By R. Kerby, T. R. lngraham

The rates of cadmiuln cementation from buffered solutions were studied on both the cylindrical and circular faces of a rotating zinc disk. The activation energies are equivalent on both surfaces, but the rate is more rapid on the cylindrical face. At higher temperatures and at pH values above 6.4, the rate of deposition increases because of an increase in the cathodic area of the deposit. The rate may also be increased by decreasing the thickness of the diffusion layer by rapid stirring. The presence of small amounts of copper, cadmium, lead, iron, or aluminum in the zinc does not affect the cementation rate, but when srnall amounts of copper, cobalt, and arsenic were present in the solution cadmium deposition ceased shortly after it started. Small amounts of copper in solution become cemented with the cadmium to form a coarse deposit of Cd3Cu. When zinc ores containing cadmium are processed for electrolysis, the cadmium appears with the zinc in the leach liquors. Because of the discharge potential of the cadmium ion and the hydrogen overvoltage on metallic cadmium, the cadmium ion must be removed prior to zinc electrolysis to prevent its codeposition. Cadmium is usually removed from acidic zinc sulfate solutions by cementation on zinc. When zinc sheets are used with the appropriate conditions of pH and temperature, a finely divided, high-purity cadmium powder is obtained; it floats to the surface with attached hydrogen bubbles and, after careful washing, may be processed directly to a marketable product.' The reaction on zinc sheets is relatively slow because of the limited amount of exposed cathodic area on the sheets. A much more rapid reaction is obtained when zinc powders are stirred into the solution, but this procedure does have a potential disadvantage: some unreacted zinc may be trapped in the cemented cadmium and thus lower its grade.1 The equilibrium constant at 25°C for the displacement of cadmium by zinc is of the order of lo", which indicates that at equilibrium the displacement would be essentially quantitative and no back reaction need be considered. This indication is not entirely true, however, because in the presence of oxygen any loose cadmium which is out of contact with metallic zinc tends to redissolve after cementation.' The overall effect is much the same as that to be expected if the equilibrium constant were much smaller. Previous experimental work on cementation reac- tions3 is in general agreement that the rates of cementation usually follow first-order kinetics. The metal on which cementation occurs is considered to consist of anodic areas from which metal dissolves and cathodic areas onto which the reactive metal is cemented. For the reaction to continue, the cemented deposit must remain open and porous for the removal of ions. Usually, the deposited metal influences the rate of cementation; when it blocks the pores in the deposit, the rate of cementation will be decreased. Alternatively, when the cemented metal grows as den-drites or as coarse powder the cathodic area is correspondingly increased and the rate of cementation increases,3 Thus, it is only during the initial stages of cementation, prior to the development of deposit effects, that the kinetic behavior of the reaction may be studied without ambiguity. In this paper, experiments will be described for cementation of cadmium from dilute solutions onto the surface of a rapidly spinning zinc cylinder. The effects of ionic concentration, disk rotation speed, temperature, and impurities will be described. APPARATUS AND PROCEDURE The apparatus used for the experiments was described in a previous paper.4 It consisted of a 2-liter vessel in which the contents were protected, against oxidation, by a stream of prepurified nitrogen. The vessel was immersed in a water bath which controlled

Jan 1, 1970

Thermodynamic properties of the solutions of hydrogen in metals and carbon in austenite were investigated and it is possible to predict the interstitial solubility in these systems over relatively wide ranges of temperature and solute activity. Monte Carlo methods were used to compute the arrangements of interstitial atoms on the tetrahedral sites in body centred cubic metals and the octahedral sites in face centred cubic metals. It was shown that the non-configurational entropies of solution of hydrogen in metals can be interpreted as being principally vibrational and on this basis the potential value of the isotopic solubility ratio theory in indicating the compositional variation of these non-configurational entropies was discussed. The need for future work along these lines is pointed out.

Jan 1, 1970

By R. M. Hays

At the present time, oxidized taconite and semitaconite are not processed on the Mesabi Range except in vely limited tonnages. However, it is estimated that by 1990 shipments from the Range will approach 75 million tons of iron ore per year. To achieve this and future production, either additional magnetic taconite reserves must be proven or oxidized taconite and semitaconite must be processed. One beneficiation process which uses high-intensity magnetic separation and flotation for concentrating oxidized taconite and semitaconite is described. Detailed metallurgical results are given and an economic evaluation of the process is presented with comparison to other processes. The results of the present study indicate that the high-intensity magnetic separation and flotation process appears nearer commercialization for the processing of Mesabi Range semitaconite. The disadvantages of the process are nearer solution and are being solved by well-defined programs. During the twentieth century, the Mesabi Range in northeastern Minnesota has been the main source of iron ore for American steel mills. The Mesabi Range, which is about 120 miles long and up to 3 miles wide, is the pre-glacial outcrop of a group of sedimentary iron-bearing rocks known as the Biwabik formation. The formation, which is 200 to 650 ft thick and dips 50 to 10° to the southeast, is divided into four stratigraphic units. From top to bottom, these are the Upper Slaty, Upper Cherty, Lower Slaty, and Lower Cherty. Since its deposition in Precambrian time, most of the original Biwabik formation has been subject to alteration. Thus, although the iron content of the original formation was quite uniform, major variations in mineral composition now occur both laterally along the length of the formation and vertically within its units. Details of the mineralogical variations in the Biwabik formation have been described by Wolff,' Gruner, 2 and White.3 The unaltered portion of the Biwabik formation includes the magnetite taconites which are being commercially processed by Reserve Mining, Erie Mining, Eveleth Taconite, National Steel, Butler Taconite, and U.S. Steel. These six operations have a capacity of 32 million tons of iron ore pellets per year and have produced approximately 170milion tons of pellets since 1956. Capacity for another 30 million tons of pellets per year is being considered by the industry for the next ten years. This increase will be obtained by constructing new plants and by expanding present operations. Thus, by ! 978, it is estimated that approximately 60 million tons of iron ore vellets will be produced each vear from the magnetite taconites of the Biwabik formation. The portions of the Biwabik formation subjected to intense alteration resulted in direct shipping, wash, and heavy-media ores. Since 1892, 1.8 billion tons of direct shipping ore have been shipped from the Mesabi Range. This ore has been the major source of iron ore for American steel mills. In 1967, about 11 million tons of direct shipping ore and 13 million tons of wash, jig, heavy-media, and other gravity concentrates were shipped from the Mesabi Range.4 These products generally have poorer physical and chemical properties than the iron pellets produced from magnetic taconite. It is predicted that the shipment of these materials will decrease from 24 million tons in 1967 to 6 to 8 million tons in 1975.' This decrease will

