By William C. Sleppy

The nmgnetic susceptibility of heat-treatable aluminuin alloys is sensitive to chanyes such as solution or dissolution of solute and the precipitation of mew phases. By measuring the change in the magnetic susceptibility of aluminum alloys caused by various heat treatments, an empirical relation was found from which atomic arrangements in dilute binary alloys of copper, zinc, and magnesiutn in aluminum have been delineated. The relation predicts the ultimate formation of C1LA12 when copper is precipitated from solid solution in aluminum. Euidexce joy silovt- range order is found for copper in solid solution in aluminum in the sense that copper atoms avoid being nearest neighbors to an extent greater than would result from a purely random arrangertzeizt. Hume-Rothery has predicted such short-range order joy solid solution of copper in aluminum The Al-Zn system agrees with evidence obtained from X-ray scattering at small angles and predicts a tendency for zinc atoms to cluster in solid solution in aluminum. In the Al-mg system, the empirical relation indicates an approach to randor distribution of magnesium in solid solution in aluminum with a tendency for magnesium segvegation which increases with incveasing temperature. ThE magnetic properties of metals are complicated by the fact that contributions are made to them both by electrons of a "metallic" type which belong to the crystal as a whole, and by electrons in states localized on particular atoms. An expression1'2 for the bulk magnetic susceptibility of aluminum may be written as the sum of three contributions: where XA1 is the bulk susceptibility of aluminum per gram of material (in the cgs system, the units are those of reciprocal density); Xa1+3 is the diamagnetic contribution of the electrons localized in ion cores; Xa1 is. the paramagnetic spin contribution of conduction electrons often called Pauli paramag-netism: Xa1 is the diamagnetic contribution of the conduction electrons often called Landau diamag-netism. Ion core diamagnetism arises from the precession of the electron orbits which occurs when a magnetic field is applied to a system of electrons moving about a nucleus. Its contribution to the magnetic suscepti- bility is small, temperature-independent, and unaffected by alloying. The conduction electron diamagnetism is also temperature-independent and arises from the translatory motion of the electrons. For perfectly free electrons this contribution should be exactly one-third of the Pauli spin paramagnetism, but this relation is seldom even approximately true. Blythe2 determined the conduction electron diamagnetism in pure aluminum and found it to be extremely small. Any change in the conduction electron diamagnetism caused by alloying is neglected in this work. The Pauli paramagnetic contribution3 to the magnetic susceptibility of aluminum depends upon the number of electrons that occupy excited states and whose spins can be turned parallel to an applied magnetic field. The number of electrons free to turn in the field is proportional to the temperature and each spin contribution to the susceptibility is inversely proportional to the temperature. A slight temperature dependence of Pauli paramagnetism occurs when the number of electrons occupying excited states cannot increase sufficiently to balance the inverse dependence on temperature of each spin contribution. The decrease of the magnetic susceptibility of aluminum with increasing temperature is attributed to a temperature dependence of the Pauli paramagnetism. Estimates of the Pauli paramagnetism of aluminum have been made by several workers.2,4,5 All of the values are in reasonably good agreement with each other. In this work Xal at 17°C is taken as 0.761 X 10-8 cu cm per g. An expression similar to [I] can be written for the magnetic susceptibility of an aluminum base alloy containing a fractional weight percent x of solute:' Xa = (1 -x)XAl+3 +xXsoluteion * XaPauli +Xadia) [2] where X, is the magnetic susceptibility per gram of alloy, Xal'3and Xsolute ion are the ion core diamag-netic contributions, and xpauli and xdia are the Pauli and diamagnetic contributions of conduction electrons in the alloy. If the components of a mixture are not alloyed but simply mixed together in their pure states without producing a new phase, then the magnetic susceptibility of the mixture is given by the Wiedemann additivity law: Xm =x1X1 +x2x2 + ..xnxp [3] where X, is the susceptibility per gram of mixture and xnXp are the weight fractions and susceptibilities, respectively,-. for the pure components. The additivity law is not applicable to alloys because the outer electronic structures of the components are changed by alloying.' Both the Pauli paramagnetism and Landau diamagnetism are affected; hence the magnetic susceptibilitv of an alloy is usually different from that calculated using the additivity law. In this work the difference, X, -X,, is taken as a measure of the change caused by alloying.

Jan 1, 1968

By Bayly MG, Harris JA

The current operational practice at the Territory Enterprises Pty, Limited uranium oxide plant,, and some aspects of researc$ and development work at Rum Jungle are outlined with pertinent comments on some overseas practices.

