By P. W. Bennett, E. M. Elkin

A new technique for the recovery of palladium and platinum and sludge from go12 electrolyte eliminates many of the drawbacks of the zinc-dust cementation process. In the electrolytic refining of gold by the Wohwill method, the electrolyte contains about 100 gpl gold as AuCl, and 100 gpl free hydrochloric acid. Any palladium and platinum contained in impure gold dissolve and accumulate in the electrolyte. When their concentration approaches that of gold, it becomes desirable to discard the electrolyte and to recover the gold and the palladium and platinum. As practiced at Canadian Copper Refiners until recently, discarded electrolyte was treated with sulfur dioxide to precipitate the gold. 2AuCl3 + 6H2O + 3SO2 —2Au + 6HC1 + 3H2SO4 The gold precipitate was filtered off, washed with water, and melted with scrap anodes. The wash water was added to the gold-free filtrate and treated with zinc dust to cement the palladium and platinum. PdCl2 + Zn — Pd + ZnCl2 PtCl4 + 2Zn—Pt + 2ZnCl2 The precipitate was separated and sold as Pd-Pt concentrate, and the barren filtrate and wash water were discarded. The receipts of palladium and platinum at this company were too small to warrant their refining. The process suffered from a number of disadvantages. Handling the gold-free solution was disagreeable, as it was laden with sulfur dioxide even after blowing with air overnight. Subsequent treatment with zinc dust was also troublesome. A large excess of zinc dust was required. Spray, acid mist, and vigorous evolution of hydrogen accompanied the reaction. The Pd-Pt precipitate was grossly contaminated with occluded unreacted zinc and with yellow granules of sulfur, thought to be formed by the reduction of sulfur dioxide and its derivatives. Repeated boiling of the precipitate with hydrochloric acid and washing with water decreased somewhat, but did not eliminate, the zinc. After drying overnight, the precipitate hardened to a clinkerlike mass that was difficult to grind. Grinding, handling, and packing created heavy dusting. Even weighing in an analytical balance generated dust, indicating that the powder was easily charged with static electricity. The total palladium and platinum content of the powder varied from 56 to 72 pct, with an average of 65 pct. The powder dissolved in aqua regia with difficulty, leaving a small amount of insoluble residue. However, the main drawback of the process was the strongly hygroscopic Pd-Pt product. The powder showed a marked though erratic increase in weight and a corresponding decrease in assay on exposure to air, even during the course of laboratory analysis. Such changes were the source of disagreement between Canadian Copper Refiners and the buyers of concentrate. The cause of the change in weight is believed to be hydrogen, liberated by the action of zinc dust on hydrochloric acid. Some of this hydrogen was adsorbed so strongly by the precipitate that it could not be driven off during the drying. On exposure to air it oxidized catalytically, forming water. Experiments soon showed that the entire process of treatment of discarded electrolyte then in use would have to be changed. A small quantity of apparatus was moved into the gold room, and experimentation was held to a minimum compatible with the development of a new process. PALLADIUM AND PLATINUM PRECIPITATION It was thought that zinc could be replaced with a reagent other than a hydrogen-evolving metal. Semiquantitative experiments showed that platinum and palladium could be precipitated completely from the gold-free solutions with such well-known reagents as sodium formate, formic acid, formaldehyde, and paraformaldehyde. Sodium formate was the preferred reagent, since the other three are volatile and somewhat toxic. The gold-free solutions used were those saturated with sulfur dioxide, partly freed of sulfur dioxide by aerating overnight, completely freed by boiling, as well as strongly and weakly acidic, neutral, and alkaline solutions. The reactions are complex and can be represented by these over-all equations: PdC1, + HCOONa — Pd + NaCl + HC1 + Co2 PtCl4 + 2HCOONa — Pt + 2NaCl + 2HC1 + 2CCX, Strongly acidic solutions required as much as five times the theoretical amount of sodium formate as did solutions neutralized to pH 4.5. Increasing the pH decreased the consumption of

Jan 1, 1965

By G. R. Rigby

Used basic brick taken from copper anode furnaces, reverberatory furnace roofs, md copper converters have been examined by chemical analysis, petro-graphical examination, and X-ray diffraction tech-niques. In the anode furnace roof, brick absorb copper and copper oxides, whilst in the reverberatory roof, iron oxide with smaller amounts of alumina and silica are absorbed. Chemical reactions in the converter are most complex since the brick absorb both a copper-copper oxide slag and a fayalite-magnetite slag. CHANGES taking place in basic brick after use in copper smelting furnaces have received attention from C. Burton Clark and J. Spotts Mc Dowell,' who examined brick taken from copper converters, and by G. R. Rigby and B. G. Hamilton' who examined brick from copper anode furnaces. This paper describes the changes taking place in basic brick from all types of copper smelting furnaces and discusses the major reasons for lining wear. A) METHODS OF EXAMINING SAMPLES A variety of used brick have been taken from the following positions in various furnaces, a) roofs, reverberatory arches, and bottoms of copper anode furnaces, b) roofs of copper reverberatory furnaces and c) the tuyere line and end walls of copper converters. The method of examination was standard in that brick were first measured and the extent of wear-back computed. They were next sawn in two by a central cut vei-tical to the working face to enable the freshly cut surfaces to reveal any zonal changes and cracks, both of which usually ran parallel to the working face. Each well-defined zone was then sampled for a) chemical analyses, b) petrographical studies using transmitted and reflected light techniques under the microscope, and c) X-ray diffraction studies on powdered samples. From the data accumulated, changes taking place in a variety of

