By C. W. Clark, J. H. Schloen

Two papers have been written previously concerning operations at the Montreal East plant of Canadian Copper Refiners Limited. The first one,1 written in 1932, described silver-refinery operations at the time for producing silver and gold bullion from tankhouse anode slimes; the second,2 published in 1933, consisted of a description of the entire plant. Since publication of these papers the refinery has become the world's largest producer of refined selenium. The first selenium was produced in August 1934. Tellurium production on a commercial scale followed in October 1935. This paper will deal with selenium and tellurium production and also with present operations in the silver refinery. Blister cakes from Hudson Bay Mining and Smelting Co., Flin Flon, Manitoba, and commercial anodes from Noranda Mines Limited, Noranda, Quebec, are refined at Montreal East. Both these bullions have unusually high gold, selenium and tellurium content. The average assay of raw slimes produced from domestic and Noranda anodes is about 40 per cent Cu, 3600 oz. per ton Ag, 800 oz. per ton Au, 22 per cent Se and 3.7 per cent Te. EARLY SILVER-REFINERY OPERATIONS From the start of operations in 1931 until July 1934, the raw slimes were oxidize-roasted at 700° F. in a Nichols-Herreshoff furnace, acid¬leached with tankhouse discarded foul electrolyte (20 per cent H2SO4), filtered and charged directly to the doré furnace for refining to doré metal. This is the customary method for treating tankhouse anode slimes but was not suitable at the Montreal East plant because of the high selenium and tellurium content of our slimes. In the acid-leaching process about 50 per cent of the selenium and tellurium in the roasted slimes was dissolved in the electrolyte. These elements were recovered with the copper as a sludge in a small electrolytic

Jan 1, 1938

By Ernest Klepetko

A NOTABLE amount of fossil resin exists in many of the bituminous coal beds of Utah. The upper part of these show a marked concentration of resin, which occurs primarily in the fracture seams. In general, these seams are less than 1/8 in. thick, but it is not uncommon to find coal with areas as thick as 3/8inches. The resin is of the hard kauri variety, with coloration varying from deep blood red to lemon yellow and almost colorless. There is also an almost black variety, which is not readily soluble in the same solvents as the lighter colored resins. These resins are valuable for many industrial purposes. When refined, they are suitable for uses similar to those for which lac resins are usually employed. They are particularly desirable for preparing dielectric varnishes. They are also desirable in preparing printing inks, waterproofing agents, special synthetic rubbers and rubber cements. They are especially suitable as an admixture in synthetic rubbers and cements, as they supply the essential tackiness the synthetics lack. The following chemical trade characteristics have been found by Inter-Chemical Co. research chemists in the refined resins: [Specific gravity (melted) 1.03 -1. o6 Acid number6-8 Softening point, mercury method 160 -165°C Iodine value (Wijs)140-1.50 Refractive index1.544 Color (Hellige, 25 pct toluol) ...14 Molecular weight, average732 Purity, 99 + pct pure hydrocar Bon] "Unaffected by alkalies and resistant to one hour fusion with solid potassium hydroxide. Completely soluble in aliphatic and aromatic hydrocarbons. Insoluble in alcohols, ethyl acetate and other commonly used alcohols and esters. Compatible with natural and synthetic rubbers, chlorinated and cyclized rubbers, waxes, vegetable oils, mineral oils, rosin, ester gum, phenolic and modified phenolic resins and other natural and synthetic resins of like solvent solubility. The recovery and refining of these fossil resins has been the subject of much research work and has intrigued many investigators. Broadly speaking, the problem involves separation of the resin from the coal into a very high-grade concentrate, and subsequent treatment of this concentrate to produce an acceptable refined resin for its various usages. Obviously it is also desirable to recover the residual coal without excessive size degradation. The late W. D. Green, concentration engineer for Combined Metals Reduction Co., obtained U. S. Patent No. 1773997 for the recovery of resin from coal through

Jan 1, 1947

By J. B. Goddard

The discovery of rhenium on the ion exchange resin used at the uraniun in-situ leach operations at Palangana, TX, led to a laborabory study of possible recovery methods. Rhenium was present in small amounts in the ammonium carbonate leach liquors as the perrhenate anion, ReO4-. It concentrated on the anion exchange resin, which was a factor of 10 more selective for rhenium than for uranium. Various elution systems were investigated for stripping the rhenium from the columns after the uranium had been eluted with chloride or nitrate solutions. Although the per-chlorate ion was most efficient on a molar basis, nitrate ion combined the benefits of efficiency and low cost. A 3N or stronger concentration of nitrate containing up to 0. 5N H + was found to be the system of choice. A rhenium sulfide concentrate containing up to 14010 Re was obtained from these effluents by hydrogen sulfide precipitation. Preliminary experiments were run to produce rhenium metal powder by oxidation of the concentrate to NH4ReO4 followed by hydrogen reduction at elevated temperature.

