By James A. Hartlage

Work on the design of Kelex 100 was initiated several years ago at the Research Laboratories of Ashland Chemical Company. The effort was specifically directed toward the synthesis of an organic molecule which would strongly and selectively chelate copper ions in acidic solutions and form an oil soluble complex which would be stable in contact with an aqueous phase having a pH of approximately one. This publication describes efforts to establish data which could be used to estimate the economic utility of the new reagent. For helping to accomplish these ends, the author wishes to acknowledge the assistance of Mr. A. V. Henrickson of Hazen Research, Inc. for gathering a portion of the data presented here and to thank the copper companies who supplied leach solutions for studies described in this paper.

Jan 1, 1969

By Clarence O. Babcock

Model pillars of limestone, marble, sandstone, and granite, with length-to-diameter ratios of 3, 2, 1, 0.5, and 0.25 (0.286 for granite), were broken in axial compression to determine to what extent an increase in end constraint increased compressive strength. Radial end constraints of 13 to 23 percent of the average axial stress in the pillar, produced by solid steel rings bonded with epoxy to the ends of dogbone-shaped specimens, increased compressive strength somewhat above that of cylindrical pillars without ring constraint. However, when the results were compared with those obtained by other investigators for straight specimens of several rock types taken collectively, with L/D ratios greater than 0.5, the resulting strengths were not significantly different. Thus, the amount of end constraint produced by the solid steel rings was about the same as that produced by the friction from the steel end plates. In other tests a radial prestress of 3,000 psi or 5,000 psi was applied prior to axial loading by adjustable hardened steel rings to increase the constraint above that obtained for the solid rings. The average radial constraint stress, expressed as a percentage of the average axial pillar stress at failure for the 3,000 psi prestress, was 54.3 percent for limestone, 40.3 percent for marble, 44.7 percent for sandstone, and 23.4 percent for granite. The average radial constraint stress, expressed as a percentage of the average axial pillar stress at failure for the 5,000 psi prestress, was 74.2 percent for limestone, 51.2 percent for marble, 61.6 percent for sandstone, and 29.7 percent for granite. These constraints increased the compressive strength significantly above the strength of straight specimens and solid-ring constrained specimens. These results suggest that large horizontal stresses in orebodies mined by the room and pillar method should increase the strength of the pillars and allow an increase in ore recovery by a reduction of pillar size when major structural defects are absent.

Jan 1, 1969

By R. D. Stover, F. O. Shuck

The variation of binary-diffusion coefficients with composition in the liquid Bi-Sn system at 300°C was measured using the capillary-reservoir technique. The experimental coefficients did not exhibit a simple composition dependence. A number of tests were also made to determine the effect of variation of density with composition on convection within the capillaries. These tests indicate that the density changes arising from composition duferences may give rise to high diffusion coefficients unless care is taken to maintain a stable configuration. In recent years there has been considerable interest in diffusion in liquid metals. However, the bulk of the work done to date has involved measurements of self-diffusion or diffusion of dilute concentrations of "solute" metals. Because there are possible applications to liquid phase processing of metal alloys and since additional data may help to clarify the nature of diffusion in liquid metals, investigations of the concentration variation of diffusion coefficients in binary alloys have been undertaken. Of past studies only two have covered large ranges of binary composition. Niwa et al.' investigated the Pb-Sn, Bi-Pb, and Bi-Sn systems and Grace and Derge2 investigated the Bi-Pb system. Because of the discrepancy between the data of these investigators, it was deemed desirable to check the possibility of convection arising from the variation of density with composition. The capillary-reservoir technique of Anderson and saddington3 was chosen for the present investigation since it has been widely used for measurements involving dilute solute concentrations and it was the technique used by Grace and Derge.2 It was necessary, however, to modify the normal procedure of using a pure metal bath to avoid measurement of integral diffusion coefficients over large concentration ranges. The alloy system chosen for study was the Bi-Sn system for which there are some data available.' EXPERIMENTAL PROCEDURE In order to utilize the capillary-reservoir technique for measurements of diffusion coefficients as a function of composition, it was necessary to modify the normal procedure slightly. This modification consisted of using a reservoir composition which was only slightly different from that in the set of capillaries, in order that the integral coefficients measured might be taken over a small composition range and might thereby be assumed to approximate the differential coefficient at some average composition between that of the capillary and that of the bath. It was found that a composition difference of approximately 0.10 mass fraction provided a satisfactory compromise between a small increment in composition and reasonable accuracy in measuring changes of composition. The alloys were prepared from tin and bismuth of 99.999 pct purity. The materials were first cleaned of surface oxides, then weighed and melted to form a homogeneous alloy in a Pyrex filling apparatus. The capillaries used were of precision bore Pyrex tubing 1.000 *0.005 mm bore. Capillaries of various lengths (from 2.85 to 5.85 cm) were cut and sealed at one end by fusing a 3-mm Pyrex rod to the end. The capillaries were filled by inserting them into the filling chamber, evacuating the chamber, submerging the capillaries, and pressurizing the chamber with argon. Two sets of capillaries were prepared for each run. One set contained an alloy more dense than the bath alloy and one set a less dense alloy. This procedure was followed so that the effect of density difference on the measurement could be determined. After filling one set of capillaries, these were placed open end up in a capillary holder and transferred to the diffusion chamber which consisted of a Pyrex tube inserted into a graphite block. The second set of capillaries was then filled and placed into the diffusion chamber. The reservoir alloy, which had been melted in a separate crucible, then was poured carefully into the diffusion chamber. Sufficient reservoir alloy was used to cover all capillaries to a depth of several centimeters. All of these operations: capillary filling, melting of alloys, and diffusion anneal, were carried out in a fused-salt bath which maintained a temperature of 300"*1°C. All capillaries were permitted to diffuse for approximately 48 hr. At the end of the diffusion period the capillary holder was removed from the bath and

