By T. H. Alden

BaCKOFEN, Avery, and Turner have shown"2 that the large tensile elongation in superplastic metals is correlated with a high strain-rate sensitivity of the flow stress. At present, the reported superplastic materials are complex eutectic or eutectoid systems with a large solubility range in at least one of the terminal phases. This note describes the behavior of a solid-solution alloy (at 22°C)5,= Sn-1 wt pct Bi, which has been processed in order to produce a fine grain size.2,3,6 The chill-cast, 1/2-in.-diam ingot was homogenized for 1 week at 130°C, extruded at O°C to 0.083 in. diam, quenched within 15 sec, and stored at -196°C. Samples were warmed to room temperature 16 hr prior to mechanical testing or metallography. During tension testing at room temperature, it was found that the flow stress reached a steady-state value which depended on the imposed elongation rate and was independent of strain to an error of about ±5 pct. In Fig. 1 is plotted log a vs log e where a is the measured steady-state flow stress and i the imposed strain rate. These quantities were calculated using "instantaneous" area and length to an accuracy in the sample diameter of ±5 x 10-4 in. The log a-log 1 curve is sigmoidal. The strain-rate sensitivity, which may be given by d log old log 6,' has a maximum value of about 0.48 between i = 5 x 10-4 and 5 x 10-3 per min. The value is well above frequently measured values for metals at creep temperatures (0.1 to 0.3) and comparable to the rate sensitivity for Pb-Sn solder: which has been shown to be superplastic.2,3 Note, however, that below or above the strain rate of 10-3 per min the rate sensitivity of Sn-1 pct Bi decreases and at high rates is more nearly like that of conventional metals. The grain size of this material is relatively uniform, Fig. 2, and may be specified by an average linear intercept i.' Grain growth occurs at room temperature but after 16 hr, L = 5. Tensile elongation was measured on finer-grain-size specimens, which had been at room temperature 15 min prior to testing. After 15 min, the samples are fully recrystallized. Three strain rates, 5 x 10-3, 10-2, and 2.5 x 10-2 per min, were employed for which the measured elongations varied from 425 to 500 pct. These results would seem to justify the term superplastic, applied to this alloy, although the ductility is inferior to that of the Sn-Bi eutectic.3 The Sn-1 pct Bi alloy, which is a single-phase material with equiaxed, fine grains, is an excellent one on which to make an estimate of the Nabarro-Herring9 creep rate. According to the model of Avery and Backofen2 a substantial part of the deformation must be accomplished by N-H creep in the strain rate-temperature regime in which d log a/d log 1 = 0.5. The maximum N-H creep rate is given by9 L2kT where v is the atomic volume and D the self-diffusion coefficient. For this test v = 3.O x 10-23 cu cm, D = 1.4 e-23,300/RT = 2.5 x 10-l7 sq cm per sec,7 L = 5x 10+4 cm, T = 295°K, and a = 2000 lb per sq in. = 1.38 x 10' dyne per sq cm. The calculated creep rate is E= 4 x 10-11 per sec which may be compared with the measured creep rate at this stress, Fig. 1, of 6.7 x 10-5 per sec. The N-H creep rate is seen to be negligible. Earlier consideration2 of this question was in error because incorrect diffusion coefficients were used. The assistance of R. R. Russell in metallography is acknowledged gratefully.