Jan 1, 1970

By M. R. Lorenz

Efficient visible light emission from p-n junctions in semiconductors is currently achieved in the four materials, Sic, GaP, ]Ga1-xAs and GaAs1-x,. Recent advances in materials preparation and p-n junction formation are briefly reviewed. The radiative recombination processes in the different materials depend largely on the band structure and the impurity states of each material. The spectral distribution of the emission ranges from the blue in Sic, to green in Gap, yellow in Sic and red in Gap, Ga1-x AlxAs and GaAs1-x Px. The origin of the various processes are discussed. The conversion of the electrical power into optical power and the measurement of the conversion efficiency are reviewed. The currently maximum quantum efficiencies at 300°K are: 3 pct in GaP(red), 1 pct in SiC(yellow), 0.1 pct in GaP(green), 0.2 pct in Ga1-x AlxAs at 66001, and 0.1 pct in GaAs1-x Px at 6800. The brightness and the interplay of the quantum efficiency and the luminous efficiency are given detailed consideration. VISIBLE light generated by the application of a direct current to a semiconductor crystal was first observed by Lossev1 in 1923. Light emission came from naturally occurring junctions in Sic crystals but little was known then with regard to the mechanism of charge transport and light emission. Some nearly 30 years later and with a vastly increased understanding of semiconductors the phenomenon of electroluminescence was studied in more detail, for example in p-n junctions of germanium.2 In these early studies, the efficiency of converting the electron current into a photon current was very low and therefore aroused little interest toward practical application. More recently it became apparent that in certain materials, for instance GaAs, and under certain conditions, the conversion efficiency was not low at all.3 The subsequent discovery of the p-n junction laser4-6 provided the impetus for increased studies of electroluminescence. Light emitted from GaAs occurs in the infrared region of the electromagnetic spectrum and is not visible to the eye. At nearly the same time the use of GaAs1-xPx led to laser action at low temperatures which was visible to the eye.7 Later a red light emitting diode, made from Gap, was reportedS which emitted incoherent radiation at 300°K with an external quantum efficiency of about 1.5 pct. The fact that such efficient devices were obtainable led to a more concentrated effort in the search for highly efficient room-temperature semiconductor light sources. It is some of this later work on p-n junction luminescence with which we will be concerned here. Since our aim is centered on visible light, with hv =1.8 ev ( ?=7000?), only the wider band gap semiconductors are of interest, i.e., Eg 1 1.8 ev. Although many compounds meet this criterion, only a limited number of those are also good semiconductors, i.e. contain low resistance n and p regions. Some of the more promising candidates are listed in Table I. We will only be concerned with light generation from a p-n junction. This limitation excludes essentially the group II-VI binary compounds, although we will briefly review the case of ZnTe and the solid solution ZnTe1-xSex. As we will show they may contain a p-n junction but only of a special kind. Most of the discussion will deal with the four materials, Sic, Gap, Gal-xAlxAs, and GaAs1-xPx. These appear to be at the present time the best visible light emitting semiconductors. In the following sections we will briefly consider: 1) the electrical properties of p-n junctions; 2) some recent advances in materials preparation; 3) the formation of p-n junctions; and then in somewhat greater detail we will consider: 4) the various radiative recombination processes; 5) the measurement and observation of the external quantum efficiency; 6) the luminous efficiency; 7) the brightness of light emitting diodes (LED'S). THE P-N JUNCTION The p-n junction in a semiconductor crystal is the interface between two differently doped regions. More specifically the p region is doped predominantly with acceptor impurities and the n region contains predominantly donor impurities. The energy band structure of a degenerate p-n junction at thermal equilibrium is shown in Fig. l(a). The excess electrons on the n side of the junction are confined to this region by the barrier potential Eg. Similarly the excess holes on the p-side of the junction are confined to the p-region by a similar potential barrier. If we now apply a dc voltage V such that the p region is made positive and the n region negative, the barrier potential EB is reduced by the applied voltage, V and the junction is said to be forward biased. With the barrier potential lowered, electrons and holes can drift toward the p region and n region, respectively, see Fig. l(b). The current voltage characteristics of p-n junctions in most wide band gap materials can be described by the relation: J = Joexp(eV/BkT) [1] where the functional form of Jo is determined by the recombination mechanism. Jo is generally a complicated parameter which depends on a number of different factors including temperature, junction width, bias voltage, and carrier lifetimes. The parameter B also depends on the recombination mechanism but

Jan 1, 1970

By J. L. Wright

When management is confronted with the risk of constructing a waste disposal well, these are some of the questions which may arise. Should the company expand the present waste treatment plant? More lagoons will cut into valuable acreage which might be needed later, and yet the pollution engineer says he can guarantee results. On the other hand, does the formation being used for those successful disposal wells off to the west extend over far enough to be used for the company's own well? Will the formation be thick enough? Will it be too deep? Will it be porous and permeable enough? Apart from needing to make a profit on the products made at the plant, plant officials must sometimes act under pressure to comply with pollution standards. The manager must build the cost of the pollution control system into the price of the products made by the company.