Jan 1, 1968

By J. G. Donaldson

The Bureau of Mines investigated the formation of boron and boron-carbide coatings by vapor-phase reactions. Optimum parameters were determined for hydrogen reduction of boron trichloride and for the fonnation of boron-carbide coatings on graphite by reaction with the depositing boron. At 1,300° C, about 85 percent of the boron was deposited. Tungsten substrates did not react with the boron deposit; other substrates reacted to various extents. The hydrogen reduction of boron tribromide was briefly investigated. Boron carbide was deposited at 1,300° C by adding methane to the boron trichloride-hydrogen feed gas. The chemical composition of the vapor-deposited boron carbide approximated B4C. A method of etching B4C was developed to study its microstructure. When boron was deposited on graphite at 1,500° C, very hard, uniform, strongly adherent coatings of B4C were formed that might be useful in rocket nozzle applications.

Jan 1, 1968

By Edward M. Downs

This paper is a brief review of the lubrication requirements of enclosed gearing on earth moving equipment, particularly as they apply to intermediate and large draglines and shovels used in open pit mining operations. It discusses the requirements of spur, helical and herringbone gearing in both horizontal and vertically mounted applications. The effects of base stock, oil viscosity, additive treatment, quantity of oil and method of application are considered. In addition, a newly designed circulating oil system for enclosed swing gear cases and the reasons for its development are discussed.

Jan 1, 1968

By J. B. Wagner, B. Swaroop

The atomic ratios of oxygen to iron in zlarious corn-posilions of wustite in the vicinity oj the reported p to n transformation were determined in the temperalure range between 950" and 1250°C. For these conditions, equilibrium vacancy concenrations have also been determined at vatious mixtures of C0,-CO. The data show a continuos introduction of iron vacancies as oxygen is introduced into wuistite. No phase change is observed with in the wuustite field. However, the value of n in the isothermal oxygen pressure dependence, the weight change shifts to 1ower values as the concentration of oxygen increases. WUSTITE is a metal deficit semiconductor with the majority lattice disorder being cation vacancies. Using the notation similar to that of Kroger and ink,' the dissolution of oxygen into wiistite using C02-CO mixtures is represented by, WHere v+! denotes a cation vacancy with k effective negative charges and kh • denotes k electron holes, h -. Applying the law of mass action and assuming a dilute solution of defects in the wiistite yields Where the square brackets denote concentrations. Furthermore, when k = 2 the cation vacancies are completely ionized, and both the concentration of cation vacancies and the concentration of electron holes are proportional to the third root of the ratio, PC /PCo. This analysis is valid for one particular mael based on an ideal solution at elevated temperatures (in this case t > 1000°C). At lower temperatures, it has been shown2 that the pressure dependence of the electronic conductivity changes in a manner which suggests that vacancies interact with or "trap" electron holes. At the very high concentrations of defects, 10'' to 10" per cu cm, these simple models no longer hold. Recently Tannhauser,3 Geiger et a1.' Bransky and Tannhauser; and Hillegas' have found an apparent p to n transformation in wiistite in the temperature range of 950" to 1300°C. This junction was found by thermoelectric and electronic conductivity measurements. Geiger eta1.' found that the electronic conductivity became almost independent of the oxygen pressure at high temperatures and oxygen concentrations within the experimental error. In addition, Vallet, Raccah, and coworkers6'7 have reported the existence of several "varieties" of wiistite which were reported to exist within what was heretofor presumed to be a

