Search Documents

By J. E. Hilliard

A procedure is described for determining, from measurements on a section, the moments of any degree n (i.e., the mean value of Dn, where D is a linear dimension) of the size distribution of particles (or grains) in an opaque sarnple. The analysis is applicable to particles of alnzost any shape and to any mixture of shapes. However, if absolute values of the wloments are required, it is necessary to know what shapes are present and the relative frequency of their occurrence. In addition, certain shape-dependent parameters have to be evaluated before the formulas can be used. The measurement required is the distribution of intercept lengths. This can be determined either visually or with an automatic scanning instrument. Corrections me derived for the bias due to instrumental end effects. The proposed analysis has the following advantages over existing ones: 1) Confidence limits are easily estimated for the measured properties or, conversely, the number of counts required to achieve a given accuracy can be determined. 2) The analysis is not restricted to particles of a special shape. 3) The error resulting from any known degree of departure of the actual from the assumed particle shape can be estimated. 4) The computations are simple and, apart from a change in constants, are independent of particle shape. 5) The number of particles per unit volume can be determined by a simple counting procedure. MANY procedures have been described for determining the size distribution of particles from measurements on a section (or plane of polish). They differ from one another in the property measured on the section (radius, intercept length, profile area) and in the method used for the numerical solution of the integral equation relating the property to the particle size distribution. However, all existing analyses share at least two of the following disadvantages. 1) They are limited to a particular shape of particle (usually spherical). 2) It is very difficult to determine how the statistical sampling error is propagated into the computed size distribution. The investigator thus has no means of knowing the reliability of his result and, what is of equal concern, he is unable to estimate how many measurements are required to obtain a result of the required accuracy. 3) It is also difficult to assess the error resulting from any deviation between the actual and assumed particle shape. The foregoing limitations stem from the complex relationship between the particle size distribution and the distribution of the property measured on the section. As will be shown, they can be avoided by defining the size distribution in terms of discrete parameters

Jan 1, 1969

By D. H. Desy

The Bureau of Mines studied the properties of copper that had been oxide dispersion-strengthened with 2 vol pct of either yttria or alumina. Compounds of copper and aluminum or yttrium, coprecipitated from aqueous solution, were converted to oxides; the copper was reduced, compacted, sintered, and extruded. For the resulting copper-dispersoid composites, room temperature tensile properties after annealing in hydrogen, elevated temperature tensile and stress-rupture properties, and electrical conductivity were determined. Compared with oxygen-free copper, copper-2 vol pct alumina or yttria had improved strength after annealing between 400° and 1,000° C, and improved elevated temperature strength, with little loss in electrical conductivity.

Jan 1, 1969

By Raymond S. Shrode

Transportation is one of several important increments in the total market cost of most commodities. On a national average it has been reported that transportation accounts for about 25% of the total cost of a product at the market place. And industrial minerals are no exception. In fact, the proportionate cost frequently exceeds the 25% average. Further, it may actually determine the economic value of a deposit. Transportation may possibly be thought of as a specialized subject of concern only to a traffic manager and of only nominal interest to the mining engineer, the geologist or other technically oriented member of mineral producers' staff. However, in the industrial minerals field, interest is not commonly confined to exploration, development, production or marketing, but is in contrast an overlapping one. In a very real sense this broad area of interest in the total economics of the business is the specialty of the industrial minerals man. And transportation is a vital part of the total picture. Comments in this paper deal with rail transportation.

Jan 1, 1969

By Merle L. Bowser

The Bureau of Mines has developed a portable recording methanometer that utilizes the Bureau's methane sensor. The methanometer can operate continuously for at least 30 hours on small, sealed, rechargeable lead-acid batteries.

Jan 1, 1969

By A. U. Seybolt

DURING the course of an investigation of hot corrosion of nickel-base superalloys (combination oxidation-sulfidation attack at high temperature), it was considered possible that sulfur might gain entrance to the alloy in part, at least, by diffusion through the scale. Cr203 is nearly always observed as a prominent component of the oxide scale, and hence some experiments were carried out to examine the tracer diffusion of sulfur through Cr203 at 1000° C in the upper temperature range experienced by jet engine blades and vanes. Some hot-pressed Cr203 discs of quite high density were available from an earlier investigation1 on the rate of crf3 migration through Cr203. The Cr203 was 99.3 pct pure and contained -0.06 pct Fe as the largest metallic impurity. Additional data is given in Ref. 1. In this earlier work it was found that the rate of cation diffusion was independent of the atmosphere of thermal equilibration when using nitrogen, argon, or air, and also that the electrical conductivity of the hot-pressed Cr203 compacts was likewise independent of atmosphere in this range, thus indicating that the de-

