By H. G. Iverson

The effects of adding boron and boron plus carbon to electrorefined vanadium were evaluated with respect to mechanical properties at low temperatures and response to heat treatment. Grain size was significantly decreased with the addition of 0.05 percent boron, the decreases ranging from 30 percent at 800° C to 75 percent at 1,100° C. Increasing the boron content resulted in only a small increase in strength at room temperature, but at 77° K, boron contents of 0.005 to 0.076 percent increased the yield strength of vanadium over 50 percent, from 70,000 psi to 110,000 psi. When boron and carbon were present together, the individual grain-refining effects obtained with either element were retained. Approximately a twofold increase in strength was obtained by age-hardening the alloys containing both boron and carbon. Alloys with only boron additions did not age-harden.

Jan 1, 1968

By D. A. Woodford

In a constant-load creep test, if the density of nlobile dislocations is assumed constant for strains exceeding that corvesponding to the minimum creep rate, it is shown that the creep rate may be approximated by the equation where E is the nominal strain, o0. is the initial stress, and a' the stress fov unit dislocation velocity. The constant C contains the mean density of mobile dislocations and n is a measure of the stress sensitivity of dislocation celocity. This equation is shoum to be applicable to published data on an alloy steel and on nickel. The degree of plastic instability and hence the creep ductility is dependent on the calue of n for these materials. When instability becomes gross and local macroscopic necking occurs, the assumptions are no longer valid. On the basis of this equation, and the strain-time relation derived from it, a method of predicting the creep behavior at different stresses is suggested. MOst analyses of creep data have been concerned with time-dependent transient creep or time-independ- ent secondary creep in constant-stress tests. The far more widely used constant-load test has been neglected in terms of a mechanistic approach. In general, since the strains involved are usually small, the same laws for transient creep may be applied to both types of tests. However, there is no steady-state creep in a constant-load test since the stress increases continuously. Any apparent steady state observed on a strain-time plot is either fortuitous or illusory, and is generally revealed as a continuously varying creep rate on a carefully constructed strain rate vs time plot.* Transient creep may be understood in terms of a simple differential equation representing the change in mobile dislocation density with time:' where p is the density of mobile dislocations. The first term on the right is related to first-order kinetics of dislocation multiDlication and the second to second-order kinetics of exhaustion. On the basis of this equation, several authors2-4 have found good agreement with experimental transient creep curves for a number of materials. When k1p = k2p2, a steady-state creep

Jan 1, 1968

By Arnulf Muan, R. E. Johnson

Equilibrium CO2 /CO ratios of a gas phase coexisting with selected oxide phase assemblages of the system CaO-"Fe0"-SiOz and vnetallic iron have been determined at 1080°C. The data obtained are used to calculate activity-conzposition relations for metasili-cute, orthosilicate, and CaO- "FeO" solid solutions, and to determine a new value for the free energy of formation of C&S&0,. The metasilicate solution is practically ideal, whereas large deviations from ideality exist in the othe,r two solid solutions. BECAUSE of the geochemical and metallurgical importance of the oxides CaO, "FeO", and SiOz, the system CaO-"FeO"-SiO2 has been the subject of several experimental studies during the past 30 years. Following the delineation of phase relations at liquidus temperatures by a group of investigators at the Geophysical Laboratory of the Carnegie Institution of Washington in 1933,1 Chipman and associates in the early forties2,3 determined activities of FeO in liquids of this system. Since that time, many attempts have been made to interpret the data of Chipman et al. in terms of the constitution of the silicate liquids and the interaction parameters among the various constituents of the system (see for instance papers by Richardson4 and by Flood and coworkers5). One of the assumptions made in some of these interpretations4 is that the binary silicate systems CaSiO3-FeSiO3 and CazSi04-Fe2SiO4 mix ideally in the solid state. The objective of the present study is to provide experimental data on activity-com position relations in solid solutions of the system CaO-"FeO"-SiO2. Such data will contribute toward an understanding of the thermodynamics of silicate solid-solution phases in general, and will serve specifically to confirm or refute some of the assumptions made in interpreting liquid slag behavior. PREVIOUS WORK Phase relations in the system CaO-"FeO"-SiO2 in contact with metallic iron were determined by Bowen, Schairer, and Posnjak,1 and additional phase-equilibrium data for this system have been presented by Allen and snow.' A reproduction of the most up-to-date phase diagram for this system is shown in Fig. 1.7'8 Of particular interest in the present investigation are the relations among the various crystalline phases slightly below the lowest solidus temperature in the system, as shown in Fig. 2. The present work will be concerned primarily with some of the composition

