By R. E. Reed-Hill, W. H. Hartt

The "(3034) " twin lamellae in magnesium have been reexamined using electron microscope replicas. The double twinning sequence (1011)- (1012) for these lamellae has been reconfirmed. Evidence is presented showing that the irrational habit of these twins is probably the direct result of a need to accommodate the second-order twinning shear. This accommodation vesults in both an external shear in the matrix and an internal shear in the lamella. A model is presented which accounts for the experimental obseruations. HCP metals are generally characterized by strong textures in which the basal planes of the grains tend to be aligned parallel to the rolling direction in sheet or plate and to the axis of wires and rods. Since these directions are normally those in which finished products may be subjected to uniaxial tensile stress, these textures effectively place the crystals of magnesium objects in orientations unfavorable to both basal slip and {1012) twinning, the easily activated deformation systems of this metal. However, when magnesium crystals are deformed near room temperature by a tensile stress nearly parallel to the basal plane, another mode of deformation can occur.',2 This is _a double twin which forms first by twinning on {loll), followed by retwinning on (1012). The resulting twin lamellae are of considerable interest. First, they can be responsible for "brittle fracture''; when a tensile stress axis lies in the basal plane, because the reoriented crystal structure of a lamella is well-aligned for slip while the parent crystal is not. Extensive internal deformation may thus occur while the matrix is still almost undeformed. This deformation can produce a ductile rupture running the length of the twin.3 Complete failure of the specimen may then oc-cure by the spreading of cracks from one twin lamella to another, or by the movement of a crack into a grain boundary and then along grain boundaries. Since the the volume fraction of these doubly twinned elements is normally very small, the fracture may be classed as brittle, although the fracture mechanism is, of itself, essentially ductile. It is quite probable that the ductility transition, normally observed4 in magnesium at or slightly Obove room temperature, is closely associated with these second-order twins. The detailed relationship of these twins to fracture in single crystals will be the topic of another paper. The present paper is concerned with a second important aspect: the irrational habit of these double twins that falls close to {3034), or approximately 7 deg away from the primary (10il) twin habit. There is good reason to believe that this habit results directly

Jan 1, 1968

By T. D. Tiemann

The extraction of iron oxide from several types of siliceous iron ore by digestion in sulfuric acid solutions was investigated in the temperature range from 80 to 258°F at concentrations from 10-60% H2SO4. Degree and rate of extraction were found to be critical with respect to both temperature and acid concentration, requiring temperatures in excess of 250° F and acid concentrations of 50% to effect 80-90% extraction of iron oxide in 60 min. Rate of extraction is directly related to surface area and apparently controlled by the rate of chemical reaction. The activation energy was found to be approximately 25,000 cal per g mol. Extraction characteristics of the several ores were found to be similar. The Department of Minerals and Metals Engineering at the University of Wisconsin conducts a continuing research program to develop processes for the utilization of low-grade iron ore deposits such as the nonmagnetic taconites of the Wisconsin Gogebic range. Methods under study include high-intensity magnetic and high-tension electrical concentration, flotation, direct reduction and chemical extraction. Concentration of a number of low-grade siliceous iron ores by the extraction of silica in sodium hydroxide solutions has been reported by the writer and others in the literature.1,2,3,4 Residual concentrates containing as much as 65% iron have been obtained from taconites containing less than 30%. Currently an alternative approach is under study, namely the dissolution of iron oxides from siliceous gangue by extraction in acid, with subsequent recovery of the iron from solution. Such a process for extracting iron oxide from the low-grade oclitic deposits of Alberta with hydrochloric acid was investigated and described by Gravenor, Govett and Rigg.5 The current investigation, which is entirely devoted to extraction with sulfuric acid, is the subject of this paper. In part, the objective of this research was to determine the possibility of leaching iron ores in situ with sulfuric acid. The investigation of a recovery method is left to later research. The ores investigated contained hematite (Fe2O3) as the principal iron-bearing mineral and minor amounts of goethite (Fe2O3 .H2O), magnetite (Fe3O4), and iron-bearing silicates. The gangue was essentially quartz occurring as single crystals and microcrystalline aggregates. Detailed description of the ores may be found in the literature.1,2,4,6 A comparison of the specific ores used in this investigation is shown in the partial analyses of Table I. EXPERIMENTAL METHODS All extractions were made at atmospheric pressure using beakers with a mechanical stirrer for those tests run below the boiling point, and Erlenmeyer flasks for those at the boiling point. A thermostatically controlled hot plate was used for heating, and this maintained the mean temperature within the solution to within ±3°F during extraction. The sample of ore for extraction was weighed to + 0.02 g. For tests below the boiling point, the sample was added to the beaker containing the sulfuric acid solution at the desired temperature. For the boiling-point tests, the sample was added to the Erlenmeyer flask followed by distilled water and the

