By P. L. Raffo, T. E. Mitchell

Single crystals of Ta-Re alloys have been deformed in tension and compression as a function of solute concentration and temperature. The temperature dependence of the yield stress is decreased by alloying. At low temperatures there is a minimum in the yield stress (at about 2 at. pct) as a function of concentration. Three-stage hardening was not observed in the alloys. Linear hardening rates, where observed, were characteristic of stage II in pure tantalum. At low temperatures and high concentrations, work softening was often prominent at high strains. Electron microscopy revealed that dislocations are mostly of screw orientation, although heavily jogged and cusped, and often occurring in dipole pairs. The alloys become more prone to cleavage with increasing rhenium content, due mostly to an increasing yield stress rather than a change in cleavage strength. Alloying apparently decreases the Peierls stress of bcc metals at low temperatures by facilitating kink nucleation at solule atoms on screw dislocations. Higher solute concentrations further increase the yield stress. Quantitative calculations and comparisons with other bcc alloy systems are made to show that the predominant hardening mechanism is due to the interaction of dislocations with misfitting solute atoms close to their slip planes. The interaction is so localized that the core dilatation of dislocations could be important. CONSIDERABLE interest has arisen in recent years concerning the mechanical properties of unalloyed bcc metal single crystals.'-7 These and similar studies on polycrystalline materials have resulted in a considerable understanding of the macroscopic yielding characteristics8, 9 and the process of work hardening.'' This latter advance is due in a large part to the increased use of transmission electron microscopy in P I RAFFO junior Membar AlMF is Metallyureist Iewis such studies and the general observance of three stages of work hardening in the shear stress-shear strain curves. The properties of substitutional alloy single crystals of bcc metals have not been determined in as much detail as in the pure metals. Insufficient systematic studies have been made on the effect of alloying on the magnitude and temperature dependence of the yield stress or the stress-strain curves. The alloy systems which have been studied to some extent have been Ta-W,11, 12 Ta-Mo," Ta-Nb,12'14 Mo-Re,15 W-Re,16 and alloys of iron with nickel,17 platinum,17 vanadium,18 and aluminum.18 A large body of data exists on Fe-Si alloys, but these have mainly been a result of the experimental convenience of using this material in place of unalloyed iron, rather than a comprehensive study of the mechanical properties of the alloy system per se. The present authors have previously reported additional data on the properties of Ta-Re, Ta-W, and Ta-Mo alloy single crystals.1g Some of the data on Ta-Re alloys will be described later in this paper. Briefly, single crystals of Ta-Re (1.2 to 10.6 pct), Ta-W (6.2 and 10.2 pct), and Ta-Mo (2.9 and 9.0 pct) were grown by the floating zone method in vacuum. Compression tests were performed in the temperature range 77" to 623°K. Slip was found to occur in Ta-Re alloys at 77' and 298°K on the (~ll)[lil] system and slip lines were coarser and straighter than in unalloyed tantalum. No three-stage hardening was observed in any of the alloy systems and the curves were nearly parabolic. At temperatures above 175°K the yield stress* increased monotonically with in- creasing composition while at 77" and 175°K the yield stress initially passed through a minimum after which it began to increase again for concentrations greater than about 2 pct Re. Similar minima were observed in Ta-Mo alloys and to a lesser extent in Ta-W alloys. The minimum was interpreted as being a result of a

Jan 1, 1969

By M. A. Dayananda

Based on the Kirkendall frame of reference, a method is proposed for the determination of atomic mobilities of all the diffusing species in a multicorn-ponent system with a single diffusion couple. The method is based on an atomic mobility model developed on the concept of negligible interactions among the intrinsic fluxes. It is shown in the model that mobilities can be obtained directly from the cumulative intrinsic fluxes past the Kirkendall interface. The proposed method replaces the need for a prior determination of interdiffusion coefficients far the calculation of mobilities. Relations between intrinsic diffusion coefficients and mobilities are derived and the mobility calculations are illustrated with diffusion data in Cu-Zn-Mn alloys at 850°C. ThE concept of "intrinsic flux" with respect to a fixed lattice was introduced "i Darken1 to explain toa Kirkendall effect2 demonstrated by the motion of inert markers during isothermal diffusion in single-phase binary solid solutions. Based on this concept, intrinsic diffusion studies have been made in various binary metallic systems3,4 employing such a lattice frame of reference, commonly referred to as the Kirkendall interface. Similar approaches, both theoretical and experimental, have been presented5"10 to study intrinsic diffusion in multicomponent systems. Based on the direct integration of Fick's law extended to multicomponent diffusion, Philibert and Guy8 proposed a method for the determination of intrinsic diffusion coefficients. For an n-component system, this procedure requires an experimental study with (n — 1) diffusion couples, all having their Kirkendall interfaces at the same compositio;, where n(n — 1) intrinsic diffusion coefficients are defined. This technique has been employed for ternary diffusion studies by Dayananda and Grace" and Guy and Leroy.11 A different approach is recommended by Ziebold and Cooper,12 who have derived relations between interdiffusion coefficients and atomic mobilities employing fluxes referred to the local center of volume. Their analysis is based on the simplifying assumption of negligible interactions among intrinsic fluxes. This assumption has been considered satisfactory for dilute solutions.5"7 The use of this analysis for the calculation of mobilities requires an initial determination of interdiffusion coefficients with a set of diffusion couples having intersecting diffusion paths. It is the purpose of this paper to propose a method that would permit a direct determination of mobilities of all components of a multicomponent system from a single diffusion couple. This method is based on a mo- bility model developed with diffusion fluxes referred directly to the Kirkendall interface, generally identified by inert markers. gen erall, like that of Ziebold and Cooper,12 employs the simplifying assumption that the flux of each component relative to a fixed lattice is caused only by the driving force of its own chemical potential gradient. THE KIRKENDALL INTERFACE Inert markers are employed in diffusion couples to locate experimentally the position of the Kirkendall interface. They are initially placed at the weld interface for "sandwich" couples, or at the original vapor-solid interface for vapor-solid couples. Studies of marker motion in binary systems3'4 with both types of couples indicate that markers remain in a plane of constant composition and move with this plane para-bolically with time. Parabolic marker movements were also observed in ternary Cu-Zn-Mn couples by Dayananda and Grace.10 It is reasonable to expect a similar marker behavior even for diffusion couples with a higher number of components.