Jan 1, 1968

By M. E. Wadswort, A. S. Peck

Infrared data disclose that phenacite reacts with oleic acid to form a chemisorbed oleate monolayer on the mineral surface. The absorption band characteristic of the antisymmetrical C = 0 oleate structure appears at a spectral wavelength of 1623 cm-'. Chemisorption also results in the displacement of OH- and silicate from the mineral surface. Infrared absorbance at 1623 cm-1 is correlated with float-ability at different pH for -60-mesh phenacite particles. Phenacite, Be2SiO4, is an ore mineral often associated with quartz, microcline, and chrysoberyl in pegmatites and mica schist. Experimental phenacite beneficiating processes have been confined principally to the flotation of low grade ores occur-ing in several mountain ranges of Utah and Nevada. The U.S. Bureau of Mines ' has recently reported on the separation of phenacite from ore deposits of Mount Wheeler, Nev. Infrared techniques were previously applied by the authors to characterize the role of sodium oleate and oleic acid in the flotation of several non-sulfide minerals.23 A parallel study was projected to the flotation of the orthosilicate mineral phenacite with oleic acid. Infrared spectra provided a 'molecular fingerprint' of the mineral surface and permitted identification of the reaction mechanisms. Infrared data were complemented with flotation and chemical tests. EXPERIMENTAL PROCEDURES The experimental procedures used in this investigation, for which data are presented in graphical or spectral form, are described in chronological test order. Phenacite crystals from Mt. Antero, Colo., were obtained from Ward's Co., Monterey, Calif. The crystals were fragmented in a porcelain mortar to -60 mesh and then pretreated with 0.5 molar HC1 for 15 min to remove iron. Then, the mineral particles were washed free of acid with distilled water and dried. Part of the dried material was ground to a fine powder with a Fisher Grinder using an agate mortar and pestle. Next, the powder was placed in a graduated cylinder and mixed with 500 ml of distilled water. The mineral in suspension was decanted from the settled fraction after 5 min, and the colloidal suspension was used for adsorption tests in which a high specific mineral surface area was required for adsorption and infrared analysis. Conditioning was performed in 50 ml glass centrifuge tubes for both infrared and flotation test determinations. Twenty ml of colloidal suspension was used for the infrared adsorption tests. One and a half g of deslimed -60-mesh HCl pretreated phenacite was added to 20 ml of distilled water for flotation conditioning tests. Six mg of oleic acid was used for each infrared adsorption test, and 0.2 mg of oleic acid was used for the flotation conditioning tests. HCl and NaOH were used for pH modification. The pulps were stirred at a speed of about 1500 rpm for 3 min. Then, the solids were separated out and either dried at 50°C or immediately transferred to a float cell. The pH of the residual liquid was determined with a Beckman Zeromatic pH meter. The flotation procedure is described as follows: 1) A 325-1111 glass micro-float cell was filled with distilled water. 2) Conditioned mineral was placed in the cell and the pulp was aerated through the glass fritted bottom at 7 psi pressure. 3) Floated mineral was skimmed from the cell with a glass slide until flotation ceased. (The end point was reached in all tests in less than 2 min.) 4) The flotation products were dried, weighed, and the recovery was calculated. Samples for infrared analysis were made into mulls using either oleic acid or series 13-21 Halocarbon oil obtained from Halocarbon Products Corp., Hacken-sack, N.J. The mulls were placed between two sodium chloride windows. A characteristic phenacite infrared band at 1868 cm-' was used as an internal standard for quantitative determinations in which absorbance at this position was quantified by the baseline-tangent method4 and related to absorbance at 1623 cm-'. The ratio obtained by dividing absorbance at 1623 cm-' by absorbance at 1868 cm-' was defined as an absorbance quotient for use in graphical presentation.

Jan 1, 1968

By Sabri Ergun

Previous studies of magnetic separation of pyrite from coals have been reviewed critically. Magnetic susceptibilities of United States coals of differing rank have been measured. The effects of crushing, magnetic mixing, drying, weathering, and heat treatment on the enhancement of the magnetism of pyrite have been analyzed. The importance of size distribution of pyrite in the coal and the necessity of crushing to liberate the pyrite has been discussed. It has been found that the inherent susceptibilities of the carbonaceous, mineral-free portions of coals (? -0.5 X 10-6 in cgs units) and of relatively pure pyrite isolated from coals (? -0.3 X 10-6) do not permit efficient separation of pyrite from coal; the average susceptibility of the magnetic fraction of coal must be raised to 3 X 10-6. Friction forces encountered in crushing sedimentary pyrite embedded in coal do not increase its susceptibility. Subsequent weathering or heat treatment below 400° C leads to the formation of iron sulfate and hence increases the effective paramagnetism of pyrite. Ferromagnetic compounds of iron are not formed in significant quantities at temperatures below 400° C. The degree of liberation and apparent susceptibility of pyrite are the most important parameters in its separation. It is concluded that effective beneficiation of coals can be achieved by magnetic separation. A sufficient increase in the susceptibility can be achieved by converting less than 0.1 percent of pyrite into ferromagnetic compounds of iron. Such conversions occur only at temperatures >500° C. An investigation of the dielectric properties of coals and pyrite in the frequency range 0.1 to 60 Mhz indicates that the imaginary dielectric constant of the pyrite is about 100 times larger than that of coal. Exploratory experiments indicate that pyrite can be selectively heated to temperatures above 500° C without appreciable rise in the temperature of coal. It appears that dielectric heating of coals in the Ghz frequency range is the most feasible method of enhancing the paramagnetism of pyrite.