Jan 1, 1969

By L. J. M. Smits

A theoretical equation is developed describing membrane potentials of shaly sands as a function of the cation-exchange capacity per unit pore volume of the rock and saturating water salinity. This equation is based on the same simple physical model as that employed earlier7 describing the electrical conductivity of shaly sands. Experiments conducted with NaCl solutions showed that the equation is obeyed, except in the case of saturated salt solutions where minor deviations were observed. A possible explanation is given for this discrepancy. As the clay content and the porosity of shales may vary appreciably, shale membrane potentials also vary. It was found that membrane potentials of shales can be calculated accurately with the aid of the same theory. Consequently, changes in membrane potentials can be accounted for by simple measurement of cation-exchange capacities per unit pore volume of both shales and shaly sands. Charts are given to facilitate interpretation of the electrochemical part of the SP in terms of cation-exchange capacities and the salinities of mud filtrate and formation water. INTRODUCTION A spontaneous potential (SP) log is a record of the way in which the electrical potential of a sonde varies as it passes down a borehole. Such variations frequently reflect rock texture, e.g., permeable beds intercalated in an impermeable series often are indicated by a sharp change in potential. Nowadays it is recognized that SP logs may be interpreted in terms of formation-water salinity and formation shaliness. The four sources of the SP are illustrated in Fig. 1. El and E4 represent streaming potentials generated by the flow of mud filtrate through mud cake opposite permeable formations and through shale, respectively. An extensive review of the literature on the evaluation of these streaming potentials is given by Lynchl and will not be discussed here. The remaining part of the SP generally is called the electrochemical potential, which is divided into two parts: a membrane potential across the shale (E3, Fig. 1) and a membrane potential in the permeable sand at the diffusion boundary between formation water and mud filtrate (E2, Fig. 1). It was found by wyllie2 that the membrane potential across the shale, E3, is the most important contribution to the electrochemical potential, the shale acting as a semi permeable membrane. When the sand is clean it does not influence the diffusion process, so E2 equals the value of the so-called liquid-liquid junction potential observed when the two solutions diffuse freely into each other. When the sand contains clay, however, this interferes with the diffusion process and affects the diffusion potential generated. The greater the proportion of clay, the stronger this effect will be. Wyllie,3 Doll4 and Poupon et al.5 took this effect into account theoretically, starting from a physical

Jan 1, 1969

By R. E. Hummel, J. W. Koger

SINCE the first report about a diffusionless transformation of bcc p1 brass to tetragonal p" in 1936 by Kaminski and Kurdjumov,' a series of papers have been published about this transformation, mainly dealing with the temperature range of the martensitic-start temperature (M,) and with the crystallographic structures of the parent and product phases .s In the

