By M. J. Salkind

In order for fiber composite materials to find extensive use in structures, it is necessary to develop techniques for joining these materials. Riveting and adhesive bonding are two possible techniques which have been investigated although the former is less desirable because the low shear strength of most matrices makes this type of joint subject to bearing failure. Welding is an effective means of joining, especially for high-temperature applications where ad-hesives are weak; however, there are significant limitations placed on welding composite materials. The commonly used fusion welding techniques will find less use for joining composites because the two phases are often unable to stand exposure to such a stringent environment. In the case of eutectic composites, fusion welding will completely destroy the controlled microstructure. Solid-state techniques such as diffusion bonding offer potential success with certain design requirements placed on such joints. Since the primary mechanism of load transfer from matrix to fiber is shear parallel to the fibers, little load can be transferred across a butt-welded interface perpendicular to the aligned fibers. Successful joint designs must have a component parallel to the fibers to allow a shear area for load transfer. Configurations such as lap and scarf welds are likely to be successful. This note describes some results of experiments with diffusion-bonded joints in A13Ni whisker-reinforced aluminum. The composite material, prepared by unidirectional solidification of the A1-A13Ni eutectic, is described elsewhere.'-' It consists of aligned micron size whiskers in a matrix of aluminum. Since it has been shown that the microstructure of

Jan 1, 1969

By J. C. LaScola

Development of methanometers and anemometers for underground use in coal mines is reviewed. The first semicontinuous recording methanometer was developed in 1961 in West Germany. The Bureau of Mines developed an instrument using; pellesters that was a continuous recording methanometer. Expansion of freon gas created a vacuum which pulled the methane-air mixture through a tube to an electrically heated, catalyst-impregnated pellester where the mixture was burned. The National Coal Board of England developed a continuous recording methanometer based on the principle of the Davy flame safety lamp. A thermo-pile was used to sense the hurt output of the flame. Finally the Bureau of Mines improved its methanometer by eliminating the freon gas and using a diffuser head to a monitor methane-air mixtures. Development of recording anemometers proceeded from the use of a photo¬cell and light source to sense rotation of the Biram-type anemometer blades to the use of a Hall detector to sense, rotation by measurement of electromagnetic pulses.

Jan 1, 1969

By William J. Gillich, Gerald L. Moss

PREVIOUS studies of the shock loading of randomly oriented polycrystalline aggregates have firmly established that, after rather short load duration, hydrostatic compression closely approximates the shocked state.' However, McQueen deduced from pressure measurements with good time resolution that, during shock loading, metals begin to undergo a stress relaxation at the yield stress. He suggested that the relaxation is due to plastic deformation accompanying the change from a one-dimensional compression to a three-dimensional, hydrostatic, compression.' Stress relaxation may occur faster as stress is increased above the yield stress, but the existence of unidirectionally compressed states for finite times suggests that the concept of a unidirectionally distorted lattice should furnish considerable insight into the mechanical behavior of materials subjected to shock loading. Here, a crystallographic analysis is presented for the hypothetical situation where atom motion may be considered as unidirectional which, as indicated above, is a useful extension of the macroscopic concept of shock loading to the microscopic domain. Only motion caused by the com-pressive forces is treated; i.e., lattice vibrations upon which this motion is superimposed, as discussed by Fitzgerald, are ignored.3 The purpose of the analysis to be presented is to develop a description for single crystals of the lattice rotations that occur for idealized uniaxial strain deformation. The usefulness of such an analysis in realistic deformation is to give a method of specification of those properties of an initially distorted lattice which would affect the subsequent deformation. Non-axial complications that arise experimentally, such as off-axis rarefaction waves, must be treated in proper context. Consider the material element shown in Fig. 1 and let the compression be uniform at all regions of the element. Then, any interior point of the element is displaced in proportion to its distance from the base of the element. Accordingly, if the top of a unit element is displaced by an amount, (-K), with respect to the base, a point P(X, Y) will be displaced by (-KY). Crystal planes are, therefore, rotated by the compression. Analysis of this rotation may be accomplished from the geometry shown in Fig. 1 where the line OP is the edge of the plane {hkl} and N is its normal. The orientation of the crystal plane with respect to the shock direction is specified by the angle, before deformation. After deformation the edge of plane {hkl}