Jan 1, 1968

By F. E. Rizzo, L. R. Bidwell, D. F. Frank

THE use of galvanic cells for the determination of oxygen activities has spread rapidly since the suitability of calcia-stabilized zirconia as a solid electrolyte material was first demonstrated by Kiukkola and Wagner.' In many of these investigations:-7 including several at ARL, the free-energy changes for various oxidation-reduction reactions involving the oxides FexO, NiO, and Cu2O have been measured as a means of assuring that a cell apparatus is functioning properly. As a result, a large quantity of data pertinent to the calculation of the high-temperature standard free energy of formation (?GO) of these oxides has been accumulated. AGFexo has been carefully measured in many independent investigations, using a variety of techniques, and consequently is accurately known. chipmans has used this informa-

Jan 1, 1968

By John D. Corrick

A dilute sulfuric-acid leach was developed for extracting lead and copper from lead blast furnace mattes and the chemistry was defined. The possible application of Ferrobacillus ferrooxidans to the problem of salvaging lead and copper from blast furnace mattes was also investigated. Operating conditions were varied to determine their effect on the oxidation and hence extraction of lead and copper from the matte. Conditions varied were temperature, pH, reaction time, aeration in the slurry, and particle size of the matte. A set of optimum conditions were developed that resulted in maximum lead and copper sulfide oxidation. Tests employing these optimum conditions resulted in 82.3 percent of the lead and 98.7 percent of the copper being extracted by a dilute acid leach, while maximum lead and copper extracted using F. ferrooxidans was 69.8 percent of the lead and 78.4 percent of the copper. Tests conducted with a different sample of blast furnace matte indicated that the dilute acid leach might have wide application in extracting lead and copper from other such blast furnace mattes.

Jan 1, 1968

By C. S. Sivaramakrishnan, Manjit Singh, Rajendra Kumar

Regarding liquid nzetals structurally as a suspm-sion of clusters , having derivated solid-state coordination, in truly liquid atoms, the recently developed Kuvlar-Samarin technique of centrifuging- in liquid state enabled the determination of the cluster sizes inAl-Cu mid Pb-Sn systems. It is shown that the colutne fraction of the clusters does not exceed 9 pct and the energy of their formation in Al-Cu is about 5.5 kcal per g-atom and in Pb-Sn eutectic alloys about 25 kcal per y-atoni. STRUCTURAL investigations of liquid state have principally followed the following three courses: i) studies with X-ray, electron, or neutron diffraction; these investigations have shown that there is a certain amount of regularity in the structure of liquid metals which can be defined by a coordination number and that the structure is a derived function of that in the solid state; ii) thermodynamical investigations which are based on the concept of ideal behavior; these describe the liquid state in terms of free-energy values and other thermodynamic functions; although these investigations are of help in the study of the general effects of alloying, they do not provide any structural insight into the precise atomic distribution in liquid state; iii) measurements of surface tension and viscosity; although it is natural to expect that the viscosity is related to the structure in liquid state, these investigations have so far only provided information which can be used by the foundry technologists and has been little utilized in formulating models of the structure of liquid state. As it happens, investigators in the three groups have worked almost independently of each other and there is practically no structural correlation between the results of one group with those of another. The purpose of the present paper is to indicate that the experimentally measured parameters of these three groups of research are closely related to the structure in the liquid state. STRUCTURE OF LIQUID METALS Although atomic distribution in solid and gaseous states is rigorously known, that of the liquid state is only appreciated on the fringes. There is no universal model of atomic distribution in liquid state, but two diverse models are at present hotly contested. The first, largely expounded by ~ildebrand,' regards the liquids as condensed gas since many of their properties and much of their behavior can be adequately described by regarding them as fluids. The second mode12j3 considers that some form of near-solid as- sociation of large number of atoms exists in the liquid state. On the other hand, ~ernal' was able to predict rather precisely the radial distribution functions in liquids on the basis of statistical geometric approach which considered that liquids are "homogeneous, coherent, and essentially irregular assemblage of molecules containing no crystalline regions or holes large enough to admit another molecule". He introduced the concept of pseudonuclei in the otherwise random structure as aggregates of closely packed tetrahedra which gradually merge into irregularity and continually replace each other. To what extent the pseudonuclei can be regarded as regions of near-solid association is indefinite but Bernal suggested that the concept of pseudonuclei can be compromised with the latter model if the near-solid associations are regarded as extremely dense and not necessarily crystalline. The difficulty in projecting the structure of liquid metals arises because they exhibit duplicity of character as some of their properties are closer to those of crystalline solids and others to fluids. There is an increasing tendency to discuss the structure of liquid metals in terms of the second concept according to which the structure of liquid metals may be conceived as consisting of i) clusters of atoms where the aggregation is a close derivative of that in the crystalline state, ii) individual atoms which behave like true liquids in respect to degrees of freedom and iii) excess number of vacancies. It is noteworthy that the introduction of only 5 pct vacancies is sufficient to transform crystalline matter into the liquid state. At any instant of time thermodynamic equilibrium exists between i, ii, and iii, but the relative proportion of the clusters and random atoms is not known. That this is so can be appreciated by the fact that, when liquid metal is rapidly cooled, liquid state vacancies may condense in the form of dislocation loops and vacancies in excess of their equilibrium number in solid state. These dislocation loops have been observed in thin foils of aluminum prepared from rapid cooled aluminum. As temperature increases above melting point the number and volume fraction of clusters decrease but those of vacancies and random atoms increase. Clusters are transient in nature. In pure metals the cluster is an aggregation of the metal itself. In alloys, however, the nature of the cluster largely depends on the interaction between solvent and solute atoms. If the interaction between unlike atoms is greater than between like atoms: the clusters are then aggregates of unlike atoms. Examples of this kind of system are A1-Cu, Mg-Pb, and so forth, i.e., systems which exhibit negative departures from the Raoult's law. In systems where the interaction between unlike atoms is smaller than be-