Jan 1, 1969

By W. K. Godfrey

The highest compressive strength cement has the highest bond strength in tests in which the cement is subjected to a confining pressure. After perforating, the bond strength is reduced to nearly zero when the pipe is supported by weak cement. Perforating does not affect the bond strength, however, when the pipe is supported by strong cement. Pipe supported by weak cement is damaged by perforating with expendable capsule jets, but is not damaged by perforating with the hollow carrier gun. High strength cements are recommended for oil wells that are to be perforated. Introduction The purpose of this work is to determine the effect of jet perforating on the bonding strength of oilwell cement at simulated down-hole conditions. Bond strength is a good criterion for determining the effectiveness of cement in performing its main function, i.e., that of isolating zones. According to the literature on the subject, the optimum cement strength for perforating is low and should not exceed 2,000 psi compressive strength. This conclusion was based on the appearance of bullet and jet perforations in neat and gel cements largely done in the absence of a confining pressure more than 15 years ago. Discussion Literature A relatively weak cement has been recommended in the literature as having optimum properties for perforating. In 1947, Oliphant and Farris tested bullet perforating of neat cements at various curing times.' Some of the tests were made at down-hole conditions. They reported that the optimum cement strength for perforating was about 2,000 psi compressive strength. Enlarged holes occurred when strength was too low, and the cement shattered and cracked when the strength was too high. In 1951, Morgan and Dumbauld tested bullet and jet perforating of neat and gel cements at surface conditions.' They reported that optimum cement has a compressive strength less than 2,000 psi. In their tests at atmospheric pressure, high strength cement shattered and cracked when perforated. Thus, the optimum cement strength was based on the appearance of neat and gel cement after perforating. In 1953, Clark showed a relation between cement strength and fluid shutoff.' He concluded that a 500 psi compressive strength is required for good fluid shutoff and that maximum bonding ability is developed at approximately 1,000 psi compressive strength. In 1964, Bell and Shore invalidated most of the conclu sions by the previous authors when they demonstrated that atmospheric pressure tests cannot be used to determine casing deformation and damage that will result from perforating under down-hole conditions.' They showed that the higher the hydrostatic pressure, the more restricted will be the expansion of gases generated by the charge. Less casing deformation and damage occurs under down-hole conditions than at atmospheric pressure. In recent work, Bearden et al. reported that jet perforating at surface pressure with the hollow carrier gun caused the cement sheath to shatter and crack.' The perforating, however, did not seriously affect the pressure required to leak past the casing cement bond. Only three cementing mixtures were tested, and presumably they had strengths in excess of 2.000 psi. Bearden et al. also reported that the hydraulic bonding strength increased as the compressive strength increased. Their hydraulic test showed that approximately 1,000 psi pressure is sufficient to break the casing cement bond for a well aged neat Portland cement sheath. Unfortunately, the tests were not run with a confining pressure, so Bearden et al. were merely measuring the strength of their outer 8%-in. casing. In our investigation, we measured the hydraulic bond strength of cement to pipe under a confining pressure and found that the bond strength was not limited to 1,000 psi. Cement Bond The bond strength is a good criterion for measuring the effectiveness of cement in performing its main function, that of preventing interzonal communication of fluids behind the casing. Measuring bond strength after perforating should be a good quantitative method of determining optimum cement properties, and should be a better method than that used by previous investigators,11 ' who simply observed the appearance of the cement after perforating.

Jan 1, 1969

By Roy T. Southin*

The finding of Wojciechowski and Chalmers that columnar crystal growth can be stopped by an already existing network of equiaxed crystals is supported by other recently reported work on both static and mechanically stirred ingots.27,28 Support for the dendrite arm fragmentation mechanism, too, can be obtained by comparing the effects of spinning on ingots cast in a material which has a dendritic solid/liquid interface during solidification with one which has a cellular interface, since no evidence of change at the interface, other than a change in growth direction, can be found in the cellular material. But there are alternative ways of producing an equiaxed zone in materials which characteristically solidify with a cellular interface. For example, interrupted spinning of a normally cast ingot can do it. In this case it has been shown28 that the equiaxed zone is caused by the showing of dendritic particles from the top surface of the ingot to nucleate a network of equiaxed crystals which forms a barrier to the continued growth of the columnar grains. This showering has also been shown to be a major effect in materials solidifying with dendritic interfaces. It has also been proposed28,29 that, for an equiaxed zone to form, not only must nuclei be present ahead of the interface but also these nuclei must grow to sufficient size to be a barrier to the further growth of the columnar grains. A further requirement is that a network of these grains continually be produced ahead of the growing interface; otherwise there is a reversion to columnar growth as found by Wojciechowski and Chalmers. In normally cast ingots it is possible for nuclei ahead of the interface to grow since during a large portion of the solidification time there is no temperature gradient ahead of the interface,30 and, in fact, the liquid may be slightly undercooled.29 This then is the major difference between the work under discussion and normal industrial solidification conditions, since Wojciechowski and Chalmers imposed a considerable temperature gradient in the liquid. The statement in the Wojcieshowski and Chalmers paper that one needs to lower the temperature gradient

