Search Documents

By J. J. Pye, J. B. Drew

The surface-diffusion coefficients of Ni63 diffusing on low-index planes of nickel single crystals have been measured over the temperature range from 400° to 1000°C using a precision autoradio-gvaphic technique. The activation energy for sur -face diffusion appears to he the same on the {111}, {110), and (100) planes and amounts to -0.60 ev. This is in good agreement with the value (-0.62 ev) reported for (111) planes obtained by mass-transport techniques. In an earlier paper, the authors have reported self surface-diffusion coefficients on silver.' In that work, a deviation of the diffusion coefficients from linearity in the Arrhenius plot was observed at high temperatures. This effect was attributed to a loss of tracer atoms into the bulk by volume diffusion. The purpose of the present work was to extend the technique developed to the nickel surface-diffusion system up to the point where volume diffusion would come into play. The nickel system especially lends itself to this technique due to the high efficiency of the isotope in darkening the film and the large absorption of the weak radiation (0.063 mev /3- particle of the trapped tracer atoms. The diffusion coefficients and ictivation energy for different orientations on nickel can also be compared with a report published by Blakely and Mykura 2 where a mass-transfer technique was used. This paper reports the self surface diffusion of nickel on the low-index planes over a wide temperature range using a precision autoradiographic technique. EXPERIMENTAL PROCEDURE The experiment is similar to that described in the earlier publication consisting of a radioactive needle as a source resting on a flat, smooth, chemically polished surface annealed in a dynamic dry-hydrogen atmosphere. The needle is held snugly on the surface by a holder fabricated from commercially pure nickel. The point source is made by grinding down a small-diameter nickel rod until a tip of approximately 0.1 mm radius is formed. It is then etched and the needle tip plated with the radioactive isotope Ni63. Nickel single crystals were used whose main impurities were spectrographically determined as Co 0.05, Fe 0.007, C 0.005, and S 0.003 pct. The surfaces, oriented to within 1/2 deg of the low-index planes, were carefully mechanically polished and etched in a 50-30-10-10 hot solution of acetic, nitric, sulfuric, and phosphoric acids giving a smooth polished surface. The crystals were then washed in distilled water and alcohol. Annealing temperatures ranged from 400° to 1000°C with a furnace arrangement in which the crystals could be brought up to temperature in times short compared to diffusing times. The temperature was maintained constant to ±10°C. In the temperature range investigated, the ratio of the surface-diffusion coefficient to the volume-diffusion coefficient (Ds/Du) was 105 or more and the mean bulk-penetration values, calculated from literature values of volume-diffusion coefficients,3 were on the order of 10-5 cm. After the diffusion anneal, the sintered needle is removed, and both the radius of the needle point and spot left on the crystal face are measured. The crystal is then placed on photographic film. Diffusion profiles are obtained by scanning the film with a recording microdensitometer which has a slit width of 10µ. DISCUSSION AND RESULTS The experimental conditions are such that the source strength and needle radius are essentially constant and the time is adjusted such that the mean bulk penetration is small. An exactly analogous heat-flow problem has been considered by Carslaw and Jaeger4 and the solution can be written in integral form as:

Jan 1, 1964

By N. S. Stoloff, R. G. Davis

It is concluded from an X-ray stztdy that the formation of the hcp Mg3Cd superlattice is a nuclea-tion and growth reaction. A two-phase, ordered-plus-disordered, region is observed between 153" nnd 141"C. A maximum in the flow stress is observed both at temperature and in quenched specimens within the two-phase region. The peak arises fro112 the extra energy required to create antiphase boundary upon cutting the ordered regions. Hardening during isothermal annealing in Mg3Cd has been shown to be similar to the domain hardening in Cu3Au-type alloys in that up to the maximum the structure is ordered domains growing into a short range ordered matrix. The hardening is due to a combination of short range order strengthening and the strengthening produced when antiphase boundary has to be created. In a recent study1 of the effect of long-range order upon the mechanical properties and deformation modes of hcp Mg3Cd a comparison was made be- tween quenched (disordered) and slow-cooled (fully ordered) specimens. The most striking observations were that the disordered alloy yields at a much higher stress than the ordered alloy, and that there is a change in slip mode from primarily (_0001) ba_sal slip in the disordered state to (0001), {1010}, {1122}, and {l011} slip in the ordered state. The main purpose of the present work is to extend these observations to determine whether MgsCd exhibits a peak in flow stress at an intermediate degree of order, or at a critical domain size, as do other orderedstems. However, disagreement exists about the Mg3Cd order transformation with respect to: 1) the location of the critical temperature for order, 165°C or 153"~,' and 2) how the degree of order varies with temperature. Welber et a1.5 concluded from specific heat measurements that the formation of Mg3Cd is a second-order reaction with the degree of order a continuous function of temperature, while Moore and Raynor concluded that it is neither a first-order reaction, with the degree of order a discontinuous function of temperature, nor a second-order reaction. Consequently it was considered necessary to undertake an X-ray investigation into the change in degree of order and structure in the