Jan 1, 1968

By John Chipman

Published data on the equilibria of carbon in binary Fe-C austenite with H2-CH4 and CO2-CO gas mixtures are used to obtain the constants of an equation repre -senting the activity coefficient of carbon throughout the stable austenite range of temperatutre mid compositiotl. Calculated values for the solubility of graphite are found to be in agreement with the best-published direct observations. Its heat of solution is 10,680 calper g-atom. The free energy of formation of cementite is culculated from the equilibrium compositions of austenite and of gas. Its entropy and heat of formation are also obtained. BASIC knowledge of the high-temperature properties and treatment of steels is contained in the Fe-C diagram and its extensions for the effects of alloying elements. The application of thermodynamics to the Fe-C system, with addition of alloying elements, can serve to simplify and systematize this knowledge. The points of beginning are the binary fee solution, austenite, concerning which our information is reasonably complete, and the binary carbide, cementite. Further studies must include the other phases of the binary system, a and liquid, and for these an accurate knowledge of the ? phase boundaries is essential. These studies should provide a firm base for systematic study of the effects of alloying elements on all phases of the system, their transformations, and precipitation phenomena. With the aid of the simplifying thermodynamic concepts of activity coefficients and interaction parameters it is to be hoped that the results of these studies will be amenable to computer solution thus making the information on multicomponent systems more readily available than would be possible in multidimensional diagrams. Studies of the thermodynamic properties of austenite have utilized equilibrium measurements on the reactions:

Jan 1, 1968

By G. B. Craig, B. Ramaswami

The temperature and strain rate dependence of the flow stress ratio and the stvain rate dependence qi the flow stress of annealed polycrystalline a zirconiur were determined over the temperature range 30 0" to 1000°K. Some evidence was found for strain aging and discontinuous flow in the temperature ranges 520" to 650°Kand650" to 760°K, respectively. The Cottvell-Stokes relationship was obtained when deformation occurred by twinning as well as slip. The flow stress ratio showed a strong dependence on temperature and strain rate above 800°K. The expevirnental evidence indicated that the rate-controllitzg mechanism for the deformation of a zirconium above 800°K was dislocation climb, and that the deformation was not thermally activated in the range 520" to 800°K. The stacking-fault energy of a zirconium was estimated to be about 250 ergs per sq cm. A knowledge of the temperature and strain rate dependence of the applied stress necessary to deform a crystalline solid is essential for understanding the thermally activated processes occurring during deformation.' Several experimental techniques have been developed for studying these processes.273 One of the techniques is the deter mi nation of the strain rate dependence of the flow stress at constant temperature. In close-packed crystals, it has often been observed that the change in stress due to a change in the strain rate varies linearly with the flow stress, (~1,' This relationship, known as the Cottre ll-Stokes law, is obeyed when deformation occurs by glide alone. However, when deformation occurs by twinning as well as glide, there is disagreement among different investigators on whether the Cottrell-Stokes law is observed. Whereas Thornton et ~1.~find departures from Cottrell-Stokes law when twinning occurs in copper, ~avis~ and sasinski? find that Cottrell-Stokes law is obeyed when deformation occurs by twinning as well as slip in cadmium and magnesium, respectively. One of the main objectives of this study is to determine whether the Cottrell-Stokes law is obeyed when deformation occurs by twinning as well as slip. The second technique that has been used extensively to study the thermally activated deformation of crystals is the determination of the ratio of the flow stresses, at identical dislocation structures and con-