Jan 1, 1962

By Attilio Ligasacchi

The production of magnetite in copper smelting has been the subject of wide investigation in the past.1-9 It is accepted that most of the magnetite is produced in the converters and returned to the re-verberatory furnace with the converter slag. Part of this magnetite is circulated back to the converters in the matte. As a result, if proper fluxing practice is not followed, and temperatures in the converting process are not strictly controlled, an undesirable circulating load of magnetite may occur. This might ultimately lead to saturation in the reverberatory bath with consequent settling of the magnetite at the furnace bottom. This paper contains the cumulative results of a series of investigations on the formation and control of magnetite presently being conducted by the metallurgical department of the Chino Mines Division of Kennecott Copper Corp. THE METHOD USED FOR THE DETERMINATION OF MAGNETITE AND OTHER MAGNETIC MATERIALS Conventional wet chemical magnetite analyses are neither reproducible nor theoretically sound. These analyses are sensitive to time, temperature, and heating rate-all factors which tend to decrease their accuracy and reproducibility. To overcome the unreliability of the above method, H. W. Mossman1 developed an inductance bridge magnetite "meter" which completely replaces the wet chemical analysis with the advantage of quicker and reproducible results. Fig. 1 is a schematic diagram of the meter in use in the Chino metallurgical laboratory. When a pulverized specimen with magnetic properties is placed in coil A of the inductance bridge circuit, the permeability of the core is increased, causing a voltage drop across the coil. The unbalance is amplified to operate the balancing motor which adjusts the movable iron core in coils C and D to bring the bridge back to balance. An indicator arm connected to the movable iron core indicates directly the percent, or weight, of the magnetic material in the specimen. Coil B acts as a reference coil and a zero adjustment. The meter is standardized with a set of various amounts of -100 mesh pure magnetite crystals (99.8 pet Fe3O4) thoroughly mixed in a test tube with -100 mesh quartz sand. These mixtures are combined with inert transoptic powder and heated to 140° to 160°C (melting point of the powder) and subsequently cooled to room temperature, solidifying the whole mixture, in this manner eliminating any possible preferential orientation of the magnetite grains. In order to determine the effect of the particle size" of the magnetite and other magnetic materials on the meter determinations, five size fractions were obtained by wet screening of the 99.8 pet pure magnetite and several reverberatory matte and slag samples. The following size fractions were investigated: -80 + 100; -100 + 150; -150 + 180; -200 + 250; -250 + 300 and -100 mesh. The deviation of the meter readings for the various sizes of each sample never exceeded ±0.3 pet. This deviation is considered well within the accuracy needed for common smelter operation procedures. Further investigation proved also that grinding slag and matte samples in our laboratory disc grinder normally produced a powder constituted of 95 pet -200 + 300 mesh. For practical purposes a - 100 mesh size was used as standard for our studies. It was also found that for rapid determinations tamping of the sample in the test tube was sufficient and gave comparable results with those samples solidified with transoptic powder. For the purpose of this study we define the magnetite content in copper smelter slags and matte as the equilibrium amount of crystalline Fe3O4 existent in the specimen at a given reference temperature, excluding any secondary magnetite precipitated in the specimen during nonequilibrium conditions. MAGNETITE DETERMINATION IN SLAGS Since it is impossible to ascertain the status of equilibrium of a conventional slag sample, due to

Jan 1, 1965

By M. Shelef, A. W. Fletcher

The effect of alkali sulfates in promoting the sul-fation of nickel and copper in a bulk sulfide flota -tion concentrate by fluidized bed roasting has been studied in the laboratory, and it was shown that the various alkali sulfates promote sulfation to approximately the same extent. The sulfation of a mixture of synthetically prepared iron and nickel oxide and of nickel ferrite has also been studied. Nickel sulfation was promoted by high ratios of Fe:Ni and by the presence of sodium sulfate. THE work described in this paper was a continuation of earlier studies into the role of alkali sulfates in promoting the sulfation roasting of nickel sulfides1,2 in an endeavor to determine how the system was affected by the presence of compounds of iron and copper. The earlier work1 showed that, in the sulfation of NiO at 680°C, the reaction was limited by the formation of an impermeable film of nickel sulfate on the oxide surface. The relative effect of the various alkali sulfates in promoting nickel sulfation varied in the order: Li > Na >Cs > Rb > K A study of alkali sulfate/ nickel sulfate interactions at high temperatures showed that the promoting action was due to the fact that the nickel sulfate product layer sintered and agglomerated only when the more active additives were present. This resulted in the formation of discontinuities in the nickel sulfate layer so that diffusion of the sulfating gases to the NiO surface was no longer impeded and the reaction could proceed to completion. A similar explanation was used for the observation that sodium and lithium sulfates promote the oxidation of NiS to NiO at temperatures below 750°C since small amounts of nickel sulfate were formed during oxidation.2 It was of interest to study the effect of alkali sulfates on the sulfate roasting of a sulfide flotation concentrate which is typical of material treated commercially. In order to control temperature it is essential to roast sulfides in a fluidized bed and this technique was therefore used, although the batchwise operation of a small-scale laboratory reactor does not reproduce all conditions which prevail in full-scale continuous plant. The results obtained are therefore only comparative, and cannot be used for predicting the optimum conditions for metal extraction. The sulfation of synthetically prepared mixed oxides of nickel + copper and nickel + iron and of nickel ferrite was also studied to evaluate the relative effects of alkali sulfates with more complex systems. SULFATION ROASTING OF A SULFIDE FLOTATION CONCENTRATE The bulk sulfide flotation concentrate used in this work contained 7.92 pct Ni, 1.74 pct Cu, 35.66 pct Fe, and 31.28 pct S. The sulfide minerals present in order of abundance were pyrrhotite FeS, pyrite FeS2, pentlandite (FeNi)S, and chalcopyrite CuFeS2. Two samples described as coarse and fine were used. The coarse sample, which was a flotation concentrate (58 pct plus 300 mesh), was ground to 100 pct minus 350 mesh to produce the fine sample. Before roasting, the sample of sulfide concentrate was agglomerated by wetting witli a solution of the alkali sulfate (or water), thoroughly mixing, and drying at 110°C. This gave a cake which was gently crushed and screened, the -18 +100 mesh fraction being used for fluidized bed roasting. A similar-size fraction had been used by the authors in pilot plant work with a 4-in.-diam fluidized bed reactor.' In this work it was found that the molar ratio of additive to the total iron + nickel + copper content of the sulfide sample should be adjusted to a value of approximately 0.06, as this was the optimum amount necessary for nickel sulfation. Experimental. The fluidized bed reactor consisted of a quartz tube approximately 60 cm long and 30 mm in diameter resting in a vertical tube furnace. The sulfide bed (30 g) was supported on a bed of -4 +12 mesh quartz particles 3 cm high, which rested on a sintered quartz disc welded to the tube. The temperature of the furnace was controlled with a variable transformer to give a final bed temperature of 680°C. The bed was fluidized with air or mixtures of air + 10 pct v/v SO2, at a total apparent gas velocity of 60 to 65 cm per sec at 680°C. The SO2 was introduced into the fluidizing air stream only when the oxidation of the sulfides was completed. At the end of the roasting period the calcine was leached with boiling water and the

