Search Documents

By Che-Yu Li, J. L. Gregg, W. F. Brehm

Oriented, oxygen-doped niobium bicrystals were tested in liquid lithium. The grain boundaries were attacked preferentially. The depth of the penetrated zone varies as (time)2. The penetration was aniso-tropic, had a high activation energy, and increased with the increased oxygen doping level. A possible model was proposed to account for the experimental observations. 1 HE grain boundary penetration of a metallic system by liquid metal has been studied by several investigators. Their results are summarized by Bishop.' Most of these works show that the penetration by liquid metal corresponds to the phenomenon of liquid metal wetting. In the case of a grain boundary, wetting will occur when twice the solid-liquid interfacial tension is smaller than the grain boundary tension resulting in the replacement of the grain boundary by two new solid-liquid interfaces. Other possibilities exist; for example, the atoms of the liquid metal may diffuse into the grain boundary region due to chemical potential gradient. The gradient can be produced by impurity segregation or simply be due to the increase in solubility in the grain boundary region. The penetrated grain boundary in these cases may remain solid at the test temperature. The Nb-Li system has been of considerable interest because of its possible technological applications. For fundamental interest it provides a possibility of studying the grain boundary penetration process which is not controlled by the wetting mechanism. The pure niobium is not attacked by the liquid lithium, but if niobium containing more than 300 to 500 ppm oxygen by weight is exposed to liquid lithium, corrosion occurs at the solid-liquid interface and preferentially at grain boundaries. Previous investigators2-' have proposed that this preferential corrosion at grain boundaries is caused by oxygen segregation there, with subsequent inward diffusion of lithium to form a Li-Nb-0 compound. These investigators also found that the corrosion could be retarded by adding 1 pct Zr to the niobium to precipitate the oxygen as ZrO2 upon proper heat treatment. However, there are no quantitative data on the kinetics of the grain boundary penetration process to test the validity of the proposed corrosion mechanism. In this work an investigation of this penetration process in oriented bicrystals was made as a function of the oxygen doping level in the bulk niobium and the grain boundary orientation. A possible model for the penetration process based on the experimental results was proposed. EXPERIMENTS Oriented niobium bicrystals were grown by arc-zone melting oriented single-crystal seeds.7 These bicrystals contained simple tilt boundary. The [001] directions in the two grains were tilted about a common [110]. The bicrystals were 31/2 in. long and 5 by 4 in. in cross section with the straight, symmetric, planar grain boundary longitudinally bisecting the crystal rod. The bicrystals were doped with oxygen by anodically depositing a layer of Nb2O on the surface in a 70 pct HNO solution at 100 v, using a stainless-steel cathode. The specimens were homogenized by annealing in evacuated quartz tubes at 127 5°C. Oxygen content of the niobium was measured from microhardness values, after DiStefano and Litmman.' Supplementary checks were made with vacuum-fusion analysis.7 Individual test specimens cut from the doped bi-crystal rods, about by by % in. in size, were tested inside double jacket sealed capsules. The inner jacket was niobium, the outer was stainless steel. The niobium inner jacket eliminated the problem of dissimilar-metal mass transfer.' The lithium (99.8 pct pure, obtained from Lithium Corp. of America) was handled only in a purified argon atmosphere in a Blickman stainless-steel glove box. After introduction of lithium, the capsules were sealed by welding. Further detailed experimental procedures are given in Ref. 7. The capsules were heat-treated in vertical Marshall resistance furnaces. Temperatures were controlled to When heating above 1100°C, it was necessary to seal the furnace work tube and flow argon through to prevent failure of the stainless-steel outer jacket of the capsule. Tests were made on 6" 2", 16" 2, and 33" i2" bicrystals at oxygen levels up to 2600 ppm by weight in the 6' and 16" crystals and with 1300 ppm oxygen in the 33' crystals. The oxygen levels were controlled to 100 ppm. Most of the quantitative data were obtained from 16" bicrystals between 800" and 1050°C. The capsules were quenched into water after the test and cut open with a water-cooled abrasive wheel. The capsules were then submerged in water, which dissolved the lithium and freed the specimen. Measurement of the depth of the penetrated zone in the grain boundary was done either on metallographically prepared surfaces or directly on the grain boundary plane after the specimen was fractured in tension in the grain boundary plane. The depth of penetration measured by both methods agreed well. Further details describing these techniques have been reported elsewhere.'p7

Jan 1, 1969

By F. R. Cattoir

This Bureau of Mines study investigated molten salt electrorefining for beneficiating low-grade, high-carbon ferrochromium products which can be readily produced from domestic chromite concentrates. A second objective was to refine commercial ferrochromium into low-iron chromium products. Electrorefining of both types of ferrochromium in molten CaC12-NaCl-CrC12, CaCl2-MgC12-CrCl2, or KC1-LiCl-CrCl2 electrolytes produced chromium-iron products with virtual elimination of other impurity elements and some lowering of the iron content, Over 90 percent of the chromium present in the feed materials was recovered. The electrodeposited products were upgraded further by magnetic separation techniques into chromium containing less than 5 percent iron. The technical feasibility of preparing a premium chromium product from a low-grade, high-carbon ferrochromium made from domestic chromite was demonstrated. Chromium virtually free of carbon, oxygen, and silicon from high-carbon ferrochromiums was produced. In addition, the amenability of three commercial grades of ferrochromium to electrorefining and magnetic separation for preparing chromium metal containing less than 5 percent iron was determined.

