By J. P. Hansen

Wustite beds were reduced with carbon monoxide and mixtures of hydrogen and nitrogen in the temperature range 900° to 1,300° C to determine the effect of temperature, gas flow, and surface area on the rate of reduction to iron. The composition of the gas stream as it passed through the wustite bed was continuously measured with infrared absorption cells and heated-wire methods. The change in composition was used to calculate the reaction rates. Arrhenius plots of the data give heats of activation of 34 kcal for particles using CO, 27 kcal for particles using H2, 24 kcal for pellets using C8, and 6 kcal for pellets using H2. The velocity of reduction is dependent on the area of reacting interface and the driving potential of the gas (reducing gas concentration minus equilibrium concentration) as well as the exponential temperature effect. The reaction rate was independent of the gas velocity over the range of conditions studied.

Jan 1, 1965

By W. F. Chiao, R. B. Gordon

Tile sharp-yield point found in magnesium crystals in the solulion-treated and aged condition is studied by dislocation internal-friction experiments. The results show that the sharp yield is not file to the sudden release of pinned dislocations hut is movc likely due to the rapid multiplication of an initially small number of dislocations. Recovery or the dislocation internal friction after deformation is also studied. This yecovery results from the re-pinning of dislocations by a solute, presumably nitrogen, which moves with a relatively small activation energy. SHARP-yield points, when they occur, are a striking feature of the stress-strain curve generated during a tensile test. Although commonly associated with steel, sharp yielding has been found in a variety of metallic and nonmetallic crystalline materials. In particular, sharp-yield points have been found in zinc"' and cadmium3 containing nitrogen. With this background, Geiselman and Guy4 investigated the tensile properties of magnesium single crystals containing nitrogen to see if sharp yielding also occurs in this system. They found that sharp yields did indeed occur in solution-treated and aged specimens tested at elevated temperature but were not able to give conclusive proof that the sharp yield was caused by nitrogen, a yield drop being observed even in their purest crystals. Sharp-yield points have also been found in various polycrystalline magnesium alloys.7'8 In the study of the sharp-yield phenomenon it is desired to observe the behavior of dislocations in the earliest stages of the deformation process. Internal-friction experiments are useful for this purpose because dislocation damping is sensitive to the mobility of free-dislocation segments. At low strain amplitudes the damping, A, due to the the forced vibration of dislocation segments of average length L is ? =KAL4 [1] where A is the dislocation density and K, if the applied frequency is well below the resonant frequency of the dislocation segments? is a constant for the sample under observation.5 Dislocation damping, because of the fourth-power dependence on L, is particularly sensitive to the creation of free-dislocation segments during deformation. Since sharp yielding is associated with the sudden release of pinned-dislocation segments, marked changes in the dislocation damping are expected at the yield point.6 The use of the dislocation-damping observations to help elucidate the incompletely understood mechanism of yielding in magnesium is the primary objective of the experiments reported here. PROCEDURE Many investigations have shown that very marked and rapid changes occur in the dislocation damping of of a deformed material as soon as the straining is stopped.5 It was quite essential, then, for the purpose of this investigation, to make the damping measurements during the deformation of the samples. This can only be accomplished through the use of the ultrasonic-pulse method. In this method traveling sound-wave pulses are used and, in contrast to resonating-bar methods, only the sample ends are set in vibration. Thus, the sample can be gripped along its sides in the tensile-test machine without disturbing the damping measurements. In the pulse method, the decrease in the amplitude of a sound pulse is measured as it travels back and forth through the sample. If A is the amplitude after traversing a distance x and A. is the initial amplitude, A=Aoe-ax [2] and a is called the attenuation. It is commonly measured either in units of cm-I or as db per µ sec. The observed attenuation in a metal sample is due to a number of causes. These include scattering by grain boundaries and impurity particles, thermo-elastic damping, diffraction effects, stress-induced ordering of solute atoms, and dislocation damping. The total observed attenuation in a given sample usually cannot be resolved into these various components, but changes in a due solely to changes in dislocation damping can be accurately determined, provided the experiment is arranged so that all other sources of damping are held constant. It is desired to reduce the extraneous sources of attenuation to a minimum and for this reason the experiments are done on single crystals of high purity. Magnesium crystals offer the further advantage that, when properly oriented, only a single set of slip planes is active during deformation. Crystal Preparation. The method of sample preparation is similar to that of Geiselman and Guy.4 The starting material was high-purity, sublimed magnesium rod supplied by the Dow Chemical Co. Melting under Dow 310 flux was used to reduce the nitrogen content of the starting material: the fluxing was done under an argon atmosphere and the