Jan 1, 1968

By J. L. Walter

Tungsten ingots with and without small amounts of aluminum, silicon, and potassium were prepared by conventional powder-metallurgy techniques and hot-rolled to 0.001-in.-thick sheet. The ingots were rolled three different ways: I) initially cross-rolled, then straight-rolled; 2) straight-rolled, and 3) straig-ht-rolled, then cross-rolled. Total reductions were 99.8 pct. Samples of the sheet were annealed, in vacuo, at temperatures from 1200" to 2200°C. Substructures and textures were determined by transmission electron microscopy and X-ray diffraction. The doping agents were found to form particles of mullite (Al,Si,O,,) which, on rolling., appear to form strings of particles aligned parallel to the rolling direction. These strings of purticles are associated with an increase in the recrystal-lizution temperature from 1400°C for undoped sheet ThE addition of small amounts of aluminum, silicon, and potassium to tungsten has a profound effect on the grain structure of drawn and recrystallized wire.'" The grains generally do not occupy the entire cross section of the wire and have lengths many times the wire diameter. The grain boundaries are, in general, nearly parallel to the wire axis and have long ''fingers" projecting one into the other as may be seen in Fig. 1, a longitudinal section of recrystallized doped wire. When unsuitable additions or no additions are made or the wire is not sufficiently reduced during draw- to 2000°C for doped sheet. The particles also limit lateral grain growth while allowing growth parallel to the rolling direction. This results in the formation by primary re crystallization of large highly elongated grains of specific preferred orientation. The undoped sheet recrystallized to small equiaxed gains. The preferred orientations of the large grains were determined from axis density plots to be (113) (691). (0i3) (362), (116) (304) types for the initially cross-rolled then straight rolled material. These orientations are similar to the orientations of the large elongated grains in doped and heavily drawn tungsten wire. The nucleation of the large grains appears to occur by recovery of certain of the polygonized regions of specific orientation, followed by strain-induced boundary migration.

Jan 1, 1968

By Robert E. Goodwin

There are four main requirements which must be considered when selecting a wire rope for the best serviceability. A proper choice is made by correctly estimating the relative importance of each of these requirements and selecting s rope which has those qualities best suited to withstand the combination of destructive forces expected under continued service. A wire rope should possess: 1. Strength sufficient to support the maximum load expected and with s proper safety factor. 2. Ability to withstand bending and to resist bending fatigue without failure of the wires. 3. Ability to withstand surface abuse such so abrasive wear, pounding, and wire scrubbing. 4. Ability to withstand abuse such as crushing and distortion.