Jan 1, 1969

By N. F. Fiore, M. C. Mangalick

DISLOCATION damping in single crystals is orientation dependent.&apos; If dislocations are distributed uniformly over all the slip systems in a crystal, and if each dislocation contributes identically to the damping process, then a damping loss or decrement 6 arises. In fact, however, for a crystal of axial direction (hkl), dislocations on certain slip systems are oriented to make a larger contribution to the damping loss than are dislocations on other slip systems. Thus the measuring damping, 6 (hkl) is proportional to an orientation factor (hkl), which weights the ability of each slip system in the crystal to contribute to the total damping. If it is assumed that dislocations are distributed uniformly on all slip systems, then for a given orientation of an fcc crystal this factor is determined2,3 by the three nonzero elastic constants Cll, C12, and C44 and the density p. In this communication measured values of elastic constants for two Fe-18Cr-Ni alloys are reported, and the dislocation damping results on two different orientations of each alloy are analyzed for orientation dependence. Elastic constants were determined by measuring the ultrasonic velocities of one longitudinal and two shear waves in (110) direction of the fcc crystals.4 Variation of velocities with the change in orientation is very small for (110) orientation,3 and so this direction is ideal for orientation factor and comparative damping measurements. Experimental Procedures. The nominal compositions of the alloys studied are given in Table I. These alloys were vacuum-melted and vacuum-cast from high-purity materials at U.S. Steel Applied Research Laboratories. The single crystals were grown by the modified Bridgeman technique. The specimens were homogenized at 1350°C for 20 hr, cut to shape and size with a spark cutter, and then annealed at 1100°C for 20 hr prior to use. In the KHz frequency range, the Marx composite piezoelectric oscillator was used to obtain the damping. The ultrasonic pulse technique was used to measure the ultrasonic velocities and the attenuation in the MHz frequency range. M.c.mANGALICK,-- StudentMemberAIME,formerly Research Assistant, University of Notre Dame, is now with Casting Laboratory, Chase Brass and Copper Co., Cleveland, Ohio. N. F. FIORE, Associate Member AIME, is Assistant Professor, Department of Metallurgical Engineering and Materials Science. University of Notre Dame, Notre Dame, Ind. This communication is part of a Ph.D. thesis presented by M. C. MANGALICK to the Graduate School of the University of Notre Dame. Manuscript submitted May 20. 1968. IMD Elastic Constants. Table I gives the values of the ultrasonic velocities. Values of C11, C12, and C44 calculated from these velocities are also given in Table I, and it is evident that there is very little variation in C11, C12, and C44 with nickel content. This slight variation may be attributed to inaccuracies in velocity measurements and practical differences in the orientations of the specimens. For example, in B the time interval for vl was 2.4 ± 0.05 sec giving an error in v1 of 0.235 x or 0.005 in. per sec. The elastic constants obtained by pulse technique were tested by calculating E<110>, Young&apos;s modulus for the (110) direction, from the equation: This value was compared with the value computed from the resonance bar measurements in which where fr is the resonance frequency and I, is the length of the specimen. In all cases, the values calculated from the ultrasonic velocity measurements

Jan 1, 1969

By H. Morgolin, M. A. Greenfield, P. A. Farrar

In attempts to correlate mechanical properties with microstructure, it is desirable to determine the effect of ß grain size. Determination of 6 grain size is not a problem where a has precipitated at ß grain boundaries. However, in alloys which have been processed to produce an equiaxed a +ß structure the ß grain size is difficult to determine because ß grain boundaries do not etch. The ß grain size can sometimes be laboriously determined by searching for grains which have some a! outlining the 6 grains. This difficulty of ß grain size determination in equiaxed a + ß alloys can be overcome by heating below the ß transus temperature for a short time and water quenching. Fig. 1 shows the starting equiaxed a + ß structure of the Ti-5.25A1-5.5V-0.9Fe-0.5Cu alloy used in this investigation, and Fig. 2 shows the microstructure of the same sample water-quenched after heating 1 min at 1675"F, which is 25°F below the 0 transus. The heavily etched microstructure consists of some equiaxed a! in a structure showing considerable amounts of transformed ß. The ß grain