Jan 1, 1964

By R. D. Carnahan, J. E. White

A study of dispersion strengthening in TD-Nickel (nickel plus 2 vol pct Tho2) was conducted employing microstrain techniques at ambient room temperature. It was found that optimum strength was due primarily to the incorporation of stored energy developed by a variety of thermal-mechanical treatments. The relatively low strength of the recrys-tallized condition implies that the dispersed particles themselves offer only token resistance to deformation. The development of resistance to large-scale recovery or recrystallization at temperatures near the melting point requires a more extensive sequence of strain-anneal cycles than does the development of optimum strength. A micro-Bauschinger effect was observed which appears to be related to the lattice resistance to the movement of free dislocations. The effect was nearly identical to that in pure nickel indicating that the presence of the dispersed phase and considerably increased dislocation density (stored energy) only alters the number or effectiveness of barriers. THE early stages of deformation of engineering materials can be conveniently studied by utilizing strain-gage techniques which permit resolution of strains less than 5 X 10-7 in. per in. for testing in four-point bending (Carnahan and white1). The present investigation, part of a continuing study on the very early stages of deformation, was designed to reveal the true role of a dispersed phase in promoting high strength in a commercially available dispersion-strengthened alloy. Although this technique has been used for some time to study microdeformation in pure metals and alloys, it has just recently received attention as a means of investigating dispersion strengthening. Studying the very early stages of deformation in alloys which depend upon a finely dispersed inert phase for strength may prove to be a very important method for a better understanding of these materials. It is essential to obtain considerable clarification of actual dislocation movement and the kinds of deformation barriers which exist before optimum properties can be designed into this type of material with any degree of confidence. Considerable research on a variety of dispersion-strengthened materials has resulted in two different schools of thought regarding the strengthening mechanism. One faction2-4 favors the idea that the particles themselves resist the motion of dislocations. The criterion for yielding is the fracture of the dispersed second-phase particles due to an array of piled-up dislocations. Other invesfigators5-a have shown that particles are effective primarily by allowing a greater buildup of stored energy or dislocation density through thermal-mechanical treatments in the composite than the pure matrix material. The particles themselves, then, are not exclusive obstacles, but the complex network of particles, dislocation tangles, subboundaries, and grain boundaries are strength determining. The development of such a complex dislocation network in SAP has been studied recently in some detail by Goodrich and Ansell. The ability of dispersion-strengthened alloys to resist softening or recrystallization is also of considerable importance; however, the criteria for maximum stability may not necessarily be those for maximum strength. In this study, in addition to the evaluation of the microstrain properties of TD-Nickel, it is felt that considerable clarification of the true dependence of strength and stability on the dispersed phase is shown. I) MATERIAL AND PROCEDURE TD-Nickel is a dispersion-strengthened alloy developed by the E. I. DuPont de Nemours Co., which contains 2 vol pct thoria (Tho2) in a pure-nickel matrix. The average ThO2 particle size is approximately 0.1 p and the interparticle spacing is less than 1 u. The material was supplied by DuPont in two conditions: hot-extruded bar stock, and stress-relieved cold-rolled sheet 0.025 in. in thickness. The bar was extruded at 2200°F from a cold-pressed and sintered billet. The sheet stock was prepared from the extruded material by a process involving ten or more 50-pct cold reductions by rolling with intermediate anneals at 1800° to 2000°F. Test specimens used in this study were prepared in the form of rectangular parallelepipeds measuring 0.375 by 1.375 in. in thicknesses ranging from 0.025 to 0.040 in. Samples prepared from sheet and extruded stock were mechanically polished before heat treatment and were handled with extreme

