By J. H. Swisher

Two recent papers in this journal1,2 contain experimental evidence for an anomaly in the concentration gradient for tracer diffusion. In both papers, the authors suggest that this anomaly is due to a Gibbs' absorption effect. Their hypothesis is that surface active tracer elements tend to remain in or near the surface adsorption layer, thereby altering the diffusion flux and concentration gradient. It is not clear how the anomaly can be explained in terms of an adsorption effect. Surface tension forces act parallel rather than perpendicular to a surface and therefore should affect only the rate of spreading of surface active agents tangentially across a surface. Frenkel3 has given a short treatment of surface tension as a driving force for surface diffusion. While the equilibrium concentration of a surface active agent at the surface of a solution is known to be higher than in the bulk, its chemical potential is necessarily the same. It is difficult to see how adsorption can result in an anomaly in the chemical potential gradient, which is the driving force for diffusion. A more detailed explanation by the authors of the adsorption mechanism is in order. A similar anomaly does not seem to arise where

Jan 1, 1970

By R. R. Vandervoort

The creep behavior of Nb(Cb), Ta, Mo, and W was determined under conditions of constant atomic dif-fzisivity, constant stress to elastic modulus ratio, and nearly equivalent grain size, and the steady-state creep rates obtained from these tests were correlated with calculated stacking fault energies for the metals. These results, in conjunction with similar data for several fccMetals,13 suggest that stacking fault energy may influence the creep strength ofbcc metals. The interrelationship between steady-state creep rate, subgrain size, and stacking fault energy was examined. It was found that the subgrain size for a given creep stress, increased as stacking fault energy increased, but that this relationship did not cormpletely account for the effect of stacking fault energy on creep rate. The crystallography and energetics of stacking fault formation in bcc metals has been discussed by a num-ber of authors,1-5 and impurity stabilized stacking faults on (112) planes have been observed in Nb,6,7 w,8,9 Fe,] and V" by transmission electron microscopy. However, a crucial question is whether or not stack-ing faults influence the mechanical strength of bcc metals. Potentially, stacking faults could increase strength by reducing the mobility of the partial dis-locations bounding the fault, by acting as barriers to slip dislocations, and by retarding the climb of dislo-cations during high-temperature deformation. The objective of this study was to seek a correlation be-tween creep strength and stacking fault energy for several bcc metals; namely, Nb, Ta, Mo, and W. The creep behavior of most polycrystalline metals and alloys at high temperatures and moderate stresses can be described by the following relation:11,12 im=Af(s) where i, = minimum creep rate, A = constant, j(s) = a function involving metallurgical structure, a = applied stress, E = average elastic modulus at the test tempera-ture, w = constant (equal to 5 for most pure metals), D = diffusion coefficient. One factor in the structure function F(s) which sig- R. R. VANDERVOORT, Member AlME is Research Metallurgist, Process and Materials Development Division, Chemistry Department, Lawrence Radiation Laboratory, University of California, Livermore, Calif. Manuscript submitted February 28, 1969. IMD nificantly affects the creep resistance of fcc metals is stacking fault energy, and creep rate has been shown to vary directly with stacking fault energy to the 3.5 power." In the latter investigation, four fcc metals of widely different stacking fault energies (Ag, Cu, Ni, and Al) were creep tested at a constant stress to modulus ratio of 1.21 x 10-4, at a constant diffusivity of 2.7 x 10-12 sq cm per sec, and at nearly equivalent grain sizes of about 0.7 mm. The creep data were then correlated with stacking fault energies. In the present study, a similar procedure was followed. All materials used in this work were consolidated by powder metallurgy techniques. Impurity contents in the as-received materials are listed in Table I. Chemical analyses showed that no measurable contamination of the test specimens occurred during pretest annealing treatments or creep testing. Specimens with a gage section 0.75 by 0.125 by 0.050 in. were creep tested in tension in a vacuum of less than 10-9 torr. Deformation at temperature was measured by tracking fiducial marks on the gage section of the specimen with an optical comparator. Optical deformation measurements also permitted observation of the macroscopic characteristics of the deformation Table I. Typical Specimen Impurity Content, ppm Nb Ta Mo W C 45 10 155 6 O 185 30 4 10 N 30 6 3 2 H 5 I 1 <1 als 3 10 2 15 Ca <5 I3 5 Cr 5 <3 10 <5 Cu 10 50 2 15 Fc 10 10 150 35 Ni 2 150 20 <5 Si <I0 1 3 <10 Ta 100 Ti 10 8 1 Zi 15 50 1 3 Table II. Test Conditions for Constant Stress-Modulus Ratio of 6 X 10.&apos; and Constant Diffusivity of 2.7 X 10-12 sq cm per see, and Grain Size Values for the Given Pretest Annealing Treatments Literature references Pretest Annealing for E and D Treatment Stress, Temperature, ___"&apos;Values__ Grain Tempera-Metal psi "C E D Size, mm ture, .C Time hr Nb 745 1525 14 15 to 17 0.83 1650 I Ta 1220 1770 18 19.20 O.91 1800 I Mo 1975 1630 18 21 0.77 2200 I W 2140 2265 18 22 040 2400 5