Jan 1, 1964

By R. Schuhmann

Available thermodynamic data applicable to copper smelting systems are collected and tabulated, and the important gaps are pointed out. A few examples are given of estimations which can be made from the available data. An experimental research program is proposed to supply the thermodynamic data that appear most essential to better quantitative understanding of the chemistry of copper smelting. The proposed program is designed also to shed specific light on the practical problems of slag losses and magnetite behavior. OPPER smelting, from flotation concentrates to V-/ blister copper, is conspicuous among the large scale chemical processes which are conducted with only relatively incomplete knowledge of the physical chemistry involved. For example, no common metallurgy text explains adequately why copper enters the matte phase while iron enters only to the extent that sulphur is left over after satisfying the copper. Explaining this important phenomenon as a manifestation of the greater affinity of sulphur for copper than for iron is unsound because the affinities of copper and iron for sulphur are about the same at smelting temperatures. As will be shown, other affinities are really decisive in the relatively clear-cut separation of copper in the matte. In contrast, thermodynamic studies have contributed much to our understanding of copper refining, zinc oxide reduction, magnesium production, steelmaking, etc. For each of these processes, the important reactions are clearly recognized, and fair to good quantitative values of the free-energy changes and equilibrium constants are available. Such data have proved to be of constantly increasing practical value in process development and improvement. Work in other fields has furnished much thermodynamic data applicable to copper smelting systems. In fact, several promising starts have been made in applying such data to specific smelting problems. Kelleyl made an appraisal of the possibilities of recovering elementary sulphur from low grade matte. His calculations and compilations of thermodynamic data have represented the starting point for much of the work in this field, including the present survey. Huang and Hayward2 nd Aksoy3 used thermodynamic methods in the study of copper losses in reverberatory slags. Peretti4 used thermodynamic data in explaining the chemistry of converting. The recent publications of Darken and Gurry"." and of Darken,' dealing with the iron-oxygen and iron-silicon-oxygen systems, respectively, present equilibrium data that are applicable to copper smelting systems. Also additional data were reported recently on the affinity of sulphur for copper, manganese, and iron8 and on the sulphur pressures of iron-sulphur melts." The survey presented in this paper was made as the basis for planning an experimental program on the thermodynamics of copper smelting. Few researches on the chemistry of copper smelting have been reported in recent years, so that a reappraisal and coordination of old and new data are essential if further work is to take the directions of maximum value. The experimental program is now in progress, and the plan of attack is outlined at the end of this paper. Progressive Oxidation and Desulphurization of Copper-bearing Liquid Phases: The chemical activities of sulphur and oxygen are two of the most important thermodynamic yardsticks to be applied to copper smelting processes. Virtually the entire smelting and refining sequence involves a series of systems characterized by decreasing sulphur activity and increasing oxygen activity. In this section, therefore, an attempt is made to define and explain these activities in terms of equilibrium partial pressures of SO2, s2, and O,. Also, estimates of these quantities are presented, the estimates being based largely on calculations presented in a later section of this paper. The sequence of steps from raw flotation concentrate to fully oxidized copper ready for poling involves progressive and controlled oxidation. Iron is oxidized and enters the slag. Sulphur is oxidized and leaves in the gas. Table I summarizes several important features of this oxidation and desulphurization sequence, starting at the beginning of the matte blow in the converter. The top line gives in order the principal smelting and refining stages up to fully oxidized copper, plus the additional step, not used commercially, of oxidizing all the way to Cu,O. In the second line are shown the principal copper-bearing liquid phases which characterize the process. Through most of the sequence the copper

