Search Documents

By R. J. Fruehan, F. D. Richardson

Electrochemical measurements have been made of the activity of oxygen in copper and its alloys with silver and tin at 1100" and 1200°C. The galvanic cell used was Pt, Ni + NiO/solid ellectrolyte/[O] in metal, cermet, Pt The results do not support any of the equations so far designed for predicting the activities of dilute solutes in ternary solutions from activities in the corresponding binaries. If, however, a quasichemical equation is used with the coordination number set to unity, agreement between observed and calculated activities shows that this empirical relationship can be useful over a fair range of conditions. SEVERAL solution models have been proposed for predicting the activity coefficients of dilute solutes in ternary alloys from a knowledge of the three binary systems involved. Alcock and Richardson1 have shown that a regular model, and a quasichemical model,' in which the dissolved oxygen is coordinated with eight or so metal atoms, can reasonably predict the behavior of both metal and nonmetal solutes when the heats of solution of the solute in the separate solvent metals are similar. But when this is not so, neither model gives useful predictions unless coordination numbers of one or two are assumed. Wada and Saito3 subsequently adopted a similar model to derive the interaction energies for two dilute solutes in a solvent metal. Belton and Tankins4 Rave proposed both regular and quasichemical type models in which the oxygen is bound into molecular species, such as NiO and CuO in mixtures of Cu + Ni + 0. However, their models have only been tested on systems in which the excess free energies of solution of the solute in the two separate metals differ by a few kilocalories. Ope of the reasons why more advanced models have not been proposed is because few complete sets of data exist for ternary systems in which the solute behaves very differently in the two separate metals. For this reason measurements have been made of the activities of oxygen dissolved in Cu + Ag and Cu + Sn. Measurements on both systems were made by means of the electrochemical cell, Pt, Ni + NiO/solid electrolyte/O(in alloy), cermet,Pt [1] The activity of oxygen was calculated from the electromotive force and the standard free energy of formation of NiO, which is accurately known.5 Before investigating the alloys, studies were made of oxygen in copper to test the reliability of the cell and to check the thermodynamics of the system. Of the previous studies those by Sano and Sakao,6 Tom-linson and Young,7 and Tankins et al.8,7 have been made with gas-metal equilibrium techniques; those by Diaz and Richardson,9 Osterwald,10 wilder," Plusch-kell and Engell,12 Rickert and wagner,13 and Fischer and Ackermann14 have been made by electrochemical methods. EXPERIMENTAL The apparatus employed was the same as described previously,9 apart from slight modification. The molten sample of approximately 40 g was held in a high grade alumina crucible 1.2 in. OD and 1.6 in. long. The solid electrolytes were ZrO2 + 7½ wt pct CaO and ZrO2 + 15 wt pct CaO; the tubes 4 in. OD and 6 in. long were supplied by the Zirconia Corp. of America. They were closed (flat) at one end. In one experiment with Cu + O, both electrolytes were used in the cell at the same time. The reference electrodes inside the electrolyte tubes consisted of a mixture of Ni + NiO. They were made by mixing the powdered materials and pressing them manually into the ends of the tubes, with a platinum lead embedded in them. The tubes were then sintered overnight in the electromotive force apparatus at 1100°C. By sintering the powders inside the tubes (instead of using a presintered pellet9) better contacts were obtained between the electrolyte, the powder, and the platinum lead. Troubles arising from polarization9 were thus much reduced. The electromotive force was measured by a Vibron Electrometer with an input impedence of 1017 ohm; the temperature was measured with a Pt:13 pct Rh + Pt thermocouple protected by an alumina sheath. The couple was calibrated against the melting point of copper. The cermet conducting lead of Cr + 28 pct Al2O3, previously found to be satisfactory9 for use with Cu + 0 was also found satisfactory with Cu + Ag + 0 and Cu + Sn + 0. Superficial oxidation was observed, but it did not interfere with the working of the cell. The reaction tube containing the cell was closed at each end with cooled brass heads and suspended in a platinum resistance furnace. The tube was electrically shielded by a Kanthal A-1 ribbon which was wound round it, and the ribbon was protected by a N2 atmosphere between the furnace and the reaction tube. The cell was protected by a stream of high purity argon which was dried and passed through copper gauze at 450°C and titanium chips at 900°C. All the metals used were of spectrographic standard. Procedure. In studies of the system Cu + 0, be-

Jan 1, 1970

By R. E. Cech, T. D. Tiemann

It has been shown that hydrogen may be made to serve as a rapid and eflicient reducing agent for Cu, Ni, Co, and Fe sulfides if a scavenging agent for hydrogen sulfide is intimately mixed with the sulfide particles being reduced. Accelerated reduction kinetics are demonstrated for nickel sulfide. Copper, nickel, and cobalt sulfides, when treated at certain temperatures in a combined reducing agent-scavenging agent system, are converted to voluminous masses of fibrous metal product. Studies have been carried out to determine the conditions which lead, on the one hand, to irregular poly crystalline fibers and, on the other, to long single crystal filaments a few microns in diameter. A mechanism is proposed to account for the formation of single crystal filuments. The sulfide minerals of Cu, Ni, Co, and Fe are an important source of these metals yet there has been comparatively little scientific effort devoted towards understanding reduction mechanisms of these minerals. This may be, in part, due to the fact that the most convenient reducing agents for carrying out such studies, viz., hydrogen and carbon, do not react appreciably with sulfides. We have found that the reaction of hydrogen with metal sulfides can be markedly accelerated by placing a scavenging agent for hydrogen sulfide in close proximity to the metal sulfide. A brief series of experiments demonstrating relative reduction rates is reported in this paper to illustrate the effect. With the reduction process thus accelerated we have observed an unusual type of reduction behavior on some of the sulfides investigated. Under certain conditions the metallic product of the reduction reaction takes the form of filaments growing outward from the sulfide particles. The present paper deals largely with efforts to classify the various types of growth forms observed. This study has shown that filamentary growths from sulfides take a much greater variety of forms than has heretofore been reported by Ercker,1 Hardy,2 and Nabarro and Jackson3 in their reviews of metallic growths from copper and silver sulfides. THERMODYNAMIC CONSIDERATIONS The thermodynamics for hydrogen reduction of metal sulfides is quite unfavorable. For the sulfides considered here equilibrium constants typically range from 10-3 to 10-5. These low equilibrium constants impose severe kinetic limitations on reduction since hydrogen sulfide must be transported out of the system at concentrations of only a few hundred ppm. Unless extremely high gas flow rates are employed the atmosphere surrounding any sulfide particle will always be essentially in equilibrium with the sulfide. If, however, one places an efficient scavenging agent for hydrogen sulfide in close proximity to the metal sulfide particles the concentration of H2S near the metal sulfide will be held to a very low value. This would permit the reduction reaction to proceed with little or no inhibition from a buildup of reaction product gas. It is well known that calcium oxide is capable of removing hydrogen sulfide from a hydrogen gas stream of low dew point.4 If a sufficient quantity of calcium oxide is mixed with the metal sulfide particles the reaction: CaO+H2S=CaS+ H2O [l] will substitute moisture in place of hydrogen sulfide in the gas stream and this will not affect, in a direct manner, the reaction: MeS +H2=Me + H2S [2] A convenient method of considering the thermodynamics of the combined reducing agent-scavenging agent system is to consider the atmosphere when the partial pressure of hydrogen sulfide is the same over both the metal sulfide and the scavenging agent, i.e., pH2S (1) =pH2S (2). As a consequence: pH2O (1) pH2(2) =K1K2 The chemical driving force for reduction will depend inversely upon the moisture content of the gas and will be 0 when, in the system, pH2O = pH2.K1K2. Table I lists values of the equilibrium constants for reduction and H2S scavenging reactions for a number of sulfides at several temperatures. Data are taken from Rosenqvist4,5 and Kelly.6 The equilibrium constant products calculated from this data show that the limiting level of gaseous reaction product has been increased by a factor of 10' to l04 as a result of substituting a reducing agent-scavenging agent system for a simple reducing agent system. One possible side effect which must be considered is the possibility that the moisture evolved in the scavenging reaction might cause the atmosphere in the system to be sufficiently oxidizing to favor the formation of oxide rather than metal. This possibility was examined by comparing the equilibrium constant products listed in Table I with equilibrium constants for hydrogen reduction of the respective metal oxides. It was found that for copper, nickel, and cobalt the combined reduction-scavenging reactions could not develop a sufficiently high oxidizing potential in the

