in. cubes from the center of the vacuum-cast ingots and grinding the edges of these cubes until their shapes approximated spheres with flat bottoms. Proper handling techniques, including an acetone rinse immediately before use, assured minimum contamination from sources extraneous to the actual melting. For each experimental run a sample was placed on a BeO plaque and positioned and leveled inside a vacuum induction heating apparatus. The sample and plaque arrangement sat inside a molybdenum tube which acted as the susceptor. Diagrams of this apparatus may be found in the literature.= After heating to temperatures just above the liquidus at pressures of the order of 10-4 to 10- 5 mm Hg, photographs of the drop profile were made using its natural thermal radiation as a light source. Some measurements were made with partial pressures (-1 cm Hg) of a mixture of H2 and He gases. The H2-He atmospheres proved to be necessary at higher nickel contents to retard excessive vaporization losses. Chemical analysis for carbon and the ternary addition was performed for each alloy sample after completion of the experimental run.

Jan 1, 1964

By E. N. Silverman

Mixtures of' MnS, ZFeO-SiO,, ZMnO.SiO, FeO, and MnO were prepared synthetically and used to study the planes ZFeO. Si0,-ZMnO.SiO,-MnS, FeO-MnO-MnS, and Fe0-MnO.Si0,-MnS in the quaternary system. Because the oxides and silicates studied flux MnS, inclusions in this system are partly liquid during rolling. Also, oxygen can modify subsurface inclusions through the reaction MnS + FeO—FeS + MnO during the soaking of ingots and the reheating of blooms and billets. NONMETALLIC inclusions in steel have long been a subject of study and conjecture because the properties of many steels are known to be affected by the the kind and amount of inclusions present. In free-machining steels, the type of inclusion present has a direct bearing on their machinability; in other steels, cleanliness is important and metallurgists direct their efforts at reducing the amount of non-metallic inclusions. Thus, the accumulation of knowledge about the formation and behavior of inclusions during all stages of steelmaking and processing should aid in improving the quality of steels and decreasing the production costs resulting from rejections. Previous studies of inclusions have contributed greatly to our understanding. The investigators have generally examined inclusions in finished steel. Boulger, Moorehead, and Garvey1 found that in Bessemer steels, low silicon contents results in globular sulfide inclusions with attendant high machin- ability ratings. Van vlack2 also found that low silicon contents favor inclusion morphology that contributes to high machinability ratings. Boquist and Stoll* found that silicon content affected sulfide inclusions and machinability of blooms, billets and bars more than did the finishing temperature in the range between 1775° and 2075°F. Carney and Rudolphy3 studied the distribution of sulfur, manganese, silicon, and carbon in a commercial ingot of resulfur-ized steel and found that silicon was concentrated near the bottom. This helped to explain why bottom cuts had poorer machinability. Klinger and Koch4 developed techniques for extracting inclusions from steel, and the technique devised by Gurry, Chris-takos, and stricker5 for extracting carbides can also be adapted to the study of inclusions. A different approach to the study of inclusions in steel consists of synthesizing the constituents that form inclusions and determining the phase eauilibria in the system that contains the constituents. The resulting phase diagrams can then be used to determine the effect of the various constituents upon each other. In this way, it becomes possible to under-

Jan 1, 1962

By S. L. Payne, J. P. Morris, R. L. Kipp, G. R. Zellars

The activities of iron and nickel in liquid Fe-Ni alloys were determined by measuring the vapor pressures of iron and nickel above the alloys and comparing with the vapor pressures of the pure metals. Nickel was found to deviate negatively from Raoult's law over the entire composition range. Iron behaves ideally down to 0.7 mole fraction but shows negative deviations at lower concentrations. At 1600°C the activity coefficients at infinite dilution are 0.40 for iron and 0.66 for nickel. 1 HE formulation of the conditions of chemical equilibrium between liquid metals and gases or slags is an important application of thermodynamics to pro- cess metallurgy. Usually the metal and slag phases are solutions of several components; and for accurate calculations, it is often necessary to use the activities of the components in place of their concentrations. Data concerning activities, however, are quite meager. The evaluation of the activities of iron and nickel, presented in this paper, is part of a project to determine activities in iron alloys at elevated temperatures.