Jan 1, 1969

By Charles J. McMahon

In a recent paper, Floreen and Hayden report that additions of the noble metals iridium, rhodium, ruthenium, and platinum to Fe-C alloys containing 0.03 to 0.08 wt pct C act to significantly reduce the ductile-to-brittle transition temperature in a notched-bar impact test. They compare these results with the similar, well-known effects of nickel and manganese additions, and they note that this supports the hypothesis that addition of austenite stabilizers enhances notch toughness. Although not attempting to offer an explanation for this, they suggest that it might be found in an alteration of the bonding characteristics of the bcc lattice of iron by additions of elements which tend to stabilize the fcc lattice. While this suggestion appears to have some merit, it should perhaps be held in abeyance until two more likely possibilities have been explored. It is now fairly clear that the beneficial effect of manganese derives from its ability to promote a globular carbide morphology instead of the platelike form found in grain boundaries and pearlite patches in Fe-C al10~s.' Previous work14 has also shown that cleavage fracture in Fe-C alloys of the type tested by Floreen and Hayden originates almost exclusively in the cracking of cementite platelets, and that the ductile-brittle transition temperature is very sensitive to the volume density and size of these carbides. Treatments which lead to development of nonlamellar carbides or fine dispersions of carbides, such as quenching and tempering or appropriate alloy additions, promote toughness by removing the primary mode of cleavage initiation. The effectiveness of manganese in this regard has long been known. Nickel appears to behave in a similar manner, though the effect is perhaps not as dramatic as with manganese.15 However, nickel additions do lead to a definite refinement of ferrite grain size following a given transformation heat treatment, and this in itself acts to greatly enhance notch toughness.'' (The grain sizes of the various heats tested by Floreen and Hayden were not reported, so it is not known how much influence this factor exerted in their results.) In conclusion, it is suggested that one should consider the well-established effects of alloying elements on carbide morphology and ferrite grain size before resorting to more complex possibilities, such as modification of interatomic bonding.

Jan 1, 1969

By Henri V. Reibell

Deep open pit optimization supposes very long and sedious calculations in order to assign the best shape of the pit and the best bottom level, which will give the biggest profit. Computers give the possibility to make these calculations. More over, they allow to multiply trial calculations so that it is possible to obtain more reliable results. The paper does not expose the computer program but only the way in which mining engineers can use it.

Jan 1, 1969

By Arcy R., D&apos George

The Bureau of Mines has developed, on a laboratory scale, a superior Eluex-type circuit for eluting and recovering uranium from ion exchange resins. The improved circuit differs from conventional Eluex practice in that a stage of uranium solvent extraction is coupled with each stage of resin elution rather than the elution and solvent extraction operations being conducted separately. The new system reduces the number of stages, retention time, and resin inventory in the elution circuit to one-fourth or one-fifth that in existing circuits. The system is applicable to both resin-in-pulp and moving-bed-type ion exchange uranium recovery circuits.

Jan 1, 1969

By Hermann J. A

Over the last few years enormous dapooits of high-grade bauxite have been discovered in Australia, ;_ d an alum .nium smelting industry based on them is rapidly being developed,, This industry requires large amounts of carbon, as about 60 pounds of carbon anodes are consumed for every 100 pounds of aiumin.'.'-n produced. Tie anodes are usually made by mixing finely ground petroleum coke with coal tar or petroleum pitch, forming the mix into shapes under pressure, and baking them at around ?.200¦C0 Petroleum coke is ussd uecause its high density gives good strength and conductav_ty to the finished electrode, and its purity ensures that contamination. of the alumin- ium by extraneous i,iorganic material from tho carbon is low,

Jan 1, 1969

The treatment meIhods selected for the concentrator at Cobar Mines Pty. Ltd. called for a high degree of automatic control of both the grinding and flotation sections.The resulting concentrator layout includes a central control room overlooking both grinding and flotation sections. The control room houses process recorders, controllers, and indicators. together with motor stopstart stations and alarms.Plant instrumentation includes load cells and variable speed hydraulic drive feeders for feed-rate control of autogenous mills, together with nuclear density gauges, differential flow transmitters, and pneumatic control valves for water and pulp density control.Flotation cell pulp levels are controlled by floats and pneumatic actuators; flotation reagent controls include magnetic flowmeters and time-operated solenoid valves.