Jan 1, 1970

By Marcus Digre

The autogenous grinding method has been progressively employed in mineral dressing plants during the last 15 years. The term has been used with somewhat different meanings (1), (2), (3). In this paper the author will use it in the most restricted way, for processes where run-of-mine ore (rock) in one step is reduced to a grind product by the action of the ore itself without any other grinding media present. The pebble grinding process where the major part of the ore enters the mill as finely crushed product which is ground further with selected coarse ore pieces acting as grinding media, is not considered autogenous grinding. Processes where a minor amount extraneous media as steel-balls is added to supplement an autogenous mill charge will be called semiautogenous. Other terms need also to be defined. "Mill charge" will be used about the active part of the mill content which performs the grinding, that is the steel balls in ball grinding and the coarse ore pieces in pebble and autogenous grinding. The interstitial nearly finished material is not included in the term "mill charge", and for the wet grinding operations is called the "mill pulp' The term "pebble" will be used for any rounded ore or rock piece in the mill charge whether it is an autogenous or a pebble grinding operation.

Jan 1, 1970

By W. H. Fertl, S. J. Pirson

Well logging techniques, as used successfully in oil and gas exploration, can also be used to give a detailed evaluation of drill holes through industrial mineral deposits such as sulphur. This paper describes the logging tools used gives the theory behind the well-log interpretation and discusses the application of the method in sulphur-bearing limestone and m more complex sulphur deposits.

Jan 1, 1970

By Barry D. Lichter, Pierre Sommelet

High-temperature heat contents of InSb, GaSb, and AlSb were measured over the temperature range 400" to 1450°K using a diphenyl ether drop calorimeter. Smoothed ualues of the thermal properties, H$ - H:9s, have been derived and are tabulated at even temperature intervals. The heats of fusion of the three compounds were determined as, respectively, 5707 *100, 7780 * 100, and 9800 5 3011 cal per g-atorn at the determined melting points of 797" l°, 985" * , and 1330" * 5°K. The calculated entropies of fusion are, respectively, 7.16 0.12, 7.90 * 0.11, and 7.37 * 0.23 cal per deg per g-atotn. The heat capacities increase substantially on tnelting in contrast to the behauior of structurally related germanium and silicon. Deriations from the Kopp-Neumann rule are negative for solid compounds and positive for the liquid phases. Previously obsevrrd "post melting" in InSb is confirmed. The high-temperature thermal properties of 111-V compounds are presently not well-established, despite the technical importance of these semiconducting cbmpounds. Uncertainties in available heats of fusion and heat contents have seriously hampered thermo-chemical evaluations' and thermodynamic analyses of phase equilibria2"" in these systems. This paper reports results of high-temperature heat content investigations of InSb, GaSb, and AlSb measured in the range 400" to 1450°K employing a diphenyl ether drop calorimeter. Similar measurements for InAs and GaAs will be reported in a following publication.~ EXPERIMENTAL PROCEDURES Samples. High-purity samples of the compounds InSb and GaSb were supplied in the form of crushed crystal fragments by Dr. Carl Thurmond of the Bell Telephone Laboratories and in the form of single crystals by Dr. A. Strauss of the M.I.T. Lincoln Laboratory. Single-crystal samples of semiconductor-grade AlSb were supplied by Dr. W. P. Allred of the Bell and Howell Research Center. Chemical analyses indicated that all compounds were stoichiometric to *0.1 at. pct, which is within the experimental uncertainties of the analyses. Samples were crushed, weighed, and encapsulated in evacuated, thin-walled, fused silica capsules. The capsules were nearly identical in external shape, 2 cm by 2 cm diam, but varied in weight due to differences in wall thickness. One sample of AlSb was contained in a thin-walled, high-purity alumina cup encapsulated in silica and used for heat content determinations of liquid AlSb. The capsule materials showed no visual evidence of reaction with any of the compounds. The sample and capsule weights are given in Table I. Calorimeter. A Bunsen-type calorimeter, similar in design to a previously described instrument6 but employing diphenyl ether (C6H5)'0 as the calorimetric substance, was used for measurements of heat contents above 300.0°K, the melting point of diphenyl ether. Heat input to the calorimeter caused isothermal melting of diphenyl ether, and the resulting increase in volume was measured by displacement of mercury from the calorimeter into a 200 cm horizontal, calibrated capillary, 1.25 * 0.01 mm diam, or into a weighed beaker. The advantages of diphenyl ether over water have been previously pointed out7 and include: i) an increase by a factor of 3.5 in sensitivity as measured by the ratio of the volume change to the enthalpy change on fusion, ii) the smaller required extrapolation from the melting point to the standard temperature of 298.17"K, and iii) the positive volume change on fusion of diphenyl ether in contrast to the contraction which occurs on fusion of ice. Diphenyl ether was purified by fractional crystallization to 99.95 mol pct as determined from the melting point depression with fraction crystallized. During assembly of the calorimeter, the ether was repeatedly outgassed under high vacuum to remove dissolved air. The calorimeter receiving vessel consisted of an 8-in.-long by 1:-in.-diam copper tube with twelve horizontal 3-in.-diam radiator "fins" for dissipating heat to the surrounding mantle of diphenyl ether. Before forming the mantle the chamber surrounding the receiving vessel contained 3300 cu cm of liquid diphenyl ether above 250 cu cm of mercury which was