Jan 1, 1960

By N. A. Gokcen, E. S. Tankins, G. R. Belton

Equilibrium in the reaction H2(g) + O[in liquid iron, cobalt, or nickel] = H2O(g) has been investigated over wide temperature and composition ranges. Oxygen has been found to obey Henry's Law in each of the three metals at 1550°C. The standard free-energy changes for the above reaction are given by: (1550° to 1700°C) ?Foco = -45,360(±290) + 16.16(±0.16)T (1490° to 1700°C) ?Fo Ni = -48,170(±220) + 16.12(±0.12)T (1465° to 1700°C) where the standard state for dissolved oxygen is the I wt pet solution. ThE thermodynamic behavior of dilute solutions of oxygen in molten iron has been the subject of many investigations over the last thirty years,'-'4 the majority of the investigators having utilized the reaction:

Jan 1, 1964

By Robert Baschwitz, John Chipman

The distribution of silicon between liquid silver and Fe-Si-C alloys has been studied at 1420oand 1530°C. The data are consistent with earlier studies. New data of Hager on the liquidus lines of the system Ag-Si and the distribution data are used to obtain the activity coefficient of silicon in both liquid phases. Data on the heat of mixing in iron permit accurate extension to 1600°C. Equilibrium data involving SiO2 and silicon in liquid iron together with revised data on the free energy of SiO2 are used to fix the activity of silicon in the infinitely dilute solution. The binary system exhibits strong negative deviation from ideality. At infinite dilution ? Si at 1600" is 1.25 x 10'3, and at concentrations up to NSi = 0.4 the slope d InySi/dNSi has a constant value of r; = 13. It is found that logysi in the ternary solutzon is approximately but not exactly the same function of Nsi + NC as of NSi in the binary. The results are consistent with currently available data on the free energy of Sic and its solubility in molten iron. LIQUID solutions of the system Fe-Si-C have acquired considerable importance as the laboratory prototypes of blast furnace hot metal. Equilibrium studies involving such solutions and slags approximating those of the blast furnace have yielded useful information concerning the thermodynamic properties of blast furnace slags. In studies of this kind great importance attaches to a knowledge of the thermodynamic activity of silicon in the solution as a function of temperature and composition. An attempt was made by Chipman, Fulton, Gokcen, and askey' to evaluate all of the pertinent data on this system and to deduce the desired relation between activity, composition, and temperature. These authors published data on the solubility of graphite and Sic in molten Fe-C-Si solutions and on the distribution of silicon between liquid iron and liquid silver. They showed further how the activity of silicon in very dilute solutions in liquid iron could be calculated from equilibrium data involving the molten alloy and solid SiO,. These calculations rested on the published thermodynamic properties of SiO, in- cluding its heat of formation which at that time was recorded as -209.8 kcal. This value has been under suspicion for some time and has recently been replaced by the concordant results from two independent laboratories2,3 which place the heat of formation of a-quartz at -217.6 kcal. This revision necessitates a re-evaluation not only of the activity of SiO2 in slag but also of silicon in molten iron. It is the purpose of this paper, therefore, to recalculate the activity of silicon, and in furtherance of this objective to present new data on its distribution between liquid Fe-Si-C alloys and liquid silver. HEAT OF SOLUTION OF SILICON IN IRON In order to determine the effect of temperature upon the activity coefficient it is necessary to know the heat of solution of silicon in iron as a function of composition. This is found in the data of Korber and Oelsen4 shown in Fig. 1. The curve corresponds to the following equation, which is of a form suggested by Wagner:5 Here AH is the heat absorbed in kilocalories in forming one gram atom of molten alloy from its molten elements and the N's are atom fractions. The relative partial molal enthalpies of the components, each referred to its pureliquid state and defined as zFe = aFe - PFe and zsi = HSi — -psi, are shown graphically. At low concentrations zSi = -28.5 kcal, in agreement with Kijrber and Oelsen's computation. This is in good agreement with the value of -29.3 kcal obtained by Chipman and Grant6 using an entirely different method. ACTIVITY AT INFINITE DILUTION From the known free energy of SiO, it is possible to obtain the activity of silicon in dilute solution in liquid iron from equilibrium studies. The heat of formation of a-quartz is —217.6 kcal and the heat capacity and entropy data are given by Kelley and ~ing.' The free energy of formation of ß-cristo-balite at temperatures above the melting point of silicon is expressed by the following equation: Si(Z) + O2(g) = SiO2 (crist); AF" =-226,500 + 47.50T [I] The value of the deoxidation product for silicon [%Si] x [%O]2 at 1600°C according to Gokcen and chipmans is 2.8 x 10"5, in agreement with results of Hilty and Crafts.9 More recent works of Matoba,