Jan 1, 1968

By C. N. Reid

Slip-line studies on deformed chromium single cvystals showed the usual bcc behavior. At room temperatuve, cross slip was prevalent—slip was not confined to a given plane, but the slip direction was (111). At -10O0K, slip occuvred on (110) planes, twins on(112) planes, and cleavage on (1001 planes. A single-crystal tensile specimen with an axis close to [011] showed a pronounced yield drop and high strain rate sensitivity which zclere used to derive relevant parame tevs in a dislocation dynamics treatment. Transmission electron microscope studies confirmed the existence of (110) slip planes and showed ecidence of loops punched out by precipitates and of grown-in dislocations promoting tangling. OF recent years experimental studies have been made of the deformation characteristics of single-crystal molybdenum and tungsten, but very little has been published on the behavior of single-crystal chromium. During a study of the mechanical properties of chromium, single-crystal studies were made which have already been partially described.&apos; However, additional information was generated which was not directly relevant to the main theme of Ref. 1, and, therefore, was not reported. In view of the need for complete documentation of deformation modes, the experimental observations made on the deformation of single-crystal chromium are summarized here, together with an electron-microscope study of the associated dislocation structures. It was found that, in terms of the deformation modes, chromium is a conventional bcc metal, showing a very pronounced yield-point phenomenon. Further, it was found that the flow strength of these crystals is very sensitive to the strain rate. Finally, the crystals were observed to contain many unidentified precipitates, which often were associated with prismatic dislocation loops. EXPERIMENTAL METHODS Single crystals were grown from rods of wrought chromium by the method of zone annealing. Rods of "1/4in.-diam were supported vertically in an argon atmosphere while an induction coil was moved up the rod at 1 in. per hr. The power was adjusted to just below that required for melting, and the process produced single crystals in about 30 pct of the rods used. The orientations of the crystals, in general, lay near [011] and are summarized in Fig. 1. Before this treatment, the wrought material contained 35 pprn C, 68 ppm O, and 12 ppm N.* An analyzed single crystal *Usual metallic impurities found in iodide chromium are: Al, 5 ppm; Ca, A ppm; Cu, 2 ppm; Fe, 75 ppm; Yg, 0.5 ppm; Yn, < 3 ppm; Mo, < 3 ppm; Ni, 4 ppm; Si, < 20 ppm; Ti, < 1 ppm; V, 4 ppm; Zr, < 3 ppm. contained 10 pprn C, 79 ppm O, and 50 pprn N. Tension and compression specimens were shaped from the crystals by mechanical grinding, followed by the electrolytic removal of about 0.010 in. from the surface in a perchloric/acetic acid bath. All specimens had a gage length of 0.75 in., and tension specimens had a diameter of 0.100 in., while that of the compression samples was 0.200 in. Mechanical tests were carried out at a rate of 1.3 pct per min, and temperatures below 0°C were attained by means of a nitrogen cryostat similar to that of Wessel.2 EXPERIMENTAL RESULTS Modes of Deformation. In addition to the tensile properties of these crystals, which are described in Ref. 1, deformation markings on the surface were studied. Crystals A and F, Fig. 1, were deformed in tension at 300°K to 10 and 16 pct strain, respectively. The surfaces contained visible slip lines, about 1 C( apart, composed of both straight and wavy segments. They did not define a single plane, and so determination of the slip plane was not possible. However, the slip direction was deduced by comparing the axial orientations of the crystals before and after deformation. Fig. 2 is representative, and shows that the axis ro-

Jan 1, 1968

By H. A. Tucker

This Bureau of Mines investigation was conducted to determine the appropriate quantities of rare-earth methals (REM) in the form of silicides to add to an alloy steel for the purpose of increasing toughness and ductility. The work was conducted in a vacuum induction furnace with the rare-earth additions required to deoxidize and desulfurize a simulated basic oxygen furnace (BOF) vacuum-degassed steel initially containing 0.013 to 0.016 percent sulfur. The product proved to be as good or better than the best basic electric furnace steel of the same composition made by the steel industry. Twenty-three experimental heats of 5 Ni-Cr-Mo-V steel were made, cast into 50-1b ingots, and hot-worked in a press and a rolling mill to ½ inch plates which were then heat-treated to 130/150 ksi4 yield strength. Impact and tension tests showed that the addition of 0.025 to 0.100 percent, or ½ to 2 lb per ton, respectively, of rare-earth metals when compounded with silicon were appropriate for increasing toughness and ductility. These quantities resulted in retained cerium contents between 0.014 to 0.025 percent, and increased the Charpy V-notch energy absorption and the percent reduction of area significantly as compared with base heats at the same sulfur content levels. All the test heats, including those with additions of REH of as much as 4 lb/ton, had greater Charpy V-notch energy absorption values than the base composition could have developed at the starting sulfur range of 0.013-0.016 wt pct.

Jan 1, 1968

By F. S. Thurner

This paper, a description of the new ore-unloading and stockpiling facilities at the Sydney Works of DOSCO Steel Limited, deals with a new approach to arrive at the most economical solution to combine ore unloading facilities for common bulk carriers and for different types of self-unloading vessels. Also discussed is the design and installation of a 1-mile-long steel-cord belt conveyor sys-tem with a most modern type of mobile belt conveyor stacker, along with automatic and semi-automatic controls for the entire ship-unloading and stockpiling operations.