Jan 1, 1970

Preamble At the present time many bodies are engaged in -the formulation of standards. There is no uniformity in the rules for such procedure in the different organizations; in some cases the committees engaged in the work are not fully representative, and in. a considerable proportion of cases they do not consult all of the allied interests. The present custom results in a considerable duplication of work, and in some fields several "standards" are proposed for the same thing, differing from one another only slightly and often in unimportant details. It is very much more difficult to obtain agreement between the proposers of overlapping standards after they have been published than it would be to get the proposers to agree before they had committed themselves publicly. The American Institute of Electrical Engineers, the American Institute of Mining Engineers, the American Society of Civil Engineers, the American Society of Mechanical Engineers, and the American Society for Testing Materials have appointed a committee to consider the advisability of cooperating in engineering standardization. This committee recommends that these societies form a permanent organization by appointing a committee as proposed in the following constitution and rules of procedure to carry on this very important work.

Jan 3, 1918

Jan 1, 1935

By W. N. Tanner

THE wire-rope hoisting conditions at the mines of the Anaconda Copper Mining Co. in Butte, Mont., are very severe because of the conditions under which it is necessary to operate. A study was made, in the fall of 1919, for the purpose of changing these conditions in order to obtain longer rope and sheave life. There are at present in Butte, hoisting engines equipped with wire rope as follows: 9 main hoists using flat ropes. 7 main hoists using 1 ½ in. rope. 5 main hoists using 1 ¼ in. rope. 6 shafts using 1 1/8 in. rope. 2 chippy hoists using 1 ¼ in. rope. 9 chippy hoists using 1 1/8 in. rope. 15 shafts using 1 in. rope. 7 shafts using 7/8 in. rope. 1 shaft using ¾ in. rope. In addition, there are a number of sinking engines using 5/8 in., ¾ in., 7/8 in., and 1 in. (15.9, 19, 22, and 25 mm. rope.) The flat ropes run from ½ by 7 ½ in. (12.7 by 190.5 mm.) to ½ by 4 ½ in. (9.5 by 114 mm.) and are used on the older hoisting-engines, which are set comparatively close to the shaft. Because of swelling and moving ground at some of the shafts, these ropes present certain difficulties in operation that are more pronounced than with round ropes; they are, therefore, being superseded by round ropes as newer engines are being installed. They are, however, much more easily inspected and repaired than round ropes.

Jan 2, 1922

By G. Austin Schroter

ALTHOUGH there is now an extensive literature on the bleaching clays, not a great deal of material is to be found concerning the geological fea-tures of these deposits and their bearing on problems of exploration and development. At the same time, chemical and crystallographic research on the clay minerals during the past few years has laid a suitable founda-tion upon which to base conclusions of economic value drawn from field observations. All of the criteria and deductions herein presented are based upon extensive field work by the senior author, both in the United States and Canada, and when subjected to the ultimate tests of development and exploitation they have held up remarkably well, despite the fact that many of these conclusions apparently have not been reviewed in the litera-ture heretofore. The nomenclature of the bleaching clays is rather confusing in the light of present-day commercial standards and has even led to litigation." The old term "fuller&apos;s earth" is largely based upon trade usage and the definition of the term therefore is dependent upon the changing standards of commerce. For statistical purposes the Bureau of Mines81 classes as "fuller&apos;s earth" all natural bleaching or filtering claylike materials that possess high adsorptive capacity without previous chemical treat-ment or activation. Conversely, the so-called activated or acid activated clays are now generally recognized as any clay mineral or mixture of the clay minerals whose adsorptive capacity has been developed to commercial standards by chemical or physical treatment. Therefore, without attempting to propose any additions to the nomen-clature of bleaching clays, this paper will refer to naturally adsorptive clays and activable clays, respectively, for the two types indicated.