Jan 1, 1967

THROUGHOUT the Colonial era, Philadelphia was easily the leading city of North America, and it still held that position at the end of the period, with a population of about 25,000, though closely pressed by Boston, which had slightly over 20,000, and New York, which had nearly as many. It was the center of a region in which mineral industry was important. Thomas Rutter's bloomery, built in the Schuylkill valley in 1716, was quickly followed by many others, and during the Colonial period at least 20 blast furnaces, 45 forges, and iron- works of other types were built in eastern Pennsylvania, which easily led all the other colonies in iron manufacture. During the Revolutionary period others were erected as far west as Fort Loudon, in the Cumberland c alley.6 After 1800 the rapid development of the anthracite mining industry profoundly affected Philadelphia's development, since transportation of the coal was then necessarily by water,, and the streams of the anthracite regions mostly flowed into either the Schuylkill or the Delaware Rivers. With an abundant near-by supply of coal and iron, with the seat of government, which had been there since 1774, and with a national Bank established there in 1791, one would have seemed safe in prophesying, at the beginning of the nineteenth century, that Philadelphia would permanently remain the leading city of the United States. Education in Philadelphia was at first wholly in the hands of the Quakers, who had established a "Public School" there in 1689, but in November 1739 George Whitefield, who had created a sensation in England by his preaching, though only 24 years old, passed through Philadelphia on his way to Georgia to found an orphan school there. He preached a series of sermons in Christ Church that were so disturbing to the established church that on Nov. 25 the Rev. Richard Peters (who was also Provincial

Jan 1, 1941

By E. Douglas, D. N. Collins, J. R. Stevens

E. Douglas (Dept. of Scientific and lndustrial Re-search, Warren Spring Laboratory, Hertfordshire, England) — The authors are to be congratulated on the considerable improvements they have made in tailoring efficiency and selectivity terms which are generally superior to the alternative forms in current use. However, I feel that their efficiency expression is limited to lower-grade feeds; its accuracy reduces as the feed grade increases. For example, its application to such processes as the beneficiation of glass sands, refractories and clays will invoIve considerable inaccuracies. The reason for this lies in the direct use of recovery, which, with high-grade feeds, biases their empirical expression, R(1 - c/h). With a 90% grade feed, the recovery weighting for the slightest degree of beneficiation, over a zero efficiency sampling operation, will be 90+%+ I disagree with their second basic requirement which states that there can be no fundamental basis for any single quantifying expression. A formula giving a comprehensive representation of concentra- tion efficiency can be derived fundamentally accord-to the procedure outlined in the literature. '' This formula, called the Basic Efficiency formula, is

Jan 1, 1963

By R. W. Winson

Asbestos is the generic name given to a group of fibrous mineral silicates found in nature. They are all incombustible and can be separated by mechanical means into fibers of various lengths and cross sections, but each differs in chemical composition from the others. The commercial grades of asbestos consist of a spectrum of lengths and sizes and are not definitive as are most organic fibers. It is generally recognized that there are two main groups of asbestos. The first only contains the fibrous serpentine called chrysotile and comprises about 94% of the world production of asbestos. The second group contains five minerals in the amphibole series+rocidolite, amosite, anthophyllite, tremolite, and actinolite. The latter two have no commercial importance. Properties Physical The structures of asbestos fibers have been studied intensively over a number of years. X-ray diffraction patterns have been used as a means of identification and classification. Low angle X-ray scattering techniques have shown that chrysotile fibers are "hexagonally close packed" and parallel to each other, having cross-sectional diameters varying from 18014 to 300A units, while the amphibole fibers are many times larger in cross section. Electron micrographs of the more common types of as- bestos are shown in [Figs. 1-4]. [Fig. 1] illustrates the softness and flexibility of chrysotile which make it suitable for textile-type products. For a number of years there was considerable controversy over the exact nature of chrysotile fiber, but the photographic evidence in [Figs. 5-7] clearly show that it is tubular in structure. The curvature is the result of the mismatch in the dimensions of the silica [Si,O,l and brucite [Mg(OH),] layers which are on the inside and outside, respectively, of a double sheet. This curvature had been predicted by Pauling (1930) years ago based on the molecular dimensions of the two component structures.

Jan 1, 1975

By Charles F. King

The only investigations on record of the reactions occurring (luring the Bessemer blow are of charges containing a large percentage of manganese, with the exception of' two partial analyses by Snelus and Barker of the English method, where a low percentage of manganese was used. They do not give the analysis of the spiegel, [lor do they report any graphitic carbon after the first stage of the process. Both report only traces of manganese after the first stage until the addition of spiegel. The slags corresponding to the samples of metal were not analyzed.