Jan 1, 1970

By J. E. Gruzleski, O. Knacke, M. J. Meixner

The evolution of CO from small specimens of solidifying steel was investigated using a thermobalance technique. Gas evolution begins in the temperature range between 1400" to .1450°C. This behavior is independent of the initial carbon content and the cooling rate. At a constant temperature above 1220°C, the rate of gas evolution is temperature independent. Out-gassing of the specimen is thought to proceed through small channels formed by the coalescence of bubbles between dendrites. LIQUID metals have a higher solubility for gas than the solid. During freezing, these gases form bubbles which may either escape or remain trapped in the solid. Recent work1 on the evolution of oxygen from solidifying silver showed that the gas is not liberated until a large fraction of the melt has solidified, and that the gas is evolved in an almost explosive manner. Because of the commercial importance of CO evolution in solidifying steel, a similar investigation was undertaken to study the mechanism of gas liberation in steel. EXPERIMENTAL The thermogravimetric method of Knacke and eixner1 to follow gas evolution by weight changes was employed. Weight differences of 0.1 mg could be reproducibly measured on specimens weighing 2.5 g. These specimens were taken from alloys with varying carbon contents from <0.01 to 0.11 wt pct and <0.01 wt pct of each of silicon, manganese, and aluminum. Specimens contained in 8 mm ID magnesium alumi-nate crucibles were heated to 1550°C under 1 atm of very pure (99.995 pct) CO with a tungsten resistance furnace. The specimen temperature was measured with a Pt-Pt/Rh thermocouple located directly beside the crucible. It is felt that the temperature thus measured was within 5" to 10°C of the specimen temperature since on fusion the weight of the specimen increased due to uptake of CO, and this weight increase was always observed to begin within the temperature range of 1530" to 1540°C. Even after 3 hr there was a small weight increase with time indicating that the molten specimen was not completely saturated with CO. Therefore, complete saturation was not attempted, and all specimens were simply held for 3 hr at 1550°C before cooling. Two types of cooling experiments were performed. One consisted of continuous cooling at linear rates from 5°C to 20°C per min down to 1020°C. The second type of experiment involved continuous cooling at 10°C per min to a predetermined temperature, and then holding the specimen at this temperature for a certain time. During all of these experiments, the sample weight was recorded as a function of time and temperature. OBSERVATIONS Continuous Cooling Experiments. No gas evolution was detected above 1450°C. The initial weight decrease always occurred between 1400" and 1450°C with the average at 1430°C. With further cooling, gas evolution continued to about 1150°C. Between this temperature and 1020°C no further outgassing was observed. This behavior did not seem to depend on the initial carbon content nor on the cooling rate in the range investigated. Typical patterns of gas evolution are shown in Figs. 1 and 2 for different initial carbon levels and cooling rates. The total amount of gas liberated during solidification varied with the rate of cooling. The total weight change on continuous cooling at a rate of 10°C per min

Jan 1, 1970

By Robert A. Rapp, Ronald L. Pastorek

Solid-state electrochemical measurements by three alternative experimental procedures were made with the cell FeO, Fe3O4 |Zro.85Cao.15O1.85 |Cu| Zr0.85CaO.15O1.85 | FeO, Fe304 to establish the solubility and diffusivity of oxygen in solid copper in the temperature range 800" to 1030°C. The solubility of oxygen in solid copper and the diflusivity of oxygen in solid copper Dgu = 1.7 X 10-2 exp(-16,000/RT) Cm2/sec were determined and confirmed in alternative experiments. The enthalpy of solution of oxygen in solid copper equals —10,000 cal per mole; the partial excess entropy of the oxygen atoms in the Cu-O dilute solution is approximately the same as that found for interstitial atoms in other metals. The diffusivity of oxygen in solid copper is consistent with that expected for an interstitial atom. RELIABLE values for the saturation solubility N(s) and diffusivity DO of oxygen in solid copper have not been unambiguously established in the literature. Following three early determinations by others,1"3 Rhines and Mathewson4 reported that the solubility of oxygen in solid copper increased from 0.007 at. pct 0 at 600°C to about 0.015 pct at 1050°C. Phillips and skinner,, using essentiially the same analytical procedure, reported that the solid solubility increases from 0.0018 at. pct 0 at 550°C to about 0.0075 pct at 1050OC. The only previous value for the diffusivity of oxygen in solid copper was reported by Ransley.6 Ransley deoxidized Cu-Cu2O alloys in an atmosphere of carbon monoxide gas to yield a solubility-diffusivity product. He used the solubility data of Rhines and Mathewson to calculate the diffusivity values. Another method for obtaining the solubility-diffusivity product (N(s) DO) is by measuring the widths of internal-oxidation zones in copper alloys as reported by Verfurth and Rapp.7 However, the calculated N(S)Do products depend upon the alloy content of the specimen, so that the internal oxidation of copper alloys does not follow ideal internal oxidation kinetics. As a result, unequivocal values for the N(s) DO product were not obtained by this procedure. A solid-state coulometric titration technique similar to that employed in this work was introduced by C. Wagner8 to study the dependence on silver activity of the Ag/S ratio in silver sulfide in the temperature range of 160" to 300°C. Similar experiments have been carried out by C. Wagner and co-workers9-11 to study the stoichiometry range of silver and copper tellurides, cuprous sulfide, and cuprous selenide. Numerous authors have carried out electrochemical measurements with a solid oxygen-ion-conducting electrolyte to determine the solubility and/or diffusivity of dissolved oxygen in several liquid metals.12-l6 Rickert and Steiner17,18 have used solid-state electrochemical measurements to determine the diffusivity of oxygen in solid silver from 760" to 900°C. Two different cell geometries were used. In the cell of linear geometry Fe, FeO | ZrO2 + (CaO) | Ag + [0 (dissolved)] [1] oxygen diffused from the interior of the silver electrode to the silver/electrolyte interface where the oxygen activity had been lowered from a fixed initial value to practically zero by the application of voltage to the cell. The diffusivity of oxygen in solid silver was determined from the solution of the diffusion equation and the time dependence of the cell current. However, this determination of the diffusion coefficient depended upon a knowledge of the solubility of oxygen in solid silver. A cylindrical geometry was used for the cell Pt, O2(Po2 = 0.21 atm) | ZrO2 + (CaO) | Ag + [0 (dissolved)] [II] which also allowed the diffusivity of oxygen in solid silver to be determined. These values were in agreement with other available data.l9 Recently, Raleigh20,21 used a method involving the measurement of diffusion-limited currents in a cell involving the AgBr solid electrolyte to determine the diffusion coefficient of silver in Ag-Au alloys at 400°C. Diffusivity values on the order of l0-14 sq cm per sec were measured in the alloy composition range 10 to 60 at. pct Ag in a single experiment. From numerous electrical conductivity and galvanic cell measurements,9&apos;22"26 the solid solution Zr0.85 Ca0.15 O1.85 has been established as an electrolyte with predominant oxygen ion conduction over a wide range of intermediate and high oxygen activities. For interrelating the thermodynamics and the kinetics of the dissolution of oxygen in solid copper in this investigation, a galvanic cell was constructed with FeO-Fe3O4 as the reversible reference electrode, the Zr0.85Ca0.15 O1.85 electrolyte, and a pure copper specimen under-saturated in oxygen as the other electrode. THEORETICAL ANALYSIS Three variations of a high-temperature electrochemical technique were used in this study to provide two determinations each of the solubility and diffusivity