Jan 1, 1951

By T. P. Papazoglou, N. A. D. Parlee, W. C. Phelps

HE high vapor pressures of metals such as lead, calcium, lithium, bismuth, and magnesium at steel-making temperatures present experimental problems which have thus far rendered it almost impossible to obtain really reliable data for their solubilities in liquid iron. Many investigators have attempted to equilibrate liquid iron in the same crucible with the undissolved liquid phase of such volatile metals. The published results,l-6 although useful, are often questionable on the grounds of not being obtained under true equilibrium conditions. Such information is not always of practical value in any case since the equilibrium vapor pressure is often several atmospheres and steel is not currently made at these pressures. Solubility measurements at lower partial pressures (< 1 atm) appeared to be more practical and easier to make. These data could be used to calculate solubilities at other pressures where Henry&apos;s Law is obeyed, and to estimate solubilities under other conditions of temperature and pressure with useful accuracy. This note outlines the development of a general technique for the measurement of solubilities in systems of this kind. The method involves equilibration of the high-boiling metal at known temperatures with the vapors of a low-boiling metal at known partial pressures. Analyses of quenched samples provide vapor pressure-solubility data and make calculations of alloy thermodynamics possible. The principle involved is similar to the closed-system diffusion-transport method which is difficult to apply with most high-melting liquid metals like iron, due to closure problems. A two-zone horizontal (molybdenum wire element) tube furnace, Fig. 1, provides two constant-temperature zones in a reaction tuve (3/4 in. ID by 1 in. OD by 36 in.). A high-boiling metal sample, 9, introduced in the higher-temperature zone, is maintained at temperature T1, and a volatile metal sample, 7, in the lower-temperature zone, is held at T2. A stream of argon with 10 pct hydrogen is passed via flowmeters, 1, and mixing-drying towers, 2 and 3. through the reaction tube at a favorable flowrate and acts as a carrier gas which entrains vapor from the volatile liquid metal at a specific constant partial pressure. The gas mixture passes through a system of constrictions, 6 and 8, to the higher-temperature zone, establishes intimate contact with the high-boiling liquid sample, 9, and exits through a small condenser tube. The entire system is at (nearly) atmospheric pressure and the volume of carrier gas passed is measured with a wet gas meter. When the high-boiling sample attains equilibrium with the vapor phase, both samples are removed and quenched. Analysis of the high-boiling sample for solute content reveals its solubility for the low-boiling metal at a vapor pressure calculated from carrier-gas volume and either a) weight loss of volatile metal or 6) weight gain of high-boiling sample plus condenser (which collects the undissolved vapors). To test the capabilities of the method, liquid silver at 1403&apos;C was equilibrated with lead vapor at various partial pressures. The relatively simple Pb-Ag system was particularly suitable for uncovering experimental problems and providing the first step toward investigations with more volatile metals and more difficult combinations.

Jan 1, 1965

By Wayne L. Worrell

Thermodynamic data for the stable carbides and oxides of chromium, molybdenum, and tungsten have been critically eualuuted and are used to determine the stable condensed phases at 1 atm total pressure in each metal-carbon-oxygen system. Pourbaix-Ellingham diagrams have been constructed and are used to estimate the minimum temperatures neces.see)*y to oblain these metals by corbolhermic redlrction under reduced pressures. USING recently reported data for the carbides and oxides of chromium, molybdenum, and tungsten, the stable phases in the Group VI metal-carbon-oxygen systems at specific temperatures and pressures can be determined. The thermodynamically stable regions in each metal-carbon-oxygen system can be completely pictured using a Pourbaix-Ellingham diagram in which the two coordinates are oxygen potential (-RT In Po2) and temperature. Worrell and chipman&apos; have described and constructed such diagrams for the metal-carbon-oxygen systems of vanadium, columbium, and tantalum. Downing2 has used similar diagrams to provide a description of the reactions in submerged arc furnaces. One of the examples which he cited was the Cr-C-O system; however, an improved diagram is presented in this paper using recently obtained data for the carbides of chromium. Although some of the oxides and carbides of the Group VI metals exist over slight ranges of composition,3 all solid phases are represented as stoi-chiometric compounds in the subsequent diagrams. Any error introduced into the calculated equilibria by neglecting the compositional variation of these phases is less than the uncertainty in the thermodynamic data. In a Pourbaix-Ellingham diagram for a three-component system, the phase rule requires that at equilibrium four condensed phases specify a point, three condensed phases determine a line, and two condensed phases define an area. To obtain a well-defined area at high oxygen potentials and teniperatures, the initial carbon to oxygen mole ratio is specified to be more than sufficient to reduce the oxide but not enough to convert all the metal to carbide. Thus, the lowest regions in the subse- quent Pourbaix-Ellingham diagrams represent areas in which the metal and its carbide are the stable condensed phases. Cr-C-O SYSTEM A) Thermodynamic Data. To simplify the subsequent calculations, all thermodynamic data are presented in the form of linear Gibbs-energy-of-formation* equations which were derived for the temperature range 505° to 2000°K and are reasonably accurate over the entire temperature ranges of the diagrams. The thermodynamic data for the compounds occurring in the Cr-C-O system are summarized in Table I. Several volatile chromium oxides have been reported,4 but their influence is negligible in the Cr-C-O system. Thermodynamic data for CO and CO2 were taken from the compilation of Coughlin.5 The only solid chromium oxide sufficiently stable to exist below 1800°K in the Cr-C-O system is Cr2Os.11 The Gibbs-energy-of-formation equation for Cr2O3 was obtained by revising the data tabulated in Coughlin,5 using the heat of formation of ah&apos; and the high-temperature thermal data for chromium.7 In 1953 Richardson8 re-evaluated the original work of Kelley and coworkers,9 who measured the thermodynamic properties of the chromium carbides. However, the high-temperature equilibrium results of Boericke9 yield values for ?G°f of Cr2O3 which are 2 kcal more positive than the accepted data. His results for the chromium carbides are based on the same questionable equilibria. Gleiser10 recently determined the Gibbs energy of formation of Cr3C2 and the equation in Table I was calculated from her data and the thermal data of Kelley and coworkers.9 Thermodynamic data for the Cr7C3 and Cr23C6 carbides were obtained by combining the Cr3C2 data

Jan 1, 1965

By John Chipman, Wayne L. Worrell

Using recent thermodynamic data for the carbides and oxides of tantalum, columbium, and vanadium, the stable solid phases aboue 1300°K and at 1 atm CO(g) pressure in each M-C-O system have been determined. Pourbaix-Ellingham diagrams have been constructed and are used to estimate the minimum temperatures necessary to obtain these metals by carbothermic reduction under reduced pressures. TANTALUM, columbium, and vanadium react with carbon to form the M,C and MC carbide phases. The M,C carbides have narrow homogeneity ranges, but the MC phases possess considerable ranges of homogeneity.&apos; The free energies of formation of the MC carbides were recently measured, and those of MC and M2Ccarbides have been estimated., (The notations MC and MC denote, respectively, the carbide compositions at the carbon-rich and at the metal-rich boundaries of the homogeneous MC phase.) In this paper, these carbide data are combined with thermodynamic data for the oxides to predict the stable phases in the Ta-C-O, Cb-C-O, and V-C-O systems at specified temperatures and oxygen pressures. M-C-O PHASE DIAGRAMS The solid phases in equilibrium above 1300°K for each M-C-0 system are shown in Figs. 1, 2, and 3. Above 1300°K, the vapor would consist entirely of carbon monoxide; and these phase diagrams were obtained by specifying the vapor pressure of CO(g) to be 1 atm. The temperature at which any two solid phases become unstable is specified along the two-phase equilibrium lines in each diagram. To simplify the diagrams, all solid phases in the Ta-C-O and Cb-C-O systems are represented as stoichiometric compounds. However, the homogeneity ranges of VO and VC are indicated, because they form a complete series of solid solutions.3 It also should be noted that the homogeneity range of