Jan 1, 1965

By J. L. Brimhall

Slip-line formation during bending has been studied on neutron-irradiated molybdenum single crystals. For equivalent strains, the slip lines are coarse and distinct in the irradiated molybdenum and not resolvable in the unirradiated molybdenum. The slip lines have been directly correlated with dislocation channels present in the irradiated and deformed thin foils. The heterogeneous distribution of the dislocations during deformation in the irradiated material results from dislocation interaction with the dejects produced during irradiation. Impurities , in the form of' carbides, affected the dislocation channeling Principally by acting as dislocation sources. ALTHOUGH the mechanical behavior of irradiated materials has been studied extensively, the precise mechanism of irradiation hardening has not been established. Some information on the microstructural species responsible for hardening of irradiated materials has been derived from direct and indirect observations. The direct observation of the structure of deformed irradiated metals, particularly by transmission electron microscopy, is a relatively new and unexplored area. Slip-line studies in fcc metals have been restricted primarily to copper.1-3 Very coarse slip lines, representing slip on many closely spaced planes, have been observed in deformed, irradiated copper. Coarse slip lines have also been observed in irradiated aluminum.4 Clear channels in irradiated copper caused by dislocation motion through the defect structure have been seen by transmission electron microscopy and correlated with slip lines.5-6 To date, little work has been reported on the irradiated bcc metals. Eyre described the slip lines around hardness indentations on irradiated iron and found them to be more distinct than lines in unirradiated material.' Mastel et al.' have observed channels in deformed irradiated molybdenum similar to those reported in copper. As part of a program concerned with the effect of neutron irradiation on metals, the slip-line

Jan 1, 1965

By Barry Hunsaker

I cannot help but be reminded, as I stand here today, of my boyhood years and heritage, both of which are inextricably tied to this very valley and are, in a: bay, apropos of the theme of this Keynote Session. I remember the scarcity of people. For example, 48, 000 in Phoenix and 436, 000 in the State in 1930 and 65,000 in Phoenix and 499, 000 in the State in 1940. Today Phoenix boasts a population of over 500, 000 and the State a population of 1, 500,000. I remember the' lack of facilities, goods and services, including gas and electric power. I recall stories of my grandfather who had the freighting or teaming contract to haul all the supplies and generating equipment, by wagon mind you, up the old Apache Trail to Roosevelt Dam. . .a three day trip from the nearest railhead which, by the way, was not Phoenix, for it did not merit a railhead on those days, but the village of Maricopa approximately 25 miles south of Phoenix. I remember chopping firewood, heating wash water on an open fire in a No. 3 wash tub at the rear of the house and doing my school homework by the light of a kerosene lamp just 25 to 35 years ago within what is now a large metropolitan area

Jan 1, 1965

By Charles L. Bauer

WHEN a single crystal is annealed following plastic deformation recrystallization usually occurs rather than polygonization. Consequently, re-crystallization has received the overwhelming amount of attention albeit the intrinsic mechanisms by which dislocations rearrange and annihilate one another are just as well revealed by crystal polygonization. It is the purpose of this note to demonstrate the usefulness of studying the polygonization process by means of an etch-pit technique in sodium chloride. Sodium chloride deforms easily (the slip system is of the [110], (110) type), readily cleaves on (100) planes, and can be chemically etched so as to reveal the intersection of dislocations with a free surface. Thus it is possible to observe the distribution of dislocations after a crystal has undergone a specific deformation and annealing cycle. Various phases of the polygonization process