Jan 1, 1970

By G. L. F. Powell

g samples of Cu-20 wt pct Ag alloy have been mdercooled to a maximum of 197°C by melting under a slag of commercial soda-lime glass in a vitreous silica crucible. No grain refinement of the primary copper was observed in samples undercooled to the maximum of 197°C. When the samples contained a small amount of oxygen, the copper dendrites were partially recrystallized at undercoolings greater than 97°C. In previous papers&apos;-3 reporting the grain structure of undercooled silver and copper, it was observed that grain refinement was dependent on both undercooling and oxygen content. Grain refinement occurred in undercooled silver when the degree of undercooling exceeded the range 153" to 175"C, while in Ag-0 alloys (0.12 wt pct) fine equiaxed grains were exhibited when undercooling was greater than 50°C. Similarly, copper samples undercooled as much as 208°C displayed fan-shaped growth from a single nucleation site, while the grain structure of Cu-O alloys (0.08 wt pct) was fine and equiaxed at undercoolings larger than 150°C. Thus the presence of oxygen greatly reduced the undercooling at which grain refinement occurred. It was also observed that the change in grain size resulted from recrystallization and was not due to an enhanced nucleation rate in the liquid-solid transformation. It is possible that the influence of oxygen on recrystallization is due primarily to its presence as a solute element. walker4,&apos; reported that, although a grain size change did not occur in pure nickel until the undercooling exceeded 150°C, small grains were observed in samples of Ni-Cu alloy solidified at small and large degrees of undercooling. Jackson et al.6 suggested that the fine grained structure of the Ni-Cu alloy resulted from the melting off of dendrite arms during recalescence. This remelting process may occur in alloys as a result of segregation during freezing which causes a variation in liquidus temperature from point to point within a dendrite. It was therefore decided to undercool copper with a metallic alloying element to ascertain whether the presence of a metallic solute would have a similar effect to oxygen in inducing grain refinement. A Cu-Ag alloy was chosen, since both metals had been shown to behave similarly on undercooling. The alloy Cu-20 wt pct Ag was selected since the eutectic constituent outlines the initial growth form of the primary copper, so that the as-frozen grain structure is not obscured if subsequent recrystallization occurs. This paper describes the results of undercooling experiments carried out with Cu-20 pct Ag samples undercooled to a maximum of 197°C and the effect of oxygen content on the grain structure of the undercooled samples. EXPERIMENTAL Melting was carried out in a small cylindrical resistance furnace using "fine" silver granulate and oxygen-free high conductivity copper. The procedure adopted was to melt the required quantity of silver in air in a clean vitreous silica crucible for approximately 15 min, freeze, and add granulated commercial soda-lime glass to form a complete surface slag cover, after which the sample was melted and frozen several times to reduce the oxygen content. The glass slag cover was approximately 3 in. thick. Pieces of copper (=50 g) were added to the crucible until the required quantity to make 350-g samples of alloy had been charged. Each piece was added quickly to the crucible which was held at a temperature slightly above the melting point of silver. The piece was quickly pushed beneath the glass to minimize oxidation and any oxide coating usually decomposed before the piece had settled down into the silver. After the full quantity of copper had been added, the melt was stirred with a silica rod to hasten homogenization and a Pt/Pt 13 pct Rh thermocouple enclosed in a vitreous silica sheath inserted for temperature measurement. Heating and cooling curves were recorded on a potentiometric chart recorder fitted with a zero suppression unit. The milli-voltage range of the recorder was adjusted so that temperatures could be read to 1°C. Heating and cooling curves were taken every hour until three consecutive readings gave the same solidus-liquidus range, consistent with the solidus-liquidus range for this alloy composition by reference to Hansen and Anderko.7 Metallographic examination of samples frozen at this stage, failed to show any variation in composition from bottom to top of the ingot. Consequently, it was considered that the melt was homogeneous at this stage and undercooling experiments were then car-

Jan 1, 1970

By P. Shahinian, R. L. Stegman, M. R. Achter

Creep strength has been determined as a function of oxygen pressure for nickel at 510" and 600°C. Creep-rupture life drops from its highest value at the ultimate vacuum of 10-7 torr to a high pressure plateau of nearly constant life which, at 600°C, commences at torr. This behavior is described in terms of a model that relates surface gas adsorption and the generation of fresh crack surfaces. In a calculation based a this model the predicted pressure beyond which the creep strength should not decrease further has been found to agree well with the observed value. The introduction of oxygen during creep in vacuum was found to cause a prompt rise of the creep rate. The magnitude of the environmental effect was much less than generally observed in fatigue and this is attributed to the diffarent crack morphologies in creep and fatigue. GASEOUS environments are known to affect creep resistance adversely1-5 but the effects have received less attention than the much larger ones in fatigue. At low temperatures it has been shown for nickel that the creep rates are faster and the rupture lives are shorter in air than in vacuum and that these environmental effects can be correlated with faster crack growth rates in the reactive environment.&apos; In support of a mechanism of gas adsorption at the crack tip to explain the above effects, a calculation based on kinetic gas theory showed that surface coverage by gas was not as rapid as the exposure of fresh metal at the crack tip in the ultimate vacuum but was in air.7 In fatigue a number of investigations have demonstrated that the reduction of life with gas pressure usually follows a step curve with most of the reduction occurring in a transition range at intermediate pressures and little or no change at high and low pressure.8 There have been no studies, however, in which creep strength has been determined as a function of reactive gas pressure to see whether similar effects would be found. This investigation was undertaken to study the kinetics of the environmental effect in the creep of nickel. EXPERIMENTAL PROCEDURES The environmental creep apparatus was constructed to minimize many of the experimental conditions which can cause scatter in data. Dead weight loading is employed and weights are contained within the environmental chamber to eliminate bellows and the necessity for compensation for gas pressure changes. Elongation over the specimen gage length is recorded from a Riehle Model DV Controlled Environment Extensometer which provides readout to 2.5 x 10- in. Temperature is monitored and controlled from a thermocouple at- tached to the specimen gage length to +0.5oC or better. The freon trapped oil diffusion pump vacuum system included an auxiliary liquid nitrogen trap and, with a wide range variable conductance leak valve, pressures from the ultimate vacuum of 10"7 to l03 torr of any desired gas are obtainable. Pressure is measured by means of a hot filament ionization gage below 10"3 torr and a NRC Model 530 Alphatron Vacuum Gauge above 10-3 torr. The oxygen, which was leaked into the environmental chamber, was an Aviator&apos;s Grade of 99.5 pct purity with a dew point of -80°F. Analysis of the nominal 99.8 pct Ni showed the following percentages of major impurities: 0.02 C, 4.01 Mn, 0.005 Si, 0.01 Cu, 0.02 Fe, and 0.034 Mg. Cylindrical specimens were machined with a 0.180