Jan 1, 1969

By G. E. Warner

This paper presents a review and analysis of a highly stratified Burbank sand waterflooding project in Osage County, Okla. Permeability values in this reservoir range from less than 0.1 md to nearly 3 darcys, and 90 percent of the permeability capacity is contained in approximately 26 percent of the reservoir volume. To date, the project has recovered 103 bbl/flood-acre-ft since waterflood initiation, which represents 50 percent of the total preflood cumulative and 12 percent of the original stock-tank oil in place (OSTOIP). The outstanding feature of this project has been the economical recovery of a sizable quantity of oil at water-oil ratios higher than those normally considered prohibitive. Nearly 70 percent of the recovery to date has been achieved at water-cut values greater than 95 percent. An ultimate waterflood recovery of 138 bbl/flood-acre-ft, or 67 percent of the preflood recovery and 16 percent of the OSTOIP, is predicted. The ultimate primary and secondary recovery will be 302 bbl/acre-ft and approximutely 40 percent of the OSTOIP. The actual performance is compared with the predicted performance by both the Stiles and the Dykstra-Parsons methods, and applicabiliry of these methods to this particular reservoir is evaluated. The performance of this project indicafes highly stratified reservoirs can be successfully and economically waterflooded when either reservoir or economic conditions preclude the use of mechanical and chemical means of mdbility control. Introduction The concept of the stratified reservoir has been used by reservoir engineers for many years to describe the vertical variations in permeability within a reservoir. Numerous techniques have been advanced to predict the expected waterflood performance of the stratified reservoir, and in most cases they prove reasonably accurate. The advisability of undertaking a prospective waterflooding project is determined, based on these predictions. This paper presents a review of a waterflood project in a highly stratified reservoir that normally would be considered a marginal prospect, at best, when evaluated with any prediction technique properly adjusted for reservoir conditions. This kind of project can be successful if the predictions are used to design a waterflooding system capable of economically recovering an oil cut of 1 to 2 percent. Experience gained in the early stages of the project's development was profitably applied in the later development of the entire reservoir and could prove beneficial to other projects with similar reservoir stratification or fracture characteristics. The East Burbank pool waterflooding operations have been developed in three separate stages, each of which has been a separate project: Mid-Burbank Unit, Flood A, and Stanley Waterflood. When referred to collectively, these projects will be called the Composite Project. The Skelly Oil Co.'s Barber lease — the only portion of the pool not included in the three projects — is operated as a separate facility with a cooperative injection-well agreement. It contains less than 80 productive acres and would not significantly affect the over-all performance picture.

Jan 1, 1969

By John Nagy

The Bureau of Mines examined explosion development in a closed spherical vessel, mathematically correlating flame travel, pressure, and time with parameters defining the reaction. The model assumes that burnt and unburnt zones are separated by a thin, radially moving flame front. Isothermal and adiabatic systems are considered. Correlation with gas and dust explosion data is better for the adiabatic system, but the isothermal development is simpler and in reasonably good agreement. Interpretation of the explosion phenomena is facilitated by expressing the rate of mole change in the flame front in terms of elementary parameters. This expression is developed by examining the components of spatial-flame velocity.