Jan 1, 1984

By Frederic Benard

RECOVERY of selenium and tellurium at Copper Cliff by the Ontario Refining Co. has been previously described by the writer.1 During 1935 a new building was erected to house this operation and description of the new plant and process form the subject of this paper. The building, of modern steel and tile construction, covers an area of 5900 sq. ft. with a volume of approximately 165,000 cu. ft. The large monitored center bay is flanked by two smaller outside bays, one of which is devoted to the tellurium section. All equipment, ceilings and upper walls, are treated with aluminum paint, giving good illumination and facilitating good housekeeping, essential from a health standpoint in handling material of this nature. EQUIPMENT Layout and type of equipment conforms to the requirements of the process as described below. In the selenium section, storage tanks, neutralizing tanks and precipitators are of steel construction, lead-lined and. arranged for gravity flow (Fig. 1). The neutralizing tanks are equipped with water-cooled lead coils for controlling solution temperature, agitation being accomplished with compressed air. The precipitators are provided with mechanical agitators, and sulphur dioxide is introduced into the solution through 3-in. lead pipes leading from a manifold attached to the cover of the precipitator. Each precipitator has internal cooling coils and an air-jet exhauster to carry off fumes. Neutralized solutions are filtered in a 29-plate wooden filter press using heavy cotton duck as a filter medium, forced feed being maintained by a Welmet centrifugal pump. Dilute solutions are concentrated by evaporation in a vacuum evaporator, constructed of cast hard lead. Heat is supplied by an outside steam chest operating under 15 lb. steam pressure. The solution is circulated through the steam chest by a pump of antimonial lead at a rate approximating 400 cu. ft. per min. The evaporator is evacuated by a water-jet condenser that creates a vacuum of 26 in. of mercury under normal operating conditions. The capacity of the vessel is 60 cu. ft. and the rate of evaporation 25 cu. ft. per hour.

Jan 1, 1938

By Frederic Benard

RECOVERY of selenium and tellurium at Copper Cliff by the Ontario Refining Co. has been previously described by the writer.1 During 1935 a new building was erected to house this operation and description of the new plant and process form the subject of this paper. The building, of modern steel and tile construction, covers an area of 5900 sq. ft. with a volume of approximately 165,000 cu. ft. The large monitored center bay is flanked by two smaller outside bays, one of which is devoted to the tellurium section. All equipment, ceilings and upper walls, are treated with aluminum paint, giving good illumination and facilitating good housekeeping, essential from a health standpoint in handling material of this nature.

Jan 1, 1938

By James E. Hoffmann

This paper reviews the chemistry of selenium and its compounds as it applies to the recovery of selenium from electrolytic copper refinery slimes. Based on this chemistry various processes for the extraction and recovery of selenium from refinery slimes are explained and developed. The optimum selenium technology processes is dependent upon many factors including copper refinery location, environmental and regulatory conditions, local markets for selenium or selenium chemicals, and other plant processes. For this reason there is no one best process but rather a variety of useful processes for winning selenium. Those which have demonstrated consistent utility in both ease of recovery and reliability are discussed in more detail. Recovery of selenium by Doré furnacing of slimes is the topic of a separate paper. The companies that have developed selenium extraction technology are not being cited in this paper for the following reasons: o Their current technology may be different o The actual inventor of a process is difficult to credit since many different organizations have pursued parallel inquiries in developing better processes. Finally, some selenium extraction processes have been omitted; not because they are unworthy of consideration but rather due to limitations of space.