Jan 1, 1969

By Y. Nakada, E. J. Fasiska, A. S. Keh, L. Zwell

DURING an investigation of solid-solution hardening of nickel by carbon,' we found that there were no reliable data on the dilating effect of dissolved carbon on the unit cell of nickel. Bernier2 reported an increase in lattice parameter of nickel (3.523A) when an unknown amount of carbon was introduced into solid solution (3.536A). Similarly KG, Tsien, and Misek3 found an increase from 3.523 to 3.531A when nickel was carburized. strong4 studied the variation of nickel lattice constant as a function of dissolved carbon. However, in his case carbon was introduced into nickel by solidifying the melt at 65 kbar. Therefore, his carbon concentrations were much above the highest equilibrium solubility limit5 (2.7 at. pct C at 1 atm). Knowledge of the lattice mismatch between solute and solvent is essential in understanding the mechanism of solid-solution hardening. Therefore, we decided to determine the dilation of the nickel lattice by carbon under the more usual conditions of atmospheric pressure. The material used was Inco Electrolytic Nickel of 99.95 pct purity, as specified by the supplier. The impurity contents in wt pct were: Fe, 0.01; Cu, 0.01; Co, 0.03; 0, 0.005; C, Si, S, N, trace. To this base material various amounts of AUC-grade high-purity carbon were added during vacuum induction casting. Ingots, 2 in. in diam, were heated in a muffle furnace at 1000°C for i hr., hot-rolled to 1/2-in. thickness, and quenched into brine. All ingots with carbon concentration greater than 0.98 at. pct were enclosed in a cast iron box during the heating to minimize decar-burization. Small pieces were then either swaged down to 0.028-in.-diam wire or cold-rolled to 0.010-in.-thick sheets. After the final cold reduction in area of 50 pct, the specimens were recrystallized by heating in evacuated capsules at 1100°C for 60 to 80 sec and then quenched into brine. The final grain size was 50 to 100 µ. The carbon contents of the alloys, Table I, were determined by a combustion method

Jan 1, 1969

By S. Shapiro, G. Krauss

We will reply to Dr. Pitsch's discussion by 1) presenting in greater detail the single surface trace analysis which we performed on the reversed austenite plates in a single parent plate of martensite of known orientation, 2) relating the results of our analysis to the conclusions which Dr. Pitsch makes on the basis of our data, and 3) examining the validity of our selection of twenty-nine individual traces from the over 200 austenite plates which were observed in a surface of this single martensite plate. Fig. 7 shows a standard (001) projection of the martensite plate from which the austenite-martensite interface traces were taken. The traces are plotted on the projection as the small solid circles, and the great circles corresponding to the loci of plane normals which could contain each trace or could intersect the surface plane along the measured directions are also plotted. It can be seen that these great circles intersect at a point which corresponds to the normal of the surface plane on which the traces were observed. Also rate which occurred only at particularly low heating rates, see Figs. 1 and 3 in the paper.2 Since in this case the interpretation of Jana and Wayman is plausible and since we have no alternative to this interpretation, we would like to state only that the existence of a diffusion-controlled reversal at low temperatures seems to be not yet proved beyond any doubt. The author wishes to thank Professor G. Krauss for making available his manuscript prior to publication. It is also a pleasure to acknowledge the lively written discussions, which the author has had with Professors G. Krauss and C. M. Wayman prior to this communication. The financial support of the Deutsche For-schungsgemeinschaft for the work on which this communication is based is also gratefully acknowledged. plotted within small dotted circles which represent a i3 deg scatter in each of the twenty-four unit stereo-graphic triangles are our A and B poles7 and the pole P determined by Kessler and itsch.' The data presented in Fig. 7 permit a direct association of the measured traces and the various proposed habit plane poles for the reversed austenite plates in the martensite crystal. If the sample measurements do in fact

Jan 1, 1969

Construction of Western Mining Corporation's nickel refinery at Kwinana, Western Australia, commenced in July, 1968. Production of 15,000 tons per annum of refined nickel metal will commence early in 1970, The plant will also produce approx- imately 150,000 tons of ammonium sulphate0 The ammonia leach process which was developed by Sherritt Gordon Mines Ltd., and has been in operation at their plant at Fort Saskatchewan, Alberta, Canada, for the past 15 years, will be used at Kwinana. The refinery will cost approximately 435 million, and will employ upwards of 250 people.

Jan 1, 1969

By W. S. Sanner

A High Splint coal was carbonized in a low-temperature, fluidized-bed sys-tem to study the effects of thermal cracking on the products of decomposition. The coal was fluidized in recycle gas at 485° to 600° C, and the products were cracked at 600°, 700°, and 800° C in a bed of fluidized coke. Yields of tar, pitch, paraffins, and olefins decreased as carbonization temperature increased. Thermal cracking of the tar vapors produced the highest tar yields at 600° C, and light oil yield increased at cracking temperatures up to 700° C. At an 800° C cracking temperature, the yield of light oil decreased.

