Search Documents

By O. B. Horne, R. O. Morgan, C. E. Anderson

"Air-photo interpretation and photogrammetry are two of the most effective and versatile tools available to the petroleum industry. The techniques have proven successful in providing solutions to many of the problems encountered in the design and construction of oilfield projects.Although most technical personnel are aware that air-photo interpretation and photogrammetry are useful in the selection of routes for roads and pipelines, few realize the true scope of the techniques or the wide variety of areas in which they are applicable.This paper briefly describes the principles involved, and reviews a number of typical applications of particular interest to petroleum companies. Excessive detail is avoided, rather the emphasis is placed upon the wide spectrum of possible applications. It is stressed that on-the-ground examination generally is a necessary adjunct, and that there are certain limitations to the techniques discussed.Properly applied, however, air-photo interpretation and photogrammetry can offer significant advantages in terms of time, flexibility, secrecy and economy."

Jan 1, 1968

Jan 1, 1968

By J. L. Reuss

The Bureau of Mines derived information on the softening characteristics of both unfired and indurated iron ore pellets as measured by hot compression strength in a laboratory study. A surprisingly high hot strength (240 1b per ½ -inch spheroid) was developed by unfired magnetite pellets near 900° C; lesser maxima were developed by pellets made from hematite and specularite concentrates near 1,000° C. Those from goethite remained weak throughout the pre induration heating. Fully indurated commercial pellets retain a high resistance to softening when heated in air. On the contrary, in a hot reduing atmosphere their high cold crushing strength dissipates rapidly. At 1,000° C, for example, the average compression strength of seven different commercial pellets was 110 lb; at 1,100° C, the hot strength was only 60 lb. After a rather sharp initial drop, the loss of strength with increase of temperature was gradual. There was no sudden collapse, nor any significant difference, in behavior of commercial pellets whether made from magnetite or hematite concentrates.

Jan 1, 1968

By T. L. Berger, M. C. lnman, M. F. Rose

AFTER shock loading, mechanical twinning has been observed by several authors1-4 for a variety of fcc metals and alloys. It has been shown2,3 that low stacking fault energy materials deform primarily by the formation of mechanical twins and stacking faults during dynamic loading. Further, Inman, Murr, and Rose2 have shown that a correlation exists between the average hardness and the volume percent of mechanically twinned material in stainless steel. It has been observed in nickel' that mechanical twins are produced during shock deformation if the peak pressure associated with the shock wave is greater than 350kbar. It is the purpose of this work to discuss shock-hardening mechanisms in nickel and to determine to what extent the initial condition influences the final response. The "flying plate technique" was used to generate planar shock waves with peak pressures as high as 710 kbar. The details of the technique5" have been discussed elsewhere and will not be repeated here. The material used in this study was polycrystalline nickel of 99.98 pct purity and had an initial grain size of 0.18 mm. Prior to any deformation, all samples were given a stress-relief anneal of 6 hr at 600°C in a vacuum furnace. After annealing, the initial condition of the samples was changed by cold rolling individual samples from 0 pct to a maximum of 80 pct reduction in thickness. This provided samples with controlled initial histories for shock deformation. Immediately after shock loading, the specimens were slowed and quenched by suitable arrangement of buffer material and water bath. This technique minimized specimen damage and the effects of shock heating on the samples. Since deformation twins in high stacking fault energy fcc metals are only produced at high stress levels, the initial defect configuration prior to mechanical twinning should greatly influence the number of twins formed. In fact, Zukas and Fowler7 have found that prestraining in iron and steel greatly suppresses the formation of mechanical twins during the shock deformation process. Following the methods of Warren and warekois8 and Cohen and Wagner,9 X-ray diffraction profile analysis was performed to determine the incidence of stacking faults and mechanical twins in the deformed nickel. Analysis was made on samples in the annealed, cold-rolled, shock-loaded, and cold-rolled—shock-loaded states. The estimated accuracy of the peak position measurements is *0.01 deg in 2?. Therefore the accuracy in the measurement of the relative peak shifts between the (400) and (222) diffraction line profiles is on the order of *0.04 deg in 2?. None of our measurements indicated peak shifts greater than 0.04 in 28. This would correspond to a fault density of -1 pct and sets the limit on the sensitivity of our instrument. Similarly, analysis of the shift in the center of gravity of the diffraction line profiles yields the minimum measurable value of the twin fault probabilitya to be -0.002. Fig. 1 shows mechanical twinning in nickel shock-loaded to 400 kbar. In this photograph, fault intersections are clearly visible. The thickness of the individual fault lamellae was determined from the image widths of their lines of intersections by the