Jan 1, 1969

By K. A. Gschneidner, O. D. McMasters, T. J. O’Keefe

X-ray diffraction, differential thermal, ad rnetallo-graphic methods were used to establish the Dy-Pb Phase diagram. Lead additions lower the 1377°C transformation temperature of dysprosium to 1360°C leading to an inverted peritectic reaction. The 327°C melting point of lead is lowered by dysprosium additions to about 326°C yielding a eutectic reaction. A second eutectic reaction occurs at 13.3 at. pct Pb and 1200°C. The dysprosium-richest intermetallic compound DysPb3 melts congruently at 1695°C and crystallizes in the hexagonal Mn5Si3 (D8,) type structure. The peritectic decomposition temperatures for the remaining compounds are Dy5Pb, at 1555C, DyPb2 at 955C, and DyPb3 at 880°C. A fifth compound near the DyPb stoichiometry exists over a 310°C temperature range decomposing at 1130°C by means of an inverted peritectic reaction and melting incongruently at 1440°C. The crystal structures of the compounds are discussed. A systematic study of the rare earth-lead alloy systems is underway in an effort to supply information concerning the alloying behavior of the rare earth metals. The Dy-Pb phase diagram is the fourth system to be investigated in this study. The Yb-Pb,1 Y-Pb,2 and Eu-Pb 3 diagrams have been published recently. Utilization of the rare earth series of metals as a research tool in this manner should yield a better understanding of alloy formation. EXPERIMENTAL PROCEDURE Materials. The lead used in this investigation was obtained from Cominco Products, Inc., and was specified to be 99.99 pct pure. The dysprosium was prepared in this Laboratory by the calcium reduction of the fluoride followed by distillation of the dysprosium. The major impurities in the dysprosium in ppm are: A1 (<40), Ca (400), Er (<50), Gd (<200), Ho (<200), Mg (<50), Si (30), Ta (400), Tb (<100), Y (<50), 0 (651, H (15), N (not detected), F (430), C (35). Alloy Preparation. Most of the alloys were prepared by melting weighed amounts of dysprosium and lead in sealed tantalum crucibles. The tantalum crucibles were sealed by are-welding in a He-Ar atmosphere welding chamber. Thus the alloys are in contact with He-Ar at about 1 atm pressure. Homogenization was achieved by holding them in the liquid state for about 1 hr, cooling, inverting the crucibles, remelting, and repeating the process at least twice. Since these alloys were prepared in sealed tantalum crucibles, chemical analysis for final composition was thought to be unnecessary. No detectable reaction of these alloys with the tantalum crucible was observed by metallographic examination. Metallographic evidence was also used to confirm the homogeneity of some of the alloys prepared in this manner. The compositions of a few alloys, which were prepared by nonconsum-able are-melting, were corrected for the small weight losses involved by assuming that the weight loss is due to vaporization of lead. The specimens obtained from the alloy samples were prepared under a dry-argon atmosphere because they were rapidly attacked by air and moisture. Thermal Analysis. Differential thermal analysis methods were used to determine the liquidus curves and reaction horizontals of the system. Both Pt vs Pt + 13 pct Rh and W + 5 pct Re vs W + 26 pct Re thermocouples were used to measure the temperature. An X- Y recorder was used to record the specimen temperature and differential electromotive force between the specimen and molybdenum standard. The arrest temperatures were measured potentiometri-cally. The accuracy limits (* values) associated with the reaction temperatures obtained by this method were estimated on the basis of both the reproducibility of the particular temperature value and the accuracy of the thermocouple at a given temperature. Liquidus temperatures were obtained from cooling arrest data while both heating and cooling arrest data were used to establish the horizontals of the diagram. Heat treatments during the thermal analyses of the alloys between 40 and 70 at. pct Pb were necessary in order to approach equilibrium conditions. The samples were held at temperatures between the various peritectic horizontals for l to 2 hr before the thermal analyses were continued. The entire range of compositions was investigated at the expense of a minimum amount of materials by adding appropriate amounts of lead to master alloys. More than sixty alloys were analyzed by this differential thermal method and for each alloy the results given herein are taken from two or three heating and cooling cycles. X-Ray and Metallographic Methods. Slice specimens for metallography and powder specimens for X-ray diffraction were prepared from rod-shaped samples which had been melted in sealed 0.62 5-cm-diam tantalum crucibles. The specimens were heat-treated in sealed tantalum crucibles which were protected by sealing them in argon-filled quartz ampules. Quenching was accomplished by breaking the ampules in ice water after heat treatment. X-ray powder specimens were sealed in 0.3-mm-diam glass capillaries under a dry-argon atmosphere. Copper, iron, and chromium radiation were used to obtain the powder patterns for these alloys. More than 150 powder patterns were obtained for specimens of various compositions and heat treatments. Included in these were several patterns for specimens which had purposely been oxidized. Patterns from specimens which had been accidentally exposed

Jan 1, 1969

By Cunningham DA

Plant based on the New Jersey refluxing process has been installed at the Cockle Creek Works of Sulphide Corporation Pty. Limited to refine portion of the zinc output from the Imperial Smelting Furnace. Refining of impure zinc is effected by distillation in two stages in vertical columns compris- ing a series of superimposed silicon carbide trays designed such that ascending zinc vapours and descending liquid metal are in intimate contact. In the first stage the volatile elements (zinc and cadmium) are distilled from impure metal, condensed, and while still molten, fed to the second column in which zinc is boiled under controlled refluxing conditions to remove the cadmium content. The resultant zinc has a purity in excess of 99,995 per cent zinc. The availability of refined zinc has made possible the production of a number of zinc alloys for marketing in addition to the basis grades of zinc.

