By M. L. Rudee, R. A. Huggins

Samples of iron containing nitrogen or carbon have been given treatments similar to those used in cold-work peak (CWP) measurements and examined by transmission electron microscopy. It was observed that the unusual and nonreproducible behavior of the carbon CWP can be explained by a strong tendency for carbon to form grain boundary precipitates at temperatures below those used for CWP measurements. These precipitates dissolved at the temperatures used in the CWP measurements. There was no evidence for nitrogen precipitation at grain boundaries. There was no indication of precipitation along dislocations in either carburized or nitrided samples given treatments similar to those of CWP measurements. Although it is possible that subelectron-microscopic clustering had occurred, this observation supports the theories of the CWP that are based on continuous atmospheres rather than on individual precipitates. In an earlier paper,' the present authors developed a new distribution function to predict the occupation of sites for interstitial impurity atoms around a dislocation. When this distribution was applied to the case of carbon and nitrogen in iron, it predicted that, if the temperature dependence of the concentration of solute atoms in the matrix was controlled by the presence of equilibrium carbide or nitride precipitates, the tendency for nitrogen to segregate to dislocations would be greater than that for carbon even though their binding energies to dislocations are identical. The cold-work internal-friction peak (CWP) is considered by most authors to be produced by the interaction of interstitial impurities with dislocations. Many investigators have studied the CWP in iron containing carbon and nitrogen and have observed a significant difference between its behavior in the two cases. In this paper a series of experiments will be reported that were initiated to determine whether the application of the new distribution function would explain the observed differences between the carbon and nitrogen CWP. Although it was found that the distribution function, pev se, did not explain the differences, the differences became clear, and some insight into the mechanism of the CWP was realized. Before reporting the present experiments, the literature pertaining to the differences between the carbon and nitrogen CWP in iron and the various mechanisms proposed for the CWP will be reviewed. LITERATURE REVIEW Snoek2 first observed the CWP in iron specimens containing nitrogen, but also reported a weak and unreliable peak in carburized samples. Later, Ke3 established that the CWP height was proportional to the degree of deformation. The presence of nitrogen alone would produce a peak of the same size as found in a sample containing both nitrogen and carbon, and KG concluded that the CWP was caused by nitrogen. In a discussion of G's paper it was reported that Dijkstra had investigated the CWP in samples that contained only carbon. He found it to be much smaller than the nitrogen peak and "unstable". KG et al.4 charged specimens of iron with both carbon and nitrogen. They observed that the carbon CWP was much smaller than that observed in nitrided samples, but that aging at 300°C caused the carbon peak to increase. A similar treatment produced no change in a nitrogen peak. Annealing at higher temperatures caused the height of the CWP in both the nitrogen and carbon samples to decrease. This behavior was also observed by Kamber et al. 5 who found that the activation energy for the annealing of the CWP was identical with the activation energy for the self-diffusion of iron. They concluded that the annihilation of dislocations by climb caused the reduction in the CWP height. Kamber et al. studied the "unstable" carbon peak in detail. They measured both the Snoek and CWP during various aging treatments. In carburized samples, aging at 100°C caused the Snoek peak to disappear, although the CWP peak remained small. However, a subsequent treatment for 5 hr at 240°C caused the CWP to reach a maximum. They proposed that an additional location for the carbon, other than whatever site produced the CWP, is present. In nitrided samples the CWP was completely developed as soon as a measurement was made; additional sites are not present. No explanation of either the additional site or the difference in the behavior of carbon and nitrogen was offered. petarra5 performed a systematic study of the effect of composition on the CWP. Using three kinds of "pure" iron, he showed that there was a residual CWP when the carbon and nitrogen concentrations had been reduced to less than that detectable by Snoek-peak measurements. He observed the same general annealing behavior and composition dependence as previous investigators, with the following exceptions. On first measuring the carbon CWP, it was found to be identical with the residual peak, and essentially independent of the carbon content. If the CWP was measured a second time in the same sample, it increased in size, but was still only about one-fourth the size of a CWP in a sample of the same iron nitrided to the same composition. On the other hand, a series of annealing experiments showed that the nitrogen CWP was not al-

Jan 1, 1967

By R. C. Ku, R. G. Davies

The stress-strain behavior of Fe-C and Fe-Ni solid-solution alloys has been investigated at 25°C. It is found that the rate of solid-solution strengthening is dependent upon the strain at which the yield stress is measured, the macroyield stress being much more concentration-dependent than the microyield stress. In fact the addition of nickel does not lead to any increase in the microyield stress of iron. The primary effect of increasing the carbon or nickel content is to increase the slope of the stress-strain curve in the microyield region; this effect has been correlated, by means of transmission electron microscopy, with a decreased ability of the dislocations to cross-slip. It is concluded that the Mott-Nabarro theory is a good description of true solid-solution hardening in these and other iron-base alloys. A.LL theories of the solid-solution strengthening1-4 indicate that the flow stress of an alloy increases both with solute concentration and "misfit" between the solvent and solute atoms. The functional relationship between strength, solute concentration, C, and misfit depends upon the particular theory. Mott and Nabarro1,2 and Schoeck and Seeger3 both predict a linear increase in strength with concentration, while Fleischer4 indicates that the strength should be proportional to C1/2; there are in the literature experimental observations to support both these compositional dependencies.1'8 The experimental evidence used to support the theories is the change in macroscopic yield stress (strain, e, = 10-3) with composition. However, recent investigations have revealed that solid-solution strengthening in a Cu-Al single crystals7 and in Fe-V polycrystal-line" alloys depends upon the strain at which the flow stress is measured; a flow stress in the microplastic range (e = 10-6 to 10-5) is much less concentration-dependent than the macroyield stress. Since the theories of solid-solution strengthening are concerned in particular with the stress to move a dislocation in a dislocation-free matrix, they should only be compared with microyield-stress data; it will be shown that in a material deforming homogeneously the microyield stress (e = 10-6) is approximately the stress to move through the matrix those dislocations which have been nucleated by stress concentrations such as particles or grain boundary ledges.9-11 In contrast, the macro-yield stress is more complex in that it is affected by several phenomena: dislocation multiplication, dislocation interactions, and the ease of propagating slip across grain boundaries. For example, it is experimentally observed that when long-range order12'13 or solute effects10 restrict cross alip the grain boundary