Jan 1, 1970

By R. J. Reynik

A semiempirial small flunctation theory of diff- sion in liquids is presented, which employs a fluctuation energy assumed quadratic for a small atomic or molecular displacement and Einstein's random-iralh model. The resulting diffusion equation is given by In these equations. D is the diffusivity, is the average liquid shite coordination number (at interatomic distance d. cm. T is the absolute temperature, xu. em, is (the diffusive displacement. K, is the quadratic fluctuation energy force constant, and rg, cm, are the radii oj diffusing atoms A and B, respectively. The quantities Xn and K are calculated from the computer-filled values of the slope and intercept. respectively. The radius of self-diffusing atom or radii and of diffusing atoms A and B are eta United and compared with values reported in the literature.. The predicted linear variation of diffusivity with. It tempera lure htm been observed in approximately thirty-iire metallic liquid systems, and in over seventy-fiee other liquid systems, including the organic .alcohols, liquified inert gases, and the molten salts, ALTHOUGH the average density within a macroscopic volume element of liquid is constant for fixed total number of atoms. pressure. and temperature, there exist microscopic: density fluctuations within the respective volume element. As such the microscopic volume available to an atom and its Z first nearest neighbors at any instant of time fluctuates above and below the average volume available to these atoms. If one assumes that liquid state atoms vibrate as in a solid. and further postulates that the mean position of any atom in the liquid state is not stationary. but shifts during every .vibration a distance 0 5 j 5 xo. then every atom in the liquid state continuously undergoes diffusive displacements which vary in the range 0 5 j 5 ro. Mathematically. for a binary liquid system consisting of atcrms A and B. the maximum diffusive displacement. .YO, is defined by the equation: where d is the average liquid state interatomic distance at specified liquid state coordination number Z. and v~ \ and vg are the effective radii of diffusing atoms A and B: respectively. For self-diffusion. r^ equals rg , and Eq. [I.] reduces to: It is interesting to note that Eq. [l] or [2] can be used to compute the radii of the diffusing atoms, provided one had an experimental evaluation of xo. As such. the computed radii could be compared with metallic or crystallographic ionic radii to ascerlain the electronic character of the diffusing atoms. Thus it is proposed that in the liquid state the n~otion of an atom relative to its original equilibrium position of oscillation represents the thermal vibration of any atom and its Z first nearest neighbors. while the small and variable displacements. 0 5 1 5 xc,. of the centers of oscillation represent the complex diffusive motions of the atoms at constant temperature and pressure. This is consistent with data obtained from slow neutron scattering by liquids1 ' and resembles an itinerant oscillator model of the liquid state.'" It is further postulated that the atomic displacements characterizing the liquid state diffusion process are essentially a random-walk process. As such. it nlay be described by Einstein's equation:' where D is the diffusivity. sq cm sec-'. j2 is the mean square value of the diffusive displacement. and i> is the frequency of density fluctuations giving rise to diffusion. FORMULATION OF DIFFUSION EQUATION The effective spherical volume occupied by an atom, as a consequence of a microscopic density fluctuation which enlarges the volume available to any atom, exceeds its average liquid state atomic volume by an amount: where AV is the enlarged spherical volume, v is the radius of the diffusing atom. and j is the elementary displacement distance from the original center of oscillation of the vibrating atom to a new center of oscillation position. For small atomic displacements. where c is a constant whose value depends upon the assumed geometry of the enlarged volume. For a spherical increase in volume, c equals 4nr2. Following the treatment of Furthl' and ~walin." assuming the enlarged volu~nes AL7 for the diffusing atoms are distributed in a continuunl. the probability of finding a fluctuation in the size range 0 5 j 5 xo defined by Where c includes the geometric constant cl and Eij) is the fluctuation energy causing the volume change. But the proposed model assumes all the Z first nearest-neighbor atoms are centers of oscillation. and hence the probability that any of these atoms is adjacent to a fluctuation of magnitude 05j5xo is unity. Thus:

Jan 1, 1970

By William Y. Mo

This report presents preliminary results of a study undertaken to investigate quantitative characteristics of the demand for steel mill products and its major end-use components. The major end uses included in the study are the steel mill products used in construction, in automobiles, in producer durables, and in consumer durables. The main objectives of the research underlying this study are as follows: (1) To formulate and estimate the empirical demand relations for steel and the four major end uses in the United States; (2) to measure and calculate the responsiveness of the U.S. per capita steel consumption with respect to the changes of the steel and other nonferrous metals prices; (3) to determine and quantify the relative importance of the underlying demand explanatory factors in contributing to the average year-to-year increases (or decreases) of the U.S. per capita steel consumption; and (4) to adapt and use the estimated demand relations in making projections of the U.S. future demand for steel and the major end-use components. After extensive preliminary investigation, three versions of simple linear demand relations are selected and estimated by means of ordinary least squares (OLS) method. The annual data for the period 1947-65 are used in the estimation. Direct and cross price elasticities of demand are computed for each of major end uses. The relative importance of demand explanatory factors in contributing to the average year-to-year changes of U.S. per capita steel consumption are also calculated. For making projections, a simple autoregressive time trend model is used in estimating the future values of independent variables. Since the estimated demand relations are valid for projections only if the estimated parameters can be assumed to be unchanged in the future, and consequently, the projections derived in the study should be interpreted accordingly.