Jan 1, 1964

By Jean Howard

ALTHOUGH zone melting has found favor in recent years because of its convenience and its faster rate of production of single crystals, the older technique of strain annealing still has a number of advantages. It has been reported1 that the lattice of a crystal prepared in this manner has fewer defects than one grown from the melt and, of course, the control of the external geometry is easier. Also, the diameter of the crystal which can be grown by zone melting has a theoretical limit determined by the surface tension, thermal conductivity, and specific gravity of the material, while the size of that which can be grown in the solid state is limited only by practical considerations. In a program for the study of the structure-sensitive properties of niobium and its alloys it was desirable, for ease of handling, to have available single crystals of large diameter. This requirement dictated the choice of the strain-anneal technique. Induction heating was chosen in the present work in preference to other methods because of its deep penetration of large-diameter sections. A five-turn coil, powered by a motor generator operating at 10,000 cps, is contained in a vacuum chamber. The work is lowered through the coil for both the recrystallization and the crystal-growth steps. Starting with electron-beam melted material, the bars are cold-swaged, recrystallized, strained in a tensile machine, and then subjected to the growth step. Single crystals have been grown under the following conditions: Reduction in area during swaging— 79 to 99 pct, recrystallization temperature—1500o to 1667°C at the rate of 1.25 in. per hr, strain—1.0 to 2.5 pct, growth temperature—1600o to 2400°C at rates from 0.15 to 1.25 in. per hr. Starting grain sizes achieved after the recrystallization step varied from 0.6 to 1.55 mm. The starting grain size was found to be critical; if it is too fine and has any residual cold work, as shown by the presence of a fiberlike texture, a single crystal cannot be grown. Using this technique niobium single crystals have been grown from 0.250 in. diameter and 12 in. long to 1.00 in. diameter and 5 in. long as shown in Fig. 1. The 1-in. crystal is the largest to be reported for a refractory metal as compared to 0.500 in. for molybdenum grown by zone melting.2 As with zone melting, control of orientation is possible by the use of special procedures. Other investigators, see for example Williamson and Smallman,3 have reported that orientation control may be achieved by a bending technique. In the present work the strained rod is partially lowered through the coil to start the growth of the crystal. Then it is removed and bent at a point ahead of the interface between the single and polycrystalline portions. Finally, it is returned to the chamber and growth is continued "around the corner". The amount of bending which can be imparted to the rod is limited by coil geometry which up to now has been 10 deg. However, by repeating the bending and growing operations it should be possible to attain any desired orientation. The perfection of these single-crystal specimens as a function of process variables is being measured by X-ray and metallographic techniques and the results will be reported in a forthcoming paper. This work was partially supported by the Advanced Research Projects Agency.

Jan 1, 1964

By V I. McCallum

In 1954, Falconbridge Nickel Mines Limited began the program of deepening the Falconbridge mine workings for 2,000 feet below the bottom, or 4025, level in order to provide twelve new levels for production. Involved in this program were a production-sized internal shaft, .crushing, pumping and hoisting installations, the integration of the new shaft operations with those of existing shafts, and considerations of ventilation requirements and ground support at depth. This paper describes the major items of equipment, and the depth development of No. 9 shaft as a whole, and also emphasize the planning phases of the program. The factors involved and reasons for the equipment and layouts chosen are given. Introduction and History THIS paper describes the planning and development of that portion of the Falconbridge mine between the 4025 and 6050 mining levels. This mine, the oldest of several being operated by Falcon-bridge Nickel Mines Limited in the Sudbury district, has been a continuous producer for over thirty years.