Jan 1, 1963

By E. M. Cox, T. Rosenqvist

IN a recent investigation, carried out at the Institute for the Study of Metals, the affinity of sul-phur for iron, copper, and manganese was studied over the temperature range 700" to 1300°C.' It was found that copper exhibits a rather high affinity for sulphur, especially at higher temperatures; and attention was called to the possibility that copper when present together with sulphur in liquid steel would tend to lower the chemical activity of sulphur and thus interfere with the desulphurization process. It was clear, however, that the data for the equilibrium between pure copper and pure copper sulphide (Cu2S) could not give any quantitative information about the effect of copper when dissolved in liquid steel. The present work is concerned with the activity of sulphur in the diluted range of the binary iron-sulphur system, and with the influence of small amounts of copper on this sulphur activity. This investigation is in principle based on the same method previously described for the binary metal-sulphur studies;1,2 namely, reaction with hydrogen to form hydrogen sulphide. The equilibrium ratio PH2s/Ph2 in the equilibrium gas mixture is, for a given temperature, directly proportional to the sulphur activity. The activity of sulphur in liquid iron has previously been studied by Chipman and Ta Li,3 White and Skelly,4 and recently by Sherman, Elvander, and Chipman.5 Morris and Williams6 have studied the effect of added silicon, and Kitchener, Bockris and Liberman,7 and recently Morris and Buehl,8 the effect of added carbon on the sulphur activity. In present day steelmaking processes the steel bath contains between 0.01 and 0.1 pct sulphur, and the copper content may be as high as 0.5 pct. The equi-librium gas ratio (H2S/H2) would, for such a low-sulphur content, be too low to be measured with the experimental technique we use. It has been shown by previous investigators that the H2S/H2 ratio is closely proportional to the sulphur content up to about 1 pct sulphur. The sulphur activity at very low-sulphur content can therefore be calculated by linear interpolation between 0 and 1 pct sulphur. In order to show the general trend with increasing sulphur content, the present work has been carried out to about 3.5 pct sulphur. As the effect of copper was assumed to be more a function of the Cu/S ratio than of the absolute copper content, the runs with copper were made for certain constant values for this ratio.

Jan 1, 1951

By Donald B. Evans, Robert D. Pehlke

The solubility of nitrogen in liquid Fe-A1 alloys has been measured up to the solubility limit for formation of aluminum nitride using the Sieverts method. The activity coefficient of nitrogen decreases slightly with increasing aluminum content in the range of 0 to 4 wt pct Al. Based on a nitride composition, AlN, the standard free energy of formation of aluminum nitride from fhe elements dissolved in liquid iron has been determined to be: ?F" = -59,250 + 25.55 T in the range from 1600º to 1750ºC. The solubility of nitrogen in liquid iron alloys and the interaction of nitrogen with dissolved alloying elements in liquid iron have been the subject of a number of research investigations.' Most of this work, however, has been reported for concentrations well below those necessary for the formation of the alloy nitride phase. Data in the concentration region near the solubility limit of the alloy nitride, particularly for systems exhibiting stable nitrides, are important in evaluating the denitrifying power of various alloying elements. They are also useful in determining the stability of a given nitride if it is to be used as a refractory to contain liquid iron alloys. In view of the importance of aluminum as a deoxidizing agent in commercial steelmaking and the fact that its nitride, AIN, is a highly stable compound and has merited some consideration as an industrial refractory, the following investigation was undertaken. The use of the Sieverts technique provided a measurement of the equilibrium nitrogen solubility in liquid Fe-A1 alloys as a function of nitrogen gas pressure up to 3.85 wt pct A1 in the temperature range of 1600º to 1750°C. The values obtained by the Sieverts method were checked by means of a quenching method in which liquid iron was equilibrated with an A1N crucible under a known partial pressure of nitrogen gas, and the solubility of A1N in liquid iron determined by chemical analysis. EXPERIMENTAL PROCEDURE The theoretical considerations involved in determining the solubility product of a solid alloy nitride phase in liquid iron by measuring the point of departure of the nitrogen gas solubility from Sieverts law have been discussed by Rao and par lee.' The principal problem is to determine the variation of nitrogen solubility in an alloy as a function of the pressure of nitrogen gas over it with sufficient precision to establish the break point in the curve at the solubility limit of the alloy nitride phase. A fairly large number of data points are required to do this. A second problem is the determination of the composition of the precipitated solid nitride phase. This is necessary in order to define completely the thermodynamic relationships. The Sieverts apparatus used to make the nitrogen solubility measurements in this investigation is of essentially the same design as that described by Pehlke and E1liott.l The charge materials were Ferrovac-E high purity iron supplied by Crucible Steel Co. and 99.99+ pct pure aluminum. Recrystal-lized alumina crucibles were used, and were not attacked by the liquid alloys. The hot volume of the system which was measured for each melt ranged from 46 to 50 standard cu cm and was found to decrease linearly with decreasing pressure and with increasing temperature. The temperature coefficient of the hot volume at 1 atm pressure of argon gas was essentially constant for all experiments at a value of -6 X 10-3 cu cm per "C. The melt temperature was measured with a Leeds and Northrup disappearing filament type optical pyrometer sighted vertically downward on the center of the melt surface. The temperature scale was calibrated against the observed melting point of pure iron taken as 1536°C. The emissivity of all melts was assumed to be that of pure iron, taken as 0.43. The charge weights ranged from 110 to 140 g and the range of aluminum contents covered was from 0 to 3.85 wt pct. Aluminum additions were made as 12 to 15 wt pct A1-Fe master alloys previously prepared in the system under purified argon. The compositions of the master alloys were checked by chemical analysis and found to be in agreement with the charge analyses. Vertical cross sections of the master-alloy ingots were used as charge material for the equilibrations in order to minimize the effect of any segregation which might have occurred during solidification of the master alloys. Determinations of the solubility product of