Jan 1, 1970

By M. J. Mullikin, J. B. Conway

Several different equation forms were studied to determine the extent to which each particular equation type yielded an accurate representation of a given set of first-stage creep data. Specially developed least-squares computer programs were employed to obtain unique solutions for the creep-equation constants. In studies of creep data for lead at 14.5"C, nickel at 70OCC, and arc-cast tungsten at 2400°C consistently good representations were afforded by a third-degvee polynomial in t113. Other effective correlations were obtained with the Andrade, Cottrell-Aytekin, and de Lacombe equations along with a third-degree polynomial in t112. A newly proposed creep equation involving a hyperbolic-sine term in t1&apos;3 was also found to yield very satisfactory results. This appears to be the first use of such a functional relationship in the analysis of transient creep behavior. In general, the deformation behavior of a material subjected to a tensile load is described in a strain-time plot. Experiments have shown that, following the instantaneous elongation which results on loading, the instantaneous slope (i.e., creep rate) of the strain-time curve decreases gradually with time and approaches what appears to be a constant value. Equations, therefore, which are proposed to provide an analytical representation of such first-stage or transient creep behavior must be consistent with these observations. In other words, at time zero, these equations must yield a finite deformation value corresponding to the elongation on loading. Furthermore, the first derivative of these equations must exhibit a fairly high although finite value at time zero, and then values which decrease with time. It is also preferable, in general, that the derivative eventually assume a constant value at high time values. Although many studies of first-stage creep behavior have been made and numerous equation forms have been proposed for expressing this type of deformation behavior, it is still not possible to state with any assurance which functional relationship will be adequate for a given set of measurements. Parabolic relationships have been employed most extensively although logarithmic expressions have been shown to be applicable in some instances. Combined forms1 have been studied in considerable detail and have on occasion been found to be very effective. One such expression is that of iXndradea and involves a modified parabolic expression: where 1 is the instantaneous length, lo is the length immediately following load application, t is the time, and p and k are constants. Another combined form has been proposed by weaver3 as follows: where E is the instantaneous strain, is is the linear creep rate, t is the time, and a and b are constants.

Jan 1, 1967

By Raymond L. Orr

Calorimetric measurements have been made of the heats of solution of gold axd indium in a number of liquid tin-rich alloys at a temperature of 705°K. Relative partial molar enthalpies of gold were determined as a function of dilute solute concentrations in the binary Au-Sn system and in the ternary Ag-Au-Sn and Au-In-Sn systems. Relative partial molar enthalpies of indium were determined for dilute solute concentrations in the In-Sn, Ag-In-Sn, and Au-In-Sn systems. Through application of the interaction coefficient concept introduced by Wagner and more recently extended by Lupis and Elliott, ualues have been obtained for the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. The results are inte@reted in terms of solute atom distributions through comparisons with the predictions of dilute solution models. INTEREST in the thermodynamic behavior of dilute liquid alloys stems from two primary sources. From a practical viewpoint, it is often of importance to know or to be able to predict the effect that one solute will have on the thermodynamic properties of the other solutes in a multicomponent system. Studies of dilute solutions may also be rewarding from the theoretical point of view. Some of the difficulties arising from the more complex interactions possible in concentrated solutions are avoided, leading to easier interpretations in terms of solutibn models and bonding energies. For example, in a binary alloy the limiting values of the partial molar properties of the solute represent the case for which each solute atom is completely surrounded by atoms of the solvent, and no other interactions are possible. Solute - solute interactions in dilute solutions are conveniently treated by the interaction coefficient concept of ~agner.&apos; Using a Taylor series expansion for the logarithm of the activity coefficient, In yi, of a component, i, in a solution consisting of dilute solutes with atomic fractions xi, xj, xk, and so forth, in a solvent, s, and neglecting the second- and higher-order terms, Wagner obtained the expression: Where Wheyz is the limiting value of yi in the pure solvent, s. The interaction coefficients, e:, e:, and so forth, are defined by: Since yi is related to the excess partial molar Gibbs energy of component i by GfS = RT In yi, E: is re- ferred to as the "Gibbs energy interaction coefficient". Lupis and Elliott~ extended Wagner&apos;s treatment to the relative partial molar enthalpy, aHi, and the excess partial molar entropy, qS. They defined the enthalpy interaction coefficient as: and the excess entropy interaction coefficient as: leading to expressions similar to Eq. [I]: The three interaction coefficients are related by? The self-interaction coefficients, E:,qf,and at, represent the effects of interactions between atoms of component i in solvent s; €3, q{, and 03 represent the effects of interactions between i and j atoms in solvent s; and so forth. From the Maxwell-type relationships between partial molar quantities, it may be shown1&apos;2 that e{ = ej, r}\ =tj), and ai - crj. Experimental determination of the interaction coefficients requires extremely precise measurements of the appropriate properties as functions of solute concentrations in very dilute regions. Few such data exist for intermetallic alloys, even for binary systems, because of experimental difficulties. This is especially true with respect to enthalpy data for dilute alloys. Examination of the compilation of data for binary alloys by Hultgren, Orr, Anderson, and ~elle~~ reveals that determination of limiting values of &fii(Xi =0) often requires extrapolations to infinite dilution from xi = 0.05 to 0.10. Direct measurements of the enthalpy interaction coefficient, qi, for multicomponent systems are virtually nonexistent. This quantity is of course subject to direct calorimetric measurement, but its determination must be limited to cases where high experimental precision is possible. The heats of solution of gold and indium in liquid tin can be measured with relatively high precision, which makes determinations of 73 involving these metals as the measured solutes experimentally attractive. This paper presents the results of such determinations of the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. MODELS FOR DILUTE-SOLUTION BEHAVIOR Random-Solution Behavior. In the quasi-chemical treatment of solutions, only nearest-neighbor bonds are considered, and a composition independent value

