By G. L. F. Powell

g samples of Cu-20 wt pct Ag alloy have been mdercooled to a maximum of 197°C by melting under a slag of commercial soda-lime glass in a vitreous silica crucible. No grain refinement of the primary copper was observed in samples undercooled to the maximum of 197°C. When the samples contained a small amount of oxygen, the copper dendrites were partially recrystallized at undercoolings greater than 97°C. In previous papers'-3 reporting the grain structure of undercooled silver and copper, it was observed that grain refinement was dependent on both undercooling and oxygen content. Grain refinement occurred in undercooled silver when the degree of undercooling exceeded the range 153" to 175"C, while in Ag-0 alloys (0.12 wt pct) fine equiaxed grains were exhibited when undercooling was greater than 50°C. Similarly, copper samples undercooled as much as 208°C displayed fan-shaped growth from a single nucleation site, while the grain structure of Cu-O alloys (0.08 wt pct) was fine and equiaxed at undercoolings larger than 150°C. Thus the presence of oxygen greatly reduced the undercooling at which grain refinement occurred. It was also observed that the change in grain size resulted from recrystallization and was not due to an enhanced nucleation rate in the liquid-solid transformation. It is possible that the influence of oxygen on recrystallization is due primarily to its presence as a solute element. walker4,' reported that, although a grain size change did not occur in pure nickel until the undercooling exceeded 150°C, small grains were observed in samples of Ni-Cu alloy solidified at small and large degrees of undercooling. Jackson et al.6 suggested that the fine grained structure of the Ni-Cu alloy resulted from the melting off of dendrite arms during recalescence. This remelting process may occur in alloys as a result of segregation during freezing which causes a variation in liquidus temperature from point to point within a dendrite. It was therefore decided to undercool copper with a metallic alloying element to ascertain whether the presence of a metallic solute would have a similar effect to oxygen in inducing grain refinement. A Cu-Ag alloy was chosen, since both metals had been shown to behave similarly on undercooling. The alloy Cu-20 wt pct Ag was selected since the eutectic constituent outlines the initial growth form of the primary copper, so that the as-frozen grain structure is not obscured if subsequent recrystallization occurs. This paper describes the results of undercooling experiments carried out with Cu-20 pct Ag samples undercooled to a maximum of 197°C and the effect of oxygen content on the grain structure of the undercooled samples. EXPERIMENTAL Melting was carried out in a small cylindrical resistance furnace using "fine" silver granulate and oxygen-free high conductivity copper. The procedure adopted was to melt the required quantity of silver in air in a clean vitreous silica crucible for approximately 15 min, freeze, and add granulated commercial soda-lime glass to form a complete surface slag cover, after which the sample was melted and frozen several times to reduce the oxygen content. The glass slag cover was approximately 3 in. thick. Pieces of copper (=50 g) were added to the crucible until the required quantity to make 350-g samples of alloy had been charged. Each piece was added quickly to the crucible which was held at a temperature slightly above the melting point of silver. The piece was quickly pushed beneath the glass to minimize oxidation and any oxide coating usually decomposed before the piece had settled down into the silver. After the full quantity of copper had been added, the melt was stirred with a silica rod to hasten homogenization and a Pt/Pt 13 pct Rh thermocouple enclosed in a vitreous silica sheath inserted for temperature measurement. Heating and cooling curves were recorded on a potentiometric chart recorder fitted with a zero suppression unit. The milli-voltage range of the recorder was adjusted so that temperatures could be read to 1°C. Heating and cooling curves were taken every hour until three consecutive readings gave the same solidus-liquidus range, consistent with the solidus-liquidus range for this alloy composition by reference to Hansen and Anderko.7 Metallographic examination of samples frozen at this stage, failed to show any variation in composition from bottom to top of the ingot. Consequently, it was considered that the melt was homogeneous at this stage and undercooling experiments were then car-

Jan 1, 1970

By P. Shahinian, R. L. Stegman, M. R. Achter

Creep strength has been determined as a function of oxygen pressure for nickel at 510" and 600°C. Creep-rupture life drops from its highest value at the ultimate vacuum of 10-7 torr to a high pressure plateau of nearly constant life which, at 600°C, commences at torr. This behavior is described in terms of a model that relates surface gas adsorption and the generation of fresh crack surfaces. In a calculation based a this model the predicted pressure beyond which the creep strength should not decrease further has been found to agree well with the observed value. The introduction of oxygen during creep in vacuum was found to cause a prompt rise of the creep rate. The magnitude of the environmental effect was much less than generally observed in fatigue and this is attributed to the diffarent crack morphologies in creep and fatigue. GASEOUS environments are known to affect creep resistance adversely1-5 but the effects have received less attention than the much larger ones in fatigue. At low temperatures it has been shown for nickel that the creep rates are faster and the rupture lives are shorter in air than in vacuum and that these environmental effects can be correlated with faster crack growth rates in the reactive environment.' In support of a mechanism of gas adsorption at the crack tip to explain the above effects, a calculation based on kinetic gas theory showed that surface coverage by gas was not as rapid as the exposure of fresh metal at the crack tip in the ultimate vacuum but was in air.7 In fatigue a number of investigations have demonstrated that the reduction of life with gas pressure usually follows a step curve with most of the reduction occurring in a transition range at intermediate pressures and little or no change at high and low pressure.8 There have been no studies, however, in which creep strength has been determined as a function of reactive gas pressure to see whether similar effects would be found. This investigation was undertaken to study the kinetics of the environmental effect in the creep of nickel. EXPERIMENTAL PROCEDURES The environmental creep apparatus was constructed to minimize many of the experimental conditions which can cause scatter in data. Dead weight loading is employed and weights are contained within the environmental chamber to eliminate bellows and the necessity for compensation for gas pressure changes. Elongation over the specimen gage length is recorded from a Riehle Model DV Controlled Environment Extensometer which provides readout to 2.5 x 10- in. Temperature is monitored and controlled from a thermocouple at- tached to the specimen gage length to +0.5oC or better. The freon trapped oil diffusion pump vacuum system included an auxiliary liquid nitrogen trap and, with a wide range variable conductance leak valve, pressures from the ultimate vacuum of 10"7 to l03 torr of any desired gas are obtainable. Pressure is measured by means of a hot filament ionization gage below 10"3 torr and a NRC Model 530 Alphatron Vacuum Gauge above 10-3 torr. The oxygen, which was leaked into the environmental chamber, was an Aviator's Grade of 99.5 pct purity with a dew point of -80°F. Analysis of the nominal 99.8 pct Ni showed the following percentages of major impurities: 0.02 C, 4.01 Mn, 0.005 Si, 0.01 Cu, 0.02 Fe, and 0.034 Mg. Cylindrical specimens were machined with a 0.180