Jan 1, 1968

By William S. Miska

The study is an economic evaluation of historical, current, and projected refractory uses in the iron and steel industry of the United States. The first part of the report presents a refractories classification and identifies principal trends in the refractories industry; such as, value and volume of shipments, prices of finished refractory products, the number of manufacturers and plants for refractories production and marketing. The main part of the report treats refractory use patterns and technologic developments affecting refractories usage in the iron and steel industry. Changes in use patterns in each furnace type, refractory, and installation costs and the future outlook for refractories in ironrnaking and steelmaking are covered. The last part of the report identifies the principal raw materials used in refractories production and treats trends in refractory raw material consumption. An appendix to the report contains historical time series graphs of shipments of refractory types used primarily by the iron and steel industry and principal refractory raw materials sold or used by producers. An equation of the line of best fit was calculated from the earliest to the latest year in each time series, usually 1950 to 1965; these were extrapolated in order to derive volume estimates for the year 1975.

Jan 1, 1968

By Hillary W. St. Clair

Reaction rate coefficients were determined from analyses of the effluent gas for the reduction of granular ferrous oxide to metallic iron by passing carbon monoxide through a packed bed of oxide at a controlled rate in the temperature range 1,000° to 1,300° C. Coefficients were determined by the comparison of observed analyses and calculated analyses using a mathematical model that takes into account the nonuniform composition of both the solid oxide and the gas. A method is also given for finding the value of the rate coefficient that best fits the observed data.

Jan 1, 1968

By N. A. Gjostein

The real and apparent dependence of the surface self-diffusion coefficient, Ds, of gold on crystallo-graphic orientation has been investigated by isolated scratch smoothing and grain boundary grooving experiments. No systematic variation of Ds with orientation was found along the [100] zone. In view of the experimental scatter in these results, however, only aniso-tropy ratios, p, greater than -1.3 would be detectable. Anomalously low values of Ds were found on the [0ll] and [110] zones when the diffusion direction lies along (the scratch or grain boundary groove is perpendicular to) these zones. By comparing these results with a previous y plot study of gold, it is hypothesized that this is not an intrinsic diffusivity effect, but rather it results from a decreased driving force for mass transfer at orientations where the y-plot curvature is negative and appreciable in magnitude relative to y. The characteristics of this type of anisotropy do not appear sEVERAL investigations1-7 have dealt with the anisotropy of the surface self-diffusion coefficient, Ds, of metals as measured by the decay of single or multiple to be in agreement with the hypothesis of fast diffusion along ledges in the surface structure. In certain cases the Fourier method of determining Ds, described in Paper I of this series9 was compared with the second moment analysis in order to determine whether or not the method of analysis affects the anisotropy ratio. While the type of analysis does influence the magnitude of the anisotropy ratio, this effect is not associated with the shape of the profile, but rather is connected with the iterative volume diffusion correction used in conjunction with the second moment analysis. It is further demonstrated that the volume diffusion correction can be too large by either method when the y-plot curvature effect is large. Certain orientations exhibit an unusual temperature dependence of Ds ; this is discussed in terms of the y-plot curvature effect and/or the influence of impurities on Ds . scratches in the surface. Depending on the system investigated, both large1"3'6'7 and small4'5 anisotropies in Ds have been found. Although adsorbed impurities undoubtedly play an important role in determining the magnitude of the anisotropy,8 there are other factors that can give rise to an apparent anisotropy in Ds, thus obscuring the true nature of an intrinsic anisotropy in