Jan 1, 1969

By K. Takahashi, I. Iwasaki

it is well known1 that racemic mixtures of optical isomers can be separated by passing their solutions through a column packed with r- or 1-quartz powder so that one of the isomers becomes adsorbed selectively on the asymmetric quartz surfaces. Although the natural occurrence of r- and 1-quartz is more or less equally distributed, some localities show enough deviations toward a higher proportion of l-quartz2 to suggest that optical isomerism might influence quartz flotation. Beta-amines have an asymmetric carbon atom, and therefore optical activity may be expected. Beta-amines are reported to behave quite differently from alpha-amines in the flotation upgrading of certain oxidized iron ores.3 It is of interest, for both practical and theoretical reasons, to determine whether or not optical isomerism plays a role in the amine flotation of quartz. In this article the results of Hallimond tube flotation tests and of adsorption measurements using d-beta-phenylisopropylamine on both r- and 1-quartz are compared. D-beta-phenylisopropylamine was chosen for the tests because it is commercially available in optical isomers. MATERIALS AND METHODS Brazilian quartz crystals were hand-sorted according to the difference in trigonal trapezohedral faces, and each crystal was further checked by the Airy's spiral.4 The respective crystals were then crushed, and the -150 + 200-mesh fractions were screened out for the Hallimond tube tests. The samples were cleaned by brief leaching with warm, dilute hydrochloric acid, and then by repeated rinsing with distilled water. In preparation for the adsorption measurements, they were then dry-ground in a pebble mill for several hours, washed a few times with distilled water, and finally dried in a vacuum desiccator. By means of the Krypton gas adsorption method, the specific surfaces of r- and 1-quartz samples were determined to be 27,700 and 19,800 sq cm per gm respectively, the difference being due mainly to the decantation procedure rather than to the inherent difference in their grindability. D-beta-phenylisopropylamine was the only collector used in the study. It was solubilized by neutralizing with 110% of the stoichiometric requirement of 0.1 N hydrochloric acid. The specific rotation of the d-beta-phenylisopropylamine was determined with a polari-meter using sodium D line to be, Although the d-beta-phenylis~prop~lamine showed absorption maxima in the wave length region of 250 to 270 millimicrons, due presumably to the phenyl group, these peaks were too sensitive to be used for colorimetric determination of the residual concentration in the adsorption measurements. The amine-picrate method, used in the colorimetric analysis of dodecylammonium chloride,' was found to work satisfactorily for the d-beta-phenylisopropylamine. The adsorption densities were thus determined after equilibrating 40 gm of the ground quartz sample with 300 ml of solution by tumbling in separate glass-stoppered Erlenmeyer flasks for one hour. EXPERIMENTAL RESULTS Fig. 1 presents the adsorption densities of d-beta-phenylisopropylamine on the r- and 1-quarts in the pH range of 6 to 7.5. In agreement with data reported in the literature, the adsorption density of d-beta-phenylisopropylamine was slightly higher on the r-quartz than on the 1-quartz, although the difference was not as pronounced as one might expect from the capacity of r-quartz and 1-quartz to separate racemic

Jan 1, 1969

By Forrest T. Moyer

The safety record of the metal mining and milling industries in 1965 is reviewed by the Bureau of Mines. The overall injury-frequency rate of 23.77 per million man-hours was 5 percent lower than in 1964 and was the lowest annual rate in a statistical history beginning with 1931. The injury-severity rate of 3,521 days lost per million man-hours in 1965 represented a 5-percent improvement over 1964. However, the total of 3,825 disabling work injuries comprised 61 fatal and 3,764 nonfatal injuries, one and 92 more, respectively, than in 1964. At primary nonferrous smelters, refineries, and reduction plants, the injury-frequency rate of 8.97 per million man-hours in 1965 was 13 percent lower, but the severity rate percent higher than in 1964. these plants in 1965, 4 more of 1,173 days lost per million man-hours was 17 There were 12 fatal and 971 nonfatal injuries at and 28 fewer, respectively, than in 1964.

Jan 1, 1969

By Verne E. Hooker

In situ stresses, based on isotropic and anisotropic relations, were evaluated using computer techniques from overcoring data obtained in dimension stone quarries along the Appalachian Piedmont, the Ozark Uplift, and the Ouachita Tectonic Belt. Stresses in the horizontal plane near the surface are compressive and range from 100 to 4,500 psi. The direction of maximum compressive stress seems to be alined with the general tectonic structure for most of the determinations. The ratio of the maximum to minimum elastic parameters in the horizontal plane ranges from 1.05 to 2.46 for these competent rocks. Isotropic versus anisotropic stress determinations show differences only as great as 25 percent in stress magnitude and 25° in orientation.

Jan 1, 1969

By E. J. Wasp

The transportation of mine products incurs a cost which can have a significant bearing on the competitive position of the manufactured product. Clearly, the engineer who is responsible for selecting a mode of transport must base his decision, at least in large measure, on economic comparisons. And today, the engineer usually finds that he has to choose between several modes, including slurry pipelines. For the purpose of an initial economic screening, it is not necessary to go deeply into the technical details of a slurry system. What is usually needed, however, is a method with which the engineer can make a quick economic assessment to determine whether a slurry pipeline should be included in the detailed final analysis. This paper presents a rapid method for making such a preliminary appraisal. Experience with commercial slurry pipeline systems in several countries and with a variety of solid materials has shown that if several assumptions pertaining to critical design variables are made, it is possible to roughly estimate the transportation cost of a slurry system on the basis of only three factors: the specific gravity of the solid material, the length of the system, and the quantity of slurry to be pumped each year. It is assumed that conditions pertaining to field construction, corrosion inhibition, and the like, will be favorable. This assumption is critical because any factor which analysis shows to be particularly unfavorable will raise the total transportation cost estimate which this paper establishes. If the engineer employs this estimating procedure and decides that the use of a slurry pipeline is economically unattractive, his chances of being wrong are small. Conversely, if his quick appraisal indicates that the use of a slurry system is economically favorable, the engineer is justified in committing the time and money needed to make a more detailed investigation of the slurry pipeline potential.