Jan 1, 1881

By Gerald Edmunds

In a paper1 before this Institute in 1940, the writer reported that the surface orientation texture of zinc and cadmium differed from the texture existing within the casting, in that basal planes were parallel to the surface. He was unable to rationalize the , origin of this surface texture. It is conceivable that the surface orientation texture is influenced by the atomic force fields, which are different at the surface and within the body of metal. It was considered that a radical changc in the surface against which the metal is cast might alter the surface texture. In trial of this, zinc has been cast against a surface of molten lead, but the same result has been obtained—i.e., (001) parallel, ± 2oo, to the surface—as was obtained when it was cast against air, Transite or iron.' Into the bottom of an open cast-iron tray, 7 by 14 in. by 2 in. deep, preheated to about 275°C., about 1/4 in. of lead, then 1/2 in. of zinc was poured, and the whole was covered with an electric heater to enforce freezing from the bottom upward. After a lapse of time sufficient for the zinc but not the lead to solidify, the zinc slab was raised free of the molten lead. The bottom surface of the zinc casting was coated with a thin layer of lead. A specimen of the slab 136 in. square was metallographically polished to flatten it and remove the slight film of lead, and the orientation was determined by the method used before,' with the result stated above. Some determinations have also been made on other metals, as follows: Surface orientation determinations were made on the 3/8-in. diameter grip section of two 1/4-in. diameter aluminum-alloy die-cast tensile bars and on a 1/8 by 1/2-in. flat aluminum-alloy die-cast tensile bar. None of these three aluminum die castings exhibited any preferred orientation at the surface. A brass die casting (nominal composition: 60 Cu, 37.75 Zn, 1.00 Sn, 1.00 Pb, 0.10 Al, 0.15 Si) furnished by C. S. Smith was also examined. The surface showed a random orientation of alpha and beta. Summary A zinc casting solidified against a molten lead surface was found to have the same surface orientation texture, (001) parallel to the surface, as other zinc and cadmium castings. Aluminum and alpha-beta brass die castings were found to have random grain orientation textures at the surface. Acknowledgment The X-ray determinations were conducted by M. L. Fuller.

