By S. A. Mersol, C. T. Lynch, F. W. Vahldiek

The microhardness of single crystals of tungsten disilicide has been investigated by the Knoop method. The average random room-temperature hardness of the WSi, matrix was 1350 kg per sq mm. Hardness crnisotropy was noted with respect to plane and indenter orientation as determined by single-crq.stal X-rny studies. Annealing at 1600" and 1800°C decreased the average hardness to 1310 and 1230 kg per sq tnm, respectively, and produced a second phase identified by X-ray diffraction and electron-microprobe analysis to be wSio.7. Ball-impact experiwzents produced rosettes at 850°C. Optical and electron microscopy showed evidence of slip and cross slip and twinning produced by microhardness indentations. Prismatic (100), [001] slip was found and cor~elated with hardness data. THE present study was undertaken to investigate the hardness anisotropy of as-grown and annealed single crystals of tungsten disilicide. The existence of the silicide WSiz in the W-Si system has been well-established and its structure thoroughly investigated zachariasen2 found WSi, to have a tetragonal C type of structure, similar to that of MoSi, with lattice parameters a = 3.212A, Kieffer et al. studied the W-Si system and measured the density and microhardness (at a 100-g load) of both polycrystalline WSi, and WSi,.,. The values found were 9.25 g per cu cm and 1090 kg per sq mm for WSi,, and 12.21 per cu cm and 770 kg per sq mm for WSi0.7, respectively. According to Samsonov et a1.5 the microhardness of polycrystalline WSi2 is 1430 kg per sq mm (at a 120-g load). EXPERIMENTAL The WSi, single-crystal boules investigated in this paper were grown by a Verneuil-type process using an electric arc by the Linde Division of the Union Carbide Corp.6 The largest specimens were 8 mm in diameter by 16 mm long. The crystals had an average density of 9.01 g per cu cm with a tungsten • silicon content of 99.9 wt pct. The major impurities were: 87 ppm O, 41 ppm N. 54 pprn C, 500 ppm Zr, 50 ppm Na, and 50 ppm Mn. The crystals were silicon-poor, the average silicon content being 22.20 pct (stoichiometric value is 23.40 pct), and tungsten-rich, the average tungsten content being 77.70 pct (stoichiometric value is 76.60 pct). As-received single crystals were ground and analyzed by powder X-ray diffraction technique using Cu Ka radiation. Laue and layer line rotation patterns were obtained on cleaved sections of WSi, single crystals. Electron-microprobe traverses of representative crystals were done using a Phillips-AMR electron microanalyzer. Carbon replicas were used to prepare electron micrographs. This work was done with a JEM-6A electron microscope. Prior to the metallographic examination, the specimens were mounted in Lucite and then polished for short times on polishing wheels using 9-, 3-, and 1-p diamond-grade pastes. Finally they were fine-polished with Linde A powder for 24 hr on a Syntron vibratory polisher. The samples were etched with 4H 2 O:1HF:2HNO3, which is a medium fast-acting etchant. The combination 1HF:2HNO3:5 lactic acid is also a satisfactory etchant. Annealing runs for selected specimens were made at 1600" and 1800°C for 3 hr at 1.0 to 3.0 x 10-5 mm Hg. A Brew tantalum resistance furnace with WSi2 powder for setters was used. The WSi2 powder was the same as that used for the crystal growth. Temperatures were measured with a calibrated W, W-26 pct Re thermocouple and a microoptical pyrometer. Powder X-ray diffraction, emission spectrographic, and electron-microprobe analyses were done after the annealing runs. For microhardness measurements a Tukon Microhardness Tester Type FB with a Knoop indenter was used. Although measurements were taken at loads ranging from 25 to 1000 g, the 100-g load was chosen as the standard load. All measurements were taken at room temperature. Only indentations of cracking classes 1 and 2 were considered.' DISCUSSION OF RESULTS Powder X-ray diffraction analysis showed the as-received crystals to be single-phase WSi2. Laue and layer line rotation patterns obtained on cleaved sections of WSi2 single crystals proved them to be tetragonal WS 2 2 The results also indicated that the c axis of the crystal was oriented parallel to the boule or growth axis. Electron-microprobe traverses across the matrix of the as-grown crystals showed them to be homogeneous WSi,. Optical and electron microscopy of etched crystals, however, revealed that they contained minute amounts of the "golden" and the "blue" second phases as opposed to the "white" or WSi2 phase. These two second phases were concentrated in inclusion and etch-pit

Jan 1, 1965

By Craig R. Barrett, Jack L. Lytton, Oleg D. Sherby

The types of substructures developed during high-temperature creep of (110)[001]-oriented polycrys-talline Fe-3.1 pct Si were examined by electroetching of dislocation sites. Edge dislocations were observed to accumulate adjacent to grain boundaries and poly-gonize perpendicular to their glide planes to form a "Pile-up" of nearly parallel tilt boundaries. The dislocation density developed within the grains during steady-state creep was found to increase with increasing stress. The formation of periodically spaced groups of edge dislocations along grain boundaries was observed, and it was proposed that these formed to relive bending stresses at grain boundary shear .faults. Grain boundary serrations developed at these faults, and it was suggested that this was a result of localized grain boundary migration at the polygonized groups. THE authors have conducted a series of high-temperature creep tests on (110)[001]-oriented poly-crystalline Fe-3.1 pct Si sheet. The creep specimens were examined at various stages of creep by means of electrolytic etching of dislocation sites using the chrome-acetic acid solution developed by Morris.' Hibbard and Dunn2 have demonstrated that the etch pits produced with this technique correspond to single dislocations. It is the purpose of this paper to present and discuss the dislocation substructures which were formed during high-temperature creep at constant stress. EXPERIMENTAL PROCEDURES The polycrystalline Fe-3.1 pct Si sheet employed in this study contained a (110)[001] texture. This texture was quite strong, and the elastic properties of the sheet closely approached those of a single crystal of iron.3,4 A typical analysis in weight percent for this material is 3.1 Si, 0.1 Mn, 0.003 C,