Jan 1, 1964

By M. L. Pearce

A comparison of the isotope-dilution, vacuum-fusion, and chemical methods of analysis for nitrogen in Si-Fe is made with particular emphasis on the effect of sample history. The superiority of the isotope-dilution method from the point of view of 1 HE analytical techniques used to determine nitrogen in Si-Fe have been subjected to close scrutiny in recent years primarily because of the marked influence of the element on the properties of the alloy. These investigations have led to a diversity of opin- both precision and accuracy is demonstrated. The solubility of nitrogen in 3.06 pct Si-Fe is investigated and the effect of silicon content on the activity coefficient of nitrogen is derived. ion regarding the reliability of the vacuum-fusion and chemical methods of nitrogen analysis when applied to si- Fe.'-' A majority of workers appear to favor the vacuum-fusion method over chemical methods particularly in those cases where part of the nitrogen may exist as silicon nitride or the total nitrogen content is very low. Contrary views have been expressed, however,' and it has been demonstrated that for some Si-Fe alloys both methods yield results which are significantly lower than those

Jan 1, 1963

By J. M. Toguri, H. Flood

The application of the mass action law to the thermodynamic treatment of metal-slag equilibria is discussed. The consideration of the reactions essentially as ionic exchange equilibria is shown to be both an advantage and an aid for the elucidation of the theoretical treatment. This is illustrated by several examples. In general two different methods of application of the mass action law to metal-slag equilibria have been used by different groups of investigators. These could be called the oxide reaction and the ionic reaction approach respectively. At the recent discussion in the metallurgical section of the I.U.P.A.C. Congress in Montreal, 1961,' divergent opinions prevailed regarding the most rational way of applying the mass action law to metal-slag equilibria. This question is of fundamental importance in the treatment and understanding of theoretical chemical metallurgy. Consequently, the following is an attempt to contribute towards its clarification. As an example, the distribution of iron and manganese between molten iron and slag will be considered. I) THE OXIDE EXCHANGE REACTION APPROACH The equilibrium between iron and manganese between molten iron and slag is frequently formulated as an oxide metal exchange reaction as follows:

Jan 1, 1963

By M. G. Benz, J. F. Elliott

Otto Schaaber (Institut für Harterei-Technik, Bremen -Schönebeck, Germany)— Langenberg, Pestel, and Honeycutt gave an interesting example of the grain refining effect nonstationary magnetic fields may execute on a solidifying metal. Probably some additional comments, based on more than a decade of experience with this method of influencing crystallization, may be useful. They refer to an attempt to explain the mechanism of grain refinement by such fields, and to recent European developments which have not been mentioned in the paper. I. During studies of the temperature distribution in a metal body near the phase boundary solid/liquid, an anomaly was observed under certain special conditions: a) direction of heat transfer as horizontal as possible, b) steady state (equilibrium, i.e,, solidification resp. melting rate exactly zero). In the liquid phase, immediately adjacent to the phase boundary, the temperature was found to be constant over an appreciable distance in spite of a high value of heat transfer (40.000 to 70.000 keal/ m2h).3 Convection, which might explain this phenomenon, could not be observed. Therefore another explanation had to be sought. The assumption that a metallic melt, especially at temperatures near the point of solidification, contains some sort of atomic arrangement with a higher degree of order than the surrounding liquid, now is generally accepted. Considering the differences in energy between such an arrangement and its environs, a transport of heat even in absence of any temperature gradient is conceivable by continued formation and redissolution of regions with a higher degree of order, i.e., with lower energy level.3 At this stage, it was not necessary to postulate any special condition as to the form or size of these regions or the distance between arrangements to be newly formed and those to be redissolved. However, a simple consideration shows that an energy transfer from one region to another will only be possible without loss of energy, if the distance between will be equal to the lattice parameters, and if, secondly, crystallographic axis or planes will be parallel.4 By the way, this assumption might give a reasonable explanation of the well known orientation effect of the heat flow during solidification. Any measures to prevent columnar crystallization should act upon this ordering mechanism: a) the regions with a lower energy (higher order) should not be allowed to arrange themselves parallel to the direction of heat flow, and their growth should be disturbed; b) all conditions leading to an appreciable heat flow of uniform direction should be avoided or removed. Condition a) may be satisfied by a physical force preferably under 90 deg to the main axis of the columnar crystals (i.e., parallel to the solidification front) acting on the ordered regions; condition b) by equalizing any differences in