Jan 1, 1969

By D. R. Packard, J. D. Verhoeven

The resistivity us atom fraction relationships for dilute solutions of cadmium, mercury, and tin in molten sodium have been determined. With these data and the resistivity capillary-reservoir technique, the electro-transport mobilities, effective valences, and the diflusion coefficients of the three solutes have been determined. The mobilities are found to be higher than in other molten alloys by a factor of around 20. The results are compared to the Mmgelsdorf model for electrotrmtsport. The high values found for the mobility to diffusion coefficient ratio indicate that small quantities of the alkali metals should be susceptible to purification from many solutes by means of electrotransport. PASSAGE of a direct electric current through a liquid metal containing a solute will usually cause a relative motion between the solute and solvent atoms of the alloy. This electrotransport phenomenon may be described experimentally in terms of the mobility of the solute atoms, i.e., the drift velocity of the solute relative to the solvent per unit electric field. In dilute solutions of liquid alloys this relative mobility becomes a measure of the velocity of the solute with respect to the observer since the motion of the solvent is negligible. The mobility is a significant parameter in evaluating the potential usefulness of electrotransport for such things as purification or solute control upon solidification. Prior to around 1958, quantitative data for the mobility of solutes in liquid metals were restricted to some solutes in liquid mercury. Since that time ad- ditional data have been reported for the mobility of solutes in liquid mercury, bismuth, tin, and lead, as shown in Table I. In 1963 Drakin et al.11 reported some values of a transport number for mercury and thallium in molten sodium and potassium. When these values were converted to mobilities, it was found that the mobilities were higher than any of the previously reported values by a factor of around 20, as shown in Table I. Drakin&apos;s experimental technique did not eliminate the presence of back-diffusion and consequently his data were expected to be lower than the true values. The purpose of the present investigation was to determine the mobility of a number of solutes in molten sodium with an experimental technique which eliminates back-diffusion errors. EXPERIMENTAL The technique used to determine the mobility was a resistivity capillary-reservoir technique which had previously been used with a high degree of precision on Sn-Bi alloys.4 This technique consists of dipping the vertical Pyrex capillary cell shown in Fig. 1 into a molten bath of alloy while the bath and capillary are under vacuum. The capillary is then filled by intro-

Jan 1, 1969

By A. C. D. Chaklader, Ashok K. Kakar

The basic density equation originally dericed &apos; to predict the increase in density of a compact of spherical particles with the progressive deformation at the points of contact has been further modified to include the yield strength of the material. This has been done by assuming that the contact areas grow to stable sizes under a fixed stress which is equal to three times the yield strength. The final equation has the form: where Do and D me the initial and final bulk densities of the compact, u is the applied pressure, and Y is the yield strength of the material. This equation was tested with the data obtained on spheres of lead, K-Monel, and sapphire. The calculated yield strength t~alues for lead and sapphire are within the range of values reported in the literature. A few of the earliest hot pressing models proposed to explain the mechanism by Murray, Livey, and williams2 and then by McClelland3 are based on a plastic flow mechanism. However, more recent investigations suggest that the overall densification process is a combination of several mechanisms, such as particle rearrangement, fragmentation, plastic flow, and stress-enhanced diffusional creep. While fragmentation and particle rearrangement are considered to be responsible for the densification in the early stages,"475 it has been concluded that the final stages of hot pressing are controlled by stress-enhanced diffusional creep.516 The manner in which the densification takes place, i.e., by fragmentation, particle rearrangement, plastic flow, or stress-enhanced diffusional creep, would depend upon the type of material, the temperature, and the stress level used during the hot-pressing experiments. Metal compacts can be expected to have a much greater contribution from plastic flow than ceramic oxides. Also, plastic flow would be a significant contributing factor to densification at high temperatures and high stresses. Most of these works, directed towards elucidation of densification mechanism, have dealt with kinetics of the process. The results of most of the authors vary from one another and they have proposed either new empirical or semiempirical equations to fit their data. The densification rate was found to vary with the type of the powder, shape and size of the powder, initial packing density of the compact, and a few other factors such as rate of heating, pressure, and so forth. Beyond the initial stages, the densification process has been considered to be as time-dependent flow, controlled by a diffusional process, e.g., Nabarro-Herring creep. Palm our, Bradley, and johnson&apos; have attempted to use modified creep rate equations to interpret the data of densification under hot-pressing conditions. Beyond the initial stages, however, the densification would be controlled by a process depending upon the temperature, pressure, and size of the powders. It is the authors&apos; belief that such densification cannot be exclusively controlled by a single process and so attempts should be made to study some observable phenomenon like microstructure, yield strength, and so forth. The emphasis of this work has been toward studying the densification problem from a more fundamental point of view. Some of the principal variables, like initial packing density, mode of packing, and size of the powders, have been controlled to a great extent. The total strain produced on pressure application (instantaneous) in such a case can be considered to be due to plastic and elastic deformation. The elastic component of the strain can be determined by decreasing the load to the initial value. The strain remaining then can be correlated with the contact areas produced by deformation and the corresponding applied load. In a previous paper,&apos; the possible deformation behavior of spheres in a compact has been theoretically analyzed and experimentally tested. The change in contact area radius a relative to the particle radius R was related to the bulk density and the bulk strain for simple and systematic modes of packing. Tt was found that a density equation relating the above parameters can be represented by: where D and Do are the bulk densities of the compact at any value of a/R and a/R = 0, respectively. This basic equation should hold for any material as it was derived from geometrical considerations alone. An attempt has been made in this work to include the yield strength in the above density equation, so that a knowledge of the properties of any material can be used in predicting the densification behavior during the hot-pressing process. THEORETICAL CONSIDERATTONS The deformation of two spheres in contact under a static load can be compared to the deformation occurring between a hard spherical indentor and the flat face of a softer metal. Tt has been shown theoretically by both ~encky~ and lshlinskyg and experimentally by ~abor" that, for a material incapable of appreciable work hardening, the mean pressure required to produce plastic yielding (for deformation occurring between flat face and a hemispherical indentor) is approximately equal to three times the elastic limit, Y, of the material (in tension or compression experiments). Tabor has further observed that the same relationship is valid in the case of work-hardening materials, if the elastic limit at the edge of the indenta-