Jan 1, 1965

By R. J. Quigg, G. S. Doble

Commercial stress -relieved TD Nickel bar was shown to retain room- and elevated-temperature tensile strength after exposure up to 2501°F. Cold swaging increased both room -temperature and 2000°F tensile strength. After annealing at 2500°F the strengthening due to swaging was retained at 2000°F hilt eliminated at room temperature. Annealing produced changes in hardness and X-ray half peak width indicating the presence of recovery processes as 1071° as 1000°F but no recrystallization of swaged material was noted at any temperature. In contrast to swaging, rolling induced a recrystal-lized structure after annealing. The tensile strength of this recrystallized structure was comparable to the cold-worked condition. High-temperature tensile properties of as -received bar were highly anisotropic with the transverse tensile strength being one fifth the longitudinal value. The aniso-/ropy is affected by working direction and may he partially reversed by changing the direction of metal flow. The divergence in tensile strength, beginning above 550°F or- approximate one third the absolute melting point, is strain-rate dependent. T D Nickel is a commercial dispersion-hardened alloy containing 2 vol pct thoria. The dispersion, consisting of spherical particles 0.030 to 0.050 in diameter with an interparticle spacing of less than 1 is reported to maintain stable properties up to 2400°F.1 This stability of second phase results in maintenance of elevated-temperature strength at higher temperatures and longer times than normal nickel-base superalloys.2 The purpose of this paper is to describe the effect of various mechanical working operations on the strength and microstructural stability of TD Nickel bar. MATERIAL AND PROCEDURES All material used in this study was commercial TD Nickel bar. This material is produced by a chemical process which results in a nickel powder containing a dispersion of thoria particles. The powder is then pressed, sintered, extruded, and subsequently worked to bar stock. Three starting materials from three separate lots were used: as-extruded bar. 1-in.-diam stress-relieved bar, and 1/2-in.-diam stress-relieved bar. Since TD Nickel bar stock is cold-worked without a recrystalliza-tion anneal, the accumulated deformation or degree of cold work in these materials increases as the bar diameter decreases. Some of the 1/2-in.-diam bar was swaged to 1/4 in. diameter at room temperature in order to produce an as-worked condition for comparison with the stress-relieved stock. Tensile testing was performed on an Instron Tensile Tester at a constant crosshead speed of 0.020 in. per min. The 0.2 pct offset yield strength was measured from the load-crosshead movement plot. Specimen gage dimensions were 0.080 in. in diameter by 0.40 in. in length, producing a strain rate of approximately 0.050 min-1. Specimens were tested in air and heated within a resistance-wound furnace controlled to ±5°F. A 15-min soak at temperature was employed before testing. Samples were heat-treated in air and specimens machined after exposure with sufficient material removed to eliminate any surface contamination. X-ray line breadth was determined from a diffractometer scan of a transverse face of a bar using copper K, radiation. Metallographic preparation utilized standard mechanical polishing with Carapella's etch. Specimens for electron microscopy were electropolished in a 1:7 sulfuric/methaol solution and chromium-shadowed collodion replicas prepared. RESULTS AND DISCUSSION I) Effect of Elevated-Temperature Exposure on the properties of TD Nickel. The effect of various elevated-temperature exposures on the room-temperature tensile strength of TD Nickel is shown in Table I. In the unexposed condition the tensile strength, reduction in area, and hardness all increase with increasing accumulated deformation while the elongation decreases. After exposure at 2500°F the strength of all three materials decreases to about 65,000 psi and the elongations increase slightly. The apparent increase in strength of the 1-in. bar after a 2000°F treatment is probably experimental scatter. These results indicate that the room-temperature strengthening due to additional deformation is annealed out upon elevated-temperature exposure. In contrast to the room-temperature data, the 2000°F tensile strengths increase in order of increasing deformation even after exposure. Although some loss of strength occurs after exposure, much of the effect of working is still maintained at 2000°F. The room-temperature hardness after various

Jan 1, 1965

By A. S. Koster, G. D. Rieck

X-ray experiments were carried out to show the occurrence of cylindrical texture in drawn tungsten wire. Only a small amount of (110) (110) cylindrical texture could he found in wires of intermediate thickness, i.e., of about 1.5 mm diameter. DRAWN wires of tungsten and other bcc metals like iron and molybdenum show a well-established (110) fiber texture. Now it might be conceivable that in drawing radial stresses remove the randomness of the crystallites around the [110} axis, thus giving a fiber texture of higher symmetry. In the resulting so-called cylindrical textures a specified plane normal coincides with the radius of the wire. Several authors discuss the occurrence of cylindrical textures in bcc metals. ~ieck' found no cylindrical texture in drawn tungsten wires of 165 n diameter. Leber~ states that in tungsten wires of 3 mm diameter a cylindrical {100)(110) texture is developed, which is gradually converted to a normal fiber texture by subsequent drawing. He also reported a definite cylindrical texture at the surface of iron wires. Peck and Thomas3 observed a nonuniform mode of deformation of the grains in transverse sections of heavily drawn tungsten and iron wires. According to Bhandary and cullity4 a swaged iron wire has neither a perfect (110) fiber texture nor a perfect {100}(110) cylindrical texture. It is clear that the concept of cylindrical texture in bcc metals still lacks a firm experimental basis. Leber's eviden~e,~ which seems to be the strongest, rests upon qualitative interpretation of photographs. The appearance of the 110 and 200 lines on the photograph of 3-mm wire, however, can be very well attributed5 to a normal ( 110) fiber texture superimposed on random background; our Fig. 1, giving a Debye-Scherrer diagram of etched tungsten wire of 180 p, is free of cylindrical texture according to all authors, but is quite similar to Leber's diagram. It was therefore decided to use a different method of X-ray texture determination on tungsten wires of diameters where cylindrical textures may be expected.