Jan 1, 1970

By B. C. Allen

Grain boundary grooving has been studied in chromium, molybdenum, and tungsten under a variety of conditions using high vacuum techniques and tantalum -gettered argon. The average surface free energy of solid chromium, and the chromium-liquid silver interface free energy were respectively found to be 2200 ± 250 and 500 i 130 ergs per sq cm from groove formation kinetics and estimates of pertinent volume difffusion coefficients. The results for chromium were unffected by variations in interstitial content ranging from 0.003 to 0.09 pct C, or 0.003 to 0.03 pct O. Surface diffusion is the primary mechanism of groove formation in chromium under 1 atm argon at 1200" to 140O°C, and is essentially unaffected by 0.003 to 0.09 pct C, 0.003 to 0.03 pct O , metastable nitrogen contents up to -0.01 pct, and up to 2 torr Ag vapor. At higher temperatures, the major mechanism is volume diffusion in argon or evaporation-condensation in stutic vacuum. Surface diffusion occurs in molybdenum at 0.5 to 0.96 and in tungsten at 0.5 to 0.9 of the absolute melting tempera -ture by a single mechanism, possibly by the migration of single adatoms or vacancies. Results were slightly affected by up to 23 tory Sn vapor, and in molybdenum were essentially unaffected by 0.5 Ti or carbon in the range 0.002 to 0.02 pct. Volume difffusion through the liquid is the mechanism of groove formation in chromium-liquid silver at 1200" to 1400°C and in molybdenum-, Mo-0.5Ti-, and tungsten-liquid tin at 1200" to 2000°C. The solid-liquid interface free energies involved were estimated from grooving kanetics. WHEN a grain boundary intersects a solid surface, a groove tends to form along the line of intersection at temperatures above about half the absolute melting point (0.5 TM). The groove progressively grows by preferential atomic migration either by diffusion or evaporation. Establishment of a groove angle occurs in accordance with the grain boundary and surface free energies involved. The motivation for groove formation is a reduction in the total surface free energy of the system. This study is a continuation of previous work on thermal grooving of chromium, molybdenum, and tungsten.&apos; The temperature ranges were extended, and the effect of metallic and interstitial impurities was evaluated. The results were such that certain interface free energies and surface self-diffusion coefficients were deduced from the grooving kinetics. EXPERIMENTAL WORK Materials and Preparation. As indicated in Table I, the 0.05-0.08-cm-thick chromium, molybdenum, and tungsten sheet used was nominally 99.99 pct after recrystallization. Two lots of molybdenum with about the same analysis, Mo-0.5Ti,* and tungsten were ob- *Alloy compsitions are expressed in weight percent . tained commercially. Extruded chromium rod,&apos; prepared from iodide process crystals, was warm rolled to sheet at 700°C. Sheet of three Cr-0 impurity alloys containing up to 0.03 pct 0 was prepared by warm rolling arc melted, extruded, and swaged rod. Two Cr-C impurity alloys containing up to 0.09 pct C were made by equilibrating unalloyed chromium with a known amount of CH4 for 24 hr at 1150°C in previously evacuated quartz capsules. Chromium containing nominally 0.015 and 0.06 pct N was similarly prepared by equilibration with NH3. The sheet was recrystallized to give a stable grain size about equal to the sheet thickness. Molybdenum and Mo-O.5Ti were recrystallized in a tantalum resistance furnace 1 hr at 1 x lo-5 torr at 2300" and 220O°C, respectively. Tungsten was similarly annealed for 1 hr at 2500°C. Chromium and its impurity alloys were outgassed at 1100°C and recrystallized 1 hr at 1700°C under 1 atm Ar. Except for nitrogen, the impurity content stayed roughly constant. Nitrogen in both alloys was reduced to <0.001 pct. In fact, over 80 pct of the added nitrogen was lost after outgassing at llOO°C and annealing sheet 1 hr at 1300°C in argon in the presence of tantalum. Such a rapid loss can be rationalized since -2 torr N are required for equilibrium with 0.04 pct N in solution,3 while the equilibrium pressure is ~10-5 torr over tantalum at 1300°C.4 The recrystallized sheet was cut into small coupons which were metallographically ground and polished on one side with a minimum of grain boundary relief. The surface roughness was on the order of 0.01 µ. The tin and silver used were nominally 99.999 spec-trographically pure. After being outgassed at 1100°C and equilibrated in a molybdenum crucible for 0.5 hr at 1800°C in argon, the tin contained 3 ppm 0, <0.3 ppm N, and 0.1 ppm H. Following outgassing at 900°C and equilibration in a chromium crucible 1 hr at 1400°C in argon, the gas content of the silver was 1 ppm O, <0.5 ppm N, and 0.3 ppm H. Grooving Under Argon or Vacuum. All specimens were placed in unsealed containers made from rod or sheet of the same alloy, thereby enabling the polished surface to achieve gas-solid equilibrium. The annealing fixtures are shown in Fig. 1. The specimen was placed in a resistance furnace with a tantalum or Ta-10W heating element plus tantalum fixtures or radiation shields. Chromium was outgassed at 1100°C, and molybdenum and tungsten were outgassed at 1900°C to 1 x l0-5 torr or at the grooving temperature, whichever was lower. In vacuum anneals, the specimen was then heated directly to the intended grooving temperature. In argon anneals, 99.996 Ar was admitted