Jan 1, 1964

Jan 1, 1964

Crocidolite deposits in the Hamersley Ranges, NW. of Western Australia, occur over a length of 180 miles and a width of 20' to 30 miles. Their stratigraphic environment and mineralogy is comparable to that of similar deposits of the Cape Belt, South Africa. It is probable that the known exposures' represent only a small portion of the total extent.Current production is wholly by Australian Blue Asbestos Pty. Ltd. at Wittenoom Gorge and has been in the order of 1,2,000 to 14,000 long t.p.a over the past six years.INTRODUCTIONThe Hamersley Ranges are located in the NW. Division of Western Australia and extend, approximately, from latitudes 21° 30' to 23°S and longitudes 117° to 1200 E. Their mean height above sea level is 2,000 ft, and they rise from 600 to 800 ft above the general level of the tableland which extends SE. from the coastal town of Roebourne.Mt. Bruce, the highest peak, is 4,024 ft above sea level. The ranges are intersected by numerous north-flowing streams, which are dry during the greater part of the year. These streams have carved deep gorges, and it is in these that the principal deposits of crocidolite outcrop.The presence of the mineral was first recorded in 1917, but the deposits remained untouched until 1937 when strong market demand for crocidolite resulted in considerable prospecting and mining activity, particularly in Yampire, Wittenoom and Dale's Gorges. It was established also that the blue asbestos belt extended from Willi Wolli Springs NW. to Millstream station, Le., over a length of 180 miles and a width of 20 to 30 miles. A number of attempts were made to develop and treat the Yampire and Wittenoom...

Jan 1, 1964

By B. W. Howlett, M. B. Bever, Somnath Misra

The heats of Formation of the compounds Sb2Se3, Bi2Se3, Sb2Te3, and Bi2Te3 and the heats of solution of tellurium and selenium in liquid bismuth have been measured in a liquid metal solution calorimeter. The heat capacities near the melting point, the heats of fusion, and the melting points of the two tellurides have been measured in a constant temperature gradient calorimeter. The thermo-dynamic quantities are interpreted in relation to the stability of the compounds and the nature of the solid-liquid transition. THE selenides and tellurides of several elements of Group VB of the periodic system are of interest because of their electronic properties. The compounds Sb2Se3, Bi2Se3, Sb2Te3, and Bi2Te3 are semi- conductors; they also have gained prominence in the fields of thermoelectricity and photoconductivity. However, little is known about their thermody-namic properties. As part of a research program on the thermo-dynamic properties of intermetallic compounds, the heats of formation of the compounds Sb2Se3, Bi2Se3, Sb2Te3, and Bi2Te3 were measured in a liquid metal solution calorimeter. The heat capacities near the melting point, the heats of fusion, and the melting points of the two tellurides were measured in a constant temperature gradient calorimeter. The results, in addition to their intrinsic interest as thermodynamic quantities, contribute to an understanding of the stability of the compounds and the nature of the solid-liquid transition. 1) EXPERIMENTAL 1.1) Materials. Samples of the compounds SbzSe3 and Bi2Se3 were prepared by melting the elements in stoichiometric proportions in evacuated Vycor capsules followed by quenchinn in water. They- were then annealed in vacuum for 12 hr at 550°C. A sample of Sb2Te3, consisting mainly of one large grain, supplied by the Lincoln Laboratory,

Jan 1, 1964

By Georg Petersen

El presente texto describe la historia del primer centenario de la industria petrolera peruana (1863 -1963). La revisión va desde la historia temprana del petróleo en la primera mitad del siglo XIX, desarrollo de la industria moderna del petróleo en el Perú hasta el estado actual de este.

Jan 1, 1964

By R. M. Rose, C. S. Tedmon, J. Wulff

It is frequently of interest to study the influence of small quantities of interstitial impurities on the properties of various refractory metals and alloys.

Jan 1, 1964

By James C. M. Li

James C. M. Li (Edgar C. Bain Laboratory for Fundamental Research)—Professor Weertman has suggested the interesting possibility that dislocation tangles are formed by helical formation of dislocations stopped by long-range stresses or by jogs. Such a possibility is similar to that of "mushrooming"374 in the respect that a dislocation must first be stopped and then interact with vacancies. The effect of short-range internal stresses which may exist at the time a dislocation is stopped has not been considered. It seems that the effect of these internal stresses may be just as important as, if not more than, that of the interaction with vacancies. The internal stresses produced by dislocations of

