By J. C. Bokros

At temperatures above 950°F, zirconium which has been strained a critical amount will experience critical recrystalli-zation. The large grain size thus formed can result in a reduction in the fatigue life by a factor of 2 to a factor of 9 at both high and low temperatures. The critical strains for zirconium vary from 15 pct at 900°F to about 2 pct at 1125°F, while those for zircaloy III vary from 15 pct at 1050°F to 5 pct at 1200°F. Zircaloy II ,experiences no critical recrystallization up to 1200°F. ZIRCONIUM has become increasingly important for nuclear applications and is being employed in reactors at temperatures where recrystallization can occur. Recent work' on the fatigue properties of zirconium has shown that coarse-grained structures developed in zirconium during recrystallization have much lower fatigue lives than fine-grained material. The development of these large grain sizes under such conditions is well known to be the result of critical recrystallization.2-4 Briefly, critical recrystallization occurs when a metal is strained a critical amount and annealed in the recrystallization range. The critical strain is defined as that minimum strain necessary to promote nucleation in the time unit and temperature considered. The maximum grain size occurs at the critical strain, since at this strain the fewest stable nuclei per unit volume grow into new grains. Recrystallization is not evident below this; strain since the nucleation rate is vanishingly lolw, and metal strained more than the critical amount has a higher nucleation rate per unit volume which results in a finer grained structure. This paper describes the critical recrystallization observed in reactor-grade zirconium, zircaloy 11, and zircaloy I11 as a function of annealing temperature and temperature of strain. EXPERIMENTAL The zirconium used was hafnium-free, double arc-melted sponge obtained from the Bureau of Mines. The ingots were forged and hot reduced to 0.08 to 0.10-in. sheet and subsequently cold reduced to 0.035-in. sheet with intermediate and final anneals at 1200 OF for 15 min. The zircaloy II and zircaloy III used were 0.035-in. sheets in the annealed condition. Compositions of these materials as tested are given in Table I. To determine the critical strain at a given temperature, tensile specimens having a0.065-in. taper in a 2-in. gage length were machined from the sheets parallel to the rolling direction. The specimens were polished, etched, and examined metallographically to ensure that all of them were strain-free, initially. Tukon indentations were made every half millimeter along the gage length of each specimen. These served as fiducial marks enabling the plastic strain to be measured with a microscope and micrometer stage. The specimens were pulled to failure at a rate of 0.002 in. per min in an Instron tensile-testing machine. Three temperatures were used for straining: room temperature, 500 ºF, and 900 ºF. The 500º and 900 ºF tests were run in an argon atmosphere. Since the rate of work hardening changes with temperature, a different critical strain was obtained for each temperature of strain. Specimens, prepared in the manner described, were annealed in vacuunl at various temperatures ranging from 900" to 1200 F for up to 1000 hr, after which they were examined metallographically. The critical strain and the recrystallized grain size as a function of strain were determined for each specimen. Results for the same temperature and time indicated that the critical strain measured was reproducible to within 5 pct of each other. RESULTS AND DISCUSSION Since increasing the time of anneal increases the probability of the nucleation of a new grain, the critical strain decreases with time at a decreasing

Jan 1, 1961

By D. A. Dukelow, K. Li, G. C. Smith

Decarburization in the Fe-C system by oxygen top blowing has been studied in laboratory -scale experiments. It is shown that equilibrium models fail to explain or predict either the course of refining or endpoint conditions, giving results which either are incompatible with the chemistry of the system or do not satisfy material balance requirements. Also the path of decarburization was found to vary even for heats made under apparently identica1 conditions. A promising approach to analyzing the decarburization results is to relate oxygen efficiency fm carbon removal to bath carbon content. This relationship for Fe-C heats shows the same range of oxygen efficiencies as is obtained in pilot-plant and commercial heats using hot metal-scrap charges. This implies that oxygen transfer is primarily controlled by the decarburization reaction itself, independent of other refining reactions. Therefore, it should be possible to study separately decarburization and slag-metal reactions. DECARBURIZATION is probably the most important reaction in steelmaking. Not only is it a main reaction in the refining of iron to steel but it also provides the stirring action in the bath necessary for the diffusion processes to proceed at reasonable rates so as to make a steelmaking process practical. Kinetics of decarburization in the open-hearth process has been a subject of investigation for many years.&apos;-B It is generally accepted that at steelmaking temperatures the rate of homogeneous C-0 reaction is extremely high and cannot constitute a rate-controlling step. Diffusion of oxygen through a boundary film in the metal phase has been suggested by arken&apos; as rate-determining. Recently, Larsen and sordah16 concluded from experiments in a laboratory furnace that, with oxygen supplied from air or combustion gases, the rate of "steady-state" carbon boil is controlled essentially by a diffusion process of O2, Co2, or H2O through a film of nitrogen above the slag surface. Displacing this diffusion film by a stream of nearly pure oxygen produced a ten-fold increase in the rate of carbon boil with the rates of slag-metal oxygen transfer, bubble nucle-ation, and other steps all apparently able to keep pace. In the top-blown basic oxygen process, however, the transport of oxygen takes a more direct route. and the state of bath agitation is much more turbulent than in the open-hearth process. In addition, direct contact of the gas with the metal phase provides opportunity for direct oxidation of carbon. It is likely that the rate-limiting factor for the decarburization reaction will be different. However, only a few descriptive discussions of the subject have been reported in the literature.10-l2 Studies of the decarburization kinetics based on plant or pilot-plant data are necessarily complicated and are influenced by other refining reactions which occur simultaneously. In order to investigate the mechanism of decarburization, experiments have been conducted in which carbon-saturated iron melts were top-blown with pure oxygen over a range of conditions. It is hoped that this study will form a foundation on which a more basic understanding of this important reaction may be built. EXPERIMENTS One group of blowing experiments was made in a standard 200-lb induction furnace and another group in a 500-lb induction furnace. The furnaces were modified to the general shape of a basic oxygen furnace by adding a rammed refractory cone section to the regular crucible body. Crucible and cone were of high MgO (95 pct) material. A water-cooled lance, 1/2 in. in diam and threaded at one end to take a nozzle, was used for blowing oxygen. The lance with its water and oxygen lines was supported on a cantilever arrangement so that it could be moved up, down, or sideways. Oxygen of 99.5 pct purity was supplied from a cylinder and metered through a rotameter equipped with pressure and temperature gages. Another pressure gage was located at the top of the lance. A schematic diagram of the assembly is shown in Fig. 1. Before each experiment, a weighed amount of ingot iron, containing 0.02 pct C, < 0.01 pct Si, 0.10 pct Mn, 0.019 pct P, and 0.015 pct S, was charged in the furnace and melted down by induction heating. Graphite was then added to the molten charge until it became saturated. When the temperature of the charge reached the desired level, the lance was lowered to a predetermined height above the bath