Jan 1, 1968

By Thomas V. Falkie

4.3-1. Introduction. DEFINITION OF PRODUCTION SYSTEMS ENGINEERING. Surface mines, like most other mining and manufacturing operations, are usually organized along functional departmental lines. Frequently a mine manager will have his responsibilities divided among production, maintenance, administrative, and engineering functions. Often these are separate departments, but various combinations and variations of these functions can be found in mining companies throughout the world. The production function is responsible for physically removing the ore from the ground, processing it, and shipping the product to its market. The production manager supervises and is responsible for all man-machine systems necessary to extract and process the ore. The maintenance function, which is sometimes included within the framework of production, has the task of insuring the maximum availability and longevity of equipment needed to produce the ore. The administrative function is responsible for accounting, personnel, industrial relations, purchasing, public relations, property, and other related staff functions. For purposes of this chapter, engineering can be described as the function which plans, designs, and supervises construction of physical plant and equipment. In this context engineering includes mechanical, civil, chemical, electrical, and mining engineering. However, another phase of engineering is to prepare plans to insure that the various man-machine components function in an optimum way towards the single most important goal of any enterprise-the maximization of return on the investors&apos; money. Along with the planning, another duty of engineering is to audit all phases of the operation for the purpose of recommending improvements toward this same general goal. These latter two ideas form the basis for a discussion of production engineering and systems engineering. Production engineering is a catchall, problem-oriented function whose duties can include: 1) solution of day-to-day production problems, 2) short-

Jan 1, 1968

By J. C. Draper

This subject was introduced last April in a paper presented in Birmingham, Alabama, by James E. Elkin, General Superintendent of Duquesne&apos;s Coal Department. This paper will cover some of the same data and in addition it will update and further describe our experience. Our Portal No. 3 was started in June 1965 with battery tractor-trailer face haulage. This mine is operating in the Sewickley seam in Dunkard Township, Greene County, in Southwestern Pennsylvania as shown on Fig. 1. The Warwick group of mines fronts on the Monongahela River and extends westward for some ten miles as shown on Fig. 2.

Jan 1, 1968

By M. Boucraut

The authors investigate the influence of the basicity index CaO / Si02 on the sintering properties of hematite ore mixtures. The experimentation was performed with three different mixtures of ores from Tazadit, Nimba, Mano-River, Itabira, Marcona, Goa, Mapawa and Cassinga. Increasing the basicity index CaO / Si02 between 0.1 and 3, chiefly through limestone admixture makes possible to reduce the thermal consumption of sintering and to improve the physical and chemical properties of the sinter. In the case of a plant using hematite ores, it seems interesting to produce an hyperbasic sinter and to complete the blast furnace burden with calibrated ore or acid pellets.

Jan 1, 1968

Sphalerites from Devonian cassiterite-sulphide deposits and Pb-Zn-Ag fissure veins have similar ranges of Cd contents, but the average Cd and Fe contents could indicate a small initial difference in availability of Cd between the Zeehan-Renison Bell district and the Mt. Bischoff-Waratah district. Sphalerites from banded Pb-Zn deposits (Rosebery and Hercules) are characterized by low Cd content which is a world-wide feature of such deposits in exIrusive rocks, and may indicaIe a genetic relationship between ore deposition and vulcanism.

Jan 1, 1968

By G. R. St. Pierre, M. J. Pool, R. Speiser

The activities of chromium in solid Cr-Ti solulions contaitning from 10 to 90 at, pct Cr were measured over the temperatutre range 1250" to 1380°C. The Knzudsen effusion technique with direct weighing of the Knudsen cell was used. This was possible because the vapor pressure 0f chromium is about 600 times greater than the capor pressure of titanium so that the amount 0f titanium effusing could be neg-Lected. the activities of titanium were determined by g-raphical integration of the Gibbs-Duhertz equatiotz. The solutio~ls sllcdied exhibited positive deviations from Raoult&apos;s law, but they approached ideality as the temperature was raised from 125 to 138t C. The integral free energy of mixing was calclated from the activity values. AF has a maximum value of - 1.66 kcal a1 1390°C and a composition oj 55 at. pcl Cv. The free energy of formation of &apos;TiCr, is —0.76&apos; lzcal a1 1250°C. The heats and entropies of mixing usere determined using the second law and thus tile mlues could be in error by a considerable amount. The Cv-Ti system is not a regular solution. ThE increasing emphasis on application of various models to alloy formation and solution behavior has led to an intensified interest in the thermochemistry of alloys. In a majority of the cases where different models have been applied the alloy system used was a simple one. However, the amount of data available on more complicated systems is small and in order to fully understand the behavior of metallic solutions more experimental work has to be carried out on these systems. The Cr-Ti system is reasonably complex and even though this system was being investigated as early as 1937 by Kroll,&apos; no previous work has been done on the thermodynamic properties of either the liquid or solid state. This research was undertaken to determine the thermodynamic properties of solid Cr-Ti alloys. EXPERIMENTAL PROCEDURE The experiments on the Cr-Ti system were carried out in a water-cooled metal vacuum system. This system is composed of a brass vaporization chamber wound with copper tubing for cooling purposes, a brass liquid-nitrogen trap, an oil diffusion pump, and a Duo-Seal forepump. The pressure in the system is measured with an ionization gage. The interior of the vaporization chamber is shown schematically in Fig. 1. The Knudsen cell is supported by the molybdenum tripod, and a magnetically operated shutter is provided to protect the Pyrex sighting glass against deposition of metallic vapors in the intervals between temperature measurements. Heating is accomplished by means of a 20-kw 450-kc Westinghouse oscillator. The susceptor in this case is 10-mil tantalum seamless tubing which also forms the outside of the sample container. The remainder of the sample container consists Of an im~ervims re-crystallized alumina crucible and a 10-mil-thick tantalum lid. Two holes are drilled in the lid. The diameters of these holes were measured with the calibrated stage of a "Tukon" microhardness tester. The thicknesses were measured with a micrometer. A Leeds and Northrup disappear ing-filament optical pyrometer was used to measure the temperature. This is sighted through the smaller of the two holes in the lid and corrections for the emissivity of the sample were not necessary since the ratio bf cell length to hole diameter was large enough to insure a hohlraum. The pyrometer was calibrated at the ~~t~~~l Bureau of Standards, and the correction for the Pyrex sighting window was determined in the laboratory. The titanium used in this investigation was obtained from Mallory-Sharon and the chromium from The Union Carbide Metals Co. The reported purities were