Jan 1, 1969

By Gordon E. Agar

Several correlations have been proposed to relate energy consumption and size reduction in comminution, and although these are arrived at from different starting points, it is postulated that they are all statements of the same basic concept. To test this postulate, the dry ball mill grindability of langbeinite was determined, and the results were analyzed according to the various methods. An examination ' of the energy-particle size relationships proposed in the recent past revealed that they had much in common. In fact, the conclusion was tentatively drawn that these expressions were essentially the same, even though they were arrived at from quite different basic premises. The equations attributed to Charles2 and Holmes3 were shown to re- duce to the same single equation, W - A K-3, and the simulated continuous test used by Maxson et al.4 was shown to give the best experimental value of the required empirical parameter, ß. Furthermore, the size distribution parameter a in the Schuhmann equation, y - (x/K)2, was shown to be equal to ß in many cases. The kinetic approach used by Arbiter and Bhrany5 should give the same results as the Maxson test procedure; however, the batch operation used by Arbiter and Bhrany could not produce data that would be as precise as the simulated continuous technique. To test the validity of these conclusions, the simulated continuous method was used to obtain data on the dry grinding of langbeinite. The results are discussed in terms of the various equations and approaches. APPARATUS AND MATERIAL A ball mill with internal dimensions of 17.5 cm (6 7/8 in.) in length by 19.4 cm (7 5/8 in.) in diam was loaded to 50% of its volume with balls 3.2 cm in

Jan 1, 1969

By E. L. Kapfer

A preliminary description is made of the field of automation and optimization of the oxygen blast furnace process. The concept of static and dynamic process control is illustrated. After a short general description of all factors concerning the optimization of this process, a learning system is derived which gives better results than models previously used. This learning or self-adaptive control system uses statistical methods with exponential aging of process data and requires derivation of multi-variable functions of the process for which measurements can be made available. The practical application of this new procedure and of additional measuring instruments are discussed, and results obtained in plants using the adaptive control system are described. A survey of European steel plant automation using the Siemens technique is presented.

Jan 1, 1969

By William G. Pariseau, H. Douglas Dahl

Recent subsidence legislation indicates that mining engineers would be welt advised to be able to predict and control surface damage caused by mine subsidence. To date, such an ability is practically nonexistent. Model analysis is suggested as one of the alternative paths available which might yield fruitful results. Similitude requirements developed for a self-loaded body in static or quasi-static equilibrium indicate that complete similitude without centrifuging is an impracticability. However, a pilot experimental study which used a simplifying assumption to correctly model mine subsidence has produced results in qualitative agreement with field observations. The purpose of this paper is to present a discussion of the various approaches that can be taken in the study of mine subsidence phenomena. Particular attention is focused upon the rational selection and use of laboratory models. Broadly interpreted, mine subsidence is the deformation of the rock mass enclosing a mine. Depending upon a number of factors, the movement of the subsiding rock mass may disrupt gas and water lines or other buried utilities, damage surface structures such as buildings and bridges, dislocate streams, roads, and rail lines, aggravate acid mine drainage and fire problems, and generally mar the landscape. It is clearly a problem that no mine manager can safely ignore. It is also a problem that will grow with the general population increase. In the following discussion, a summary review of past and present approaches to subsidence studies is given. The possibilities of duplicating subsidence phenomena in laboratory models are examined, and an analysis of a particular type of model is presented. Some preliminary results obtained from a model of the particular type analyzed are then discussed. REVIEW OF PREVIOUS WORK Historically, subsidence investigations have been empirical studies in the field and laboratory or theoretical analyses of mathematically idealized media. Empirical and theoretical work in the United States has generally lagged behind investigations abroad. In the United States, field studies are mostly pre-World War 11. These are summarized in the Mining Engineer's Handbook. ' Field studies in Europe are more recent and more extensive. Those made in Great Britain are summarized in the Subsidence Engineers Handbook2 and represent observations made at 157 different collieries. Such studies by themselves are of limited usefulness as are all empirical studies. One can never be certain that conditions at one mine will be similar enough to those at another to warrant the drawing of like conclusions. European subsidence formulas rely heavily upon the "angle of draw" and "critical area" concepts. The angle of draw is defined as the angle between a vertical line through the face, and another line extending from the face to the surface at the point where movement is zero. The critical area is defined in relation to the least extraction necessary to produce maximum subsidence. Fig. 1 illustrates the angle of draw and critical area concepts. First and second "limits of influence" are also shown. The angle of draw and associated critical area concept are obviously not well defined, being dependent upon the accuracy of the surface survey. In Great Britain, the angle of draw has increased through the years from about 26 to 35°. In the United States, zero and negative angles of draw have been reported. In the authors' opinion, these purely geometrical concepts represent an oversimplification of subsidence phenomena and their use, in the United States at least, should be discouraged. Empirical observations of laboratory models containing layers of earth, sand, clay, and plaster were made by Fayol (cited by Peele) as early as 1885. An outgrowth of his work was the "dome theory," a verbal description of what is assumed to occur in subsiding rock masses. The dome theory has since fallen into disrepute. Theoretical analyses worthy of the name treat a subsiding rock mass as a deformable body. In these analyses, the actual rock mass is replaced by an idealized material that deforms according to a simple stress-strain relationship. The stress equations of equilibrium expressing the Newtonian laws of mechanical action and the geometry of strain furnish additional equations that must be satisfied. A loading criterion-generally understood, and in some cases stated explicitly-completes the theory.