Jan 1, 1964

By R. B. Elver

The level of steel consumption per capita is one of the principal indicators of a country's standard of living. It is no coincidence that the materially advanced nations possess viable iron and steel industries to provide a reliable and economic source of steal for the manufacturing industries. No other metal is as dominantly important in manufacturing as steel. The blast furnace - steel furnace complex based on coking coal, ferrous scrap and iron ore - continues to be the principal steel-producing method. Less important is the electric furnace method based on scrap, In recent years, there has been considerable interest in the many direct reduction processes that are not dependent on coking coal but usually produce a product for further refining in steel furnaces. No matter which series of processes are used, iron ore is essentially the only source of virgin iron units. Thus, to such a vital and capital-intense industry as steel, access to a relatively inexpensive, long- term supply of iron ore is essential.

Jan 1, 1964

By H. L. Lovall

Huge banks of preparation plant refuse and other non¬saleable materials have accumulated over the years in all major United States coal producing areas. These banks, esthetically and commercially undesirable, can cause air and water pollution and land reclamation and mineral conservation problems for the industry and nearby communities Although some refuse banks have been reworked to recover saleable coal, all remain and accumulation continues. Even those previously processed continue as potential hazards. Among the several problems created by refuse banks, in situ combustion is most treacherous. Of the millions of tons of major accumulations, there are at least 450 refuse banks on, fire at this time Attempts to extinguish such fires are costly, impractical and generally unfruitful. Studies are in progress to evaluate the potential of processing such materials to eliminate the combustion capability and to yield usable fuel and nonfuel products. Aspects of the study now in. development for coal refuse include: (a) evaluation of characteristics (size, sink-float, ash, sulfur and calorific value) of the coal refuse materials which are known to be highly variable, (b) development of an ignition test having significance for in situ conditions, (c) study of processing capabilities (comminution for liberation, pilot plant washing tests), and (d) investigation of potentially significant properties of fuel and nonfuel products which could be altered to enhance their market potential.. Among the latter products are lightweight aggregate, fill for mine slushing operations, construction, etc: Plans are to extend the studies to include the design, erection, and test processing of refuse with a transportable plant,; which could provide basic economic and product utilization data from several locations

Jan 1, 1964

By C. B. Daellenbach, T. D. Tiemann

The prevention of quartz flotation by chelation of activating ions with the tetrasodium salt of EDTA in oleic acid flotation was investigated using a small vacuum flotation cell. It was found that flotation of quartz could be entirely suppressed in the presence of activating ions during complete flotation of hematite. It was further shown that the concentration of activating ions liberated from Wisconsin Gogebic taconite is sufficient to float quartz in an oleic acid system. Large tonnages of low grade siliceous iron ores occur on the iron ranges of the Lake Superior district. Although the lower grade nonmagnetic types are currently not of economic importance, they constitute a large future potential source of iron and steel, and hence have been the subject for extensive research on their beneficiation. TACONITES Of particular interest to the Dept. of Minerals and Metals Engineering at the University of Wisconsin have been the low grade nonmagnetic taconites of the Wisconsin Gogebic Range. These occur as five members of the iron formation and have been described in detail elsewhere.' Essentially they consist of an intimate mixture of hematite, goethite and quartz, with minor amounts of siderite, magnetite, iron containing silicates, and manganese minerals. A typical mean analysis based on the Bureau of Mines analyses' is: SiO2-52.50%, Fe2O3-43.40%, (Fe-30.38%), A12O3-1.15%, P2O5-0.07%, Mn2O3-0.29%, CaO-0.07%, (S-0.03%), Loss on ignition-2.00%. The quartz in these ores is of a microcrystalline variety,2 and so intimately associated with the iron oxide minerals that extremely fine grinding, in the order of minus 325 mesh, is required for liberation. During grinding and subsequent flotation, the concentration of quartz activating ions in the pulp becomes sufficiently high to activate quartz which floats along with the iron minerals in the presence of oleic acid. cook3 and co-workers concluded that oxidized iron ores released appreciable quantities of quartz-activating ions in water pulps. This is shown to be true in the present investigation. As a matter of fact, application of this phenomenon, as well as the intentional addition of activating calcium ions, is made use of in the an ionic flotation of silica from the iron oxide minerals.4,5 In view of the above, it becomes almost impossible to effect a sharp separation of quartz in the oleic acid flotation of the iron oxide minerals from these taconites, even with satisfactory liberation. This fact led to the current investigation to find a means of linking the activating ions with a chelating agent. The aim was to establish basic data for the quartz-water-oleic acid system which might not only be applicable to iron ores, but also to the flotation of other siliceous ores as well. EXPERIMENTAL METHODS Vacuum Flotation Cell: The vacuum flotation used in this investigation is similar to that used by previous investigators.6,7,8 The cell consisted of a 100 ml graduated cylinder with the lip removed. Vacuum from a water aspirator was applied to the cell through a trap; suitable tubing, and a rubber stopper inserted in the top of the cell. Constant absolute pressure was maintained by means of a manometer connected to the trap with a tee. Flotation: The required amount of activating ion solution was pipetted into a beaker. This was then diluted to 99.0 ml with water having a pH below that desired for the test, or so adjusted with HC1. After addition of 1.0 ml of oleic acid solution (2.0 mg oleic acid per ml), the pH was readjusted to the desired value with NaOH, and the entire solution transferred to the cell containing 1.5 gm of quartz. After vigorously agitating the cell and its contents for 2 min, the vacuum was applied to the cell and the estimated degree of flotation observed for a 3-min period. Activating ions studied included Ca++, Mg++, Al+++, and Fe+ + + added as chloride solutions. In addition,