Jan 1, 1969

By J. H. Swisher

HIGH-temperature anneals in wet hydrogen are widely used in research as a technique for decarburiz-ing Fe-C alloys. This technique is also used commercially in processing low-carbon steels for magnetic applications. The results of some calculations to be presented show that for temperatures up to 1100°C there is a critical temperature for maximizing the decarburization rate of alloys containing about 0.1 pct C. The low-temperature portion of the iron side of the Fe-C phase diagram1 is reproduced in Fig. 1. Preliminary calculations show that the critical temperature is between 727" and 905°C. In this range, the alloy contains two phases during heat treatment, ferrite and austenite. Decarburization therefore occurs by a process termed "diffusion accompanied by a phase change".&apos; For intermediate stages of decarburization, the carbon concentration profile in a flat plate is shown in Fig. 2. The carbon content increases linearly from zero at the surface to a value, cB , at the two-phase boundary. cB is known from the phase diagram, see Fig. 1. At the interface where x = 5, the carbon content increases to ci, the initial concentration in the alloy. smith3 has derived an equation which describes the rate of movement of the boundary. With a rearrange-

Jan 1, 1969

By D. J. Mottern, F. Wald

SEVERAL systems have been investigated by Bates, Wald, and weinstein&apos; to determine the compatibility of pure PbTe with various metals. This was accomplished by experimentally determining the direction of the reaction given by Eq. [I]: The direction of this reaction is very important if alloys of the PbTe system are to be used in thermoelectric generators because the presence of free lead in the matrix, followed by incipient melting in the vicinity of the hot junction, could cause a bonding failure. According to anssen,&apos; the Au-Te system contains only one stable compound, AuTez. The initial alloy which was reacted was therefore of the composition AuTez + 2Pb. Ten-gram samples of PbTe plus 1, 10, 20, 30, 40, 50, and 70 at. pct Au were encapsulated in carbon-coated quartz capsules in vacuo. All materials were of semiconductor (99.999+ pct) purity. Carbon coating was used to prevent reaction of the quartz with any of the alloying constituents (the solubility of carbon in the constituents of the alloys is negligible). Each capsule was then placed in a thermal analysis furnace, melted, and cooled through the transformation region. Thermal arrests were monitored on a strip chart recorder. Each sample was subsequently examined microscopically after standard grinding and polishing techniques were applied. For better contrast between the phases, the samples were etched in Murakami&apos;s etch; however, both phases could be identified without etching. Several of the samples were ground into powder, stress-relieved, and X-rayed in a Debye-Scherrer camera using nickel-filtered Cu-Ka radiation. The phase diagram shown in Fig. 1 indicates that the pseudobinary system exists as a simple eutectic with no measurable (<I pct) solid solubility at either limit. Figs. 2,3, and 4 are photomicrographs of the structures obtained with 20, 40, and 50 at. pct Au, respectively. At higher concentrations of gold (>40 pct) slight divorcement of the eutectic occurred, apparently due to a) the difference in density between gold and PbTe (19.6 and 8.25 g per cu cm, respectively) or b) the nonideality of the liquid as noted by the curvature of the liquidus lines. The eutectic temperature was determined to be 742° ± 5°C. The composition of the eutectic was determined by extrapola-

Jan 1, 1969

By Ralph B. Adair

The Bureau of Mines conducted laboratory and continuous pilot plant flotation tests to determine the feasibility of recovering commercial-grade mica from an Alabama graphitic-mica schist. Preconcentration of the ground ore on a Humphrey&apos;s spiral was employed to reject the heavy minerals and part of the quartz in a product virtually free of mica. The acid-cationic mica flotation process recovered over 89 percent of the mica in a product containing 98.7 percent mica. Grinding of the mica concentrate in a fluid energy mill produced a product with a bulk density of 12 lb per cubic foot.

Jan 1, 1969

By V. Sobitsky

In open cast mining of coal, the cost per ton of output is four to five times less and labor productivity five to six times higher than in under- ground mining. This is why the coal industry of the USSR is oriented toward giving priority to the development of open cast coal mining. Deposits of coal which lend themselves to open cast mining in the USSR are enormous, with 90% of them located in the eastern part of the country. The technique is by no means limited to the eastern part, however-despite wide variations in climate, other parts of the Soviet Union also use open cast mining. The occurrence and type of coal deposits in the USSR vary greatly. Some of them are flat coal seams 2 to 40 m thick, and a few are even thicker. There are also deposits having a complex mode of occurrence, such as a series of seams of different thicknesses with angles of dip varying from slightly inclined to steep, often with dislocations. Overburden materials are quite diverse with regard to physical and mechanical properties. There are three kinds encountered-loose or unconsolidated overburden, medium-hard material, and hard rock. The stripping ratio, i.e., the amount of cover per ton of mined coal, varies from 1 to 12 cu m per ton. SYSTEMS OF MINING The great diversity of natural conditions has brought forth a variety of technologies and techniques in the open cast mining of coal. In open cast practice, the following systems of mining are used : (1) a transportation system in which the overburden is transported to spoil banks by rail or by truck; (2) a system with direct disposal of overburden, the rocks being dumped on spoil banks with a stripping excavator; and

Jan 1, 1969

By M. O. Serbousek

To further investigate the potential of precast concrete sets as a support medium for underground mines, the Bureau of Mines designed an eight-piece precast reinforced concrete drift set for a small opening. Twenty-two sets of three different member sizes were tested to destruction under two loading conditions. A discussion of the test results and typical failure patterns is presented.