Jan 1, 1968

By R. B. Tippin

Research investigations conducted on five ore samples show the applicability of heavy liquid separation (HLS) techniques to mineral processing. Under proper operating conditions, semicontinuous tests in small fluid cyclones yielded 90 percent sink-float concentrates with recoveries exceeding 90 percent on minus 35-mesh ore samples of kyanite, potash, spodumene, fluorspar, and beryl. Although none of the ores were examined in detail, their response to this novel concentration method provides basic examples that are typical of the process. Various aspects of cyclone design and operational characteristics of heavy liquid cyclone circuits were studied which demonstrated the flexibility of HLS by using multiple units connected in series. A comparison of two heavy liquid solutions, tetrabromoethane and methylene bromide, exhibited their individual advantages and limitations. Unique problems relative to this process are discussed including liquid viscosity, mineral composition of the ore, toxicity, and material handling hazards.

Jan 1, 1968

By P. S. Rudman

The solubility limit and the diffusivity of carbon in molybdenum have been obtained by duffising carbon into molybdenum rods from a Mo + Mo2C powder mixture. The solubility limit was taken as the long-time asymptotic limit of the rod composition. The diffusiv-ity was obtained from fractionally saturated rods from the rate of change of the average composition. Compositions were determined by chemical analysis. The solubility limit obtained is: WhILE the Mo-C system is important in refractory alloy technology neither the solubility limit nor the diffusivity of carbon in molybdenum is unambiguously known. In Fig. 1 the Mo-C phase diagram is presented. The heavy lines, the terminal solution solubility limit, and the eutectic temperature are results of the present investigation and will be discussed in detail later. However, it is readily seen that the previously published solubility limit determinations, Few and Manning1 and Fromm and ROy2 differ by up to an order of magnitude. The general form of Fig. 1, the Mo2C field, and a eu- tectic temperature -2200°C are due to an early Investigation by Sykes et a1.3 Although they did not determine the solubility limit, they did establish that the maximum at the eutectic temperature was about 1000 ppm. The only other prior data found on the solubility limit is from a lattice-parameter study by Speiser et a1 .,4 from which it can be concluded that the maximum solubility is greater than 1800 ppm. There does not appear to be any data oh the diffusivity of carbon in molybdenum. However, Samsonov and Epik5 have determined, from the rate of growth of an MozC layer, the diffusivity of carbon in Mo2C, and this has been erroneously interpreted, for example by ~c~eil,' as applicable to diffusion of carbon in molybdenum.

Jan 1, 1968

By F. W. Wood

The use of consumable.-electrode arc melting as a production technology is growing. One advantageous feature of this process is that it avoids ingot contamination by soluble crucible materials by employing a chilled metal crucible. Because the thermal balance under these conditions is rather delicate and does not necessarily provide a favorable environment for solidification, catastrophic imbalances can occur. The effectiveness and mechanistic roles of various factors are mostly unknown, and more intelligent insight regarding the distribution of temperature and heat is needed. Experience has provided several pertinent observations, some of which are quite superficial. The most meaningful data have resulted from studies of molten pool shapes and sizes and from measurements of heat flow through crucible walls. Overall experience, intuitively interpreted and supplemented, is sufficient nevertheless as a basis for a boundary-value treatment of the problem. A mathematical analysis based on a separation of variables, using conventional differential equation methods, provides a useful solution. For a cylindrical ingot, the temperature varies as a Bessel function of an argument proportional to the radius and as an exponential function of longitudinal position. Trial calculations using the problem solution seem to verify the general correctness of the result as compared with experience. The role and nature of solution parameters are also clarified, though not entirely resolved. It is revealed that the barrier to heat flow at the ingot-crucible surface has a prominent influence. Utility of the model embodied in the problem solution is readily demonstrated by considering a variety of contemporary questions about arc melting, and it is hoped that utility can be enhanced by improvement of the model.