Jan 1, 1970

By M. J. Mullikin, J. B. Conway

Several different equation forms were studied to determine the extent to which each particular equation type yielded an accurate representation of a given set of first-stage creep data. Specially developed least-squares computer programs were employed to obtain unique solutions for the creep-equation constants. In studies of creep data for lead at 14.5"C, nickel at 70OCC, and arc-cast tungsten at 2400°C consistently good representations were afforded by a third-degvee polynomial in t113. Other effective correlations were obtained with the Andrade, Cottrell-Aytekin, and de Lacombe equations along with a third-degree polynomial in t112. A newly proposed creep equation involving a hyperbolic-sine term in t1'3 was also found to yield very satisfactory results. This appears to be the first use of such a functional relationship in the analysis of transient creep behavior. In general, the deformation behavior of a material subjected to a tensile load is described in a strain-time plot. Experiments have shown that, following the instantaneous elongation which results on loading, the instantaneous slope (i.e., creep rate) of the strain-time curve decreases gradually with time and approaches what appears to be a constant value. Equations, therefore, which are proposed to provide an analytical representation of such first-stage or transient creep behavior must be consistent with these observations. In other words, at time zero, these equations must yield a finite deformation value corresponding to the elongation on loading. Furthermore, the first derivative of these equations must exhibit a fairly high although finite value at time zero, and then values which decrease with time. It is also preferable, in general, that the derivative eventually assume a constant value at high time values. Although many studies of first-stage creep behavior have been made and numerous equation forms have been proposed for expressing this type of deformation behavior, it is still not possible to state with any assurance which functional relationship will be adequate for a given set of measurements. Parabolic relationships have been employed most extensively although logarithmic expressions have been shown to be applicable in some instances. Combined forms1 have been studied in considerable detail and have on occasion been found to be very effective. One such expression is that of iXndradea and involves a modified parabolic expression: where 1 is the instantaneous length, lo is the length immediately following load application, t is the time, and p and k are constants. Another combined form has been proposed by weaver3 as follows: where E is the instantaneous strain, is is the linear creep rate, t is the time, and a and b are constants.

Jan 1, 1967

By Raymond L. Orr

Calorimetric measurements have been made of the heats of solution of gold axd indium in a number of liquid tin-rich alloys at a temperature of 705°K. Relative partial molar enthalpies of gold were determined as a function of dilute solute concentrations in the binary Au-Sn system and in the ternary Ag-Au-Sn and Au-In-Sn systems. Relative partial molar enthalpies of indium were determined for dilute solute concentrations in the In-Sn, Ag-In-Sn, and Au-In-Sn systems. Through application of the interaction coefficient concept introduced by Wagner and more recently extended by Lupis and Elliott, ualues have been obtained for the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. The results are inte@reted in terms of solute atom distributions through comparisons with the predictions of dilute solution models. INTEREST in the thermodynamic behavior of dilute liquid alloys stems from two primary sources. From a practical viewpoint, it is often of importance to know or to be able to predict the effect that one solute will have on the thermodynamic properties of the other solutes in a multicomponent system. Studies of dilute solutions may also be rewarding from the theoretical point of view. Some of the difficulties arising from the more complex interactions possible in concentrated solutions are avoided, leading to easier interpretations in terms of solutibn models and bonding energies. For example, in a binary alloy the limiting values of the partial molar properties of the solute represent the case for which each solute atom is completely surrounded by atoms of the solvent, and no other interactions are possible. Solute - solute interactions in dilute solutions are conveniently treated by the interaction coefficient concept of ~agner.' Using a Taylor series expansion for the logarithm of the activity coefficient, In yi, of a component, i, in a solution consisting of dilute solutes with atomic fractions xi, xj, xk, and so forth, in a solvent, s, and neglecting the second- and higher-order terms, Wagner obtained the expression: Where Wheyz is the limiting value of yi in the pure solvent, s. The interaction coefficients, e:, e:, and so forth, are defined by: Since yi is related to the excess partial molar Gibbs energy of component i by GfS = RT In yi, E: is re- ferred to as the "Gibbs energy interaction coefficient". Lupis and Elliott~ extended Wagner's treatment to the relative partial molar enthalpy, aHi, and the excess partial molar entropy, qS. They defined the enthalpy interaction coefficient as: and the excess entropy interaction coefficient as: leading to expressions similar to Eq. [I]: The three interaction coefficients are related by? The self-interaction coefficients, E:,qf,and at, represent the effects of interactions between atoms of component i in solvent s; €3, q{, and 03 represent the effects of interactions between i and j atoms in solvent s; and so forth. From the Maxwell-type relationships between partial molar quantities, it may be shown1'2 that e{ = ej, r}\ =tj), and ai - crj. Experimental determination of the interaction coefficients requires extremely precise measurements of the appropriate properties as functions of solute concentrations in very dilute regions. Few such data exist for intermetallic alloys, even for binary systems, because of experimental difficulties. This is especially true with respect to enthalpy data for dilute alloys. Examination of the compilation of data for binary alloys by Hultgren, Orr, Anderson, and ~elle~~ reveals that determination of limiting values of &fii(Xi =0) often requires extrapolations to infinite dilution from xi = 0.05 to 0.10. Direct measurements of the enthalpy interaction coefficient, qi, for multicomponent systems are virtually nonexistent. This quantity is of course subject to direct calorimetric measurement, but its determination must be limited to cases where high experimental precision is possible. The heats of solution of gold and indium in liquid tin can be measured with relatively high precision, which makes determinations of 73 involving these metals as the measured solutes experimentally attractive. This paper presents the results of such determinations of the Au-Au, Ag-Au, Au-In, and Ag-In enthalpy interaction coefficients in liquid tin. MODELS FOR DILUTE-SOLUTION BEHAVIOR Random-Solution Behavior. In the quasi-chemical treatment of solutions, only nearest-neighbor bonds are considered, and a composition independent value