Jan 1, 1969

By N. N. Breyer, W. R. Warke, S. Dinda

A model for the low-temperature peak, LTP, in fcc metals is presented. In high stacking fault energy metals, e.g., aluminum and nickel, it is proposed that a reversible dislocation glide and climb process might give rise to the observed high relaxation strengths and activation energies equivalent to volume self-diffusion values. In low stacking fault energy metals such as copper, gold, and silver, dislocation climb is energetically unfavorable at T < 0.5 Tm and the relaxation process is therefore mainly one of reversible glide. This model is used to explain the effect of a change in grain size and impurities on the LTP. THE low-temperature grain boundary damping peak, LTP, in spectroscopically pure aluminum,&apos; copper,17&apos; gold,2 nickel,3 and silver4 has recently been the subject of a detailed investigation by our laboratory. The main results are summarized in Table I. An empirical relationship was found between the peak relaxation strength, AE, and the width of the dissociated dislocation, do,* given by: do = µa2/24p? (Ref. 5) [I] where p is the shear modulus, y is the stacking fault energy,6-8 and a is the lattice parameter, Table 11. 4E is plotted against do in Fig. 1. Two regions are apparent: region (a)! which contains all but one of the metals, where AE decreases linearly with increasing do, i.e,, AE 1/do; and region (b), where ?E is approximately independent of do. A similar trend is observed when the ratio Qp/QL is plotted as a function of do, Fig. 2. (Qp and Ql are the activation energies for the peak and for lattice diffusion, respectively). In the past, when Qp and QL were found to be comparable, the relaxation peak was explained in terms of grain boundary sliding.10 The equivalence of Q, and Qb. the activation energy for grain boundary diffusion, prompted the suggestion that it was a consequence of reversible grain boundary migration on an atomic scale." A new model for the LTP, which is based on the experimental relationships in Figs. 1 and 2, is presented. In region (a) it is suggested that stress relaxation occurs through the reversible glide and climb of grain boundary dislocations; in region (b) only reversible glide can take place. The resultant effect on the grain boundary might be sliding or "a bowing out", but, since the total distance moved will be 50A, the atomic movements are considered of primary im- portance. It must be emphasized that this is only a qualitative model, but at the moment it appears the most likely way to explain the widely varying, but re-

Jan 1, 1969

By John G. Holmes

The generation of low cost power is but one phase of the TVA program for regional development. During the 36 years since TVA began, growth in its generation of electric power has necessitated a shift from a predominantly hydroelectric power system to a combination steam and hydroelectric system. The addition of steam-electric power plants to TVA&apos;s generating system was necessitated by the rapid increase in the traditional and defense demands for electric power in the 80,000-square-mile area served by TVA, the need to firm up the hydroelectric power, and the fact that all available sites for sizeable hydroelectric projects had been developed. At present TVA owns and operates 40 power plants--29 hydroelectric and 11 steam-electric plants. The total generating capacity of the hydroelectric plants is 3,105,430 kw, and the capacity of the steam plants is 13,951,135 kw. This provides a total generating capacity of 17,056,565 kw for the plants operated by TVA. Individual capacity of the 112 hydroelectric units ranges from 10,000 to 67,500 kw, and the individual capacity of the steam-electric units now in operation ranges from 60,000 to 950,000 kw. In addition to this generating capacity, TVA distributes the power from 6 U. S. Army Corps of Engineers hydroelectric plants on the Cumberland River. These plants contribute an additional 725,000 kw. Also, under an agreement with the Aluminum Company of America, TVA directs the stream flows and generation of their 423,715-kw system on Tennessee River tributaries and shares with Alcoa in the increased generation resulting from this coordinated operation.