Jan 1, 1962

By Donald B. Evans, Robert D. Pehlke

The solubility of nitrogen in liquid Fe-B alloys has been measured up to the solubility limit for the formation of boron nitride. The activity coefficient of nitrogen increases with increasing boron content in the range 0 to 7 wt pct B. From experimen -tal data, values have been calculated for the B-N interaction parameter e3 at temperatures in the range 1550" to 1750°C. A value of 0.038 has been estimated for the boron self-interaction parameter eg at 1550°C. The standard free energy of decomposition of boron nitride into the elements dissolved in liquid iron has been determined to be: ?F° = 45,900 -21.25T in the range from 1550° to 1750°C. The nitride is assumed to be of composition BN. BORON nitride has an unusual combination of properties which make it appear attractive in a wide range of engineering applications. Some of its more important and most recent applications are in the nuclear area, particularly in connection with the liquid-metal cooled reactor concept now receiving considerable emphasis. Boron nitride has a high degree of stability at elevated temperatures. It also has excellent ma-chinability and the ease with which its crystals deform suggests applications as a lubricant. These properties stem from a hexagonal layer-type structure similar to the structure of graphite. One of its primary uses to date has been for seals in liquid-metal pumping systems. It is also used in nuclear reactors as an insulating layer to separate two solid metals which are not themselves compatible under the conditions of temperature and atmosphere in which they are used. Its inertness to liquid metals has also suggested use as a mold-release agent in casting processes. In addition to its excellent machinability and reported inertness to liquid metals such as iron, silicon, aluminum, copper, and zinc, boron nitride has high thermal conductivity and excellent thermal shock resistance. This combination of properties would make it appear ideal as a refractory crucible material for refining of high-purity liquid metals, for example high-quality steels. However, since it is known that concentrations of boron as low as 50 ppm can have a marked effect on the physical properties of certain steels,' in particular on the creep and stress-rupture properties, an investigation was undertaken to define accurately the chemical equilibrium among boron, nitrogen, and liquid iron in the range of steelmaking temperatures. EXPERIMENTAL PROCEDURE Two experimental approaches to this problem were employed: a Sieverts' method and a quenching method. In the first method, the Sieverts' technique was used to measure the equilibrium nitrogen solubility in liquid Fe-B alloys of 0 to 7 pct B as a function of nitrogen gas pressure over the melt. The solubility limit of the boron nitride phase formed was determined by the point of departure of the nitrogen absorption from Sieverts' Law. This technique has been applied to liquid Fe-Ti alloys by Rao and parlee,' to liquid Fe-A1 alloys by Evans and Pehlke,3 and to solid Fe-V alloys by Fountain and Chipman.4 In the second method a melt of liquid iron was held in a crucible of boron nitride under a known partial pressure of nitrogen gas. After thermodynamic equilibrium was attained, the melt was quenched in a stream of helium and then analyzed by wet-chemical methods for boron and nitrogen. The Sieverts' apparatus used in the first method was essentially of the same design as the one described by Pehlke and Elliott.5 The charge materials were vacuum-melted high-purity iron (Ferro-vac E) supplied by the Crucible Steel Co. and -325 mesh boron powder supplied by Cooper Metallurgical Associates of Cleveland, Ohio. The boron contained less than 0.02 wt pct O, according to supplier's analysis. Recrystallized alumina crucibles were used to contain the melt. Examination of solidified melts showed these crucibles to be satisfactory with no evidence of any reaction or physical penetration of the crucible wall by the melt. The melt temperature was measured by a disappearing filament-type optical pyrometer sighted vertically downward on the melt surface through a 1/4-in.-diam sight hole in the crucible lid. The pyrometer was calibrated against the melting point of pure iron in the same apparatus, taking the emissivity of