Jan 1, 1964

By T. Rosenqvist

From the chemical, metallurgical, and mineralogical points of view, the importance of thermodynamic data for metal-sulphides and sulphur dissolved in molten metal has long been realized. Such data will give a basis for thermo-dynamic calculations of processes such as roasting and the distribution of sulphur between molten metal and slags. Furthermore, it will help us understand the chemical forces which tie sulphur to the metal and to the melt. Thermodynamic studies of solid sulphides and the equilibria between solid sulphides and metals have been carried out in a rather large number of cases by several investigators. An excellent review of this work is given by Kelley.1 On the other hand, very little is known about the thermodynamic properties of molten sulphides and of sulphur dissolved in molten metal. The only system which previously has been investigated in this respect is the iron/sulphur system. The purpose of the present investigation was primarily to obtain further data for metalisulphur melts and the system silver/sulphur was chosen, not because this system was expected to be of special interest in itself, but because the silver/sulphur system is a typical example of a metal/sulphur system. Because of the low melting temperatures, the work could be carried out without appreciable furnace and refractory difficulties. The sulphur in this system possesses a rather high escaping tendency compared to most other metal/sulphur systems. By the method employed (reaction with hydrogen to form hydrogen sulphide) this gives ratios Ph2s/Ph2 up to 0.30, which may be determined accurately. &apos;rhermodynamic investigations of the heterogeneous reaction Ag2S +H2 —+ 2Ag + H2S have previously been carried out by Pelabon,2 Keyes and Felsing,3 Jellineb and Zakowski,4 Wat-anabe,6 and Britzke and Kapustinsky.6 Their results are in rather poor agreement. Experimental Part PRINCIPLE In the present invehgation the escaping tendency of sulphur from the condensed phase was determined by the reaction: S + H2 = H2S The ratio Ph2s/Ph2 is at constant temperature, directly proportional to the escaping tendency of sulphur and to its chemical activity in the condensed phase. (This ratio will subsequently be denoted by H2S/H2.) From this ratio and its variation with temperature and with change in the com- position of the condensed phase, thermodyrlamic quantities such as free energy and heat of reaction can be derived. The apparatus used is shown in Fig 1. The silver/sulphur alloy was placed in a crucible inside a refractory tube and mounted inside the furnace to the left. The tube was a part of a closed, gas-tight system in which the gas mixture could circulate until equilibrium was established. Circulation was maintained by the glass propeller to the right, driven by an external magnet, and promoted by the chimney action of the furnace. The gas passed up through the furnace, down into the crucible where it came in contact with the alloy, passed rapidly up through a narrow tube and out of the hot zone. After equilibrium was established between the gas and the condensed phase, the composition of the gas mixture was determined from its density. In its circulation, the gas mixture passed through a chamber (lower right on Fig 1) containing a buoyancy-balance, where the density of the gas was determined by magnetic balancing. From the measured density,

Jan 1, 1950

By C. B. Alcock, L. I. Cheng

By the use of radiochemical methods for the study of the gas-liquid equilibria at low temperature, and for the determination of the sulfur contents of metal beads which had been equilibrated with H2S/H2 mixtures of known sulfur potential, it has been possible to obtain the liquid solubility and the free energy of solution of sulfur in liquid tin and lead at temperatures between 500°and 680°C. THE gas-liquid equilibrium method has proved in the past to be most successful in the determination of the thermodynamic behavior of dilute solutions of sulfur in liquid metals.1,2 One of the basic requirements for success with this method is that the volatility of both the metal and its lowest sulfide should be small, otherwise sulfide will be deposited at the cool end of the furnace, where it may react with the outgoing gases to form either sulfur-rich lowest sulfide or higher sulfides. The resultant value of the apparent equilibrium constant will then be lower than the correct one. This argument applies even at sulfur potentials below that in equilibrium with a separate condensed phase of the lowest sulfide at the reaction temperature, T. The mass of sulfide which is deposited at the cold end of the furnace, and hence the extent to which further reaction occurs with the outgoing gases, depends on the time taken for equilibrium to be reached between metal and gas. Since this will depend principally on the bulk of the metal phase which is used, one should clearly attempt to uie as small metal samples as possible. These considerations are important in the study of dilute solutions of sulfur dissolved in liquid tin and lead which both have moderately high vapor pressures as metals and form volatile sulfides. The limit on the size of the metal samples which may be used is set chiefly by the difficulties of analysis for very small amounts of sulfur. The oxygen or carbon dioxide combustion method, followed by iodimetric determination of the sulfur dioxide which is formed,has been found to be successful for the determination of small amounts of sulfur in copper, iron, cobalt and nickel.4 This method was unsatisfactory for sulfur dissolved in tin and lead, mainly because the sulfur dioxide was to some extent absorbed by the copious tin or lead oxide deposits which were formed on the walls of the combustion tube. Furthermore some of the sulfur was found to segregate on the surface of the beads as flaky sulfide crystals which would easily be lost in the transfer of a bead from a boat in the gas equilibration apparatus to one in the combustion apparatus. Oxidation in aqueous media to sulfate ion followed by precipitation as barium sulfate was, therefore, adopted as the analytical procedure. The gas-metal equilibrium experiments were all carried out with radioactive sulfur and thus the analysis involved the counting of barium radiosulfate. Furthermore the use of the radioisotope meant that the approach to the gas-metal equilibrium could be followed continuously by gas counting.&apos; The metal beads were held separately in glass crucibles during equilibration and were transferred from the furnace to the beaker for dissolution in nitric acid still in the crucibles, and thus the possibility of sulfur loss by detachment of the sulfide segregates was eliminated. The temperature range of this investigation was 500° to 680°C. EXPERIMENTAL APPARATUS AND METHOD The apparatus consisted of two furnaces placed in series in a gas recirculation system, Fig. 1. One furnace F1, which was vertical was used to heat the alumina crucible, A, holding six metal beads in separate glass crucibles. The beads weighed between 300 and 700 mg each. The crucible assembly was introduced and removed from the furnace mechanically under a stream of oxygen-free argon. The other furnace, F2, was horizontal and was used to heat a cobalt Co9S8 mixture, held in an alumina boat, and made with radiosulfur containing about 1/2 millicurie per g of sulphur. This mixture, which was finely powdered, was used as a source of known H2S/H2 mixtures6 for a given furnace temperature. The recirculation system also contained a gas re-circulation pump (P), an end window Geiger-Miiller counter (N)—placed downstream of F1 so as to monitor the H2S pressure in the gas leaving this furnace— a sample volume for chemical analysis of the gas phase (G), gas drying tubes (D), filling taps and other standard ancillary equipment. The gas sampling volume was principally used in the cali-