Jan 1, 1968

By R. M. Hays

Prior to use of this model siphon finisher, the only means of evaluating metallurgical performance of the siphon finisher was by pilot plant studies. These are costly and require large quantities of material. A model siphon finisher and a test procedure which permits the evaluation of siphon finisher metallurgical performance has been developed. Metallurgical results between the model siphon finisher and pilot plant or commercial units show fairly good correlation. The upgrading of magnetic taconite concentrates by hydraulic concentration has been practiced for several years. In the 1940's, Braund1 used a multistage upflow classifier to upgrade magnetized magnetic concentrates. In present taconite plants, the SiphonSizer, marketed by Dorr-Oliver, Inc., has been particularly suitable for upgrading magnetic concentrates. When the hydraulic SiphonSizer is used to upgrade the concentrates in the finishing portion of the overall flowscheme, the unit will be called a siphon finisher to distinguish this application from classification. Prior to this work the only means of evaluating the metallurgical performance of the siphon finisher was by pilot plant studies which are costly and require large quantities of material. Therefore, it was desirable to develop a model siphon finisher and a test procedure which would simulate siphon finisher performance and require only small samples of material. This model would permit the evaluation of small samples such as drill core samples and be useful in evaluation of commercial siphon finisher design and performance. THE SIPHON FINISHER The siphon finisher, as shown in Fig. 1, is a tank equipped with a system of water jets which distribute the hydraulic water uniformly across the bottom of the vessel with an energy release for agitation in the teeter bed. The feed to the siphon finisher is intre duced through a feed well in the center of the unit. The silica and middling particles overflow a peripheral weir into the overflow launder. The magnetite fraction is discharged by a siphon or a modulated discharge valve. The siphon or the discharge valve is usually operated automatically by a float assembly which is responsive to the depth of the teeter bed. Various interface sensing devices have also been

Jan 1, 1968

By N. C. Carter, Wm. H. White, J. E. Harakal

"Of twenty-one ore deposits in British Columbia which are either in production or advanced stages of exploration, five have potassium-argon ages in a range of 165-205 m.y., eight are in a range of 44-55 m.y. and the remainder are either ca. 140 m.y. or ca. 100 m.y. old. Deposits of the oldest group have generally similar geological environments and radiometrically indistinguishable ages of magmatic and hydrothermal minerals. Deposits of the youngest group also have similar geological environments, with successive magmatic and hydrothermal events closely intermingled in time and place. Such deposits find no comfortable home in existing classifications of ore deposits. 1t is suggested, therefore, that those epigenetic deposits which can be shown by radiometrie and/or geologie means to be coeval with genetically related magmatism be designated as ""paramagmatic deposits."""

Jan 1, 1968

By J. L. Goodier

The paper points up the hesitance of private capital to pursue development of offshore mineral mining endeavors due to the deterrent effect of the clouded legal status of such endeavors. Some states have no laws or regulations to protect the potential exploiter. Others have regulations which give no proprietary rights of exploration to mineral discoveries. The above factors and others are discussed and analyzed in some detail, covering, in turn, summations of the federal regulations and of each of the coastal states. Some comparative analyses are provided, and some recommendations for encouragement to capital investors are made.

Jan 1, 1968

By M. S. Burton, J. E. Ritter

The sessile-drop technique was employed to study the effect of atmosphere and alloy additions of titanium and chromium on the surface tension and contact angle of nickel on sapphire substrates at 1500oC. Shear tests were conducted on the solidified sessile drops. The liquid-gas surface tension of pure nickel on sapphire was found to be 1747 ergs per sq cm, with a contact angle of 109.6 deg. The surface tension and contact angle were not affected significantly by the four atmospheres, vacuum, impure argon, pure argon, and pure hydrogen. Small additions of titanium and chromium decreased the contact angle and for the same alloy content, contact angles were lower in pure argon than in pure hydrogen. On the basis of shear-test results , the most probable cause for adhesion in the Ni-Al2O system is the formation of NiO:Al2O3 spinel at the interface; in the titanium alloy-Al2O3 system adhesion is thought to be due to a mechanical interlocking effect; in the chromium alloy-Al2O3 system adhesion is believed to be the result of solid-solution formation involving Cr2O3 and Al2O3 at the interface. In the last few years there has been considerable interest in reinforcing metals with ceramic whiskers. It has been postulated that, by reinforcing nickel with sapphire whiskers, high-temperature strengths su- perior to those of the best current nickel alloys can be achieved.' To fabricate a whisker-metal composite having optimum density and strength, understanding of wettability and adherence in the system is of prime importance. Although there has been some previous research in this a a need for further studies has been cited4-8 to understand better the effects of impurities, alloys additions, and atmosphere on the wetting and bonding of metals to metal oxides. The purpose of this research was to investigate the factors involved in the wetting and adherence of nickel/nickel alloys to sapphire (single-crystal a Al2O3). Sessile-drop experiments were conducted in vacuum, impure argon, pure argon, and pure hydrogen, to determine the effect of atmosphere on the contact angle of the metals on sapphire, and the liquid-gas surface tension of pure nickel. The solidified sessile drops were sheared from the sapphire substrate to measure the bond strength between the metal and ceramic. The alloy additions chosen were titanium and chromium since both enhance the wetting of nickel on sapphire.2, 3c Also, titanium is commonly used when brazing metal-to-ceramic seals to improve adherence. Since chromium forms an oxide that is completely soluble in sapphire, it was thought that the oxide could serve as a transition phase to promote bonding between the Ni-Cr alloy and sapphire. I) EXPERIMENTAL APPARATUS AND PROCEDURE The sessile-drop apparatus was a horizontal furnace, with an induction-heated, cylindrical molybdenum susceptor in a water-cooled Pyrex chamber. This apparatus was patterned after that of Williams and Nielsen.7 A flat Pyrex window at each end of the furnace allowed temperature measurements to be made at one