Jan 1, 1964

By S. Y. Ogawa

The effects of sulfur (up to 0.1 pet) on the deformation and fracture characteristics of iron, in cast form, were studied at strain rates up to 100 pct pcr sec and at temperatures of 1600o to -3300 oF. The effects of oxygen and manganese additions on the behavior of Fe-S alloys were studied under comparable test conditions. Brittle fracture characteristics, evident at all strain rates, resulted from the presence of the liquid iron sulfide phase at grain boundaries. Ductility could be restored in three ways: solution of the sulfide in solid y iron at higher temperatures, spheroid-zzation of the liquid sulfide, and increase. in the melting point ot the sulfide. THE literature shows that most previous studies of deformation and fracture at hot working temperatures have been based on measurements of energy absorption, reduction of height in forging upset tests, torsion tests of bar or wire samples, and so forth,&apos; but that relatively few tension tests have been used at high temperatures and strain rates. The present work was initiated to study the ef- fects of temperature, strain rate, composition, and structure on the deformation and fracture characteristics of iron, utilizing cast specimens tested in tension. As in a previous study,&apos; strain rates up to 100 pct per sec were chosen for the temperature range 1600° to 2400° to provide data which might be useful in the interpretation of the deformation and fracture behavior of steels under hot working conditions. The previous work was with Fe-P solid solution al10ys;2 this work is concerned with Fe-S alloys, and with the effects of oxygen and manganese additions. MATERIALS AND PROCEDURE Cast tes! specimens were employed throughout, since most of the difficulty during hot working occurs in the initial breakdown of the ingot. Alloy Systems. Ten 25 lb. heats containing sulphur were prepared. Of these, three had manganese additions, and two had oxygen additions. The sulfur content varied from 0.023 to 0.10 pct. Manganese contents were intended to be ten to twenty times the sulfur content of the particular alloy. Oxygen, being more difficult to control in small melts, was varied by the amount of solid deoxidizer added, but poor control of the oxygen content was experienced in most instances. Table I shows the chemical analyses of the heats. Melting and Casting. Electrolytic-iron chips were melted by high frequency induction in a prefired, clay-graphite crucible lined with rammed magnesite.

Jan 1, 1962

By R. G. Ward, P. L. Sachdev

Using an improved maximum bubble pressure technique, the densities of iron silicates at 1400°C have been measured under nitrogen. At the wiistite composition the density has been measured by bubble-blowing experments with both argon and nitrogen and calculated from the measured volume of a known mass of melt under nitrogen. The densities under nitrogen are significantly different from those measured under argon for melts containing less than 28 wt pct SiO2. THE constitution of liquid slags is not well understood, largely because no single property or parameter can be measured which gives conclusive evi- dence of the types and packing of the ions present. Of the many property measurements which can provide information leading to a picture of the constitution of slags, density gives the most direct evidence and has been studied extensively. The work reported here is part of a program of study of densities in multicomponent melts in which the iron oxide-silica system is the solvent. These melts are important as they are fundamental to basic steelmaking, and they allow the study of basic silicate compositions which have hitherto been largely neglected. As considerable disparity exists

Jan 1, 1965

By John Henderson

Densities of melts 0f the lime-iron oxide-silica system in contact with solid iron have been measured by the maximum bubble pressure method in the temperature range 1250° to 1440°C and the composition range 0 to 40 mol pct lime, 15 to 100 mol pct iron oxide, and 0 to 55 mol pct silica. Densities range from 4.65 g cm 3 for wustite at 1440°C to 2.75 g cm-&apos; at 1350°C for a melt containing 30 mol pct lime, 20 mol pct iron oxide, and 50 mol pct silica. The results are interpreted in terms of a postulate that the melts can be regarded as a random array of oxygen ions in which regions of local order exist to satisfy the coordination requirements 0.f the cations. An understanding of the nature of metallurgical slags is basic to the development of a sound theoretical description of heavy metallurgical extractive and refining processes. Because these liquids are complex, direct measurements of their properties has not thrown much light on their structure. This has led to the approach of measuring the properties of simpler liquids, and building up their complexity until slag compositions are reached. In this way the density of liquid iron silicates was measured in a previous study1 and the present work represents a further stage in this synthesis. EXPERIMENTAL The technique used in the measurement of density was the maximum bubble pressure method. Details of the apparatus and procedure were similar to those previously reported,&apos; with the exception that a constant voltage transformer was used to supply the power input to the furnace and six silicon carbide resistance elements were used in place of the molybdenum winding. With these modifications melt temperature could be maintained within 1 centigrade degree during the course of a run. The silica used to prepare the melts was washed natural quartz ignited at 1000°C; wustite was prepared by air-melting A.R. grade ferric oxide in an iron crucible and lime was prepared by air ignition, at 1000°C, of weighed quantities of A.R. grade calcium carbonate, previously air-dried at 110°C. The finely ground constituents were intimately mixed in a glass ball mill prior to melting. Temperatures quoted are accurate to * 5°C and the standard deviation of the density values, calculated by the method of least squares, ranged from 0.5 to 1.8 pet. However, replicate determinations of density on different melts of the same nominal composition at the same nominal temperature did not vary by more than 1 pct, Table I, and this figure has been taken as an estimate of the accuracy of the density results. The density of carbon tetra-chloride was also measured as a check on the absolute performance of the experimental method. At 20°C a value of 1.593 * 0.002 g cm"3 was obtained; this compares with the literature value2 of 1.595 g cm"3. Results of experiments designed to measure the dependence of the density of lime-iron oxide-silica melts, in contact with solid iron, on composition and temperature are shown in Table I. Because iron sometimes precipitated in the sample during quenching, the Fe203 chemical analyses were only poorly reproducible and should be taken as a guide rather than as absolute values. Fig. 1 shows the data from various sources for the density of liquid iron silicates and Fig. 2 shows isodensity contours at 1410°C for lime-iron oxide-silica melts, calculated by graphical interpolation of smoothed curves drawn through the experimental results, together with the 1400°C results of Adachi and ogino3 and Pope1 and Esin.4 Fig. 3 shows the isothermal variation with composition of the volume of melt per gram ion of oxygen at 1410°C and Fig. 4 shows regions in which the temperature coefficient of this volume is negative, positive, or negligible (<0.005 cm3 deg-I). DISCUSSION a) Disparity Between Reported Density Results. Consider the system iron oxide-silica, the results for which are summarized in Fig. 1. Although there is some difference in the temperatures at which the various densities apply, this difference is not sufficiently large to account for the observed discrepancies. The reliability of the present results for the low-silica region has been confirmed by measurement of the density of liquid wustite by three different techniques. At 1410°C the density measured by a balanced-column method was 4.55 g cm"3, by a combination balanced-column and gas-densitometer method 4.59 g emd3, and by a pycnometer method 4.53 g cm"3. Schenck, Frohberg, and Hoffermann&apos; have also reported a value of 4.55 g cm"3 for the density of liquid wustite at 1400°C. It must be concluded, therefore, that neither Pope1