Jan 1, 1984

By William Romanoff

IN AN ARTICLE on "Recovering Smelter Dust and Oxide," published in the Engineering and Mining Journal (Vol. 131, No. 2), the authors briefly described some dust-recovery equipment and its operation at a secondary-metals brass-smelting and refining plant. A description of our experience in overcoming certain operating difficulties may prove of interest or value to those who are confronted with some of the same problems or who should equip their furnaces with dust-collecting equipment. The dust loss from reverberatory smelting and refining of brass con¬sists largely of zinc, with smaller percentages of lead, tin, and copper in the order named. At the Kramer plant, the fume discharge from the two stacks amounted to 3 to 4 tons of solids per day, making a dense smoke. With dust equipment in operation, the discharge from the stacks is invisible and approximately 2500 lb. of zinc and other metals is recovered daily thereby from each furnace operating.

Jan 1, 1933

By Edward L. Fidler, Thomas E. Finch

Thin seam coal mining in the western US nominally equates to recovery of stray seams associated with thicker, major seams. The thin or stray seams encountered are generally recovered, but not in all cases. The alternative to extraction is, of course, spoiling. The majority of thin seams are encountered somewhere in the overburden above the major seam or in the parting between thick seams. Although some are true strays and appear anywhere in the geologic sequence, others might be classified as thin "rider" seams immediately above or below a thick seam and separated by some equally thin parting. For the purpose of this discussion, stray or thin seams are defined as those which are less than 1.2 m thick or represent less than 10% of the expected extractable coal. [Figure 1] is a graphic representation of typical thin, stray, or rider seams which actually appear in a western operation. Operationally, stray seams create irritating scheduling problems and require special handling techniques which do not always lead to efficient equipment utilization. Additionally, coal recovery from a thin seam is considerably less than the 95% usually recovered from thick seams. Higher recovery in thin seams leads to dilution problems, which depreciates Btu quality, and most western coals are not in a position to lose heating value. Thin western seams also undulate and pinch or swell more than thick seams, and this leads to more difficult recovery. Often they are associated with equally dark carbonaceous shales and visual selectivity is difficult at best during daylight hours. Resource Recovery Regulations Thin seam recovery in western mines is encouraged by both federal and state regulations and by the mining industry's concern for total resource recovery. [Table 1] lists the western coal states and their recovery regulations. The federal regulations are found in the Surface Mining Control and Reclamation Act of 1977. They state, "General performance standards shall . . . require the operation as a minimum to … conduct the surface coal mining operations so as to maximize the utilization and conservation of the solid fuel resource being recovered." Economic stimulation for thin seam recovery appears to be marginal or at the least controversial. Scheduling and operational problems often outweigh the nebulous profits created by engineering analysis. The only alternative to extracting thin seams occurring above major production seams is to strip directly through them and lose the resource to the spoil pile. Although this is not palatable to environmental emotions or resource promoters, it is the most simple expedient to operations people.

Jan 1, 1981

By Fred J. Hurst

In 1934, Irvin Lavine (A), University of North Dakota, stated that the low-rank coals (lignite and subbituminous) of this country represent a vast tonnage of fuel of commercial value and predicted that some day they will play an important role in our economic welfare. Lavine also pointed out that one of the major problems with efficient utilization of the low-rank coals is their high moisture content. Following the discovery of uranium-bearing lignite in the Williston basin of North and South Dakota in 1948 by D. G. Wyant and E. P. Beroni, detailed investigations were conducted (primarily during 1950 to 1954) by members of the U. S. Geological Survey to evaluate the geologic factors and economic possibilities of the radioactive lignites as a source of uranium. The information gained in these studies and summarized in several papers indicated that a large potential reserve of uranium is contained in the subbituminous coal and lignite deposits of the Dakotas and Wyoming (2,3,4). Most investigators concluded that an epigenetic emplacement of uranium in the coal by means of circulating groundwater and the more extensive concentrations of uranium in coal are apparently related to the permeability of the rocks enclosing the coal beds. Breger (5) and others have shown that uranium is readily adsorbed by coal and is held irreversibly as a disseminated adsorbed constituent. Briefly, lignite beds containing 0.1 to 10% uranium have been discovered in the Dakotas and Wyoming. The distribution of uranium was found to be erratic and was usually concentrated in thin layers, which were characteristically 10 to 14 in. thick and occasionally 30 to 36 in. thick. Lignite beds more than 3 ft. thick generally contain more uranium at the top of the bed than at the bottom. Special strip mining techniques are required to mine these thin