Jan 1, 1969

By Andrew J. Freyman, Graham T. Armstrong

"In September, 1968, a survey of operating mines in the Yukon and the Northwest Territories was undertaken to determine the role of Indigenes (Indian, Metis, Eskimo) on the mines, and the attitude of mine management to these employees. The operating mines in the Territories had (at that date) a total employment of 2,002 men, of which 91 (4.5 per cent) were Indigenes. Indigenes make up 45 per cent of the Territorial population (18 per cent in the Yukon and 63 percent in the Northwest Territories). The paper documents some of the problems associated with indigenous employment in mines. A study was undertaken to determine the role of Indigenes (Indians, Metis, Eskimos) in operating mines in the Yukon and in the North-west Territories. In addition to the mines north of the 60th parallel, the experience of several other Canadian mines was examined. The general picture obtained is considered to be representative of the Canadian mining industry."

Jan 1, 1969

By A. J. Mortlock

Cobalt and nickel have been diffused at tracer concentrations in gold at several temperatures in the range from approximately 700° to 950°C. The diffusion penetration profiles were determined by a serial sectioning technique in which the gold is first anodized and then the anodic layer is dissolved in acid. In this ulay sections as thin as 250A could be removed reproduci-bly. In all cases, the region close to the specimen surface was characterized by irregular behavior in the sense that the logarithm of concentration was not linear in the square of the penetration distance. In sotne cases, there zuas an indication of the operation of very slow dijfusion in this region, while in others the apparent diffusion coejj&apos;icient was negative. Possible reasons for this anomalous behavior are briefly discussed. In recent years it has been found that the region close to the surface of a metal can sometimes exhibit anomalously slow diffusion characteristics relative to the interior of the metal. One of the best examples of this fact is the work of Styris and omizuka,&apos; who showed that the apparent diffusion coefficient for zinc in the region withi: about 1 p of the free surface of copper was about ,,,, that at deeper penetrations. This result is particularly interesting, because it is free from the possibly complicating effects of low solubility of the diffusing tracer in the solvent metal. In the case of diffusion under conditions of low solubilitjr, interpretaticn of the results in terms of lattice diffusion is difficult because of the enhanced short-circuiting produced by segregation to dislocations.2&apos;3 Measurements by Duhl et 1. suggest that cobalt diffusing in gold may also show a near-surface effect of this type. Once again the solubility is high, so that this result could be of great interest. However, the technique used for analyzing the diffusion penetration zones by Duhl, viz. the counting of residual gamma activity in the specimen following sectioning, appears to have indicated a near-surface effect in a parallel experiment on the self-diffusion of gold reported at the same time. The latter result is known to be spurious, since Kidson5 has demonstrated that self-diffusion in gold does not show this effect. Duhl et 01. also reported some measurements on the diffusion of nickel in gold, but failed to give any data for the near-surface region. As the solubility of nickel in gold is high, such data would also be of special interest. We, therefore, decided to conduct another set of experiments on the diffusion of nickel and cobalt in gold, using a sectioning technique that allows the individual sections to be assayed for solute content and thus gives direct determinations of penetration profiles. Also, by sectioning with an anodizing/stripping tech- nique, very thin layers can be removed and the region close to the surface studied in detail. MATERIALS The gold specimens were supplied as single crystal disks $ in. in diam by a in. high by Monocrystals Co. of Cleveland, Ohio. The gold itself was of spectro-scopic purity, i.e., better than 99.99 pct pure. METHOD Specimen Preparation. One flat end face of each gold crystal was spark planed with a Servomet spark erosion machine set for minimum spark energy. Following this treatment the crystals were preannealed for 2 to 4 days at temperatures of either 400" or 700°C. The three crystals preannealed at 700°C showed signs of recrystallization. The spark-planed end face of each crystal was then coated with the appropriate amount of 63i or 60 radioactive tracer. This deposit was laid down in a simple plating bath containing the as-supplied solution of the radioactive isotope as well as sufficient ammonium oxalate to saturate the solution. Some ammonium oxalate remained undissolved on the floor of the bath for this purpose. During plating further additions of ammonium oxalate were sometimes required to allow the plating to continue satisfactorily, perhaps due to passivation of the undissolved oxalate already present. The thickness of the deposited layer was determined by comparison of the apparent surface activity of the plated specimen with that of a similar specimen having a weighable deposit of the isotope on its end face. Correction for self-absorption of the radiation was made in this calculation. Annealing. The deposited crystals were annealed in a hydrogen atmosphere in sealed silica tubes. During this heat treatment they were supported, active face down, on optically flat silica plates. The temperature was measured with calibrated Pt vs Pt-10 pct Rh thermocouples, and the tabulated values can be taken to be correct to Z°C. All the crystals showed evidence of recrystallization following these heat treatments, suggesting that initially they may not have been good single crystals or had suffered strain during delivery. Concentration Profile Analysis. After annealing, the crystals were sectioned by the anodizing-stripping technique.6 The anodizing involved suspension of the specimen with its cylindrical axis horiz6ntal by a gold wire in a 200-ml beaker containing 1 M Hg304. A cathode in the form of a strip of gold sheet, 2 in. wide and positioned to be in contact with the curved side of the beaker, completely encircled the specimen. An anodizing current of 30 ma, corresponding to a current density of 5 ma per sq cm on the surface of the specimen, was passed for times ranging from 5 to 150 min depending on the thickness of gold to be removed; the solution was stirred continuously during this process. Following this treatment, the specimen