Jan 1, 1967

By G. R. Love, M. L. Picklesirner

THE use of color adds a new beauty, power, and versatility to metallography. This has been amply demonstrated in a number of public exhibits and on the walls of corporate, government, and university metallographic laboratories around the world. Indeed, in a number of cases, the color not only is of esthetic value but is scientifically essential to the competent examination of particular samples and systems. Optical strain analysis,&apos; determination of true grain size in U-A1 alloys: phase identification in Nb-base alloys,3 analysis of transformation rates in heat-treated Nb-Zr alloys,4 measurement of solidification segregation in cast Nb-Zr alloys,&apos; study of the intermediate phases in Nb/Sn diffusion couples,6 investigation of the oxidation kinetics at various surface orientations in single crystals,7&apos;8 and a number of other research efforts9&apos;10 would have been vastly more difficult without the extra clarity and distinction introduced by color—either the colors resulting from particular polarized light techniques or the interference colors obtained by oxidation. It is unfortunate that the beauty of colored micro-structures cannot be shared more widely, but the economics of publishing a technical magazine apparently prohibits color plates except under extraordinary circumstances. It is doubly unfortunate that no convenient, general method exists for communicating the information available in colored microstructures to the scientific community. True, in some instances the color changes observed are dramatic enough that direct black and white photography is adequate. In photoelastic stress analysis, several orders of interference fringes may be produced and it is frequently desirable to suppress the color effects (use monochromatic light) to simplify interpretation. On the other hand, relatively minute color variations may be readily detectable by eye, be of considerable assistance in interpreting a structure, and yet be enormously difficult to reduce to an unambiguous black and white print. In order to illustrate a possible compromise or solution to the above problems, we wish to show three black and white photographs of the same region of an Nb/Sn diffusion couple whose interpretation depends heavily upon use of color techniques. These micro-structures were obtained from a section through a rod consisting of commercial-purity niobium tubing filled with 99.995 pct Sn (melt-filled in 10"6 Torr vacuum). The composite rod, measuring 500 mm long, was bent into a hairpin shape and inserted into water-cooled copper grips in a vacuum high-temperature furnace. The rod was outgassed for 2 hr at a furnace temperature of 800°C and was further heated by self-resistance using a 2.2-kva ac power supply. The rod was raised to 1910°C over a 4+-hr period, held for 15 min, slow-cooled to 1500°C over a -hr period, and free-cooled to room temperature (all temperatures were measured with W5Re/W26Re thermocouple). Throughout the heat treatment the ambient pressure was kept below 8 x lo-&apos; Torr. Metallographic preparation of the sample was completely conventional except that it was necessary to extend the grinding steps to remove damage in the brittle NbsSn phase introduced by sectioning. No satisfactory chemical or electrochemical etch has been found for these diffusion couples; of those which have been tried, any that attack the niobium-rich phases at all attack the tin-rich phases disastrously. However, the final polishing steps did produce a slight relief effect and this, coupled with anodizing, yielded excellent clarity in the microstructures for direct observation. The anodizing voltage was chosen to give maximum change in color per unit change in composition. In this case, indeed normally, this maximum sensitivity occurred in the blue-to-red color range. The pure niobium tube wall anodized to a relatively bright blue

Jan 1, 1967

By E. Lifshin, R. E. Hanneman

QUANTITATIVE applications of the electron micro-beam probe frequently involve the evaluation of complex mathematical expressions and/or the analysis of large amounts of experimental data. The purpose of this communication is to describe briefly a versatile and useful computer program system that is applicable to analyze rapidly a wide variety of practical microprobe problems. This system consists of a group of ten FORTRAN programs that can be stored on tape, cards, or in the memory disc of the computer. These programs, or links, can be run individually or in any prespecified sequence without interrupting the operation of the computer or without destroying information which is being transfered from one link to another. For the program system described here a GE-235 computer with disc storage was used, so that the DCHAIN method of program linking was employed. Included in the library are programs to: 1) initiate analysis of a new set of data and transfer control between all other programs in any predetermined manner; 2) generate theoretical calibration curves of composition vs relative intensity; 3) generate empirical deviation parameters from least-square fits of experimental calibration data from standards of known composition; 4) convert raw X-ray data to corrected composition; 5) determine inter diffusion coefficients by Matano analysis of con centrat ion -distance data on a uniaxial diffusion couple; 6) determine activation energies and frequency factors of temperature-activated processes such as diffusion; and 7) generate calibration curves for determination of the thickness of thin films using microanalysis. A detailed description of these computer programs and their underlying principles is available on request from the authors."&apos; The first program to generate theoretical calibration curves of corrected relative intensities vs composition uses the Poole and Thomas atomic number correction&apos; and the Philibert absorption factor&apos; with a voltage-dependent mass absorption coefficient for electrons in the alloy. A modified Castaing fluores- cence correction is also used which includes the effects of both Ka and KO radiation and over voltage.&apos; Once the theoretical curves have been calculated in 1 wt pct intervals, these results are least-squares fit to obtain Ziebold deviation parameters&apos; which are stored in COMMON in the computer memory. The net discrepancies between the original theoretical calibration curve and the regenerated curve using the Ziebold parameter are computed. Although this link is explicitly written for K-K fluorescent interactions, it can be applied to K-L, L-K, and L-L interactions as previously disc~ssed."~ Similar programs have also been written to utilize the Wittry fluorescence correction, Birks combined corrections, and various other corrections.&apos; These modified programs have proved to be quite useful for quantitative comparisons of the results of the various theories. The program for conversion of raw X-ray data to corrected composition includes corrections for drift, backround, and instrumental dead time. The corrected intensities are converted to composition by use of the Ziebold equation"2 and parameter obtained from the program system. The results can be obtained for either atom or weight fractions. In addition to accurately computing interdiffusion coefficients the Matano analysis program calculates least-square smoothed values of concentration, concentration gradient, and curvature for each point on the raw input concentration profile. In order to obtain high accuracies a unique method of performing a least-square polynomial fit to incrementally advancing profile segments which overlap is used.&apos; This program has been successfully modified for use in ternary diffusion problems3 and can readily be modified to handle analysis of diffusion profiles which include phase boundary discontinuities. This link is generally applicable to analysis of interdiffusion data obtained by other techniques as well as by the microprobe. The primary function of the next program is to least-squares fit experimental diffusion data to the normal Arrhenius function: D = Doexp(-Q/RT), to obtain values of Do and Q. In addition the probable error and one, two, and three u statistical confidence limits of DO, Q, and log D are evaluated. This program is also directly useful for analysis of any other simple temperature-activated processes including conductivity, and certain deformation and chemical processes. The program to generate calibration curves for film-thickness determination using the microprobe is based on a numerical integration of the equation derived by Cockett and ~avis.&apos; Values of film thickness obtained by this program for copper on various substrates are in good agreement with measurements made by other techniques. Versions of the above program system have been prepared for use with or without a remote teletype connection to the computer for processing on either a real-time or time-share basis. The instrumentation coupling a microprobe to a teletype for automatic data collection and analysis by the presently described program system has been reported elsewhere by the authors.&apos; If teletype equipment is not used to communicate with the computer, standard methods of card reading and tape reading can be used. In either