Jan 1, 1964

By Tasuku Fuwa, John Chipman

Equilibrium data on the reactions of gases with carbon and oxygen dissolved in liquid iron are reviewed and correlated. A source of error in oxygen analysis of graphitic samples is exposed. New experimental data on the oxygen content of high -carbon iron in equilibrium with carbon monoxide indicate that the activity coefficient of oxygen is decreased by additions of carbon. The carbon-oxygen product decreases slightly with increasing carbon content. In recent years a number of investigations have been reported dealing with the equilibria between carbon and oxygen in liquid iron and gases containing carbon oxides. The laboratory study of these reactions dates back to 1931 with the publication of a paper by Vacher and Hamilton' on "The Carbon-Oxygen Equilibrium in Liquid Iron". The principal object of this study was to obtain data on the reaction shown by Eq. [3] below; their data and others by vacherZ permit evaluation of the other equilibrium constants as well. Subsequent studies have been reported by Matoba, Phragmen and Kalling and by Marshall and Chipman.5 The equilibria may be expressed by the following three equations: C + CO,= 2CO;Kl = Pc° [1] 0-+CO = CO,;K2=-P co, "0.PCO c + O = CO; K3 = In the equilibrium constants, ac and a0 are taken as equal to [% C] and [% 0] respectively in the infinitely dilute solution. At finite concentrations an activity coefficient is introduced such that ac =fc [%C], and so forth. It is to be noted that these equations represent only two independent relations, the third being derivable from any two. Richardson and Dennis have determined the conditions of equilibrium in reaction [I] at temperatures of 1560" to 1760°C. Their results have been confirmed by Rist and chipman7 who have shown how the data may be extended to cover the entire range of liquid compositions at temperatures from the eutectic up to 1760°C. An approximate confirmation has been reported by Fuwa and chipman.' These investigations also established the activity coefficient of carbon which was shown to increase rather rapidly with increasing concentration. For the very dilute solutions the value of Kl is expressed in the equation: log^i = - 7280/T+ 6.65 This equation leads to a value of Kl = 430 at 1540° C in excellent agreement with the average value of Marshall and Chipman.5 It is shown as line 1 in Fig. 1 together with the experimental observations. In the case of reaction [2] the direct experimental results can be supplemented by observations on the corresponding reaction with hydrogen, namely reaction [4]:

Jan 1, 1961

By G. W. Healy, J. C. Schottmiller

Molten silicates were found to exist in the Cr-Si-0 system at temperatures above 1450°C. one atom of oxygen is readily removed from CrzOs in the presence of Si02 at 1700°C, forming a silicate melt. Steam-hydrogen ratio measurements made at this temperature indicate that the free energy of the reaction: Cr20s(c) + Hz = 2CrO (in Si02 -saturated melt) + H20 is approximately 5600 * 1500 cal. A deep-blue chromous silicate, probably Cr2Si04, forms from these melts at about 1400" to 1500°C, and is characterized by.its distinctive X-ray diffraction pattern and optical properties—distinct pleochroism and high refractive indices. THE question of the state of oxidation of chromium in slags has vexed metallurgists for many years The experiments of Koerber and Oelsenl suggested the probable presence of divalent chromium in silica-saturated slags equilibrated with high-chromium melts. Hilty and coworkers2 had also found chromium at lower valency, as Cr304, in inclusions formed from oxygen-saturated Fe-Cr melts with as little as 10 pct Cr. In both cases, disproportiona-tion of the lower oxide to CraO3 and chromium was found to occur to a greater or lesser extent, depending upon the rate of cooling from the high temperature. The work on Cr304 was sufficiently detailed for chipmans to derive its thermodynamic properties, but Oelsen's experiments in the silicate system were not extensive enough since most of his runs were made with slags containing large amounts of manganese oxide in addition to iron and chrome oxide and silica. The present study describes experiments carried out to map out an approximate liquidus diagram in the CrzOs, "CrO", SiOa portion of the Cr-Si-0 system, and to measure the partial free energy of solution of oxygen in the system. EXPERIMENTAL 1) Approximate Melting-Point Determinations. Preliminary trials showed that when an equimolar mixture of Cr20s and SiOa was treated with hydrogen in the temperature range 1500" to 1600°C, copious amounts of steam were evolved, and a low-melting liquid formed which could be quenched to a blue, crystalline, material having a distinctive X-ray diffraction pattern. It was found that the identical material could be produced by heating intimately mixed, finely divided Cra03, Cr, and SiOa, held in a tungsten crucible, under purified argon. Thus, it was possible to prepare mixtures containing any desired proportions of chromium, silicon, and oxygen, pel-letize them, heat to temperature in the furnace shown in Fig. 1, and observe, after cooling, whether the pellet remained unchanged or showed signs of incipient, partial, or complete melting. 2) Free Energy of Solution of Oxygen. This was studied by measurement of steam-hydrogen ratios for the reaction: H20 (gas) + O (dissolved in charge) + Ha (gas) The experimental method chosen was to prepare a