Jan 1, 1968

By W. W. Anderson, S. Razi

Electroluminescetrce of single crystals of terbium-(loped ZnS prepared by vapor-transport technique shows the sharp line specirum characteristic of the 4f— 4ft,ansitiotzs of the trivalent Tb3 rotz. V-I tt~easuverr~ents give evidence of space-ellarge-lirrlited curvent but the thrveshold for trap-filled law behavior is not iu agreement with Lampert&apos;s theory for. Single injection. Variations of &apos;brightness with applied voltage, the observation of double peaks its brightness because joms, and the spatial distribution oi electroLur?zir~escerrce indicate that the accelet~atiotz-collision mechanism involving the bst lattice and/ov shallow traps is most likely to be responsible fov excitation of&apos; electrolnminescence. Efficiency rtreusuver)~etits show the quantwn efficiency to be about 10 pct and powev efficiency about 0.05 pct. Effect of anr~eallng the crystal in sulfur vapor is to enluztzce llle rare-earth emission. It rs pvoposed tlzat sulfitv anr~ealing crreates acceptorr-lvpe defects with which the donor-type vare-eavtll ion can associate more readily vesulting in enhanced rare-earth emission. A&apos;o such e~zlznr~cerr~etrt is obserued when the crystal is atztrealetl in zinc vapor. Photolianinescence of ZnS doped nith a variety of rare earths also shows tile slurvp l~rze rwve-eavtlz erriission which in sorrretirr~es accompanied by broad band, stvuctureless lattice emission. Photo-atrd electrolutr~itzesce?~ce of ZIIS:Tb slw~rj do!rlit~unt rare-earth emission in the ~ticirzity of 54(3OA corre-sporrdit~g to the transition D* — Fj. Hoz~!el)er, the detailed line structuve of the luo spectvtr is cliffevet~t, irzdicutit~g that different sites are active in the two processes. Decay of rave-eartlr fluorescence in ZnS doped with any of sei!evul vuve eurtlzs car1 be described by a single exporleritial e.scepl joy ZrlS:lIo. Tl~is exceptiotr can be explaitred it~ tevrr~s of tlre closely spaced er~evgy 1e1:els Jov the HO~&apos; iorr. Decay lime measurertzekzts jov ZnS:Tb, using pulsed elect,-ical ar~d pulsed opticcll excitutiorzs, (11-e itz goor1 agrcetrier~t. LUMINESCENCE of rare-earth-doped materials has been a subject of interest for the past 20 years. Within the past few years there has been a considerable increase in rare-earth research motivated in search of new and more efficient laser materials and also due to the use of certain-rare-earth compounds in the preparation of color television screens. The purpose of this study has been to seek an understanding of some of the basic processes involved in exciting the rare-earth luminescence which is associated with transitions within the 4f shell of the trivalent rare-earth ion. Single crystals of ZnS doped with a variety of rare-earth ions have been prepared by vapor-transport technique described elsewhere.&apos; Photoluminescence was excited by a high-pressure short-arc mercury lamp together with suitable glass and chemical filters. For electroluminescence, sinusoidal and pulse excitations were used. 1) ELECTRICAL CHARACTERISTICS 1.1) V-I Measurements. Electroluminescence experiments were performed on crystals of terbium-doped ZnS. The samples were cleaned and etched and indium or In-Ga alloy contacts were alloyed on by heating in H2 atmosphere to 600°C for times ranging up to 10 min. Static voltage-current measurements were made on several samples. Fig. 1 shows the results for a typical sample. For voltage V < 20 v, the V-I relationship is linear giving a resistivity of 2.5 x 109 ohm-cm for this particular sample at room temperature. In the range of 20 to 250 v, I varies as V "3 and at still higher voltages (when electroluminescence is visible to the scotopic eye) current varies as Vs up to 600 v, all at room temperature. At 77"K, for V > 200 v, / I vge5 up to 1000 v. The V-I characteristics at room temperature follow reasonably well the behavior predicted by Lampert&apos; for one carrier space-charge-limited current in an insulator with traps although, as shown later, the expression derived by Lampert2 for the threshold for trap-filled law behavior Vtfl yields an unrealistically low value for trap density if we use the experimental value of 300 v for VtfL. Assuming the case for shallow trapping, the transition from Ohm&apos;s law behavior to space-charge-limited behavior occurs at voltage Vtr given by where no = thermally generated free carrier density, L = length of the sample, e = static dielectric constant, 6 = ratio of free to trapped electron densities, e = electron charge. For the ZnS:Tb crystal, L = 0.5 mm, E = 8.3 €0, Vtr - 20 v, and no = 5 x 10&apos; per cu cm, calculated from the ohmic behavior assuming electron mobility of 100 sq cm per v-sec. This results in 9 = 0= As more and more electrons are injected the Fermi level moves up in the forbidden gap toward the conduction band. If we assume a single-energy level for traps (which is not strictly correct, as we will show later), the current voltage characteristic is profoundly affected when the Fermi level crosses the trap level. The traps are now filled and injected carriers can no longer be immobilized in traps. Hence, current rises sharply with voltage. The transition from space-charge-limited behavior to the trap-filled behavior occurs at voltage VTFL given by

Jan 1, 1968

By Leland E. Paulson

This investigation examined the feasibility of altering the inorganic component of North Dakota lignite by ion exchange. Lignite of specific size consist was washed with various ionic solutions and examined for evidence of exchange. Ions of higher valance substituted preferentially at equivalent concentrations. Results indicate that a major portion of the inorganic material associated with lignite is combined in exchangeable form with the organic component. Particle size of the treated coal is a critical factor in determining the rate of exchange. The data indicate that monovalent ions are easily replaced by divalent and trivalent ions, and the presence of ionic material in slurries containing finely divided lignite significantly increases filtration rates.