Jan 1, 1964

By J. Wade Watkins

One potential peaceful application of nuclear explosives is stimulating the production of liquid or gaseous hydrocarbons from essentially nonproductive deposits of petroleum, natural gas, oil shale, and tar sands. Within the United States the appreciable difference between producible proved reserves and ultimate reserves and resources of hydrocarbon deposits is of such magnitude that much petroleum, natural gas, shale oil, and bitumen will not be produced unless significant technological progress is made in production techniques. The shattering effect of contained nuclear explosives and, to a lesser extent, the heat produced, have been considered as stimulative forces when the thickness, depth, and nature of such deposits permit considering the use of nuclear devices. Mechanical production problems would be less in an oil or gas reservoir than in an oil-shale or tar-sands deposit. Also, tar-sands resources in the United States may not be adequate to warrant serious consideration of applying nuclear-explosives stimulation. Gas reservoirs should present the least-radioactive-contamination problem. The technical feasibility of using nuclear explosives cannot be evaluated fully at present. Additional information is needed on the effects of pressure, heat, and radioactivity on the solids and fluids of hydrocarbon deposits, the nature and extent of induced fractures in different rock media, and the possibility of isolating and confining or removing radioactive contaminants. Final technical feasibility can only be determined by a field test. If technical feasibility is established, economic feasibility will depend upon the comparative cost of producing hydrocarbons by nuclear explosives and by conventional means. It is probable that an economic comparison would favor nuclear stimulation only where devices of relatively high yield could be used practicably and safely.