Jan 1, 1965

By H. H. Podgurski, Hsun Hu

Large cryslals of high-purily iron (99.996+ pcl) cannot be obtained by the usual strain-ameal technique. Repealed phase transformation by thermal cycling prior to crilical deformation improves the capabilily of cryslal growith but fails to yield satisfactory crystals. Imperfect columnar crystals can be produced by the phase-transition method. The addition of a small amounl (0.005 wl pet) of nilrogen IT was reported'-4 that for metals of very high purity the usual procedures of the strain-anneal technique fail to produce large crystals. This was eliminates practically all the difficulties in crystal growth by the normal strain-anneal procedures. An actual example is presented, showing that most parts of a strip have been converted into a large crystal by this method. The addition of nitrogen, which can be removed from iron with less difficulty, is believed to be more desirable than carbon additions for the same purpose. thought to be due to the strong tendency for recovery in the high-purity metals: hence the critically strained matrix undergoes polygonization instead of recrystallization upon annealing for crystal growth. Talbot1,2 succeeded in overcoming this difficulty by adding 0.03 to 0.04 pct C to high-purity iron before critical deformation. followed by annealing in hydro-

Jan 1, 1965

By L. F. Rooney

In June 1964 the Indiana Geological Survey discovered gypsum beds more than 10 ft thick in rocks of Devonian age in La Porte County, Ind. Although the extension of the Michigan Basin evaporites into northern Indiana has been recognized for some time, the gypsum beds have been regarded as either too thin or too deep for exploitation. Current Survey research, however, indicates that exploration by industry might find commercial deposits of gypsum less than 50 miles from Chicago. In four cores taken by the Survey within 1 sq mile in La Porte County, the maximum thickness of inter-bedded gypsum and anhydrite is 35.8 ft. Both gypsum and anhydrite beds contain irregular masses of limestone and dolomite that average a few inches in cross section and total about 20% of the rock by weight. The maximum thickness of gypsum in one minable unit verified by core is 12.5 ft, and its purity is 81.3%. Chloride content of the gypsum beds is less than 0.005%. Depth to the gypsum in La Porte County is 330 to 500 ft, about the same depth as the gypsum being mined in Martin County, Ind. In June 1964 the Indiana Geological Survey discovered gypsum deposits of probable commercial thickness near La Porte, Ind. (Fig. 1). This article presents preliminary data on the distribution, thickness, depth and chemical composition of the gypsum, the possible causes of gypsification, and economic considerations of immediate interest to industry. Because of the preliminary nature of the work, only a few geologic relationships concerning the genesis of the deposits will be mentioned. DEFINITIONS The following terms used throughout this article have been restricted to the following definitions: evaporites: anyydrite (CaSO4) or gypsum (CaSO4 . 2H2O). minable evaporites: any evaporite unit which may contain more than 80% evaporites, which is more than 10 ft thick, and which in places may be completely gypsified. PREVIOUS WORK The presence of gypsum and anhydrite in the Devonian rocks of northern Indiana has been recognized for at least 70 years1-4 and can be inferred from a number of reports on the geology of Michigan. For example, in a cross section from southwestern to central Michigan, Ells5 indicated the presence of

Jan 1, 1965

By Richard D. Miller

This publication contains routine analyses and related source data for 295 natural gas samples from 18 States collected during calendar year 1963 as part of a continuous survey of the United States for occurrences of helium in natural gas. This survey has been conducted by the Bureau of Mines since 1917. The analyses published herein were made by mass spectrometer and a special helium analysis apparatus, which are described in Bureau of Mines Bulletins 4863/ and 576.4/