Jan 1, 1968

By Sidney Diamond, Charles Wert

The anelastic behavior of Ni-C alloys of nominal 0.5 wt pct C has been determined over a wide temperature range. The most prominent damping effect, that due to the presence of C-C pairs, was measured both above and below the Curie temperature. The effect on diffusion of the C-C pairs by magnetic spin ordering is deduced to be very small. The diffusion coefficient for C-C pairs in nickel is given by the expression ThE solid-state diffusion of both interstitial and sub-stitutional solutes in ferromagnetic solvents has been the subject of a number of investigations. Measurements of the self-diffusion of iron,"&apos; the diffusion of nickel1,4 gold,"1 and cobalt4 into iron, the diffusion of vanadium in an Fe-V alloy,&apos; and the diffusion of cobalt and nickel in Co-Ni alloys9 show an unusual behavior. In both the ferromagnetic and paramagnetic regions, far removed from the Curie temperature, the diffusion coefficient, D, obeys an Arrhenius relation. However, in the ferromagnetic region D is markedly lower than would be expected from an extrapolation of D from the paramagnetic region; this results in an increase in the activation energy in the ferromagnetic region. The cause of this effect for self- and substitutional diffusion is uncertain. Since substitutional diffusion is presumed to proceed by the vacancy mechanism, it has been variously suggested that the increase in activation energy below the Curie temperature is due to one of the following causes: 1) an increase in the energy of formation of a vacancy because of local demagnetization around the vacancy,2,3 2) a decrease in vacancy mobility in the ferromagnetic state,&apos; or 3) an effect on the entropy of motion of a vacancy in the ferromagnetic state.5 Quite another explanation for the observed effect has been proposed by Borg.7 The diffusion coefficient is a function of the elastic constants of a metal. Since the temperature dependence of the elastic constants often changes at the Curie temperature, the temperature dependence of D might be expected to undergo a universal change in the vicinity of the Curie temperature. The magnitude of the change in D would, of course, depend on the magnitude of the change in the elastic constants. One might attempt to differentiate between vacancy effects and elastic effects by making measurements on interstitial alloys, in which vacancy effects play no role. Some measurements of this type have been made; this paper reports additional observations. Measurements of the diffusion of carbon in a Fe by a tracer technique8 and of the diffusion of carbon in a Co and in Co-Fe alloys by a decarburization method9 reveal a small effect, if any, on D of the magnetic change at the Curie temperature. If the effect of spin ordering is only to alter the parameters controlling formation or mobility of a vacancy, interstitial diffusion should indeed remain unchanged through the magnetic transition, as these measurements imply.

Jan 1, 1968

By F. R. Brotzen, L. D. Whitmire

Single crystals of high-purity molybdenum were de-formed at temperatures from 195°to 473°K, and the effect of deformation on the electrical resistivily was deler-mined. To separale the resislivity components of point and line defecls some cryslals were annealed at 473°K. The vale of resislivily increase wilh strain was nearly linear and was strongly dependent upon the deformation temperature. Point dejects are annealed out without any effect on the flow stress. At low temperatures the flow stress is a linear function of the square root of the resistivity increase attributable to dislocations. ELECTRICAL-resistivity measurements have been used successfully to gain information on structural changes in metallic materials. During plastic deformation the electrical resistivity rises because of electron scattering from newly created lattice defects. Such measurements lend themselves, therefore, to corroborating results from direct observation of lattice defects and, to a certain extent, to correlating defect densities and distribution with mechanical properties. Published information on research with single crystals of the bcc metals of Group VI, particularly molybdenum, is still limited. Yet, molybdenum single crystals of relatively high purity can be readily prepared by electron-beam-melting techniques. Furthermore, some valuable information on the defect structure of deformed crystals by direct observation is available. Lawley and Gaigher,1 for example, have examined dislocation configurations in deformed molybdenum crystals by means of transmission electron microscopy. Their results revealed that the dislocation density and distribution were strongly dependent upon the deformation temperature. These findings differed from those by Keh and weissmann,2 who found that the average dislocation density in polycrystalline iron deformed between 138° and 298°K depended only on the degree of strain and not on the deformation temperature. Martin3 and peiffer4 showed that point defects introduced in polycrystalline molybdenum by cold work can be eliminated by annealing at a relatively low tempera-ture. In view of their work it became apparent that resistivity measurements of suitably annealed crystals could disclose changes in their dislocation structure and contribute to the understanding of the work hardening of molybdenum crystals. EXPERIMENTAL PROCEDURE Crystals were grown by electron-beam zone melting5,6 of 0.062-in.-diam molybdenum rods (99.99 pct) supplied by General Electric Lamp and Wire Division, Dover, Ohio. The crystals, about 4 in. long, were prepared by using five zone-refining passes at a speed of about 6 mm per min in a vacuum of about 5 X l0-6 Torr. The resistivity ratio of the crystal, p(4.Z°K)/p(273°K), was generally near 10-3. These crystals were used as tensile specimens of uniform diameter in the "as-grown" condition. They were oriented for maximum shear on the (011)[111] slip system (Schmid factor >0.49). The specimens were held in spherically seated Templin-type grips so as to minimize bending. Samples were deformed on an Instron machine at a strain rate of about 5 X 10-5 sec-1 in an isopentane bath with dry ice at 195°K, in ice water at 273°K, and in a vegetable-oil thermostat at 373° and 473°K. The temperature in the latter was maintained constant within +2°K. Resistance measurements were carried out with a Kelvin double bridge. The resistance of the potential leads was kept low by using large-diameter wires outside the low-temperature bath. Many of the resistance data were checked by measurements made with an ac bridge. Current and potential leads were spot-welded to the specimens. The distance between the potential leads, about 3 in., was also considered to be the gage length for the strain measurements. Diameter and gage length of the samples were measured optically with an error of less than 2 pct. These measurements were used also to insure that the deformation had been uniform over the gage length of the specimen. Resistivity changes were then determined from the resistance measurements at 4.2°K assuming constancy of volume. In the course of a test, the crystal diameter, gage length, and resistance at 4.2°K were determined first in the initial state and subsequently for various amounts of elongation.