Jan 1, 1968

By John B. Shutack

In an effort to improve the performance of the explosive-anchored rock bolt, the Bureau of Mines studied the effect of the detonation velocity of the explosive and type of charge (linear or nonlinear) on the fracturing tendency of the anchor tube. Also, different types of tubing were compared to determine the one most suitable for use as an anchor tube. The Bruceton up-and-down method was applied in tests in which steel shooting blocks having boreholes ranging from 1-3/8 to 2-1/8 inches in diameter were used. Of the four types of tubing evaluated, a welded A-178 tubing that was drawn over a mandrel and renormalized gave the most promising results. The A-179 seamless tubing that is normally used with the explosive bolt was the most inferior. Both types, however, gave significantly better anchorage than the conventional shell when tested in both laboratory and underground experiments. Within the range of velocities studied (5,000 to 7,000 m/sec), the type of explosive showed no significant effect on anchor-tube performance. In general; linear explosive charges provided better anchorage than nonlinear charges.

Jan 1, 1968

By Raymond F. Gray, Victor J. Hoffman, Richard J. Bagan, Harold L. McKinley

The first indication of tungsten in the Bishop area was the discovery of scheelite concentrations in a gold placer operation in the ( since named) Tungsten Hills in 1913. After early intermittent production, the deposits of the district were slowly discovered and developed. The Pine Creek mine, located in 1916 and under the direction of Union Carbide Corporation since 1935, became the principal producer in the district. By the end of 1965, the total production of the district had reached 3,450,932 units of WO3, 17,071,242 pounds of molybdenum, and 19,599,110 pounds of copper. The topography of the district is characterized by its extreme relief, ranging in elevation from 13,986 feet to about 4400 feet in the Mount Tom quadrangle. The present topography is the result of the uplift and erosion of the Sierra Nevada and the great subsidence of the Owens Valley with its related deposition and volcanism. The general structure of the pre-Tertiary rocks consists of a series of tightly-folded metasedimentary and metavolcanic rock remnants surrounded by exposed plutons ranging in composition from hornblende gabbro to alaskite. The metasedimentary rocks consist of low- to intermediate-grade metamorphic equivalents of fine-grained sediments deposited during the Paleozoic era in a miogeosynclinal environment. Later volcanics were deposited in a eugeosyncline. The ore bodies in the Bishop district consist of scheelite-bearing tactite formed by the pyrometasomatic replacement* of calcareous sediments along the contact with an acidic granitic intrusive. A number of the metasedimentary remnants have had tungsten deposited along their edges.