Jan 1, 1945

By Richard O. Carlson

Ions of p31 and B 11 were implanted in natural insulating diamond macles. The thin (-0.4µ) layers showed sheet resistances of 107 to 1011 ohm per sq and activation energies of 0.17 to 0.34 ev above room temperature. However, no Hall effect could be measured, indicating that mobilities were less than I to 10 sq cm per (v-sec). Such low mobilities may be due to excessive scattering due to radiation damage in the bombarded layer or to very high concentrations of active compensating impurities. Annealing did not materially change the room -temperature properties, but the temperature was limited to -800°C by surface graphitization, the latter process probably being accelerated by lattice damage in our diamonds arising from the ion bombardment. A weak n-type thermoelectric power was detected after p31 irradiation, but it cannot be presumed that we have made the phosphorus ions active as donors in diamond. The natural diamonds have a high and uncontrolled concentration of impurities and, when coupled with the radiation damage and graphitization problems, would appear to seriously limit the quality of semiconductor that we can presently achieve by ion implantation in diamond. ALTHOUGH diamonds are usually thought of as insulating in terms of their electrical conductivity, it was found about 15 years ago that natural semiconducting diamonds do occur rarely, and these were designated as type IIb diamonds. These p-type semiconducting diamonds were found to be dominated by an impurity level 0.37 ev from the valence band. Evidence today based on correlation of the concentration of acceptor states from Hall effect measurements with the impurity concentrations determined by neutron activation analysis point to aluminum as the dominant acceptor impurity.' The compensating donor is believed to be nitrogen, which has a donor level 1.6 ev above the valence band.' However, only a small fraction of the total nitrogen content in the diamond is electrically active. An infrared absorption band at 7.8 p and ultraviolet absorption near 4 ev have been associated with nitrogen, the former providing a quantitative measure of nitrogen content.3 The nitrogen content is -l020 cm-3 in insulating or type I diamonds, but is less than 10'' in natural semiconducting diamonds. Much of this nitrogen is distributed in platelets oriented in (100) planes and not atomically dispersed in the diamond lattice.4 Semiconducting diamonds have been deliberately formed by incorporating impurities into the graphite charge in the high-pressure apparatus used to form diamonds.5 These manufactured semiconducting diamonds are always p-type, and while some show the 0.37 ev level due to aluminum, most such samples have been ascribed to impurity banding effects.6 The best natural or manufactured semiconducting diamonds have hole mobilities near 1500 sq cm per (v-sec) at room temperature, and those with the 0.37-ev level can be analyzed to reveal an acceptor concentration of 3 to 8 X 1016 cm-3 and a donor concentration 3 to 10 times lower.' NO bulk n-type diamonds have ever been reported, but the electron mobility has been measured as 1900 sq cm per (v-sec) by irradiating a diamond with ultraviolet to excite electrons out of the deep nitrogen donor level or other levels.7 New hope for the formation of n-type diamond has emerged from the ion-implantation method whereby desired impurities are introduced into a crystal lattice by bombardment with a high-energy beam of the impurity ion. It was found in the case of silicon that the usual donors such as phosphorus and arsenic and acceptors such as boron and gallium could be implanted into silicon. Wentorf and arrow' produced semiconducting layers on diamonds by an ionic bombardment in a glow discharge at potentials of about 2 kv. The observed typeness from thermoelectric probing seemed to depend on the atmosphere gas (nitrogen, argon, or hydrogen) rather than on the electrode material, but the nature of the conduction process in the thin damaged surface layer is completely unknown. A Russian group under Vavilov has attempted high-energy ion implantation in natural diamonds using boron and lithium ions9 and later also phosphorus, aluminum, and carbon ions.10 Their papers claim n-type layers from lithium, phosphorus, and carbon implant and a p-type layer from boron and aluminum implant, though the methods of type determination are not described in detail. Under government contract support, the Ion Physics Corp. has studied ion implantation in several semiconductors. While the bulk of their study1' was devoted to the irradiation of silicon, they did carry out a short study on boron and phosphorus implantation into natural diamonds. They did observe surface conducting layers but did not determine the typeness of the layers. For our experiments, phosphorus and boron were chosen as the dopant ions because of their respective donor and acceptor behavior in germanium and silicon. Moreover, they are the lightest mass dopants of the shallow level donors and acceptors from columns 111 and V of the Periodic Table (excluding nitrogen which is already present in diamond), and will have the largest depth penetration into the diamond lattice. EXPERIMENTAL Diamonds. As the target diamonds for our ion implantation study, we chose commercially available macles, which are flat, twinned diamond crystals. By scanning through the stock of a wholesale distributor