Jan 1, 1965

By G. T. Horne, P. J. Wray, S. Kinoshita

CONSIDERABLE evidence exists for a strengthening mechanism operative at intermediate temperatures in bee metals containing interstitial solute atoms. The strengthening is indicated by a maximum in the ultimate tensile strength1 as well as the fatigue

Jan 1, 1965

By W. E. Howlett, R. L. Slobod

Jan 1, 1965

By R. F. Hehemann, R. H. Goodenow

Thermal arrest, hot-stage microscopy, and transtnission electron microscopy techniques have been employed to study the transformations in low-carbon iron and Fe-9 pct Ni alloys. In continuous cooling experiments, each alloy transforms at an essentially constant temperature for cooling rates below the critical rate required for martensite formation. However, high-tenzperature transformation in pure iron takes place by a different mechanism than that in the 9 pct Ni alloys. Pure iron exhibits an equi-a a structure with a low and random dislocation density while the 9 pct Ni alloy exhibits a cell or lathlike substructure analogous to that of low-carbon martensite. This same substructure characterizes upper bainite in higher-carbon inaterials. UNTIL relatively recently, diffusionless transformations have been considered to take place by the same mechanism and have been termed mar-tensitic transformations.l-3 The most characteristic feature2 of this mode of transformation is the shape change produced by a shear deformation and growth of the product phase frequently occurs at an extremely high velocity approaching that of an elastic wave.4'5 A different mechanism of diffusionless transformation was recognized first in Cu-Ga and other copper-base alloys.6,7 From the absence of surface tilting in these alloys, it has been concluded that transformation is not accomplished by the cooperative shear displacements that occur in mar-tensitic reactions. Transformation presumably takes place by the rapid movement of an incoherent interface which is capable of propagating across parent grain boundaries. Although the transformation is diffusionless in the macroscopic sense, advancement of these interfaces is accomplished by an atom by atom rearrangement. Transformations of this type therefore require thermal activation and are generally operative only at high temperature. Although requiring short-range diffusion at the interface, propagation still occurs so rapidly that the reaction cannot be suppressed with normal cooling rates.7 The resulting microstructures exhibit large, irregular-shaped regions of the product phase, which are essentially free of crystallographic features. Consequently, these reactions have been termed massive transformations. Transformation by the massive mechanism has been reported to occur in ferrous systems involving pure iron and binary alloys of iron with nickel, chromium, and silicon by Gilbert and owen.' The Fe-Ni system is of special interest in that the massive transformation was observed in alloys with less than 15 pct Ni while alloys having more than about 28 pct Ni transformed by the conventional mar-tensitic mechanism. By employing cooling rates substantially higher than those used by Gilbert and Owen, Swanson and Parr have been able to suppress the massive transformation in alloys with 0 to 10 pct Ni9 and produce martensite as revealed by surface relief. The massive transformation in the alloys having less than 15 pct Ni was identified by the lack of surface relief and an irregular rather than clearly acicular microstructure.' Speich and Swann, using thin-foil electron microscopy, identified three distinctly different structures10 in quenched binary Fe-Ni alloys. From 0 to 4 pct Ni the structure consisted of blocky grains of a with a low and random dislocation density. Alloys with 4 to 25 pct Ni exhibited a cell structure with a high dislocation density; and at greater than 25 pct Ni the structure consisted of internally twinned plates. The structural change at approximately 4 pct Ni suggests that alloys with low nickel content transform by a different mechanism than those with intermediate nickel contents and the transition from the cellular to the internally twinned structures at approximately 25 pct Ni is analogous to the transition from needles to internally twinned plates that occurs over a narrow range of carbon contents in Fe-C martensites.11,12 Conventional bainitic and martensitic modes of austenite decomposition operate in ternary Fe-C-Ni alloys having less than 10 pct Ni. This investigation was conducted in order to explore the conditions under which the massive, bainitic, and martensitic transformations occur and the relationships between these modes of decomposition.

Jan 1, 1965

By D. E. Peacock, B. Harris

The mechanical behavior of a niobium (columbium)TUNG alloy containing 20 wt pet Ta. 15 wt pet W, and 5 wt pct Mo has been studied in the temperature range 77° to 423°K. All specitrzens tested, apart from those into which oxygen was introduced deliberately, were fully recrystallized at 1500°C, had an average grain diameter of approximately 0.03 mm, and a combined carbon, ox-vgen. nitrogen, and hydrogen content of not not more than 250 ppm The meckatnical behavior of this alloy was found to be similar in seine respects to that of unalloyed bcc transilion metals. Both yield and flow stresses were sensililae to changes in deformation rate and both increased rapidly as the temperature was lowered below 150°C. A detailed examination revealed, however, that most of the temperature dependencc of the yield stress could be accounted for by the temperature dependence of the elaslic, modulus, whish is not true of the unualloyed metals. In lension at moderate strain rates, the trunsition fvom ducfile to hvittle behavior occurred just belour room teunperature bur incveasing the oxygen content from 190 to 200 pptn raised the transition temperature to about 4000K. TUNGSTEN and molybdenum have been found to be very effective high-temperature solid-solution strengtheners of niobium, but the amounts of these elements that can be added are limited if the alloy is to retain useful room-temperature ductility. It has been shown, however, that partial replacement of niobium with tantalum lowers the ductile-to-brittle transition temperature of such alloys and allows larger additions of molybdenum and tungsten to be made. Some of the high-temperature properties of niobium alloys containing these elements have been reported by Bartlett et al.,' and the work presented here describes the low-temperature behavior of one of these, a solid-solution alloy containing, by weight, 20 pct Ta, 15 pct W, and 5 pct Mo. The elastic modulus, the temperature and strain-rate dependence of the yield and ultimate tensile stresses, and strain-hardening effects are discussed and compared with those of unalloyed niobium. EXPERIMENTAL MATERIAL AND PROCEDURE The material used in this investigation was produced from a 6-in.-diameter, double arc-melted ingot. This was can-extruded at about 1150°C to a 3-in.-diameter billet, and after annealing for 1 hr at 1345°C the billet was heated to 1315OC and part rolled and part forged to 0.5-in.-thick plate. The resulting material exhibited a cold-worked structure