Jan 1, 1962

By A. W. Schlechten, R. P. Abendroth

Equilibrium H2S/4 ratios were determined as functions of temperatunz and composition in a hydrogen recirculation apparatus. A high-temperature solid solution exists in the range two-phase regionfrom TiS 1.96, to TiS1.30, Various thermodynamic quantities were calculated from the data. COMPOUNDS in the titanium -sulfur system have not receiyed much attention in the past, probably because they do not occur naturally in the earth&apos;s crust. However, titanium-sulfur compounds have been used in various metallurgical processes. The U.S. Bureau of klines&apos; studied the formation of ti- tanium-sulfide mattes from charges composed of rutile, pyrite, and carbon, with the resulting sulfide matte being chlorinated to form titanium tetrachlo-ride. Fishel, Roe, and Ellis&apos; investigated the de-sulfurizing action of titanium in steels, and Schwarz and Koster studied the preparation of metallic titanium from the sulfide using aluminum and magnesium reduction. The thermodynamic properties of some of the compounds present in the titanium-sulfur system may prove to be of some use in the consideration of future processes using these sulfides, and would

Jan 1, 1960

By A. W. Schlechten, R. P. Abendroth

Jan 1, 1960

By A. W. Schlechten, A. H. Larson

Equilibrium H2S/H2 ratios were determined as functions of temperature (500o to 900°C) and composition in a hydrogen-circulation apparatus. Within the composition range studied there exists a two-phase region of "Zr3S4" and "ZrS2". The upper composition limit of this two-phase region is hounded by a disulfide phase and is practically constant over the temperature range investigated. The lower composition limit of this two-phase region is bounded a "Zr3S4 " phase and varies appreciably with tem- perature. The upper composition limit of the homogeneous region of the disulfide phase is not definitely determined, but it appears to he bounded by the stoichiometric composition of ZrS2. The lower composition limit of the homogeneous region of the Zr3S4 phase could not he determined due to the extremely low values of the equilibrium H2S/H2 ratios. Various thermodynamic quantities are evaluated from the data. PUBLISHED free-energy data for the Zr-S system are practically nonexistent. Strotzer, Biltz, and Meisel1 measured the sulfur pressures for the reaction 2ZrS2(s) + S2(g) = ZrS3(s) in the temperature range 783" to 874°C. The average heat of reaction calculated from the temperature dependence of the sulfur pressure is -47 keal. It should be noted, however, that according to these investigators, the two-phase region as determined by sulfur pressure constancy under isothermal conditions extended from approximately ZrS2, 3 to ZrS2.7. From consideration of X-ray data they concluded that the homogeneous regions of the disulfide and trisulfide phases are ZrS1.8-2.0 and ZrS2.8-3.2, respectively. Hahn and coworkers2 have made a structure study of the zirconium sulfide phases. They summarized the zirconium sulfide phases as follows: the compounds ZrS3 and ZrS2 with narrow homogeneous regions, a "Zr3S4" phase with a homogeneous region roughly within the limits of ZrSl.5 and ZrSo.9, the compounds ZrS and Zr4S3, and a "Zr3S2" phase with a homogeneous region within the limits ZrSo.8 and ZrSo.5. It is noted that the compounds ZrS and Zr4S3 are only formed in the gaseous state through sublimation of a phase which has the approximate composition of the compound. This paper describes the determination of the stability of the zirconium sulfide phases by a hydrogen-reduction method in which hydrogen is circulated over the heated sulfide until equilibrium is attained. The resulting H2S-H2 mixture is then analyzed. Partial molar free energies, enthalpies,