Jan 1, 1970

By Martin Rubenstein

CdS crystals have been grown from a number of metallic solvents such as bismuth, tin, lead, and cadmium. Etching studies have shown that plastic deformation occurs if the crystals are not removed from the solvent prior to the solidification of the solvent, on cooling. The deformed crystals show a umique exciton fluorescence as a function of edge dislocation density. If one grows the CdS in the eutectic alloy of the above four metals (commonly called Wood&apos;s metal) the crystals can be removed from the solvent with hot water and no plastic deformation occurs. In this paper, the liquidus solubility measurements of CdS, as a function of temperature, are presented. The data were obtained using a high -temperature filtration technique. CADMIUM-SULFIDE crystals have been grown from a number of metallic solvents1 such as cadmium, bismuth, tin, and lead. Liquidus solubilities of CdS in cadmium,2 bismuth,3 and tin4 have already been measured. Crystals of CdS, in all four metals, have been grown by solution growth: 1) by cooling a saturated solution and 2) by a solution transport method.1&apos;"1 CdS crystals grown in these four solvents have a few characteristics in common: 1) 1.8°K photolumines-cent emission consisted mainly of the radiative recombination of the bound exciton commonly known as I,, 2) slip lines which could easily be seen by the naked eye, and 3) edge dislocation densities in the order of l05 per cu cm.1 It was decided that these slip lines and the high edge dislocation densities were caused by a plastic deformation of the CdS crystals. It was felt that this plastic deformation did not occur during the growth of the crystals nor during the cooling of the solution, but did occur when the solvent which was in contact with the crystals froze. If these assumptions were valid, the slip lines and the high number of dislocations could be reduced or eliminated by removing the crystals from the solvent before the solvent froze. Since crystals of CdS had already been grown separately in such solvents as bismuth, lead, tin, and cadmium, it was felt that crystals could be grown in a eutectic mixture of these four metals. In this work a eutectic (or near eutectic) mixture of bismuth, lead, tin and cadmium in the proportion 50, 26.5, 13.5, and 10 wt pct, respectively, was used to grow CdS crystals. Such a mixture has a melting point of about 70°C and is close in composition to the alloy commonly known as Wood&apos;s metals. If the crystals could be grown from this mixture of solvents, and if hot water (>75°C) could be used to separate the crystals of CdS from the metallic solvent, it was hoped that CdS crystals could be grown with little or no plastic deformation which had been ob- served when crystals were grown from these solvents uncombined. CdS crystals were grown from this low melting eutectic mixture of bismuth, lead, tin, and cadmium using the solvent transport method. CdS powder and the appropriate amount of metals were sealed in a quartz tube under a pressure of about 5 X 10-6 torr. This ampule was then placed in a vertical position in a furnace. The temperature was raised to about 900°C. The furnace was designed so that the top of the liquid column within the ampule was between 10° to 40°C higher than the bottom of the liquid column. These temperatures were measured on the outside of the quartz ampule. The ampule was maintained at temperature for 7 to 14 days (depending on the temperature at which transport was taking place) and then the furnace temperature was lowered until the temperature was about 125°C. The ampule was then removed from the furnace, placed in water maintained at about 90°C, and opened in this 90°C environment. The crystals could then be removed from this two-phase liquid (Wood&apos;s metal and water) by mechanically picking them out. Alternatively, the crystals could be quantitatively removed by adding an excess of mercury to the mixture of metals, crystals, and hot water. The hot solution of metals and the hot water could be evacuated using a small diameter tube connected to a vacuum. Small amounts of mercury and water could be removed by heating the crystals in vacuum. Crystals prepared using this technique showed no evidence of slip. However, some of these crystals did show edge dislocation densities as high as l04 per cu cm. Some few selected crystals showed no dislocations. Single crystals of CdS were grown as large as 5 by 5 by 0.5 mm. The ampules for the growth of these crystals were 13 mm O.D., 11 mm I.D., 150 mm! LIQUIDUS SOLUBILITY MEASUREMENTS The CdS starting materials was G.E. 118-8-2 powder which was fired in H2S at 1000°C, and then a vapor transport technique5 was applied to produce a "sound" mass of CdS. The Wood&apos;s metal was prepared by weighing out bismuth, lead, tin, and cadmium in the proportions of 50, 26.5, 13.5, and 10 wt pct, respectively. The bismuth, cadmium, and lead were from the American Smelting and Refining Co. (ASARCO) and all had purities of 99.999+ pct. The tin was 99.9999 pct spectroscopic grade from the Vulcan Materials Co. The appropriate mixture was placed in a quartz tube, evacuated to a pressure of 5 X 10-6 torr, melted to a liquid, cooled to room temperature under this same vacuum. This ingot was then placed in another quartz tube, evacuated to 5 x l0-6 torr, and sealed off under vacuum. The ampule was then horizontally placed in a furnace. The temperature was raised to 600°C, and over a period of several hours the ampule was vigorously shaken several times. The ampule was then removed from the furnace, and the metallic liquid was

Jan 1, 1970

Jan 1, 1970

By B. S. Ignasiak, B. N. Nandi, D. S. Montgomery

The growing need to measure the extent of weathering of coking coal in storage and in transit prompted the comparison of the dilatation of coking coal on heating, which is known to be a sensitive index of oxidation, with the composition and volume of the gases produced by a mild pyrolysis of the same coal. It was found that the pyrolysis method had the advantage in that it could be used to study coking coals in advanced stages of oxidation, when the swelling properties had been largely destroyed. Of the various constituents in the pyrolysis gas, the most sensitive indication of coal oxidation was the volume of carbon monoxide evolved per gram of coal. For the coals examined, this index appeared to be at its best when the temperature of pyrolysis was approximately 35oC.