Jan 1, 1940

By W. D. Robertson, H. Conrad

Incremental loading creep tests were conducted on magnesium single crystals in tension and direct shear at 78" to 364°K. The creep curves were transient in character and exhibited waves or periodic behavior, especially at small strain rates. A sigmoidal curve was frequently observed following the first occurrence of creep. Repeating of segments of a master curve was observed at all temperatures indicating that identical conditions for flow existed after various stress and strain histories. A logarithmic time law with a independent of temperature whs observed at 78°and 203°K, while a parabolic (power) time law was approximated at 298" and 364°K. The departure from logarithmic creep was attributed. to recovery, which was observed at 298" and 364°K. The temperature independence of a represents a serious objection to the theory of low-temperature creep based on the intersection of dislocations. IN a previous paper1 it was found that the initial creep rate of magnesium single crystals, y, following the addition of a stress increment in the range of 78° to 364°K, was given by the expression ? = C exp - {?H/kT} exp {B(T- h ?)} [1] where B and C are constants, AH is an activation energy of 10,300 cal per mole, T is the applied stress, ? is the total strain at the time of the stress increment, and h is the strain-hardening coefficient. The present paper is concerned with certain other features of creep behavior observed during this investigation; namely, the form of the creep curves, time laws for creep, recovery, and microscopic and X-ray observations of the structural manifestations of the creep flow. To the authors&apos; knowledge the temperature range of the present investigation (0.08 Tm to 0.40 Tm) has not been covered previ-

Jan 1, 1959

Coal Division Industrial Minerals Division Minerals Beneficiation Division Mining, Geology and Geophysics Division OFFICERS AND COMMITTEES S D Michaelson, President J W Woomer, President-elect Elmer A Jones, Past President C E Lawall, Eastern Regional Vice-President G Donald Emigh, Central Regional Vice-President J D Forrester, Western Regional Vice-president R B Ladoo, Treasurer John Cameron Fox, Secretary

Jan 1, 1958

D. K. CRAMPTON, Chairman EDMUND M. WISE, Past-Chairman CYRIL S. SMITH, Vice-Chairman CARL E. SWARTZ, Vice-Chairman H. A. MALONEY, Treasurer Executive Committee 1942 1943 FRANCES H. CLARK ERIC R. JETTE W. L. FINK LOUIS W. KEMPF J. T. NORTON GEORGE SACHS 1944 WILLIAM C. ELLIS ALAN MORRIS KENT R. VAN HORN Finance JOHN L. CHRISTIE, Chairman J. R. FREEMAN, JR. H. M. ST. JOHN W. M. PEIRCE JEROME STRAUSS

Jan 1, 1941

Photographs of Officers

Jan 1, 1923

By Norman Weiss

The need for more efficient utilization of labor in the metal-mining industry has been the subject of several recent editorials in the mining press, and one attractive possibility for such improvement lies in the designing of future milling plants particularly with economy of manpower in mind. We are accustomed to think of mill design as the selection and coordinated arrangement of process equipment, but if labor is to be efficiently utilized it must be given early consideration in planning the new mill. There are three good reasons for economizing in labor: (I) to reduce costs, not only in the form of wages but also in housing, hospital, welfare, and other obligations that a company accepts when a new man is added to the payroll; (2) to prepare for recurrent periods of manpower shortage, during which a well-designed plant can manage to get along with skeleton crews; (3) because a milling plant that must depend upon an inordinately large labor force for its operation and maintenance is certain to be inefficient in other respects, for many of the shortcomings in design that make necessary the excessive use of labor are generally not corrected merely by having too many men. A simple example of this is a poorly designed ore-feeding system : if this is inadequate to the extent that one man must be constantly unclogging feed chutes, it may help the situation to put two men or three at this task instead of one, but the feed rate will still be inconstant. First of the factors that affect labor saving is the location of the mill. This is often determined by transportation costs alone, and as a result the mill may be placed close to the mine regardless of the nature of the terrain. The designer must then adapt his layout to the conditions, favorable or not. This happens often at small properties, where capital investment may seem more important than operating expense. In most instances, however, a mill site carefully selected for the advantages it gives the designer in laying out the plant is the most economical in the long run, even if it involves a slight increase in cost of ore haulage. Given some freedom of choice, the design engineer may be able to find just the piece of ground that provides the proper gradient for the needs of the flowsheet, permits installation of essential yards and trackage, and perhaps supplies an excellent site for a tailing dam. Further justification for having placed the mill not too close to the mine sometimes emerges only years later as an opportunity to treat ores from other properties. When it is known from the beginning that the new mill will serve a number of scattered mines, a free choice of mill site is naturally stimulated. The most important single factor in limiting the labor requirements of a mill is its materials-handling system for bring-