Jan 1, 1964

By R. G. Ward, John Henderson

It has been shown1 that the observed density1-&apos; of liquid iron silicates in contact with solid iron depends upon whether nitrogen or argon is used to protect the experimental system from oxidation. These densities have been measured by the maximum bubble-pressure method, in five different labora-

Jan 1, 1965

By R. G. Ward, John Henderson. R. G. Hudson, G. Derge

Densities of melts of the iron oxide-silica system in contact with solid iron have been measured by the maximum hubble pressure method in the composition range O to 37 wt pct SiOz and the temperature range 1255 to 1410C. The constitution of the melts is discussed and it is postulated that the structure changes from a dislribution of iron ions in an oxygen ion network at pure "FeO" to a distribution. of iron ions in a network of silicate tetrahedra at the orthosilicate composition. JOHN HENDERSON, Junior Member AIME, was formerly with the Metals Research Loborotory, Carnegie Institute of Technology, Pittsburgh, Pa., on leave from Broken Hill Proprietary Co., Ltd., Research Division, Shortland, Australia. R. G. HUDSON, formerly with Metals Research Laboratory, is now with the John Jay Hopkins Loborotory for Pure and Applied Science, General Atomic Division, General Dynamics Corp., LaJolla, Calif. R. G. WARD, was formerly with the Department of Metal lurgical Engineering, Carnegie lnstitute of Technology, while on leave from the Department of Metallurgy, University of Sheffield, England. G. DERGE, Member AIME, is Jones and Laughlin Professor of Metallurgical Engineering, Carnegie lnstitute of Technology. Manuscript submitted January 19, 1961. ISD The system iron oxide-silica is an important one metallurgically because it forms the basis of several complex slag systems in use for industrial smelting and refining processes. In recent years considerable work has been done on liquids of this system but there are still many points of difference among workers using different experimental techniques and theoretical approaches. Phase equilibria/"3 activity,4-6 electrical conductivity,&apos; current efficiency,&apos; transference number,8 viscosity,9 surface tension,&apos;&apos; and density" measurements have all contributed to an understanding of the problem. Measurement of density is one procedure which is directly indicative of liquid structure since any deviation from ideality must be a result of structural interactions. Liquids of the iron oxide-silica system are of special interest because this is one of the few metal oxide-silica systems on which measurements can be carried out conveniently over the entire composition range from pure oxide to silica saturation. This includes the range of high basicity which has received relatively little attention in other systems. Although one investigation of density in this system has previously been undertaken," the results seem of sufficient importance to warrant the independent redeter-mination reported here.

Jan 1, 1962

By M. J. Ginsberg, N. A. Gokcen

THE preliminary study of electrochemical desul-furization performed by Ohtani and Gokcen1 left a number of points concerning the process to be investigated. Two of these were i) the determination of the effect of greater current and voltage on the desulfurizing Flower of acid slags (% CaO/% SiO2- 1) and ii) the possibility of the loss of silica in slag by the reactions 2C (in metal) + SiO2 (slag) = Si (in metal) + 2CO(g) and C + SiO2 (in slag) = SiO(g) + cO(g) proceeding to a point at which the composition of the slag was sufficiently altered toward the basic side so a1.s to noticeably affect the rate of de-sulfurization. The apparatus and the procedure used in the present investigation were the same as those used by Ohtani and Gokcen, except the control circuit was connected to 120 v dc instead of 24 v dc and thereby allowed greater freedom in choosing the values of both current and voltage. The graphite crucible containing the melt and serving as the cathode was 3-in. high, and was of 1 1/2-in. ID with a graphite bar of 3/8-in. diam and 8-in. length threaded into the bottom for electrical connection. This was placed into a magnesja outer crucible with a hole in the bottom and alumina insulation was packed between the two crucibles. A charge consisting of 180 g of