Jan 1, 1967

By G. R. Love, M. L. Picklesirner

THE use of color adds a new beauty, power, and versatility to metallography. This has been amply demonstrated in a number of public exhibits and on the walls of corporate, government, and university metallographic laboratories around the world. Indeed, in a number of cases, the color not only is of esthetic value but is scientifically essential to the competent examination of particular samples and systems. Optical strain analysis,' determination of true grain size in U-A1 alloys: phase identification in Nb-base alloys,3 analysis of transformation rates in heat-treated Nb-Zr alloys,4 measurement of solidification segregation in cast Nb-Zr alloys,' study of the intermediate phases in Nb/Sn diffusion couples,6 investigation of the oxidation kinetics at various surface orientations in single crystals,7'8 and a number of other research efforts9'10 would have been vastly more difficult without the extra clarity and distinction introduced by color—either the colors resulting from particular polarized light techniques or the interference colors obtained by oxidation. It is unfortunate that the beauty of colored micro-structures cannot be shared more widely, but the economics of publishing a technical magazine apparently prohibits color plates except under extraordinary circumstances. It is doubly unfortunate that no convenient, general method exists for communicating the information available in colored microstructures to the scientific community. True, in some instances the color changes observed are dramatic enough that direct black and white photography is adequate. In photoelastic stress analysis, several orders of interference fringes may be produced and it is frequently desirable to suppress the color effects (use monochromatic light) to simplify interpretation. On the other hand, relatively minute color variations may be readily detectable by eye, be of considerable assistance in interpreting a structure, and yet be enormously difficult to reduce to an unambiguous black and white print. In order to illustrate a possible compromise or solution to the above problems, we wish to show three black and white photographs of the same region of an Nb/Sn diffusion couple whose interpretation depends heavily upon use of color techniques. These micro-structures were obtained from a section through a rod consisting of commercial-purity niobium tubing filled with 99.995 pct Sn (melt-filled in 10"6 Torr vacuum). The composite rod, measuring 500 mm long, was bent into a hairpin shape and inserted into water-cooled copper grips in a vacuum high-temperature furnace. The rod was outgassed for 2 hr at a furnace temperature of 800°C and was further heated by self-resistance using a 2.2-kva ac power supply. The rod was raised to 1910°C over a 4+-hr period, held for 15 min, slow-cooled to 1500°C over a -hr period, and free-cooled to room temperature (all temperatures were measured with W5Re/W26Re thermocouple). Throughout the heat treatment the ambient pressure was kept below 8 x lo-' Torr. Metallographic preparation of the sample was completely conventional except that it was necessary to extend the grinding steps to remove damage in the brittle NbsSn phase introduced by sectioning. No satisfactory chemical or electrochemical etch has been found for these diffusion couples; of those which have been tried, any that attack the niobium-rich phases at all attack the tin-rich phases disastrously. However, the final polishing steps did produce a slight relief effect and this, coupled with anodizing, yielded excellent clarity in the microstructures for direct observation. The anodizing voltage was chosen to give maximum change in color per unit change in composition. In this case, indeed normally, this maximum sensitivity occurred in the blue-to-red color range. The pure niobium tube wall anodized to a relatively bright blue

Jan 1, 1967

By E. Lifshin, R. E. Hanneman

QUANTITATIVE applications of the electron micro-beam probe frequently involve the evaluation of complex mathematical expressions and/or the analysis of large amounts of experimental data. The purpose of this communication is to describe briefly a versatile and useful computer program system that is applicable to analyze rapidly a wide variety of practical microprobe problems. This system consists of a group of ten FORTRAN programs that can be stored on tape, cards, or in the memory disc of the computer. These programs, or links, can be run individually or in any prespecified sequence without interrupting the operation of the computer or without destroying information which is being transfered from one link to another. For the program system described here a GE-235 computer with disc storage was used, so that the DCHAIN method of program linking was employed. Included in the library are programs to: 1) initiate analysis of a new set of data and transfer control between all other programs in any predetermined manner; 2) generate theoretical calibration curves of composition vs relative intensity; 3) generate empirical deviation parameters from least-square fits of experimental calibration data from standards of known composition; 4) convert raw X-ray data to corrected composition; 5) determine inter diffusion coefficients by Matano analysis of con centrat ion -distance data on a uniaxial diffusion couple; 6) determine activation energies and frequency factors of temperature-activated processes such as diffusion; and 7) generate calibration curves for determination of the thickness of thin films using microanalysis. A detailed description of these computer programs and their underlying principles is available on request from the authors."' The first program to generate theoretical calibration curves of corrected relative intensities vs composition uses the Poole and Thomas atomic number correction' and the Philibert absorption factor' with a voltage-dependent mass absorption coefficient for electrons in the alloy. A modified Castaing fluores- cence correction is also used which includes the effects of both Ka and KO radiation and over voltage.' Once the theoretical curves have been calculated in 1 wt pct intervals, these results are least-squares fit to obtain Ziebold deviation parameters' which are stored in COMMON in the computer memory. The net discrepancies between the original theoretical calibration curve and the regenerated curve using the Ziebold parameter are computed. Although this link is explicitly written for K-K fluorescent interactions, it can be applied to K-L, L-K, and L-L interactions as previously disc~ssed."~ Similar programs have also been written to utilize the Wittry fluorescence correction, Birks combined corrections, and various other corrections.' These modified programs have proved to be quite useful for quantitative comparisons of the results of the various theories. The program for conversion of raw X-ray data to corrected composition includes corrections for drift, backround, and instrumental dead time. The corrected intensities are converted to composition by use of the Ziebold equation"2 and parameter obtained from the program system. The results can be obtained for either atom or weight fractions. In addition to accurately computing interdiffusion coefficients the Matano analysis program calculates least-square smoothed values of concentration, concentration gradient, and curvature for each point on the raw input concentration profile. In order to obtain high accuracies a unique method of performing a least-square polynomial fit to incrementally advancing profile segments which overlap is used.' This program has been successfully modified for use in ternary diffusion problems3 and can readily be modified to handle analysis of diffusion profiles which include phase boundary discontinuities. This link is generally applicable to analysis of interdiffusion data obtained by other techniques as well as by the microprobe. The primary function of the next program is to least-squares fit experimental diffusion data to the normal Arrhenius function: D = Doexp(-Q/RT), to obtain values of Do and Q. In addition the probable error and one, two, and three u statistical confidence limits of DO, Q, and log D are evaluated. This program is also directly useful for analysis of any other simple temperature-activated processes including conductivity, and certain deformation and chemical processes. The program to generate calibration curves for film-thickness determination using the microprobe is based on a numerical integration of the equation derived by Cockett and ~avis.' Values of film thickness obtained by this program for copper on various substrates are in good agreement with measurements made by other techniques. Versions of the above program system have been prepared for use with or without a remote teletype connection to the computer for processing on either a real-time or time-share basis. The instrumentation coupling a microprobe to a teletype for automatic data collection and analysis by the presently described program system has been reported elsewhere by the authors.' If teletype equipment is not used to communicate with the computer, standard methods of card reading and tape reading can be used. In either