Jan 1, 1967

By E. R. Gilbert

Klopp et al. have reported data on tensile and creep properties of are-melted and electron-beam-melted tungsten. We would like to point out some similarities between their creep results and ours on are-melted and powder-metallurgy tungstenand offer some alternate interpretations of the data which lead to different rate-controlling mechanisms. Klopp et al. observed extensive transient creep in the 2250" to 3500°F temperature range where the acthetivation energy is 106,400 ± 3300 cal mole-1. They suggest cross slip as the possible rate-controlling mechanism since "cross slip may occur only by the movement of screw dislocations, and not edge dislocations, thus allowing only partial recovery of the strain hardening and resulting in a continuously decreasing creep rate, characteristic of transient creep.&apos;&apos; Our tests on are-melted tungsten and powder-metallurgy tungsten displayed an extensive transient creep stage in the same temperature range but they also displayed a steady-state creep stage. The stress levels and strain rates of the two investigations, 1.4 to 7 kg mm-2 and 10-7 to 10-4 sec-1 for that of Klopp et al. and 4.5 to 10 kg mm-2 and 10-8 to 10-4 sec-1 for those of Gilbert et al., are overlapping. The activation energy for creep of our powder-metallurgy tungsten is 105,000 cal mole-1. This close agreement with the value found by Klopp et al. suggests that the same mechanism may be common to both types of materials. It may be possible to gain some additional insight into the rate-controlling mechanism by applying the analysis made by conrad22 in terms of the activation volume. The value for the activation volume depends upon the dislocation mechanism and may be used to help differentiate between various dislocation mechanisms. The activation volume for cross slip is 10 to 100 b3. Values determined from our data were 130 to 220 b3 which are in better agreement with the range of 102 to 104 b3 for nonconservative motion of jogs. Values determined from data of Klopp et al. are 240 to 1040 b3. We suggest that the rate-controlling mechanism for creep in this temperature range may be nonconservative motion of jogs assisted by enhanced diffusion along grain boundaries or dislocations. This model requires an activation energy lower than that for self-diffusion as is observed. If this is the controlling mechanism, a higher activation energy which is closer to that for self-diffusion might be expected for tests conducted on specimens with reduced grain boundary area, i.e., larger grain size. In support of this premise we have conducted tests on speci- mens having one to three grains per cross section for which a higher activation energy of 130,000 cal mole-1 was observed. Also, in agreement with results of Klopp et al., a faster creep rate resulted from the increased grain size and probable decreased dislocation density. Further argument against the cross slip mechanism is based on the constant activation energy we obsserved over the range of 5.0 to 10 kg mm-2,21 whereas the activation energy for cross slip displays a significant stress dependence.23 In addition to this, the powe on the stress term for the strain-rate dependence appears too high for cross slip. The values for tungsten fall in the range of 4.5 to 7 (Klopp et al. and Ref. 21) whereas values of approximately 2 are observed in creep by cross slip for hep metals.24 At temperatures from 3300° to 4000°F, Klopp et al. observed an activation energy of 141,000 ± 4000 cal mole-&apos; which is less than that for self-diffusion, 153,000 cal mole-1, 25 and less than that reported for high-temperature creep of powder-metallurgy tungsten by Green:&apos; 160,000 cal mole-1. Klopp et al. suggested that recovery of strain hardening by dislocation climb is the rate-controlling mechanism in this temperature region. Actually an activation energy larger than that for self-diffusion is predicted by this model if the temperature dependence of the elastic modulus27 is taken into consideration. Klopp et al. attributed this lack of correlation to the compositional differences between powder-metallurgy tungsten used by Green and their own arc- and EB-melted tungsten. It is our position that the value of 141,000 ± 4000 cal mole-&apos; represents a transitional value between the higher and lower activation energies and does not represent a discrete mechanism of deformation. If the tests had been extended to higher temperatures the higher value of activation energy would have been observed as has been demonstrated by both our analy sis&apos;&apos; of isothermal test data by GE-NMPO28 and differential temperature tests28 on are-melted tungsten. The activation energies determined (170,000 and 160,000 cal mole-1) were greater than that for self-diffusion and are in better agreement with the value found by Green. The model of dislocation climb is associated with ; activation volume of 1 b3 according to Conrad.22 The activation volume calculated for the creep data of fou independent investigators in the temperature range where the activation energy for creep is near that for self-diffusion (Klopp et al. and Refs. 26, 28, and 30) is 110 to 2800 b3 and is in the range suggested for nonconservative motion of jogs. In the case of tungsten this mechanism may be preferred over that of dislocation climb. Sincere appreciation is expressed to Messrs. J. E. Flinn and F. L. Yaggee for the helpful discussions and suggestions in the preparation of this communication.

Jan 1, 1967

By J. E. Flinn, E. R. Gilbert

Recently, Green reported some high-temperature, 0.60 to 0.89 T3, creep results on unalloyed tantalum. From his study he determined an activation energy of 114 kcal per mole for steady-state creep using the T, differential-temperature method25 for testing. He accounted for the difference between this value and 110 kcal per mole for self-diffusion by the temperature dependence of the elastic modulus, 4 kcal per mole. This reported activation energy is in apparent disagreement with that which can be determined from Green&apos;s isothermal data, which we have plotted as log creep rate vs 1/T in Fig. 15. From this figure, it appears that there are two activation energies of -185 kcal per mole at the higher temperatures and -75 kcal per mole at the lower temperatures. It is not obvious that the data can be fitted to a straight line corresponding to an activation energy of 114 kcal per mole. One is led to two possible conclusions regarding Green&apos;s study: there are two discrete processes controlling the creep rate from 0.60 to 0.89 Tm or the apparent activation energy is not discrete but continuously increases with increasing temperature. The former speculation would be in closer agreement with the high-temperature creep behavior of tungsten.28 The apparent disagreement between the activation energies determined by the AT and isothermal methods certainly suggests that further study on the high-temperature creep of tantalum is needed.

Jan 1, 1967

By C. G. Dunn

James, Jones, and Leak (JJL) conclude that growth-rate and orientation-distribution data obtained in a steep thermal gradient should be used with caution to account for isothermally produced recrystallization textures. I agree. However, it is not clear whether they conclude a) that the orientation dependence of rate of growth of secondaries in (commercial) silicon iron depends on both temperature and a temperature gradient or b) that, in applying rate data obtained in a steep thermal gradient, the isothermal annealing temperature must be close to the temperature for which the rate data apply. Also, it is not clear what tem-

Jan 1, 1967

By H. M. Strong, R. A. Oriani

THE technological interest attaching to light, age-hardening alloys for structural uses has been pointed out to one of us.1 A potentially interesting alloy would be titanium-rich Ti-Mg alloy, provided that sufficient solid solubility exists. or could be induced at high pressure. and provided also that age hardening can be induced by proper temperature and/or pressure annealing. It was decided therefore to explore the feasibility of producing a Ti-Mg alloy in the high-pressure apparatus. Experimental. Three high-pressure runs have been carried out. In each case the geometry of the sample was that of a cylinder of titanium of commercial purity, into which a narrow hole had been drilled along the axis; this hole was filled with magnesium wire,