Jan 1, 1967

By P. L. Hendricks, J. W. Spretnak

The interstitial atom principally responsible for the yield point and strain aging in electron-beam-melted tantalum is identified by analysis of the kinetics of the return of the yield point after an increment of plastic deformation. Two sets of specimens contained two levels of oxygen with very low hydrogen contents and the third set had comparable oxygen and hydrogen contents. The activation energy for the return of the yield point agrees well with that for diffusion of oxygen for the first two sets of specimens. For the third set of specimens, the activation-energy value lies between those for diffusion of hydrogen and for diffusion of oxygen. The advent of the dislocation model of plastic deformation in metals has revitalized interest in the yield point and strain aging in bcc metals containing a certain minimum content of interstitial solute elements. Much theoretical and experimental work has been performed in recent years to elucidate the detailed mechanism of these phenomena. The purpose of this investigation is to attempt to identify the principal interstitial element responsible for the yield-point phenomenon in electron-beam-melted tantalum by analysis of the kinetics of the return of the yield point after an increment of plastic deformation. Some of the earlier theories of the yield-point phenomenon proposed a grain boundary film of iron carbide. Such models could not satisfactorily explain all features of strain aging and the yield-point phenomena. The most widely accepted explanation is that of Cottrell,1 later extended by Cottrell and Bilby.2 Strain aging is ascribed to "locking" of dislocations by interstitial solute "atmospheres". The yield-point phenomenon results when the dislocations are torn away from their atmospheres. The strain-aged condition is re-established after sufficient time to allow the interstitial atoms to diffuse to the dislocation lines and re-establish the locking atmospheres. Clearly, the Cottrell-Bilby model is concerned with the bulk of the grain and does not specifically involve the grain boundary. The recent modification of the Cottrell-Bilby model is a redirection of attention to the role of the grain boundary and the possibility of multiplication of a limited number of free dislocations rather than unlocking all of the dislocations. Theories have been advanced by Hahn3 and conrad4 which are modifications of the Cottrell-Bilby theory. The model proposed by Hahn indicates that, although the possibility of un- locking anchored dislocations is not excluded, it implies that unlocking is not necessarily required to explain yield drop. Locking of dislocations during the aging treatment is a necessary part of the theory; however, it assumes that dislocations once locked remain locked. It is suggested that the yield drop observed is a result of the following factors: 1) the presence of a small number of mobile dislocations initially, 2) rapid dislocation multiplication, 3) the stress dependence of dislocation velocity. In the case of bcc metals, locking is considered to be the means by which dislocations are immobilized. Cold working of the metal results in the generation of larger numbers of new dislocations and the stress dependence of the dislocation velocity accounts for yield drop observed. Conrad' has proposed a model similar to the one just described which applies to strain aging of iron and steel and which logically could be extended to other bcc metals. This model also does not require large-scale unlocking of dislocations. It is proposed that, during initial loading of a specimen below the upper yield stress, a few dislocations are torn free of their Cottrell atmospheres at regions of stress concentrations. With an increasing stress, some multiplication of dislocations occurs by a double cross slip mechanism, thus giving a preyield microstrain. At some critical stress represented by the upper yield stress, sudden profuse multiplication of dislocations occurs, enabling plastic flow to proceed at a lower stress. In this model, microstrain, preyielding, and flow represent the movement of free dislocations. It should be noted that this model also requires the locking of dislocations by interstitial solute atoms for the occurrence of a yield point; however, unlocking of large numbers of dislocations is not required. If it is assumed that the yield point will return when some fraction of free dislocations produced during pre-straining are pinned, the number of solute atoms required to pin unit length of a dislocation line can be calculated when prestrain and reloading are done at the same temperature and strain rate. Since the migration of solute atoms back to the stress fields of dislocation lines is controlled by the diffusion rate of interstitial solute atoms, it is to be expected that the activation energy for strain aging would be identical to the activation energy for diffusion. It would also be expected that the strain aging observed will be controlled by the fastest diffusing species capable of producing locking over the temperature range investigated. The rate of yield-point return has been found to be adequately expressed by an empirical rate equation of the form: rate=Ae-Q/RT [1] where A = constant, Q = activation energy, R = gas constant, and T = absolute temperature. Cottrell and Bilby2 have expressed the number of atoms per unit length of dislocation line which arrive