Jan 1, 1965

By N. De Nevers

A calculation method has been developed for carbonated water flooding. This method takes into account the effects of oil viscosity reduction and oil swelling, due to carbon dioxide transferred to the reservoir oil from the carbonated flood water. It shows the effect of changes in carbonation pressure and carbonated water slug size. The method is based on a Buckley-Leverett-type linear flow model. The mathematical approach is similar to that developed by Welge, et al, for enriched gas drives. However, it contains a very important advance over the previous papers in its solution to the problem of injection of a "slug" of carbonated water rather than continuous injection of fluid of constant composition. The method also shows the chromatographic nature of the transport of Co 2 in a carbonated water flood. Sample calculations indicate that viscosity reduction is the most important source of incremental oil recovery. Swelling contributes to a lesser extent. Raising the carbonation pressure increases recovery, but this effect diminishes as pressure is increased. increasing the slug size also increases recovery, but again this effect diminishes as slug size is increased. INTRODUCTION In recent years there has been considerable interest in carbonated water flooding as a secondary recovery method. Several carbonated waterflood field tests are now in progress.1'3 Yet there is no published method for predicting the results of a carbonated water flood. This paper presents a method for predicting the oil recovery for ; carbonated water flood. In a carbonated water flood. a carbonated water slug is injected into the reservoir. Then this slug is driven forward by injecting plain water behind it. The field operator must choose the carbonated water slug size and the CO2:water ratio in the slug. The calculation method presented here shows the effects of both slug size and CO2:water ratio on oil recovery. The calculation assumes that the addition of carbon dioxide to flood water increases the oil recovery by two mechanisms: 1. Carbon dioxide transfers from the flood water to the oil, thereby reducing the viscosity of the oil. At the lower viscosity, the oil flows more readily and is more easily swept out by flood water. 2. The carbon dioxide which transfers to the oil phase causes the oil phase to swell. Assume that the residual oil saturation (volume per cent of pore space) is the same whether the oil is carbonated or not. Then the same volume will contain less stock tank oil if it is carbonated, due to oil swelling. The plain water driving the carbonated water slug forward will strip the CO2 out of this residual oil., causing this oil to shrink. This swelling-followed-by-shrinking leaves behind a lower residual oil saturation than would have been left behind by a plain water flood. Since some oils swell to almost twice their original volume at reasonable CO2 pressures, this effect may be large. Two additional benefits sometimes claimed for carbonated water flooding are: 1. Adding CO2 to flood water greatly increases the water injectivity in some cases.1 (Injectivity = BPD of water injected/ft of sand x differential bottom-hole pressure, psi.) CO2 forms a weak acid in water; injecting carbonated water is, therefore, somewhat like acid treating. If a formation responds to acid treating, it will probably have a higher injectivity for carbonated water than for plain water. Although the increased injectivity increases the profitability of a carbonated water flood over a plain water flood, it does not change the production curve based on total fluid injected. Therefore, the method presented here does not show any effect of increased injectivity. 2. It is claimed in one patent4 that carbon dioxide will react with some constituents of the oil to form detergents. These detergents are expected to increase the oil recovery. There is little data available to support this idea. The calculation method presented here takes no credit for extra oil recovery due to the formation of any such detergents.

Jan 1, 1965

By H. M. Otte, A. L. Esquivel

A new leasl-squares method is Presented for determining lattice parameters of hexagonal or tetragonul structures. The method is adapted for use on electronic computers and involves a reiterative procedure. The correction factor employed raries linearly with the lattice parameter, a (determined from the Brag, angle). In contrast, Cohen's method and recent modifications of it use a correction factor that varies incersely as the squure of the lattice paramneter, a. While the recent modifications attempt to improve the precision of the extrapolated lattice parameter, a, (or-cu). by stressing the importance of the weighting factor. the present approach emphasizes the need for choosing the correct extrapolation function. A comparison between the present method (the Linear method) and Cohen's method indicates that the Linear method may be more appropriale in certain cases. through a priori no critertion appears to he available for making a chorce between the methods. The size of hexagonal and tetragonal crystal lattices is determined by two parameters, a, and c,. Although in principle the two lattice parameters can be determined independently from reflections for which h - k = 0 and 1 = 0, respectively, in practice this may be inconvenient (because of the angular positions at which these reflections may occur) or not easily possible (because of low intensity). Furthermore, if a high precision or accuracy is required, the limited number of reflections of this type available, particularly in the high-angle region, is not sufficient for the necessary corrections (mainly due to absorption) to be determined with accuracy. Several methods1-7,11-13 have been proposed employing all reflections, to obtain the optimum values, a. and co, either by a trial and error procedure or a least-squares fit. Of the latter method, cohen's5 is the best known one since it provides explicit expressions for the optimum a. and c,. However, Cohen's method is only strictly valid if an extrapolation function is used that varies linearly with l/a2 or lie2 (see Section 3), a requirement that does not appear to be generally appreciated. On the other hand, all the better known and more widely used A recent trial and error method was proposed by Massalski and King8,7 who computed extensive auxiliary tables of axial ratios vs the functions A = [(4/3)(h2 + hk +k2) + l2+(a/c)2] and C = A(c/a)2 used in computing a and c values from the observed Bragg angles. These values of a and c were then plotted against a function which permitted linear extrapolation. As a criteria; for the "optimum" values, Massalski and King rely upon a visual fitting of the line through points representing reflections of low 1-index points to compute the extrapolated value of ao and high 1-index reflections to obtain CO. The successive computations and graphical plotting required to reach the "optimum" value are quite lengthy and tedious even on a desk calculator and no quantitative assurance is obtained of having in fact selected the optimum value.* If the method of Massalski and King is used on an electronic computer, then their published tables become redundant and a least-squares fit becomes a natural selection for the choice of optimum values. Such an approach will be called the Linear method. For work now in progress on the effect of certain physical variables on the lattice parameters of hexagonal crystals, it has become essential to determine the confidence limits of small changes in the lattice parameters. Since extrapolation functions that varied linearly with a and c actually also appeared to vary linearly with l/a2 or l/c2 when tested against published as well as our data, a comparison of Cohen's method and the Linear method was considered desirable (Sections 3 and 4). For the latter method an electronic computer was required since a reiterative procedure to obtain the optimum ao and co values had to be employed. The purpose of this paper is to describe the principles of the Linear method, illustrate its application, and compare it with Cohen's method. 1) THE LINEAR METHOD The standard practice in obtaining the lattice parameters in the Debye-Scherrer method is to