Jan 1, 1969

By Amitava Gangulee, Michael B. Bever

The effects of changes in short-range order on some thermodynamic, electrical, and mechanical properties of the silver-rich Ag-Mg solid solutions have been investigated. The heats of formation at 273°K of several alloys after two different thermal treatments were measured by liquid metal solution calorimetry. Their electrical resistivities were measured at temperatures ranging from 4° to 773°k. Tensile tests and microhard-ness measurements were carried out at room temperature. An effective short-range order parameter and an effective interaction energy are defined. The measured changes in the properties are interpreted in terms of these quantities. The short-range order parameter is evaluated separately from calorimetric and X-ray data; the results are in fair agreement. Increasing short-range order lowers the resistivity of- the silver-rich Ag-Mg alloys but does not measurably affect the temperature dependence of the resistivity. Short-range order increases the yield stress of these alloys but does not affect the ultimate tensile stress. Changes in the effective short-range order parameter independently obtained from measured changes in the heat of formation, resistivity, and yield stress are in fair agreement. THE thermodynamic, electrical, and mechanical properties of solid solutions have been investigated as functions of composition in many alloy systems, but the effects of configurational variables, such as short-range or long-range order, on these properties have received much less attention. The silver-rich terminal solid solutions in the system Ag-Mg are well-suited for the investigation of the effects of order. The composition of these solid solutions may be varied over a range extending to about 27 at. pct Mg.1 Appreciable short-range ordering is likely to take place in these solid solutions; the degree of short-range order can be varied by suitable thermal treatments. In the alloy Ag3Mg long-range ordering is possible.2 This paper is primarily concerned with the effects of short-range order on some thermodynamic, electrical, and mechanical properties of the silver-rich Ag-Mg solid solutions.-The long-range ordering transition is the subject of a concurrent paper.3 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Specimens. Ag-Mg alloys containing up to 26.4 at. pct Mg were prepared by melting 99.99 pct pure Ag (obtained from Baker Chemical Co.) and 99.99 pct pure Mg (obtained from Eastman Chemi- cal Co. or Johnson Mathey & Co.) in graphite crucibles under molten potassium chloride. The solidified ingots were homogenized at 823°K for 10 days in evacuated Vycor capsules. A surface layer 6 in. thick was then removed by machining. The ingots were swaged into rods (2.5 mm diam) which were drawn into wires (1.0 mm diam). The wire specimens were annealed at 773°K for 24 hr in vacuum and either quenched into iced brine or cooled to room temperature over a period of 15 days. The average grain diameter (obtained from the linear intercepts) was about 0.1 mm. 1.2) Calorimetry. The heats of formation of the alloys were measured in a tin solution calorimeter as the difference in the heat effects of alternate additions of samples of an alloy and the mechanical mixture of its component elements. The additions were made from 273°K to the bath at about 623°K. The heat effect on addition of the alloys was approximately 5.5 kcal per g-atom. The procedure and the method of calculation have been described.4 1.3) X-Ray Diffraction. Short-range order parameters of two alloys were calculated from diffuse scattering intensities,&apos; obtained with briquettes made from powdered specimens. A GE-XRD 5 diffractometer with filtered copper radiation was used. The absolute intensities were based on calibrations with paraffin. 1.4) Resistivity Measurements. The electrical resistivities were measured by a potentiometric method in which the potential drop across the specimen was compared with that across a standard resistance. For measurements below room temperature, the specimens were immersed in liquid helium (4°K), liquid nitrogen (78°K), dry ice and trichloroethylene (195°K), or ice and water (273°K). Measurements above room temperature were made on specimens held in a furnace under helium or in vacuum. The resistivity measurements were reproducible to ±0.5 pct or less. 1.5) Mechanical Tests. Tensile tests were carried out at room temperature with a Tinius-Olsen XY elec-tromatic Universal testing machine. Wire specimens (nominal gage length 1 in.) were used. The strain was measured with an extensometer, which had a sensitivity of 4 x 10-5; the strain rate was 10-3 min-1. Microhard-ness measurements were made with a square-pyramid indenter and a 100-g load.11 2) RESULTS AND DISCUSSION All measurements were made on two parallel sets of specimens, one quenched and the other slowly cooled from 773°K. The reported values are the averages of at least three measurements. In the range of magnesium concentration substantially below that of the composition Ag3Mg, quenched alloys have less short-range order than slowly cooled alloys. As the magnesium concentration approaches that of Ag3Mg, slow cooling develops long-range order. Quenching sup-