Jan 1, 1962

By Ottar Dragge, C. Danielsson, Bo Kalling

THE desulphurizing of pig iron has been accomplished with a number of different additions. The oldest and still most commonly used agent is soda, the extensive use of which commenced about 1925, when it was used principally for cupola furnace iron. More recent experience&apos; seems to show that better results can be obtained with sodium hydroxide. The well-known desulphurizing properties of lime have also been exploited in different technical processes. Another material with even more powerful effect is calcium carbide.&apos; The desulphurizing ability of manganese, when added to the ladle in sufficient quantity, should also be mentioned in this connection. During recent years increasing attention has been paid to the desulphurizing properties of metallic magnesium." An addition of a suitable alloy of magnesium is now in use purely for the purpose of sulphur elimination. Of the desulphurizing agents mentioned, lime is by far the cheapest, provided that the reaction can be brought about rapidly and completely. Therefore, a method that makes full use of the desulphurizing ability of lime may be able to compete with other processes. A method developed at the Dom-narfvet Iron and Steel Works (Sweden) will be described, which enables pig iron to be rapidly desulphurized to very low sulphur contents by using a burnt lime powder. as the desulphurizing agent. Lime in Older Processes In cases where lime has been used for the desul-phurization of pig iron, it has generally not been used alone, but mixed with other substances such as fluorspar, to obtain the formation of a molten slag during the process. This method has been tried by Tigerschiold,&apos; who treated the iron with a lime-fluorspar mixture, the stirring of the iron being brought about inductively with low frequency alternating current. Very good results were obtained. A process of this type has also been suggested by R. P. Heuer, U. S. A. The principles of this method, which has been tested in Great Britain by Newell. Lanener. and Parsons." re that a mixture of lime and fluoispar is added to the hot metal in the ladle, while a powerful stream of nitrogen gas is blown into the bath to produce the required intermixing. The results of the tests were unsatisfactory, however. A similar process has been developed at The Steel Co. of Canada, according to a statement by H. M. Griffith.&apos; Here the tests were carried out in a carbon-lined ladle provided with carbon tuyeres in the side wall for blowing nitrogen into the bath. The addition consisted of about 20 lb of a mixture of burnt lime and fluorspar per ton of pig iron. Good results appear to have been achieved. The sulphur content of the pig iron is stated to have been reduced from 0.025 to 0.050 pct down to 0.006 pct. Various methods of desulphurizing pig iron have been tried using lime powder without fluxing material for fusing. Eichholz and Behrendt7 have experimented with blowing a powdered limeicoke mixture with air into the ladle. Their results were, however, not conclusive and the experiments do not appear to have been continued. Similar experiments have been carried out at Domnarfvet, using nitrogen instead of air in order to avoid oxidation. But these attempts were not particularly successful. It appears to be difficult to achieve the required agitation by this means. The strong cooling effect of the gas on the iron is also a serious drawback. A method in many respects similar to that tried at Domnarfvet was tried by Eulenberg and Krus at the end of the 1930&apos;s. Here again desulphurization was carried out with lime alone, brought into contact with the molten iron in a rotary furnace. The temperature was kept at the required level, 1400" to 1500°C, by the introduction of a pulverized coal burner in one end of the furnace. The speed of rotating was not given. A paper by Bading and Krus states that, in one of the first experiments, the sulphur content in 56 tons of pig iron was brought down from 0.186 to 0.035 pct in 117 min, but that a considerable shortening of the time would be possible. According to later reports by Eichholz and Behrendt,&apos; it should be possible by this process to achieve a desulphurization speed of 0.35 pct S per hr for a consumption of 6 to 10 pct limestone and 2 to 3 pct coke, as fuel exclusively. The final sulphur content is, however, not stated. Domnarfvet Method After a number of different procedures had been investigated, the tests at Domnarfvet were directed to desulphurization with lime in a rotary furnace. Before going into the practical details of the method, the theoretical aspects will be discussed briefly. If the pig iron does not contain alloying elements other than carbon, the reaction can be expressed most simply by the usual equation: FeS + CaO + C = Fe + CaS + CO [I] 4H,. ~ 34,000 cal That this reaction can be carried through to a very complete desulphurization of pig iron has been shown by OelsenD in a discussion in connection with the Eulenberg and Krus&apos; method. He mentions two laboratory tests, in one of which the sulphur content in the pig iron at 1400°C was reduced from 0.540 to 0.006 pct after treating with 3.35 pct lime. The pig iron had a low manganese content, but other analysis is th. given. Mention also should be made of the recently published investigations by Fischer and Cohnen&apos;" dealing with the influence of the carbon content of the iron on desulphurization with lime, although in this case fluorspar was added also. The tests show that efficient desulphurization is possible with lime in the steel bath, provided that the carbon content is sufficiently high. The temperature employed in these tests was considerably higher (1620") than that normal for treatment of pig iron. The author concludes that the product S% X C% - 0.011 at the temperature in question.

Jan 1, 1952

By William P. Roe, James F. Ellis, W. P. Fishel

This paper reports the distribution of sulphur between iron and titanium in Fe-Ti-S alloys and in Fe-Ti-C-S alloys. The compound TiS was found, which exists as a separate phase at temperatures below 1200°C. Titanium in steels reacts with sulphur in preference to carbon. THE general relationship between sulphides and oxides suggests that titanium should form a sulphide having properties similar to those of titanium oxide. Specifically, titanium should form a sulphide having a high melting point, indicating a stable compound of low solubility in iron. In order for titanium to function as a desulphurizer or sulphur-fixing agent, it must form a stable sulphide. In order for titanium to be useful in steels as a sulphur-fixing agent, it must react with sulphur in preference to carbon; and to prevent red shortness, the sulphide formed must have solubility characteristics such that grain-boundary precipitation of a low melting phase be prevented. The terms desulphurizer and sulphur-fixing agent when used in this paper mean that titanium effectively ties up the sulphur as a stable sulphide of titanium and prevents the formation of FeS. The partition of sulphur between iron and titanium was studied first in a series of Fe-Ti-S alloys with carbon absent, and then in similar alloys with carbon present. It has been established1 a that titanium forms in Fe-Ti-S alloys a sulphide of undetermined composition which can be identified microscopically, and that the titanium-sulphur compound does not respond to sulphur printing. It has been suggested" that titanium acts as a sulphur-fixing agent, although little proof has been given. A report% f The Advisory Committee on Metals and Minerals summarizes the existing knowledge concerning substitutes for manganese in steels. Distribution of Sulphur Between lron and Titanium with Carbon Absent The alloys for this investigation were made by -melting Armco iron, metallic titanium, and iron sulphide in alundum crucibles in an induction furnace. The titanium was added after the other ingredients had melted. In these alloys it is recognized that some TiO, is present, since the melts were made in the air and since no other deoxidizing agent was used; therefore, some of the titanium was not available for union with sulphur. Thirteen ingots were made. Ingots 2 to 8 were cast in baked-sand molds; ingots 12 and 13 were cast in metal molds; and ingot 9 was allowed to cool in the crucible in which it was melted. All ingots were annealed at 900°C for 3 hr and were cooled slowly in the furnace. Subsequent information indicates that this anneal had no effect upon the titanium sulphide particle size, since the sulphide does not go into solution at this temperature. The ingots as-cast were approximately 8 in. long and % in. diam. The compositions of the eight ingots and the results of the partition of sulphur are recorded in Table I. Total titanium and total sulphur were determined by standard gravimetric methods. Sulphur, as iron sulphide, was determined by the evolution method. Boiling HC1 (1:4) liberates the sulphur from iron sulphide, but leaves the titanium sulphide practically undecomposed. A complete separation of titanium sulphide and iron sulphide cannot be made by digesting these compounds in dilute HC1 since titanium sulphide was found to dissolve slowly. The amount of titanium sulphide decomposed will depend upon the time in contact with the acid and upon the particle size of the sulphide. The point