Jan 1, 1970

By A. S. Venkatadri, H. B. Bell

The equilibrium sulfur distribution between molten iron and Ca0-Mg0-Al203 slags containing iron oxide was investigated at 1550°C. The results were used to derive the iron oxide activities at low iron oxide concentrations in the slag by combining the sulfide capacity data obtained from gas-slag work with the free energies of both the sulfur solution in iron and the iron oxide formation in slag. The derived ferrous oxide activities were compared with values based on Tem-kin's kin's and Flood's ionic models. One difficulty in using these models is that the nature of the aluminate ion in slag is uncertain. Nevertheless, such indirect methods, in particular, those described in the present paper, are of value because of the difficulty of measuring small amounts of oxygen in liquid iron in equilibrium with slag. It is shown that these methods confirm the consistency of thermodynamics data on liquid iron and slags. It is well established that decreasing the iron oxide activity in the slag increases the desulfurization of molten iron at constant slag basicity. This effect is most pronounced at the very low iron oxide activities, characteristic of blast furnace slags. Yet a precise quantitative determination of the significance of low iron oxide contents in slag in blast furnace desulfuri-zation is not possible for the following reasons: a) difficulty of separation of iron "shots" from the slag, and b) errors in chemical analysis of small amounts of iron oxide in slags. In view of these obstacles, one must resort to indirect methods of calculating iron oxide activities. EXPERIMENTAL TECHNIQUE The apparatus for providing the sulfur equilibrium data has been described previously1 and was similar to that used by ell' in connection with the study of slag-metal manganese equilibrium. The procedure consisted of: a) melting about 50 g of Armco iron in a magnesia crucible in a platinum furnace, b) adding a mixture of about 15 g of lime-alumina slag and varying amounts of Fe2O3 and CaS, and c) maintaining the temperature at 1550°C for more than an hour in an atmosphere of argon to enable the sulfur equilibrium to be attained. Several melts were made using lime-alumina slags with basic composition 55, 50, and 45 pct lime. During the experiment the temperature was controlled manually using a Pt/10 pet Rh-Pt thermocouple. After the experiment, the Power was shut off and the flow rate of argon was increased to freeze the melt as quickly as possible. The analysis of sulfur in the metal was carried out by the oxygen combustion method3 using uniform drillings from the top and bottom of the metal button. After crushing and grinding and removal of any iron particles with the aid of a hand magnet, the slag was analyzed for sulfur by the CO2 combustion method.4 The E.D.T.A. method was employed for the analysis of lime5,6 and magnesia,= the ceric sulfate method7 for the analysis of slag iron oxide, and the perchloric acid dehydration method5 for the analysis of silica. The remaining amount was taken to be Al2O3 precipitation with ammonium hydroxide in several preliminary melts had confirmed the propriety of using this simple procedure. RESULTS The activity of iron oxide in binary, ternary, and more complex slags has been the object of numerous investigations, and the two experimental methods for its determination are: 1) Equilibrating the metal with the slag in question and measuring the oxygen content of the metal. The ferrous oxide activity is then given by aFeO L%OJSat where [%0]sat is the oxygen content of the metal in equilibrium with pure iron oxide slag. This method was used by Chipman et al.8,9 2) Equilibrating the slag in iron crucibles with known partial pressures of H2/H2O or CO/CO2 mix-tures.10-12 This method is limited to temperatures between 1265" and 1500°C. The very low oxygen content of the melts in this investigation made it impossible to derive the ferrous oxide activity by the first of these methods. Therefore, the iron oxide activities were computed by means of: Sulfide capacity data from the gas-slag work" Temkin's concept14 Flood's approach15 a FeO from Sulfide Capacity. The method of calculating the aFeO involves the sulfide capacity of the slag (c,), the sulfur distribution coefficient (Ls), the free energy of dissolution of sulfur in iron, and the free energy of formation of iron oxide in the slag. Bell and Kalyanram13 have investigated the sulfur absorption characteristics of lime-alumina slags containing magnesia by the Carter-Macfarlane method16 (based on comparing the sulfide capacity of the slag in question with that of a standard slag of unit lime activity) and have derived lime activity values. The relation between sulfide capacity and their lime activity a'CaO is given by: Cs= 3—: Xa'CaO at 1500°C

Jan 1, 1970

Data about production are practically non-existent before 1860. The Census of 1840 reported a small amount, and a number of small mines were opened in the forties, all of the coal being used locally, or hauled to consumers in wagons. Tonnages shown in Table 72 are estimated from those for which authority is given. Railroads reported coal tonnages carried in the state in 1878 and subsequent years for years ending June 30th;, it is not stated that the tonnage originated in the state. Considering this fact, and the considerable amounts used locally, the tonnages given in Table 72 are certainly not larger than the actual amounts produced.

Jan 1, 1942

By S. J. McCarroll

THE Three Kids mine, some six miles east of Henderson, Nev., is in a typical southwest desert area, with high dry summer heat and cool to cold winter seasons. The manganese deposit was located during World War I.1 During this period 15,000 to 20,000 tons of ore assaying up to 41 pct manganese were shipped. Interest in the deposit was not revived until the middle thirties, when experiments on the ore were initiated. Test work indicated possible recovery of only 70 pct by flotation, but in 1941 additional work was done at the Boulder City pilot plant of the U. S. Bureau of Mines and also by M. A. Hanna Co. As a result, the Manganese Ore Co. was formed and a plant utilizing the SO, process was constructed. Numerous operation difficulties ensued, and the plant was closed when the manganese situation in the country eased.