Jan 1, 1968

By C. E. Brukl, E. Rudy, St. Windisch

The ternary-alloy system Nb-Mo-C was investigated by means of X-ray, melting point, DTA, and metallo-graphic techniques; a complete phase diagram for temperatures above 1500°C was established. Above 1960°C, niobium monocarbide and the cubic (Bl) high-tenzperature phase in the Mo-C system form an uninterrupted series of solid solutions. The ternary range of the pseudocubic q MoCl-, is very restricted. Dimolyb-denum carbide dissolves up to 44 mol pct Nb2C (2240°C), whereas the maximum solid solubility of MO2C in Nb2C does not exceed 5 mol pct. The order-disorder transformation temperatures in Mo2C and Nb2C are lowered by the mutual metal exchanges. Six invariant (p = const) reactzons occur in the ternary system; three correspond to class 11-type four-phase reactions involving a liquid phase, one to a class I (eutectoid)-type, and two further isotherms are associated with limiting tie lines. The results of the Phase diagram investigation are discussed, and the thermodynamic interpretation identifies the low relative stability of the binary sub-carbides in conjunction with the large stability diflerences between niobium and molybdenum carbides as the cause for the formation of a stable equilibrium between the monocarbide and the metal phase in the ternary reson. Due to their refractoriness, the carbides of the high-melting transition metals have received increased interest in recent years as base materials in composite structures for aerospace applications at high temperatures and for the development of self-bonded cutting tool materials; other novel fields of application include power reactors, where operation at high temperatures becomes essential for attaining high power efficiencies. In these applications, the increased reaction rates at high temperatures require a close consideration of the chemical interactions between the alloy constituents. As a consequence, a detailed knowledge of the phase relationships in the alloy systems is required in order to provide a sound basis for developmental -type work. Partly as a result of the considerable experimental difficulties associated with the investigation of this high-melting alloy class, no complete studies of ternary metal-carbon systems have been performed until recently. Even the high-temperature phase relationships in the binary transition metal-carbon systems have been delineated only during the past few years to a degree of accuracy required for a more detailed study of ternary or higher-order alloys. In recent investigations of binary and ternary systems of refractory transition metals with carbon, boron, and silicon,&apos; alloys from the ternary systems Nb-Mo-C became of interest because of the demonstrated possibility2,3 of obtaining compatible composites based on metal + monocarbide combinations. In the meantime, however, studies in other, but related, ternary metal-carbon systems, such as Ta-W-C, have shown that the solid-state equilibria may change significantly toward higher temperatures (>2000°C), and that extrapolations based on low-temperature equilibrium data are, in general, not very reliable. Although the lower-temperature (<2000°C) phase relationships in the Nb-Mo-C system are similar to those found in Ta-W-C, a cursory thermodynamic analysis of the equilibria indicated4 that complete solid-solution formation between Mo2C and Nb2C should not occur at higher temperatures. The present work was conducted in order to experimentally verify these expectations and, in addition, to provide phase equilibrium data in the melting range of the alloys. In the boundary systems, niobium and molybdenum are known to form a continuous series of solid solutions.576 The continuous solubility was also confirmed by Kornilov and Polyakova,7,8 who also observed a minimum melting point at 22 at. pct Mo and 2345°C. The phase diagram investigations of the Nb-C system by Storms and Krikorian9 and Kimura and Sasaki10 were recently supplemented by Rudy et al.11,12 The system contains a high-melting monocarbide with the B1 structure, Table I, and a subcarbide, Nb2C, which exists in at least two different states of sublattice order at low temperatures47"-&apos;3 and a disordered state above approximately 2500°C.11,12 The melting-point measurements by Rudy et al .11,14 are in close confirmation of the data by Kimura and Sasaki.10 The rather complex phase relationships in the Mo-C system were only recently Clarified.15,18 The system is characterized by three congruently melting, intermediate phases, MozC, ? MoC1-x and a Mol-,, Table I, of which only Mo2C is stable at temperatures below 1650°C. Substoichiometric MozC exists in several states of sublattice order which interconvert in homogeneous phase transitions. Hyperstoichiometric compositions cannot exist in the ordered state. Upon cooling through a critical temperature range, the

Jan 1, 1968

By M. Adnan Goksel

The hydrothermal agglomerating process described (U.S. Pat. 3,235,371, (1966)) is different from the conventional high temperature processes. Green pellets or briquettes made with mixtures of moist iron ore concentrates and burned or hydrated lime fines are hardened in an autoclave at 198°C and under steam pressure for 1/2 to 5 hours, with or without previous drying. Under the neutral conditions, oxidation of magnetite does not occur as in the conventional processes. The resulting agglomerates are hard and resistant to abrasion and weathering, and they do not disintegrate in the Linder test. The equipment required for the process is not complicated, and favorable operating costs are projected because of the low temperature and efficient heat recuperation. A low capital investment makes the process attractive even when the annual pellet production is below a million tons.

Jan 1, 1968

By Karl C. Dean

The Bureau of Mines studied the precipitation of copper from dilute acidic sulfate solutions using shredded automobile scrap in a rotary drum. The tests established that the scrap in the rotary drum precipitated copper faster and more completely than shredded, detinned, tinplate scrap in a launder, with comparable iron consumption. Although power is required to rotate the drum, the faster precipitation and continuous recovery of cement copper are advantages of the tumbler method. Cost evaluation indicates that the rotary drum method, which uses relatively low-cost and readily available shredded automobile scrap, is competitive with the launder method, which uses relatively high-cost shredded tinplate scrap or detinned shredded cans.

Jan 1, 1968

By Robert W. Holliday

Natural resources are the reservoir from which society draws its material sustenance. Although there is a growing awareness of the need for aesthetic resources such as space for recreation and natural beauty, the basic resources are soil, air, water, and minerals including fuel. Minera&apos;s and all sources of energy gain in relative importance with advancing technology and expanding industrilization. In the highly industrialized economy of the United States, almost every aspect of man&apos;s life is touched in some way by a product of, the mineral; industries. Agriculture owes much of its productivity to mineral-based fertilizers, insecticides, and mechanical equipment. Modern construction, manufacturing, communications, and transportation are all dependent on nonmetallic minerals, metals, and fuels. Throughout history, those nations with access to minerals, and the technology for using them, have gained ascendency. Before World War II the leading powers also were, leading coal producers. In order of declining rank the five leading&apos; coal producers were the United States, the United Kingdom, Germany, the USSR, and Japan. That the military victory went to the side with the greater&apos; capacity to convert iron and coal into tools of industry, and weapons, is&apos; more than coincidence. It is a fundamental&apos; fact of existence. It is axiomatic that the United States must have a continually increasing supply of minerals if we are to meet the needs of our burgeoning population for a comfortable standard of living and for national security.