Jan 1, 1964

By W. D. Forgeng, P. F. Wieser

MnSi alloys containing from 2 to 24 at. pct Si have been investigated by metallographic and X-ray methods. Contrary to published data, the temperature of the ß-manganese to a-manganese transformation is lowered by the addition of silicon. The existence of two additional intermediate phases E and ( is demonstrated. E, ranging in composition from 12 to 15.5 at. pct Si, forms by a peritectoid reaction between ß manganese and the second new phase, (. The latter phase is homogeneous at silicon contents from 16.2 to 18 at. pct and forms peritectically from the 0 phase and liquid. The eutectic reaction occurs between the ( phase and MnsSi rather than the ß phase and Mn3Si. As a result of this investigation, a modification of the manganese-rich section of the MnSi equilihrium diagram is proposed. The binary diagram of Mn-Si, according to Hansen,' Fig. 1, exhibits in the low-silicon region (below 24 at. pct Si) a peritectic transformation at 900°C of 0 manganese + Mn3Si to a manganese as determined by R. Vogel and H. Bedarff2 as well as a thermal effect at 980°C between 16.2 and 22.6 at. pct Si reported by the same authors. The nature of the latter transformation was unknown. K. Amark, B. Boren, and A. westgren3 reported indications that possibly four more phases existed in the range of 10 to 27 at. pct Si. The present investigation deals with the phase relations in the range of 2.1 to 17.7 at. pct Si. A few spot checks were conducted up to 23.84 at. pct Si. EXPERIMENTAL PROCEDURE Small experimental heats were prepared by induction melting in a vacuum furnace using argon as a protective atmosphere. The crucible was of commercial-quality magnesia. The furnace charge consisted of silicon metal and dehydrogenated electrolytic manganese. The typical analysis for these materials is shown in Table I. The molten alloy was tapped into 2-in.-square, 7-in.-long ingots. After visual inspection, a small quantity of alloy in the middle portion of the ingot was separated for use in this investigation.MnSi alloys containing from 2 to 24 at. pct Si have been investigated by metallographic and X-ray methods. Contrary to published data, the temperature of the ß-manganese to a-manganese transformation is lowered by the addition of silicon. The existence of two additional intermediate phases E and ( is demonstrated. E, ranging in composition from 12 to 15.5 at. pct Si, forms by a peritectoid reaction between ß manganese and the second new phase, (. The latter phase is homogeneous at silicon contents from 16.2 to 18 at. pct and forms peritectically from the 0 phase and liquid. The eutectic reaction occurs between the ( phase and MnsSi rather than the ß phase and Mn3Si. As a result of this investigation, a modification of the manganese-rich section of the MnSi equilihrium diagram is proposed. The binary diagram of Mn-Si, according to Hansen,' Fig. 1, exhibits in the low-silicon region (below 24 at. pct Si) a peritectic transformation at 900°C of 0 manganese + Mn3Si to a manganese as determined by R. Vogel and H. Bedarff2 as well as a thermal effect at 980°C between 16.2 and 22.6 at. pct Si reported by the same authors. The nature of the latter transformation was unknown. K. Amark, B. Boren, and A. westgren3 reported indications that possibly four more phases existed in the range of 10 to 27 at. pct Si. The present investigation deals with the phase relations in the range of 2.1 to 17.7 at. pct Si. A few spot checks were conducted up to 23.84 at. pct Si. EXPERIMENTAL PROCEDURE Small experimental heats were prepared by induction melting in a vacuum furnace using argon as a protective atmosphere. The crucible was of commercial-quality magnesia. The furnace charge consisted of silicon metal and dehydrogenated electrolytic manganese. The typical analysis for these materials is shown in Table I. The molten alloy was tapped into 2-in.-square, 7-in.-long ingots. After visual inspection, a small quantity of alloy in the middle portion of the ingot was separated for use in this investigation.

Jan 1, 1964

The efficiency of water sprays in suppressing airborne colliery dust depends on many variable factors. A survey of previous work in this field shows that swirl spray nozzles are the best dust suppressors.Investigations carried out in an experimental dust chamber show that, in spite of limitations to the application of water sprays in underground use, promising dust suppression efficiencies in mechanised mining can be obtained with swirl spray nozzles.INTRODUCTIONA dust hazard has always been associated with coal mining, and the recent growth of mechanisation has resulted in a greater production of fine coal and dust, thus increasing the hazard. A better knowledge and appreciation of the medical aspects and dust explosion factors has led to practices reducing the seriousness of the problem. However, the dust hazard still exists and its control is basically an engineering problem.Dust, as with any atmospheric pollution, may be removed from the, mine by ventilation, which is an indirect method of control. Direct methods, in which the dust is prevented from being produced and from becoming airborne, should be employed where possible. Of these direct methods the most significant is the use of water sprays.THE DUST HAZARDAn appreciation of the physical nature of the more important dust hazards is necessary before considering the removal of the hazard. The main hazards associated with colliery dusts are the health hazard and the explosion hazard. "Dust" comprises solid particles of size minus 20 mesh Tyler (833 microns).

Jan 1, 1964

The principle activities of the Explosives Research Laboratory from July 1, 1961 to June 30, 1962, are described briefly in part 1. Part 2 gives short abstracts of publications that appeared during fiscal year 1962; in general, the research reported in these publications antedates the report period. Part 3 gives the results of an investigation which, although too limited to warrant separate publication, merits presentation in some detail because of current interest in ammonium nitrate-fuel oil compositions.