Jan 1, 1983

By Henry G. Petrow, Edward S. Porter

MAJOR occurrences of lignite with significant uranium concentrations have been reported in western parts of the Dakotas, especially in Harding County, S.D., and Billings and Slope counties, N.D. Samples containing as much as 2 pct U3O8 were received at the Winchester Laboratory, but those deposits reportedly of major significance have generally contained 2 to 4 lb of uranium per ton of lignite. Most of the uranium appears to be associated with the carbon in the lignite as a urano-organic complex, although in most instances analysis of inorganic material has shown uranium values. Molybdenum is similarly associated with the carbon, and its concentrations generally parallel the uranium. The noncarboniferous material is mainly composed of gypsum, jarosite, bentonite, sandstone, and miscellaneous carbonates and silicates. The heating value of these lignites has been determined as about 3500 Btu on a dry lignite basis. The ash content of lignite has varied widely, the important samples containing 30 to 60 pct ash on a dry lignite basis. Because of the significant upgrading of uranium values obtained by ashing the lignite, and because recovery of uranium from raw lignite presented formidable processing problems, major emphasis at Winchester has been placed on devising methods to recover uranium from lignite calcines. Proper roasting removes the problem of organic fouling of solutions, reduces the size of the leaching plant for an equivalent uranium throughout, and generally provides equal or better acid leaching efficiency with less acid than can be obtained from the raw lignite.

Jan 9, 1957

By M. Streat, R. Y. Qassim

Summary This paper reviews the developments in uranium process technology as a result of modern trends in the design of ion exchange equipment. The operation of the Cloete-Streat fluidised bed contactor is described and pilot-plant development of this contactor for uranium slurry work at Imperial College is outlined. The properties of a suitable ion exchange resin for slurry treatment are discussed, together with a description of relevant rheological properties of ore suspensions. A prediction of ion exchange resin- slurry behaviour is presented in order to establish the feasible operating limits for this type of R-I-P contactor.

Jan 1, 1973

By F. J. Hurst

The rapid expansion of the phosphate fertilizer industry in conjunction with the projected shortage and spiraling price increase of uranium has greatly renewed interest in wet- process phosphoric acid as a significant source of uranium. Two attractive solvent extraction processes for recovering uranium from the acid have recently been developed and tested through bench-scale at Oak Ridge National Laboratory. One of the processes has been successfully tested on a pilot-plant scale at phosphate plants; the second process, which offers several potential advantages, still needs additional testing. The merits of each process are discussed.

Jan 1, 1978

By Clyde Wyman

THERE has always been a question as to the extent to which oxidizable alloys might he recovered from charged scrap in the, acid electric furnace. While qualitative information was not lacking, the quantities that might be recovered and the conditions best suited for such recovery were not clearly defined. The present investigation was carried out to determine the efficiency of alloy recovery from residuals contained in the bath, especially in regard to the recovery of vanadium. A series of 24 heats was produced at the Burnside Steel Foundry Co., including medium manganese-molybdenum-vanadium, manganese-chromium, and grade B steels, in which vanadium recoveries from the residual vanadium were investigated. Recoveries of other alloys were also studied from the accumulated data. These heats were produced in a 5-ton acid-lined electric furnace. The analysis of metal and slag samples and the micrographs were prepared by the Research Laboratories of the Vanadium Corporation of America. In addition to the vanadium contained in the scrap charge, ferrovanadium was added to the charge and to the molten bath to bring the residuals up to the desired level. Vanadium pentoxide (V2O5) in one series of heats was added to the bath after meltdown, for the same reason. In addition to the general furnace practice, the slags of these various heats were treated with coke breeze, Ferrocarbo-S (silicon carbide), and aluminum dross to determine the effects of different reducing agents upon the alloy recoveries and upon the final product.

Jan 1, 1947

By P. J. Potter

PRACTICALLY all tin-base babbitt metals used in engine bearings are made to customers' specifications, which are many and varied. The copper ranges from 3 to 8 per cent. and the antimony from 4 to 13 per cent.; generally, the babbitt with lower copper content will contain from 4 to 8 per cent. antimony and that with higher copper will have from 7 to 13 per cent. antimony. The allowable lead content varies from 0.20 to 2.00 per cent. If a solder is used as a bonding material instead of tin, the resulting material in the finished bearing will have a higher lead content, but it would not be enough to bring the lead above specificational limits. Impurities such as iron, arsenic and bismuth should be determined in the tin before using to insure a uniform and high-grade product. These points must be considered when segregating and grading the waste that comes from the finishing operations on lined bearings.