Jan 1, 1969

By D. E. Wolfson

As energy requirements in the United States expand with the growth of the Nation, use of coal also can be expected to increase. This optimistic outlook for the coal industry is based on our vast reserves of high quality coals and the possibility of converting coal to end uses other than electricity and metallurgical coke. Potentially, millions of tons of coal might be needed in the form of gas and liquid fuels to supplement our reserves and imports of these natural products. Exactly when they will enter the economy on a large scale depends on many factors. On January 1, 1960, the estimated remaining reserves of coal were 1-1/2 trillion tons, about 50 percent of which is bituminous coal. In 1965, the production of bituminous coal and lignite passed the 500-million-ton mark, emphasizing the steady upward trend from the recent low of 403 million tons, and if the present rate of increase continues within the next five years, output should pass the alltime high of 631 million tons achieved in 1947.

Jan 1, 1969

By Immo H. Redeker

Tile Asheville Minerals Research Laboratory is a member of the Engineering Research Department of North Carolina State University. The Laboratory is engaged mainly in applied nonmetallic mineral processing research to assist the North Carolina mining industry. A few out of state projects are handled at times. The Laboratory helped to bring the flotation process to North Carolina feldspar, spodumene, mica and phosphate producers and maintains versatile batch and pilot plant facilities at Asheville. It is of interest that North Carolina has now one of the newest and largest flotation plants at Lee Creek where Texas Gulf Sulphur Company produces 10,000 tons of phosphate concentrate per day, and one of the smallest flotation plants at Pittsburgh Plate Glass Company&apos;s fiberglass plant in Shelby, North Carolina where $50,000 per year of platinum-rhodium metal is reclaimed from wasted fiberglass furnace refractories in a tiny flotation operation of pilot plant size. The conservation of mineral resources through improved processing methods has been the object of most of the Laboratory&apos;s projects. This work has been extremely interesting and rewarding in many instances. Or, the example of projects for Kings Mountain Mica Company it will be demonstrated how waste could be reduced step by step from 20 tons of waste per ton of product to LO tons of product per ton of waste by improved processing methods. Brick, high grade potash feldspar, and silica sand are now produced from formerly wasted materials. AL this time Laboratory work sponsored by three feldspar companies, the State of North Carolina, and the U. S. Bureau of Mines, is aimed at reducing the amounts of feldspar tailings in the Spruce Pine area. Mineral dressing techniques are applied to reclaim saleable mineral products such as feldspar, mica quartz, and to make more uniform material for possible ceramic and other applications. Processes to produce new products such as sand-lime brick, and lightweight foamed autoclaved calcium silicate building products will be tested.