Jan 1, 1969

By A. Tanaka, K. G. Carroll

The existence of local room-temperature plastic flow in germanium, which has been a subject of controversy for nearly two decades, has recently received renewed attention, albeit no more agreement than hitherto. Phenomenologically one major facet of the problem has been reduced to the question whether or not indentation can be effected in germanium without the introduction of cracks. That plastic flow can be induced at room temperature by fracture appears to have been rather convincingly demonstrated recently by Suzuki and Kamada and by Noble and Henisch.1 The literature contains both direct and incidental references to Vickers and Knoop indentations showing no cracks, within resolution of optical microscopy. Recently, however, following a controversy on the subject,2,3 johnson4 made a study of indentations produced by spherical indenters and concluded that these are accompanied by cracking. This study in-

Jan 1, 1969

By D. W. McGlashan

Zeta potential changes were determined as a function of pH, metal ion, and surfactant concentrations. Prom the analysis of data, flotation experiments were carried out to correlate float-ability with the differences in zeta potential. Cassiterite in water bears a negative zeta potential, The zeta potential of cassiterite is sensitive to pH changes; the electric double layer arises from the preferential adsorption of H+ and OH- ions and subsequent ionization of the hydroxylated surface. It is suspected that hydronium-ion concentration may cause reversal in the sign of the zeta potential. The ZPC was found to occur at pH 3.4. Metallic ions and the hydrated ions thereof affect the zeta potential of cassiterite in differing degrees of intensity. Without prior activation, sulfonated surfactants do not change the zeta potential of cassiterite. Sodium alkyl aryl sulfonate is especially active on lead-activated cassiterite and ferric-activated cassiteriten Microcalorimetric fiests confimed the activity of ions on cassiterite and showed the hydrated character of cassiterite smfaces. Close correlation between zeta potential and microflotation results was achieved.

Jan 1, 1969

By Rees D. Rawlings, C. W. A. Newey

The aging characteristics of an Fe-11 at. pct Mo alloy have been studied by means of light metallography together with density, Young&apos;s modulus, and hardness measurements. The results were consistent with the precipitation of a single intermetallic compound during aging; overaging was slow relative to that in other iron-based binary alloys. The solution treatment temperature had a small effect on the rate of hardening whereas deformation prior to aging had a marked effect on both the rate of hardening and the peak hardness. The density data indicate that the compound precipitated is Fe3MO2 and not the Laves phase Fe2Mo. Analysis of the modulus and density results gave values for the time exponent for precipitate growth of approximately 1.0 and 1.5 for the alloy aged with and without prior deformation, respectively. DETAILED studies of precipitation hardening in bcc matrices have been confined largely to the effects of carbides and nitrides. In view of this and the growing technological interest in intermetallic compound strengthening, e.g., in maraging steels, a study of precipitation in iron-based alloys with a low interstitial content has been undertaken. This paper is concerned with the aging behavior of an Fe-11 at. pct Mo alloy; the mechanical behavior of the alloy will be reported later. The early work of sykes on Fe-Mo alloys showed that precipitation of the intermetallic compound was accompanied by an increase in hardness and a decrease in volume of the material. More recent surveys of the strengthening associated with precipitation have been made3-5 and, in particular, Elsen and wassermann4 showed that deformation prior to aging increased the rate of hardening. These latter workers also followed the precipitation process by means of dilatometry, electrical resistivity, and lattice parameter measurements. Their results confirmed that there is a decrease in volume on aging. Except for the work of Hornbogen on an Fe-20 at. pct Mo alloy, neither clustering nor the precipitation of a nonequilibrium phase has been observed in Fe-Mo alloys. Studies of alloys of lower molybdenum content475 indicate that the equilibrium intermetallic compound is precipitated during aging. However, there is some doubt concerning the nature of the equilibrium precipitate phase. According to the phase diagram constructed by Hansen,8 the phase should be precipitated. This phase has a rhombohedra1 crystal structure which is characterized by the formula Fe706,&apos; although the composition of the molybdenum-rich boundary corresponds approximately to Fe3Mo2. The version of the diagram proposed by Sinha, Buckley, and Hume-Rother indicates that the A phase, a Laves phase Fe2Mo, should be precipitated. Their observation of a Laves phase supports the earlier findings of Bechtoldt and Vacher,13 although, in a recent study of the system by means of diffusion couples, Rawlings and Newey did not detect the phase. The work presented here describes the effect of solution-treatment temperature, aging temperature, and prior deformation on the aging characteristics of the alloy as revealed by light metallography together with hardness, density, and Young&apos;s modulus measurements. In addition the density data are used in an attempt to determine the compound precipitated during aging. EXPERIMENTAL PROCEDURE A 29-kg ingot of the alloy was cast at R.A.R.D.E., Fort Halstead, from deoxidized, Japanese electrolytic iron and sintered molybdenum. The ingot was homogenized for 6 hr at 1473°K and then worked, with intermediate anneals, into 6- and 16-mm-diam rods and 6-mm plate. Chemical analysis of the alloy gave, wt pct: Mo, 17.5 (11 at. pct); C, 0.003; Si, 0.002; S, 0.005; P, <0.002; and02, 0.0098. Solution treatments were carried out under a dynamic argon atmosphere in a vertical, "crusilite" element, furnace which had a facility for rapid quenching into iced water. Except for the study of the effect of solution treatment temperature, all specimens were solution-treated at 1573" * 2°K for 1 hr. Salt baths were used for the aging treatments. Specimens for hardness, density, and Young&apos;s modulus measurements were produced, after heat treatment, from the stock rod or bar using a precision silicon carbide slitting wheel. As described later, the quenching treatment produced local plastic strain in the stock material; consequently, care was taken to ensure that the specimens were not prepared from these regions. Those specimens used in the studies of the effects of prior deformation on the aging behavior were strained in compression in a Denison universal testing machine. Specimens for light metallographic observations were mechanically polished on successively finer grades of diamond paste down to and then etched in either alcoholic ferric chloride or in a 2 pct nital solution. Vickers diamond pyramid hardness data were obtained using a 30-kg load. At least five impressions were averaged for each determination. Density measurements were made using a displacement technique in which each specimen was weighed in air and in dibromoethane at 296°K. The specimens were cylindrical and weighed 3 to 4 g; all weighings were made on a balance reading to 1 x 10"5 g. For each specimen the mean value of five weighings was used to calculate the density. The density of the dibromoethane was determined using the displacement procedure and a standard nickel specimen. The error in an absolute density value was estimated to be HI.01 pct. To obtain the density as a function of aging time a single specimen was used and the density meas-