Jan 1, 1968

By H. H. Kellogg

A model of the slag-fuming process for recovery of zinc oxide fume from lead blast furnace slags, adapted to solution by a digital computer, is presented. The model incorporates the variaticm with time of the following: the fuming of zinc and lead, the change in the ferrous-ferric ratio in the slag, the transfer of sulfur to and from the slag, the temperature of the liquid slag, the temperature of the gases and fume which exit to the flue, the heat losses to the water jackets, and the amount of frozen slag on the water jackets. The assumptions which underlie the model-some of which are but crude approximations—are discussed. Despite some obvious shortcomings, the model simulates faithfully many of the important features of practical slag-fuming operations. The behavior of the model is compared with the operation of the American Smelting and Refining Co. fumzace at El Paso, Tex. The model is used to predict the effects on performance of changes in the coal rate, the temperature of the secondary air, and the composition of the coal. THE fuming of lead blast furnace slag for recovery of zinc oxide is standard practice today, and it has been the subject of several previous attempts at mathematical process analysis.&apos;-&apos; The mathematical process model described in this paper incorporates many of the features from the earlier studies, but it is a far more complete and realistic representation of the commercial process in that the following additional features have been included: the fuming of lead as well as zinc; the transfer of sulfur between slag and gas; the addition of slag feed in batches, over a period of time; tapping of the final slag over a period of time; the change of slag temperature with time. The additional features of the present model add greatly to the mathematical complexity, but this difficulty has been obviated by programming the model for solution by a digital computer. The IBM 7094 computer solves the model for one operating cycle of the fuming furnace in less than 1 min. It is doubtful if the same calculations could be completed with the aid of a desk calculator in less than a month. The computer program, written in the Fortran IV language, is too lengthy for presentation here.* Instead, this paper As shown in the sections which follow, it does simulate with remarkable faithfulness most of the known behavior of the industrial process. On the other hand, the model contains several gross simplifications of both the chemistry and heat balance, necessitated by the lack of more exact knowledge. In addition to these known weaknesses, it is not unlikely that those more intimately acquainted with industrial practice than the author will find other additions to or modifications of the model which will improve its utility and reliability. CHEMISTRY In brief outline, the present model treats the fuming furnace as two units, A and B, in series. In A the batch of slag reacts with the continuous stream of air (primary and secondary) and fuel injected at the tuyeres, to produce a stream of hot, reduced gases containing zinc vapor. The zinc content of both the slag and the product gas changes with time because of the batch nature of the process. Unit A is called the "lower furnace" in this paper; physically, it is considered to be that part of the fuming furnace which lies below the charge port. In B, the "upper furnace", the product gas from A is burned with the stream of "tertiary" air, to produce zinc oxide fume. The performance of B also depends on time because of the time dependence inherited from the product gas of A. The rate behavior in the lower furnace determines the important features of the process—the rate of elimination of zinc and lead from the slag, and the amount of fuel required for this purpose. Bell, Turner, and peters&apos; published the first useful model of the lower furnace. They employed the assumption that, at any instant of time, the slag and reduced gas reach a state of equilibrium, according to the reactions: They cited only indirect evidence in support of their assumption of slag-gas equilibrium, yet several more recent laboratory studies of the activity of zinc oxide in slags4-8 have produced evidence which supports their view. On first acquaintance it seems unlikely that a high-output "rate" process like slag fuming would even approach an equilibrium state. The author, in an earlier study,&apos; established, however, that the gas-slag interface in a fuming furnace was capable of such high mass-transfer rates that a close approach to equilibrium between gas and slag was quite probable. In devising the present model it was decided to assume a state of equilibrium between slag and gas at the outset, and then to modify this assumption as necessary in order to make the model agree with the be -havior of the actual process. Up to this time the assumption remains a part of the model, since no behavior