Jan 1, 1969

By Andersen AK

As part of a research program sponsored by Continental Copper and Steel Industries, Inc. (cos), investigations have been conducted by the Colorado School of Mines Research Foundation, Inc. to study the effect of high current densities on electrolytic processes. The importance of high current densities has long been recognized, particularly in the deposition of copper, and the results of considerable research on the subject have been reported in recent years (19 29 39). This is not surprising because, besides plant capacity, current density is the other major factor which will determine the process economics. In the production of electrolytic copper, current efficiency, steam consumption, number of cells, building area, metal inventory, cathode purity, and power consumption are all affected by current density. The ability to maintain a high current efficiency and satisfactory cathode purity while increasing the current density to twice or three times that commonly practiced could result in considerable saving of capital investment and reduce the operating cost per ton of metal produced. The optimum current density i.e., that current density of which production cost would be at a minimum, can be established from an analysis of the various inter- relating factors (49 59). A review of.all operating electrolytic plants (electrowinning and electrorefining) will indicate that most of these plants are operating at 50% or less of the optimum current density (6). One of the reasons for not using the optimum current density may be attributed to the fact that conventional electrolytic tank- house equipment does not perform satisfactorily at high current density operations. Various investigators (19 79 8) have attempted to overcome this limitation by modifying the design of the electrolytic cell, virtually unchanged since it was first introduced in the late 1800&apos;s. Previously, these attempts have not resulted in,a cell design suitable for commercial application. However, recently, a cell has been designed which performs efficiently under such conditions. This is a CCS development (patents applied for).

Jan 1, 1969

By C. A. Stickels, C. M. Yen

Secondary recrystallization was investigated in vacuum-melted electrolytic iron to which 70 pm N was vacuum-meltedadded. The secondary texture is "near {554}<225>" for material cold-rolled 75 to 90 pct, the sharpness of the texture increasing with increased rolling reduction and with decreased annealing temperature. At reductions of 95 and 97.5 pct the secondary texture is &apos;"near {322)(296)". Both secondary orientations also exist as major components of the primary re-crystallization texture. Development of a strong "near {554) (225)" secondary texture appears to depend on the evolution of the Primary texture to a transition texture depleted in orientations near the secondary orientation before the onset of secondary growth. A variety of qualitative experinzents have been used to show that nitrogen is important in limiling primary grain growth. The presence of nitrogen does not seem essential for the establishment of a transition texture, but a loss of nitrogen during annealing may facilitate growth of grains in the secondary orientation. Secondary grains we shown to form initially at the specimen surface. This is not thought to indicate that surface energies are important in the growth process. It is proposed that the quasi-two-dimensional character of surface grains permits discontinuous growth parallel to the surface before secondary growth of interior grains is possible. An earlier study of recrystallization textures in 90 pct cold-rolled electrolytic iron showed that secondary recrystallization occurred after annealing for several days at 700C1 This type of secondary recrystallization, which had not been reported previously, results in the formation of a strong texture, best described by the indices "near {554}(225)". The purpose of the present work was to investigate the effect of various processing variables on secondary recrystallization in this material and determine the mechanism of secondary grain growth. LITERATURE REVIEW An understanding of the mechanism of a secondary recrystallization process depends on knowing: 1) how grains in the secondary orientation come to be in the primary recrystallization texture; 2) why normal grain growth does not occur; and 3) what factors determine the strength of the secondary texture. For secondary growth of grains of a particular orientation, a certain minimum fraction of the grains must be in that orientation after primary recrystallization. This requirement is apparently satisfied "naturally" in certain systems, i.e., when the primary texture obtained by rolling and recrystallizing material initially randomly oriented contains a sufficient fraction of primaries in the secondary orientation. However, in other cases, e.g., {110}<001> and {100}<001> secondary growth in silicon iron,2 it is necessary to enhance the fraction of primary grains in the secondary orientation by rolling and recrystallizing textured material. In the present case, the "near {554}<225>" orientation is contained within the spread of orientations found in the primary recrystallization texture of iron or bbc iron-base alloys. In systems where the main driving force for secondary growth is the reduction in total grain boundary energy, secondary growth is observed only when normal grain growth is minimized. Four ways in which normal grain growth can be limited are: 1) Limitation by a strong primary texture. When a very strong primary texture consisting of a single component or twin-related components develop, most primary grains are separated from one another by relatively immobile small-angle grain boundaries. The classic instance of this is secondary growth into the primary cube texture in some fcc metals. 2) Limitation by precipitates. Precipitates present in the proper volume fraction with a suitable dispersion will limit primary grain growth. The role of MnS inclusions in impeding normal grain growth in Si-Fe is well-documented.5 3) Limitation by sheet thickness. Normal grain growth slows drastically when the mean grain diameter is of the same order as the sheet thickness. This effect has been used to obtain secondary recrystallization in thin sheets of high-purity silicon iron.&apos; 4) Limitation by solute impurities. It is well-established that certain impurity elements in solution can have a large effect on grain boundary mobility.&apos; However, there does not seem to be any secondary recrystallization process in which primary grain size stabilization has been shown to be due to the drag exerted on grain boundaries by dissolved impurities. In certain systems, e.g., secondary recrystallization in silver,&apos; the means by which normal grain growth is limited has not been identified, and solute-impurity limitation might be suspected. In order to understand the factors which determine secondary texture strength in three-dimensional growth, it is necessary to examine in more detail the current picture of general secondary recrystallization processes. Following Cahn,9 it is assumed that the primary grains have a range of sizes and that secondary growth of one of the large grains in this distribution is possible when it exceeds a critical size with respect to its neighboring grains. The critical size depends on the ratio ?S/?p, where ?s is some sort of average grain boundary energy between the potential secondary and the primary grains and ?p is some sort of average grain boundary energy between primary grains. For a constant primary grain size, the critical size for secondary growth increases as ?$/?p increases. May and Turnbull5 have incorporated the