Jan 1, 1968

By D. M. Blacknall, N. N. Winogradoff, E. W. Williams

Low-temperature measurements of photolumines-cence were used to evaluate the progvess in materials development. Variation of the impurity type, impurity concentration, and method of growth were used to clarify the chemical origin of defects in GaAs. Melt-g~ozun, epitaxial vapor-, and solution-grown samples were studied. A comparison of measurements at 77" and 20°K shows that more defects can be observed at the lower temperature. Th&apos;vee residual defects were identified in relatively pure GaAs. These were: silicon, copper, and a gallium vacancy-donor complex. Solution growth from a gallium solution inhibits the formation of the latter two. Eleven defects were studied and the "optical" activation energy of some of these, namely, silicon, cobalt, and chromium, has not been reported in the literature before. THE discovery of the injection laser in 1962 prompted extensive measurements of the photoluminescence of GaAs. The measurements were made at 77°K on GaAs doped with shallow impurities at various doping levels and compared with electroluminescence1&apos;2 and absorp- tion data.374 In addition, lower-temperature studies were made on relatively pure GaAS&apos; and on GaAs doped with oxygen,5&apos;" manganese,&apos; and copper.&apos; The observation of defects* in GaAs with photolu- *The word "defects" ~efers to both chemical impurities and native defects. minescence at low temperatures makes photolu mines-cence an invaluable tool in evaluating the progress in materials development. The only previous evaluation was done at 77°K when solution-grown and melt-grown GaAs were compared.O No identification of defects was made but it was shown that some of the deep-level luminescence seen in melt-grown GaAs was absent in solution-grown GaAs. The present work extends the comparison of preparation techniques to lower temperatures and to a study of epitaxial vapor-grown GaAs. It is particularly valuable for thin epitaxial layers since they cannot be analyzed by conventional analytical techniques. In addition, by varying the impurity type and impurity concentration the chemical origin and nature of defects in GaAs was demonstrated. Eleven defects were studied in all. Three of the defects were identified as residual defects which often contaminate GaAs prepared from the melt and the vapor. Only one such defect was observed in GaAs grown from a gallium solution and this was identified as silicon.