Jan 1, 1965

By T. S. Plaskett

A striated structure perpendicular to the growth axis was observed by the copper-decoration tech-nique in dislocation-free, .float-zoned silicon crystals. The striations, which were spaced about 100 p apart, fitted the relationship d = f/u , where d is the spacing, f is the growth rate, and u is the crystal rotation rate. Each stria was resolved into an UNDOPED silicon crystals pulled from quartz crucibles by the Czochralski technique usually exhibit a striated structure perpendicular to the growth axis.'-' This structure has been attributed to oxygen segregation, with the oxygen being introduced from the quartz crucible. If the crucible is rotated, the level of oxygen contamination has been reported as high as 10° atoms per cu cm.10 These striations are similar to solute striations commonly observed in doped Czochralski-grown crystals. The periodic nature of the striations is caused by a periodic variation in the growth rate",12 which is attributed mainly to thermal gradients in the melt.13 A finer striated structure14 attributed to constitutional supercooling is sometimes observed between the coarse striae. The oxygen striations have been observed by infrared transmission techniques,' by the copper-decoration technique,' by X-ray diffraction microscopy,6-8 and by 9 p absorption measurements3 on crystals pulled from the melt both with and without dislocations. In this investigation float-zoned dislocation-free crystals were examined by the copper-decoration technique. The level of oxygen for float-zone material is less than 1016 atoms per cu cm the lower limit of detection by 9 p absorption measurement. EXPERIMENTAL TECHNIQUE The crystals were grown by the float-zone process with the rf heating coil outside of the quartz envelope containing the silicon. All float zoning was done under an atmosphere of purified helium. The Dash technique15 was used to grow the crystal dislocation-free. This involves growing the crystal initially with a diameter between 2 and 3 mm and at array of starlike precipitates of copper. The strucLure was not .found at the surface tor a depth of about 1.5 mm, or in a region of similar width ahead of a dislocation network. The structure is postulated to consist of vacancy clusterings or dislocation loops. very rapid rates, about 20 mm per min, for a distance of about 3 cm. The diameter of the crystal is then increased to the diameter of the source of silicon, which in this case was about 19 mm. Because of the arrangement of the apparatus, the zone was passed downward rather than upward, contrary to the standard float-zoning practice. Also, the source was rotated rather than the seed. ziegler17 has made dislocation-free crystals by a similar technique but has passed the zone upwards. The starting material was zone-refined and had a p-type resistivity of 150 ohm-cm. The major impurity was boron; the total impurity excluding the boron was reported by the supplier (Dow-Corning) to be typically less than 2 x 1013 atoms per cu cm. The crystals were examined by the Dash copper-decoration technique18'19—a method in which about 10" atoms per cu cm of copper are diffused at a temperature between 900" and 1000°C into silicon which is then quenched to room temperature. On quenching, the copper precipitates on crystalline defects which are then visible when viewed by transmission infrared microscopy. The photomicrographs shown were taken either of the infrared image tube screen or directly on infrared film. All sections prior to decorating were chemically polished and, for some sections, given a sirtlZ0 dislocation etch-pit examination. After decorating, the samples were mechanically polished. RESULTS A photomicrograph, taken in transmission of a decorated cross section, is shown in Fig. 1. The portion of the section shown is near the surface of the crystal. The entire cross section showed no dislocation etch pits after being given a Sirtl etch treatment. It is seen that the copper precipitated randomly. Each precipitate, as has been reported by others, was found to have a starlike structure.

Jan 1, 1965

By M. J. Marcinkowski, R. M. Fisher

The flow stress-grain size relationship has been determined at room temperature in both a disordered and a fully ordered FeCo for plastic strains up to 30 pct. The results are in agreement with a Hall-Petch relation of the type given by Of =a,+kd-1/2 where of is the flour stress and a, increases mono-tonically with increasing strain to a maximum value which is much higher for the ordered than for the disordered alloy. The slope, k, is found to increase FOLLOWING the original work of Halll and petch relating the effect of grain size to the lower yield stress of iron and steel, it has been generally found that the yield stress oy.s. of polycrystalline metals with strain to a maximum and then decrease for both ordered and disordered alloys. However, k for the ordered alloy is in general higher than that for the disordered alloy and the critical strain for k max somewhat larger. All of these observations can be satisfactorily accounted for quantitatively and in some cases semiquantitatively by using a slip band-grain boundary intersection model, and by taking note of the fact that, in general, moss slip, while quite common in the disordered alloy, is extremely difficult in the ordered alloy. obeys a relation of the form oy.s.=a0+kd-1/2 [1] where a, and k are constants and d is the mean grain diameter. For convenience, and in accord with prevailing custom, Eq. [I] will be referred to simply as the Petch relation. Tjerkstra3 and Armstrong, Codd, Douthwaite, and petch4 showed that the flow stress af of iron or steel measured at strains of up to at least 20 pct also obeyed a relationship of the type given by Eq. (11. The latter investigators have also shown that Eq. [I] applies to fcc and hcp metals and alloys.

Jan 1, 1965

By Roman Šejnoha, Karel Mazanec

A pronounced tendency for delayed fracture zoas observed in the martensite structure of low-alloy steels in the as-quenched condition. Cracks of predominantly intercrystalline nature nucleated and propagated at stresses substantially lower than the short-titne tensile strength of- the steels, and were observed even in hydrogen-free speciunens. The occurrence of delayed fractures in the as-quenched condition is interpreted as a supevposition of the effect of free dislocations generated during the martensite transforlnation, and of a weakening of the prior austenite grain boundaries caused by dynamic shocks exerted on the boundaries by growing martensite plates. AN important metallurgical problem, connected with the production and use of high-strength steels, is delayed fracture in martensitic structures. Such fractures occur in quenched steels as a result of prolonged loading with external stresses far lower than the short-time tensile strength of the steel. The same effect can be produced by sufficiently high internal stresses: it is well-known that quenched structures will in some cases crack intergranularly at room temperature if not tempered quickly enough even in the absence of any externally applied stress. In Troiano's papers1,2 on delayed fractures in high-strength steels, the fundamental role of hydrogen migrating under the influence of multiaxial stress towards the nuclei of cracks was found. Fig. 1 shows the typical relationship between stress and the time to fracture found by Troiano in hydrogen-charged high-strength steels. On the other hand, Shurakov 3,4 explains the realization of delayed fractures in martensite as due to a "quasi-viscous" behavior of the austenite grain boundaries immediately after the martensitic transformation. 1) MATERIALS AND EXPERIMENTAL METHODS Two low-alloy steels of commercial purity were used for the experiments reported in this paper. Their chemical composition is shown in Table I. The heats were melted in a laboratory furnace, cast to ingots, forged to bars of 3/4 in. diameter, and annealed. Machined test pieces were heat-treated as follows: Ni-Cr-Mo steel held at 900°C for 30 min and quenched in oil; Mn-Si-Cr steel held at 900°C for 30 min and quenched in water. For the delayed-fracture tests, notched cylindrical test pieces, Fig. 2, stressed in torsion, and unnotched cylindrical tensile-test pieces, 1/4 in. diameter, were used. The specimens were normally loaded with a constant static load 45 min after quenching for the torsional tests and 10 min