Jan 1, 1967

By L. Seigle, R. Resnick

An inert-marker movement experiment indicates that the ratio of the intrinsic diffusion coefficients DC:DTa = 80:l in TaC at 2500°C. Measurements of the diffmion coefficient of carbon in nonstoichiometric TaC at temperatures from 1700° to 2700°C reveal that Dc increases with decreasing carbon content, but much less than expected from the probable change in vacancy concentration with carbon content. A diffusion process involving two simultaneously operating mechanisms is postulated, and shown to be theoretically feasible. The average value of the carbon diffusion coefficient is given by DC = 0.18 exp[(-85,000 ± 3000)/RT] sq cm per sec over the composition range 46 to 49.5 at. pct C. BECAUSE of their high melting points and hardness, the carbides of the IV, V, and VI group transition metals, along with those of uranium, have attracted considerable interest for applications at high temperatures. In these applications the reactivity of the materials is important, and, since rates of diffusion within the compounds influence reactivity, a knowledge of diffusion kinetics and mechanisms is desirable. While many investigations of the mechanical and electrical properties of these compounds have been made, only two fundamental investigations of diffusion in the carbides are known. Chubb, Getz, and Townleyl measured the diffusivity of carbon and uranium in UC, and Gel'd and Liubimov2 measured the diffusivity of carbon and niobium in NbC. This paper describes an investigation of the diffusion of carbon in tantalum monocarbide and, in particular, the influence of carbon deficiency on this process. Tantalum carbide melts at approximately 3800°C, which makes it one of the highest melting materials known. The compound exists over a rather wide range of carbon Content.3-7 At the peritectic temperature, 3240°C, the phase extends from about 36 to 50 at. pct C. Although the compound can exist with a substantial carbon deficiency, the high carbon phase boundary remains near the stoichiometric composition over the entire temperature range; i.e., no carbon excess is observed. The structure of TaC is the NaCl type wherein carbon atoms normally occupy the octahedral sites in a somewhat expanded fcc lattice of tantalum. Decrease of the lattice parameter with decreasing carbon suggests that the removal of carbon introduces octahedral vacancies into the lattice. I) EXPERIMENTAL DETAILS AND RESULTS Inert-Marker Experiments. In a compound such as TaC the interstitial element would be expected to diffuse more rapidly than the metal. This was confirmed by an inert-marker experiment, following Srnigelskas and irkeendall.8 Ideally, the markers should be placed at the interface between a slab of low-carbon TaC and graphite, and their movement during subsequent inter-diffusion measured. Unfortunately, no solid could be found which is unreactive in contact with carbon at the high temperatures employed in these experiments. In order to circumvent this problem, a specimen was designed in which the markers consisted of several small canals running just below the surface of a tantalum slab. This specimen was prepared by machining grooves on the surface of the tantalum slab and then diffusion-bonding a thin plate of tantalum to the slab over the grooves. The surface of the plate was then ground down until the distance between the canals and surface was as small as possible (about 0.01 cm). Thus, the canals would lie entirely within the TaC phase after a short period of diffusion. The diffusion anneal consisted of immersing the metal sample in high-purity graphite powder and heating for approximately 10 hr at 2500°C under vacuum. At this temperature, the vapor pressure is sufficiently high and the transfer of carbon from graphite sufficiently rapid to allow the surface of the diffusion sample to attain the stoichiometric carbon concentration very quickly. Conclusions regarding the relative diffusion rates of carbon and tantalum in the compound layers (TaC and Ta2C) can be drawn from the location of the canals after the diffusion anneals. If the growth of the layers is governed mainly by the diffusion of carbon, as expected, the canals should remain close to the sample surface. If the diffusion of tantalum contributes appreciably to formation of the compound layers, the distance from the markers (canals) to the surface should increase. Fig. 1 shows, diagrammatically, the appearance of the specimens after diffusion, and Table I presents the depth below the surface at which the

Jan 1, 1967

By Edna A. Dancy, Gerhard J. Derge

The specific conductance of FeOx,-CaO melts in contact with iron was found to decrease from 200 ohm-1 cm-1 for FeO, to 40 ohm-1 cm-1 for a melt containing 26.3 pct CaO at 1400°C. The temperature coefficient was positive at all compositions, but became smaller at high CaO contents. Current efficiencies for electrolysis increased from 2.5 pct in FeOx to 17.3 pct at the high CaO composition, indicating a change from predominantly electronic conduction to conduction with a substantial ionic contribution. It was shown that Ca++ ions as well as Fe++ ions carry the ionic current. A subsidiary investigation on the apparent effect of atmospheres of argon, helium, and nitrogen on the electrical conductivity showed that this could be correlated with surface temperature losses, which varied with the thermal conductivities of the gases and resulted in precipitation of metal by the reaction 3 Fe++ = 2 Fe+++ + Fe. The work described in this paper is offered as a contribution to the general fund of knowledge concerning metallurgical slags. Measurement of electrical conductivity and electrolysis are comparatively trouble -free methods for investigating molten materials, but, although these methods had been used for complex slags, it was not until the work of Bockris et al.1 that the approach of examining simple binary slag systems was employed, and CaO-SiO2, MnO-SiO2, and Al2O3-Si9 were studied. Two groups have performed work of particular relevance to the present investigation. Inouye, Tomlinson, and chipman2 studied the conductivity of wustite as a function of temperature and of the addition of 5 mol pct of a number of oxides, including CaO. They concluded that molten FeOx in equilibrium with iron is a semiconductor. Simnad, Derge, and ceorge3 demonstrated the ionic nature of liquid iron silicate slags and also concluded that, although the conductivity of FeOx in equilibrium with iron is predominantly electronic in nature, there is a small ionic contribution. The work reported here on FeOx,-CaO slags consists of three main parts, namely, the determination of the specific conductance over a wide composition range, an investigation into the nature of the conductivity through current-efficiency measurements over the same composition range, and an attempt to identify the current-carrying ions, as well as a subsidiary investigation on the apparent effect of the nature of the inert atmosphere on the conductivity. EXPERIMENTAL Materials. The slags, varying in composition from FeOx to 27 pct CaO, were prepared by heating reagent- grade Fe2O3 in an ingot iron crucible with a suitable amount of CaCO3 and, in some cases, powdered iron, in air. This prefused material was then used for the runs. At the end of each run the cell was removed from the furnace and quenched by immersing the bottom half in water. After crushing, the slags were analyzed for calcium and total iron by the usual wet methods. The oxygen content was obtained by difference. Specific Conductance: Apparatus and Method. Fig. shows the experimental setup, with the conductivity cell and leads of ingot iron. The standard four-probe method for measuring high conductivities was used. In this, the potential drop across the unknown resistance is compared with the potential drop across a known resistance connected in series, i .e., same current through both resistances. Thus there are both current and potential leads to the center electrode and to the crucible, which acts as th other electrode. Both ac and dc circuits were available for the measurements; they have been described in earlier work performed in this laboratory.4,5 The geometry of the cell was such that the center electrode was equidistant from the bottom and sides of the crucible. This ensured that the current path was the same irrespective of the magnitude of the conductivity of the material in the cell. Cell constant were measured with KC1 or NaCl solutions, which have considerably lower conductivities (0.0013 to 0.25 ohm-' cm) than the slags, and this precaution in design made sure that the determined cell constants applied to the cells with contents of any conductivity. The cell-constant determinations were made with the ac measuring circuit to prevent polarization. The four-probe method eliminates lead resistance but not the resistance of those parts of the center