Jan 1, 1970

By Ashok K. Sinha

The quasi-binary systems "VFe3"—VCo,—VNi,— "VCu3"and "TiFe3"—TiCo3,—TiNi3-"TiCu3"have been studied by a combination of microscopic and X-ray methods. Of the Phases encountered, eleven had close-packed ordered layer structures. Within each system, there is an approximately linear variation of the degree of hexagonality of the stacking arrangement with electron concentration, e/a. A study of eighty -four known examples of AB3 structures in transition metal alloys indicates that at e/a = 8.65 the ordered structure of the close -packed layers changes from "triangular" (AuCu3 type) to "rectangular" (SbCu3 type). At e/a < 8.65, the slope of hexagonality us e/a line increases with the group number of the A component. An interesting series of close-packed ordered structures is known to exist at the composition AB3; however, their alloy chemistry has not yet been fully understood. Dwight and Beck1 observed a correlation between position of the components in the periodic table and the type of crystal structure of the binary AB2 structures formed by transition metals. No consistent effect due to atomic size was noted and they proposed that electron concentration* predominates in In the present paper, the AB3 structures are characterized by a symbol describing the stacking and a symbol specifying the ordered layer. The stacking symbol used was introduced by Zhdanov,7 and later used in the International Tables,8 and by Beck9 in his survey of possible layer stacking structures. Alternating positive and negative integers are used to represent the number of positive (e.g., in abcabc...) and negative (e.g., in cbacba...) stacking sequences. T denotes the triangular ordering found in close-packed planes of the AuCu3 structure and R the rectangular ordering found in close-packed planes of the SbCu3 structure, Figs. 3(a) and (b). The present structure symbols are listed in Table I alongside the prototypes, where known, and other structural characteristics of AB3 phases found in the present investigation. EXPERIMENTAL The starting materials were metals of 99.9+ purity. The alloys were prepared by arc melting under argon atmosphere using a nonconsumable tungsten electrode and water-cooled copper hearth. The total weight loss upon melting and subsequent annealing was always less than 0.5 pct and hence the alloys will be referred to by their intended (unanalyzed) compositions. The alloys were homogenized and annealed at suitable temperatures in the range 750" to 1200°C, the annealing periods varying from 3 days at 1200°C to 10 days at 750°C. The heat treatments were carried out in sealed silica capsules under argon atmosphere and with a molybdenum foil cover between the alloy and the walls of the capsule. The quenched alloys were microscopically examined and reduced to powder by crushing or filing. The powders were, whenever necessary, given a stress-relieving anneal at the original annealing temperature. X-ray powder patterns were obtained with an asymmetrical focusing camera, a Guinier-deWolff focusing camera, or a Debye-Scherrer camera. Cr, Co, or Cu radiations were used. In some cases, to ensure the minimum degree of contamination, the deeply etched specimens were mounted in the asymmetrical focusing camera to obtain an X-ray pattern. Internal silicon standards were employed for lattice parameter determinations. The intensity calculations were made by using a Fortran IV program

Jan 1, 1970

By J. Lyndon Rosenblad

The strength of a jointed-rock mass is not well-understood. It is believed, however, that the behavior of a rock mass is governed by both the intact rock properties and the properties of the discontinuities. Rock research in the past has been concentrated on the determination of intact rock properties. Several studies are presently underway which should provide more insight into the properties of the discontinuities. Few research programs, however, have been undertaken with the intent of studying the composite rock mass behavior where either the intact rock strength or the properties of the discontinuities may control failure. There are three approaches available for studying the behavior of a rock mass, namely, field studies, mathematical models (finite element), and geomechanical models. A geomechanical model has been developed in this study where the strength and failure modes of a model rock mass are studied as a function of intact block geometry, joint orientation, joint properties, and confining pressure. The objective of this study is to gain some insight into the parameters that govern the behavior of a rock mass, which parameters are most important, and when these parameters control. This chapter describes only one phase of the study, the development of equipment for use with the rock-blocks model. The models being tested are approximately 22 x 22 x 6-in. The size varies slightly depending upon the joint orientation used. The equipment developed includes model material molds, reaction frames, loading apparatus, measuring and recording instrumentation, and other accessory equipment pertinent to the operation of a successful study. The usual problems in equipment development, such as uniformity of load application, loading capabilities, and reaction capacities are all

Jan 1, 1970

Jan 1, 1970

By Edwin S. Smith

Current research in the phenomenon of liquefaction has indicated some of the in situ material properties which should be considered in the planning of waste deposits. Practical experience in tailings disposal, however, must be combined with the results of theoretical and laboratory studies to develop the most economical and safe techniques against liquefaction failure. One of the many responsibilities of mining engineers and mill superintendents is providing for the safe and economic disposal of wastes (or tailings) that remain after a mineral has been extracted from an ore. The cost of disposal of these tailings exerts a considerable influence on the minimum grade of ore extracted from the mine. It varies to a great extent with each project and is dependent on many diverse factors, such as the local topographical, meteorological and seismological conditions together with the applicable water pollution laws of the area. The process used to extract a mineral from an ore determines the physical characteristics of the tailings and, thus, is one of the more important factors to be considered in the planning of disposal facilities. Today&apos;s trends in ore-processing operations complicate the problems of waste disposal: recently developed extraction methods result in the production of finer tailings, the use of lower grade ores produces greater volumes of wastes, and the enhanced land values in the vicinity of industrial plants preclude the former practice of spreading wastes laterally and force the expansion of waste deposits upwards to greater heights. The frequent occurrence of stability problems in waste deposits indicates that many mining organizations may not be employing current soil mechanics concepts and practices. One of the most spectacular, and often most disastrous, types of tailings dike failure is that resulting from liquefaction of the fine particles combined with a breach of the main retaining dike. TAILINGS DISPOSAL Since the many variations in site conditions, ore bodies and extraction processes dictate the general disposal procedures and mill superintendents incorporate special facilities to provide the most economical disposal method consistent with accepted safety standards, it is only natural that there are almost as many different disposal techniques as there are disposal areas. Methods used in the construction of retaining dikes include: (1) transporting granular material from an adjacent borrow pit and (2) mechanically segregating the total effluent and allowing the coarse fraction to form a retaining dike by hydraulic deposition. The location of a plant and the surrounding topography exert the greatest influence on the layout of tailings disposal facilities. Most of the above-ground waste deposits can be classified as side-hill, (Fig. 1,) cross-valley, (Fig. 2,) or stockpile deposits. Side-hill disposal areas are probably the most common type of layout because of the natural advantage of gravity flow, without the disadvantage of river diversion usually needed for tailings ponds formed behind cross-valley dikes. Stockpiles, which are placed on relatively level ground, require four retaining dikes and the effluent generally has to be pumped up into the disposal area. Changing production techniques or developments adjacent to disposal areas have produced variations or partial combinations of these three categories. In a series of articles, Lenhart describes many of the problems encountered in the disposal of tailings and certain innovations used to overcome them. He discusses weaknesses in design and layout and shows that disposal techniques are often learned the