Jan 1, 1969

By W. H. Herrnstein, F. H. Beck, M. G. Fontana

Sulfur solubility in a iron was measured in the 750 to 890°C temperature range and was found to be insensitive to ferrite purity within a limited composition range. The permeability of sulfur in ferrite was determined from the internal sulfidation of Fe-Mn alloys. From the solubility and permeability results, the diffusivity of sulfur in ferrite could be calculated. These results are summarized as follows: Dissolved sulfur decreased the lattice parameter of ferrite. The effect of dissolved sulfur on the tensile properties of ferrite at low temperatures was also determined. SINCE sulfur is an important residual impurity in commercial irons and steels, effects associated with the presence of sulfur as a solute in iron are of considerable practical interest. Unfortunately, certain basic information relative to the Fe-S system appears to be lacking in the literature, e.g., the effect of dissolved sulfur on the lattice parameter and mechanical properties of ferrite. In addition, discrepancies exist in previously reported results for the solubility of sulfur in ferrite. These discrepancies raise questions regarding the sensitivity of sulfur solubility to the purity and microstructure of iron. This study was undertaken primarily in an effort to obtain reliable data on the solubility of sulfur in ferrite. Additional objectives included determination of the permeability and diffusivity of sulfur in ferrite by the internal sulfidation method and determination of the effect of dissolved sulfur on the lattice parameter and tensile properties of ferrite. EXPERIMENTAL METHOD Three grades of iron, encompassing a range of impurity levels, were employed in the study. The grades were designated VME (vacuum-melted electrolytic), SPZR (single-pass zone-refined), and MPZR (multipass zone-refined). The composition of each grade is given in Table I. Poly crystalline and single-crystal strip specimens were employed in the solubility experiments. Uniform grain size strip (ASTM 3 to 5) of 0.005 to 0.020 in. thickness was obtained by alternate cold reductions of 60 thickness 60 to 80 pct and recrystallization at 650°C for i hr in pure, dry argon. Single-crystal specimens were produced in 0.010-in.-thick SPZR iron strip by the strain-gradient anneal technique. Recrystallized strip 0.25 in. wide was strained until a Luders band or bands had propagated over the length of the strip; the strip was then annealed by drawing it through a 150°C per in. gradient (890°C peak temperature) at 1 in. per hr in an atmosphere of pure, dry argon. Laue photographs of the crystals produced exhibited no discernible asterism. Specimens were equilibrated with H-H, atmospheres at temperatures between 750" and 890" by one of two methods, each of which makes use of the reaction: The encapsulation sulfurization method was employed in the majority of the solubility experiments. A strip

Jan 1, 1969

By M. R. TECK, N. Rudd, L. K. Thomas, D. L. Katz

The authors are to be congratulated for presenting the first comprehensive paper on the theory and practice of threshold pressure determination in connection with underground gas storage. It is of particular value since most previous experimental work on this subject has been proprietary to the commercial laboratories engaged in such testing and to their clients. This dlscussion is presented in amplification of the subject paper, not in criticism, and is based upon our experience with approximately 5,000 threshold pressure determinations. Our comments are directed primarily to the experimental procedures as described by Thomas et al. It should be noted that, while clay mineral-rich lithologies are the most common caprock materials, the samples used (Table 1) include low permeability sandstones and carbonates, but do not include shales or other formations in which clav minerals exert a dominant effect. While our experience on samples analogous to those investigated by the authors generally confirms their findings, we have found that even more rigorous experimental conditions must be imposed where clay minerals are the controlling factor. These additional conditions result from the well-known molecular character of the clay minerals themselves in which water is interlaminated with, and bonded to, silicate sheets, thus becoming an essential component of the molecule. In many clay minerals the character of the intersheet bonding, and thus the dimension of the lattice, is strongly affected by variations in the identity and concentration of cations present in the intersilicate water. On a supermolecular scale, adsorbed water films on particle or "flakes" of shale provide much of the cohesive force necessary to maintain mechanical strength. The thickness of these films is variable and inversely proportional to intergranular pressure within the dimensional limits involved in caprock investigation. The thickness of the intersilicate water layers may also be subject to pressure under some conditions. These considerations are reflected in several necessary modifications of the experimental procedures described by the authors. Two of these are, in our judgment and experience, of such importance that they cast real doubt on the validity of data obtained on argillaceous materials without their application. The very careful resaturation procedures proposed by the authors should give good results in connection with the relatively "inert" lithologies used in their experiments. Our experience suggests, however, that they would create more problems than they would eliminate if applied to argillaceous materials. 1. Drying of the sample at the temperature and for the duration indicated by the authors not only will dessicate the sample with consequent shrinkage cracking, parting along bedding planes, and even total disassociation in the case of fissile shales, but it may also alter the character of the clay minerals themselves — in some cases irreversibly. 2. Prolonged evacuation to 2 microns Hg further dessicates the sample and is even more effective in reducing the intersilicate water content. 3. Resaturation with water differing in pH or chemical content from that existing originally in the sample also serves to alter the nature of the sample, particularly its structure and strength. 4. Our experience has been that, even with the thorough precautions proposed by the authors, complete resaturation of very fine grained materials is rarely obtained. Yet our experience confirms the