Jan 1, 1969

By J. L. Jorstad

The hypereutectic Al-Si alloys 390 and A390 have wear characteristics superior to any of the more common aluminum casting alloys. This excellent wear resistance, coupled with good mechanical properties, high hardness, and low coefficient of thermal expansion, has made these alloys candidates for the all-aluminum internal combustion engine, the application for which they were primarily developed. A390 alloy is intended for sand and permanent mold casting, and requires a lower iron ccxltent (0.5 pct maximum) than its die casting companion 390 alloy (0.6 to 1.1 pct Fe). The 17 pct nominal silicon in these alloys provides sufficient quantities of the hard primary silicon phase to assure a high degree of wear resistance, yet little enough of this phase, to minimize the casting and m achining problems associated in the past with the hypereutectic alloys. The mechanical and physical properties of 390 and A390 alloys are competitive with the best of the common aluminum casting alloys with the exception of low ductility. This low ductility is not considered a detriment, since in many applications these alloys replace cast iron. Corrosion resistance is similar to the standard alloys 380 and 333. Numerous parts, of varying degrees of complexity, have been cast of alloys 390 and A390, including engine blocks and heads. The deviations from normal good handling and casting practices that are required for the alloys are those associated with the presence of the primary silicon. To obtain optimum strength and machinability, the molten alloys should be treated with phosphorus to refine the primary silicon phase. Care must be exercised to properly control the pouring temperature and rate in order to minimize primary silicon growth and segregation. AUTOMOTIVE engineers have for years recognized the advantages of lighter weight and better heat transfer that aluminum could offer as material of construction for engine blocks. These advantages alone, however, are insufficient justification for acceptance of aluminum engines by the automotive industry. To be acceptable, an aluminum engine first must pass all tests to which cast-iron engines are subjected, and, in addition, must represent no cost penalty in manufacturing. None of the conventional aluminum casting alloys have sufficient wear resistance to withstand the tests to which cast iron is subjected as a cylinder bore material, and recent attempts to manufacture aluminum engines with cast-in-place iron sleeves could not compete costwise with the equivalent cast-iron engine. The prerequisite to an acceptable aluminum engine seemed to be a casting alloy with a high degree of wear resistance that would eliminate the necessity of cast-in iron sleeves or liners. The hypereutectic A1-Si alloys 390 and A390 have met this challenge.' Combined with modified pistons and a patented cylinder bore surface finish,2 the performance of these alloys in more than 1300 cold start and cold scuff tests, over 3500 hr of dynamometer wear and endurance tests, and more than 350,000 miles of road tests leaves no doubt as to the feasibility of running on bare aluminum cylinder bores. ALLOY DEVELOPMENT The desirable characteristics of the hypereutectic A1-Si alloys have been recognized for some time. Their excellent wear resistance and low coefficient of thermal expansions have been used to advantage in the production of diesel-type pistons in Europe and to a limited extent in this country. The major contributor to the good wear resistance of these alloys is the extremely hard primary silicon phase in the microstructure. Although the percent silicon used experimentally has been much higher, most commercial alloys have ranged from about 14 to 25 pct. Generally, as the silicon content is increased, wear resistance increases, and the coefficient of thermal expansion decreases. With increases in silicon, however, machinability and cast-ability tend to suffer. The development of a satisfactory aluminum engine block material at Reynolds involved the testing and evaluation of many alloys, covering a wide range of silicon contents and numerous variations of iron, copper, magnesium, manganese, and other alloying additions. Castability, mechanical and physical prop-