Jan 1, 1968

By N. B. Gray, R. V. Culver, W. S. Boundy, N. W. Stump

The kinetics of sulfation of single crystals of lead sulfide to lead sulfate have been studied between 969" and 1073°K in gas atmospheres of known composition using a thermobalance technique. The data are described by an equation derived on the basis that diffusion outward through the Product layer is the major controlling step. The rate of sulfation is linearly related to the logarithm of the sulfur trioxide partial DESPITE its industrial significance the oxidation of lead sulfide has received limited attention. The oxidation reactions have been studied using beds, briquettes, single crystals, or thin films of lead sulfide. Lead oxide and lead sulfate (PbSO,) were formed when Mclntoshl and Gardner2 roasted beds of galena pressure and the temperature coefficient of reaction is 40 ± 5 kcal per g mole. Gold marker experiments show that the sulfate layer grows by outward movement of ions through the sulfate layer. Initially the PbSO, adheres to the PbS but later forms an irnpewious spheroidal envelope; PbS vaporizes and pb2' ions diffuse through the envelope to react at the external surface. in air at temperatures up to 800°C. In a more extensive investigation, Tchizhykov3 obtained Pb, PbO, and PbS04 in accordance with Eqs. [1] to [4], when a bed of -200 mesh galena was oxidized in O2-N2 mixtures at 700° to 900°C.

Jan 1, 1968

By E. Miller, J. M. Eldridge, K. L. Komarek

The thermodynamic properties of- liquid Mg-Pb allojs have been determined by an isopiestic method from 18 to 42 at. pct Pb and by a thevmodynumic analysis of the phase diagram frofiz 0 to 100 at. pct Pb. In the overlapping composition range the magneszupn activity values derived by the two methods are in excellent agreement, thus mutually supporting the correctness of the Mg-Pb phase diagram previously determined by the authors and of the acticitzes deriz~ed isopiestically. SEVERAL studies have been made of the thermody-namic properties of liquid Mg-Pb alloys. Wagner and Engelhardt,1 Lantratov,2 Knappwost,3 Sryvalin et al.* and Wilson5 used the electromotive-force method, Scheil and Wolf8 and Schmahl and Sieben" applied the transpiration technique, and the present authors8 utilized the phase diagram to determine the activity of magnesium in the Mg-Pb system. The results of these studies are not in very good agreement and could not be incorporated into a general systematic analysis of the thermodynamic properties of the homologous series of the Mg-Group IV B systems Mg-Pb,8 Mg-Sn,° Mg-Ge,10and Mg-Si.11 The thermodynamic properties of the Mg-Pb system were therefore re investigated by an isopiestic technique which has been developed for similar studies in the Mg-SnB and Mg-Ge10 systems- Lead specimens, contained in iron or graphite crucibles, were heated in a temperature gradient in an evacuated and sealed titanium reaction tube and equilibrated with magnesium vapor of known vapor pressure to form alloys of compositions which depended on their temperatures, the temperature of the magnesium vapor source, and the thermodynamic properties of the system. EXPERIMENTAL PROCEDURE Magnesium (Dominion Magnesium Ltd., Toronto, Canada) of 99.99+ pct purity and lead (American Smelting and Refining Co.) of 99.999 pct purity were used. In the early experiments, Runs 2 and 3, the alloys were contained in uncovered high-purity iron crucibles. Alloys formed in the uncovered iron crucibles had to be chemically analyzed owing to the slight volatility of lead under the imposed experimental equilibration conditions. The compositions of these alloys were determined by a gravimetric analysis of lead as lead chromate. To avoid this problem, the remaining runs were made in covered graphite crucibles machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non- i reactivity of graphite with lead and magnesium has been previously established,' and the experimental procedure has been described in full detail.' In the runs using covered graphite crucibles it was found that the weight increases of the crucibles and their contents after equilibration equaled the magnesium contents of the alloys within the accuracy of the chemical analysis (i0.3 at. pct Pb). Clearly, the small lid openings of the graphite crucibles prevented significant lead losses during a run, and the weight increase was therefore taken as the magnesium content of the alloys. EXPERIMENTAL RESULTS At thermodynamic equilibrium the magnesium partial pressure of the specimens equaled that of the reservoir. Since the magnesium reservoir was always maintained at the temperature minimum of the system, the activity of magnesium of any specimen was given by the ratio of the magnesium reservoir pressure to the vapor pressure of pure magnesium at the specimen temperature. The standard state was chosen as liquid magnesium and the vapor pressure of liquid magnesium