Jan 1, 1969

By Wesley T. Holmes

In this final stage of a three-part investigation of the smelting of titania-bearing iron materials, the Bureau of Mines conducted semicontinuous smelting tests in a laboratory electric arc furnace on four concentrates and one are. The objective was to substantiate the significance of liquidus temperature measurements in predicting satisfactory slag compositions in electric furnace smelting of titaniferous magnetites to produce pig iron. Previously obtained liquidus temperature data were used in determining flux requirements. Self-fluxing pellets of either ore or concentrate plus fluxes and reductants were made to produce pig iron and slags containing 0.2 to 0.6 percent titanium. Individual constituents of the slags generally agreed within 5 percent with the value of the corresponding constituent of target composition. Liquidus temperature of furnace slags generally agreed within 50° C of the value obtained from corresponding nominal synthetic slag. The results of the three phases of the investigation may serve as guide-lines for determining flux requirements in smelting a wide variety of titaniferous magnetites and other titania and iron-bearing materials.

Jan 1, 1969

By S. K. Asunmaa, W. D. English, N. A. Tiner, W. A. Cannon

This paper discusses the reaction of metal surfaces with fluorine. Fluorination reactions result in the formation of metal fluoride films which are "passive" toward further reaction of the metal with fluorine. These films are very adherent, and do not easily detach from the substrate metal by mechanical flexing or thermal shock. Exposure of passive films to a humid atmosphere produces hydrated metal fluorides which cause secondary fluorination reactions upon reexpo-sure of the metal surface to fluorine. The surface films formed range from 10 to 30A in thickness and they pow at the expense of surface oxide films. The apparent film formation is completed rapidly in 15 to 30 min on stainless steel and nickel surfaces. On copper and on Monel surfaces, the film at first grows rapidly, then increases slowly over an extended period of time. Passive films are formed at all fluorine pressures in the range from 0.1 to 1.4 atm at room temperature. ALL metals react when exposed to fluorine. These reactions generally produce surface films which consist of metal fluorides. The rate of reaction is largely determined by the extent to which these films are protective. Although there is an extensive literature concerning reactions of oxygen with metals, there are very few investigations reported concerning fluorine-metal reactions. Brown, Crabtree, and ~uncan' investigated the kinetics of the reaction of gaseous fluorine with copper metal which had been freshly reduced in hydrogen. The reaction rate was independent of pressure over the range from 6 to 60 torr. A logarithmic rate law was obeyed in the temperature range from 25" to 300" ~. There was some deviation at higher temperatures which could have been the onset of a parabolic law. The calculated film thicknesses ranged from about two molecular layers, 10A, for 5 hr exposure at room temperature to thirty-five molecular layers for 5 hr exposure at 200" . The authors concluded that no single mechanism could explain all the observations. O7Donnell and spatkowski2 studied the reaction of fluorine with copper at 450°C at pressures from lo to 133 torr. The reaction was found to be pressure -dependent and followed a logarithmic rate law. It was not entirely diffusion-controlled, and fluorine was thought to be the migrating species in the reaction. Miscellaneous metal-fluorine reactions were investigated by Haendler et ~1.~ Reaction products were identified but no rate data were determined. Air Prod- ucts and Chemicals, Inc., have conducted an investigation of reactions between fluorine and various metal powders at room temperature and 85° C. Fluoride film thickness as a function of time of exposure was reported on the assumption that the reaction takes place between fluorine and metal to form the normal metal fluoride. Surface areas of the powders were only estimated so the relative film thicknesses may not be exact. The data showed reaction rates which were generally logarithmic in character, the rate of film growth virtually ceasing after a few hours exposure time for some alloy powders. The effect of moisture on fluoride films was also investigated by measuring additional reaction with fluorine after exposure of passivated powders to atmosperic moisture. The fluorination of iron was studied by 0'~onnell~ at temperatures from 225" to 525" ~ and at pressures ranging from 20 to 200 torr. In all ranges, the reaction followed a logarithmic rate law and was dependent on the square root of the gas pressure. The author concluded that fluorine gas passes through pores in the film. As the film grows, the blocking of pores leads to a rapid decrease in reaction rate; hence a logarithmic rate law is observed. Jarry, Fischer, and Gunther' investigated the mechanism of the reaction of fluorine with nickel at about 600" to 700°C. On the basis of the metallographic examination of fluoride scales growing on the nickel and from separate radioautographic data, it was claimed that fluorine is the migrating species in the reaction. This is in sharp contrast to the growth of oxide films on nickel where it has been shown that nickel ions migrate through the scale to the gas-solid interface to react with oxygen. Few investigations have been reported of the reaction of fluorine with metal oxides. Such investigations should be of great significance for a better understanding of passivation in view of the ubiquitous oxide films on technical alloys. Haendler et al.3 studied the reaction of fluorine with oxides of copper, tin, titanium, zirconium, and vanadium. Copper (I) oxide reacted as follows in the temperature range 150" to 300"~: temperature above 300" ~ was required for the CuO to react to form additional copper fluoride. Ritter and smith7 also investigated the reaction of fluorine with copper (11) oxide. An oxide powder comprised of spherical particles with a fairly high surface area was reacted with fluorine, starting at room temperature and increasing to 100° C over a period of 3 or 4 hr. The initial reaction was slow until the fluoride film thickness reached about to or 15R at which time the reaction rate accelerated, then decreased again. Most of the kinetic data was obtained during this final phase of reaction. The authors conclude that the film grows slowly at first until the stresses developed in the distorted lattice are sufficient to rupture the initial