Jan 1, 1969

By R. Fawley, M. A. Quader, R. A. Dodd

Stacking fault energies and annealing twin frequencies have been measured for austenitic stainless steels having a) constant 20 wt pct Cr and varying nickel contents, and b) constant 20 wt pct Ni and varying chromium contents. The effect of nitrogen has also been studied and, to a lesser extent, so has the effect of carbon. All measured stacking fault energies plot linearly against the corresponding annealing twin frequencies, suggesting that, for constant prior deformation and grain size, twinning frequency can be used to estimate stacking fault energy. Compositions low in nickel possess the lowest fault energy, while the maximum fault energy within the investigated composition range occurs mound 20 pct Cr-20 pct Ni. Nitrogen has practically no effect on stacking fault energy when increased from 0.005 to 0.05 wt pct, although Planar dislocation glide is associated with higher nitrogen contents; this may be a short-range order effect. Carbon may raise the stacking fault energy a little, and causes pronounced dislocation tangling in deformed alloys. The basically different dislocation structures promoted by nitrogen and carbon, respectively, are not associated with large variations in stacking fault energy, and the reason for the difference remains unknown. INTEREST in the dislocation configurations developed in plastically deformed alloys arises principally from a desire for an understanding of mechanisms of plastic deformation and fracture. Comparatively little basic work has been concerned with austenitic stainless steels, although considerable interest has developed in the fundamental aspects of deformation of these alloys since the suggestion that those compositions deforming essentially by planar glide are particularly prone to transgranular stress corrosion cracking.' Certain facts are well-established. An 18 Cr-8 Ni steel (type 304) has a low stacking fault energy which is increased by higher nickel contents, and the structure of these steels when moderately plastically deformed changes concomitantly from planar to less planar to distinctly tangled dislocation configurations. These changes are thought to relate to changes in stacking fault energy, and considerable effort has been expended in measuring stacking fault energies of austenitic stainless steels through the determination of node curvatures2"4 even though the method has limitations due to formula approximations,5 an upper limit of measurement of 50 erg cm-2 at the most,5 and the necessity of an extremely meticulous experimental technique. Therefore, it is not surprising that only qualitative agreement between different investigators is generally to be found.'-' At high energies where node radius measurements are inappropriate, some use has been made of annealing twin frequencies to estimate relative stacking fault energies, although a recent critical evaluation of the method suggests that it should be used cautionsly with due regard to effects of grain size and prior deformation.6 Finally, there is a question as to whether the structures of some deformed steels are due to ordering effects. In particular, the role of nitrogen in promoting planar dislocation motion has been suggested to be due to ordering,' but similar suggestions have been made for steels having low interstitial contents.4 EXPERIMENTAL Small ingots of austenitic stainless steels (-50 g) were prepared from components exceeding 99.99 pct purity, the nickel and chromium being Johnson Matthey "Specpure" metals. Carbon was added as pure graphite, and nitrogen as CrN. The components were accurately weighed, and it was assumed that the final composition was the same as the nominal composition

Jan 1, 1969

By Winston A. Wong, John J. Jonas

Commercial purity aluminum was deformed by extrusion over the temperature range 320° to 616°C and the strain rate range 0.1 to 10 per sec. Flow stresses and strain rates were calculated from the experimenLa1 ram pressures and speeds. The stress-strain rate-lemperature relationship in extrusion was found to be similar to that in creep. Extrusion, torsion, compression, and creep data extending over ten orders of magnitude of strain rate and over two orders of magnitude of stress were correlated by a single creep equation. It was concluded that hot-working is a thermally activated process, in which the rate-controlling mechanism is either the climb of edge dislocations or [he motion of jogged screw dislocations. The microstructural changes observed during extrusion were consistent with the proposed deformation mechanisms. ALTHOUGH great progress has been made in understanding the technology of extrusion, very little is known about the actual deformation mechanisms operating during flow. Previous accounts describing extrusion have indicated that the relationship between ram speed (V), pressure (P), and temperature (T) can be given as follows:1 V = apb and P = A' exp(-AT). In these equations, a and b are constants which depend on temperature, A' is a constant which depends on ram speed, and A is a "coefficient" with a different value for each metal. Although these equations have fairly wide application, they do not contribute much to a fundamental understanding of the deformation. Furthermore, extrusion has not hitherto been considered as a thermally activated rate process. This lacuna is surprising because hot-working is similar to high-temperature creep in several respects. There is, in fact, a fair body of experimental evidence suggesting that the material response under hot-working conditions is similar to that occurring under creep conditions, in spite of the many orders of magnitude difference in strain rate.2"4 Since creep has been extensively analyzed in terms of dislocation mechanisms, the comparison of hot-working to creep is useful, for it can suggest the possible deformation mechanisms operating during hot-working. In this paper, the hot extrusion of aluminum will be examined from the point of view of thermally activated deformation mechanisms, such as operate during creep. EXPERIMENTAL PROCEDURE The experimental procedure consisted of extruding commercial purity aluminum* over a range of ram velocities and temperatures at constant die reduction by the direct method. Details of the experimental equipment have been published elsewhere.5 Extrusion was carried out at each of the following billet temperatures: 320°, 376°, 445°, 490°, 555°, and 616°C at the following constant ram speeds: 0.002, 0.008, 0.02, 0.1, and 0.2 in. per sec.* All results were obtained using a square-shouldered die with an extrusion ratio of 40:1, giving a reduction in area of 97.5 pct. The ram force was the dependent variable, and was measured by means of strain gages on the ram and was plotted as a function of ram travel. The sequence of events before making an extrusion was duplicated before each run so as to minimize as much as possible variations in experimental conditions. For example, after the equipment had been assembled, the billet was allowed to heat up to temperature inside the insulated container. Once the container attained the desired temperature, a period of 1/2 hr was allowed to elapse before the extrusion was made. This time was found to be required to allow the billet to reach a steady-state temperature, as determined from previous tests. When all was ready, extrusion was carried out without interruption; that is, the billet was upset and extruded in one operation. EXPERIMENTAL RESULTS AND DISCUSSION The two usual experimental approaches for investigating high-temperature deformation exhibit an important common feature. In the first approach, which corresponds to creep, a constant stress (or load) is applied to the material at constant temperature and the resultant strain is recorded against time. After an initial transient stage, a state of constant strain rate exists (secondary creep), in which a steady-state condition is established which is sensitive to variation in either applied stress or temperature. In the second approach, a constant strain rate is applied and the resultant flow stress is recorded. This corresponds to the situation in hot torsion or hot compression, where it is observed that, for a constant test temperature, there is an initial rise in stress to a steady value which is maintained up to very high strains. In tests of this type, a steady-state region is also established in which the stress is sensitive to variation in either the strain rate or the temperature.3,4,6-16 In both types of tests, therefore, a steady-state region is established after an initial transient. In the case of hot-working this region may be called steady-state hot-working, and it is analogous to steady-state creep with which it has many common features. Stress Dependence of the strain Rate in Extrusion. In order to assess the stress dependence of the strain rate under extrusion conditions, and to compare it to that of creep, as well as of hot torsion and hot compression, the extrusion data were analyzed according to power, exponential and hyperbolic sine creep equations.