Jan 1, 1968

The mineralisation consists principally of layered pyrite, phalerite and galena, situated conformably within a sequence of tuffaceous, bituminous shales and dolomitic sediments that include slump breccias. The sediments show little evidence of post sedimentary reconstitution. A volcanic-exhalative-sedimentary origin is postulated for the mineralisation. Attention is drawn to the similarity between the McArthur deposit and the lead-zinc-silver orebodies at Mount Isa. The primitive nature of the sulphides is reflected by their adverse metallurgical behaviour, and it seems that the best prospect for milling and flotation benefication may lie in the production of separate zinc and bulk concentrates

Jan 1, 1968

By J. J. Bikerman

In a recent study&apos; of the martensitic transformation of Cu-Zn ß-phase alloys, it was noted that the MS temperature at the surface was raised due to the loss of zinc by volatilization. It seems likely, therefore, that the MS temperature may serve as a guide for the measurement of composition. From a knowledge of the dependence of the transformation temperature on composition, 2 it should be possible to detect variations in zinc content which are less than 0.1 at. pct by measuring the MS temperature throughout the sample. It is unlikely that an electron microprobe analysis could detect accurately such small zinc losses because the presently accepted limits of accuracy of the micro-probe analysis in simple ternary systems are of the order of 2 to 5 pct of the amount present.3 In the present study, a composition gradient was produced by precipitating the a primary solid solution, and reheating for a very short time within the 0-phase field. The nominal composition, in atomic percent, of the ternary ß-phase alloy used, 64.2 Cu, 34 Zn, 1.8 Si, was selected because it had an MS temperature of +4°C, thereby simplifying the experi-

Jan 1, 1968

By R. W. Coughlin, W. U. Ault

Experiments in laboratory and mine have clearly demonstrated the usefulness of radioactivity detection for directly measuring the potassium content of potash ore as mined. This paper presents the results of these tests and documents the design of a system for automatically grading and sorting potash ore on the basis of radiation detection. It is shown how the experimental results in the subject mine lead directly to the design of this kind of an automatic control system. The system is capable of grading the ore with an accuracy of approximately ±2% K20 content or better. Due to the usual stratification of the ore body, mining potash seldom presents an extreme problem of gangue separation. Nevertheless, it is frequently necessary to transport within a potash mine and even hoist to the surface considerable quantities of halite and other valueless materials. Up to recent times it has been customary to recognize and route these materials by simple visual and manual techniques. However, the work reported here clearly demonstrates that it is now practical and economical to improve upon these techniques by continuous measurement1 of the naturally occurring radioactive isotope, potassium-40. It was the purpose of the work reported here to investigate this technique and assess its applicability. LOCALE OF EXPERIMENTS The work described here was carried out in a potash mine in Carlsbad, N.M. At the working face of this mine the potash ore is freed by blasting; it is then transported a short distance by shuttle car to a moving-belt system which conveys it to the main shaft where it is hoisted to the surface. Quantities of gangue which are also produced in the mining operation are disposed of in mined-out sections of the mine where possible. Otherwise, this material which contains only a small percentage of potassium (as K2O) must also be transported by the conveyor-belt system to the main shaft and then hoisted to the surface and discarded. With this situation, any measuring device for automatic control purposes must be capable of clearly distinguishing between gangue containing insignificant amounts of K2O and ore containing larger percentages of the same mineral. The conveyor-belt system transports the material from the mine face to a rotary crusher and then to temporary storage pits at the main shaft. This is shown in Fig. 1. Upon leaving the conveyor belt the material enters either one of the two storage pits according to the position of a manually operated gate. It was decided that all experiments should be carried out at the conveyor belt between the crusher and gate with a view to the possibility of providing a signal which could operate the gate automatically. THEORETICAL BASIS AND LABORATORY EXPERIMENTS In principle it is possible to grade potassium-bearing ore on the basis of radioactivity. Natural potassium contains 0.012% K40, which is radioactive with a half-life of 1.3 x 10&apos; years. Although about 89% of the K40 disintegrates to Ca40 by beta decay, the other 11% changes to Ar40 by electron capture and the emission of gamma rays. Unlike the ß-rays which are readily absorbed in the first few millimeters of ore surrounding the disintegrating nucleus, the y-ray photons will escape from an ore sample several inches in size. A detector rigidly mounted under a conveyor belt loaded with potash ore will intercept some constant fraction of all the photons emitted from the ore within its field of view. Under these