Jan 1, 1969

By S. S. Shen, M. J. Pool, P. J. Spencer, J. R. Guadagno

VERY few thermodynamic data are available for rare-earth alloys, partly because of the difficulties of obtaining the metals in sufficiently pure form and also because of their comparative scarcity up to the present time. The rare earths form a very interesting series in the periodic table in view of the progressive filling of their 4f subvalence electron shell and would be expected to provide useful information with regard to alloying characteristics of transition elements. It has been found in recent calorimetric investigations that the heats of solution of a number of the rare-earth metals in liquid tin are highly exothermic.1-4 Exceptionally strong bonding between rare-earth and tin atoms is clearly indicated in the liquid solutions. Continued thermodynamic studies of the behavior of rare earths in solution could thus contribute a great deal to present theoretical knowledge of alloying behavior and would yield an insight into bonding of a strength hitherto unencountered in liquid alloys. The determination of the heats of solution of the pure components in liquid tin is an essential preliminary to calorimetric work of this nature. Heats of solution of praseodymium, neodymium, and samarium in liquid tin at 750" &apos; and the heats of mixing of Pr-Nd solid solutions&apos; have already been determined in this laboratory. The present investigations with lanthanum continue the study of rare-earth elements. Details of the construction and operation of the liquid metal solution calorimeter used in this work have been published previously by Pool and Peluso and no further description will be given here. The lanthanum used in heat of solution determinations was supplied by Lunex who quoted the purity as 99.9 pct. Their detailed analysis of the material is given in Table I. Samples of 0.0003 to 0.0005 g-atom were used for each run and great care was taken to remove all surface oxide prior to weighing. The samples were stored at all other times in a beaker of oil to prevent their otherwise rapid oxidation. The compounds LaSn (Cudu, L1P type structure) and La&, (structure not classified) were prepared from the appropriate quantities of the two pure components by arc melting under a purified argon atmosphere and once again great precautions were taken to avoid any subsequent oxidation of the specimens. Although no structural examination of the compounds was made, the consistency of thermodynarnic measurements carried out on twenty or so individual samples of each indicates that the compounds were in fact homogeneous, single phase alloys. Samples of the compounds consisting of 0.0003 to 0.002 moles were used in the calorimetric measurements. A solvent bath consisting of approximately 80 g of 99.9 pct pure Sn was used for each series of runs and its heat capacity was determined at regular intervals throughout the experiments using pure tin or tungsten calibration samples. Measurements were made of the heat of solution of lanthanum in liquid tin at 725", 750C, and 775°K and at compositions up to 2.21, 4.76, and 5.25 at. pct La at the three temperatures respectively. In every case, the heat of solution of lanthanum remained constant at its limiting value, within experimental limits, up to the highest lanthanum concentration investigated. Since no change in was observed, it was concluded that the liquid/liquid + LaSn, phase boundary had not been

Jan 1, 1969

By D. E. Wolfson

Destructive distillation (carbonization) was shown to be a feasible method of disposing of scrap tires. The Bureau of Mines conducted tests under a variety of conditions. Solid, liquid, and gaseous products were produced, recovered, and analyzed. The quantities of the various products were shown to be quite dependent on the test temperature. Variability in composition of the liquid and gaseous products with changes in test temperature was also significant.

Jan 1, 1969

By J. G. Lang

"This paper gives an outline of the principles used in E.M. wire rope testing, showing the practical application of the device and its value in industry and in mining operations.It presents: case histories involving deterioration, such as corrosion, peening and broken wires; anomalies indicating conditions peculiar to drum hoists and friction hoists; tests of locked coil ropes; low-frequency testing; and experiments and development."

Jan 1, 1969

By G. W. Neumann

"In order to avoid pollution of water in Flemming Brook and Little River, which drain the area in which the Brunswick No. 12 Mine and Concentrator are located, the company has gone to considerable expense in preparing tailings storage and effluent setting ponds. The attached drawing gives a plan of the six settling ponds together with elevations of the dikes and the effluent weirs.All original dikes for the six ponds were constructed from humus-free clay and rock material, which was obtained, preferentially, by excavating from within the dike area. Run-off water, precipitated on the outside slopes of the dams will drain off without contacting the tailing material. A ditch was made north of the dam site to deflect surface run-off to the east into a branch of Flemming Brook.A secondary dike, made from tailings, has recently been erected on No. 1 and No. 2 tailings pond inside and above the earth-filled dike which serves as a roadway. Run-off from the tailings dikes will be retained inside the ponds by ditching between the roadway and tailings dike into ponds 4 and 6."

Jan 1, 1969