Jan 1, 1969

A new test coke oven of seven cubic foot capacity is described. The oven was designed to simulate conditions in a central section of a battery oven and a special feature is the achievement of unidirectional heating from the flues on either side of the charge. The method of charging permits close control of charge conditions&apos;such as bulk density and moisture content. These conditions, as well as coking conditions (e.g. flue temper- atures., coking time) must be varied to simulate conditions in different batteries, The effects of several variables on coke quality are discussed. Using test oven conditions corresponding to those of Newcastle steelworks batteries, good agreement was obtained between strength indices of test oven and battery cokes; for 17 tests, the average A.S.T.M. stability and hardness indices for the test oven coke were 38,5% and 69.7%, while those for the battery coke were 37.1.% and 67.6%.

Jan 1, 1969

By A. U. Seybolt

Experiments on both suljidation and hot corrosion have been carried out using ternary Ni-Cr-X alloys and commercial nickel-base superalloys. It has been shown that lhere are certain micro structural similarities between sulfidation using H,S/H2 mixtures and hot corvosion using Na,S04 in "crucible" experiments or hot corrosion tests using a flame tunnel apparatus. It is proposed that two key processes in the hot cowosion process are: 1) formation of chromium sulfides which deplete the alloy matrix, and 2) oxidation which can be accelerated because of chromium depletion. Other processes play an important role in the hot corrosion process, such as accelerated oxidation attack due to the presence of a N& S04 or N&SO,- NaC2 film which inhibits the formation of a protective external oxide scale. However, this latter phenomenon was not studied in this work. THE term hot corrosion has come to mean a combination of sulfur and oxygen attack on nickel-base or cobalt-base superalloys used as gas turbine blades or partitions. This attack can be initiated by any combustion process in air involving fuel containing sulfur if the sulfur level is sufficiently high. Levels of 5 pet SO2l for example, in the combusting gas have been observed to produce hot corrosion attack on nickel-base alloys. The important immediate corroding medium in aircraft gas turbines, however, has been established to be Na2S04, formed from reaction between NaCl from sea air and sulfur in the fuel.&apos; The Na2S04 concentrates the sulfur sufficiently so that superalloy parts heated in the range 1400" to 1900°F can become sulfided by reducing the Na2S04 film which forms on the parts, and this reaction allows sulfur to gain access to the alloy. The sulfur thus released diffuses into the superalloy and forms primarily chromium sulfides of various compositions, but frequently Cr2S, has been identified. Figs. 1 and 2 show the morphology typical of hot corrosion of a cobalt-base superalloy X-45 (25 Cr, 10 Ni, 7.5 W, 0.25 C) and a nickel-base alloy, Udimet 500 (19 Cr, 19 Co, 4 Mo, 3 Ti, 2.9 Al, 0.07 C). Both alloy samples were subjected to the same hot corrosion conditions: 616 hr at 1600°F in a combusted 2.9 pct S distillate oil containing 125 ppm Na as NaC1. It will be noted at once that the nickel-base alloy is much more severely attacked. The depth of corrosion is much greater and the number and size of the sulfides present are much greater. Both alloys show a duplex oxide scale, which is more noticeable in the X-45 alloy. The external scale is probably a spinel in both cases, with CrQ3 lying next to the alloy. Many investigators1 -"ve been concerned with hot corrosion phenomena, but there has been a lack of unanimity of opinion as to the details of the hot corrosion mechanism. More than one definition of hot corrosion is possible. Some investigators con- sider as a measure of hot corrosion only the weight gain due to an accelerated oxidation. However another point of view is that the total depth of affected alloy may be used as a measure. While it is recognized that surface oxidation attack is greatly accelerated by the