Jan 1, 1968

By P. C. Claspy, P. H. Smakula

The electro-optic coefficients of LiNbO, and KTao.,5Nboe3,O3 (KTN) have been experimentally determined at the HeNe laser wavelengths of 0.6328, 1.15, and 3.39 µ. The coefficients were calculated fronz the retardation induced by an applied electric field. The retardations were measured by observing one or move transmission maxima and minima as a function of the applied field, and by measuring the retardation directly with a Babinet-Soleil compensator. The values obtained agree quite well with those previo~lsly reported by others. Extinction ratios as high as 3000:l have been observed. Resistivities and Curie temperatures have also been measured. Light-induced optical inhornogeneities in LiNbO, repovted by others have been observed. CONSIDERABLE interest has recently been shown in the electro-optic properties of LiNb03 (Refs. 1 and 2) and KTN.3, 4 These crystals have a number of advantages over such well-known materials as KDP. These advantages include: 1) the infrared transmission of KTN and LiNb03 extends to 5 p whereas that of KDP cuts off at 1.5 p ; 2) driving voltages required for modulators using these materials are considerably lower than those required for KDP. After first discussing some theoretical considerations of the electro-optic effect, we will report the results of measurements of the dc electro-optic coefficients of these materials at wavelengths of 0.6328, 1.15, and 3.39 p. THEORY The generalized equation for the electro-optic effect can be written: Although lattice polarization is the fundamental variable, rather than the applied electric field, we follow the convention of expressing the linear electro-optic effect in terms of the applied field. For LiNbO the quadratic terms are negligible. Since KTN has a center of symmetry the rijk tensor is 0. After applying the usual symmetry considerations and index contractions,* the rijk and gijkl tensors can be expressed as follows: LiNbOaT If field directions are now chosen, the change in refractive index and the angle between the induced optic axes and the crystallographic axes can be found. The induced rotations of the principal axes of the index ellipsoid for fields in principal crystallographic directions are given in Table I. Since KTN is initially isotropic, the principal axes in the zero-field condition are parallel to the crystallographic axes. The induced retardations are given in Table 11. EXPERIMENTAL We obtained the various electro-optic coefficients by measuring the induced retardation as a function of

Jan 1, 1968

By A. G. Starliper

The Bureau of Mines made laboratory investigations to determine the feasibility of utilizing fine tungsten wires to reinforce a number of nonferrous metals and alloys and a superalloy, S-8l6. The composites of tungsten filament and metals were chosen to attain elevated temperature strength and corrosion resistance. Oriented clean or precoated tungsten wires were incorporated with the other metals by extrusion, swaging, and infiltration casting. Although widely varying characteristics were found in the composites, none were considered satisfactory for high-temperature use, chiefly because of reactions between the matrix metal-tungsten surface. Diffusion, solution, and chemical reactions between matrix and tungsten wires were sufficiently slow for some combinations, such as 15 v/o 8-816, to exhibit increased high-temperature strength for a limited time. A few metals failed to wet or bond to the tungsten surfaces, while a few responded after precoating with a third metal.

Jan 1, 1968

About 11,000 tons of contaminated zinc flotation concentrate were available in the form of earth walls from dams used for atmospheric drying of the concentrate.Following successful laboratory tests this material was treated in a plant by crushing, grinding, and then flotation in a circuit consisting of roughing, scavenging, and two stages of cleaning. Reagents used were copper sulphate and a little butyl xanthate and frother. About 5,720 tons of zinc concentrate assaying 52&#183; 3 per cent zinc were produced.