Jan 1, 1969

By Douglas A. Elkins

The unique characteristics of plasmas, their current applications, and ongoing research into new applications are described. Major technical and economic problems in application of plasma technology are discussed. Examples of potential applications of plasma in extractive metallurgy are described and evaluated. The report includes a selected bibliography of articles on plasma and related high-temperature technology.

Jan 1, 1969

By E. J. Hammer

In the crushing and grinding of metallics for beneficiation, the sizing is normally done to liberate the metals or sulphides for further processing to improve recoveries of the basic metals or minerals. The objective is to reduce the ore in size through various closely controlled stages to that degree of fineness which gives an economic liberation of valuable mineral, but which avoids as much as possible the production of sliming fractions. A different philosophy applies to the crushing and grinding of Gypsum. Our requirements normally demand controlled grinding and/or crushing of the material not only to a fineness suitable for further processing of the mineral into end products, but to produce various sizes of material which are them- selves saleable products. The majority of our tonnage ultimately ends up in stucco for Wallboard. Therefore, our mineral reduction is normally designed toward this end, but it is done in a manner that permits drawing off inter- mediate products to meet various Customer requirements. This forces us into compromises at times in our equipment installations, and our equipment must sometimes be more versatile and complex than we would like it to be. We try to process our basic rock, Gypsum, for the most efficient size reduction. We market 5 to 6 different sizes intermediate to the end product, which generally is the fineness of material to be used for stucco for Wallboard, and we do this with controlled crushing, grinding and sizing cycles of the material. To summarize, we use a different philosophy of crushing and grinding than the metallic field which uses comminution or crushing and grinding to improve recovery, whereas we choose our equipment to crush and grind primarily for product performance.

Jan 1, 1969

By M. H. Richman, W. D. Sproul

THE indexing of a field-ion micrograph is in many cases similar to the indexing of the poles of a stereo-graphic projection.* If one has a standard projection as a guide, the task of indexing is relatively simple. In this way, field-ion micrographs of bcc and fcc wires have been oriented from projections available in most any text on X-ray diffraction. These books always illustrate the projections for the bcc and fcc structures and even for a particular hcp structure. There is no "standard" hcp projection because the angles between planes depend on the c/o ratio of the unit cell. In order to index field-ion micrographs of hcp metals, one must compute the angles between various planes—a rather laborious task. In recent work,, we have had to identify the structure and index the orientation of field-ion micrographs of the compounds WC and W,C. To overcome the problem of computing angles by hand or calculator, a program was written in Fortran lV for use on the IBM 360, Model 50 which will compute all angles between planeswith indices (hlklll) and (17,k,l2) in the range from (447) to (444) for any given c/o ratio. The program, which is more specific than that of Camp and clum, was so written as to take advantage of the multiplicity of the hexagonal system, and, for the limits defined above, only 26,649 values out of a possible 265,721 values had to be computed. This is a 90 pct saving in time (and cost) and was accomplished in the following way. Because the lattice parameters of the hexagonal crystal system are defined such that: a = b * c [1] the I index does not enter into the multiplicity (i.e., it cannot be transposed with the h or k indices), and all possible values of h and I, from 4 to 4 must be used—a total of eighty-one combinations. The index h2 varies the most—it must assume values from - Ill,: to 3Ihl. The indices kl and k2 are always equal and vary

Jan 1, 1969

By Floyd G. Anderson

This report reviews and summarizes information on prevention and suppression of dust in mining, tunneling, and quarrying published in the United States from 1961 through 1967. Unpublished pertinent data developed or assembled by the Bureau of Mines during this period also are included.

Jan 1, 1969

By W. A. Oates, J. S. Blakemore, E. O. Hall

AS part of an investigation into the effect of hydrogen on the serrated yielding of Ni-Cu alloys,' it was necessary to determine the solubility of hydrogen in the alloys of interest. With the exception of the work by Fukusima and Mitui2 who investigated the solubility of hydrogen in solid Ni-Cu alloys at 20 wt pct intervals at 1050°, 700°, and 350°C, the information in the literature is limited.3-10 Alloys were prepared from deoxidized Analar Copper and Mond Nickel pellets.' Wire samples were hydrogenated at 7.8 atm in an autoclave consisting of 5 ft of thick-walled Inconel 600 tube with a resistance furnace around the middle portion. The top end, at room temperature, was fitted with a safety valve, a calibrated pressure gage, and a sample inlet, while the bottom end, again at room temperature, was filled with water. After reaching equilibrium samples were quenched by dropping from the high-temperature region of the autoclave into water. They were then quickly transferred to liquid nitrogen where they were stored until analyzed for hydrogen using an Exhalograph.11 The results, which are shown in Fig. 1, represent the mean of two separate determinations on each sample. Because of the lower level of hydrogen at the high copper end of the series, the results here are of poor precision using this method. Fortunately, the results of Himmler9 using the Sieverts technique are available for these copper-rich alloys (>80 at. pct Cu)