Jan 1, 1967

By Robert E. Ogilvie, Zvonimir Ban

Oxidation experiments were conducted above 600°C to investigate the oxidation products formed on the surface of MoSi2. Results are presented which indicate that minor iron impurities play a key role in the oxidation behavior of MoSi2 above 600 °C. Based on considerations of the crystal chemistry of the oxidation products, MoSi2 with rhenium and iron additions was found to be resistant to oxidation in the pesting temperature range. AS early as 1914, Honigschmidtl observed that some silicides of molybdenum exhibited high resistance to oxidation at elevated temperatures. This fact did not arouse much interest until 1950, when Kieffer and cerwenka2 examined this property in more detail. They found that Mo-Si alloys with approximately 70 pct Mo (by weight) could be heated to 1600°C in an oxidizing atmosphere without any significant damage. The surface was found to be protected by the formation of an extremely thin silica glass layer which had no tendency to spa11 during subsequent thermal cycling. In 1955, Fitzer3 discovered that even solid bodies made of MoSi2 completely oxidized within a relatively short time when exposed to the air in the temperature range from 300° to 600°C. To describe this phenomenon he proposed the name "molybdenum disilicide 'pest' ", clearly analogous to the previously observed "tin plague" ("tin pest") which, however, arises as the result of a phase transformation. Studies performed by Fitzer and, in particular, one published recently by Berkowitz, Blackburn, and Fel-ten,' comprise the most extensive research to date on the pest phenomenon in MoSi2, as far as the fundamen- tal mechanism of the process is concerned. The first of these studies revealed the existence of a crystalline phase which appeared at the surface at 750°C and dissolved in the glassy silica layer at 1150°C. The logical assumption was that this phase was some reaction product of MOO3 and SiO2. The formation of a reaction product of this type seemed probable since it had been mentioned by Glemser and Lutz6 in a paper describing their studies of molybdenum oxides; however, this assumption was later disproved.8 It is our belief that information concerning the exact nature of this crystalline phase may be important for a better understanding of both pesting and the protection mechanism. Therefore, since the only available general description of the pest phenomenon was that of Fitzer, it was decided to reproduce his experiments. These experiments established that, in addition to the "pest" and "nonpest" temperature range, an intermediate region exists between 600" and approximately 650°C. This region is characterized by the appearance of a variable amount of yellow to orange colored crystals. The electron-beam microanalyzer was used to qualitatively determine their composition. Iron and molybdenum were found to be major constituents. This result can be explained based on the following facts: 1) iron, according to literature data,* is the most common impurity in molybdenum powder, and its content can be as high as 0.25 pct; 2) technical silicon powder usually contains iron; 3) steel ball mills are often used for the crushing and grinding of MoSi2. In order to clarify the exact role of iron, it was deliberately added to a stoichiometric mixture of molybdenum and silicon. The observed results corroborated the previous experiment, proving that iron (probably as some silicide phase) concentrates along the grain boundaries. I) EXPERIMENTAL PROCEDURE A) Oxidation of MoSi2 with Iron Additions. 1) Specimen Preparation. Specimens were prepared by both

Jan 1, 1967

By C. M. Wayman, R. Bullough

The rediffraction of Bragg diffracted beams by differently oriented regions (such as twins) of a crystal may give rise to "extra" reflections or reciprocal lattice points. These two papers are concerned with predicting these additional reflections which result from twin related regions of a lattice. Analysis is made for {111}fcc twins, (112)bcc twins, and {hkil}hcp twins. It is first required, knowing the specific variant of the twinning plane in each case, to predict the positions of the twin reflections relative to the matrix reciprocal lattice. Once this is done, the positions of the "extra" multiply diffracted reflections may be deduced. Part I is devoted to establishing "selection ru1es" for twinning, i.e., the necessary and sufficient conditions for the existence of twinned reciprocal lattice points. 1. INTRODUCTION. Transmission electron diffraction patterns are frequently complicated by multiply diffracted beams. Pashley and stowell1 have recently demonstrated that certain extra reflections in evapo- rated films of gold result from the rediffraction of matrix Bragg diffracted beams by (111) microtwins in the gold. It was previously (and erroneously) suggested 2,3 that observed "irrational" reflections in fine-grained gold were due to the presence of some hcp gold. A similar situation exists, apparently, for some bcc materials; fine (112) twins in bcc martensite in Fe-Ni alloys4 give rise to extra reflections. There are many other examples. The number of transmission electron microscopic investigations is continually increasing, and because of the importance of double (and multiple) diffraction in the interpretation of diffraction patterns, it was judged that a detailed elaboration of the principles involved is desirable, as well as the extension of these principles in reasonably closed form to other crystal structures, particularly bcc and hcp. The present analysis considers double diffraction caused by (111) twins in fcc metals, (112) twins in bcc metals, and {hkil} = {hkl) twins in hcp metals. For each case of twinning, the various possible (variants of) twins give rise to a set of interpenetrating reciprocal lattices. The relative spatial arrangements of these reciprocal lattices can be deduced (Part I) and are expressed in terms of simple "selection rules". The resulting sets of interpenetrating reciprocal lattices are then analyzed for possible doubly diffracted reflections (Part II). The notation used, and some important formulas are given in Appendices I and 11.