Jan 1, 1964

By Michel Elle, John Chipman

The equilibrium of gaseous H20-H2 mixtures with liquid iron-columbium alloys in the range 0.2 to 2.4 pct Cb shows that the activity coefficient of oxygen is strongly diminished by Cb. The oxide in equilibvium with the melt is identified as CbO2. The equi-librium constant at 1600 deg C is [%Cb][fo. % 0]2 = 2.9 x 10-4 where log fo= —0.14 [%Cb]. The deoxidizing power is comparable to that of vanadium, COLUMBIUM (niobium) is finding increasing use as an alloying element in steel. It forms several stable oxides and is removed from the steel bath by oxidizing slags. The specific oxide formed in steel-making is not known although Sazanov snd Shvarts-man,' in their study of its partition between slag and metal, have assumed this to be Cb2O5 It is the purpose of this study to determine its deoxidation equilibrium at 1600°c, the nature of the oxide formed and the interaction between columbium and oxygen in the melt. The investigation was based on the reaction H2 + O=H2O; Kl=ph2o/(pH2[%O]) [1] in which 0 signifies oxygen dissolved in the liquid Fe-Cb alloy. The method and equipment of recent studies2,3 were utilized. In brief, the molten alloy, contained in a small crucible, is held in a controlled mixture of steam, hydrogen, and argon until equilibrium is reached. It is then cooled quickly in a stream of helium and analyzed for columbium and oxygen, the latter by vacuum fusion.4 The solubility of the oxide in liquid iron is determined by visual observation of scum formation on the surface of the melt. Crucibles of MgO proved unsatisfactory because of partial reduction at the metal interface. Pure A12O3 crucibles were heavily blackened by the melt and could not be used at high concentrations of columbium. Silica crucibles were more satisfactory but these introduced some silicon into the melt thus necessitating an uncertain but small correction for its effect on the activities of the other solutes. In silica it was possible to observe the scum formation when the melt became saturated and there was no apparent reaction between scum and crucible. The procedure for saturated melts was as follows. The alloy charge composed of electrolytic iron and columbium grain was melted and held at constant temperature. The gas ratio H2O:H2 was progressively increased by raising the saturator temperature until a point was reached at which a bright film appeared on the surface and covered it completely. This film could be dissolved by raising the temperature of the melt and it reappeared when the temperature was lowered. Under a partial film covering, utilizing bare areas for temperature measurement, the melt was brought to equilibrium with the atmosphere by holding at temperature for about 1 hr as suggested by Dastur.5 INTERACTION IN THE MELT Several experiments were made without columbium to establish a base in silica crucibles. The results are shown in Table I. Except for one run, they agreed well with Floridis1 comparable results in other crucibles. The value of log K1 is taken from Table I as 0.58. This is slightly larger than Floridis' result, probably because of less elaborate safeguards against thermal diffusion. Results obtained in the Fe-Cb-0 series in which no scum formed are shown in Table 11. The equilibrium ratio Kl is defined as ph2o/(ph2[%O]). It is related to the equilibrium constant K1 as follows:

Jan 1, 1962

By J. A. Cahill, A. D. Kirshenbaum

Using an alumina or zirconia crucible with an alumina sinker or a molybdenum sinker coated with zirconium dioxide, the density of liquid iron was determined by the immersed-sinker method over the temperature range of 1800" to 2500°K. The density, with respect to temperature, is ex-Dressed by the equation Dg/cm = 8.523 - 8.358 X 10 T'K The molar Volumes and thermal coefficients of expansion were calculated. Iron, upon me1ting, was found to expand 3.5 pct. A basic knowledge of the physical properties of materials at high temperatures is becoming increasingly important. A check of the literature shows, that in spite of the importance of iron, very few measurements have been made of its physical properties in the liquid state. Density measurements have been made by Benedicks and his collaborators1g using the method of balanced columns, by Desch and smith4 using the immersed sinker method with an alumina sinker, by Lucas using the maximum bubble method5 and by Stott and endall' who used an alumina pyknometer. In the method of balanced columns, the difference in level of molten iron in two arms of a U-tube, together with the corresponding difference of pressure had to be measured. The formation of gas bubbles in one or both arms was a great source of error. These values are very erratic. They vary from 6.83 to 7.45 g per cm3 at the melting point (1805"~) and from 6.45 to 7.15 g per cm3 at 1890°K. Stott and Rendall determined the density at 1837"K, with a reproducibility of *0.2 pct. They used an alumina pyknometer fired to 1973°K. The vessel was filled in a vacuum furnace by immersion in the liquid metal. When thermal equilibrium was attained, the pyknometer was withdrawn, cooled, the ingot removed and then weighed. The chief disadvantage of the method was the difficulty of inserting the pyknometer without cracking it. The authors have been able to determine the density of liquid iron from its melting point up to 2500°K, by using the immersed-sinker method, with A1203 or ZrOz crucibles and A1203 or molybdenum sinkers coated with Zr02, Fig. 1. EXPERIMENTAL Apparatus. In these studies the source of heat was the carbon tube resistance furnace with an argon atmosphere described previously.7 Experimental runs were made using either Ala3 or ZrOz crucibles. The sinkers used were 1) pure A1a3 and 2) molybdenum coated with ZrOz. The crucible, 2 1/8 in. in diam and 3 in. high, was centered in the furnace on an Ala3 of Zr02 pedestal. The sinker, 1/2 in. in diam and 1 1/2 in. long, together with a counter weight, was suspended from an analytical balance into the melt by a molybdenum wire. Procedure. The procedure, as described previously,' consisted in measuring the weight loss of the sinker in the liquid iron while determining simultaneously the liquid iron temperature by means

Jan 1, 1962

By John Chipman

THE equilibrium between titanium in liquid iron and titanium oxides has been studied by Hadley and Derge.' They have shown that a minimum occurs in the oxygen content of the metal between 0.1 and 1.0 pct Ti, but its exact level was not fixed. The oxide phase in this minimum range was principally TiO, containing some iron oxide. On the other hand, for concentrations above 5 pct Ti the oxide phase was TiO and the oxygen content of the metal increased rapidly with increasing titanium content. From their observations and the free energy of Ti0 and TiOz reported by Kelley and ah,' it is possible to derive approximate values for the activity coefficients of titanium and oxygen in liquid iron-titanium alloys and the conditions for equilibrium in steel deoxidation. Neglecting possible departures from the stoichio-metric composition, the condition of equilibrium with Ti0 may be expressed as follows: TiO= Ti_ + C) log K = log NTl + log [% O] + log yTi + log fQ Here as a matter of convenience the titanium concentration is expressed in mol fraction while that of oxygen is in weight percent. The activity coefficients are yTi and fo. The value of log fo approaches zero as the concentration of titanium approaches zero, while that of log yTi approaches a limiting value of In Fig. 1 the sum of log NTi + log [% 0] is plotted for mol fractions of titanium between 0.05 and 0.50. The smooth extrapolation gives a value of —4.15 which corresponds to log K — log y:i . We therefore have the equation: According to the data of Kelley and Mah,' the free energy of formation of Ti0 at 1900°K is -82,400 cal. The free energy of solution of half a mol of oxygen in iron, taking 1 pct 0 as the standard state, is -29,300 cal. From these we write: From these equations the activity coefficient of titanium at infinite dilution in iron is found to have a value of 0.011 or log y°. = -1.96. This is only an approximate value but is certainly better than the estimated 0.05 in Basic Open Hearth Steelmaking To obtain approximate values for the activity coefficient at intermediate concentrations, it is as- sumed that log yTi(l is constant and equal to -1.96. This corresponds to a value of E;: = 3 In yTi/aNTi = 9.0 which is not unreasonable We now have the value for the activity of titanium and the percentage of oxygen in equilibrium with TiO. It is therefore a simple matter to calculate the activity coefficient of oxygen which is shown in Fig. 2. The effect of titanium is rather large, being comparable to that of vanadium, but not so large as has been reported for aluminum. The slope of the line at low concentrations corresponds to E: = aln yo/ aNTi=-0.37. At concentrations below 1 pct Ti the deoxidation constant and oxygen content for equilibrium with TiO, can be calculated from the foregoing data and the free energy of formation of TiO,, which according to Kelley and Mah is -144,600 cal at 1900°K. The free energy of solution of oxygen has been given; that of Ti to form a dilute solution with 1 pct Ti as the standard state is RT ln (0.5585 y:i/47.9) = -34,800 cal. From these data we find (for concentrations in wt pct): TiO, = Ti + 2 -0; hFTgO0= + 51,200 cal log if =-5.89 The interaction coefficients, concentrations being expressed as wt pct, are e;: = alogfTi/a[% Ti] = +0.048 and e:' = a logfo,/a[ojTi] = -0.187. The calculation gives the following results which, in view of the impurity of the oxide phase, must be regarded as approximate:

Jan 1, 1961