Jan 1, 1969

By A. E. Chute

The shortage of sulfur is not only continuing but appears to be worsening, attended by steadily rising prices. At the same time emphasis on air-pollution abatement is also increasing. These two factors, a rising market and the growth of environmental attention, have encouraged producers to carefully review all possible sulfur sources. As a result, production of sulfur from hydrogen sulfide occurring in petroleum is receiving greater attention than ever before. Until about a decade ago, the practice of recovering sulfur from hydrogen sulfide separated from gases (either found naturally or generated in desulfurization of liquid petroleum) was wide1y recognized but contributed little to total free-world sulfur production. However, during the past ten years, the production of sulfur from this source has increased so rapidly that it now accounts for a substantial portion of total production. This trend shows no signs of slackening, and current forecasts predict that recovered sulfur may become the dominant source of supply within ten years, exceeding mined sulfur production. This paper is intended to list sulfur sources and relationships, and to discuss the potential of producing sulfur from petroleum. The processing involved, in addition to product storage and transportation will also be discussed along with important economic aspects of sulfur recovered from hydrogen sulfide. For many years, most of the world's elemental sulfur has been produced from salt domes, predominantly by the Frasch process. During the past decade, however, another production source has developed so quickly that it is expected to surpass the Frasch production sources within a short time. This new source lies in the petroleum gases and liquids from which dramatically increasing quantities of elemental sulfur are being recovered. In the phraseology of the trade, the sulfur so obtained is know as "recovered sulfur," a term which does not, as one might expect, include sulfur recovered from other sources such as smelter gases. The growth rate of recovered sulfur compared to that of Frasch sulfur, total elemental sulfur, and total Free World sulfur in all forms is shown in Fig. 1 Since 1963, sulfur consumption has exceeded production,with the natural result that the price of sulfurhas continually increased. The posted price reported for f.o.b. Port Sulphur, La., has risen from as low as $18 per ton in 1962 to $32.50 per ton in mid-1967. With freight and other charges, delivered prices have of course run much higher, amounting to $45 or $46 per ton on the east and west coasts. In some cases, spot sales for as much as $60 have been reported. Although it is playing an ever-increasing role in the sulfur market, recovered sulfur was originally a by-product of the removal of hydrogen sulfide from natural and petroleum refinery gases. Today, however, it is often the most valuable product of a multi-product processing facility. Since there are two major sources of recovered sulfur—production and refining processes —natural gas is included with liquid petroleum for purposes of this discussion. Sulfur from these sources is produced in the form of gaseous hydrogen sulfide which is removed from a gas stream and converted to elemental sulfur. Gases in which hydrogen sulfide occurs naturally are natural gas and the gas produced from a high=pres-sure crude=oil or condensate field.