Jan 3, 1954

By W. A. J. M. Van Waterschoot Van Der Gracht

The commercial production of petroleum in Germany is confined to the North German plain, in the Hereynian foreland, and the intramontane Permian salt basin of Thuringia, south of the Hare Mountains. Petroleum is produced in the former only in connection with salt domes, upthrust through Tertiary and Mezozoic strata of great thickness. In the basin of Thuringia petroleum is found in a Permian dolomite underlying a salt formation. It is exclusively in the peripheric zone of a few of the salt plugs in the North German plains region that commercial oil has so far been developed, notably in the following fields, all in the general region northeast of the city of Hanover: (1) Hänigsen-Obershagen-Nienhagen, south of Celle; producing from horizons in the Upper Triassic, the Middle Jurassic and the Lower Cretaceous; (2) Oberg, south of Peine; producing from horizons in the Middle Jurassic and Lower Cretaceous; (3) Oelheim-Eddesse, north of Peine; producing from horizons in the Upper Triassic, Lower and Middle Jurassic; (4) Wietze, west of Celle, where the main producing horizon is in the Lower Cretaceous. In some of these oil fields production from surface seepages was mentioned as early as 1669 (Oberg). Commercial production of importance dates only from recent time.

Jan 1, 1932

By Freeman Bishop

More than a few discussions are taking place these days among management economists seeking a way out of the dilemma of lower productivity vs. higher labor costs. Most suggestions would be illegal under present antitrust laws. Otherwise interindustry cooperation could be used to divide up some of management's tasks. Or price structures might be tuned to the special machinery and skills of some plants. Both remedies would be under attack almost immediately. There is one other remedy that is getting lots of attention: some form of compromise between management and labor to phase out no longer needed work practices that unions insist shall be retained. Railroads are the national industry suffering the most from this disease, still known as "featherbedding," an epithet coined by the railroaders themselves.

Jan 1, 1971

By M. A. Steinberg, J. Wulff, R. Kamm

In a previous paper1 from this laboratory, the development of a lead grid method for exploring the distribution of strain and density within metal powder compacts was described. In that work thin lead foil with rectangular holes cut at regular intervals was inserted with the powder fill, the arrangement pressed and then radiographed to permit measurement of the deformation of the lead grid. Densities at each grid element obtained in this manner were plotted as a function of the die dimensions. From such plots it was found that the densest part of a compact pressed from one side (the top) is at the top outer region and the least dense at the bottom outer region of the specimen. The axial density maximum occurs more often nearer the bottom than at the top. As a result of such exploratory measurements, it appeared reasonable to conclude that variations in density could be attributed in the main to die wall friction. Thus compacts of large diameter appeared relatively uniform in density except where the die fill had been uneven. Finally it was found that lubrication of the finely finished die cavity contributed more to magnitude and uniformity of density within the compact than interparticle lubrication. Since publication of the above results, it was found that circular-hole grids could be more accurately made and, when deformed within the powder, more readily measured and analyzed. Much of the former work was repeated and new results which include the effect of lubrication, compact height, pressure, speed of pressing and vacuum pressing are reported in the present paper. Circular-hole Grids and Analyses OF Radiographs Commercial lead sheet 0.008 in. in thickness was used in all the work reported. The 0.0938-in. diam holes were punched in the sheet on 1/8-in. centers to an accuracy of 0.001 in. The finished grid used contained eight or more holes in a row and from I to 24 rows. The lead sheet was clamped between two pairs of brass strips bolted to a small milling machine table which was itself bolted to a bench in correct position near a vise which held the punch. Travel of the lead grid in two dimensions was controlled by two steel lead screws calibrated in 0.001-in. divisions. A stripper plate was used on the punch to avoid distortion of the lead foil. A high carbon-high chromium (chrocar) one-piece steel die was used throughout the work. The die cavity was 1.125 in. in diam and the clearance between plungers and die wall was 0.001 in. The die was also used for pressing from both ends with two long plungers. Finally, lapping of die and plungers gave a surface whose rms value On an Abbot profilometer was 5 micro-in. The die walls and plungers were, except where otherwise noted, lubricated with a stearic acid suspension in benzene. This was put on in multiple layers and allowed to dry before filling the die.