Jan 1, 1968

By H. Habenicht, J. J. Scott

An experimental method is described to compare strain data for rock and rock bolts when exposed to shock waves released by blastings. Static and dynamic strains were measured. Bolt gage response indicated a static decay of the bolt anchorage coupled with a reaction due to blasting vibrations. A distinct loss of bolt tension was indicated during vibrations and this was accompanied by a smaller but steady loss of tension due to static loading. The strain losses were found to relate to the shock source distance and the vibrational amplitude in the rock and bolts. Millions of roof bolts are used each year to stabilize mine openings and prevent their failure. Frequently, bolts become loose and lose their effectiveness as reinforcement to the mine structure. Many attempts have been made to determine the cause of loosening, including observation of the bolt tension or bolt torque through the use of torque wrenches, compression pads, and load cells. Pull tests have been used extensively to determine anchorage characteristics.102 These investigations have shown that even when bolts are loaded below the nominal anchorage capacity of the rock under 'static' conditions they exhibit a decay of load through adjustments and slippage at the bolt anchor. Since bolts are quite often found with the plate hanging loose from the rock surface, this condition suggests that some additional mechanism may have played a part in loosening the anchorage. Vibration from blasting or shock loading have been suggested as one cause in this type of anchorage deterioration. This paper gives the results of an investigation carried on at the University of Missouri at Rolla to determine the influence of shock waves on rock-bolt anchorage stability. ROCK BOLT ANCHORAGE UNDER DYNAMIC LOADING CONDITIONS In this report dynamic loading conditions are defined as conditions under which rock and bolts are exposed to vibrations occurring as a consequence of blasting, machine vibrations, earthquakes, rock bursts, etc. Whatever the location of the shock source, the waves created suffer extensive alterations along their travel paths, depending upon the vibrational properties and geometric parameters of the transmitting media. Together with reflection, refraction and diffraction at material boundaries, waves suffer changes in their nature to form tensile, compressive and shear waves. They become polarized, retracted, accelerated, dispersed, so that the waves incident at a point in the material can be the result of either one or a combination of this wide range of processes. A certain fraction of the wave energy will be lost due to friction, deformation, and material failure at the anchor-rock contact. Thus, the physical nature of wave propagation is such that it inhibits an exact analytical solution. For this reason this investigation should be considered qualitative rather than quantitative even though numerical data have been used as a base. CONCEPT OF THE INVESTIGATION Experiments were designed to find, from a series of rock bolts installed in natural mine rock, whether or not, and to what extent, bolt tensions would be influenced when bolts were exposed repeatedly to shock waves such as those produced by blasting. Electronic instrumentation available in the rock mechanics laboratory of the University of Missouri at Rolla was used to observe wave development in the rock and vibrational reactions in the bolts. EXPERIMENTAL PROCEDURE Fig. 1 illustrates schematically the experimental equipment. Electric resistance wire strain gages were used as sensors for the strain response of the rock and the bolts. Bolts were 5 ft long and 5/8 in. in diam, equipped with two-leaf type expansion shells for 1 3/8 in. boreholes. The bolt gages were mounted by use of Du Pont Household Cement, covered with an epoxy insulation and then enclosed in a copper foil for electronic shielding. For details of placement and the wiring diagram see Fig. 2 and 3. The output of both the rock gages and the bolt gages was fed into cathode ray oscilloscopes from which the vibrational traces could be photographed. A static strain indicator was also used to read the output of all gages.