presence of salts like Na2S04 or Na2S04-NaC1 mixtures, sulfur penetration into the alloy also undoubtedly produces very important effects. The region of sul-fide penetration which is so prominent in Fig. 2 is one of the outstanding characteristics of hot corrosion. For highly stressed parts, such as first-stage buckets, this sulfur-penetrated region can be more significant in mechanical property loss than the reduction of cross section produced by the formation of the massive external scale. In addition, evidence will be presented that this sulfided region can be less resistant to subsequent oxidation attack. Since it appears that the sulfided region below the surface oxide scale plays an important role in the overall corrosion process,

Jan 1, 1969

By T. H. Ramsey, Richard Shield

A process has been developed for fabricating thin-film resistors that are compatible with integrated circuits. Films are produced by evaporation of single refractory metals using an electron beam heating source. Resistor paths are then made using standard photoresist etching techniques. A low-temperature coefficient of resistance is obtained by control of nucleation during deposition of the film. One application of the process has been the development of a discrete resistor used for current setting in linear integrated circuits. Multiple thin-film resistors were formed on oxidized silicon substrates using molybdenum metal as a source. An evaporated protective layer of SiO2 over the resistor prevents resistance changes which might occur during subsequent high-temperature processing. Properties of a typical resistor are as follows: R = 15.7 ohm per sq, tolerance surface dimensions = 0.028 by 0.028 in., stable after 4000 hr at 0. 75 w without heat sink. THIN-FILM resistors have been investigated for many years with a large selection of usable resistors resulting from a wide variety of materials. Many of the processes necessitate a high degree of complexity but in nearly all cases the conclusions have been that the materials used in each case were acceptable provided the deposition process was reproducible and could be controlled sufficiently to give the required tolerances. It is our opinion that simplicity is still the key to thin-film resistor fabrication. In this regard, the single metal is obviously the simplest process to control, provided all the necessary properties can be obtained. The idea is not original in this laboratory by any means. Others have taken this approach.&apos; It has been demonstrated that a fairly wide range of resistivities can be obtained by careful control of deposition parameters for any given metal, and by selection of several single metals a very broad range of stable resistors can be obtained. The transition from one metal to the next is made when a film becomes too thin for adequate process control or long-term stability. A great deal of emphasis is once again being placed on the thin-film resistor. Although they have been thoroughly studied in the past, new applications have been found that require the properties obtainable only from thin-film resistors. Integrated circuits, in general, are advancing toward higher speeds and radiation environments which require replacement of the present diffused resistors. Linear circuits in particular are requiring high-power, high-precision resistors for the more advanced applications. The particular requirements of some linear circuits are such that a discrete resistor is required. The resistor described in this paper was developed as a 15.7-ohm precision discrete resistor for use in a current regulating circuit requiring a +2 pct end of life overall tolerance, a dissipation of 750 mw, and the ability to operate over a fairly broad temperature range (i.e., a low temperature coefficient of resistance, TCR). State-of-the-art integrated circuit and silicon processing technology lends itself well to the fabrication of thin-film resistors. Not only is the resistor thin film well-suited to integration on individual circuits, but the oxidized silicon surface provides one of

Jan 1, 1969