Jan 1, 1964

By A. L. Labbe

SOON after the Cottrell treater was placed in operation in the Murray plant in 1918 to treat combined lead sinter and Wedge roaster smoke, it was noticed that the power flowing through the treater did not remain constant. This was indicated by the varying milliamperes and also by the total amount of power consumed by the rectifiers. At times, for then unknown reasons, the treater current fluctuated through a wide range of from 40 to 300 milliamperes. Fortunately, these variations in power did not affect the treater&apos;s overall recovery, as this installation consisted of three independent units in series, a feature which made the Murray Cottrell an outstanding installation over many years of operation. Water conditioning of the smoke as a means of improving recovery was already known, but was not adaptable to this installation for reasons of excessive corrosion, which had been the case with other treaters using water as a conditioner exclusively. Tests conducted on the smoke had proved conclusively that water vapor played no part in the fluctuation of power, and the same was true of the SO2 contents and dust burden of the smoke. Neither did temperature variations of from 150 to 400°F have any effect on the power. Finally it was noticed that the variation in power taken by the treater, and the efficiency of recovery, had some definite relation to the number of Wedge roasters operating, and particularly to the sulphur contents of the charge. This observation soon led to the discovery that free sulphuric acid was the conditioner for Murray smoke and that variations in acid contents of smoke accounted for fluctuations of treater power. Analysis of recovered dust revealed that only a few hundredths of a per cent free acid was necessary to maintain a very efficient recovery. Once this knowledge was available, the roaster charge was adjusted as to sulphur contents to produce the necessary acid conditioner. For a number of years this practice was followed, but with improvements in the field of flotation, excess pyrites were eliminated from the smelting picture, so with a change in metallurgical practice we were confronted with the problem of providing the deficiency in acid by some other means. The situation was aggravated and our problem of acid conditioning made more difficult by the increase in the lead contents of concentrates roasted resulting from better flotation methods. The first step towards introducing acid vapors into the smoke stream by accessory means was accomplished by boiling sulphuric acid in cast iron pots placed in an open fire box. Acid fumes evaporated from the pots together with the combustion gases from the fire box were discharged into the flue through a cast iron pipe. Capacity of the iron pots was quite limited because of the comparatively slow rate of evaporation and the use of lump coal as a fuel, which did not lend itself to practical temperature control. This method of firing resulted in frequent pot failures due to overheating. In spite of these incidental difficulties, encountered in any new venture, the pot evaporator demonstrated the practicability of fuming sufficient acid to make up the deficiency in that naturally evolved in the Wedge furnace operation. As time progressed, less and less high sulphur material was available for Wedge roasting, and the necessity for accessory acid conditioning reached a climax when the supply of this material was entirely eliminated. Since the cast iron pots could only evaporate a few hundred pounds of acid per day, and were costly to replace, the logical thought presented itself of spraying the acid in a heated chamber. This new type of acid evaporator was simpler and more economical to operate and had sufficient capacity to fume several thousand pounds per day. The attached fig. 1 presents the outstanding features of the new furnace. A is the vaporizing drum, which is heated by the combustion gases of coal stoker fire box, B. Acid is sprayed into the hot gas stream within the drum through a number of air-acid atomizers, C, and the acid vapor, together with combustion gases, is introduced into the smoke stream through two cast iron pipes extending to different points in the flue. The operation of this type of furnace requires control of temperature inside the drum to prevent overheating, which dissociates the acid vapor to SO, and eventually to SO2, with resulting loss of acid. The dissociation to SO, at elevated temperatures is comparatively high, and in some cases accounts for as much as 60 pct of the acid sprayed into the drum. To reduce the loss of acid, through dissociation, some Cottrell plants, where the rate of acid sprayed reaches at times 9 ppm, use two evaporating units. Fuming the acid into the smoke stream is only

Jan 1, 1951

By F. A. Forward, J. Halpern

A new process is described for extracting uranium from ores containing sulphidic minerals, which comprises treating an aqueous pulp of the ore with air or oxygen at elevated temperatures and pressures. The acid required to dissolve the uranium is generated during the leach through oxidation of the sulphides. The chemistry of the process is discussed and laboratory results are presented to illustrate the operation of the method and the variables which control it. With most ores, leaching at a temperature of 130°C and an oxygen partial pressure of 10 psi provides uranium extractions of 90 to 95 pct in 4 to 6 hr. The acidity and level of dissolved impurities in the leach liquor can be kept fairly low. The method is characterized by a number of advantageous features including low reagent cost, short retention times, and high recoveries. RECENTLY there have been developed several processes for extracting metal values from ores by pressure leaching techniques;&apos; -&apos; an example is the carbonate leaching process for uranium ores which has been studied in this laboratory.&apos; Leaching is carried out under oxygen pressure to ensure oxidation of the uranium to hexavalent compounds which are soluble in carbonate solutions. During the course of investigations relating to this process, it was observed that sulphide minerals, such as pyrite, usually were oxidized under the conditions of the leach treatment resulting in the formation of iron hydroxides and sodium sulphate, i.e. 2 FeS= + 7Vz O2 + 8 Na,CO3 + 7 H,,O -* 2 Fe(OH)3 + 4 Na2SO4 + 8 NaHCO.,. [1]