Jan 1, 1949

By Joseph Hyde Pratt, Douglas B. Sterrett

Monazite is one of the minerals which, for a long time, was considered somewhat rare in its occurrence, but, upon a commercial demand arising for it, prospectors and engineers soon located large deposits of it in the Carolinas arid Brazil, and the supply has always been able to meet the demand. During 1908 further sources of supply of monazite have been discovered and developed in Idaho. North and South Carolina, however, are the only States that have thus far put any monazite on the market. Monazite is essentially an anhydrous phosphate of the rare-earth metals,ceriunl, lanthanum, and didymium,(Ce,La,Di)PO,. There is nearly always present a varying but small percentage of thoria, Tho2, and silicic acid, SiO2,, which are very probably united in the form of a thorium silicate, ThSiO4. Some mona-zites contain but a fraction of a per cent. of thoria, while others have been recorded that showed the presence of from 18 to 32 per cent.; but the majority contain from 3 to 9 per cent. of this oxide. It is the presence of the thorium oxide that gives the monazite its commercial value. The analysis occasionally shows also the presence of other constituents, as the yttrium and erbium oxides, zirconia, alumina, magnesia, lime, iron oxides, manganese oxide, and titanium oxide. Monazite is light-yellow, honey-yellow, reddish-, brownish-, or greenish-yellop. in color, with a resinous to vitreous luster, and is translucent to subtransparent. It is brittle, with a con-choidal to uneven fracture, and is from 5 to 5.5 in hardness, and from 4.64 to 5.3 in specific gravity. It crystallizes in the monoclinic system, and some crystals have been observed that werc 6 in. in length. The more perfect crystals are,-however,

Jan 1, 1910

By Roy McLellan

THE slags derived from the smelting of lead and copper ores are composed essentially of silicates. The problems arising from the smelting of these ores consequently involve the study of silicate fusions. In the absence of specific knowledge concerning the compounds occurring in slags, it has been the practice of metallurgists to treat them in terms of their total chemical composition. Slags have been classified as monosilicates, bisilicates, sesquisilicates, and subsilicates according to the relative amounts of oxygen in the acid and basic radicles of the hypothetical salt produced. While this has been a useful guide to metallurgists in computing the furnace charges, it falls far short of a basis for the scientific investigation of slags. In order to understand the nature of a slag as a whole it is necessary to learn the physical and chemical properties of the mineral compounds which go to make up that slag. The efficiency with which an ore is smelted in a furnace depends primarily on the physical properties of the compounds formed during the operation. When the melting points and fields of stability of each of the mineral compounds in slags have been established, it will be possible to determine the properties of any given slag by examining the nature and amounts of its mineral constituents.

Jan 1, 1930

By G. W. Maynard

In this paper I desire to embody the results of some personal observations of the working of the Siemens direct process as I witnessed it for a part of three days at the works of the Siemens-Anderson Company, in Pittsburgh. This preliminary investigation was to have been followed up by one extending over a considerable period of time, and would have embraced analytical and physical tests. Circumstances over which I had no control, resulting in the temporay suspension of work, have postponed the presentation of a complete paper. If the opportunity is afforded me, I purpose doing this at a future meeting of the Institute. To those interested in the development of the process, reference is made to the papers of Dr. Siemens in the Journal of the Iron and Steel Institute for the years 1873 and 1877, and to the paper of our late lamented brother, Holley, in the 8th volume of the Transactions of our owu Institute. Dr. Siemens, in the introduction to his paper "On the Manufacture of Iron and Steel by Direct Process," read before the Iron and Steel Institute in september, 1877, says: " In mixing comparatively rich iron ore in powder with about 25 per cent. of its weight of pounded coal, and in exposing this mixture for some hours to the heat of a common stove or of a smith's fire, metallic iron is formed, which, on being heated to the welding-point on the same smith's hearth, may be forged into a horseshoe of excellent quality. The admixture with the ore of some fluxiug materials, such as lime or clay, will, in most cases, be of advantage to rid the iron of adherent slog." This is the keynote of the Siemens direct process. Dr. Siemens says further: " If we regard the production of wrought iron from an abstract point of view, we perceive that we have to accomplish two things, viz., the deoxidation of the ore, arid the fusion of the earthy matter mixed with it; and if we calculate the amount of carbon necessary to accomplish this end, weshall rind that in using, say, hematite ore, consisting of peroxide of iron with from 10 to 15 per cent. of silica, we shall require barely 40 per cent. of carbonsceous matter per ton of iron contained in the ore to effect its reduction, and also the fusion of the slag."