Jan 1, 1968

By T. R. Cass

THE renewed interest in titanium, resulting from its increasing application as a structural material, has stimulated basic deformation studies on this metal. In the course of our work, we have developed a dislocation etchant and applied it to a perfection study of melt-grown single crystals as well as to a preliminary investigation of plastic deformation in titanium. The etchant, Keller&apos;s etch (21 cu cm HF, 64 cu cm HC1, 106 cu cm HNO3, and 160 cu cm H20), reveals the emergence of both grown-in and fresh dislocations on pure titanium and a-phase Ti-Al single crystals. Pits are produced only on surfaces within a few degrees of the basal plane; the more exactly parallel to a basal plane the surface is, the more distinct are the pits. The observed pit density, however, does not appear to depend on the surface orientation; the pits simul- taneously become less distinct as the misorientation from a basal plane increases. Etch times are short, a few seconds, for pure titanium; longer times are necessary for alloy crystals.

Jan 1, 1968

By David L. Sikarskie

The measurement of residual stress fields using X-ray diffraction techniques requires the removal of successive layers of material from the specimen. In the process of removing these layers, the underlying residual stress field is altered; hence, if the original stress field is desired, corrections must be made to the measured stresses. Although these corrections already exist for a number of cases, an alternate procedure is outlined herein whereby the corrections are presented in series form. This form is numerically more convenient within certain ranges of correction depths and in its simplicity gives additional insight into the factors affecting the corrections. It, further, readily permits determining the proper slice depth to remove and the effect on the correction of both specimen thickness and magnitude and form of the measured residual stress itself. ONE of the techniques currently being used to determine residual stress fields is X-ray diffraction. Since X-rays are diffracted essentially from the layers of atoms near the surface of the specimen, of the order of 0.0001 to 0.001 in. depending on conditions, the method can only determine stresses* in this very thin surface region. Therefore, if the residual stress field at some depth into the specimen is required it is necessary to remove successive layers of material taking measurements after each cut. In the process of removing a thin surface layer of stressed material, however, the over-all equilibrium of a cross section of the specimen is disturbed with the result that the internal residual stress which existed before the slice of material was removed is altered. This alteration of stress occurs after each slice and its effect is cumulative. Thus, if the original stress distribution is desired, corrections must be applied to the measured stresses. These corrections can be found by satisfying equilibrium on each new cross section. These corrections have been derived in detail for a number of cases, e.g., cylinders, bars, plates,&apos; and also are given in Appendix VI of Ref. 2. In each of the above cases the correction terms require the evaluation of definite integrals of the measured residual stress distribution. In general, this is indeed the way one would proceed with the corrections. There are a number of instances, however, where the integrals can be replaced by a series form of correction which is considerably more convenient numerically and, also, gives added insight into the factors which influence the corrections. Such a form of the correction is particularly useful, for example, if one is interested in designing a test such that stress corrections will be small. Also, the question of what depth of slice to use in relation to both specimen thickness and residual stress distribution itself must invariably be answered. Questions of this type can be readily answered using a series form of correction. In addition, if the correct residual stress distribution is needed only for limited depths into the specimen the series correction provides numerical results which are equivalent to the integral correction. I) DERIVATION OF THE SERIES CORRECTION The problem to be considered here is that of a bar or plate,* i.e., either one or two dimensions of the specimen is large compared with the third. Also, the residual stress distributions considered depend only on z, see Fig. 1. In view of this it can be shown&apos; that a stress correction, based on simple beam theory, satisfies all conditions of "elasticity theory" and hence is the correct (and only) solution. The integral form of the correction (this assumes that the measured residual stress is a piecewise continuous function) as given in Ref. 1 is:

Jan 1, 1968

By William Paxton Hewitt

Mineral deposits of western Utah and eastern and central Nevada have produced in excess of $8,500,000,000 since 1871. Through 1965, Bingham Canyon had produced over $4,600,000,000 and seven other camps over $100,000,000 each, principally from base metals. In addition, they yield iron and uranium ores; contain the world's largest beryllium reserves; and have produced the United States' most important gold discovery in 25 years. The area is famous for its silver production and its bonanza-type precious metal deposits, but such production has become unimportant. The area's greatest producers of metallic wealth are base-metal deposits in limestones and porphyry-type copper ores. In contrast to silver's decline, gold production has been rising-the result of by-product operations at Bingham Canyon. The area also contains gold deposits in which the gold is so finely disseminated it is not recoverable by panning. The area's gold ores frequently are associated with realgar, cinnabar, and carbon. The ore deposits generally are attributed to Tertiary intrusives,* but, at Mountain City, they may be related to Paleozoic volcanism. Mountain City has yielded rich chalcocite from quartz-pyrite-chalcopyrite bodies in siliceous sediments. Regional stratigraphy and structure are difficult to interpret, 69 per cent of the area being obscured by alluvium or volcanics. In general, central Nevada consists of chert, shale, silty sandstones, lavas, and pyroclastics; eastern Nevada and western Utah of many alternations of limestone, shale, and sandstone. Central Nevada has been structurally active since late Devonian. Although granitic stocks may have intruded eastern Nevada and western Utah prior to the Cretaceous, these areas remained quite stable until affected by the Laramide Revolution. Precambrian exposures, occupying 3 per cent of the area, have not been important hosts. However, the question is raised as to whether Precambrian carbonates, properly situated with respect to invading mineralizers, might yet prove to be important. This paper describes 16 precious metal camps, 6 limestone replacement districts, 2 silver-base metal vein deposits, and 9 miscellaneous types and discusses briefly the 11 * Some ores, as at Ely, are associated with intrusives of. Cretaceous age. major camps that are described in detail in this Volume.