Jan 1, 1965

By R. W. Hertzberg, F. D. Lemkey, J. A. Ford

The effect oj unidirectional solidification upon the microstructural, crystallographic and mechanical characteristics of high -purity A1-A13Ni eutectic a1loy specimens has been investigated. varying the growth rate caused the morphology of the Al3Ni phase to gradually change from platelets to rods. In addition, the effect of increasing the rate of planar liquid-solid interlace movement is to decrease the Al3Ni rod diameter and inter-rod spacing. The platelets and rods grow approxinlately parallel to each other and are aligned in a faulted substructure. A single unique crystallographic relationship hetween the A1 and ASNi phases was found and may he descrihed as : interface {001} Al3Ni {331} Al and growth direction <010>Al3Ni || <110> Al The platelet interlace and the aligned rows of rods are both uniquely defined by the above statements. Alignment of the Al3Ni phase by unidirectional solidification has given rise to a threefold increase in strength over that exhibited by specimens with an as-cast microstructure. These results illustrate the possible use of this eutectic alloy as a zohisker -reinforced structure. It has been demonstrated by Winegard et al.,1 Kraft and Albrighht,2 Chilton and winegard,3 Chad-wick,4 Yue,5 Tiller,6 and others that a planar liquid-solid interface may be established in binary eutectic alloys by proper control of heat flow during the solidification process. The unidirectional movement of such an interface results in a eutectic mi-crostructure consisting of an essentially parallel array of the two phases over an entire ingot. Two dominant phase micromorphologies have been produced using this technique: that of substantially parallel alternating lamellae of each phase or long thin parallel rods of one phase imbedded in a continuous matrix of the other phase. While not all eutectics can be controlled in this manner, it has been shown that a "normal" eutectic may, under properly controlled conditions of purity, liquid and solid thermal gradients, and solidification rate, be forced to solidify with essentially parallel phase particles. Kraft and Albright2 have demonstrated that, when the growth rate is too rapid or when the thermal gradient in the liquid at the growing interface is too low, a layer of constitutionally supercooled liquid, formed by impurity build-up, will stabilize a cellular rather than a planar interface. The unidirectional movement of the cellular interface forms the macrostructure of eutectic colonies.7 Chilton,3 Chadwick,4 and Tiller,&apos; studying eutectics of zone-refined Pb-Sn, A1-CuAl2, Zn-Sn, and Cd-Zn systems, noted that in the absence of impurities a planar interface is stabilized even when rapidly solidified. Although it is generally agreed that impurities break down a planar interface to form the eutectic-colony macrostructure, at present the origin of the varying micromorphologies (i.c., plates or rods) in a given normal eutectic alloy is not completely understood. Tiller8 has predicted that the micromor-phology produced may be dependent on solidification rate (i.e., at fast rates a rodlike structure is preferred whereas at slow rates a lamellar structure should form), and also suggested that rod formation may be favored at large phase-volume ratios. yue5 has experimentally verified Tiller&apos;s prediction in the eutectic Mg-Mg17Al12 by observing a lamellae-to-rod transition with increasing growth rate where the phase-volume ratio was approximately 2.3:1. However, Hunt and chilton9 more recently unidirec-tionally solidified over a wide range of growth velocities six different eutectic systems with phase-volume ratios between 12:l and 2.7:1 and observed no lamellae-to-rod transition. chadwickl0 has proposed that the change in micromorphology in some eutectic alloys is due entirely to the presence of impurities and further states that the lamellar structure is the characteristic structure of pure eutectic alloys even when the phase-volume ratio is as great as 12:l. Kraft11,12 has shown that the parallel lamellae in certain eutectic alloys assume a unique crystallographic relationship during unidirectional growth. This preferred crystallography may be developed