Jan 1, 1968

By Eugene A. Mizikar

A mathetnatical model of heal transfer in continuously cast steel slabs is described. The model, consisting of a unidimensional transient conduction equation and boundary condition equations, has been pvogrammed for computer solution. Temperatuve and solidification profiles calculated for a 6-in. slab, being cast under several conditions of secondary cooling, are presented and compared. Calculated solidification profiles are in agreement with reported expevinle~ztal values. For the mold zone, the predicted slab shell thickness can be described by: Resuilts of the study indicate that multibank spray cooling followed by radiant cooling should be employed when solidifying thick slabs with minimum surface temperature of 1600°F. Under these conditions, a 6-in. slab can be expected to solidify in about 8.3 min. Computer results also indicate that radiant cooling can replace spray cooling during solidification of the final 30 pct of slab with little increase in overall solidification time. CONTINUOUS casting has come to the forefront of the steel industry in recent years because of economic advantages resulting from increased yields and elimination of several processing steps. Considerable work, however, remains to be done regarding modifications to the process and operating procedures. Both a lack of operating plants in this country and the experimental difficulties associated with direct measurements on moving castings have made determination of solidification rates and temperature distributions difficult. An alternate approach is to mathematically simulate heat transfer in a continuously cast section, and then calculate the temperature distributions as a function of the controllable variables of the process. Simulation of heat transfer during solidification requires that a nonlinear mathematical problem be solved. As pointed out by Ruddle,&apos; there are two mathematical approaches to the problem- the analytical approach and the numerical approach. While the analytical approach is certainly the more elegant of the two, it does require a number of inexact assumptions because of the complexity of the problem. For example, noteworthy analytical treatments of heat transfer in continuous casting have been developed by Savage Hills,3 and pehlke4 only by making one or more simplifying assumptions such as invariant thermophysical properties, constant heat-transfer coefficients in the mold, and linear temperature profiles in the shell. Simplifying assumptions such as these can introduce considerable uncertainty in the validity of results calculated with analytical solutions. Numerical solutions, which are considerably more versatile, appear to be better suited for solving solidification problems. Complex variations in the boundary conditions and variable thermophysical properties can be handled readily with this technique. Whereas numerical computations can be long and tedious when done by hand, results can now be obtained quite rapidly with the use of either the digital or analog computer. Several numerical models of heat transfer in continuous casting have been published. In 1963, Adenis, Coats, and Ragones published a numerical model used to calculate temperature distributions in direct-chill-cast magnesium billets. More recently, Donaldson and Hess 6 presented results obtained with a numerical computer model of heat transfer in continuously cast steel billets. In the present study, a model of unidimensional heat transfer in continuously cast slabs is presented. The method of solution on a digital computer is also included. Calculated temperature distributions and solidification profiles for various schemes of secondary cooling along with attempts to verify the model are also discussed. MATHEMATICAL MODEL The schematic representation of the slab continuous casting process in Fig. 1 illustrates that the slab passes through three distinct zones of cooling. Accordingly, the mathematical model consists of three parts: 1) solidification in the mold; 2) solidification in the spray cooling zone ; 3) solidification in the radiant cooling zone. Heat-Transfer Equations. The model was developed bymaking a heat balance on a horizontal slice of slab over the time period required for the slice to proceed from the liquid metal meniscus in the mold to the cutoff station. As shown in Fig. 2, the imaginary slice extends from the center line to the surface of the slab. As the slice moves downward, heat is conducted from the center line to the surface of the slab at a rate governed by the surface boundary condition and thermophysical properties of the metal in the slice. The following partial differential equation describes the conduction of heat in a medium moving at velocity U in direction Z:

Jan 1, 1968

A paper describing the treatment of the Mary Kathleen uranium ores must necessarily be historical and confined mainly to a review of the four papers which have already appeared. Couche and Hartley (1958) described the development of the treatment process just prior to the commencement of operations in June, 1958. Harris, Boag and Hemingway (1961) described the treatment during the operations, and Wreford (1965) reviewed all aspects of the mine and mill, when operations were suspended in November, 1963. Harris and Steele (&apos;1960 presented a paper especially describing the radiometric sorting operation. Some hitherto unpublished information is also presented in the paper to describe some of the peculiarities of the ore, indicate reasons for the adoption of the treatment flowsheet, and some interesting problems connected with this treatment.