Jan 1, 1970

By A. J. Heckler, J. A. Peterson

A capsule technique was successfully employed to investigate the effect of nickel on the activity of nitrogen in Fe-Ni-N austenite in the temperature range 600" to 1200°C. This technique consisted of equilibrating nitrogen among various Fe-Ni alloys within a sealed silica capsule. Nitrogen transfer among the specimens occurred by N, gas at 900°, lOOO? and 1200?C. Nitrogen gas pressures within the capsules were estimated to be as high as 22 atm. The activity coefficient of nitrogen, fN , in Fe-Ni-N austenite is adequately described by the linear interaction equation: log . wt pct Ni where the standard state is chosen such that fN = I as wt pct Napproaches zero in binary Fe-N. This relationship was determined over the temperature range 873" to 1473°K and for nickel contents of 0 to 35 wt pct. ALTHOUGH chemical thermodynamics of liquid iron alloys have been extensively studied, experimental data for the solid state are needed. These thermody-namic data will provide a basis for understanding phase transformations, precipitation reactions, metal-gas equilibria, and so forth. The interaction of sub-stitutional alloying elements with the interstitial elements is of particular interest. In this investigation the thermodynamic behavior of Fe-Ni-N austenite has been studied. The solubility of nitrogen gas in iron austenite is known to obey Sieverts&apos; law up to about 65 atm.1-6 In addition, the solubility of nitrogen in Fe-Ni austenite has been investigated5"8 using the classical method of equilibrating Fe-Ni alloys with nitrogen gas at 1 atm. A capsule technique similar to that used to study the activity of carbon in alloyed austeniteg&apos;&apos;&apos; was employed in the present work to determine the effect of nickel on the activity of nitrogen in Fe-Ni austenite over the temperature range 600" to 1200°C. EXPERIMENTAL PROCEDURE A series of Fe-Ni alloys up to 35 wt pct Ni was vacuum melted and cast into 1 by 3 by 6 in. ingots. Chemical analyses at the top and bottom of each ingot demonstrated that the ingots were homogeneous with respect to nickel content. The nickel contents are given in Table I. Additional chemical analyses showed that wt pct Si < 0.05, s < 0.01, C < 0.01, Al < 0.006, 0 < 0.004, Mn < 0.002, and P < 0.002. A 2 in. section of each ingot was cold rolled to 0.015 in. The material was then decarburized to a carbon content of less than 0.004 wt pct. A portion of the material of each nickel content was nitrided to various levels in a H2-NH3 gas atmosphere to provide a source of nitrogen during subsequent equilibration. The experimental technique consisted of equilibrating the series of Fe-Ni-N alloys in a partially evacuated sealed silica capsule at the temperature of interest. Both Vycor and quartz capsules were used. In general, the final equilibrium nitrogen content for each Fe-Ni alloy was approached from both higher and lower nitrogen levels. The criterion for establishing that equilibrium was attained was that the final nitrogen content for each Fe-Ni alloy was the same irrespective of the initial level. A schematic drawing of the sample configuration in a capsule is shown in Fig. 1. The samples were arranged so that there was a minimum of physical contact. The samples were also dusted with a fine, high purity alumina powder to help prevent sticking. Several different types of furnaces were used in this study. In each case, a thermocouple was placed immediately adjacent to the capsule during equilibration and the temperature was controlled to within *4?C of that reported. At each equilibration temperature, the following times were found to be more than sufficient to attain equilibrium: 600°C-250 hr, 900°C-150 hr, 1000°C-150 hr, and 1200°C-50 hr. After equilibration the capsules were quenched in water and the nitrogen contents of the specimens determined by a Strohlein analyzer. Analyses of samples after equilibration at 1000" and 1200°C showed no silicon pickup from the silica capsules. RESULTS AND DISCUSSION Transfer Mechanism. The mechanism by which nitrogen was transferred among specimens in an initially hydrogen flushed and partially evacuated capsule equilibrated at 1000°C was investigated. After equilibration the gas in the capsule was collected over water and an estimate of the pressure at temperature

Jan 1, 1970

By William C. Maurer

A survey of 25 novel drills has shown that spark drills have potential for drilling oil wells and blastholes at higher rates than rotary drills. Available laboratory and field data were extrapolated to drilling rates of 70 to 280 fph for full-scale spark drills. Most of the data used in these extrapolations were from small-scale laboratory tests at atmospheric pressure. Accurate extrapolation of the small-scale spark drill tests to full-scale field drills was complicated by the fact that the effect of fluid pressure in the well bore and the effect of spark size were not known. In order to answer these questions and to more accurately evaluate the potential of spark drills for drilling blastholes and oil wells economically, a high-voltage spark discharge system was assembled. This equipment produced powerful sparks (10,000 joules) equivalent to those that would be used on a 100-kw full-scale field drill. These sparks are 100 times more powerful than those previously used on spark drills, thus eliminating extrapolation of the spark size. In addition, a pressure chamber was modified to enable using these sparks to produce craters in rocks at fluid pressures up to 15,000 psi, thus eliminating extrapolation from atmospheric pressure to the high pressure existing in deep oil wells. These tests have provided considerable information for more accurately evaluating spark drills for oil-field drilling. MECHANISM AND THEORY OF SPARK DRILLING Spark-Drilling Mechanism When a high-voltage capacitor is discharged across two electrodes, the dissipated energy produces a high-temperature, high-pressure plasma for a few µsec. When these sparks are discharged in air, they undergo considerable expansion (Fig. 1) and produce low-pressure pulses (103-

Jan 1, 1970