Jan 1, 1965

By J. Nutting, D. H. Kirkwood

The oxidation of lead sulfide in air between 200° and 350°C has been investigated by electron diffraction from thick sulfide films and from galena surfnces. It has been demonstrated that sulfate is the stable reaction product up to 570°C. Sulfate is HAGIHARA has investigated' single crystals of galena roasted in air by the reflection electron-diffraction technique, which owing to the very limited penetration of the beam into the crystal gives information of the nature of the surface only. He has shown that up to 280°C the first oxidation product is lead sulfate, followed by lead mono-oxysulfate (PbO . PbS04). At longer times and higher temperatures more complex patterns appeared which could not be analyzed. All of these patterns were of streaks or spots arising from crystals oriented on the galena surface, and it is probable that these crystals are lead compounds whose structures have not been determined, such as the other oxysulfates (2Pb0 • PbS04 and 4Pb0 . PbS04) or a number of oxides. Certain lead sulfide films, formed chemically, give ring patterns in transmission electron diffraction2 because they are polycrystalline, and should also give ring patterns of the products after oxidation. It was thought that a diffraction study would reveal the sequence of phases produced in the reactions at different temperatures, since X-ray powder patterns are available for many lead compounds. PREPARATION OF FILMS The films were prepared by passing H2S over a saturated solution of lead nitrate in water. Once a silvery film had formed on the solution surface, no further thickening was apparent. The films were transferred by a gauze to a bath of distilled water for washing and pieces of film were caught on small discs on which they were dried. The discs were formed initially on galena up to temperatures of 300°C, followed by oxide and oxysulfates in turn at longer times. The appearance of- these phases is believed to result from an inadequate rate of supply of sulfur to the top surface 01. the crystal. standard Siemens mounts, made of platinum alloy, and had seven 20-p apertures drilled through them. The parts of the film which had dried onto the disc surface were light blue in color, which is the interference color of a film about 600A in thickness. A strong pattern of lead sulfide was obtained in transmission electron diffraction through the apertures but slight broadening indicated a crystallite size of around 200A. Tilting a sulfide film in the beam produced arcing of the rings, increasing the intensities of the (Ill), (3111, and (222) rings and reducing (200) and (220). This arises from preferred orientation in the film, a [loo] direction of the crystallites being normal to the plane of the film. These specimens were oxidized in an oven maintained at the required temperature. The reported times include that taken to heat the film to the reaction temperature. STABLE PHASES FORMED IN OXIDATION The conditions in which various oxidation products of lead sulfide are stable have been considered by the authors in a previous paper.3 It was shown that in a normal atmosphere, taken as containing lo-' atm of SOs, lead sulfate would be stable up lo about 570°C. This was confirmed by oxidizing thin films of sulfide for several days, and the analysis of the transmission-diffraction pattern is given in Table 1. The fit with the patt$rn from X-rays is good, except for the missing 3.62A ring. Some disagreement in intensities of reflections given by X-rays and electrons is to be expected. Up to 570°C a spotty pattern of sulfate was still obtained, indicating grain growth, but above this temperature the film disintegrated. Probably this is associated with the decomposition to PbO . PbS04. It needs to be emphasized that the atmosphere

Jan 1, 1965

By H. G. Sell, G. W. King

An investigation was made of the lensile proper-ties of recrystallized high-purity tungsten and a W-1 pel ThO2 dispersed-phase alloy over the temperature region of 800° to 2400°C. The thoria addition resulted in a modest strengthening effect over the entire temperature region. A decrease in ductility of both materials occurred above 0.5 Tm which was caused by void formation. Current theories of IT has long been recognized that a second phase of hard particles has a strengthening effect on a pure metal. At low or intermediate temperatures (<0.5 Tm), the strengthening effect is thought to arise mainly from the interaction of dislocations with dispersed particles. Above 0.5 Tm, dynamic recovery processes greatly alter the deformation mechanisms from those simply involving glide, and grain bound- strengthening by a dispersed second phase do not adequately explain the tensile results. Melallographic examination suggests that the improved strength of tire alloy results from the effect of thoria on the mierostructure. Stress-dependent thermally activated processes were found to occur high temperatures. aries may act as sources of weakness rather than strength because of grain boundary sliding. Grain boundary sliding at high temperatures has been postulated to be the primary factor giving rise to the formation of voids or cavities at grain boundaries1-3 which in turn cause premature failure and poor ductility.4 Voids, once formed, can grow by the condensation of vacancies from the equilibrium concentration&apos; or from the excess vacancies produced by the deformation.4,5 The high-temperature tensile properties of unalloyed tungsten have previously been investigated by Sikora and Ha116 and also by Taylor and Boone.7 The purpose of the present work was to investigate