Jan 1, 1952

By S. D. Baumer, P. M. Hulme

IN the late thirties, the National Carbide Co. cooperated with C. E. Wood, of the U. S. Bureau of Mines, in his investigation of the relative merits of various desulphurizers, including soda ash, caustic soda, and calcium carbide. Laboratory tests showed that carbide, when it could be made to react, is an excellent desulphurizing agent for molten iron. Sulphur content can be driven to lower levels and higher extractions obtained with carbide than with actionsany of the more common reagents. Wood&apos;s results1 are shown in Table I. Unfortunately, as the Handbook of Cupola Operation puts it, the chemical fact that carbide is a good desulphurizer was of only academic interest because it was found to be extremely difficult to devise a practical means to make it react with molten iron. Calcium carbide is formed in the electric furnace at 4000°F and above, and its softening point is probably at least 500 °F above the usual working temperatures encountered in iron and steel practice. Consequently, carbide does not form a true slag but floats as a dry powder on top of the metal and only a very small portion of it ever comes in actual contact with the iron. Stirring with a rabble, or pouring the metal over the carbide, increases the efficiency only slightly. Extractions of 20 to 30 pct can be obtained in this manner, but conventional soda slag treatment can do better than this and do it more cheaply. All attempts to lower the melting point of carbide in order to obtain a reactive, liquid slag have so far proved fruitless. Directly under the arc in a metallurgical electric furnace, carbide becomes highly reactive. Excellent sulphur removal can be obtained without any slag other than a thin layer of carbide." imilarly, good results are obtained by adding small amounts of carbide to the finishing slag in double-slag arc furnace practice. To react a liquid with a solid, it is axiomatic that the liquid has to wet the solid before anything can happen. If the solid is heavier than the liquid, the problem is easy, but it becomes more difficult when the solid is much lighter than the liquid, as in the case of carbide and liquid iron. Wood recognized this problem and solved it in a unique fashion. The results shown in Table I were obtained by spinning the carbide beneath the surface of the molten iron by means of a refractory centrifuge. This technique allowed each particle of the finely divided carbide to come into intimate contact with the metal and to be wetted thereby. Wood&apos;s centrifuge technique was successful in the laboratory where it achieved excellent and consistent results. Some attempts were made to expand this method to commercial practice, but serious difficulty was encountered in obtaining a refractory centrifuge head that would be economically feasible. About this time the war intervened and the project lay dormant for several years. In 1944, it was revived. It was suggested that the carbide could be blown into the metal with a carrier gas in an attempt to eliminate the necessity for the expensive and brittle centrifuge. The idea was first tried out in a fairly large ladle of iron using natural gas as the carrier. Considerable sulphur was removed, but it was quite obvious that the use of natural gas was not practical. Attempts then were made to blow carbide into molten iron using, in turn, nitrogen, argon, carbon dioxide, air, and oxygen. The latter two gases proved unsatisfactory. Calcium evidently prefers oxygen to sulphur because in the tests calcium oxide and carbon dioxide were produced, the sulphur still being untouched in the iron. Nitrogen, argon, and carbon dioxide gave much better results, although the efficiencies and extractions were erratic, and only a few isolated tests approached the results obtained by Wood. Table II shows typical results obtained with these gases. The sulphur removals were interesting, sometimes even encouraging, but it is evident that such erratic behavior could not be tolerated in commercial practice. A number of different types of equipment, such as sand blasting machines, refractory guns, and the like can used to blow the solid into the metal. All types required relatively large quantities of gas in order to maintain the flow of solid carbide through the system and into the metal. It was observed that the bubbles of gas breaking through the surface of the metal contained quantities of unreacted carbide. The liquid metal never came in contact with these particles and if it cannot wet them it cannot react with them. The initial work had shown that carbide had great possibilities as a desulphurizer. In practice

Jan 1, 1952

By S. D. Baumer, P. M. Hulme

B. M. Larsen (U. S. Steel Co., Kearny, N. J.)—Could we have some sort of an estimate on the cost of calcium carbide for this treatment? Also, if you used calcium carbide on carbon-saturated iron, would some effect hold back the reaction? P. M. Hulme (authors&apos; reply)—As far as I know we have not worked on carbon-saturated iron. About 3½ pct C is the highest we have worked on. As far as cost goes, it depends on how much sulphur You have to take out. It will run anywhere from $0.75 to $2.00 a ton overall cost including the cost of carbide per ton of metal treated. That is, using the efficiencies that we show in this paper. We are getting better efficiencies now. T. L. Joseph (University of Minnesota, Minneapolis, Minn.)—Did you say 2 lb of calcium compound? Mr. Hulme—That is based on 10 lb of calcium carbide per lb of sulphur removed. D. E. Babcock (Republic Steel Corp., Youngstown, Ohio)—We have run this type of desulphurization process at the blast furnace. We have desulphurized between 100 and 200 at the blast furnace and taken the iron right out of the furnace with an injector system. The process gave us quite varied results; stratified iron, high sulphur on the top and low sulphur on the bottom, and we decided it was impractical. Mr. Hulme Just what was the type of injection equipment? Dr. Babcock—Nitrogen gas for one injection method and we used fairly large gun equipment. We followed the same general type of pattern you show only on a larger scale. Mr. Hulme—It sounds very much like what we call the gale of wind method. We have very erratic results with that. Dr. Babcock—We have tried several types, and particle sizes. The operation was not satisfactory. Mr. Hulme—Of course, we have never tried it on that scale except on a continuous basis. That is the reason we abandoned the idea of working on 35 ton ladles on a batch principle and took it as it came out of the cupola and treated it on the fly on a continuous basis. Dr. Babcock—When you compare the relative effectiveness of the process as carried out, it does not give a very favorable comparison of that process which is already developed. We did not feel it was worth the