Jan 1, 1968

By H. E. Cline

Mechanical properties of the eutectic between CoAl and cobalt were measured over a range of- temnperatures and strain rates for a variety of microstructures produced by directional solidification and by thermo-mechanical processing. Directional solidification led to rodlike, lamellar, and irregular microstructures. The unusually high volume fraction of the cobalt-rich rods and the lurge spacing of the rods were explained by the phase diagram. The hot-worked structure consisted of fibers of COAL in a cobalt-rich matrix. The roonl- tevlperature strength of the uvrought material increased with decreasing grain size but the 1000°C strength decreased with decreasing pain size. At high temperatures the directionally solidified tnaterial was stronger and less strain-rate-sensitice than the hot-rolled material. The fine-grained hot-worked ma-terial became superplastic at high temperatures, with tensile elongations greater than 850 pct, while at root temperature this material was ductile and impact-resistant because of the ductile matrix. Fracture occurred in the directionally solidified material at elevated temperatures by inter phase separation and at roorn temperature by cracks in the intermetallic phase. Growth of these cracks was impeded by the ductile cobalt-rich phase. It was found that the CoAl intermetallic remains ordered at elevated temperatures. DIRECTIONAL solidification of eutectic alloys has been used to produce structures consisting of parallel rods or lamellae. Although the spacing of the phases depends on the growth rate, it has been observed to be of the order of 1 µ in many eutectics. A strong intermetallic phase has been used to reinforce a ductile matrix in the rod eutectic A1-Al3Ni and the lamellar eutectic Al-Al2cu.1 The microstructure of the eutectics A1-A13Ni and A1-A12Cu remained aligned after samples of these alloys were exposed to temperatures just below their melting points for long times. Stability of the microstructure at elevated temperatures makes directionally solidified eutectics a candidate for high-temperature applications. Recently Thompson4 has developed the Ni-NiMo eutectic containing 40 pct NiMo lamellae, giving a tensile strength superior to nickel-base superalloys. Unfortunately, this eutectic oxidizes rapidly at elevated temperatures. By mechanically processing a two-phase structure, one may reach strengths as high as 700,000 psi, as demonstrated by drawn pearlite.5 In this case the strengthening mechanism was thought to be related to the fine substructure formed during deformation.5 However, a heavily worked structure may recrystallize and coarsen at elevated temperatures. Some worked eutectics such as Al-Al2Cu,6 Pb-Sn,7 and Sn-Bi7 have shown unusually large elongations in tension when tested at elevated temperatures. This phenomenon of large extension, called "superplasticity", was related to the fine grain size of wrought two-phase alloys at elevated temperatures. A mode of deformation of "superplastic" material has been shown to be grain boundary sliding,' which has also been observed during creep of polycrystalline materials.9 The Co-A1 system was chosen for this investigation after examining the phase diagrams of binary eutectics." The high melting point of 1400°C, the aluminum content which was expected to give oxidation resistance, and the properties of the intermetallic CoAl were the chief factors influencing this choice. This eutectic consists of a mixture of the intermetallic CoAl and a cobalt-rich solid solution. The intermetallic CoAl has a large range of solubility and a CsCl structure." From the similarity between CoAl and NiAl one would expect CoAl to be ordered at elevated temperatures; however, specific heat measurements" show a transition at 800°C. West-brookL2 has measured the hot hardness of CoAl and found a rapid decrease in hardness above 600°C. The tensile properties and stress rupture properties of as-cast CoAl-Co eutectic were measured by Ashbrook and wallace13 who report a room-temperature tensile elongation of less than 1 pct. I) EXPERIMENTAL A) Sample Preparation. Experimental materials were prepared by directional solidification, by hot working, and by powder processing. The starting materials were electrolytic 99.9 pct pure cobalt and 99.99 pct pure aluminum. 1) Directional Solidification. A vertical Bridgman apparatus heated by induction was used to directionally solidify cylindrical ingots $ in. in diam and 5 in. long. The apparatus was first evacuated and then an argon atmosphere was introduced to retard evaporation. The ingots were contained in an alumina crucible inside a graphite susceptor that rested on a movable water-cooled base. The base was lowered out of the induction coil at a constant rate. Eight of the ingots were solidified using a drive rate of 2.5 cm per hr, two of the ingots at 1.2 cm per hr, and one ingot at 10 cm per hr. The eutectic composition Co 10 wt pct A1 was used in all but one ingot which had the composition of the stoichiometric CoAl intermetallic, Co 32 wt pct Al. 2) Mechanical Processing. At 1000°C the eutectic Co 10 wt pct A1 is a mixture of an intermetallic phase, Co 21 wt pct Al, and a cobalt-rich phase, Co 5 wt pct Al.10 These phases differ from the stoichiometric CO 32 wt pct A1 and pure cobalt because of the large solubility of this eutectic at elevated temperatures." Four rectangular slab ingots, 4 by 1 by 12 in. high, of Co 10 wt pct Al, Co 5 wt pct Al, Co 21 wt pct Al, and Co 32 wt pct A1 were cast for hot rolling. The cobalt was first vacuum-melted, H2-treated for 20 min,

Jan 1, 1968