Jan 1, 1965

By C. E. Ells, A. Sawatzky

The effect of neutron irradiation on tensile properties of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy has been evaluated for integrated neutron fluxes up to 3 x 1020 n per sq cm (E > 1 Mev). Specimen temperature during irradiation was normally 300°C. The material was studied both in annealed and in quenched and aged conditions. When the alloy (fab-ricatedfrom sponge zirconium) is quenched from a temperature =40°C below the a + ß/ß transformation and aged 6 hr at 535oC, neutron irradiation up to the maximum studied has little effect 071 reduction in area, although there is a drop in uniform elongation and the yield strength is increased by = 25 pct. Conversely, irradiation of the alloy in an annealed condition can result in much greater changes in properties, with yield-strength increases of up to 200 pet. The dose dependence of irradiation hardening obeys the saturation equntion proposed by Makin and Minter to explain hardening in copper and nickel: Act = C[1 - exp(-Døt)/1/2 A rnodel is proposed to explain the effect of niobium content and metallurgical condition on irradiatiotz behavior. THE Zr-Nb alloys form a class of material susceptible to marked strengthening by quench and age heat treatment. With niobium concentrations as low as 2.5 wt pet, strengths can be developed which are double those of annealed zircaloy-2.1 Since the neutron-capture cross section of the Zr-2.5 wt pet Nb alloy is nearly identical to that of Zircaloy-2, significant gains in power-reactor neutron economy could be obtained by replacing stressed in-reactor components of Zircaloy-2 with the heat-treated Zr-Nb alloy. When the solution heat-treatment temperature is in the high (a + ß) phase, then the tensile properties of the quenched (and aged at 500°C) material have been shown to be relatively insensitive to neutron irradiation.1-3 Addition of small quantities of copper to the binary Zr-2.5 wt pet Nb alloy gives a useful reduction to the corrosion rate in air and carbon di- oxide,&apos; and a ternary alloy of composition Zr-2.5 wt pet Nb-0.5 wt pet Cu was chosen for one component in the Douglas Point Reactor. This application utilizes both the corrosion resistance to a moist air-carbon dioxide environment and the strength developed by a quench and age heat treatment. By suitable choice of solution heat treatment and aging temperatures, tensile properties of the ternary alloy can be made nearly identical to those considered as optimum for the binary alloy. One effect of the copper addition, however, is to give marked changes in the aging kinetics of the alloy.&apos; For this reason, it appeared that neutron irradiation might promote overaging in the ternary alloy, particularly at the elevated service temperature (=300°C). This paper describes the effect of neutron irradiation on the tensile behavior of the Zr-2.5 wt pet Nb-0.5 wt pet Cu alloy in several metallurgical conditions pertinent to its use as a reactor material. The metallurgical conditions included those for which aging occurs in the unirradiated material, and fully annealed conditions for which a higher degree of thermal stability could be expected. 1) EXPERIMENTAL Two batches of alloy were used, both made from sponge zirconium. The fabricator&apos;s analysis of principle constituents showed no significant difference between the two batches, Table I. The rod material was rolled to 1.5 in. diam, and then swaged to final sizes of 0.5 to 0.375 in. diam at nominal temperatures of 785" and 625°C for the AM and AS batches, respectively. Subsequent hydrogen analyses at CRNL confirmed that the hydrogen concentration of the as-received rod was indeed <20 ppm. However, it was found that the (a + ß)/ß transus for the AM material was approximately 25°C lower than that of the AS material, indicating rather more difference in oxygen concentration than given in Table I. Except for a small difference in yield-point behavior, the tensile prop-

Jan 1, 1965

By P. A. Toynbee, D. G. Wilson

The combustion performance of sub-bituminous slack coal is greatly improved by the removal of the smaller size fractions. Screening processes are not well suited to the size separation, at 1/8 in. or 1/16 in., with coals which are normally wet, and the use of an alternative size-separation device has been investigated. It is felt that this classifier might be applied equally well to other minerals in cases such as this, where precise size limits are not essential. Coal is dropped as a curtain onto a curved metal plate, shaped rather like a ski-jump. The smaller particles, slowed up in their free fall to the plate and also by contact with the metal, leave the plate with a lower horizontal velocity; they can be separated from the larger particles by virtue of their shorter trajectory. The principle of the classifier is obvious from the diagram (see Fig. 1) which shows also the positions, relative to the curved plate, of the point of coal feed and of the dividing plate which separates the streams of coal particles. The horizontal distance between the curved plate and the dividing plate is varied in the tests. It is designated in the general case, by X. Tests were carried out using slack coal with a free moisture content higher than that expected in any commercial operation. The results given in Table I. show the percentage recovery of upgraded product, and the cumulative screen analysis of both the upgraded and reject material, for three different positions of the dividing plate. The results show, for example, that the original coal can be upgraded, with a recovery of 80%, to reduce the minus 1/8 in. frac-

Jan 1, 1965

By R. Scot Clark

The reactively sputtered silicon dioxide capacitor -was developed for use in the monolithic integrated circuit, thereby requiring the capacitor to be fabricated on an oxidized silicon slice. The silicon dioxide film is formed by reactively sputtering silicon in a 50 pct Ar-50 pct 0, atmosphere and the physical properties are indistinguishable from silica. A practical upper limit of capacitance per unit area of 0.25 pf per sq mil is reached with the capacitors fabricated from the Si0, film. Methods shown to enhance this value are double stacking the thin-film capacitors and addition of aluminum to the silicon cathode during sputtering to form an aluminosilicate dielectric. A major contribution to the field of diffused integrated circuits would be the addition of auxiliary passive devices for replacement of diffused passive devices which are currently being fabricated for many integrated circuits. This accomplishment would increase the flexibility of the diffusion process in order to concentrate more on transistor parameters rather than on fabricating diffused resistors and capacitors. To pursue this technique, a thin-film SiOz capacitor was developed which has _ proven applicable to many integrated circuits. Although the SiOl capacitor has an application, the major deterrent from extending the integrated circuit into many useful areas such as low-frequency linear application is the low dielectric constant of SiO, and the low usable capacitance in an integrated circuit. This paper will cover the sputtering techniques used for forming the SiO, film, the physical and electrical properties of sputtered SiO,, and yield information concerning the application of these capacitors to integrated circuits. REACTIVE SPUTTERING Reactive sputtering is simply the sputtering of a metal or semiconductor in glow discharge in the presence of a reactive gas. The material to be sputtered is seen in Fig. 1 as the cathode of the system and is bombarded with positively charged ions of the ambient gas. In this investigation, the ambient gas is composed of 50 pct Ar and 50 pct O2 at a pressure of approximately 2.5 X l0-&apos; Torr. The ions are accelerated toward the cathode in the cathode dark space by the electric field and upon striking the cathode effect a momentum energy transfer to the surface atoms. The transferred energy is sufficient to dislodge a surface atom or atoms and these particles diffuse through the glow discharge to the collector or anode. Several mechanisms of oxidation in the reaction chamber can be considered during reactive sputtering. 1) The surface of the cathode is oxidized and the oxide is subsequently sputtered. 2) Oxidation and sputtering occur simultaneously. 3) Sputtering of the cathode material is followed