Jan 1, 1965

Jan 1, 1965

By W. C. Hagel, H. J. Beattie

Phases present at 2200° and 1500°F (1204° and 816°C) were identified in sixty wrought developmental austenitic alloys possessing wide compositional variations. The bases were iron-, cobalt-, and nickel-rich as well as a base with equal parts of each. There are only two structure types previously not found in similar alloys, viz .-the Co3 W and the Fe3Al types. A molybdenum-rich monocarbide decorates dislocations with unusual clarity. Other results provide correlations between alloy composition and phas e precipitation. Grouping intermetal -lic phases into three general classes : I) geometrically close-packed, 2) topologically close-packed, and 3) bcc derivatives, the nickel base prefers the first, the iron base the second, and the cobalt base the third—each base tending to shun the other two classes. Thus, a crystal-chemistry effect previously noted by Laves and Wallbaum can he expanded for these Group VIII elemental bases. There appear to he no quaternary or higher -order structure types requiring more than three atomic species. AFTER studying aging reactions in many diverse commercial austenitic alloys1-4 as a function of detailed time-temperature variations in heat treatment, it became apparent that matrix composition influenced structure types and morphologies to a large extent. These tendencies were related4 to a crystal-chemistry effect uncovered by Laves and Wallbaum.5,6 We have now directed our efforts to exploration of the whole ternary field, covering the standard base elements—iron, cobalt. and nickel— with 10 to 20 pct Cr and moderate amounts, up to 10 pct, of the usual alloy additions. Solutioning and aging treatments were held constant with major emphasis on X-ray identification of microconstituents. The possible existence of exceptions to the Laves-Wallbaum effect, or any new phases, was sought. Phases appearing in austenitic alloys can be classified as geometrically close-packed (gcp), octahedral or nonoctahedral interstitial compounds, topologically close-packed (tcp), semicarbides, and bcc derivatives. Crystal structures of the first four classifications can be visualized as a dense packing of semirigid spheres of different sizes, while the bcc derivatives represent a less efficient packing of spheres. The Laves-Wallbaum effect involves the gcp and tcp phases. Gcp phases possess both tetrahedral and large octahedral interstices; examples are Ni3Ti(n), NiSAl(y&apos;), Co3W(E), and other ordered AB3 compounds where B atoms are smaller than A. Their precipitation is primarily intragranular, presumably coherent with an austenitic matrix, and a chief source of strengthening. Most octahedral interstitial compounds (e.g., CbC, Tic, TiN, Mo2C) have a gcp lattice of large metal atoms which accommodate small carbon or nitrogen atoms in the octahedral interstices. The compound Ti2SC, previously designated Y phase or T phase, can, with some reservation due to its partial co-valency, be placed in this category.7 The nonoctahedral interstitials (e.g., M7C3, Fe3C) represent close-packings of spheres in structures that provide larger triangular-prism interstices for carbon, since the octahedral interstices formed by chromium and iron atoms are too small. Tcp phases possess only tetrahedral interstices; examples are Laves (Fe2Ti, Fe2Cb, Fe2W...AB2), p(Fe7MO6, Co7W8.... A8B7), and (FeCr, Co2Cr3)