Jan 1, 1956

By J. F. Elliott

PRESENT knowledge of the usual metallurgical slags indicates that they are, for the most part, rather complex in behavior and as yet there is no ready means for describing, in a simple manner, the behavior of any one of them. One of the best known slag systems is the iron oxide-silica-lime ternary which is the basic "solvent" in a number of important metallurgical refining operations, the basic open hearth being one of the most important. In this operation, the slag dissolves such components as sulphur, phosphorus, manganese oxide, and magnesia. Considerable study of this slag system and the behavior of these additions has been carried out in the past by a number of authors, as has been summarized in several critical reviews.&apos;,&apos;2 However, except for determination of the activity of iron oxide, only a limited amount of effort has been directed towards developing, from these data, an understanding of the general behavior of the basic solvent. Reported here are the results from a series of calculations based on data from the literature which permit a semiquantitative evaluation of the activities of iron oxide, silica, and lime (plus magnesia) in the ternary system at 1600°C. The preliminary results, which were reported briefly at a symposium held by AIME in 1953, have been revised and are completed. The steps in the calculation are as follows:* I—establish the activity curves and the curve of the excess molar free energy of mixing at 1600°C for each of the binary systems, 2—construct the activity surface of iron oxide for the ternary from the data on the binary systems and information available in the literature for the ternary area, 3—determine the surface of excess molar free energy of mixing for the ternary system from the activity surface of iron oxide and from the molar curves obtained for the binary system, and 4—differentiate the ternary surface of the molar excess free energy of mixing to obtain the ternary surfaces for the logarithm of the activity coefficients for silica and lime (log rslo, and log rc.~). Si0,-Fe,O: Schuhmann and Ensio have measured the activity of iron oxide in simple iron oxide-silica slags when in equilibrium with y iron. Their data recalculated to 1600°C are shown in Fig. 1. Also included is a point representing a measurement by Gokcen and Chipmana of the activity of iron oxide at 1600°C at the point of saturation with solid silica. For convenience and in accordance with other treatments,&apos; the calculations are based on the hypothetical component, FelO, which is obtained by converting all the analyzed iron in the slag to FeO. In spite of Schuhmann and Ensio&apos;s conclusion that the activity of iron oxide in the system does not vary with temperature over the experimental range of 1258" to 1407"C, the data are corrected to 1600°C assuming that temperature does have an effect. It was felt to be most reasonable to assume that the term log rr.10 is a linear function of the reciprocal of the temperature. Reyu has indicated that an effect of temperature on the activities in this system is to be expected from the Schuhmann and Ensio data. In essence, the correction consists of multiplying the experimental value of log rf,,o by the ratio of the experimental temperature in Kelvin to 1873°K. The magnitude of the correction is not large, being approximately 11.5 pct of the experimental value of log rve10. A very minor correction was necessary to compensate for the fact that the slags were in equilibrium with y iron in the experiment, while at steel-making temperatures they would be in equilibrium with liquid iron. Data for the correction were obtained from Darken and Gurry. The standard states established are pure liquid iron oxide (FelO) in equilibrium with pure liquid iron (with the appropriate amount of oxygen in solution) and pure liquid silica. The method of plotting in Fig. 1 is convenient for the calculation of the activity of liquid silica and permits a reasonable extrapolation for the activity of Fe,O in the ranges where no experimental data are available. The uncertainty in the extrapolation to infinity at one terminal where Nvelo = 1 for the usual Gibbs-Duhem integration is reduced considerably by this method. The region of two coexisting liquid phases is estimated to range from 1.8 to 41.7 mol pct Fe,O. The nature of the activity curve for the single-phase region indicates that the activity of iron oxide across the two-phase region is very close to 0.39. Computation of the function log ~F,,o/(1— NF,,o)&apos; for this region (dashed line) in conjunction with the curve through the adjusted experimental data indicate the best probable value of 0.382 for alPe,o in the two-phase area. The line from 0 to 0.018 Nf~~o is obtained by assuming that the component follows Henry&apos;s law. In this range, the value for log rveto is 2.59. Appropriate mathematical manipulation of the plotted linet yields the activity curves for the The curve AF", the excess molar free energy of mixing (actual minus ideal), as shown in Fig. 3 is also computed from Fig. 1. This curve is required for subsequent calculations. CaO-Fe,O: The phase diagram for the lime-iron oxide system when in equilibrium with liquid iron is not well known but there appears to be no intermediate compound present. This fact as well as the activity values for Fe,O extrapolated to the CaO-Fe,O binary from Taylor and Chipman&apos; tend to indicate somewhat negative deviations from ideality for the activity curves for the two components. Strong indication of this is evident in Fig. 1 where are plotted the points computed from the estimated activities of Fe,O for the binary system.&apos; It appears that the best line through the data is a horizontal straight line. Because of the general indication of the slight negative departure from ideality, the line is extrapolated horizontally to NF~,o = 0. It is con-

Jan 1, 1956

By G. W. Toop, C. S. Samis

Jan 1, 1962

By John M. Dealy, Robert D. Pehlke

This note presents a summary of the available literature on activity coefficients at infinite dilution in binary metallic solutions, Table I. These data should prove useful in not only examining the therm-odynamic properties of binary metallic solutions, but also in predicting the activity of a component in a complex alloy. The relationship proposed by wagner1 for expressing the activity coefficient in dilute solution is of the form:

Jan 1, 1963

By Klaus Schwerdtfeger, Hans-Jürgen Engell

Activities of silicon in Ni-Si melts have beelz determined in the temperature range 1480° to 1610°C from electromotive-force measurements involving the cells The data obtained are used to derive the activities of nickel and the integal free energies of mixing. Entropies of mixing are calculated from the free energies of mixing as obtained in the present study and the heats of mixing as available in the literature. ACTIVITIES in Fe-Si and Co-Si melts have been determined recently by the authors&apos; using galvanic cells consisting of alloy, an oxygen electrode, and an oxide melt as electrolyte. The present paper deals with activities in Ni-Si melts as measured with the same technique. A schematic diagram of the cell is shown in Fig. 1. The alloy and the electrolyte consisting of CaO and SiO2 are contained together in a silica-glass crucible. During the experiment the silica glass crystallizes to cristobalite on the surface of the crucible. Nickel contents of the electrolyte are very small (<0.1 pct as checked with chemical analysis), because of the noble character of nickel in comparison with silicon. A tapered silica tube is connected to the crucible through which a platinum or molybdenum wire is inserted, as shown in Fig. 1. A platinum tube reaches the surface of the CaO-SiO2 electrolyte from above. The platinum tube is provided with four holes on its side, through which oxygen of 1 atm pressure is blown over the electrolyte. The cell reaction is given by the equation Si(metal) + O2(gas) = SiO2(electrolyte) [3] and the galvanic electromotive force of the cell is given by the formula

Jan 1, 1965

By Arnulf Muan, Klaus Schwerdtfeger

Activity-composition relations in Pt-Cr and Pd-Cr alloys of low chromium concentrations UCr < 0.3) have been determined in order to ascertain quantitatively the extent of reactions to be expected between Cr2O3-containing oxide phases and platinum or palladium crucibles used as containers in studies of oxide equilibria at low oxygen pressures. This work is a continuation of similar work previously

Jan 1, 1965