Jan 1, 1969

By David L. Holt

The contribution of grain boundary shear to total elongation, CS/E&apos;, has been measured in an Al-Zn eu-tectoid alloy that was quenched from above the invariant temperature, then annealed at 250° C to a grain size of&apos; 1.8 p. At 250°C, ks/E&apos; is low at both high and low strain rates, but reaches a maximum, estimated as 60 pct at an intermediate rate of 5 X 10 per rnin. Rate sensitivity, as measured by the index m = a log a/a log E&apos;, follows the same trend, and furthermore the maximum values of m and -cur at approximately the same strain rate. This result, combined with the metallographic observation that boundary migration enhances boundary shearing, is interpreted as supporting a previous suggestion that the high rate sensitivity characterizing super-plasticity is the result of combined boundary shearing and migration. It is suggested that the latter event relieves stress concentrations at triple points, and smoothes boundaries so that stress is governed largely by a viscous boundary shear. GrAIN boundary shear has been considered in relation to superplasticity in several recent papers.&apos; The problem has been to explain the high strain rate sensitivity of flow stress, and the variation of rate sensitivity with strain rate (E&apos;) and grain size (L). The requirements for superplasticity, small L and high T, suggest the reasonableness of an approach to high rate sensitivity involving grain boundary shear. Further support came from experiments on the A1-Cu eutectic alloy,&apos; where it was found that strain rate sensitivity of cast material annealed to produce an equiaxed, micron-size grain is always low; taking as an index of rate sensitivity m = a log a/a log <, m < 0.3. However, m in hot-worked alloy of comparable grain size can be as high as 0.7. In the cast and annealed material, each phase is a single crystal, the only boundaries are interphase boundaries, and it is, consequently, geometrically impossible for boundary shear to contribute to deformation in any major way. Other observations (for hot-worked material) were a-L at constant (low) strain rates and indications that the rate of recrystallization was enhanced as strain rate increased. As a result of this work, it was proposed that high rate sensitivity arises from a deformation mode of boundary shear associated with boundary migration. Migration serves to relieve stress concentrations at triple points, and smoothes boundaries so that they assume properties of fluid films. On the other hand, the low rate sensitivity observed at high and low strain rates reflects deformation of bulk material. Measurement of the variation of grain boundary shear with strain rate and m have not yet been made. Such measurements are important, especially in view of a proposal, differing in detail from the above, that high m arises merely from a transition between a grain boundary shear mode of deformation at low rates to a transgranular mode at high rates.2&apos;4 In the present work, the contribution of boundary shear to total deformation is measured and in addition metallographic observations are made on surfaces of deformed specimens to look at the interaction between boundary shear and migration. The Al-Zn eutectoid alloy was chosen for its homogeneous, fine-grained structure, which is obtained readily without hot-working. It has also been the subject of a previous phenom-enologically directed study. EXPERIMENTAL Material. Compression specimens, cross section 4 by + in., length \ in., were machined from a sand-cast ingot of composition 77.5 wt pct Zn, 22.5 wt pct Al. (The melt was prepared from 99.9 pct Zn and 99.99 pct Al.) After homogenization at 375°C for 50 hr, the specimens were quenched in brine and removed before the heat evolution that accompanies de -composition of the high-temperature phase.5&apos;6 The resulting microstructure, see Fig. l(a), was too fine for grain boundary sliding to be easily studied; coarser structures were obtained by annealing for various times at 2 50°C. Annealing was terminated by a brine quench. Final average intercept lengths between all grain boundaries (both interphase and those lying in a phase), L, were: 0.5 p [annealed for 15 min, Fig. (a)], 0.8, 1.1, and 1.8 p [Fig. l(b)l. Testing Procedure. An Instron machine was used for most of the compressive deformation. Tests were of two types: those in which crosshead velocity was changed in steps to measure m as a function of strain rate15 and tests at constant velocity to a fixed (engineering) strain of -0.2 (20 pct). Stress reached a steady-state value (a) which was plotted, on a logarithmic scale, against log strain rate (E&apos;). An alternate and equivalent evaluation of m was to take the slope of the log o vs log 6 curve. Time at temperature before testing was 15 min. Strain rates covered by the Instron (4 x lo-&apos; to 4 x 10&apos; per min) were insufficient; at a higher rate of 5 x lo2 per min a gas-operated testing machine was used, the gas driving a piston to compress the specimen at a controlled velocity.&apos; To obtain points on the log a vs log E&apos; curve at low rates, specimens were compressed by a dead weight. strain rate was an average value computed by dividing strain at the end of test by loading time. In some tests strain was measured at fractions of the loading time; creep rate was found to be reasonably constant.