Jan 1, 1969

By E. J. Nielsen, P. R. Strutt

A study has been made of the progressive changes in the distribution of etch-pit structures occurring during high-temperature creep in copper + 7 wt pct Al single crystals oriented with a [113] tensile axis. The two equally stressed glide systems with the highest Schmid factor would be expected to form subboundaries of the type predicted by Kear.2 The alignments of etch-pits on sections parallel to different (111} planes consistent with these types of boundaries were not observed. However, they were consistent with planar subboundaries (on a macroscopic scale). From an analysis of Amelinckx1 it may be shown that stable cross-grid dislocation boundaries may form in the primary slip planes. These boundaries form when dislocations with a Burgers vector not in the slip plane move into the plane by combination of climb and glide. THE geometry of subboundaries formed by the interaction of dislocations of two glide systems has been analyzed by Amelinckx,1 and the particular types produced by deforming fee crystals are predicted by ear.' In this paper types of boundaries which may be formed when climb as well as glide occur are discussed as this is relevant in high-temperature creep. It is assumed in the present investigation that the etch-pits observed in Cu + 7 wt pct A1 on surfaces parallel to {111} planes delineate the sites of dislocations. Although there is no direct evidence for this previous work on a-Cu/Al single crystals by Mitchell, Chevrier, Hockey, and Mon-aghan,3 would show this assumption to be reasonable. The alignments of etch-pits which form during creep are studied on sections parallel to each {111) plane. It is then deduced that these alignments are consistent with a specific type of planar subboundary. The Cu + 7 wt pct A1 single crystals had a [113] tensile axis and Fig. 1(a) shows schematically the relation of the slip planes and slip directions (as represented by tetrahedron ABCD) with reference to the tensile axis. The two equally stressed glide systems with the maximum Schmid factor namely ß-AD and (a-BD, from the analysis of Kear,2 would be expected to form the boundaries shown in Fig. l(a) and (b), also Fig. 5(a) and (b). EXPERIMENTAL PROCEDURE The a-Cu/Al single crystals were grown and annealed in a "gettered" argon atmosphere. Chemical analysis showed the aluminum content to be uniform in each crystal and the difference between crystals was maintained to an accuracy of ± 0.25 wt pct. The initial dislocation density and mean subgrain diameter after annealing was -106 cm-2 and 250 µ, respectively. Surfaces parallel to (111) planes were produced by specially developed electrolytic machining processes. The {111} faces were next electropolished for 5 min in a solution consisting of 25 g chromium trioxide, 113 ml glacial acetic acid and 40 ml water; the applied potential was 8 v. Dislocation etch-pits were revealed using l an etchant described by 1 ml bromine, 45 ml HCl, and - 250 ml water. RESULTS In crystals strained into secondary creep at higher stresses (443 and 750 g - mm-2 at 650° C aligned rows of etch-pits parallel to slip plane traces were evident in sections parallel to the (1111, (ill), and (111) planes, see Fig. 3. As well as the longitudinal alignments in Fig. 3, well formed randomly oriented arrays indicative of an equiaxed subgrain structure are evident. At the lower stresses (100 to 230 g . mm-2) only an equiaxed structure formed during creep. The sections in Fig. 3 are from a crystal crept for 70 hr at 650°C with a CRSS of 443 g.mm-2. Two identically oriented crystals were also deformed at the same temperature and stress for 5 min and 4 hr. In the crystal crept for 5 min, the etch-pits were randomly distributed with no tendency for directional alignment, see Fig. 2(a). As shown in Fig. 2(b) aligned arrays were evident after 4 hr creep but they were not nearly so well defined as in Fig. 3. The alignments (parallel to the arrows) in Fig. 3 are consistent with the existence of boundaries in the two main slip planes a and ß. The way in which this is deduced is seen by reference to Fig. l(c), where the existence of boundaries in the a and ß planes is verified by sectioning parallel to a,ß, and d. The (111) and ß(111) planes intersect the d(111) plane along BC [101 ] and AT [011] and alignments parallel to [101] and [011] are clearly evident in Fig. 3(c) in a section parallel to the d(111) plane. Similarly the a, and ß planes in Fig. l(a) intersect each other along DC [110] and hence there will be an alignment parallel to [110 ] in sections parallel to the a-plane and the ß-plane; this is evident in Fig. 3(a) and Fig. 3(b). It is interesting to note that alignments of etch-pits consistent with the boundaries predicted by Kear2 were not observed; see Figs. l(a) and l(b). The geometry of boundaries in {111} planes as shown in Fig. l(c) is discussed later. In Fig. 4(a) the individual etch-pits are resolved and the alignments are exactly parallel to the slip trace direction [101]. However, in some areas alignments deviate away from the slip trace direction by as much as 10 to 15 deg, this is evident in Fig. 4(b), and in Fig.

Jan 1, 1969

By Albert H. Fay

The gypsum industry makes significant contribution to the wealth of our nation. This non-metallic mineral ranks in the highest order with America's most precious resources. Evidence of this is borne out by the fact that gypsum is a vitally necessary element in the building, industrial and agricultural industries. In 1967, the United States consumed 14 million tons of this valuable ore. Of .this amount 69% was required by the building industry for the manufacture of building materials. An additional 21% was directed to the industrial market, for the manufacture of Portland Cement and for other industrial uses. The remaining 10% was used for agricultural purposes.

Jan 1, 1969