Jan 1, 1929

By D. Pearson

INTRODUCTION In 1975 278x10 3 tonnes of zinc was consumed in the United Kingdom, of which 69.3x10 3 tonnes was obtained from secondary sources. Of this secondary zinc 37.7x10 3 tonnes was used in brass making, the remainder was used in non metallic applications - eg oxides and salts. Many forms of zinc-bearing wastes arise, for example as galvaniser's drosses and residues, fumes from ferrous and non-ferrous metallurgical processes, and filter cakes from rayon manufacture and metal finishing. In the case of zinc-bearing dusts and fumes, the quantities available for recycle are at present restricted by the failure to collect them efficiently, hut environmental factors are leading to improvements in gas cleaning, with the result that quantities collected will increase and then exceed those required for the production of chemicals, so that some dusts may either have to be dumped or processed to metal. The recovery of zinc from steelmaking dusts is practised in W. Germany (1) and Japan (2) employing processes based on reduction in rotary kilns in order to produce sponge iron and a zinc- rich oxide suitable for feeding to the zinc-lead blast furnace. Although the zinc-lead blast furnace is the only zinc-making process used in the UK, no similar treatment of steelmaking dusts is carried out, a pilot scheme was tested by the British Steel Corporation, but development was abandoned for economic reasons. It appears to be cheaper to pelletise suitable dusts and export them for treatment elsewhere.

Jan 1, 1981

By Tsuyoshi Miyashita

Onahama Refinery of Ryoho Recycle Company employs the electrothermic process for producing marketable zinc oxide from steelmaking dusts. The process comprises washing, filtration, drying, sintering and furnacing. Fume from the sinter machine is treated hydrometallurgically to recover zinc, cadmium and lead.

Jan 1, 1976

By Maurice Cook

A procedure of obtaining specimens of lead, tin, and cadmium with a moderately equiaxed structure and a smooth surface suitable for etching without grinding and polishing is described; the advantages of general oblique illumination (as opposed to vertical illumination) in the photomicrography of pure metals .are stated. Using these methods, a statistical study of the changes brought about in deformed lead, on annealing, has been made. The common mode of structural change was found to be recrystallization. Cases of growth of one original grain into another were rare; but if a totally recrystallized specimen was annealed above 200° C., a few large grains appeared and spread over the whole area, except for a certain number of small grains which remain unabsorbed. The temperature needed to produce structural change in lead was found to be lower, the greater the degree of deformation. With tin, an extension of 28 per cent. caused practically no recrystallization at ordinary temperatures, but recrystallization occurred if the specimen was heated to 100° C. In cadmium at low temperatures, the grain size decreased in marked manner as the deformation increased; but at high annealing temperatures, the grain size was comparatively independent of the degree of deformation. THE structural changes in metals brought about by annealing following a deformation at a low temperature has been the subject of many investigations. No less than eleven metals and alloys have been studied in some detail; namely, aluminum,1 tungsten,2 iron,3 copper,4 gold,5

Jan 11, 1924

By Henry Howe

THIS paper is a discussion of the extremely valuable one of Mathewson and Phillips, The Recrystallization of Cold-Worked Alpha Brass on Annealing,1 which not only gives us a wealth of important data reached with great intelligence, but also shows both uncommon powers of imagination and a perfectly fair spirit. Let me try to analyze some of their results, and to enunciate some of the laws to which these results point. For brevity I refer to them as "The Authors." The page numbers in parentheses refer to their paper. 1. The Visible Aspects of Recrystallization.-Plastic deformation in a single direction, as in cold-rolling, draws the grains out in that direction, that is, inequiaxes them, without destroying their apparent individuality. Each grain seems to endure the drawing out without changing either its volume or its orientation materially, for the etching tint of each grain seems to be as uniform after as before the drawing out, save for the "etch bands,"2 shown in Figs. A to D of the Authors' Plate I. As the drawn-out metal is heated progressively, on reaching a certain "disintegration temperature" these old grains seem to break up, probably into submicroscopic fragments, and this apparent disintegration is followed by a coalescence of these fragments, so that their number decreases and their size increases, till they may become very much coarser than before the drawing out. Ruder3 coarsened the grains of silicon steel in this way till single grains reached an area of 50 cm. (7.75 sq. in.). The deformation itself probably breaks each grain up into many very small fragments, but the fact that each grain continues to have a uniform etching tint different from that of its neighbors indicates that these fragments retain the initial common orientation of the grain. The apparent disintegration which we observe, then, is rather an abandonment of community of orientation for individuality of orientation, by the fragments formed earlier during the deformation. Hence we