Jan 1, 1967

By C. S. Yust, C. S. Morgan

ThIS note reports the observation of masses of dislocation etch pits around the weld necks of small single-crystal particles of calcium fluoride sintered to a cleaved face of a larger CaFz crystal. Crystal particles in the -50 +I00 mesh size range were placed on freshly cleaved CaFz surfaces and heated at 1250°C for 30 min in a tantalum container in an argon atmosphere. The sintered specimens were then etched at room temperature for 40 to 50 min in a 2 pct sulfamic acid solution which is a selective etch for dislocations in caF2.&apos; Figs. 1 through 3 show the masses of dislocation etch pits observed around weld necks after etching. In some cases, particles were gone after removal of the specimens from the furnace although weld necks were readily visible. In other instances, no etch pits formed around a weld neck. A possible cause of concentrations of dislocations on the crystal surface is mechanical deformation of the base crystal when particles are dropped on it. If such a deformation does occur, it would be much smaller than that caused by the light punching of a crystal with a sharp instrument which results in large concentrations of etch pits. However, crystals deformed by punching with the sharp instrument and annealed at the conditions of these experiments (1250°C for 30 min) before etching showed no concentrations of dislocation etch pits. It is obvious that dislocations from the much smaller deformations, possibly created when particles are placed on the surface, would also anneal out. Etching of large crystals which had particles placed on them in the usual manner but which were not heated showed no dislocation concentrations such as shown in Fig. 1. The magnitude of dislocation etch-pit concentrations did not vary with extensive variation of the cooling rate. The appearance of many of the etch-pit clusters is typical of a well-annealed condition, indicating that the dislocation concentrations formed before the specimen temperature was lowered. Therefore, it is evident that thermal stresses in the neck area did not create the deformation indicated by the presence of the dislocations. The possibility exists that the etch-pit concentrations at places where particles had been removed may be the result of deformation accompanying the fracture of the sintered bond. That this is not so was demonstrated by breaking off particles around which no etch pits occurred. Re-etching never resulted in the large concentrations observed at sintering sites. The stress available to effect material movement during sintering of two particles will depend on the geometry at the contact point but can easily exceed the macroscopic yield stress in CaFz systems. It appears that the plastic deformation observed results from sintering or simply from the weight of the small particles. It has been previously argued that plastic flow makes an important contribution to the initial densification of oxides having the fluorite crystal structure.2p3 If plastic deformation occurs, it would begin as soon as the temperature is sufficiently high

Jan 1, 1967

By J. W. Downey, A. E. Dwight, R. A. Conner

In a previous paper&apos; we have reported the existence of a number of AB2 Laves phases in which A is a member of the scandium group (including the 1an-

Jan 1, 1967

By R. N. Orava, L. A. Rice

One of the difficulties encountered in the preparation of titanium specimens for transmission electron microscopy is the formation of a surface hydride phase during the thinning operation at ambient temperatures. This necessarily destroys contrast, obscures features of interest, and often leads to misleading results. By cooling the polishing solution to temperatures below 0°C this problem has been overcome in the past.&apos; However, since the cooling procedure is somewhat inconvenient, a technique was developed at this laboratory for thinning titanium at room temperature. The material examined was A-70 grade commercial-purity titanium purchased from the Crucible Steel Co. of America. The mechanical and thermal treatments, described elsewhere,* yielded a recrystallized grain size of 4 to 5 p. A slice, 0.5 mm thick and 1.5 mm wide, was cut from a bulk specimen2 using a diamond cut-off wheel. The sample was then coated with paraffin wax. Two concentric holes, about 0.03 in. in diam, one at each broad face, were scribed through the wax to the surface of the metal. Subsequent polishing for several minutes resulted in a preferentially thinned or "dimpled" region. Thereafter, the wax was removed and the entire specimen polished to the point of breakthrough at the base of the dimple. Polishing was effected chemically in a solution comprised of 30 pct HF and 70 pct HN03 by volume, kept at room temperature (20" to 25OC). The specimens were mounted in a stereo holder and examined at 100 kv in a Philips l00 B Electron Microscope. A micrograph from a foil prepared in this way is shown in Fig. 1. Several points are noteworthy. This electron micrograph shows neither evidence for the formation of a hydride phase due to specimen preparation nor, moreover, any obvious surface contamination in electron-transparent areas of a freshly prepared foil. Localized variations in foil thickness observed in some specimens seem to be a characteristic of this chemical polish but do not seriously detract from foil quality. With care, the lifetime of a good specimen exceeded 2 hr in the beam. On the other hand, the exposure of a sample to air at atmospheric pressure, when still warm from the beam, clearly resulted in the deterioration of a formerly clean area just previously in the field of view. An example in Fig. 2 of a contaminated region reveals features, and "spots", not unlike those observed in much purer material by Yamane and Ueda. Consequently, one can conclude that: 1) titanium can be thinned satisfactorily in a solution at room temperature for transmission electron microscopy; 2) large-scale precipitates, >50A in diam, are absent in commercial-purity, recrystallized, furnace-cooled, A-70 titanium containing about 3800 wt ppm interstitials and the same amount of iron; 3) care must be taken not to attribute surface contaminants to precipitates. The authors are grateful to the Franklin Institute for financial support and permission to publish.

Jan 1, 1967

By Edward J. Ryan, E. A. Peretti

iV preliminary X-ray and metallographic survey of the ternary system Bi-In-Te revealed that the following isopleths could form quasibinary systems: InTe-Bi, InTe-InBi, InTe-BizTe3, and InzTe3-Bi2Te3. The nature of the InTe-Bi phase diagram was established by Bologna and Peretti.&apos; This article presents the results of an investigation of the InTe-InBi system by thermal analysis, X-ray methods, and metallographic examination. The bismuth and tellurium were bought from the American Smelting and Refining Co. The tellurium had the following spectrographic analysis: 0.0001 pct Mg, 0.0001 pct Si, 0.0001 pct Fe, 0.0002 pct Al, and 99.999+ pct Te (by difference). The bismuth assayed: 0.0001 pct Mg, 0.0001 pct Pb, 0.0001 pct Fe, 0.0001 pct Cu, and 99.999+ pct Bi (by difference). The indium was obtained from the Indium Corp. of America and contained 0.002 pct Cu, 0.006 pct Pb, 0.01 pct Sn, 0.01 pct Zn, and 99.97+pct In. The alloys were made by melting the required proPortions of InTe and in evacuated, sealed quartz