Jan 1, 1952

By C. R. Masson, M. L. Pearce

The nitrogen contents of seven specimens of iron and steel were determined by the three methods. Good agreement won generally observed between the results of the isotope -dilution and Kjeldahl determinations, tltzts establishing the reliability of the isotope -dilutzon technique. For some specimens, the vacuum-fusion values at 1650 °C were lower than the corresponding Kjeldahl values by up to 0.0015 pct absolute. These differences were eliminated for a specimen of "pure" iron by performing the vacuum-fusion analyses at 2100 ° to 2240 °C. The reason for this relatively high temperature required m the vaczium-fusion analyses is discussed. ThE determination of nitrogen in iron and steel has been the subject of numerous investigations and a concise review of the extensive literature in this field has recently appeared.&apos; Two methods of analysis are most commonly employed, the vacuum -fusion and the chemical or Kjeldahl method. Except in special cases where the presence of certain alloying elements may present difficulties, both methods are generally regarded as applicable, although the vacuum-fusion method is more sensitive and is often preferred for samples of very low-nitrogen content. The method of isotope dilution, first employed for the determination of gases in metals by Kirshenbaum and Grosse,2 has recently been applied to the determination of nitrogen in iron and steel.3,4 The method is attractive in that it does not require the quantitative extraction of gas from the metal specimen. Staley and Svec3 modified the standard Kjeldahlpro-cedure by introducing, along with the steel sample, a measured amount of ammonium sulfate enriched in the isotope 15N. The nitrogen content was obtained by measuring the isotopic ratio 15N/14N in the resultant solution. The technique involved the distillation of nitrogen as ammonia from alkaline solution and subsequent oxidation of NH4+ in the distillate to gaseous nitrogen. The results for iron and steel samples of commercial origin were often in reasonable agreement with values quoted by the suppliers, although occasional marked discrepancies were observed, particularly with the results of vacuum-fusion analyses. Preliminary work in this laboratory4 on the determination of nitrogen by isotope-dilution in the gas phase yielded results for three samples which were significantly higher than the values obtained by vacuum-fusion. The present paper describes an extension of this work to a wider variety of samples. Analytical results by the Kjeldahl method are also reported. EXPERIMENTAL The technique employed for the isotope-dilution determinations was similar to that described elsewhere.4 Several minor modifications were made to the apparatus. These included the use of molybdenum instead of platinum-rhodium suspending wires when crucibles were degassed at temperatures above 1600°C. The circulatory system used previously for converting CO to CO2 was replaced by a single chamber, the walls of which were cooled directly in liquid nitrogen. Temperatures were measured with an optical pyrometer which had been recently calibrated and, as in the previous study, were minimum values obtained by sighting on the center bottom of the crucible. Temperatures obtained by sighting on the interior walls were always higher by 100&apos; to 130°C with the design of crucible employed. Flat-bottomed crucibles exhibited an even larger temperature difference. To check the efficiency with which crucibles were degassed in the isotope-dilution apparatus, several experiments were done in the vacuum-fusion apparatus, suitably modified4 for isotope-dilution studies. Faster pumping speeds and higher degassing temperatures were possible, the latter due to the use of a generator with a higher power output (10 Kva at 398 kc per sec). In these experiments the combustion of CO was omitted and a correction4 was made for the contribution of CO to the ion current at m/e 28, used in determining the isotopic ratio R = l5NP4N. This correction did not seriously influence the re-

Jan 1, 1962

By R. M. Fowler, H. L. Hamner

DURING the last 25 years, there appeared in the literature a number of papers describing equipment and operating techniques for the determination of total oxygen in iron and steel. In the early papers, comparatively little attention was paid to side reactions that occur when iron is saturated with carbon at a high temperature in a high vacuum. As more experience was gained with the new method, the limitations appeared. Metals, with a boiling point lower than iron, distilled out of the crucible, condensed in the cooler part of the furnace, and subsequently reacted with carbon monoxide to form oxides and carbon. Aluminum, manganese, and the alkaline earth metals proved troublesome in this respect. Modifications have been devised to overcome the difficulties due to aluminum and manganese, while the alkaline earth metals are not of too much concern as yet to the steel chemist. The reactions of sulphur have received less attention, although it is generally recognized that some carbon disulphide is probably formed. Liquid air traps have been used in some cases to prevent any carbon disulphide from entering the analytical train. Sulphur was not a particular problem at the Union Carbide and Carbon Research Laboratories until the analysis of the irons of higher than usual sulphur contents became necessary. In order to describe the procedure developed for such irons, it will be necessary to first describe the type of vacuum-fusion equipment employed because the operation of vacuum-fusion equipment is an art to a considerable extent. At the Laboratories, vacuum-fusion equipment has been in daily operation since about 1930. Over the years, the evolution of this apparatus has been governed by the versatility required to analyze a wide variety of materials. Since all types of materials from high purity metals to slags are analyzed and, since seldom more than a few samples of one type are analyzed in succession, the apparatus was designed for accuracy and flexibility rather than for speed. A general view of the equipment is shown in Fig. 1, while Fig. 2 shows the relationship of the various parts. In Fig. 2, A is a vertical double-glazed 24X27/8 in. OD silica tube heated with a 20 kva mercury-arc high frequency generator. The tube is closed with a water-cooled brass head attached with de Khotinsky cement. A turret cap fits on this head and is sealed with a 1/8x3 in. "0" ring. The head contains a sight glass and two 8 in. horizontal glass tubes, for sample storage, cemented in with de Khotinsky cement. B is a four-stage Gaede mercury diffusion pump connected to the water-cooled head with a 11/2 in. copper tube through a flange with an "0" ring. The output of the vacuum pump feeds into an automatic Toepler F pump which compresses the gas sample over mercury in the measuring burettes, G and H. There are bypasses in this line for a McLeod gage C and a Piranni gage D, a manometer E, and for initial pumping out of the system with a Cenco Megavac backing-up pump. The reduction crucible shown in Fig. 3 is machined of Tungar Bulb quality (A.G.K.T.E.-2) graphite. The sample is guided into the crucible with the graphite funnel depicted on this figure. The arrangement of the crucible, radiation screens, etc. in the furnace is as follows: A 1 15/16x61/2 in. Alundum thimble, porosity RA-84, with two 1/8 in. holes near the top and opposite each other which take a pair of special tongs used for lowering it in place, is prepared. A 3/4 in. layer of powdered graphite is placed in this Alundum thimble, and the graphite crucible containing 20 g of ingot iron and 0.5 g of carbon is carefully centered on this bed of graphite powder and graphite powder is packed around it to the top of the graphite cru-