Jan 1, 1965

By F. Paredes, W. R. Holman, R. W. Crawford

The diffusion coefficient for hydrogen in the ß titanium alloy containing 13 pct V, 11 pct CY, and 3 pct A1 was measured over the temperature range 20° to 500°C. Results fit the expression: D= 1.58 x lgs exp-------==-----) cm2,sec THE diffusion coefficient for hydrogen in the metastable ß-phase titanium alloy containing 13 pct V, 11 pct Cr, and 3 pct A1 was measured as part of an investigation of the effects of hydrogen on the mechanical properties of titanium alloys. Several theories on the mechanisms of hydrogen embrittle-ment include diffusion of hydrogen at ambient temperature as an important step in the embrittling process.&apos;-5 In hydrogen-contaminated a-ß titanium alloys, it has been postulated that the rate-controlling step may be the rate at which hydrogen diffuses from the ß phase to stress- or strain-nucleated brittle hydride platelets at the a-ß interface.&apos; However, embrittlement of the all-ß alloy investigated in this work may proceed by a different mechanism, since this alloy can be embrittled without the formation of detectable hydride platelets.6 Troiano has suggested that in this case the mechanism of delayed failure or embrittlement is similar to that proposed for high-strength steel, i.e., repeated crack initiation caused by a decrease in bonding energy as hydrogen diffuses to points of high tri-axial stress at the root of a notch. In both types of alloy the rate of embrittlement is believed to be controlled by diffusion of hydrogen in the ß phase. Accurate hydrogen-diffusion data in the vicinity of room temperature should therefore be of some assistance in understanding the mechanisms of embrittlement in these two classes of titanium alloys. Diffusion of hydrogen in pure titanium has been studied by Wasilewski and Kehl7 at temperatures above 500°C. Their measurements on diffusion in the ß phase were extended below the ß-a transformation temperature (882°C) to approximately 600°C. This was possible because of the 8 stabilizing effect of hydrogen. No results at lower temperatures have been published and there are no data in the literature on hydrogen diffusion in the ß -phase alloy used in this program. Hydrogen diffusion in metals is generally investigated by measuring the rate of transport of hydrogen past a solid-gas interface, i.e., by absorption, permeation, or degassing-rate measurements. These methods produce accurate diffusion data when bulk diffusion is the rate-determining step in the over-all process. However, at the lower temperatures of interest in hydrogen-embrittlement studies or under conditions where surface films are present, the measured rates may be surface-controlled and the calculated diffusion coefficients will be in error. Surface effects were eliminated in the present work by using a modification of the common welded-couple technique m which two bars with uniform but different compositions are joined before the diffusion anneal." The same type of step change in the initial concentration vs distance curve was produced by electrolytically hydrogenating thin-strip specimens which had been electrically insulated over half of their length. Concentration vs distance curves were determined, after appropriate diffusion-annealing treatments, by vacuum-extraction analyses of transverse samples sheared from the strips. Diffusion coefficients were calculated by the methods of Grube.M This technique was feasible because of the large concentrations of hydrogen which can be charged into p -phase alloys without the formation of hydrides15&apos;16 and because of the extremely low degassing rates observed when hydrogenated titanium alloys are heated in air. EXPERIMENTAL WORK The diffusion couples were cut from a 0.022-in.-thick mi ll-annealed sheet.* Strips 8 in. long by 1/2

Jan 1, 1965

By C. J. Beevers

Tlze influence of zirconium hydride precipitate mprphology on the fructure of Zr-H alloys tested at strain rates of 10- sec at 20° and - 196°C and at strain rates of -500 sec.-1 at 20°C has been inves-tigated. The critical stage in the embrittlement of these alloys was the fracture of the zirconium hyhide precipitates to form large interval cracks at a stress of 25,000 10 137,000 psi. In specimens con-temping up to 100 ppm H the preciptates existed as isolafed platelets in the zirconium matrix and their fracture as enhanced by low temperature (—196°C) and high strain rate (-500 set-f) loading. These resl~lts lead to the conclusion that the rate of strain hardening of the zirconium metal controls the frac-tzrm of the hydride platelets. Increased hydrogen contents of 500 to 2000 ppm resulted in an increase in the 1)volume fraction and size of precipitates and crlso led to crack propogation in the hydride at both 20 and —196C at the low strain rates (10&apos;* sec-&apos;). Quenching led to refinerment of hydride precipitate size and reduced the degree of embrittlement at — 196°C; this effect is attributed to the absence of fracture of the fine precipitates. The formation of zirconium hydride precipitates has been shown to be the cause of hydrogen embrittlement of zirconium.&apos; Several investigators&apos;-" have studied the problem in broad outline, demonstrating that impact-loading conditions, testing temperatures below room temperature, and increasing hydrogen content produce increased brittleness. For example, Muehlenkamp and schwope2 showed that the transition temperature for notched impact tests was raised from 150" to 350°C on increasing the hydrogen content from 45 to 490 ppm. The degree of embrittlement is also controlled by the morphology of the zirconium hydride precipitates. The solubility of hydrogen in zirconium decreases from 600 ppm at 550°C to 10 ppm at 20"C,~ so that the form of the zirconium hydride precipitates (ZrH2) can be modified by varying the cooling rate through the Zr-aZr + ZrH2 phase boundary.= Forscher showed that quenching a specimen containing 35 ppm H from above 315°C resulted in a reduction in area of 70 pct at -196"C, whereas slowly cooling from above 315°C resulted in a ductility of half this value. The role of the hydride precipitate in the fracture process has been examined by Young and schwartz6 and more recently by westlake.&apos; From metallo-graphic observations on slowly cooled Zr-H alloys they have suggested that cracks are nucleated in the hydride precipitates by the interactions of twins in the zirconium metal with the hydride. The experiments reported in this paper show that crack propagation in the zirconium hydride precipitates is the critical stage in the embrittlement of Zr-H alloys. The factors influencing fracture of the hydride precipitates and crack propagation in the zirconium metal will be related to the problem of embrittlement. EXPERIMENTAL TECHNIQUES The zirconium used in these experiments was produced from an ingot of vacuum arc-melted iodide zirconium forged down to 1 in. diameter at 800&apos; to 850°C. The 1-in.-diameter bar was surface-machined and cold-swaged to 0.375 in. diameter. After a vacuum anneal at 800°C for 1 hr the hardness was 60 to 70 Vdh. The total impurity content was approxi-