Jan 1, 1965

By R. L. Grunes, F. K. Kies, C. D&apos, Antonio

THE several studies concerned with the annealing of thin nickel films have largely been restricted to films of a single thickness.1-4 It is well-known, however, that both physical and mechanical properties depend upon film thickness.5, 6 The strength-thickness relations found in vapor-deposited nickel films in the annealed and as-deposited states, as an example, are at least partially due to the density and arrangement of imperfections within the films.7, 8 For these reasons, the annealing characteristics of thin nickel films as a function of thickness were investigated. Electrical resistance was chosen to monitor annealing behavior since resistance changes are partially dependent upon defect structure. In addition, the equations predicting film resistivity as a function of thickness are already available.9, 10 Further advantages afforded by electrical-resistance measurements are its adaption to continuous readings during annealing and its relative simplicity. Nickel films were vapor-deposited, at average rates of 60Å per sec, on Vycor substrates held at room temperature in vacuums of about 10-5 torr. Afterwards, deposition-thickness measurements were made using a multiple-beam interferometric technique. A more detailed description of deposition procedures and the interferometer appear elsewhere.7, 8 The four-probe method was employed in measuring electrical resistance since this technique measures film resistance without contributions from lead wires and contacts. Resistance measurements were made before, during, and after annealing to temperatures of 700°C under vacuums of approximately 10-4 torr. Measurements were made every 25°C or more often when necessitated by unusual resistance changes. Cooling and heating rates were maintained at approximately 5°C per min. Typical resistivity vs temperature curves are shown in Figs. 1 through 4. It is apparent from these

Jan 1, 1965

By R. H. Barham, G. W. Nabor

Linear aquifers, either limited or essentially infinite, may be encountered in reservoir engineering practice. In areas where faulting fixes reservoir boundaries, the fault block reservoir may have an aquifer of limited extent whose geometry is best approximated as linear. An infinite linear aquifer can occur as a regional feature whenever water movement through the aquifer member is constrained to one direction. Such constraints can arise from major faults, facies changes or pinchout of the member. Miller* pointed out that linear aquifers have received only meager attention in the past. He analyzed the performance of finite and infinite aquifers, developed working equations and curves, and presented examples. While Miller&apos;s curves may be used fairly easily, a separate one is required for each size of aquifer. In this paper, Miller&apos;s equations have been used as a starting point. By modifying them slightly, they can be reduced to a form which yields a single working curve, applicable to any size of aquifer. Thus. interpolation between curves is eliminated and accuracy is improved. Miller&apos;s results for finite aquifers covered only the boundary condition of no flow across the outer aquifer boundary. This paper also includes the case of constant pressure at the outer aquifer boundary.

Jan 1, 1965

By M. C. Lavine, H. C. Gatos, R. S. Mroczkowski

The structure of GaAs-Ge heterojunctions prepared by a back-melting process was studied by X-rav diffraction, melallographic, and electron-micro-analyzer techniques. The boundary region between the GaAs and the germanium was found to consist of a four-layered band. A discontinuity between the two inner bands was brought about by solidification occurring simultaneously from the GaAs and the germanium side. The junction material OH either side of the central discotinuity was found to have grown as a single Crystal with the orientation of the parent substrate. It was found essential to determine the GaAs-Ge phase diagram. This was accomplished by a series of alloys containing 0 to 40 wt pet GaAs. Over this range the diagram is a simple eutectic with the eutectic point at 74 wt pet Ge and 845 C. The limiting- solubility of Coils in germanium was found to bc less than 5 wt pet. The Kossel divergent-beam X-ray technique was used to study orientation relationships across the boundary lager. A great deal of effort has been recently expended on the electrical properties of heterojunctions. Little attention, however, has been given to the metallurgical variables which may be of importance in the formation of the junctions. The present work was undertaken to investigate some of the more pertinent metallurgical aspects of interface-alloyed GaAs-Ge heterojunctions. Such parameters as solidification processes, composition gradients, orientation effects, and the accommodation of crystal structures have been the objects of study in this program. EXPERIMENTAL PROCEDURES Phase Diagram. The phase diagram of the GaAs-Ge pseudobinary system was determined by means of cooling curves. A Bridgeman furnace was employed with the center section maintained at 1200°C and the upper section at 800°C. Melts varying from 0 to 40 at. pct in GaAs content were used. Each charge was incapsulated under a two-thirds atmosphere of argon in a carbon-coated quartz tube. Five min in the furnace hot zone provided rapid melting and homogenization. The capsule was then removed to the cooler portion of the furnace. Cooling times were of the order of 3 min. The resulting homogeneous microstructure indicated that equilibrium conditions were obtained by this procedure. Formation of Heterojunctions. Rectangular parallelepiped single-crystal samples were cut with the large faces of either the (l00), (110), or (111) orientation. The remaining four surfaces were also cut to specific orientations to permit accurate relative orientation of the GaAs-Ge pairs. The