Jan 1, 1947

By Edwin Chance

DURING the past 10 years, the safe and efficient lighting of the coal mines of this country has received an ever-increasing amount of attention. Several States have passed laws attempting to regulate the type of lamp to be used and the nature of the fuel to be burned, and the mining departments of coal-mining States have generally shown a keen and intelligent interest in this subject. The passage of the recent Employers&apos; Liability Act in Pennsylvania has made it necessary for many coal-mining companies to take out liability insurance, and the companies underwriting such insurance have made it desirable for the insured to permit the use of, none but illuminants of established worth. While these conditions have not obtained for a sufficient length of time to permit the statement that the illumination of coal mines by portable lamps has been standardized, still, considerable progress has been made and the direction of future practice in this branch of coal-mining technology is very evident. Under these conditions it seemed that a review of the methods now used in coal-mine illumination, together, with a brief consideration of the principles underlying these methods, might be of some interest. Miners&apos; lamps may be divided into three classes: The open light, the electric cap lamp and the flame safety lamp. It will be desirable to consider each of these classes separately, as each has properties peculiar to itself and one class is hardly comparable with another. In this country, without question, the open light is the most generally used of all miners&apos; lamps. This fact is explained by the relative freedom of a large proportion of our mines from gaseous conditions, and by the admirable systems of ventilation installed in those that show a tendency toward such conditions. In the metal relines, the miner&apos;s candle has had and still has considerable vogue. Because of the small amount of ventilation usually supplied in metal mines, the freedom of the candle from any tendency to produce noxious gases or offensive odors, and the small amount of air it consumes, are. valuable assets, while, because

Jan 2, 1917

By M. E. Wadsworth, J. R. Lewis, J. M. Quets

Samples of snythetic magnetite were reduced in hydrogen at various partial pressures and temperatures. The reaction mas found to be surface controlled and directly proportional to hydrogen partial pressure over the temperature range studied (400° to 1000°C). A transition in the mechanism occurred at approxirnately 590°C. This has been attributed to a change in the slow step of the reduction reaction resulting from the presence of stable wüstite at higher temperatures. Below 590°C the heat of activation for the reduction was found to be 14,700 cal per mole and it was 3,200 cal per mole above 590°C. THE reduction of the oxides of iron has been a subject of study and interest for many years. Edstrom1 has reviewed the work up to 1953 and his findings provide much basic information concerning details of the reduction of hematite (Fe2O3 ) and magnetite (Fe3O4) with both H2 and CO. He concluded that below 600°C the reduction of both hematite and magnetite was essentially identical, since the rate was controlled by a surface reaction at a magnetite gas interface and the iron formed was very porous. The decrease in the reduction rate for both hematite and magnetite immediately above 600°C was attributed to the formation of a stable wüstite phase across which diffusion was very slow. The wide difference in reduction kinetics for hematite and magnetite above 600°C was explained in terms of the character of the wüstite formed. The rate of magnetite reduction increased slowly with temperature beyond the minimum immediately above 600°C and rates equivalent to those observed at 550°C were not obtained until the temperature was increased beyond 850oC. Edstrom and Bitsianes2 studied the solid-state reduction of magnetite, the reaction of which can be written (4x-3)Fe + Fe3O4—4 FexO [1] where x is between 0.83 and 0.95. The rate was found to be controlled by the kinetics of transport of iron ions through the wüstite phase. Bogdandy and Riecke3 studied the kinetics of reduction of small grains of iron oxide in hydrogen and qualitatively attributed the slow step in the reduction process to the diffusion of hydrogen and water vapor through pores. McKewan4 has analysed the data of Joseph,5 Stalhane and Malmburg,6 and Lewis7 and has demonstrated that the kinetics of reduction of both hematite and magnetite are controlled by surface reactions and also that the variation in surface area during reduction must be accounted for. McKewan was able to correlate the reduction data by the equation rodo[1-(1-R)1/3] = Kt [2] where ro is the initial particle radius, do is the density of the iron oxide, R is the fraction reduced at time t, and K is a rate constant. The applicability of Eq. [2] for temperatures above 600°C where a stable wüstite phase is present, indicates the slow step in the over-all kinetics does not result from diffusion unless diffusion occurs laterally along the oxide metal interface or through a wüstite layer of constant thickness. Diffusional control through a layer of wüstite is unlikely, however, in view of the pressure effects demonstrated by Tenenbaum and Joseph,&apos; Diepschlag,9 McKewan,10 and the results of the present study. McKewan has demonstrated a linear rate dependence on the hydrogen partial pressure over the temperature range 400" to 1050°C for the reduction of hematite.