Jan 1, 1967

By E. R. Gilbert

Klopp et al. have reported data on tensile and creep properties of are-melted and electron-beam-melted tungsten. We would like to point out some similarities between their creep results and ours on are-melted and powder-metallurgy tungstenand offer some alternate interpretations of the data which lead to different rate-controlling mechanisms. Klopp et al. observed extensive transient creep in the 2250" to 3500°F temperature range where the acthetivation energy is 106,400 ± 3300 cal mole-1. They suggest cross slip as the possible rate-controlling mechanism since "cross slip may occur only by the movement of screw dislocations, and not edge dislocations, thus allowing only partial recovery of the strain hardening and resulting in a continuously decreasing creep rate, characteristic of transient creep.'' Our tests on are-melted tungsten and powder-metallurgy tungsten displayed an extensive transient creep stage in the same temperature range but they also displayed a steady-state creep stage. The stress levels and strain rates of the two investigations, 1.4 to 7 kg mm-2 and 10-7 to 10-4 sec-1 for that of Klopp et al. and 4.5 to 10 kg mm-2 and 10-8 to 10-4 sec-1 for those of Gilbert et al., are overlapping. The activation energy for creep of our powder-metallurgy tungsten is 105,000 cal mole-1. This close agreement with the value found by Klopp et al. suggests that the same mechanism may be common to both types of materials. It may be possible to gain some additional insight into the rate-controlling mechanism by applying the analysis made by conrad22 in terms of the activation volume. The value for the activation volume depends upon the dislocation mechanism and may be used to help differentiate between various dislocation mechanisms. The activation volume for cross slip is 10 to 100 b3. Values determined from our data were 130 to 220 b3 which are in better agreement with the range of 102 to 104 b3 for nonconservative motion of jogs. Values determined from data of Klopp et al. are 240 to 1040 b3. We suggest that the rate-controlling mechanism for creep in this temperature range may be nonconservative motion of jogs assisted by enhanced diffusion along grain boundaries or dislocations. This model requires an activation energy lower than that for self-diffusion as is observed. If this is the controlling mechanism, a higher activation energy which is closer to that for self-diffusion might be expected for tests conducted on specimens with reduced grain boundary area, i.e., larger grain size. In support of this premise we have conducted tests on speci- mens having one to three grains per cross section for which a higher activation energy of 130,000 cal mole-1 was observed. Also, in agreement with results of Klopp et al., a faster creep rate resulted from the increased grain size and probable decreased dislocation density. Further argument against the cross slip mechanism is based on the constant activation energy we obsserved over the range of 5.0 to 10 kg mm-2,21 whereas the activation energy for cross slip displays a significant stress dependence.23 In addition to this, the powe on the stress term for the strain-rate dependence appears too high for cross slip. The values for tungsten fall in the range of 4.5 to 7 (Klopp et al. and Ref. 21) whereas values of approximately 2 are observed in creep by cross slip for hep metals.24 At temperatures from 3300° to 4000°F, Klopp et al. observed an activation energy of 141,000 ± 4000 cal mole-' which is less than that for self-diffusion, 153,000 cal mole-1, 25 and less than that reported for high-temperature creep of powder-metallurgy tungsten by Green:' 160,000 cal mole-1. Klopp et al. suggested that recovery of strain hardening by dislocation climb is the rate-controlling mechanism in this temperature region. Actually an activation energy larger than that for self-diffusion is predicted by this model if the temperature dependence of the elastic modulus27 is taken into consideration. Klopp et al. attributed this lack of correlation to the compositional differences between powder-metallurgy tungsten used by Green and their own arc- and EB-melted tungsten. It is our position that the value of 141,000 ± 4000 cal mole-' represents a transitional value between the higher and lower activation energies and does not represent a discrete mechanism of deformation. If the tests had been extended to higher temperatures the higher value of activation energy would have been observed as has been demonstrated by both our analy sis'' of isothermal test data by GE-NMPO28 and differential temperature tests28 on are-melted tungsten. The activation energies determined (170,000 and 160,000 cal mole-1) were greater than that for self-diffusion and are in better agreement with the value found by Green. The model of dislocation climb is associated with ; activation volume of 1 b3 according to Conrad.22 The activation volume calculated for the creep data of fou independent investigators in the temperature range where the activation energy for creep is near that for self-diffusion (Klopp et al. and Refs. 26, 28, and 30) is 110 to 2800 b3 and is in the range suggested for nonconservative motion of jogs. In the case of tungsten this mechanism may be preferred over that of dislocation climb. Sincere appreciation is expressed to Messrs. J. E. Flinn and F. L. Yaggee for the helpful discussions and suggestions in the preparation of this communication.

Jan 1, 1967

By J. E. Flinn, E. R. Gilbert

Recently, Green reported some high-temperature, 0.60 to 0.89 T3, creep results on unalloyed tantalum. From his study he determined an activation energy of 114 kcal per mole for steady-state creep using the T, differential-temperature method25 for testing. He accounted for the difference between this value and 110 kcal per mole for self-diffusion by the temperature dependence of the elastic modulus, 4 kcal per mole. This reported activation energy is in apparent disagreement with that which can be determined from Green's isothermal data, which we have plotted as log creep rate vs 1/T in Fig. 15. From this figure, it appears that there are two activation energies of -185 kcal per mole at the higher temperatures and -75 kcal per mole at the lower temperatures. It is not obvious that the data can be fitted to a straight line corresponding to an activation energy of 114 kcal per mole. One is led to two possible conclusions regarding Green's study: there are two discrete processes controlling the creep rate from 0.60 to 0.89 Tm or the apparent activation energy is not discrete but continuously increases with increasing temperature. The former speculation would be in closer agreement with the high-temperature creep behavior of tungsten.28 The apparent disagreement between the activation energies determined by the AT and isothermal methods certainly suggests that further study on the high-temperature creep of tantalum is needed.

Jan 1, 1967

By C. G. Dunn

James, Jones, and Leak (JJL) conclude that growth-rate and orientation-distribution data obtained in a steep thermal gradient should be used with caution to account for isothermally produced recrystallization textures. I agree. However, it is not clear whether they conclude a) that the orientation dependence of rate of growth of secondaries in (commercial) silicon iron depends on both temperature and a temperature gradient or b) that, in applying rate data obtained in a steep thermal gradient, the isothermal annealing temperature must be close to the temperature for which the rate data apply. Also, it is not clear what tem-

Jan 1, 1967

By H. M. Strong, R. A. Oriani

THE technological interest attaching to light, age-hardening alloys for structural uses has been pointed out to one of us.1 A potentially interesting alloy would be titanium-rich Ti-Mg alloy, provided that sufficient solid solubility exists. or could be induced at high pressure. and provided also that age hardening can be induced by proper temperature and/or pressure annealing. It was decided therefore to explore the feasibility of producing a Ti-Mg alloy in the high-pressure apparatus. Experimental. Three high-pressure runs have been carried out. In each case the geometry of the sample was that of a cylinder of titanium of commercial purity, into which a narrow hole had been drilled along the axis; this hole was filled with magnesium wire,