Jan 1, 1969

By C. J. Rosa, W. C. Hagel

An attempt is made to determine the diffusion coefficients of oxygen ions in hypostoichiometric zirconium oxide. A phenomenological theory is developed for three-phase, unidirectional volume diffusion of a gaseous species from a planar source. Knowledge about oxygen diffusion in a and ß zirconium and experimentally measured rates of movements of interfaces permit the evaluation of oxygen ion diffusivi-ties in ZrO2-x. The results conform to the relationship: sq cm per sec, for the temperature range of 875" to 1050° C. DIFFUSION coefficients of oxygen ions in stoichio-metric oxides have been studied by many investigators. The obtained results not only supplement the knowledge about the lattice-defect structures of oxides and conduction mechanisms but also provide information of technological importance. Rate processes such as oxide sintering, high-temperature creep deformation, and oxidation of metals and their alloys are directly dependent on diffusion phenomena. Unfortunately, diffusion coefficients obtained from studies on stoichio-metric oxides cannot be treated without restraints when applied to oxidation kinetics, if precise evaluations of oxidation rates are desired. Oxides formed on metals are usually nonstoichiometric and exhibit nonuniform distribution of either cation or anion vacancies across their thicknesses. Debuigne and Lehr1 extended Danckwerts'2 mathematical analyses and furnished a semitheoretical treatment for evaluating oxygen diffusion coefficients in zirconium oxide in terms of weight gain measurements during oxidation of zirconium in the temperature range 400° to 850°C. Their calculations are based on theoretical partitioning3 of the total amount of oxygen between a zirconium and its oxide phase. An inherent discrepancy appears to continue throughout their calculations. The amount of oxygen confined to the oxide phase should be corrected by multiplying the calculated oxide thickness by the inverse of Pilling-Bedworth ratio, if expansion of zirconium dioxide is taken into account. The purpose of the present investigation is to provide a new semitheoretical treatment for evaluating diffusion coefficients of moving species in hypostoichiometric oxide. The analyses are relevant to unidirectional volume diffusion. Although the presented method is quite general, its applicability will be discussed in terms of kinetic measurements from oxidation of zirconium at temperatures above the a/ß transition, for reasons stated in the later part of this paper. EXPERIMENTAL Pure, 99.93 wt pct, zirconium samples of approximately 2 by 1 by 0.35 cm were exposed to oxygen for various times at four temperature levels: 875°, 950°, 1000°, and 1050°C. High-purity, better than 99.9 vol pct oxygen was passed through a cold trap and columns containing anhydrous CaSO4 to remove residual water vapor. Before exposing to oxygen at a pressure of 500 Torr, specimens were subjected to wet abrasion on 200- through 600-grit Sic papers and polished with 1—p diamond dust. Prior to oxidizing, all zirconium samples were vacuum-annealed at 10-6 mm Hg for about 15 min at the test temperature. The temperature variation across the uniform heat zone was ±2°C from the preset value. Final polishing, for phase thicknesses measurements, was performed by using 8- and 1-p diamond dust and followed by vibrator polishing with 0.05-µ ? Al2O3 solution. Measurements of phase thicknesses were made by projection on a metallographic viewing screen. Conventional powder X-ray analyses for the oxide were employed. RESULTS Fig. 1 is an example of the cross section of oxidized zirconium. Designations of phases given below this figure are the same as those used in the three-phase diffusion system represented by Fig. 5 in the following section. Zirconium oxidized for longer exposure times showed two types of oxides: white oxide at the surface and an underlaying layer of gray oxide. X-ray powder patterns of these oxides at room tern-

Jan 1, 1969

By D. A. Rice, M. C. Fuerstenau

Flotation data indicate that sulfonate and amine adsorb physically on manganese oxide; oleate also adsorbs physically if the zero point of charge is sufficiently high. Chemisorption of oleate occurs on pyrolusite between pH 8 and 9, and possible mechan- isms of collector adsorption involving metal ion hydrolysis are discussed. The flotation characteristics of most metal oxides1-15 have been examined with standard collectors such as fatty acids and sulfonates. From these studies it would appear as though electrical phenomena are important when shorte r-chained collectors are involved. For example, Iwasaki, Cooke, and Choi9 have shown that dodecyl amine and dodecyl sulfate float iron oxide above and below the zero point of charge, respectively. In another system, D.W. Fuerstenau and Modi10 have shown that dodecyl sulfate, dodecyl