Jan 1, 1968

By Raymond C. Boettner

The present work had for its purpose: 1) the identification of crack nucleation sites in AISI 4340, quenched to martensite and tempered over a range of &apos;temperatures; and 2) the comparison of fatigue processes in AISI 4340 with processes observed previously in pure metals From constant def1ection-bending fatigue tests, martensite boundaries were identified as the favored crack nucleation sites in quenched and tempered AISI 4340. It, also, was concluded that the fatigue processes operating- in this lous-alloy steel were similar to Processes observed in pure tnetals. ALTHOUGH much engineering data has been accumulated on the fatigue properties of quenched and tempered martensitic steels,&apos; fatigue as a process is not as well understood in martensite as it is in pure metals.&apos; Important features of the fatigue process, such as the identity of the nucleation sites, have not been determined in the commercially important high-strength low-alloy structural steels. The present work had for its purpose: 1) the identification of crack nucleation sites in a low-alloy steel, i.e., AISI 4340, which had been quenched to martensite and tempered over a range of temperatures; and 2) the comparison of fatigue processes in the AISI 4340 with processes observed previously in pure metals. This comparison of the fatigue processes in the different tempers was restricted to the high-strain low-cycle part of the S-N curve. Under these test conditions, previous work on a number of metals has shown that a large number of cracks are nucleated in less than 30 pct of the fatigue life.3 Furthermore, crack nucleation sites are not restricted to inclusions but are also associated with intrinsic structural characteristics of the metal. MATERIAL A 20-lb ingot of vacuum-melted AISI 4340 (for composition see Table I) was hot-rolled to 1-in.-diam rod and then cold-rolled to a 1-in.-wide strip, 0.08 in. thick. Fatigue specimens, see insert of Fig. 1, were machined from the strip with the long dimension parallel to the rolling direction. m this orientation, the stringers of 1 to 2 p inclusions present in the sheet lay parallel to the stress axis in the specimens. The specimens were austenitited at 2050°F in order to obtain a large prior austenite grain size, i.e., 2 mm, which facilitated the subsequent identification of the prior austenite boundaries. A helium atmosphere was used to minimize decarburization. After austenitiza-tion at 2050°F, the specimens were transferred to a 1450°F furnace so that specimen distortion was held to a minimum in the subsequent oil quench. Previous work4 indicated that refrigeration in liquid nitrogen prior to tempering reduced the percentage of retained austenite in the quenched specimens to less than 5 pct. Tempering was carried out in air over the temperature interval of 200°to 800°F to produce a range of mechanical properties, Table I. The preparation of the fatigue specimen was completed by grinding about 0.005 in. from each surface and electropolishing in a chrome trioxide-acetic acid solution for 30 min. Examination of etched cross sections of specimens prepared in this fashion showed the foregoing specimen preparation to be adequate for the removal of the decarburized layer present after the heat treatment. Transmission electron microscopy showed that the as-quenched microstructure of this alloy consisted of a mixture of martensite plates containing either a high density of dislocations or microtwins. Previous work5&apos;6 indicated that in the course of oil quenching autotem-pering resulted in the formation of E carbide on the martensite and microtwin boundaries. Tempering for 2 hr at temperatures up to about 400°F resulted in further precipitation of the E carbide. Finally, at about 400°F, cementite began to replace the E carbide on the martensite and microtwin boundaries in addition to forming a Widmanstatten structure within the plate matrix. EXPERIMENTAL S-N curves were obtained using electropolished specimens cycled at 1800 cpm as cantilever beams in fully reversed bending at selected constant deflections. The deflections were translated into surface strains by means of a calibration curve obtained through the use of strain gages. An argon atmosphere was used to minimize environmental effects. To investigate the development of fatigue slip bands, the specimens of the different tempers were unidirec-tionally bent to a surface strain of 0.005 to 0.007, photographed to record the location and appearance of slip bands so introduced, and then cycled to failure

Jan 1, 1968

By R. B. Schluter

Magnetite pellets were simultaneously reduced and indurated on a laboratory scale in order to determine the effects of temperature, induration time, degree of metallization, and sulfur content upon the physical and chemical properties of prereduced pellets. The reductants were commercially-pure tank gases. Among the findings were these: 1,100° C is the minimum temperature that will produce acceptably hard pellets using carbon monoxide as the reduc-ing gas. Prolonged treatment time improves the pellets&apos; crushing strength, but the rate of improvement falls off sharply after 2 hours&apos; induration. At 1,120° C, 75-percent metallization produces the maximum crushing strength; there was no corresponding peak at 900° or 1,050° C. Sulfur in the furnace atmosphere lowers the required induration temperature. A few tenths of 1 percent sulfur in the pellet increases the sintering rate of metallic iron in pellets by forming a liquid FeS phase that facilitates iron transfer.