Jan 1, 1882

By Massimo Guarascio

Computer data processing and ore reserve evaluation techniques, mainly based on geostatistical methodologies, have been developed at Agip Mining Division with the assistance of the Department of Mining Engineering of the University of Rome. A number of computer programs are available when facing problems such as optimization of sampling patterns, minable reserve estimation, grade control of output, and so on. In the present paper, the aims and the criteria followed in developing these programs are discussed. Some recent examples of application are also cited.

Jan 1, 1977

By H. M. Chance

The iron-ore deposits of the Hartville district are located near the new town of Guernsey, about 100 miles north of Cheyenne. The writer has been familiar with them since 1887, having visited the district several times for different clients— his last examination having been made in November and December, 1897. The deposits extend in a general N.E.-S.W. direction from a point in Section 33, Range 65 W., Township 28 N., on the west side of Whalen cañon, through Sections 4, 5, 6, 7 and 8 of Township 27 N. in the same Range, and over into Sections 1 and 12 of Township 27 N., Range 66 W. General Characteristics. The ore is a remarkably pure red hematite, extremely low in phosphorus, and carrying a small percentage of silica, as shown by analyses given below, and similar in many respects

Jan 1, 1901

By P. E. Landolt

MILITARY necessities and economic scarcities, occasioned by the first and second World Wars, led to the search for substitute materials and new products to meet the demands of advancing technology accelerated by research development. Among others, lithium came to attention. Its chemistry had been studied for a long period, but its general use was quite restricted due to limited known sources of raw material. In World War I, Germany used lithium metallurgically for two principal purposes: 1-hardened lead alloy, B-Metal, for railway bearings as a substitute for lead-tin-antimony alloys; and 2-light strong aluminum alloys, Scleron, in which zinc was largely substituted for copper.

Jan 12, 1951

By C. F. Smart

SINCE their comparatively recent development, the alloys of cadmium with silver and copper or nickel, and of cadmium with nickel alone, have been used somewhat extensively as liners for connecting rod bearings and main bearings of internal-combustion engines. In applications where, owing to high hearing loads and elevated operating temperatures, the life of hearings made from tin-hale or lead-base alloys has been undesirably short, cadmium alloys have demonstrated considerable advantage. In applications where, because of deflection of the crankshaft or bearing supports, copper-lead bearing metals have resulted in scored shafts, cadmium alloys have been operated successfully. The somewhat serious drawback to these alloys in hearing service has been that they, in common with copper-lead and certain lead alloys, are susceptible to corrosion in the presence of lubricants containing organic acids. These acids may be fatty acids (such as oleic acid) derived from animal or vegetable oils that sometimes have been compounded with engine lubricants, or they may be compounds of an acid nature developed by the oxidation of some petroleum oils under operating conditions. The result of such acid attack on hearings is illustrated by the photograph, Fig. 1. The petroleum oils that are most readily oxidized to a corrosive condition, and the operating conditions under which such oxidation most readily occurs, are now rather well known among the technical organizations of both the petroleum and automotive industries. While means have been developed for inhibiting petroleum oils against such acid formation, the knowledge that this condition may be encountered has been a factor in restricting the wider use of cadmium alloys as engine bearings. It has appeared, therefore, that their value and use would be enhanced if they could be made corrosion-resistant to a degree compatible with the most severe operating requirements. Investigation, undertaken with this in view, indicated that the addition of fractional percentages of the metal indium to the cadmium bearing

Jan 1, 1938