Jan 1, 1967

By C. S. Yust, C. S. Morgan

ThIS note reports the observation of masses of dislocation etch pits around the weld necks of small single-crystal particles of calcium fluoride sintered to a cleaved face of a larger CaFz crystal. Crystal particles in the -50 +I00 mesh size range were placed on freshly cleaved CaFz surfaces and heated at 1250°C for 30 min in a tantalum container in an argon atmosphere. The sintered specimens were then etched at room temperature for 40 to 50 min in a 2 pct sulfamic acid solution which is a selective etch for dislocations in caF2.' Figs. 1 through 3 show the masses of dislocation etch pits observed around weld necks after etching. In some cases, particles were gone after removal of the specimens from the furnace although weld necks were readily visible. In other instances, no etch pits formed around a weld neck. A possible cause of concentrations of dislocations on the crystal surface is mechanical deformation of the base crystal when particles are dropped on it. If such a deformation does occur, it would be much smaller than that caused by the light punching of a crystal with a sharp instrument which results in large concentrations of etch pits. However, crystals deformed by punching with the sharp instrument and annealed at the conditions of these experiments (1250°C for 30 min) before etching showed no concentrations of dislocation etch pits. It is obvious that dislocations from the much smaller deformations, possibly created when particles are placed on the surface, would also anneal out. Etching of large crystals which had particles placed on them in the usual manner but which were not heated showed no dislocation concentrations such as shown in Fig. 1. The magnitude of dislocation etch-pit concentrations did not vary with extensive variation of the cooling rate. The appearance of many of the etch-pit clusters is typical of a well-annealed condition, indicating that the dislocation concentrations formed before the specimen temperature was lowered. Therefore, it is evident that thermal stresses in the neck area did not create the deformation indicated by the presence of the dislocations. The possibility exists that the etch-pit concentrations at places where particles had been removed may be the result of deformation accompanying the fracture of the sintered bond. That this is not so was demonstrated by breaking off particles around which no etch pits occurred. Re-etching never resulted in the large concentrations observed at sintering sites. The stress available to effect material movement during sintering of two particles will depend on the geometry at the contact point but can easily exceed the macroscopic yield stress in CaFz systems. It appears that the plastic deformation observed results from sintering or simply from the weight of the small particles. It has been previously argued that plastic flow makes an important contribution to the initial densification of oxides having the fluorite crystal structure.2p3 If plastic deformation occurs, it would begin as soon as the temperature is sufficiently high

Jan 1, 1967

By J. W. Downey, A. E. Dwight, R. A. Conner

In a previous paper' we have reported the existence of a number of AB2 Laves phases in which A is a member of the scandium group (including the 1an-

Jan 1, 1967

By R. N. Orava, L. A. Rice

One of the difficulties encountered in the preparation of titanium specimens for transmission electron microscopy is the formation of a surface hydride phase during the thinning operation at ambient temperatures. This necessarily destroys contrast, obscures features of interest, and often leads to misleading results. By cooling the polishing solution to temperatures below 0°C this problem has been overcome in the past.' However, since the cooling procedure is somewhat inconvenient, a technique was developed at this laboratory for thinning titanium at room temperature. The material examined was A-70 grade commercial-purity titanium purchased from the Crucible Steel Co. of America. The mechanical and thermal treatments, described elsewhere,* yielded a recrystallized grain size of 4 to 5 p. A slice, 0.5 mm thick and 1.5 mm wide, was cut from a bulk specimen2 using a diamond cut-off wheel. The sample was then coated with paraffin wax. Two concentric holes, about 0.03 in. in diam, one at each broad face, were scribed through the wax to the surface of the metal. Subsequent polishing for several minutes resulted in a preferentially thinned or "dimpled" region. Thereafter, the wax was removed and the entire specimen polished to the point of breakthrough at the base of the dimple. Polishing was effected chemically in a solution comprised of 30 pct HF and 70 pct HN03 by volume, kept at room temperature (20" to 25OC). The specimens were mounted in a stereo holder and examined at 100 kv in a Philips l00 B Electron Microscope. A micrograph from a foil prepared in this way is shown in Fig. 1. Several points are noteworthy. This electron micrograph shows neither evidence for the formation of a hydride phase due to specimen preparation nor, moreover, any obvious surface contamination in electron-transparent areas of a freshly prepared foil. Localized variations in foil thickness observed in some specimens seem to be a characteristic of this chemical polish but do not seriously detract from foil quality. With care, the lifetime of a good specimen exceeded 2 hr in the beam. On the other hand, the exposure of a sample to air at atmospheric pressure, when still warm from the beam, clearly resulted in the deterioration of a formerly clean area just previously in the field of view. An example in Fig. 2 of a contaminated region reveals features, and "spots", not unlike those observed in much purer material by Yamane and Ueda. Consequently, one can conclude that: 1) titanium can be thinned satisfactorily in a solution at room temperature for transmission electron microscopy; 2) large-scale precipitates, >50A in diam, are absent in commercial-purity, recrystallized, furnace-cooled, A-70 titanium containing about 3800 wt ppm interstitials and the same amount of iron; 3) care must be taken not to attribute surface contaminants to precipitates. The authors are grateful to the Franklin Institute for financial support and permission to publish.

Jan 1, 1967

By Edward J. Ryan, E. A. Peretti

iV preliminary X-ray and metallographic survey of the ternary system Bi-In-Te revealed that the following isopleths could form quasibinary systems: InTe-Bi, InTe-InBi, InTe-BizTe3, and InzTe3-Bi2Te3. The nature of the InTe-Bi phase diagram was established by Bologna and Peretti.' This article presents the results of an investigation of the InTe-InBi system by thermal analysis, X-ray methods, and metallographic examination. The bismuth and tellurium were bought from the American Smelting and Refining Co. The tellurium had the following spectrographic analysis: 0.0001 pct Mg, 0.0001 pct Si, 0.0001 pct Fe, 0.0002 pct Al, and 99.999+ pct Te (by difference). The bismuth assayed: 0.0001 pct Mg, 0.0001 pct Pb, 0.0001 pct Fe, 0.0001 pct Cu, and 99.999+ pct Bi (by difference). The indium was obtained from the Indium Corp. of America and contained 0.002 pct Cu, 0.006 pct Pb, 0.01 pct Sn, 0.01 pct Zn, and 99.97+pct In. The alloys were made by melting the required proPortions of InTe and in evacuated, sealed quartz