Jan 1, 1969

By H. I. Aaronson, C. Laird

The kinetics of thickening and of lengthening of ?' plates in an Al-3.93 pct Cu alloy in the temperature range 203" to 300" C were determined by means of transmission electron microscopy. The rate of thickening was found to be less than that allowed by volume diffusion control at all temperatures, by amounts which increased with decreasing temperature, in agreement with the predictions of a general theory of precipitate morphology.1 Thickening was treated on the basis of the ledge mechanism. Ledges were deduced to spread across the broad faces of ?' plates at volume dzjrfusion-controlled rates, as anticipated from the disordered structure of their edges. Lengthening of 8' plates, on the other hand, took Place more rapidly than allowed by volume dzjrfusion. This occurred despite clear morPhological evidence of a bmrier to growth at the edges of these plates. It was concluded that the misfit dislocation structure comprising the barrier requires that lengthening take place by a jog mechanism. The tnisfit dislocations, however, also serve as diffusion short circuits, and allow high overall lengthening rates to be achieved. In Part I' it was shown that, within the range of aging temperatures and times studied, the broad faces of 8' plates formed in Al-4 pct Cu are fully coherent with the a, matrix. Virtually .all of the dislocations present in these faces were found to have developed as a result of plastic deformation in the a phase. Such dislocations are thus "intruders", rather than the more usual misfit-compensating variety. The edges of 8' plates were confirmed, by extension of the earlier studies of Mat-suura and Koda,3 to be made up of edge-type misfit dislocations, in sessile orientation with respect to lengthening of the plates. These interfacial structures should cause 8' plates to thicken and to lengthen at rates less than those allowed under the condition of volume diffusion control, such as would be expected if the interphase boundaries had disordered structures.' The narrow width of 8' plates, the reproducible crystallography of their broad faces, and the appearance of these plates in cross section as octagons rather than as circular discs2 provide qualitative support for these deductions. The present study of the rate of thickening and the rate of lengthening of 8' plates was undertaken in order to examine them on a quantitative basis. I) THICKENING KINETICS OF THE BROAD FACES OF?' PLATES A) Literature Review. The measurements now available on the thickening kinetics of single-phase precipitate plates consist of one plot of the thickening of a proeutectoid ferrite plate in an Fe-C alloy,' showing (as predicted) thickening rates less than those allowed by volume diffusion control. B) Experimental Procedure. Details of the preparation of the 4-3.93 pct Cu alloy used in this study have been previously reported.4 As in Part 1,' transmission electron microscopy was the observational tool employed. A general description of the apparatus and procedures of the electron microscopy studies is given in Section I of Part I. In thin foils, 0' plates tend to form at and parallel to the foil surface.' A direct investigation of the thickening process by means of hot-stage transmission electron microscopy was therefore not feasible. It was thus necessary to use the conventional method of aging individual bulk specimens for a wide range of different times at the various temperatures studied. In each specimen, the thicknesses of a number of plates were measured. Since thin foils prepared from "bulk-aged" material contain a large proportion of grains with orientations near (001) , it was relatively easy to find, near the edges of the foils, the characteristic multifold patterns of intersecting extinction contours which indicate regions where the foil is exactly at an (001) orientation. The thicknesses of large numbers of plates were measured along the (200) branches of the "stars" so that the 8' plates were precisely parallel to the optical axis of the microscope. Wherever possible, intersecting extinction contours were adjusted with the parameter s > 0 to improve the visibility of the plates in bright-field illumination. These precautions, in combination with taking the measurements at the thinnest parts of the foils, minimized the errors in the measurement of the thickness of the plates resulting from inexact parallelism to the electron beam. Since the plates were very thin, it was not easy to measure their thickness on the photographs. The techniques of enlargement and of microdensitometry were employed to minimize errors from this part of the measurement. A further source of possible error, that the plates can appear thicker because of contrast associated with mismatch normal to the plane of the plate, was also considered. The images of the plates were usually thinner than those of dislocations, however, and no anomalous changes in apparent plate thickness were observed when regions of foil containing plates were tilted through various diffracting conditions. Any error from this cause must therefore be small. Other sources contributing errors were: a) the microdensitometer traces per se and the subjective estimates of their peak limits, and b) slight fluctuations in magnification associated with small changes in the current of the objective lens of the electron microscope. The overall error probably amounted to no more than 5 to 10 pct. In order to obtain readily interpretable data on thickening kinetics, it is essential that the diffusion fields of adjacent ?' plates not be allowed to overlap. Calculations'-' showed that this condition is definitely not ful-

Jan 1, 1969

By F. A. Veer, W. G. Burgers, B. H. Kolster

Starting-- from Cu-Si diffusion couples a study of diffusion in the intermetallic compound Cu3Si of the Cu-Si system has been made. Mmker experiments showed copper to be the diffusing element. From the rate of growth of the Cu3Si phase diffusion coefficients were derived. The activation energy for diffusion is 18.6 kcal per mole. The couples show some interesting microscopic features, for which a tentative explanation is given. THE synthesis of dimethyldichlorosilane, (CH3)2SiC12, an important compound in the manufacture of methyl-silicones, takes place at the surface of a thin Cu3Si layer deposited on a mass of silicon particles."' By passing CH3C1 vapor at about 350°C, silicon atoms are consumed from Cu3Si in forming the volatile silane molecules, thus leaving copper atoms at the surface. It is well-known that copper acts as a poison for the above-mentioned reaction by catalyzing the dissociation of methylchloride.' However, no poisonous effect is observed, at least not before most of the silicon from the particles is converted into silane.3 This would be understandable, if either the copper atoms diffuse through the Cu3Si deposit to the underlying silicon or silicon atoms diffuse in the reverse direction to the copper, both processes resulting in the formation of new Cu3Si and so ensuring the proceeding of the reaction. In this paper experiments are described, demonstrating copper to be the diffusing element. Also a very low activation energy for the diffusion is observed. EXPERIMENTAL The silicon used contained 1 ppm Mg and 1 ppm Cu; the copper was spectroscopically pure (Fe: 2 ppm; Ag, Mg, Si: 1 ppm). The copper and silicon samples were prepared in the form of blocks of approximately 10 by 10 by 5 mm with two parallel sides by spark-machining. The blocks were ground on emery paper (grit 600), etched (copper with nitric acid, silicon with a 4:l nitric acid:hydrofluoric acid mixture), and cleaned with alcohol. As the brittleness of the silicon did not allow a welding procedure to prepare the diffusion couples, the copper and silicon blocks were pressed together in a steel clamp. The pressure exerted by the clamp brought about contact between the parts of the couple and so ensured proceeding of the diffusion. The couples were heated in a vacuum furnace (about 10"5 Torr). The temperature was stabilized within 1 pct. After a heat treatment a section parallel to the direction of diffusion was examined in the microscope and in the X-ray scanning microanalyzer. To determine whether copper or silicon is the diffusing element marker experiments were carried out using tungsten wires with a 20-p diam. EXPERIMENTAL RESULTS Figs. 1, 2, 3, and 4 give micrographs of diffusion zones of Cu/Si couples. Analysis by the electron mi-croprobe of the Cu/Si samples after a definite heat treatment revealed the existence of only one intermetallic phase as can be seen from the line scan shown in Fig. 5. From the X-ray diffraction pattern it could be deduced that this phase was CU 3 Si.4 Even when diffusion zones of considerable width (up to 600 p) were obtained, no other phases occurring in the Cu-Si system could be detected, neither by the electron microprobe nor by X-ray diffraction analysis. The optical anisotropy of the Cu3Si phase made it possible to observe the columnar shape of the crystal-