Jan 1, 1968

By T. F. Bower, M. C. Flemings

The classical explanation for formation of the fine equiaxed "chill zone " in ingot solidification is that local supercooling near the chill wall causes copious nucleation in this region. This work indicates, however, that convection is an essential element in formation of the chill zone. In the absence of convection, no chill zone forms even though rate of. heat extraction is extremely vapid. Alloy studied was Al-l.5 pct Cu alloy solidified against a copper chill wall. When solidification was initiated at the chill wall in absence of. cor-vection, surface grain size was large (>I cm diam). When it was initiated in the presence of convection, it was fine (<0.05 cm diam). It is concluded that some form of "crystal multiplication" plays an important role in formation of the chill zone. INGOT macrostructures are generally classed as containing one or more of the three zones: "chill zone", "columnar zone", and central "equiaxed zone". These three zones are sketched in Fig. 1; their origin has been discussed in some detail.&apos;-&apos; The classical explanation for formation of the chill zone is that supercooling occurs in the region of liquid metal adjacent the mold wall, and copious nu-cleation then takes place in this region forming numerous small crystals. The columnar region then results by growth of favorably oriented grains (den-drites) which crowd out their less favorably oriented neighbors."5 The mechanism of the columnar-equiaxed transition has been the subject of considerable interest. The generally accepted mechanism, until recently, was that constitutional supercooling developed in front of the growing columnar grains with eventual nucleation of new, equiaxed, grains ahead of the growing solid front.&apos; Recently, it became evident this explanation was not completely satisfactory and it is now evident that "crystal multiplication" plays an important role. This crystal multiplication occurs by separation of dendrite arms from growing dendrites,8?"&apos; and has been shown to be strongly influenced by convection.6, 10-13 Reduced convection results, for a given alloy, in longer columnar zone, larger columnar grains, and larger equiaxed grains.7, 12

Jan 1, 1968

By J. C. Rudolph

"THE TOPIC on which I am speaking this afternoon is ""The Future of the Canadian Oil Industry.'' At the time of C + 100, we should take a searching look at ourselves, an honest appraisal of our achievements and a forthright accounting of our shortcomings as well as the uniquely Canadian aspects of this industry. I would like to put before you some of my views on the direction we are taking in the exploration field and in the production field. I would also like to speak briefly on some of our problems and the role of the various segments of our industry in solving these problems.First of all, let us look at the exploration picture. We are in the midst of an exploration boom. There were 133 seismic crews active in Western Canada this winter, the highest since 1957, land prices are appreciating rapidly, Canadian oil reserves increased + 16 per cent during 1966, there is a great demand for technical personnel of every kind and the whole industry, except the drilling segment, seems to be prospering. This surge of activity has its roots in two major occurrences. The first of these was the change in the pro-ration system in Alberta, the major producing province, accompanied by the change in spacing pat-terns. The proration change was designed primarily to encourage in-creased exploration and it has certainly had this effect. It has also had the unforeseen effect of put-ting everyone into what we, in the oil business, call ""elephant hunting."" In other words, the days of the development of barely economic, marginal fields are over. Oil companies today are only interested in high-reserve, high-productivity, high-quality reservoirs."

Jan 1, 1968

By Herbert R. Babitzke

The purpose of this investigation was to optimize the high-temperature properties of columbium and tantalum. Columbium and tantalum were combined with selected alloying elements to achieve solid solution and dispersion strengthening. Fifty-six alloys were evaluated to determine their formability, hardness, strength at elevated temperatures, and oxidation resistance. The following six alloys showed high-temperature strength: [Cb-15Hf-5W-2Zr-4Al-4Ti-2N Cb-15Hf -5W-5Zr Cb-15.3Ti-4.1Zr-13.7Hf Ta-20Hf-4Al Ta-30Hf-4Al Ta-20Hf-5W-4Al] At 1,200° C, the columbium alloys had strength values of 40,000 psi or greater, and the tantalum alloys had strength values from 50,000 to 58,000 psi. For a 2-hour test period at 1,000° C, weight gains of only 9 and 8 mg/cm2, respectively, were observed on oxidation testing of two alloys, Cb-15Hf-5W-2Zr-4Al-4Ti-2N and Ta-20Hf-5W-4Al.

Jan 1, 1968