Jan 1, 1967

By G. P. Conard, E. H. Rennhack

The creep behavior of hot-rolled, hypoeutectic Zn-Ti alloys was investigated in the temperature range from 0.43 to 0.53 TM. Secondary flow was found to originate primarily from strain-induced gvain growth where grain boundary )nigvation served to relieve the strain energy of distortion introduced by slip, grain boundary sliding, and subgvain formation. The extent to which this recovery mechanism operated was determined by the ratio of grain width to the spacing between planar fibers of TiZn,, compound particles generated in these alloys during rolling. When this ratio was unity, creep resistance demonstrated a marked improvement. In this condition, which was fulfilled by annealing following rolling, structural stability was enhanced with decreasing grain size below the equicohesive temperature (-0.5Tm), while the reverse was true above this temperature. TITANIUM concentrations approaching the eutectic composition of 0.23 wt pctl have been shown to promote a significant increase in the creep resistance of rolled zinc,2 The alloying effect created with titanium is somewhat unique; a structure closely resembling that of a fiber-reinforced metal composite can be developed which selectively modifies creep strength in preference to other mechanical properties. In an earlier investigation,~ the present authors found that, while the fiber network, composed of individual TiZn,, compound particles, had a distinct influence on rolled texture, the crystallographic variations produced were of minor importance with respect to creep. Rather, creep resistance seemingly increased when the grain size appeared to coincide with the in-terfiber spacing. The work described here was undertaken to explore this effect in greater detail. EXPERIMENTAL PROCEDURE Three zinc-base alloys containing 0.05, 0.12, and 0.16 wt pct Ti were prepared from CP zinc and iodide titanium in the form of 4 by 2 by f in. chill-cast ingots. The melting and casting procedures for these alloys have been detailed el~ewhere.~ Individual ingots of each alloy were hot-rolled at 200°C (392°F) to total reductions of 10, 25, 50, 75, and 90 pct in from one to five passes, respectively, employing a 10-min reheat prior to each rolling pass. With grain, tensile-type creep specimens with a 1-in.-long, -in.-wide gage section were machined from the rolled strips for test purposes. Annealing studies to explore the influence of grain size on secondary creep flow were carried out at 400°C (752°F) in argon for times extending up to 60 min. The grain-size effect was evaluated in terms of average grain width and length values statistically derived from lineal intersection measurements.4 A similar method was applied in establishing the average interfiber spacing, i.e., average perpendicular distance between adjacent planar fibers. The creep characteristics of the alloys were investigated by means of constant-load and constant-stress creep tests. The former tests were conducted at 25°C (77°F) under an initial stress of 10,000 psi, while the latter were performed in the range from 25°C (77°F) to 90°C (194°F) at stress levels varying from 8000 to 22,000 psi. Total specimen strain, as determined with Budd HE-1161-B strain gages, was in excess of 0.10. Maintenance of constant stress was achieved through periodic load reductions made at 0.01 strain intervals to compensate for the attendant incremental reduction in specimen cross-sectional area. The maximum indicated error in the applied stress at these strain intervals was less than 3.0 pct. RESULTS AND DISCUSSION Constant-Load Creep. In an effort to clarify the in-terrelation between interfiber spacing and grain size with respect to the creep resistance of the Zn-Ti alloys, their separate effects on secondary creep rate were determined as a function of titanium content and rolling reduction. These results are set forth in Figs. 1 and 2, respectively. The average grain diameter plotted in Fig. 2 was resolved from average grain width and length values. No data are presented for reductions of less than 50 pct because of the inability to obtain consistent measurements on these strips. The curves of Fig. 1 indicated that, for a given titanium content, a decrease in interfiber spacing, as produced with increasing reduction, promoted a decrease in creep rate. Depending on titanium content, however, wide variations in creep rate occurred at the same interfiber spacing suggesting that interfiber spacing, by itself, has little or no influence on creep resistance. Grain size, on the other hand, decreased progressively with both increasing rolling reduction and titanium content, the effect of which led to a pronounced decrease in creep rate, particularly when the average grain diameter became smaller than 3.0 x 10"4 in., Fig. 2. The continuity of this relationship tended to support the view that grain size rather than interfiber spacing was predominant in controlling secondary creep. Annealing Effect. The observed dependence of creep flow on grain size suggested that a further contribution to creep resistance would result when the alloys were annealed to effect a coincidence between grain width and interfiber spacing, see Fig. 3(b). ~eiides creating an immediate barrier to grain boundary movement, annealing offered the possibility of providing increased structural stability by eliminating many high-energy, mobile grain boundaries.= To test this hypothesis, specimens from the Zn-0.16 Ti strips reduced 75 and

Jan 1, 1967

By P. Wynblatt, J. E. Dorn

The effect of strain rate, temperature, and interstitial impurity concentration on the flow stress was investigated in a poly crystalline Fe-2 pct Mn alloy. The temperature dependence of the flow stress was found to be independent of the interstitial impurity concentration, removal of interstitials merely decreasing the atherma1 stress level. Below 160%, the large temperature dependence of the flow stress was interpreted in terms of the Dorn-Rajnak theory of the Peierls mechanism of plastic deformation. Above 160"K, some other thermally activated intrinsic meckanisln seems to be operating. The strong temperature dependence of the flow stress of bcc iron at low temperatures has been studied by numerous investigators and interpreted in terms of several different thermally activated dislocation mechanisms. The following mechanisms have been proposed: a) interaction of dislocations with interstitial impurity atoms1 or with solute atoms in general; b) interaction of dislocations with clusters of impurity atoms;3 c) resistance to the motion of dislocations due to jogs on screw dislocations;* d) resistance to the motion of dislocations due to the Snoeck effect;' and e) interaction of dislocations with the intrinsic resistance of the bcc lattice or Peierls "hills". In previous work: it was found that the plastic behavior of polycrystalline iron containing 2 wt pct Mn (and 100 ppm C + N) is in good agreement with predictions based on the Peierls mechanismlo from 77" to 160°K whereas from 160" to about 370°K another as yet unidentified thermally activated mechanism is operative. The purpose of the present investigation was to determine the effect of interstitial impurities on the temperature dependence of the flow stress, by purifying the previously investigated alloy with respect to interstitial impurities. The investigation revealed that removal of the interstitial impurities to a level that eliminated Cottrell locking and the Portevin-LeChatelier effect (i.e., serrations in the stress-strain curve due to dynamic strain aging) affects neither the strong temperature dependence of the flow stress at low temperatures nor the general characteristics of the higher-temperature behavior. Such purification, however, lowered the athermal yield stress. I) EXPERIMENTAL PROCEDURE AND RESULTS The material used in this investigation consisted of an Fe-2 wt pct Mn alloy having the following additional elements present: 0.004 pct C, 0.006 pct N, 0.05 pct 0, 0.004 pct S, 0.003 pct P, and 0.001 pct Si. This was the same material as that studied in the previous investigation and will henceforth be referred to as the "impure material". The as received -jr by 2 in. hot-rolled bars were cold-rolled to 0.08-in. thickness, recrys-tallized under argon for 30 min at 80O0C, and further cold-rolled to 0.053-in. thickness. Flat tensile specimens 3 in. wide having a 1.625-in.-long gage section were machined from the sheet and then purified. The first stage of purification consisted of holding the specimens at 850°C for 24 hr in a stream of hydrogen saturated with water vapor at room temperature. Material prepared in this fashion will subsequently be referred to as "wet hydrogen purified material". It has been estimated that this type of treatment reduces the carbon content of iron to less than 5 ppm.' The second stage of purification consisted of holding the specimens in a closed system through which hydrogen was circulated past the heated specimens as well as a zirconium hydride getter. The specimens were held at 850°C and the getter at 800°C. The process was continued for 212 hr. The starting material for this process was wet hydrogen purified material. Material prepared in this manner will be referred to as "ZrHz purified material". The technique used was substantially the same as that described by Stein et al.' who have shown that the carbon level at the end of the process is reduced to about 5 parts per billion. The mean grain size of the three materials was found to be -60 C( for the impure material and -160p for the wet hydrogen and ZrHz purified materials. All tensile testing was carried out on an Instron Testing Machine either in controlled-temperature baths or at fixed-point baths such as boiling liquid nitrogen, and so forth. When fixed points were used the temperature was kept constant to better than *1°C whereas in all other tests the temperature variation was less than *2°C. Test of Purity. It was not possible to determine the purity achieved at each stage of the purification because the resulting level of interstitial impurities was near or below the limit of sensitivity of standard analytical techniques. It was possible, however, to obtain a qualitative measure of the extent of purification from the appearance of the stress-strain curves for the three materials. Fig. 1 shows the stress-strain curves for the three different materials tested at 300°K. It can be seen that the effect of wet hydrogen