Jan 1, 1968

By Robert K. Linn

The New ldria Mining District is in the southern part of the Diablo mountains of the California Coast Range, 140 miles southeast of San Francisco. The district, noted primarily for quicksilver, also has become important recently as a producer of short-fiber chrysotile asbestos. Between 1853 and 1966, the New Idria district produced 568,092 flasks of quicksilver valued at about $55,600,000, 99 per cent of which was recovered from one deposit, the New Idria mine. In 1944, the district was ranked third in all-time production of North American quicksilver districts, and, since that time, the New Idria mine produced an additional 129,045 flasks, placing the district and the New Idria mine second in all-time production. The major structure of the region is the northwest-trending Coalinga anticline consisting of an asymmetric dome of sedimentary beds ranging in age from Jurassic to Quaternary and marked at its northwest end by an oval body of sheared serpentine 14 miles long by 4 miles wide. The serpentine core, rimmed by Franciscan sandstone of probable Jurassic age, was uplifted in stages between Jurassic and Quaternary time and was intruded along a ring of faults into beds of the Panoche Formation of upper Cretaceous age. The core of serpentine and Franciscan rocks is the locus of about 20 quicksilver mines that rim the faultbounded core and lie within the serpentine mass. The host rock of the most productive deposits is altered Panoche shale and sandstone that lies intermittently along the perimeter of the core. Deposits of the New Idria group of mines and those of a few other small mines lie along the northeast contact in the footwall of the New ldria thrust fault, and a few others occur on steep normal faults around the south and southwest. The chief ore mineral in all quicksilver mines is cinnabar, but minor amounts of metacinnabar and native mercury are found in some of the mines. Ore shoots were deposited in fracture zones and stockworks in altered Panoche shale and sandstone and in definite fissure veins in Franciscan sandstone. Rocks made highly amenable to fracturing by hydrothermal alteration were fractured extensively by late faults. The resulting fracture zones, located along the late faults and at changes in strike or dip of the hanging wall or footwall, are the principal controls of most ore shoots. The largest and richest ore shoots are those of the New Idria mine. The major ore bodies occur in fractured shale and sandstone beneath the New ldria thrust fault at its junction with major tear faults.

Jan 1, 1968

By R. L. Schmidt, J. D. Verhoeven

The diffusion coefficients and electrotralzsport mobilities of aluminum, gallium, and arsenic have been determined in molten germanium with the capillary reservoir technique. The diffusion coefficients are slightly higher than those determined by the solidification technique of Brirton et a1.1 It was found that aluminium and gallium migrate to the cathode in molten germanium) whereas arsenic migrates to the anode under an electric field. A possible technique for producing p-n junctions by means of electric field freezing is discussed in view of the experimental data. In the past decade or so the literature has abounded with articles concerning the solid-state properties of the semiconducting elements germanium and silicon. It is surprising by comparison how little has been published concerning the liquid-state properties of these materials. In the production of doped germanium or silicon the diffusion coefficient of the dopant in liquid germanium or silicon is an important quantity. Yet, to the best of our knowledge, no one has ever made a direct measurement of the diffusion coefficient of solutes in either molten germanium or silicon. A number of authors&apos;-4 have determined some diffusion coefficients by the indirect technique developed by Burton et al.1 This technique appears to give numbers of the correct order of magnitude but it does depend upon a number of assumptions in the analysis and also requires prior knowledge of the viscosity of the melt. In the present work a more direct measure of the diffusion coefficients of arsenic, gallium: and aluminum in molten germanium has been made. It has been shown independently by two groups of authors5, 6 that, when an electric current is passed through the interface of a solidifying metal containing an impurity, the resulting electrotransport in the liquid boundary layer at the interface offers a mechanism for control over the redistribution of the impurity accompanying the solidification. These authors show that the degree of control is proportional to the mobility, U of the impurity atoms in the liquid boundary layer, where the mobility is defined as the drift velocity relative to the solvent per unit electric field. In principle the results apply to the solidification of a doped semiconductor and offer an interesting technique for control of the doping of a semiconductor. In the present work the mobilities of aluminum, gallium, and arsenic were determined in molten germanium in order to evaluate the potential usefulness of electro-transport as a technique for solute control when applied to the solidification of doped germanium. EXPERIMENTAL PROCEDURE Both the diffusion coefficients and the mobilities were measured using high-purity alumina capillaries and a resistivity technique for analysis. A schematic diagram of the electrotransport apparatus is shown in Fig. 1 and the details of the cell design are shown in Fig. 2. For the mobility experiments electrical contact with the bottom of the capillary was made with graphite, as shown in Fig. 2. In order to prevent electrical contact with the melt the graphite was coated with a thin layer of alumina using a plasma spray torch. The cell assembly, a graphite electrode, and another assembly containing two blank capillaries were fastened to the lavite disk shown in Fig. 1. To make a run the system was evacuated and the doped germanium was outgassed at the operating temperature of 1030°C. The cell and blank capillaries were then submerged beneath the melt and a slightly positive pressure of helium was introduced to fill them. After passing current through the cell for a given time the cell and blank capillaries were raised from the melt and the furnace was shut off. The temperature of the cells dropped below the freezing point of germanium within 1 to 2 min after the furnace was shut off.

Jan 1, 1968