Jan 1, 1965

By J. Lohrenz, C. R. Clark, B. G. Bray

Procedures to calculate the viscosities of in situ reservoir gases and liquids from their composition have been developed and evaluated. Given a composition expressed in methane through heptanes-plus, hydrogen sulfide, nitrogen and carbon dioxide together with the molecular weight and specific gravity of the heptanes-plus fraction, the procedures are capable of calculating the viscosity of the gas or liquid at the desired temperature and pressure. The procedure for reservoir liquids was developed using the residual viscosity concept and the theory of corresponding states, and was evaluated by comparing experimental and calculated results for 260 different reservoir oils ranging from black to highly volatile. The average absolute deviation was 16 per cent. This is the first known procedure for calculating the viscosity of reservoir liquids from their compositions as normally available, i.e., including the heptanes-plus fraction. The procedure for reservoir gases uses a sequence of previously published correlations. Evaluation of the procedure was accomplished by comparison of 300 calculated and experimental viscosities for high-pressure gar mixtures in the literature. The average absolute deviation was 4 per cent. The calculations are useful for (I) determining viscosities in compositional material balance computations and (2) predicting the viscosity decrease which occurs when gases, LPG, or carbon dioxide dissolve in reservoir oils. INTRODUCTION Methods to predict viscosities of reservoir fluids from the normally available field-measured variables have been presented. Beal,1 Standing,2 and Chew and Connally3 orrelated oil viscosities with temperature, pressure, oil gravity and gas-oil ratio. Carr, Kobayashi, and Burrows4 and Katz et al.5 have presented correlations for reservoir gas viscosities as a function of temperature, pressure and gas gravity. Lie all intensive physical properties, viscosity is completely described by the following function: Eq. 1 simply states that viscosity is a function of pressure, temperature and composition. These previous correlations1- hay be viewed as modifications of Eq. 1, wherein one assumes more simple functions may be used. The assumptions are practical, because the composition is frequently not known. Further, the assumptions are sufficiently valid so that these correlations are frequently used for reservoir engineering computations. In compositional material balance"&apos; computations, the compositions of the reservoir gases and oils are known. The calculation of the viscosities of these fluids using this composition information is required for a true and complete compositional material balance. For reservoir gases, Carr, Kobayashi and Burrows4 have presented a suitable compositional correlation. For reservoir oils, no correlation is available, and data from reservoir fluid analyses have been used7-9 for compositional material balance calculations.* From a theoretical point of view, this is entirely invalid. The reservoir fluid analysis, whether flash, differential, or other process, does not duplicate the compositions which occur during the actual reservoir depletion process, therefore the viscosities measured during reservoir fluid analysis are not those which occur in the reservoir. From a practical point of view, the "error" of using viscosities from reservoir fluid analysis is of varying and unknown significance. One can say qualitatively that the error is greatest where compositional effects are greatest, i.e., for volatile oil and gas condensate reservoirs and pressure maintenance operations. The first requirement to obtain a quantitative estimate of the significance of the error is to develop a reliable compositional correlation for the viscmities of reservoir oils. No such correlation has been available. Consistent with this requirement, the objective of this study was to develop a procedure to predict the viscosity of reservoir fluids from their compositions. Normally, the compositions of reservoir fluids are available expressed as mole fractions of hydrogen sulfide, nitrogen, carbon dioxide and the hydrocarbons methane through the heptane-plus fraction, with the average molecular weight and specific gravity of the latter. The final correlation was to use the composition in this form. While the more challenging objective of the study was the development of a correlation for the viscosities of reservoir oils, the viscosities of reservoir gases were also studied. The end result of the study was a procedure to calculate the viscosities of reservoir gases and liquids suitable

Jan 1, 1965

By D. I. Bardos, Paul A. Beck

A MARK, Boren, and westgrenl in their X-ray diffraction study of manganese alloys with 10 to 25 at. pct Si reported the occurrence of a phase with complex crystal structure in a Mn + 14.5 at. pct Si alloy after annealing at 800° or at 600°C. Recently Kuzma and Gladyshevskii2 identified Mn6Si as an R phase,3,4 the second binary R phase known. (A binary R phase was previously found in the Mn-Ti system by Waterstrat.5) A ternary R phase was reported earlier0 near the Mn-Si binary border of the Ti-Mn-Si system at 1000°C. In the light of the Russian work it now appears that this "ternary" R phase may be in fact an extension of the binary (Mn6Si)R phase. As already found by Amark, Boren, and Westgren, the corresponding binary phase is absent at 1000°C; the effect of titanium is evidently to stabilize it up to higher temperatures. In a recent paper Wieser and Forgeng7 gave the boundaries of this binary phase, which they referred to as 6. In order to re-examine the identity of this phase, an alloy of Mn + 14.5 at. pct Si was prepared by induction melting in helium atmosphere and annealed for 3 days at 800°C. The powder pattern, taken with an asymmetrical focusing camera of large dispersion and shown in Table I, was found to be that of the R phase, in agreement with the results of Kuzma and Gladyshevskii. For comparison, Table I also lists

Jan 1, 1965