Jan 1, 1969

The specification for tender nominated the requirements for ore hoisting and servicing; this showed that one common duty winder could be selected. Foliowing the design of the shaft layout, the merits of fixed or rope guides were compared and the latter selected.The specification called for the supply and installation of the complete hoisting system. Construction of the winder tower and shaft bottom steel work had to proceed while mine development was in progress using the sinking winder and headframe. Guide ropes, winder ropes, and the sky shaft were installed in the shortest possible time, and as the shaft was not equipped with ladder-ways, a second means of access had to be provided.Very few problems were encountered witll the commissioning of the winder, and in the first 2 years of operation the only significant modification was to the circuitry associated witll the moving access platforms.Hoist rope tension checking and adjustment are simple, and non-destructive testing has shown no deterioration of these ropes. The operation of the balance ropes has been very satisfactory but cleaning presented problems in the early stages. Guide ropes have been trouble free and require minimum attention.Normal wear on the PVC rope groove inserts on the winder drum has been negligible.Since the commissioning on fully automatic ·control, the winder has operated with very few, minor delays.

Jan 1, 1969

By E. P. Pfleider, W. G. Pariseau

This paper reports the theoretical and experimental results of an analysis of ore pass drawdown as a problem in soil plasticity. The method of analysis developed appears to be a promising technique of investigating the mechanics of fragmented materials. A reconstructed plasticity theory brings experiment and theory into reasonable agreement, and hence may provide the foundation needed for rational ore pass design. The gravity-induced movement of broken rock through ore passes is an economical method of transporting fragmented materials through large vertical distances in underground mines, provided the ore pass is well designed. Unfortunately, the design procedures now followed do not very often result in ore passes that function properly. On the one hand, the huge accumulation of empirical data pertaining to the movement of materials in gravel bunkers, storage bins, deep grain silos and other structures that have features in common with ore passes remains uncorrelated. On the other hand, there is a dearth of experimental data substantiating theoretical models of material behavior. Consequently, reliable generalizations encompassing the broad spectrum of problems involved have not been forthcoming. AS an initial step towards improving the situation, a detailed case study of two-dimensional ore pass drawdown was made. The mechanics of the process were analyzed theoretically as a problem in soil plasticity and tested experimentally through observations of a laboratory ore pass model. THEORY Taylor1 defines a soil as a "mass commonly considered to consist of a network or skeleton of solid particles, enclosing voids of varying size." Broken rock in an ore pass is such a material. In plasticity theory this material is replaced by an idealized substance that deforms elastically up to some state of stress at which slip or yield occurs,2 For com-pressive states of stress, the Mohr-Coulomb criterion is a satisfactory yield condition. After the yield point is reached, the ideal soil deforms in accordance with the concept of plastic potential.4 Under plane strain conditions the governing equations separate into a system of stress equations and a system of velocity equations.' Only stress variables appear in the stress system. The velocity system, however, contains a stress variable. The two systems are, therefore, coupled. Both systems are hyperbolic, and each has two real, distinct families of characteristic curves that coincide according to the classical theory of ideal soil plasticity. The

Jan 1, 1969

The Fraser Range is composed dominantly of basic pyroxene granulites derived from basalts, many of which appear to have been vesicular and pillowed. Acidic and basic garnet-bearing granulites are important in the west, and acidic granulites and narrow anorthosite layers are dominant in some regions east of the Fraser Range. An extensive flat-lying olivine gabbro sheet cuts the granulites, and in places has been converted to spineI-bearingmeta-gabbros and pyroxene granulites. The granulites of the Fraser Range (Proterozoic) are separated from the gneisses and schists of the goldfields regions (Archaean) by the Fraser Fault, over which there is a large gravity anomaly (gradient 20 milligals per mile). Some of the problems associated with the concentration of Cu, and Ni liberated from mineral lattices during metamorphism, and other principles of metal concentration in granulite terranes, are discussed. The recognition of vesicular and pillowed zones, even though highly metamorphosed, is of fundamental importance.