Jan 1, 1965

The principal activities of the Bureau of Mines Explosives Research Center from July 1, 1962, to June 30, 1963, are described briefly in part 1. Part 2 gives short abstracts of publications that appeared during fiscal year 1963; in general, the research reported in these publications antedates the report period.

Jan 1, 1965

By Forrest T. Moyer

THE SAFETY record of the mineral and mineral-fuel-mining-and-processing industries retrogressed slightly in 1964, as indicated by the 3-percent increase in the frequency rate of all injuries. A slight improvement in the fatality rate was more than offset by the less-favorable rate of occurrence of nonfatal injuries. The overall-operating activity of these industries was lower in 1964 as measured by slight declines in employment and total man-hours of worktime. Injury Experience.-The rate of occurrence of all disabling work injuries in the mineral industries was 18.00 per million man-hours. This overall rate in 1964 comprised frequencies of 0.29 for fatal injuries and 17.71 for nonfatal work disabilities, which compared with respective rates of 0.30 and 17.20 in 1963. Fatalities totaled 538 or 30 less than in 1963. However, the total nonfatal disabilities of 33,151 in 1964 was 492 higher than in the preceding year.

Jan 1, 1965

By Mulligan John J.

The Bureau of Mines investigated lode tin deposits on Potato Mountain, Seward Peninsula, Alaska. Tin was found to occur as cassiterite associated with quartz, tourmaline, pyrite, arsenopyrite, and earthy clays, but the deposits lack the varied accessory minerals commonly found in tin districts. The tin-bearing deposits are in metasediments along minor breaks and bedding planes but not in the crushed earthy filling of major faults. Cassiterite and sulfides occur with quartz in veins, both with and without earthy clays, and disseminated through tourmalinized wall rocks. The deposits are characterized by irregular segregations containing 1 to 10 percent tin within zones averaging not over 0.25 percent tin. The largest segregation exposed is on the summit of a low hill on the east-central slopes of Little Potato Mountain; most of the outcroppings are in an area trending east to west, roughly 10 to 30 feet wide and 300 feet long. Sample values ranged as high as 12 percent tin, but the average grade may be about 1 percent tin. The extreme irregularity of both grade and composition precludes a more exact determination. Similar concentrations are scattered for over 1,000 feet to the west and north, but these are smaller and lower in grade. Elsewhere on Potato Mountain, generally similar deposits occur as clusters of veinlets at widely separated points in the metasedimentary walls of major faults.

Jan 1, 1965

Of the twelve known ore zones on the Sunro property, acquired by Cowichan Copper Co., only the "B" and "C" orebodies of the "River Zone" had been explored sufficiently to indicate the grade and tonnage. The "B" zone was selected for initial production. The portion of this orebody above the main adit level was developed for horizontal-ring, longhole mining. Ore from the stope would be scraped directly to the coarse ore bin. The lack of a suitable mill site on surface, as well as the 8,000-ft. tramming distance, led naturally to the installation ground. I N November, 1960, a lease was obtained by Co-wichan Copper Co. Ltd. (N.P.L.) from Sunro Mines Ltd., covering the main ore (River) zone of the Sunro property. A total of twelve zones had been located on the property. Nine of these lay within the leased area. With the exception of the "B" and "C" orebodies of the River Zone, there had been insufficient exploration for tonnage and grade calculations. Exploration by previous companies had

Jan 1, 1965