Jan 1, 1969

By C. Laird, C. E. Feltner

May different kinds of dislocation structures have been observed in strain-cycled metals and alloys. In order to understand their pattern and causes, an experimental program has been carried out to determine the influence on the dislocation structures of the three variables: 1) slip character of the material, 2) test temperature, and 3) strain amplitude. The results show that at high strain amplitudes cell structures me formed when the slip character is wavy, and that these are progressively replaced by uniform distributions of dislocations as the stacking fault energy is decreased. At lower strains, dislocation debris is formed which consists primarily of dipoles in wavy slip mode materials and multipoles in planar slip mode materials. Temperature merely acts to change the scale of the structure, smaller cells, and clumps of dislocation debris being associated with lower temperatures. It is shown that the results for many metals fit this pattern, which Parallels that occurring in unidirectional deformation. DISLOCATION structures produced by cyclic strain (fatigue) have been examined in a number of metals by transmission electron microscopy. These studies have produced a variety of interesting and often seemingly conflicting results. For example, different investigators have reported such structural features as cells.le4 bands of tangled dislocations,4&apos;5 dense patches or clusters of prismatic dislocation loops, planar arrays,4&apos;10 and various combinations or mixtures of these different structures. Most of these observations have been made on materials which were initially annealed and cyclically strained at low amplitudes resulting in long lives. Recently we have reported observations of the dislocation structures produced in copper and Cu-7.5 pct Al cycled at large amplitudes, resulting in lives of less than 104 cycles.4 These results, examined in combination with those in the literature, have suggested that a common or consistent structural pattern exists. Variations in this pattern appear to be determined chiefly by the three variables, namely, the slip character of the material,4,11 test temperature. and the strain amplitude. To verify this interpretation, we have studied [he influence of the above three variables (in different combinations) on the resultant structures in cyclically strained metals. Copper, fatigued at room temperature, was chosen as a reference state to which all other observations can be compared. The effect of slip character has been investigated by employing fcc metals of different stacking fault energy. Thus aluminum which has a more wavy slip character than copper, and Cu-2.5 pct A1 having a more planar slip char- acter, have been examined. The aluminum samples were fatigued at 210°K thus making their homologous temperature equal to that of copper at room temperature. The influence of temperature has been evaluated by examining the structures in copper at room temperature and 78°K. Finally the effect of strain amplitude was studied by looking at the structures at amplitudes giving lives ranging from 104 to 107 cycles. All of the specimens were examined at the 50 pct life level at which stage the structures have reached a stable configuration.12 I) EXPERIMENTAL PROCEDURE Strip specimens, 0.006 in. in thickness, were prepared from base elements of 99.99 pct purity or greater. Specimens were fatigued by cementing the strips to a lucite substrate which was subjected to reverse plane bending. This method of testing has been described e1sewhere.7 After fatiguing, specimens were thinned and examined in a Philips EM 200 which was equipped with a goniometer stage capable of ±30-deg tilt and 330-deg rotation of the specimen. On the basis of separate calibrations,13 allowances were made for the relative rotation and inversions between the bright-field images and the diffraction patterns. II) RESULTS AND DISCUSSION The life behavior of the materials under different test conditions is shown in Fig. 1 in the form of plots of total strain range vs cycles to failure. Comparisons of structures produced in the different materials were made at amplitudes which produced equal numbers of cycles to failure. The influence of strain amplitude on the structures produced in the reference state material (copper tested at room temperature) is shown in Fig. 2. At the 104 life level the structure produced comprises cells similar to those previously observed.3,4 They are approximately 0.5 p in diam and the cell walls are generally more regular or sharper than those produced by unidirectional deformation.14 At the 10&apos; life level the