Jan 1, 1967

By George A. Colligan, John M. Lo

Electrical resistivity as a function of temperature was investigated in undercooled gallium and under-cooled Ga-In alloy of eutectic compositian to examine structural changes in undercooled melts. A continuous linear extension of the resistivity was determined for 99.999 pct pure gallium when undercooled below the stable Ga(l)-liquid, and the metastable Gafl)-liquid equilibria. In icndercooled Ga-In, a significant continuous negative departure from linear resistivity behavior was observed below the eutectic temperature. All resistivity measurements were made by the four-point probe technique. ThE temperature range for investigations into the physical properties of liquids before freezing has been greatly extended with the undercooling of massive melts of pure metals and alloys. Experimental determinations of thermal and transport properties and diffraction patterns in undercooled systems should throw further light on the structural behavior of liquids. Many measurements showing prefreezing anomalies in viscosity1'5 have been regarded677 as evidence for structural groupings in the liquid state. However, the majority of viscosity results,~)~-~~ conforming to the law 17 =A exp(~/RT), do not support theories of atomic aggregation. For the system Cd-Sb, which exhibits a metastable solid phase, Fisher and Phillipsg reported that, in undercooled alloys, the activation energies for viscous flow below the stable liquidus are much higher than those above it. Similarly, Miller et a1." observed a doubling of the activation energies for electrical conductivity in undercooled Cd-ib alloys. These effects were suggested as indicative of atomic association and clustering in the liquids at lower temperatures. With the recent establishment of metastable phases in pure gallium22 and its alloys,23 attempts were made during this investigation to undercool bulk samples and to determine the temperature dependence of electrical resistivitv. Pure gallium, when undercooled below -17°C at atmospheric pressure, can crystallize to either a stable Ga(1) phase (mp, 29.78"C) or a metastable phase identi-

Jan 1, 1967

By A. W. H. Morris, G. H. Laurie, J. N. Pratt

Using- galvanic cells of the form Sn(liq)/Sn" (LiCl-KC1-SnCl,)/Sn-Ag (alloy), measurements have been made of relative thermodynamic properties of the a, C, E, and liquid phases of the Ag-Sn alloy system. Partial heats of solution of the components in the liquid alloys lzave also been observed by direct cal-orimetric measurement in an isoperibol calorimeter. The thermodynanzic quantities are disczlssed in relation to structural and other properties and the existence of anomalous minor fluctuations in the partial heats and entropies of solution in liquid alloys is tentatively suggested. In the course of a recent electro motive-force study of the thermodynamic properties of Sn-Ag-Pd liquids,' some measurements were also performed on the Ag-Sn binary system. Most previous thermodynamic studies of this system have been concerned with the liquid state. Measurements confined to the limiting heat of solution of silver in liquid tin have been made by many calorimetric workers2 while high-temperature calorimetric measurements of the heats of formation of the full range of liquid alloys are reported in the early work of Kawakami~ (1323°K) and more recently by Wittig and Gehrin~(1248°K). Electromotive-force studies on liquid alloys have been made by Yanko, Drake, and Hovorka' (606" to 686°K; 86 to 99.4 at. pct Sn) and by Frantik and Mc Donald' (900°K; 30 to 90 at. pct Sn). The only known measurements on the solid state are of heats of formation of the a, £, and c phases; these values were obtained using tin-solution calorimetry, at 723"K, by Kleppa,~ whose investigation also yielded heats of formation of liquid alloys containing more than 64 at. pct Sn. The present experiments on the Ag-Sn alloys include a re-examination of the liquid phase and, because of the dearth of free-energy data for the solid state, attempted measurements on the a, c, and E phases. The principal new feature of electromotive-force results obtained for the liquid phase was an indication of anomalous fluctuations in the partial heats and entropies of solution of tin at certain compositions. However, since the values for these thermodynamic quantities were determined from the temperature coefficients of cell potentials, which are commonly subject to considerable error, confirmation by calorimetric measurements was considered desirable. A detailed investigation of the partial heats of solution of the components in the binary liquids was made using a liquid metal solution calorimeter. I) GALVANIC CELL STUDIES a) Experimental Details. Measurements were made, as a function of alloy composition and temperature, of the potentials of reversible galvanic cells of the form: ~n(liq)/~n++/~n-Ag (solid or liquid alloy) Details of the apparatus and experimental techniques have been given elsewhere.' so that a brief account will suffice here. Molten salt, 58 mole pct LiC1-42 mole pct KC1, containing small amounts (1 to 2 mole pct) of stannous chloride was used as the electrolyte. The salts were dehydrated by pre-electrolysis and vacuum -drying techniques. Cells were established under an argon atmosphere by immersing tin and alloy electrodes in the molten salt contained in a large silica tube, heated in a vertical resistance furnace. The tube was sealed at the top by a head plate provided with openings permitting the simultaneous insertion of six electrodes, a central thermocouple sheath, and connections to vacuum and argon lines. Temperatures were controlled to *0.2"C over prolonged periods, with maximum variation over the electrodes at any time of 0.l°C. Temperatures were measured with a standardized Pt/13 pct Rh-Pt couple. The electromotive force of this and the cell potentials were measured on a Cambridge Vernier potentiometer and short-period galvanometer. Alloys were prepared from Pass "S" tin (99.999 pct) and Johnson-Matthey high-purity silver (99.999 pct) by melting in evacuated silica capsules and quenching in cold water. For liquid phase experiments, pieces of the resulting alloys were remelted into prepared silica electrode units, while solid electrodes were prepared by remelting into 3-mm bore tubing, inserting a cleaned molybdenum lead wire, and quenching to produce uniform rods about 3 cm in length, with soundly attached leads. In all cases remelting was done under an argon atmosphere. The solid electrodes were subsequently annealed in evacu ated silica tubes for 14 days at about 20°C below the solidus and quenched. Analyses showed that these techniques produced uniform electrodes with no significant change from weighed out compositions. b) Results and Discussion. Measurements were made on about forty alloys in the solid and liquid states, over varying ranges of temperature between 550" and 1050°K. Stable, mutually consistent, and reproducible electromotive-force data were obtained with most liquid alloys and these are shown in Fig. 1. Investigations were extended below the liquidus tem-