Jan 1, 1961

By Robert M. Cox

A roof bolting theory and structural model are presented which explain the success of most roof bolting installations as the creation of a competent roof bolt reinforced rock arch within the immediate roof rock overlying an underground opening. Likewise, the failure of some bolted mine roofs can be explained as a failure to create a structually competent rock arch by roof bolting.

Jan 1, 1975

By M. K. Yen, W. R. Hibbard

Previous studies of plastic deformation of metals have emphasized the important role of bending and constraints during strain under relatively pure stresses.1"5 Some new phenomena such as early conjugate slip6 and polygonization7 are intimately concerned with the relief of bending stresses, the former by slip and the latter by a process analogous to re-crystallization. However, few analyses of the bending deformation of single crystals were found in the literature, and those8,9 are sufficiently previous to the modern interpretations of slip to invite further investigation in this area. The transverse bending mode of testing, using the two-point loading method, was selected because the center portion of the specimen may be considered as under a theoretically pure bending stress with a uniform bending moment. Considerable attention was given to both the lattice distortion and flow characteristics of the crystals during deformation. Experimental Proeedare A specimen under the action of equal and opposite couples at both ends is said to undergo pure bending. The shear and moment diagrams of a specimen under the two-point loading method of transverse bending are shown in Fig 1. The moment over the middle-third of the span is equal to PL/6, and the vertical shear is zero. Fig 2 (A) illustrates the stress distribution in the elastic range on a plane across the middle of the specimen. It can be seen that the normal stress has a maximum value at the extreme surfaces on the tension and compression sides, and decreases proportionately to zero as it approaches the neutral plane. However, when the plastic range is reached, the stress distribution is no longer a straight line relation, but changes in a manner which can be best illustrated as shown in Fig 2(B). The following calculation and stress analysis are mainly in accordance with the works reported by Timoshenkol0 and Kochendörfer.9 From the simple beam formula, the maximum normal stress will occur at the surface of the specimen. For a round specimen with a radius r and for a rectangular specimen with a height 2h and width 2b, the maximum normal stress, Sp, will be given by the following formulas: For round specimen: 2PL Sp = 3pr3 [1] For rectangular specimen: Sn = 8bh2 [2] Since it is reasonable to consider that slip takes place under the same conditions as in uniaxial loading, the resolved shear stress S?, along the operative slip direction will be as follows: For round specimen: 2PL sin x cos ? Sp = 3pr3 sin x cos ? [3] For rectangular specimen: PL S8 = 8bh2 sin x cos ? [4] where X is the angle between the specimen axis and the slip direction and X, the angle between the specimen axis and the major axis of the glide ellipse. It was also reported by Kochenclorfer9 that the critical bending moment, that is, the bending moment exerted on the specimen to initiate slip, should be higher than the value given by the equations stated above. Based