Jan 1, 1968

By R. P. McNitt

TITANIUM hydrides have received considerable study in recent years because of the adverse effects of the hydrides on mechanical material properties such as ductility and tensile strengths. Generally speaking, as the hydrogen content increases, ductility and strength levels decrease. While the amount of hydrogen present in commercial titanium is negligible, hydrogen may enter the material during welding, electroplating, and so forth. The hydrogen will then precipitate, in the form of titanium hydride. If the material

Jan 1, 1968

By B. F. Oliver, C. W. Haworth

Pure tin and Sn-0.5pct Pb ingots have been frozen unidirectionally from the base. For quiescent melts that were initially undercooled, a transition from lower eqlciaxed structure to an upper columnar structure is found in the alloy ingots. Columnar to equi-axed back to columnar transitions are observed in superheated alloy ingots, but no such equiaxed band is observed impure tin. The reproducible equiaxed band is associated with a thermal undercooling followed by a recalescence. This undercooling is <5"C, whereas the critical (maximum obtainable) under-cooling for both the pure tin and the alloys used is -20°C. A similar undercooling is observed at the same position in the pure tin ingots, although in this case no clear transition in structure can be seen. The structure of the pure tin ingots is either entirely columnar or mixed columnar-equiaxed. A consideration of the detailed thermal history of the ingots indicates that the ingot macrostructures are determined by the occurrence of a local therlnal undercooling in conjunction with nuclei multiplication and transport mechanisrris. GENERALLY it is found that a pure metal ingot solidifies so as to produce an entirely columnar structure. Frequently an alloy ingot is found to have a columnar outer zone and an equiaxed central portion. Early systematic work to examine the factors controlling the formation of the equiaxed structure was reported by Northcott&apos; who showed that, for copper alloys frozen unidirectionally with a given ingot practice, the alloying element influenced the length of columnar crystals and the extent of the equiaxed structure. Northcott showed that alloys with a wider freezing range more readily produced the equiaxed structure. The nucleation process can be important in producing equiaxed structures; frequently an alloy which readily solidifies with an entirely columnar structure will produce an entirely equiaxed structure when a nucleating agent is added to the melt.&apos; The formation of the equiaxed structure was attributed by Winegard and chalmers3 to the presence of constitutional supercooling; that is, a region of liquid in front of the growing solid could have a temperature below its equilibrium liquidus temperature. Thus, with a small enough temperature gradient in the liquid, it was suggested that the presence of constitutional supercooling may be sufficient to bring about the nuclea-tion necessary for the formation of an equiaxed structure. Although this explanation is plausible, and may be relevant in many ingots, Walker has described an experiment&apos; for which constitutional supercooling seems to be an unlikely cause of nucleation. A Ni-20 pct Cu alloy, repeatedly undercooled more than 50"C, was crystallized and found to show the typical colum-nar-equiaxed structure. The separation between the liquidus and the solidus for the alloy is 40°C. Thus, in this experiment the nucleation required for the formation of the equiaxed structure must have come about in some other way than by the nucleation catalysis constitutional supercooling hypothesis. Chalmers has suggested more recently5 that nuclei (in a typical ingot) are present immediately after pouring and are prevented from redissolving by the constitutional supercooling effect. More recently Uhlman, Seward, Jackson, and ~unt&apos; have shown direct evidence using ice and organic materials that freeze dendritically that the "remelt mechanism" may be an extremely effective crystal multiplication process during the freezing of ingots under conditions involving dendritic growth. JSlia" experimentally demonstrated the detachment of dendrite arms. chernov14 has analyzed the dendrite arm detachment process as a coarsening phenomena driven by the minimization of interphase area. Katta-mis and ~lemings" working with undercooled steel melts give evidence supporting this mechanism. Mechanisms of dendrite arm detachment such as those assisted by convection are believed to be the origin of the macrostructures obtained in this study. This study makes no attempt to distinguish the relative contributions of these mechanisms. The object of the present work was to obtain accurate temperature measurements during the solidification of an ingot and to correlate these measurements with the formation of equiaxed grains in the resulting ingot structures. Similar previous work is very limited. The measurements carried out by Northcott are neither sufficiently extensive nor sufficiently accurate for any interpretation. Plaskett and winegard7 carried out experiments on A1-Mg alloys in which they observed values of the temperature gradient, G, in the liquid and rate of freezing, R (for a given alloy solute content Co), at the transition from a columnar to an equiaxed structure. They reported that equiaxed crystals were produced at values of G/G approximately proportional to the solidus composition. Similar experiments using Pb-Sn alloys carried out by £111011" showed a linear relation between G/R and the solidus composition. However, the thermocouples were in the mold wall rather than in the melt and, in one case, ingot surfaces were examined. There is ambiguity in the meaning of the values of G and R measured in all these experiments. APPARATUS AND EXPERIMENTAL PROCEDURE Alloys were prepared by induction melting 99.999 pct Sn and 99.999 pct Pb to form a Sn-0.5 wt pct Pb alloy in air in a graphite crucible and casting into a cylindrical graphite mold 6 in. long, 1 in. in diarn , and with a & in. wall thickness. This mold was mounted on a copper base through which cooling water could be