Jan 1, 1967

By C. M. Wayman, R. Bullough

The selection rules fir twinning in fcc, bcc, and hcp lattices as established in Part I are used to predict the positions, relative to the matrix (untwinned) reciprocal lattice, of reflections due to double diffraction from the twins. These doubly diffracted reciprocal lattice points, which often coincide with ordinary matrix reciprocal lattice points, are deduced from kinematical considerations. 1. INTRODUCTION. A Bragg diffracted beam under certain conditions may be rediffracted to produce a third beam i .e., the incident beam, the first diffracted beam, and the rediffracted beam). In such a case an initial incident beam is diffracted by a set of planes; the diffracted beam may then be rediffracted by a second set of crystallographically different planes. The initially diffracted beam acts as an incident beam for the second set of planes, thus resulting in a twice-diffracted beam. This twice-diffracted beam may be regarded as a singly diffracted beam from a set of lattice planes whose structure factor is zero. In order to find the reciprocal lattice point corresponding to the doubly diffracted beam, it is customary1,2 to combine vectorially the component reciprocal lattice vectors which head to the extra reflections. For example, hcp metals may exhibit the forbidden (0001) reflections.* As Fig. 1 shows, the (0001) reciprocal lattice point results from: (1010) + (1011) = (0001) Similarly, combination of the beams (1011) and (1010) gives rise to: (1011)- (1010) = (0001) As Pashley and stowell2 have pointed out, even if in fact the double diffraction points lie on the Ewald sphere, they may not actually represent observed doubly diffracted beams because the initially diffracted primary beam, i.e., the source, must also correspond to a reciprocal lattice point which lies on the sphere of reflection; however, the reciprocal lattice point corresponding to the planes causing the rediffraction need not lie on the sphere. A little consideration of the Ewald construction in Fig. 2 makes this argument clear. In Fig. 2 the incident beam is represented by the wave vector ko. This beam is initially diffracted by the lattice planes (hkl) which are represented by the reciprocal lattice vector r(hk1) The reciprocal lattice point (hkl) of course lies on the Ewald sphere in order that the Bragg condition be satisfied. The initially diffracted beam is represented by the wave vector kl. If now kl is rediffracted by a second set of planes (h'k'l') resulting in k2 the lattice point (h"k"l") must lie on the Ewald sphere if the double diffracted beam k2 is to be observed. It is clear that (h"k"l") is the vector sum of (hkl) and (h'k'l'), and that (h'k'l') need not in fact lie on the Ewald sphere. In the usual1,2 analysis the origin (000) of the reciprocal lattice is shifted to the point (hkl). However the translation (000)— (hkl) automatically shifts the point (h'k'l') to the Ewald sphere, i.e., (h'k'l')— (h"k"1"). It is to be seen that (hkl), the source reflection, must lie on the Ewald sphere; if it does not the translation (000) — (hkl) places the "new" origin off the sphere, not satisfying the Ewald construction and hence the Bragg condition. The point (h"k"1") of course must lie on the sphere if it corresponds to an observed doubly diffracted beam. It is to be noted that crystals having the hcp structure, as just discussed, are intrinsically capable (i.e., without lattice defects such as twins) of double diffraction, as contrasted to fcc and bcc crystals which are extrinsically capable (requiring lattice defects or reoriented lattice regions). The "allowed" bcc reciprocal lattice points (which comprise an fcc lattice) are (110), (2001, (211), (220), (310), (2221, (321), (4001, and so forth. The combination

Jan 1, 1967

By S. Feuerstein, L. Rice

The effect of low pressures on the flow and fracture behavior of molybdenum is described. For poly crystalline samples, room-temperature tensile tests indicate greater ductility under 10 Torr than under intermediate pressures up to and including atmospheric pressure (760 Torr). In addition, tests conducted at 760 Torr under atmospheres of air, dry nitrogen, and purified argon exhibited no apparent difference in mechanical properties. Critical tests involving baking in situ as well as those involving single-crystal deformation further imply that the ductility effect is a pressure-dependent phenomenon related only to the fracture process. This dependency is discussed in terms of adsorption and diffusion contributions. THE effect of very low pressures on material properties has heretofore been presumed to be important only for substances possessing relatively high vapor pressures at ambient temperatures. Research has therefore been concentrated primarily on organic solids and liquids, and in some instances on metals such as zinc and cadmium. Most vacuum-effect studies' on the mechanical behavior of metals have been performed under conditions of either cyclic loading or creep rupture at elevated temperatures, i.e., over extended time periods. These studies were not restricted to high vapor pressure materials but also encompassed such metals as gold, copper, and nickel. Very little concern, however, was placed upon the importance of a vacuum environment on the mechanical behavior of metals subjected to a simple unidirectional deformation at ambient temperatures. A tension test is generally of short duration as compared to a creep test, and at room temperature vacuum effects if any would be expected to be surface-limited. In early 1963, Kramer and podlaseck2 reported a change in the bulk flow behavior of aluminum single crystals during room-temperature tension tests. The deformations were performed under pressure conditions of 760 to 3.4 X 10-8 Torr and indicated for the first time a vacuum surface effect contributing to the bulk tensile behavior of metal specimens. As a consequence, an experimental program was initiated in this Laboratory to study the effects of ultrahigh-vacuum conditions on the mechanical behavior of metals. The results of a preliminary study on poly-crystalline molybdenum3 revealed, unlike Kramer's observations of changes in the stress-strain behavior, only an increased ductility under ultrahigh vacuum. Flow behaviors were nearly identical for all tests re- gardless of pressure. This paper presents comprehensive results obtained in this area of research. 1) EXPERIMENTAL PROCEDURE Three material categories were used in this study: sintered and are-cast polycrystalline molybdenum of nominal purity 99.93+ pct and single-pass electron-beam zone-refined molybdenum single crystals having a nominal purity level of 99.99+ pct. The interstitial levels (weight percent) as determined by the Materials Testing Laboratories, Division of Magnaflux Corp., were as follows: sintered molybdenum (C— 0.005, H—0.0004, O—0.015, N—0.008); and arc-cast molybdenum (C-0.0038, H-0.0003, O-0.015, N-0.023). Single-crystal molybdenum obtained from Materials Research Corp. had a typical interstitial analysis of C-0.0015, H-0.00007, O—0.00045, and N-0.0001. Tensile specimens having a 5 mm diam by 50.8 mm length were prepared from these materials. An average grain diameter of 0.059 mm was obtained for the sintered specimens following a 4-hr, 1600°C heat treatment. Grain sizes from 0.019 to 0.149 mm were obtained in the arc-cast specimens following heat treatments from 1100° to 1600°C for 1 hr. This series of specimens was used exclusively for the grain-size effect studies. All samples were electrolytically polished in 97 pct sulfuric acid solution prior to testing. Experiments were performed at room temperature in an ion-pumped ultrahigh-vacuum system positioned in an Instron tensile machine, Fig. 1. A constant strain rate of 4.2 x 10-4 sec-1 as derived from crosshead displacement was assumed for the deformations. Starting vacuums ranged from 2 to 0.5 X 10-10 Torr. These pressure measurements were made using corrected values4 of an NRC Redhead gage. Comparative readings were also made against a G.E. triggered dis-