Jan 1, 1953

By R. H. Singleton

ThE purpose of this investigation was to determine the effect of cerium upon the nonmetallic inclusions found in cast and wrought steel containing various amounts of sulfur, oxygen, and nitrogen. Interest of the Physical Metallurgy Laboratory of the Watertown Arsenal Laboratories in this type of research was stimulated by the reports from industry that rare-earth metals imparted beneficial effects upon the mechanical properties of steel, but that the mechanism was not understood. Berry and Dorvel&apos; found that misch metal improved the impact properties of aluminum-killed cast steels. They reported that the rare earths modified the intergranular-film type nonmetallic inclusion, present with aluminum as the sole deoxidant, to a randomly distributed globular type. Lilliequist and Mickelson2 observed the improvement of ductility and toughness of quenched and tempered cast steels through rare-earth additions. They also observed the change from angular to duplex inclusions when rare earths were present. They con-

Jan 1, 1960

By O. Cuscoleca

The Austrian plants at Donawitz and Linz were the first to blow steel with high purity oxygen. The paper shows how the process was developed and gives a survey of the results achieved to date. Compared with open hearth steel of equal quality, the obvious advantages of oxygen steel are the low investment and conversion costs. The nitrogen content of oxygen steel is not higher than that of good open hearth steel. Rimmed and killed steel products made by the oxygen process are superior to rimmed and killed steel products made by the best open hearth process. TWO new steel plants using the principle of making steel with high purity oxygen went into operation in Austria, one at Linz (Vereinigte oster-reichische Stahlwerke) in November 1952 and the other at Donawitz (dsterreichisch-Alpine Montan-gesellschaft) in May 1953. An estimated 330,000 metric tons were produced by the two plants in 1953, the first year of operation. In 1954 production by Austrian plants- using the high purity oxygen approach will be raised to 450,000 metric tons. This will be in addition to facilities in Huckingen (Man-nesmann A. G., Düsseldorf, Germany), those planned and under construction at Hamilton, Ontario, Canada (Dominion Foundries and Steel, Ltd.), and elsewhere. It is expected that by 1955 a total capacity of one million tons of high purity oxygen steel will be available. At the close of the last century, because of increasing availability of scrap, open hearth steel production forged ahead at an ever increasing pace. This caused world steel production to rise faster than pig iron production and finally to overtake it. In 1911 65 million tons of steel were produced against 64 million tons of pig iron. World steel production was 209 million tons in 1951, while pig iron output was only 147 million tons. The 1951 breakdown for steel shows 118 million tons made from pig iron, while the balance, 91 million tons or 44 pct of the total tonnage of steel produced, was made from scrap. This increase in crude steel production on a basis of high scrap consumption led to the world market scrap shortage and soaring scrap prices. In the United States and other nations, production of converter steel has fallen far behind that of open hearth steel. The surplus of processing scrap, un-absorbable by converting mills and thus a welcome source for open hearth and electric melting shops in the past, together with regular scrap purchases, no longer can meet requirements of both open hearth and electric steel production in Europe. In addition, recent modification of the basic bessemer process, blowing with oxygenated blast, substantially raised the scrap capacity of these plants. Any further expansion of world steel production will necessitate utilization of self-containing processes in regard to scrap because of the shortage.