Jan 1, 1968

By W. S. Stahmann, F. W. Bowdish

Previously published experimental data showing that both collectable and non-collectable sulfide films may be formed on chrysocolla were analysed, and chemical mechanisms were proposed for the formation of the films. A special technique was developed by which the quantity of sulfur adsorbed was determined for samples sulfidized under different conditions of pH and soluble sulfide concentration. The data on sulfur adsorption were used together with the expression for the equilibrium constant for the proposed reaction to indicate the validity of the chemical mechanism theory. A recent paper 1 about contact angle studies on chrysocolla reported the effects of pH value and sodium sulfide concentration during sulfidization upon the character of the surfaces produced. In each experiment the surface of a specimen of chrysocolla was prepared by grinding it with fine abrasive and washing it in tap water. The specimen was then placed in the sulfidizing solution for 10 min, rinsed in tap water, treated for 15 min in a solution containing 30 mg of potassium amyl xanthate per liter, rinsed in distilled water, and tested for air adhesion in a contact angle apparatus. The results, when plotted as in Fig. 1, showed an island representing conditions giving air adherent or collectable surfaces surrounded by conditions giving non-collectable surfaces. Particular interest may be attached to the region of non-collectability to the right of and above the island in Fig. 1, and to the boundry curve separating these two regions. It is apparent that at any pH from 4.0 to 6.0, where a collectable surface may be produced, a sufficient increase in the sulfide concentration results in a non-collectable surface. Thus it appears that too much soluble sulfide has a depressing effect upon the mineral, just as it has in sulfide flotation. This paper presents some speculations regarding the chemical mechanisms by which the collectable and non-collectable sulfide films may be formed and reports on a physical-chemical study intended to support these speculations. THEORETICAL CONSIDERATIONS The experimental results presented in the previous paper were analysed in several ways in an attempt to understand better the chemical mechanisms involved. For several points on the boundary to the right of the region of contact in Fig. 1, molar concentrations of H+, OH-, HS-, and S= ions, as well as various ion concentration products, were calculated. Following the reasoning of Wark and Cox, 2,3 no single kind of ions may be credited with causing depression of the surface because none of them have a constant con-

Jan 1, 1968

By D. R. Cook, W. M. Shepard, H. T. Morris

The East Tintic district in central Utah has produced ores of gold, silver, copper, lead, and zinc valued at more than $120,000,000. All of this ore has been produced from blind ore bodies in Paleozoic sedimentary rocks that are concealed beneath hydrothermally altered volcanic rocks and cut by intrusive bodies of Eocene age. The Paleozoic rocks, which range in age from Early Cambrian to Mississippian form the core and limbs of a large, northtrending asymmetric anticline that is cut by low-angle thrust faults, high-angle transcurrent faults, mineralized fissures and faults, and normal faults that are both older and younger than the mineralized fissures. The ore bodies generally may be grouped into two classes: ( 1) massive replacement bodies that are rich in silver, lead, zinc and manganese and (2) fissure veins that are valuable primarily for their content of gold, copper, and silver. The replacement ore bodies are localized chiefly in the Middle Limestone Member of the Ophir Formation of Middle Cambrian age where it has been thrust-faulted against older or younger rocks and cut by northeast-trending mineralized fissure zones. The fissure veins primarily are productive only in the Lower Cambrian Tintic Quartzite. Extensive lowgrade deposits of lead-zinc-silver ore recently have been discovered in Devonian carbonate rocks in the Lower plate of the East Tintic thrust fault but as yet are unevaluated. The principal guides to ore include: ( 1) intersections of northeast-trending fissures and crossbreaking faults that brecciate the carbonate rocks; (2) zones of late-stage pyritic, calcitic, and sericitic alteration in the lavas; ( 3) primary geochemical anomalies in the altered rocks; and ( 4) mineral zoning patterns of the known ore bodies. The present development of the Burgin mine would seem to assure the continued productivity of the district for at least a decade.

Jan 1, 1968

By Nelson C. White

This paper summarizes the present state and future prospects of the potash industry, with special reference to its impact on production in Saskatchewan.

Jan 1, 1968