Jan 1, 1967

By W. A. Backofen, D. Lee

The deformation of textured sheet of titanium and several of its all-a (hcp) alloys was investigated with two kinds of experiments: tension testing along different directions in the plane of the sheet, and combined-stress loading along the principal axes of anisotropy (the rolling and transverse directions). Texture and plastic anisotropy were evaluated with pole figures and by measurement, as a function of orientation, of the tensile transverse-strain ratio, or R parameter. The results as a whole can be rationalized qualitatively with the present understanding of deformation mechanisms in titanium. Quantitative agreement between the orientation dependence of tensile yield strength and the Predictions of continuum ANISOTROPY in the properties of engineering materials is more the rule than the exception because anisotropy in structure is so common, and the one generally follows the other. Two broad categories of structural anisotropy are represented by mechanical fibering and crystallographic texture. The former is important in many aspects of fracture.' The latter has more significance for yielding and plastic deformation, theory, using the R measurements, was relatively poor. However, in tension-tension quadrants of the yield-locus diagrams, the difference between theory and experiment was hardly more than 10 pct. The maximum texture-hardening effect was found in a 4Al-1/4O2 alloy to be nearly 50 pct. In the compression-compression quadrant, {1012} deformation twinning prevented the locus from expanding much beyond the Position predicted for isotropic material. With increasing temperature the trend in R was downwards, approaching unity (isotropy) near the a-transus temperature; an accompanying development was large amounts of neck-free extension. which are of special concern in this paper. The tendency has been to view crystallographic texture more as a liability or curio than as an asset. The prominent exception is found in silicon-ferrite sheet for power-transformer cores, which is processed to develop a new optimum texture for high electrical efficiency. Yet it should be possible to find other examples, involving other kinds of properties. More specifically, there is good analytical reason to expect improved combined-stress yielding resistance in suitably textured material,2,3 and it has now been shown by experiment that texture hardening or softening is a potentially useful phenomenon in certain engineering devices and processes.'-I To date, work has included measurements of the transverse (width to thickness) strain ratios in the

Jan 1, 1967

Jan 1, 1967

By N. A. D. Parlee, M. M. A. El-Naggar, G. 8. Horsley

The apparatus was of a modified Sieverts type1&apos;2 with a reaction tube designed to function also as the cell component of an oxygen pressure gage. The reaction tube assembly is shown in Fig. 1 and described in Table I. The main body is a 1-in.-OD 15 mol pct calcia-stabilized zirconia tube. The ground-glass joint, g, the male part of which carried a prism for optical pyrometer use, was connected to the remainder of the Sieverts apparatus. The calibration of the cell (at its 1000°K operating temperature) for internal oxygen pressures (PO2in) in the range 0.2 to 10 9 atm was made against internal air pressures measured by mercury manometer and McLeod gage. At very low po2in values down to l<Tn atm the performance was checked by comparing pQ calculated from electromotive force measurement when the apparatus was filled with a) pure CO gas and b) a CO-CO2 mixture of the ratio CO-CO2 = 1:0.398, with Po, values calculated from the equilibrium constants of the following reactions at 1000°K:

Jan 1, 1968

By Akira Yazawa, Alžbeta Gubcova

RECENT lead-smelting techniques have tended toward use of high-grade concentrates with minimum amounts of flu, accompanied by profitable employment of roast reaction.1-5 In order to better understand these smelting processes, thermodynamical calculations have been carried out on the Pb-S-0 system, and the results obtained have been presented in isothermal reaction diagrams in which log Ps, and logPo, were the axes. The diagram thus constructed seems to be more convenient to grasp the equilibrium aspect than those published hitherto.6-8

Jan 1, 1968

By R. C. Hall

We are pleased to confirm some of the mechanical data presented by Dr. Detert on the 18 pct Ni marag-ing steel.15 Bar 3 in. in diam and containing 0.02 wt pct C, 18.5 Ni, 8.9 Co, 5.1 MO, 0.55 Ti, 0.05 Al, and balance iron has been examined in our laboratory. Cylinders 0.5 in. high and 0.4 to 0.5 in. in diam were cold-compressed from 3 to 40 pct reduction in height. Table VI shows some typical data; deformation in-