Jan 1, 1964

By W. A. Backofen, A. T. English

The kinetics of re crystallization were determined metallographically for a 3-1/4 pcl Si-Fe rapidly compressed at temperatures of 710° to 911°C, and held for various times at the working temperature. As in re crystallization following cold wwk, the time for re crystallization was reduced by increased temperature and strain. Nucleation occurred chiefly at grain edges, although other pre-existing interfaces, notably inclusions, also served as nucleation sites. The importance of intragranular nucleation to grain refinement in hot working is pointed out, together with some possible techniques by which nucleation might be induced within the grains. The observed isothermal growth rates are quite accurately described by the equation G = 4 x 10-'/t (cm per sec), independent of temperature and strain at all but the shortest times. Changes in G during recrystalliza-tion can exceed two orders of magnitude. It is argued that release of stored energy associated with lattice defects cannot adequately explain the time dependence. A suggested alternative involves processes of solute segregation and desegregation in the unrecrystallized matrix and at the moving boundary, respectively. EFFORTS to improve hot-working practice are hampered by an incomplete understanding of the fundamental metallurgy involved. Research directed at establishing the required basic foundation falls into two categories, the first concerned with measurement of mechanical properties under the conditions of high temperature and strain rate which characterize such processing, the second focused on structure and its relation to the deformation conditions. Rossard,' Rossard and Blain,2 and Hardwick and Tegart have conducted many high-speed, high-temperature torsion tests on various metals. One of their objectives was interpretation of stress-strain curves in terms of the structures of specimens rapidly quenched following interruption of twisting. They showed that appreciable hardening occurred in the early part of the test, and that this hardening reflected the concurrent development of an increasingly dense substructure within the grains. The detailed nature of this substructure was observed to depend on the ease of polygonization which, at least in fcc metals, varies with the stacking-fault energy.= By holding specimens after interruption but before quenching, the nucleation and growth of new grains could also be studied. Some success has been realized in relating the microstructure of hot-rolled steel to its temperature:strain rate:strain history with such testing.' The same general observations have been made by others investigating rolling4f5 and drop-hammer forging.~-~ Incident to these experiments, some efforts were made to determine the kinetics of re-crystallization as well as the velocity of the migrating boundaries. The results have been largely qualitative, owing to difficulties of interpreting hardness measurements5 and microstructures. The work described here was undertaken to obtain more quantitative information from tests on a material having suitable metallographic properties, and, in this way, to provide further insight into the fundamentals of this practically most important kind of deformation processing. I) MATERIALS AND EXPERIMENTAL TECHNIQUES Materials. Electrolytic etching of a Si-Fe alloy reveals dislocations and substructure in unrecrystallized grains.8'9 This unique characteristic makes possible a precise determination of the extent of recrystallization. For that reason, it was the material selected for all experiments in the present work. The two particular alloys that were used are identified in Table I. A major difference between "A" and "B" is the number of inclusions, as noted in the table. Most of the experiments were made with material "A". It was received as hot-rolled plate 1 in. thick, sawed to 2-in. widths, hot-forged at 1200°C to 5/8-in. rounds, and finally annealed in a mechanical vacuum at 1000°C for 24 hr. The result was substructure-free grains of mean diameter 0.05 cm.*

Jan 1, 1964

By J F. Davies

A review is presented of the fundamental differences between the Superior and Churchill geologic provinces. Structure, lithology, grade of metamorphism and a single recent age determination suggest that the Flin Flon -Snow Lake and Lynn Lake belts are remnant blocks of originally Superior rocks lying within the Churchill province. Major mineral belts occur along the main boundary between the Superior and Churchill provinces (the Thompson -Moak Lake nickel belt) and within the remnant Superior blocks inside the Churchill province (Fiin Flon -Snow Lake and Lynn Lake). During the Hudsonian orogeny, metamorphic gradients must have existed across the Churchill-Superior boundary and between the remnants of Superior rocks and the enclosing gneisses of the Churchill province. It is possible that not only the unusual nickel deposits of the Thompson belt but also the base metal deposits of the Flin Flon -Snow Lake and Lynn Lake districts are due to redistribution, or diffusion and migration of metals to areas of lower-grade metamorphism during the Hudsonian orogeny.

Jan 1, 1964