Jan 1, 1967

By R. E. Mussler, F. E. Block, T. T. Campbell

An exploratovy study was made to deternzine the feasibility of preparing beryllium by the metallother-. mic reduction of beryllium oxide. The procedure involved heating a relatively nonvolatile metal reductant in contact with beryllium oxide in a vacuum. Beryllium vapors formed in the reaction were condensed as a coherent deposit on a heated surface. Reductants tested included tanthanun, yttrium, thorium, Th-Mg, and Zr- Ti alloys, and the hydrides of lanthaniir~z, yttriunz, and zirconiur?7,. Test ten7pevatures ranged from 1350'to 175O' C, and reaction times ranged frot 30 to 100 lzr. In most cases metal recoveries were lola, although yields close to 90 pct of theoretical were obtained with latzthanum, yttrium, and zirconium reductants. In most cases metal deposits were contanzinated by beryllides, /ls/cally of the Beln M or Bel3 M type. BERYLLIUM has a variety of unique properties including light weight (sp gr 1.85), low thermal neutron absorption cross section, high scattering cross section, excellent dimensional stability, high strength to weight ratio, high melting point (1285"C), high specific heat, and high thermal conductivity. Interest in beryllium as a structural material in aerospace and nuclear-reactor applications is based on these properties. In general, the potential of beryllium has been only partially realized, largely because of the brittleness of poly crystalline forms of beryllium, difficulties associated in its fabrication, and joining problems encountered in its use in structural applications. Several excellent books and monographs are available to those interested in the occurrence, extractive metallurgy, and utilization of beryllium.1"* Although an extensive amount of research on beryllium has been in progress during the past 10 years, much of the work has been concerned either with the so-called "ductility problem" or with the development of methods of fabrication and evaluation of properties of various commercial or purified grades of metal. A recent survey of the literature indicates that only limited efforts are presently being directed toward developing new methods for reducing beryllium compounds to metal. Two major commercial methods now used to produce beryllium are the magnesium reduction of beryllium fluoride and e lec trow inn ing of beryllium from fused sodium chloride-beryllium chloride salt baths. Only a limited amount of work has been done on the direct reduction of beryllium oxide. Major factors which complicate this method are the great stability of beryllium oxide and the reactive nature of beryllium metal. The stability of the oxide necessitates extremely high reduction temperatures and vacuum operation to liberate beryllium metal vapor and cause reactions of the following type to proceed: XBeO(s) +YM(s)-MYOX(s) + XBe(& As early as 1939, roll' used this reaction for the direct reduction of beryllia by zirconium and titanium, and later in 1952 ~a~el~ studied the reduction of beryl-

Jan 1, 1967

By S. A. Mersol, C. T. Lynch, F. W. Vahldiek

The room-temperature microhardness of as-grown and annealed MoaC single crystals was measured on the (0001), {2110), and1012) planes using Knoop and Vickevs indenters at loads ranging front 25 to 1000 g. The orientatimz dependence of hardness with respect to crystal axes was also studied. The average random hardness of as-grown crystals was determined to be 1520 kg per sq nm. Annealing to 2000°C decreased. the average hardness by 150 units. An increase in hardness after annealing at 2200 ;C was noted. Optical and electron microscopy revealed slip and twin traces on all planes studied, as produced by mi-cvohavdness indentations. Basal (0001)(2i10) slip was determined to be the primary slip system and was substantiated by electron transmission microscopy. A secondary {1010)(2110) slip was produced by mi-crohardness indentations. The lattev also produced twinning- of the {10i2)[0001] type, as proven by electron diffraction. Electrical resistivity and elastic-modulus anisotropy were found and correlated with hardness anisotropy and Mo2C crystal structure. Elastic-modulus values were obtained by microhard-uess and ullrasonic methods. Bonding mechanism of Mo2C is discussed. ROOM-TEMPERATURE microhardness indentations are useful for studying hardness anisotropy, slip, and twinning in brittle materials. Slip has previously been produced in this manner in and WS~~.~ Recently, the authors5 reported slip of the {10i0)(11~0) type produced by high pressure and microhardness indentations on hexagonal TiBz (c/a = 1.066) single and polycrystals. This slip system was also reported by French and ~homas' and Taka-hashi and ~reise~ for hexagonal WC (c/a = 0.976) crystals. These results suggest that prismatic rather than basal slip is favored in hexagonal nonmetallic materials having a c/a ratio considerably less than the ideal (1.633). Buerger precession and cylindrical X-ray rotation patterns were previously' taken on cleaved sections of the Mo2C single crystals studied in this work. Th~y were found to be hexagonal MoaC with a. = 3.0233A, co = 4.7344A, and C/O = 1.5660. The latter ratio is close to that of the beryllium metal (c/a = 1.57), which slips primarily on the (0001) plane: but also slips on the (1010) planes.'0 ~irconium" (c/u = 1.59) and titanium12 (c/o = 1.59) deform mainly by slip on nonbasal planes which contain a close-packed direction. This is due to the fact that for these two metals the initial resolved shear stress for slip on the (10i0) prismatic planes is lower than that on the (0001) plane. The prominence of basal rather than prismatic slip in metals of high c/o ratios is shown by cadmium (c/a = 1.89), zinc (c/a = 1.86), and magnesium (c/a = 1.62) which deform mainly by basal slip. However, in case of the latter, by stressing magnesium crystals in tension or compression parallel to the basal plane, slip on (10i0) planes can also be produced.13 Several hardness values for polycrystalline Mo2C are reported in the literature: Biickle ' and Samsonov'~ give a value of 1800 and 1479 kg per sq mm, respectively, at a 100-g load; and Kieffer and Benesovsk~'~ report a value of 1950 kg per sq mm at a 50-g load. ~ott'~ reports a Vickers hardness value of 2000 kg per sq mm, with the load unspecified. A Rockwell A hardness value of RA = 88 has also been reported.'' In the present work, for comparison with single-crystal Mo2C hardness values, a Khnloo value of 1600 It 150 kg per sq mm was found on 99.6 pct pure and 99 pct dense hot-pressed Mo2C. This work was undertaken partly to explain the considerable differences in hardness values reported for polycrystalline Mo2C. EXPERIMENTAL The Mo2C single crystals investigated were prepared by a Verneuil-type process using an electric arc by the Linde Co. of the Union Carbide Corp.lg The largest specimens grown were boules 7 mm in diam by 40 mm in length. The crystals had an average density of 9.04 g per cu cm, with a Mo + C content of 99.8 wt pct. The major impurities were: 100 ppm each Na, Zr, and Ca; 85 ppm 0, 55 ppm Fe, and 10 ppm each Cr and Ta. The crystals were found to be carbon-poor, the average carbon content being 5.73 wt pct (stoichiometric value is 5.89 pct). The molybdenum content was found to be 94.08 pct, which is nearly stoichiometric. Electron-microprobe traverses of selected specimens were done with a Phillips-AMR microanalyzer. Thin-film and carbon replicas were used to prepare electron micrographs. This work was done with a JEM-6A electron microscope. Prior to optical and electron-optical studies, specimens were mounted in Lucite and polished on a vibratory polisher using diamond-paste grades ranging from 9-1 p and Linde A powder for up to 48 hr. Dilute nitric acid was used for thin-section polishing and chemical etching for 1-15 min. Electrical-resistivity measurements at room temperature were taken with a Rubicon bridge, using gold contacts. For hardness measurements, a Tukon Microhardness Tester Type FB with Knoop and Vickers indenters was used. Measurements were taken at loads ranging from 25 to 1000 g; however, the 100-g load was chosen as the standard load. All measurements were taken at room temperature. Indentations of cracking classes 1 and 2 only were considered for hardness determinations.20)21 (There are six cracking classes, ranging from "class 1" for a perfect inden-

Jan 1, 1967