Jan 1, 1968

By J. Weertman

The paper of Gifkins and Snowden considers the interesting but difficult problem of determining the stress dependence of secondary (steady-state) creep at low stresses. These authors have concluded that at stresses below 250 psi (2 x 107 dynes per sq cm) the secondary creep rate of lead is proportional to the stress (viscous creep) and is not proportional to the stress raised to about a fifth power. The experimental data considered by them were obtained on tests conducted at room temperature and at 50°C. The lowest stress employed was 50 psi (3.5 X 106 dynes per sq cm). The authors pointed out the main difficulty in determining the stress dependence of creep at low stresses. The creep tests must be run for very long lengths of time. However they made no estimates of when an experimental creep rate determination must be rejected because it does not represent a true steady-state or minimum creep rate. In order to be certain that a creep curve is within the steady-state region, the total creep strain should be of the order of 0.1 to 0.2. For a creep test of a year&apos;s duration this requirement implies that a secondary creep rate smaller than about 10-3 per hr cannot be measured reliably. The corresponding creep rate for a 10-year test is 10-6 per hr. The creep rates of the tests that were considered by the authors to prove the existence of viscous creep were of the order of or less than 10-6 per hr. One can conclude reasonably that this data does not prove unambiguously that large strain steady-state creep rate of lead is proportional to the stress in the stress range of 50 to 250 psi (3.5 x 106 to 2 X 107 dynes per sq cm). Another technique can be used to obtain the stress dependence at low stress levels. The creep rate is a very sensitive function of temperature. The creep rate can be increased by very large amounts merely by increasing the temperature. We carried out steady-state creep tests on lead single crystals25 at temperatures up to 320°C. We were able to obtain creep rate data down to stresses as low as 35 psi (2.5 x 10&apos; dynes per sq cm). Our smallest creep rate was 8 x 10-5 per hr. Thus we obtained large strain, steady-state creep rates to even lower stresses than were considered by Gifkins and Snowden. No evidence was seen for viscous creep. The creep rate was proportional to the stress raised to about a 4.5 power down to the lowest stresses. Since there is no reason to believe that changing the temperature should change the stress dependence of steady-state creep, we feel that large strain viscous creep does not occur in the stress range quoted by the authors for lead single crystals or large-grain polycrystalline samples of lead. This conclusion does not imply that viscous creep may nat occur in a lower stress range or in the same stress range for fine grain material or at creep strains very much smaller than 0.1. Support by the U.S. Office of Naval Research is acknowledged. Authors&apos; Reply R. C. Gifkins and K. U. Snowden We thank Dr. Weertman for his discussion and although, as we hope to show, we do not agree with his reservations, we do concur in stressing the importance of ensuring that creep rates are reliably obtained. Dr. Weertman appears to be content to accept n = 1 for low stresses with fine-grained material but not for single crystals. We believe our results show that the former result cannot be accepted without also accepting the latter. We will also show that the probable errors in our minimum creep rates are insufficient to alter our conclusions, that the criterion proposed by Dr. Weertman is arbitrarily restrictive and his alternative experimental approach possibly invalid. 1) A principal result of our Fig. 1(a) is that n = 1 for polycrystalline specimens at room temperature and 50°C for stresses below -250 psi. There was evidence that crystal slip and grain boundary sliding contributed approximately equaily to the overall strain in this low-stress regime. This implies that either a) grain boundary sliding controls slip within the grains or b) both grain boundary sliding and crystal slip independently occur according to mechanisms which give n = 1. Alternative a does not seem acceptable, so we were forced to consider b. This led us to reexamine work on bicrystals by Strutt and Gifkins and plot curves Fig. l(b). Previously Strutt et al. (loc. cit.), had merged these points with others using the Zener-Holloman parameter and thus, we now believe, had been led to overlook the behavior where n = 1. Curves C and D in Fig. l(b) did appear to confirm the hypotheses that n = 1 for crystal slip at these low stresses and the sliding curve F was similarly of the expected form. It was comparatively easy to find a quantitative theory to account for n = 1 for sliding and the similarity of curves C and D to curve F (all obtained from the same set of specimens) led us to feel that the single-crystal curves were valid. 2) We believe the secondary creep rates for both the polycrystalline and single-crystal specimens to be in error by factors c2. In Fig. 6 creep curves for polycrystalline specimens of lead(1) and lead(II) are reproduced as curves a and b, respectively, and curve c is for a single crystal at 100 psi. It is clear that, although the attainment of secondary creep rate takes 2 years for a and 150 days for b, thereafter the curve is linear for periods of 7 and -1 year, respectively. The single crystal has a linear portion commencing after 20 and extending to 90 days. Creep extension was measured directly using a traveling microscope reading to 0.01 mm on gage lengths marked on the specimens; the gage lengths

Jan 1, 1968

By Ronald C. Koo

SMALL additions of potassium, aluminum, and silicon as oxides (referred to as dope) to tungsten have been known for several decades to have a very large effect in raising the recrystallization temperature and altering the recrystallized grain morphology of heavily drawn wire. Previous investigations of this doping effect1 6 have led to various speculations but all failed to deduce unequivocally the physical state or the mechanistic influence of the dopant. Recently, walter7 has observed, by transmission electron microscopy, strings of "fine particles" in heavily rolled and annealed doped tungsten sheet and concluded that they were particles of mullite (Al6Si2013). His conclusion was inferred from the electron diffraction patterns of large particles ex-trated by carbon replication of fractured surfaces of slabs rolled from sintered ingots. That the strings of "fine particles" in heavily rolled and annealed sheet were also mullite was an assumption for which no evidence was presented. A similar investigation has been carried out in this laboratory over the past 2 years on a variety of tungsten wire: doped tungsten, and undoped tungsten, as well as 218 doped tungsten purchased from the Lamp Metals and Components Department of the G.E. Lamp Division. Although the electron microscope observations are similar to those reported by Walter, the writer has reached a different conclusion concerning the physical state of the dopant in annealed tungsten. The purpose of this communication is to present evidence that the strings of "fine particles" observed in transmission specimens are not mullite, but are voids. In the present investigation, tungsten wire, 0.88 mm in diam, was rolled into ribbon 0.2 mm by 125 µ thick. The ribbons were annealed in vacuo at a pressure of -1 x 10-5 Torr and then thinned electrolytically in a 2 pct KOH solution. Fig. 1 shows a typical transmissicjn electron micrograph of a sample annealed at 1700°C for 30 min which reveals rows of closely spaced voids having a light contrast (referred to as "fine particles" by Walter) aligned parallel to the working direction. Stereo micrographs (by D. Moon, Westinghouse Research and Development Center) have shown that these voids do not exist on the surfaces of the specimens as a result of thinning but are within the thin-foil specimens. The following experiments have been performed to verify that these are indeed voids. I) Effect of Annealing. Voids are absent in unannealed specimens and appear only after annealing. This behavior cannot be explained if they were solid particles such as mullite. Precipitation (in an unquenched specimen) upon annealing requires solute elements having decreasing solubilities with increasing temperature. Although the solubility of aluminum in tungsten does decrease with increasing temperature, precipitation requires a concentration in excess of 1.4 wt pct,8 which is at least two orders of magnitude higher than the aluminum content in doped tungsten. It is also unreasonable to assume that particles aligned in rows initially present in unannealed specimens were too

Jan 1, 1968

By V. K. Grotzky, F. J. Fraikor

A number of investigators have noted the importance of various precipitation reactions on the properties of commercial-purity beryllium.1-5 Carrabine, for example, has demonstrated the interaction of iron and aluminum on the mechanical properties of hot-pressed polycrystalline beryllium.6 He considered the determining factor on elevated-temperature properties to be a reversible AlFeBe, precipitation reaction which could be directly related to the Fe/Al impurity ratio of the beryllium. Any aluminum in excess of the stoichio-metric amount required to form A1FeBe4 was presumed to remain primarily in the grain boundaries. We have observed, by transmission electron microscopy, such a grain boundary effect after various heat treatments of beryllium sheet. The starting material in this investigation was bare-rolled beryllium ingot sheet (0.001 to 0.005 in. thick), in contrast to the hot-pressed powder utilized by Carra-bine. It should be noted from the ingot sheet analysis shown in Table I that the Fe/Al weight ratio was near unity which would provide some free aluminum although the total aluminum and iron content was still small. Fig. l(a) shows some aluminum or aluminum-rich precipitates in the grain boundaries of a beryllium foil which had been quenched from 1200°C into brine at -TPC. Similar grain boundary precipitates were found, particularly at grain boundary intersections, in other samples quenched from 1100° and 1000°C. The length of annealing time at these elevated temperatures did not appear to substantially alter the amount of grain boundary precipitates, thus attesting to their relative insolubility. No matrix precipitates were observed other than the normal BeO and Be2C inclusions. A microprobe analysis of the larger precipitates at