Jan 10, 1916

ZAY JEFFRIES (communication to the Secretary*).-Having seen Mr. Ruder's micrographs of electrolytic iron, I am of the opinion that the tentative explanation offered verbally is correct. Mr. Ruder has informed me that both of the samples were cooled in the furnace. The structures as shown in Figs. Band C resulted from the last cooling through the temperature range near 900° C. Assuming that the rate of cooling through this range was the same in both cases, the differences in struc-ture of the gamma iron in the two samples must have ]:)]-ought about, in some way, the variations in grain size and grain shape shown in Mr. Ruder's micrographs. Even though there is practically no temperature gradient in muffle-furnace treatment during the "soaking" period, during both heating and cooling, there is a temperature gradient. Fig. B should normally have been fine-grained prior to the last cooling, due to the comparatively low maximum temperature to which it was heated (1,000° C.). On cooling through the allotropic change point at 900°, these small gamma grains, iii conjunction with the temperature gradient, should form an ideal condition for germination. Germinant grains should form near the surface of the sample (the-colder portions) and the small gamma grains would be progressively absorbed as they changed into non-gamma iron. The elongated grains in Fig. B, converging toward the axis of the piece of iron, indicate that germinant grains first formed near tine surface and advanced their boundaries toward the interior of the sample. The gamma grains in Fig. C, however, should have been large, prior to the last cooling, due to time high temperature treatment (1,250 to 1,300° C.). In other words, to use one of Prof. Howe's expressions, the crystalline organization should be very complete and the change from gamma to non-gamma iron on cooling would take place reluctantly. This resistance to change from gamma to non-gamma iron would probably be greater in the interior of the large grains than at their boundaries. Non-gamma iron centers or nuclei would probably form at a great many places, at the grain boundaries, thus masking the influence, to a large

Jan 6, 1917

By Henry Howe

W. E. RUDER, Schenectady, N. Y.-In 1913 I presented a paper before this society on Grain Growth, and at that time it seemed to me that the only explanation for grain growth was that of critical strain. I do not think I published the photographs at the time, but I made some experiments on the effect of stretching sheets of metal. This allowed for fairly accurate determinations of the amount of cold deformation, At the time I worked-with silicon steel because one could see the change in grain growth with the naked eye. I stretched about 10-samples from 0.5 per cent. to 10 per cent., and, after heating to 1,050° C., I found that the maximum grain growth occurred at about 2 ½ per cent. cold deformation. This I designated "the critical strain" for maximum grain growth. About a year ago I talked with Prof. Jeffries, who explained to me his ideas of grain growth. It occurred to me that it would be a very easy thing to check the strain hypothesis against the strain and temperature hypothesis, if we took a certain number of these strips, strained exactly alike and heated to different temperatures; in that case the maximum grain growth ought to appear at a different percentage of deformation for each temperature. These experiments showed that there was, as Mr. Jeffries shows in his present paper, a decrease in germinative temperature with increased cold deformation. The samples were stretched from ½ to 8 per cent. and heated for 10 hr. in hydrogen. Samples were introduced into a furnace previously heated to temperature. A maximum grain growth was obtained at 5 per cent. deformation, when heated to 750° C.; at 2 ½ per cent. when heated to 800' C.; at 1 1/4 per cent., if heated at 950°C.; and at 5/8 per cent.. when heated at 1,100° C. This shows very clearly that the germinative temperature decreases with the increase in cold deformation. The growth was very much more marked, however, at the high temperature, i.e., the grain grew more rapidly and attained a much larger size than at lower temperature. In considering the photographs (Fig. A) those along the lateral edges should be ignored because.

Jan 4, 1917