Jan 1, 1955

By J. Chipman, H. Towers, M. Paris

A simple radioactive tracer technique is used to measure the diffusion coefficient of calcium ion in molten slags. In a slag of 40 pct Ca0-40 pct Si0,-20 pct Al203, Dc " at 1450°C is 1.3x10-6 cm&apos; sec-&apos;. THE application of the principles of thermodynamics to steel and iron making problems has proved so fruitful that the kinetic approach has tended to be neglected. It seems probable that in some reactions the rate-determining step is the dif-fusivity of the reactants or of the products. But knowledge of the diffusion coefficients of the constituents of liquid slag and metal is singularly lacking. The present work was undertaken as a first step toward supplying such data for slags. Furthermore, any additional information on the physical properties of liquid slags might be expected to help in elucidating their structure. It is essentially a preliminary investigation, the course of which was determined more by the necessity of establishing a method than by the immediate intrinsic interest of the results. For example, the selection of calcium ion to be studied was dictated by the suitability of the isotope Ca45 in that it is a simple emitter with a long half-life. Of the other ions commonly encountered in slags, the isotopes of iron and manganese have relatively complex radiations as well as the normal disadvantage of requiring control of the oxygen potential of the atmosphere; Mg27 and Al29 have half-lives measured only in minutes; Si3&apos; has a simple decay process but its half-life of 2.8 hr is too short for preliminary studies; the only useful oxygen isotope is the stable O18; and there remain only sulphur and phosphorus both of which have suitable isotopes but were rejected as being of less fundamental interest than calcium. Similarly a lime-alumina- silica slag was used in preference to calcium silicate primarily because of its low melting point and its capacity to form a glass on fairly rapid cooling. Literature Review Very few studies of diffusion in liquid silicate systems have been reported. In order to determine the origin of diopside inclusions in felspathic rocks, Bowen1 investigated the diffusion between diopside and various mixtures of albite and anorthite. Platinum crucibles were used with diopside, the heavier of the two liquids, forming the lower half of the cell and diffusion taking place against gravity. Change in concentration along the diffusion path was found by measuring the refractive index of the quenched glass. Nearly thirty years later McCallum and Barrett2 used essentially the same method to determine the diffusion coefficient of lime in lime-alumina-silica slags. In this case the interest was to find the rate-determining step in the process of slag attack on refractory materials. In an investigation of the kinetics of the sulphur reaction, Derge, Philbrook, and Goldman8 determined the diffusion coefficient of sulphur in a typical blast furnace slag by the simple procedure of melting a slag containing 2 pct S over an identical slag sulphur-free. They make no claim to a high degree of accuracy but suggest that D, is of the order of 10-6 cm2 sec-l. Other high temperature liquid diffusion studies have been concerned with metals. Holbrook, Furnas, and Joseph4 determined the diffusion coefficients of silicon, phosphorus, sulphur, manganese, and carbon in liquid iron by immersing a small carbon crucible containing pure iron-carbon alloy in a large vessel containing iron with a high concentration of the particular element. Their results were confirmed by Paschke and Hauttmann5 using a similar method. Diffusion coefficients in silicates in the glassy state have been studied by Johnson, Bristow, and Blau6 Both Na24 and Ca45 were used as tracers but only the

Jan 1, 1954

By K. L. Komarek

Based on theoretical and experimental evidence a discussion follows of the behavior of phosphorus -bearing iron ores in the R-N Direct Reduction Process and suggestions are made of methods of reducing the amount of phosphorus in the metallic end product. In ferrous metallurgy a direct reduction process is one in which iron ores are reduced to metallic iron with gaseous or solid reductants without the appearance of a liquid phase. A number of attractive features have induced several companies and government agencies to invest in the development of direct reduction processes. A summary of all direct reduction processes up to 1954 has been given by Barrett,&apos; and Wiberg,2 and Willems3 have reviewed the most recent developments in this rapidly expanding field. Many difficulties have been encountered in direct reduction processes and the nature of these difficulties has varied from process to process. One problem common to almost all of them is the removal of phosphorus which is one of the reasons for the rather pessimistic outlook given by some government publications4&apos;5 to direct reduction processes. In this paper an attempt is made to give a theoretical explanation of the variations in phosphorus removal observed in the R-NY Direct Reduction Process. However, many conclusions are general enough to be applicable to other processes. Most iron ores treated by the R-N process yield products lower in phosphorus than the original ore. A qualitative account of the factors has been given by Stewart, Reed, and Herasymenkoe but the erratic removal of phosphorus from some ores and the general importance of this problem make a more careful analysis of the theoretical aspects desirable. In the R-N process mixed ore or balled fines, ex-

Jan 1, 1963

By G. W. Healy

G. W. Healy (union Carbide Metals 0.)-The author&apos;s paper is a useful contribution to the store of maps of chemical activities of oxides in multi-component slag systems. It is also a good example of the utility of the Gibbs-Schuhmann technique for calculating activities in a system where that of one of the components has been measured. This paper Koh and Caugherty. This plot is reproduced by alor in X-ray Metallography. Because of this nonlinearity, preparation cf suitable standards and/or correction for absorption and enhancement are essential in microanalysis. However, our objection is not the conclusion that Dr. Aaronson has arrived at nor the technique he has used; but only to the foot-note credited to V. Macres. The level of chromium that he was concerned with (less than 3 pet) is so low that the deviation of uncorrected Cr-curve will be negligible. Besides Dr. Aaronson has used chromium intensity from martensite and set it equal the bulk chromium content of the alloy. Using this chromium-intensity as a reference, he has calculated the amount of chromium in the ferrite. This amounts to the same as using an internal standard. Since the chromium content in austenite and ferrite are almost the same, enhancement due to iron in both will be the same and therefore does not need to be corrected. together with the author&apos;s recently published one1 on the CaO-FeO-Fe2O3 system will be most helpful to others learning to apply Schuhmann&apos;s method, which merits a far wider application than it has received to date and should greatly aid our understanding of equilibria between metal and oxide phases. As shown by okcen" its use may even be extended to sections of systems with any number of oxides. I have some questions as to the selection of equilibrium constants made by Dr. Turkdogan. He has chosen one for the formation of Fez03 from FeO and oxygen which gives Fea3 activities 50 pct higher

Jan 1, 1963

By W. F. Hosford

W. F. Hosford, (Massachusetts Institute of Technology) —evelopment of methods for predicting the plastic anisotropy of textured metals is an important step toward the improvement of properties by texture control. The engineering value of the present analysis is indicated by the good agreement between prediction and experimental findings. The purpose of this discussion, however, is to point out the weakness of the assumptions on which the analysis is based. The authors state that "the relative width and thickness strains are believed to depend only on the slip direction" and accordingly they disregard the orientation of the active slip plane. where E,, cW, and et are the tensile, width, and thickness strains, A,, A,, and At are the angles between the tensile axis x, the width direction w, and the thickness direction t, respectively; and G,, GW, and 4 are the angles between the slip-plane normal and x, w, and t, respectively. Therefore, the ratio of width to thickness strains resulting from slip on a single system would be These relations hold regardless of whether the slip plane is a crystallographic plane of the {110}, (1121, or (123) type or whether noncrystallographic slip occurs. If noncrystallographic slip occurs, it might be reasonable to assume that the effective slip plane is the most highly stressed plane containing the slip direction. In this case the slip direction, S.D., the slip plane normal, S.P.N., and the tensile axis, x, are coplanar (Fig. 19) and the angles are related by following expressions: where 9 is the angle between t and the projection of the slip direction in the w-t plane (igs. 1 and 2). The normal strains, Eq. [9], become

Jan 1, 1963