Jan 1, 1968

By W. A. Nordland

BISMUTH can be readily grown into single-crystal form using the so-called "quick freeze" growth method.&apos; Some advantages of this method are that very large crystals can be grown in a relatively short time, and with comparatively simple apparatus. We have found the general quality of crystals grown by this method to be not as good as that of "pulled" crystals.&apos; This communication describes a "quick-freeze"

Jan 1, 1968

By J. Warner, M. J. Marcinkowski, B. Cullen, T. Prevender, J. Mcllwain, T. Carnahan, J. Pahlman, J. Demel, J. Munford

The following analysis was an outgrowth of a midterm examination given by one of the authors (M.J.M) in a course entitled Metallurgy 541 "Applications of Dislocation Theory&apos;&apos; at Iowa State University. Fig, l(a) shows the three-layer sequence of atoms lying in the (111) plane which characterizes the fully ordered AB3 fcc crystal, i.e., LI2 type. If any two-layer sequence of close-packed planes is constructed from Fig. 16)&apos; the structure would be hcp of the DO,, type. Consider for convenience that the circled atoms lie in the plane of the drawing while those shown square and triangular lie immediately above and below the plane of the drawing, respectively. It has already been shown&apos; that if a Shockley partial dislocation is passed over the plane of the paper, then the square atoms in Fig. 1(a) are displaced from their original positions as shown by the arrows in Fig. l(b). Not only is an intrinsic fault produced but the crystal is simultaneously disordered across the slip plane. In particular, 2AB bonds are converted to 1AA and 1BB bonds when referred to the area outlined by the solid line in Fig. 1. If, on the other hand, a Shockley partial is allowed to pass immediately above and immediately below the plane of the paper so as to displace the atoms in opposite directions as shown in Fig. l(c), an extrinsic fault is producedZ and twice the amount of disorder is introduced into the crystal as compared to the dislocation-produced intrinsic fault, if only broken first-neighbor bonds are counted. If an intrinsic stacking fault is produced by removing a close-packed plane of atoms in Fig. l(a) and displacing the two adjacent planes by 1/3a0[111], no wrong nearest-neighbor bonds are produced. Similarly, if an extra half plane of atoms with the same arrangement as any of those shown in Fig. l(a) is inserted between any two planes in the same figure, then an extrinsic stacking fault is produced in which once again no wrong nearest-neighbor bonds are produced. The latter two faults are bounded by Frank partial dislocations. Since, at least in the alloy CU3AU,3 nearly all of the ordering energy resides in the first nearest-neighbor interactions, intrinsic and extrinsic stacking faults and associated APB&apos;s of the Frank type are expected to have significantly lower energy than those of the Shockley type in CusAu in particular and quite likely in L1, and DO19 type alloys in general. Also, because of the higher degree of disorder plus loop interaction

Jan 1, 1968

By R. DiBella, H. Biloni, G. F. Bolling

A study of the detailed relationship between solidification substructure and microsegregation in dilute tin alloys has been continued. New observations reveal that depressions form at the solid-liquid interface not only as an initial form of segregation but throughout the range of increasing constitutional supercooling. In order to show the importance of this node formation it proves convenient to make two simplifications. Although substructure changes continuously as constitutional- supercooling increases,&apos; the following discrete stages may be used for discussion: 1) the planar solid-liquid interface; 2) ordered nodes, or depressions at the interface;&apos; 3) two-dimensional or elongated cells;3 4) regular or hexagonal cells;4 5) distorted cells, or hexagonal cells with branches;4 6) dendrites. It is also convenient to ignore observations made near grain boundaries which interact with the cellular substructure.2-4 And, it should be clearly pointed out that all singular depressions at the solid-liquid interface will be called nodes. Heretofore, the term "node" has been used without clear justification to describe both the truly isolated depression and the junction of cell walls appearing in a later stage of segregation. This usage is continued because it seems proved by the observations. Standard systematic growth of tin crystals was undertaken over a broad range of constitutional supercooling using various added solutes. Except for one or two chance observations, this research failed to reveal any appreciable range of growth conditions over which a disordered array of isolated nodes exists. Even though &apos;some finite range of random instability must exist, it is now concluded that stage one passes very rapidly to stage two. Next, after confirming that stage two passes to stage three by the elongation of isolated nodes: a reexamina-tion of stages three, four, and five followed. Standard metallography showed that pockets of higher solute concentration (for ko < 1) became more numerous in cell walls the more severe the growth conditions. These high-concentration regions must arise from depressions; however, in stage three their segregation is not distinguishable from the segregation of the nodes which join cell walls together. It seems, therefore, that the presence of nodes is causal in the formation of new cell walls, and that the mechanism by which stage three passes to stage four is initiated by nodes. If a similar reasoning is followed, the separation of stage four from stage five appears to be just a convenience that has arisen from the decanted interface observations made in the past. The present observations again show that more severe growth conditions relate directly to an increase in the number of nodes in the hexagonal cell walls. These nodes apparently serve as the origin for lines of segregation extending within the body of a cell, and can thus be assumed to represent the earliest form of branching,* as shown here in Fig. 1. The examination of stage six involved decanted-interface structures as in Fig. 2, which are similar to those considered by Rutter and Chalmers,5 Plaskett and winegard,6 and Hellawell and Herbert,7 and where distinct protrusions are each surrounded by a depressed boundary. The corresponding microsegregation behind the interface, but not far enough behind to allow a smearing of the segregation because of diffusion,4 is shown in Fig. 3. Both the shape of the decanted interface and the segregation pattern behind it

Jan 1, 1968