Jan 1, 1967

By G. P. Conard, E. H. Rennhack

The creep behavior of hot-rolled, hypoeutectic Zn-Ti alloys was investigated in the temperature range from 0.43 to 0.53 TM. Secondary flow was found to originate primarily from strain-induced gvain growth where grain boundary )nigvation served to relieve the strain energy of distortion introduced by slip, grain boundary sliding, and subgvain formation. The extent to which this recovery mechanism operated was determined by the ratio of grain width to the spacing between planar fibers of TiZn,, compound particles generated in these alloys during rolling. When this ratio was unity, creep resistance demonstrated a marked improvement. In this condition, which was fulfilled by annealing following rolling, structural stability was enhanced with decreasing grain size below the equicohesive temperature (-0.5Tm), while the reverse was true above this temperature. TITANIUM concentrations approaching the eutectic composition of 0.23 wt pctl have been shown to promote a significant increase in the creep resistance of rolled zinc,2 The alloying effect created with titanium is somewhat unique; a structure closely resembling that of a fiber-reinforced metal composite can be developed which selectively modifies creep strength in preference to other mechanical properties. In an earlier investigation,~ the present authors found that, while the fiber network, composed of individual TiZn,, compound particles, had a distinct influence on rolled texture, the crystallographic variations produced were of minor importance with respect to creep. Rather, creep resistance seemingly increased when the grain size appeared to coincide with the in-terfiber spacing. The work described here was undertaken to explore this effect in greater detail. EXPERIMENTAL PROCEDURE Three zinc-base alloys containing 0.05, 0.12, and 0.16 wt pct Ti were prepared from CP zinc and iodide titanium in the form of 4 by 2 by f in. chill-cast ingots. The melting and casting procedures for these alloys have been detailed el~ewhere.~ Individual ingots of each alloy were hot-rolled at 200°C (392°F) to total reductions of 10, 25, 50, 75, and 90 pct in from one to five passes, respectively, employing a 10-min reheat prior to each rolling pass. With grain, tensile-type creep specimens with a 1-in.-long, -in.-wide gage section were machined from the rolled strips for test purposes. Annealing studies to explore the influence of grain size on secondary creep flow were carried out at 400°C (752°F) in argon for times extending up to 60 min. The grain-size effect was evaluated in terms of average grain width and length values statistically derived from lineal intersection measurements.4 A similar method was applied in establishing the average interfiber spacing, i.e., average perpendicular distance between adjacent planar fibers. The creep characteristics of the alloys were investigated by means of constant-load and constant-stress creep tests. The former tests were conducted at 25°C (77°F) under an initial stress of 10,000 psi, while the latter were performed in the range from 25°C (77°F) to 90°C (194°F) at stress levels varying from 8000 to 22,000 psi. Total specimen strain, as determined with Budd HE-1161-B strain gages, was in excess of 0.10. Maintenance of constant stress was achieved through periodic load reductions made at 0.01 strain intervals to compensate for the attendant incremental reduction in specimen cross-sectional area. The maximum indicated error in the applied stress at these strain intervals was less than 3.0 pct. RESULTS AND DISCUSSION Constant-Load Creep. In an effort to clarify the in-terrelation between interfiber spacing and grain size with respect to the creep resistance of the Zn-Ti alloys, their separate effects on secondary creep rate were determined as a function of titanium content and rolling reduction. These results are set forth in Figs. 1 and 2, respectively. The average grain diameter plotted in Fig. 2 was resolved from average grain width and length values. No data are presented for reductions of less than 50 pct because of the inability to obtain consistent measurements on these strips. The curves of Fig. 1 indicated that, for a given titanium content, a decrease in interfiber spacing, as produced with increasing reduction, promoted a decrease in creep rate. Depending on titanium content, however, wide variations in creep rate occurred at the same interfiber spacing suggesting that interfiber spacing, by itself, has little or no influence on creep resistance. Grain size, on the other hand, decreased progressively with both increasing rolling reduction and titanium content, the effect of which led to a pronounced decrease in creep rate, particularly when the average grain diameter became smaller than 3.0 x 10"4 in., Fig. 2. The continuity of this relationship tended to support the view that grain size rather than interfiber spacing was predominant in controlling secondary creep. Annealing Effect. The observed dependence of creep flow on grain size suggested that a further contribution to creep resistance would result when the alloys were annealed to effect a coincidence between grain width and interfiber spacing, see Fig. 3(b). ~eiides creating an immediate barrier to grain boundary movement, annealing offered the possibility of providing increased structural stability by eliminating many high-energy, mobile grain boundaries.= To test this hypothesis, specimens from the Zn-0.16 Ti strips reduced 75 and

Jan 1, 1967

By P. Wynblatt, J. E. Dorn

The effect of strain rate, temperature, and interstitial impurity concentration on the flow stress was investigated in a poly crystalline Fe-2 pct Mn alloy. The temperature dependence of the flow stress was found to be independent of the interstitial impurity concentration, removal of interstitials merely decreasing the atherma1 stress level. Below 160%, the large temperature dependence of the flow stress was interpreted in terms of the Dorn-Rajnak theory of the Peierls mechanism of plastic deformation. Above 160"K, some other thermally activated intrinsic meckanisln seems to be operating. The strong temperature dependence of the flow stress of bcc iron at low temperatures has been studied by numerous investigators and interpreted in terms of several different thermally activated dislocation mechanisms. The following mechanisms have been proposed: a) interaction of dislocations with interstitial impurity atoms1 or with solute atoms in general; b) interaction of dislocations with clusters of impurity atoms;3 c) resistance to the motion of dislocations due to jogs on screw dislocations;* d) resistance to the motion of dislocations due to the Snoeck effect;&apos; and e) interaction of dislocations with the intrinsic resistance of the bcc lattice or Peierls "hills". In previous work: it was found that the plastic behavior of polycrystalline iron containing 2 wt pct Mn (and 100 ppm C + N) is in good agreement with predictions based on the Peierls mechanismlo from 77" to 160°K whereas from 160" to about 370°K another as yet unidentified thermally activated mechanism is operative. The purpose of the present investigation was to determine the effect of interstitial impurities on the temperature dependence of the flow stress, by purifying the previously investigated alloy with respect to interstitial impurities. The investigation revealed that removal of the interstitial impurities to a level that eliminated Cottrell locking and the Portevin-LeChatelier effect (i.e., serrations in the stress-strain curve due to dynamic strain aging) affects neither the strong temperature dependence of the flow stress at low temperatures nor the general characteristics of the higher-temperature behavior. Such purification, however, lowered the athermal yield stress. I) EXPERIMENTAL PROCEDURE AND RESULTS The material used in this investigation consisted of an Fe-2 wt pct Mn alloy having the following additional elements present: 0.004 pct C, 0.006 pct N, 0.05 pct 0, 0.004 pct S, 0.003 pct P, and 0.001 pct Si. This was the same material as that studied in the previous investigation and will henceforth be referred to as the "impure material". The as received -jr by 2 in. hot-rolled bars were cold-rolled to 0.08-in. thickness, recrys-tallized under argon for 30 min at 80O0C, and further cold-rolled to 0.053-in. thickness. Flat tensile specimens 3 in. wide having a 1.625-in.-long gage section were machined from the sheet and then purified. The first stage of purification consisted of holding the specimens at 850°C for 24 hr in a stream of hydrogen saturated with water vapor at room temperature. Material prepared in this fashion will subsequently be referred to as "wet hydrogen purified material". It has been estimated that this type of treatment reduces the carbon content of iron to less than 5 ppm.&apos; The second stage of purification consisted of holding the specimens in a closed system through which hydrogen was circulated past the heated specimens as well as a zirconium hydride getter. The specimens were held at 850°C and the getter at 800°C. The process was continued for 212 hr. The starting material for this process was wet hydrogen purified material. Material prepared in this manner will be referred to as "ZrHz purified material". The technique used was substantially the same as that described by Stein et al.&apos; who have shown that the carbon level at the end of the process is reduced to about 5 parts per billion. The mean grain size of the three materials was found to be -60 C( for the impure material and -160p for the wet hydrogen and ZrHz purified materials. All tensile testing was carried out on an Instron Testing Machine either in controlled-temperature baths or at fixed-point baths such as boiling liquid nitrogen, and so forth. When fixed points were used the temperature was kept constant to better than *1°C whereas in all other tests the temperature variation was less than *2°C. Test of Purity. It was not possible to determine the purity achieved at each stage of the purification because the resulting level of interstitial impurities was near or below the limit of sensitivity of standard analytical techniques. It was possible, however, to obtain a qualitative measure of the extent of purification from the appearance of the stress-strain curves for the three materials. Fig. 1 shows the stress-strain curves for the three different materials tested at 300°K. It can be seen that the effect of wet hydrogen

Jan 1, 1967