Jan 1, 1969

By A. Coskun, J. F. Elliott

The activity of aluminum in liquid Al-Fe alloys .has been measured by an improved version of the transportation method in which the metallic vapor has been collected by its solution in a metallic condenser. The results can be represented by the equation: log yAl = -3.0(1 - xAl2) (0.6 < XAl < 1.0) This equation applies at 1315°C. MORRIS and zellarsl adapted the transportation method for measuring the vapor pressure of a com- ponent of an alloy at high temperature. We have modified their technique further2 for use with metals that are strong oxide formers. In the present case the method has been applied to the Al- Fe system to obtain the activity of aluminum in the liquid region at 1315°C. Dried ultrahigh-purity hydrogen (Matheson) is the carrier gas. The operations, Fig. 1, of deoxidizing the gas, equilibrating the gas with the sample at 1315";, and then collecting the aluminum vapor are all accomplished within a single, continuous alumina tube to avoid contamination of the system by leaks. De-oxidation to a very low level of PO2 (<10-25 atm) is Obtained by passing the hydrogen through a tightly packed bed of aluminum powder. The temperature of this bed increases to approximately 550°C in the direction of the gas flow. The boat containing three pellets of the alloy is supported on the end of a

Jan 1, 1969

By Juan Sodi, John F. Elliott

The standard free energy of ReS2 has been measured in the range of 1050° to 1250°K using H2/H2S mixtures and a slight variation of the method described by Hager and Elliott.1 The result is: The experimental method and apparatus were modified slightly for this study. Measurements on Cu2S were made to verify the application of the method to the work on ReS2. THE EXPERIMENTS AND RESULTS Briefly, the experimental method consisted of exposing a chip of copper or rhenium at a known temperature for 8 hr to a slowly flowing gas stream at the same temperature in which Ph2S and PH2 were known. The chip was withdrawn quickly from the hot furnace, and subsequently it was inspected for the presence of a sulfided surface. In the experiments described here, there was no ambiguity in any case as to the presence or the absence of the sulfide. At a given temperature, gas compositions for sulfidization were explored systematically until two compositions were found whose values of ?G°, Eqs. [I] and [2], were within approximately 100 cal of each other, one of which was sulfi-dizing and the other was not. These are termed the "straddle" compositions and it is assumed that the equilibrium composition lies between them. The chief modification to the apparatus, which is shown schematically in Fig. 1 of Ref. 1, was to support the metal specimen on a small alumina boat which could be moved along the reaction tube, 6 mm ID, by platinum wires. An appropriate seal at each end of the reaction tube permitted the sample to be moved from the cold end of the tube into the hot zone in 2 to 3 sec, and the sample could be withdrawn equally rapidly. Thus, it was possible essentially to quench the specimen from the reaction temperature with the reaction gas or helium flowing and without danger of breaking the reaction tube. The usual practice at the end of the experiment was to switch the gas system to the helium tank, flood the reaction chamber with helium, and pull the sample out of the hot zone. The purpose of the modification was to permit study of the sulfidization of copper without the complication of the back-reaction between the gas and the specimen as the latter cooled during slow withdrawal of it from the hot zone; this was a problem in the earlier work.&apos; A further improvement located the tip of the temperature-indieating thermocouple and the specimen precisely at the hottest part of the furnace. A carefully calibrated thermocouple, with its tip at the position of the specimen and with other conditions duplicating those of an actual experiment, showed that in the temperature range of 900° to 1122°C the temperature of the specimen differed from that of the tip of the indicating thermocouple by less than 0.5°C. The two positions were 0.5 cm apart. The reaction gas was prepared from ultrahigh-purity hydrogen (<l ppm O2, <0.5 ppm H2O) and CP grade hydrogen sulfide (99.5 pct H2S). High-purity helium (99.995 pct He) was used. All of these gases were purchased from the Matheson Co. All flow meters were recalibrated by the soap-bubble method with hydrogen, H2S, helium, and several gas compositions used during the study. These calibrations gave a linear relationship with a slope of 1.0 for the plot of log flow rate vs log pressure drop across the flow meter, in accordance with the Hagen-Poiseuille equation. The analysis of the gas was determined in the same manner as was reported previously. Good checks were obtained between the composition of the gas established by the flow-meter settings and by chemical analysis of the gas taken after the mixing bulb and ahead of the furnace. The pressures of H2S, H2, S2, and HS in the equilibrium gas at temperature were calculated from the following data :3 The pressures of the species S and S8 were negligible for the conditions of the experiments.3 There was no sign of vaporization of ReS2 either by weight loss or deposits in the reaction tube. Thus it is not possible to account for the apparent volatility of the compound reported by Juza and Biltz.2 The inlet gas composition and the calculated equilibrium ratio of PH2 S/PH2 for the "straddle" points of each experiment are shown in Table I. The specimens of metal for the experiment were small clippings of annealed copper (99.9+ pct) sheet 0.005 in. thick that was obtained from Baker and Adamson and of "high-purity" rhenium (99.9+ pct) sheet 0.005 in. thick that was purchased from Chase Brass and Copper Co. A specimen was removed from the apparatus; inspected for the presence of the sulfide, and then stored in a sealed vial. A fresh clipping was used in each measurement. The condition of the surface of each specimen after the experiment is noted in Table I.

Jan 1, 1969