Jan 1, 1950

By C. G. Bieber, R. F. Decker

The effects of minor constituents on the malleability of nickel alloys are described. These effects are related to the atomic diameter, valence, and position on the Periodic Table. The basic methods for removal or neutralization of deleterious elements are then reviewed. Finally, practical methods for melting nickel alloys are described in detail and related to minor constituent control. L HE first malleable nickel was produced by Fleit-man in about 1870 by the addition of manganese and magnesium to the molten metal to counteract the harmful effects of sulfur. Merica and Waltenbergl explained the mechanism by which these elements accomplished the desired result. They showed that sulfur in concentrations in excess of about 0.005 pct produced films of a brittle low melting eutectic of nickel-nickel sulfide which completely surrounded the grains. When manganese was added to molten nickel it reacted with the sulfur to form manganese sulfide which precipitated as widely scattered globules in the grain boundaries. The further addition of small amounts of magnesium converted the sulfur to a very stable sulfide of magnesium which was relatively insoluble in both the liauid and solid states and therefore occurred as finely divided particles within the grains where it had relatively little detrimental effect upon the malleability of nickel or its alloys. The practice of treating nickel with manganese and magnesium came to be called "deoxidation" and was employed without appreciable modification for the commercial production of wrought nickel and high nickel alloys (in this paper—50 pct or more nickel) until about 1930 even though the results were never entirely satisfactory. At that time a more extensive study was made of the effects of minor constituents on malleability and metallurgical quality. The results, small portions of which have been published,2-4 are presented here with other pertinent data. EFFECTS OF MINOR CONSTITUENTS UPON NICKEL Systematic additions were made of 0.5 pct or less of each of most of the elements of the periodic ta- ble. It was established in this study that some minor constituents other than manganese and magnesium were extremely influential. The malleability, as evaluated by the reduction of area in tension tests, depended roughly on temperature as shown in Fig. 1. Four temperature zones are of interest; the cold malleable zone (up to about 1000° F), the red short zone from roughly 1000° to 1500&apos; F, the hot malleable zone around 2000° F and the incipient melting zone. Most of the malleability problems are associated with the red short zone and the discussion will concern this mainly. The reduction of area in normal tensile tests on high-purity nickel (see curve A of Fig. 1) appeared to have no

Jan 1, 1962

By Frank Hall

THE needs of the World War showed the necessity of a metal stronger than cast iron which would supplement the supply of steel. So patriotic metallurgists were spurred to new efforts to improve the status of that half-breed of the metal world that had been, more or less erroneously, christened semisteel. As a result, it was developed that for certain purposes semisteel was superior to steel in the manufacture of shells. Steel, because of its greater strength and toughness, is able to carry a greater charge of explosive, weight for weight; consequently, a steel shell can be expected to cause greater destruction when used against fortifications or other inanimate objects, while semisteel, because of its comparative brittleness and its resulting greater fragmentation, is capable of inflicting more serious loss of life when used against opposing forces of men. Therefore, each has its proper place in the economy of war. For the present purpose, steel may be defined as a comparatively pure iron whose physical nature is modified by small amounts of carbon, silicon, sulfur, phosphorus, manganese, and possibly other rarer elements; while cast iron generally is limited to approximately 93 per cent. of iron, the remainder consisting of larger percentages of carbon, silicon, sulfur, phosphorus, and manganese. Semisteel may be defined as cast iron in which the carbon and silicon have been reduced to as low a point as is consistent with maintaining the nature of gray iron, and in which the remaining elements are manipulated so as to give the greatest strength.

Jan 1, 1920

By H. E. Rorschach

Oil-field activities in Oklahoma made 1936 the best year since 1930. Approximately 2800 wells were completed, an increase of about 20 per cent over 1935. Purchasers&apos; reports filed with the Corporation Commission showed a total of 200,240,252 bbl. of oil purchased from leases in 1936. The assembly of a complete table of the oil fields of the state was not achieved, as many of the early records of operators and pipe-line companies are not complete, and data for the older fields will perhaps never be fully tabulated. Table 1 includes all of the new fields and most of the important fields of the State of Oklahoma. The outstanding developments of the year were: the discovery of rich Wilcox-sand production in the Moore pool; the spectacular drilling campaign in the Capitol or Mansion extension in the Oklahoma City pool; the surprising extension of the Olympic pool and the Hunton lime zone in the Fitts pool; and the failure to find more Ordovician production in southern Oklahoma. Wildcat discoveries, which were on a par with 1935, resulted in the discovery of such promising pools as Billings-Wilcox, North Bethel, North Earlsboro and North Lucien. The Fitts-Upper Simpson, Edmond, Jesse, Keokuk Falls and South Burbank pools underwent considerable development. Fitts Pool.—The Fitts area in Pontotoc County was greatly extended during the year and was the leader in drilling activity in the state. The producing limits were pushed to the east and north and the development of the Hunton lime horizon was outstanding. In the Upper Simpson zone 162 wells were completed; 137 in the Hunton lime zone and 26 in the Wilcox zone. The Oil Creek zone, a sand body below the Wilcox member, was discovered by the Magnolia-Statler No. 3 well located in the 1/4. 1/4 of sec. 28-2N.-7E. Moore Pool.—The Moore pool, in Cleveland County, which was opened in 1935 by the Sinclair Prairie-Franklin Community No. 1 well, surprised the oil industry when the Sinclair Prairie-Marvel No. 1 well, on Apr. 1, 1936, discovered a rich body of Wilcox sand below the distillate