Jan 1, 1969

Stope control information at the C.S.A. mine is obtained by diamond drilling inclined holes from within the stapes. Practical mining outlines are determined from complicated ore contours by a joint mining engineering and geological study. Production holes to achieve this outline are individually marked up and checked. Stope control also extends to selective mucking of ore mixtures for metallurgical reasons and to marginal ore and waste mixtures for economic reasons.

Jan 1, 1969

By Martin H. Stanczyk

Under the Solid Waste Disposal Act, the Bureau of Mines initiated several accelerated in-house research programs to develop new and improved methods of proper and economic solid waste disposal. The program being conducted at the Bureau&apos; College Park Metallurgy Research Center is concerned with eliminating the current waste of valuable materials in municipal refuse by developing low-cost methods for reclaiming and recycling the metal and mineral values contained in incinerator residues. Each year the United States must collect and dispose of in some manner or other, about 150 to 200 million tons of municipal solid wastes. The monetary output for this service ranks third among public services, exceeded only by the costs for schools and roads based on population growth projections and materials use patterns, the quantity of refuse generated by the early 1980&apos;s may approach 300 million tons annually. Currant estimates indicate that only 10 to 20 percent of the total municipal refuse generated is disposed of by incineration. If all refuse were properly incinerated the residues would contain more than 11 million tons of iron and nearly a million tons of mixed nonferrous metals including aluminum, copper, lend, zinc, and tin.

Jan 1, 1969

By J. R. Hauber, N. R. Borch

A study uras made on the creep behavior of cast and extruded SR grade beryllium. It is shown that, for stresses below about 1000 psi in the temperature range 760" to 85o° c, the creep behatior is nearly exactly described by the Nabarro-Herring mechanism. The activation energy is apparently that for self-diffusion, 42 2 kcal per mole, below 1000 psi, but it rises to 88.6&apos; kcal per mole at higher stresses. The slress exponent is 4.5 at the higher stresses. Tertiary creep in this material is clearly related to void formation apparently caused by grain boundary sliding. BERYLLIUM is becoming an increasingly important technological material. A search of the literature has revealed a lack of fundamental studies on the creep of beryllium. This investigation was therefore undertaken to gain insight into the creep behavior of this material. EXPERIMENTAL PROCEDURE Tensile creep samples were prepared from cast and extruded SR grade beryllium. The vendor&apos;s chemical analysis of the beryllium tested is shown in Table I. The test specimens were machined as shown in Fig. 1 from i -in.-diam rods. The machined creep specimens were annealed to remove surface damage and to establish a variation in grain size. The heat treatments and their resulting grain diameters are shown in Table 11. The average grain diameters were determined by the intercept method. True average grain diameters were estimated by multiplying the measured average grain diameters by 1.5.&apos; The creep tests were performed at temperatures from 700" to 850°C in a vacuum of 105 Torr or better in a tantalum-element resistance furnace. Loads were applied by an Instron testing machine such that the stress was held constant to within 20 psi. The test temperature was measured by thermocouples on the sample. With one exception the deviation from the desired test temperature was 2"C, and in that case the deviation was 4"C. Elongations were measured by an extensometer within the vacuum chamber which was fastened to the creep specimens at the grooves in the grip ends, as shown in Fig. 1. The precision of measurement of elongation was 1 X loe4 in. The creep tests were begun only after thermal equilibrium had been established in the sample and the extensometer to insure that there was no strain rate component due to transient thermal effects. Two kinds of creep experiments were performed. First, at constant grain size, the effects of varying stress and temperature were studied. In the second set of experiments, the temperature was held constant and the grain size was varied. The activation energy for creep was determined by varying the temperature at constant stress, as described by orn, during the first set of experiments. The variable grain size experiments revealed that creep at low stress apparently occurred by the abarro-errin&apos; mechanism. In all of the creep tests, the stress was held constant only until sufficient strain had occurred to accurately determine the creep rate. The stress was then raised to a new value and the new creep rate determined. This process was reported until tertiary creep occurred. In this manner several data points were obtained from each specimen. The assumption was made that the structure was not changing appreciably between the incremental stress levels. This was verified by reducing stresses to previously tested levels and comparing the creep rates with the creep rates obtained at the lower strains. The re-producibility was within experimental error over strains on the order of 1 pct. EXPERIMENTAL RESULTS A typical series of creep tests is shown in Fig. 2. Primary creep was not observed in any test. Transient creep, which we define as creep rates that are nonlinear with time, was not observed for any change in stress except where tertiary creep occurred. The absence of both primary and transient creep has been previously reported for hot-pressed powder beryllium.= The data for the creep behavior at constant grain size are summarized in Fig. 3. The data show two distinctly different stress dependencies. At stresses below about 1000 psi, in the equation:

Jan 1, 1969

By C. C. Shale

A semicommercia1, high-temperature electrostatic precipitator and adjunct equipment are described, and operating characteristics at 1,470° F and 80 psig are presented for both positive and negative polarity. Removal efficiency for negative corona waS about 91 to 96 percent while that for positive corona was only about 75 to 77 percent. Results are compared with those from bench-scale investigations, and equipment limitations are discussed. Theoretical aspects of the precipitation process are related to the operating characteristics.

Jan 1, 1969

By J. H. Bechtold, R. Kossowsky

1 HE superplastic behavior of the eutectoid A1-78 wt pct Zn alloy has been thoroughly investigated by Back-ofen et al.&apos; The superplastic elongations and the marked resistance to necking were rationalized in terms of high strain rate sensitivity. In a subsequent paper2 superplastic behavior was formulated to show Nabarro-Herring diffusional creep as rate controlling at low strain rates, giving way to a dislocation climb process at higher strain rates. In a paper devoted to an interpretation of superplasticity in two-phase alloys, Packer and sherby3 have included the results of an examination of the structure of an Al-Zn eutectoid specimen before and after superplastic deformation. No significant change in grain size or directionality was observed in the deformed microstructures. This one observation led the authors3 to suggest that con- tinuous recrystallization or grain boundary migration was responsible for superplasticity. The purpose of this note is to report our observations on the superplastic behavior of the Al-Zn eutectoid alloy which differ in certain respects from works previously reported. Following Hayden et al., the results are discussed in terms of dislocation climb as the important factor during superplastic deformation. A heat of nominally high (99.995) purity 22 wt pct A1-78 wt pct Zn was induction-melted and cast into a 0.5 by 6 by 12 in. slab. The slab was heated to 350°C and rolled to 1/8-in.-thick plate. The plate was then cold-rolled to 0.040-in. thickness, annealed at 35OaC, and rolled to the final thickness of 0.020 in.* Speci-

Jan 1, 1969

By Donald S. Colby

This Bureau of Mines report is essentially a handbook, or manual, for making the type of mineral resource valuation commonly required for such public policy problems as mineral leasing. The principle of resource valuation through the capitalization of cash flow is well established. A mathematical procedure, based on a simplified accounting system, is detailed for calculating cash flow from revenue, plant costs, and operating expense. Variations of procedure cover cost depletion, percentage depletion, and depletion limited to 50 percent of net income. The influence of the depletion provisions of the tax regulations on the value of a resource to an owner and to an operator is analyzed. The relationship of royalty, bonus payments, and sales price to resource value is also described, and methods for approximating resource values using these payments as input data are developed.

Jan 1, 1969

The lead concentration of flotation feed ore slurries is determined using two ?-ray absorption gauges mounted directly on a 6 in. diameter flotation feed pipeline. One gauge is a conventional &quot;density&quot; gauge using CS137. The other is a &quot;lead-sensitive&quot; gauge, which depends on the preferential absorption. by lead of 225 key y-rays resulting from Compton backscatter of CS137 y-rays.Gauge outputs are combined using an analogue computer the output signal of which is directly proportional to the lead concentration of the pulp. The accuracy of measurement of the pulp lead concentration is &#177; 3&#183;6 per cent for ore slurries with lead concentrations in the range 0&apos;07-0&#183;16 g/c.c. and pulp densities 1.43-1.60 g/c.c.This paper sets out the development of the technique and details are given of the two experiments (1964, 1966) conducted in the plant at North Broken Hill Limited. The installation of the two-gauge system inthe plant during May 1968 is described. Details are given of the calibration technique used and the results obtained.

Jan 1, 1969