Jan 1, 1937

By P. R. Sheorey

Understanding of in situ rock mass behaviour has taken a step forward with the advent of the refined rock mass classifications of Wickham, Bieniawski and Barton et al. In this paper six case studies are given in brief showing how Barton&apos;s classification could be used in mining situations. The cases cover stability of roadway junctions under shallow covers, support pressure estimation in roadways in intact and failed rock conditions, determination of the safe unsupported span of a wide stope and estimating the stability of roadways in two contiguous seams standing 011 small pillars against puncture of the parting rock.

Jan 1, 1983

By J. M. Campbell, T. S. Buxton

The most widely used methods of predicting the volumetric properties of gas are based on the principle of corresponding states, which asserts that the compressibility factor is a universal function of reduced temperature and pressure. Previous studies have shown that the acentric factor, as proposed by Pitzer, l is an important addition to reduced pressure and reduced temperature as factors affecting the compressibility factor. Results of this study indicate that, if the pseudocritical temperature and pressure used to determine the reduced conditions are adequately predicted, characterization of natural gas-carbon dioxide mixtures with the acentric factor will allow reliable determination of the compressibility factor. Comparisons of predicted and experimental compressibility factors have shown that the pseudo-critical constant rules of Stewart, Burkhardt and Voo 2 are satisfactory for hydrocarbon mixtures. However, these rules fail to predict the pseduo-critical constants for hydrocarbon-carbon dioxide mixtures. Based on graphically determined pseudocritical temperatures for binary hydrocarbon-carbon dioxide mixtures, a correlation which gives the required correction to the Stewart, Burkhardt and Voo rules was prepared and a compressibility factor prediction technique was proposed. To test the proposed technique, compressibility factors for live mixtures of methane, carbon dioxide and either ethne or propane were experimentally determined at 100, 130 and 160F and pressures up to 7,026 psia. The predicted and experimental compressibility factors for these live mixtures had an average absolute deviation of 0.55 percent. INTRODUCTION Two-parameter generalized correlations based on the principle of corresponding states (PCS) are presently available for reliably predicting the compressibility factor of lean natural gas, i.e., natural gas with low concentrations of hydrocarbons heavier than methane. When these same correlations are used for mixtures of natural gas and carbon dioxide, large deviations between actual and predicted compressibility factors are observed. This study was undertaken to provide a means for accurately predicting the compressibility factor for such mixtures. In the past, two avenues of approach have been employed to extend the applicability of the PCS. The first has been to introduce additional parameters. The second has been to develop combination rules for predicting pseudocritical constants which do not suffer from the limitations of the commonly used molal average constants. In this study, both of these approaches have been considered and employed to arrive at a method for predicting the compressibility factor of mixtures of hydrocarbons and carbon dioxide. SELECTION OF A THIRD PARAMETER Failure of the original PCS to predict the compressibility factor for all pure gases, regardless of their mass, shape or polar moment, has led to the introduction of additional parameters into the PCS. Parameters have been introduced to correct for quantum deviations,3-5 non-spherical or globular shapes6-9 and for polar moments.8-12 In addition to these parameters which are based on some microscopic property and intended to correct for some specific cause of deviation, more general parameters based on some bulk property have also been introduced.1913-16 To use additional parameters to correct for each of the possible causes of deviation among the individual constituents of a gas mixture would require a rather complex form of the PCS. To maintain the PCS in as simple a form as possible, it is more desirable to have a single third parameter which is based on some bulk property influenced by several of the factors causing deviations. The third parameter selected for use in this study is a factor originally proposed by Pitzer.9